Number of datasets at 200 K and below = 10,663

Key to property symbols (number of datasets):

D = Density (628)	DLL = Linear thermal expansion (ΔL/L) (833)
MTE = Mean coefficient of thermal expansion (828)	CTE = Coefficient of thermal expansion (CTE) (376)
E = Elastic/Young's modulus (605)	G = Shear modulus (464)
v = Poisson's ratio (442)	K = Bulk modulus (435)
TC = Thermal conductivity (805)	TD = Thermal diffusivity (199)
SH = Specific heat (472)	HC = Heat capacity (312)
SSC = True stress-strain curve (tension) (304)	SSCC = True stress-strain curve (compression) (35)
UTS = Tensile strength (673)	YS = Yield strength (tension) (628)
UCS = Compressive strength (3)	YSC = Yield strength (compression) (16)
%El = Elongation (313)	SR = Stress rupture (0)
FEN = Fatigue ε-N curve (39)	FSN = Fatigue S-N curve (216)
CRS = Creep strength (0)	IC = Isochronous creep (0)
HE = Hemispherical total emissivity (70)	NE = Normal total emissivity (60)
VP = Vapor pressure (64)	Vis = Viscosity (35)
ST = Surface tension (20)	RHO = Electrical resistivity (736)
SIGMA = Electrical conductivity (744)	SV = Specific volume (0)
AV = Apparent viscosity (0)	FM = Flexural modulus (6)
FS = Flexural strength (3)	ESSC = Engineering stress-strain curve (tension) (0)
ESSCC = Engineering stress-strain curve (compression) (7)	CRM = Creep modulus (0)
RPB = Relative permeability (0)	AP = Absolute permeability (0)
BH = B-H curve (0)	HB = H-B curve (0)
CL = Core loss (0)	EP = Exciting Power (0)
DCRPT = Relative permittivity (3)	DF = Dissipation factor (2)
RIW = Refractive index vs λ (47)	RIT = Refractive index vs T (55)
S = Seebeck coefficient (185)

Data in Version 9.81

ABS (acrylonitrile butadiene styrene)	Acetal/POM (polyoxymethylene)	Aluminum alloys	Bimetal alloys
Borides	Carbides	Carbons	Cast irons
Ceramic matrix composites	Cermets	Circuit boards & Antenna substrates	Cobalt alloys
Complex oxides, Silicates, & Slags	Controlled expansion alloys	Copper alloys	DAP & DAIP (diallyl (ortho-, iso-) phthalates)
ECTFE (polyethylene chlorotrifluoroethylene)	Electro-ceramics	Elements	Epoxies
EVA (ethylene-vinyl acetate)	Foods	Glasses	High entropy & Equiatomic alloys
Hydrides	Intermetallics	Iron alloys	LCP (liquid crystal polymer)
m-PPE (modified polyphenylene ether)	Magnesium alloys	Magnetic alloys & Electrical steels	Metal matrix composites
Metallic glasses	Minerals, Rocks, & Soils	Miscellaneous polymer composites	Miscellaneous polymers
Mold materials	Nickel alloys	Nitrides & Oxynitrides	Nylons & PA/PI (polyamides)
Organics, Hydrocarbons, & Lubricants	Other materials	Oxides	PAEK & PEEK (polyaryletherketone)
PAI (polyamide-imide)	PARA (polyarylamide)	Parylenes & Polyolefins	PBT (polybutylene terephthalate) & PBT/PET
PC (polycarbonates) & blends	PCT (polycyclohexylenedimethylene terephthalate)	PE (polyethylene)	PEBA (polyether block amide)
PEI (polyetherimide)	PES/PESU (polyether sulfone)	PET (polyethylene terephthalate)	PFA & ETFE (fluorocarbons)
PLA (polylactic acid)	PMMA, PMMI, & Acrylics	Polyesters	PP (polypropylenes)
PPA (polyphthalamides)	PPE/PA (polyphenylene ether/polyamide)	PPE/PP (polyphenylene ether/polyproplyene)	PPE/PS (polyphenylene ether/polystyrene)
PPE/TPE, TPV, & SEBS	PPS (polyphenylene sulfide)	PPSU/PPSF (polyphenyl sulfone)	Precious metal alloys
PSU (polysulfone)	PVF/PVDF/PVC (poly(vinyl/idene fluoride/chloride))	Refractory metal alloys	Resistance alloys
Salts (binary mixtures; Ag-CaF)	Salts (binary mixtures; Ca(NO₂)₂-KBr)	Salts (binary mixtures; KCHO₂-LiClO₄)	Salts (binary mixtures; LiF-Zn)
Salts (monatomic; Br & Cl)	Salts (monatomic; F & I)	Salts (monatomic; S)	Salts (polyatomic)
Salts (ternary mixtures)	Semi/Superconductors & Optical materials	Silicides	Silicones & Elastomers
Solders, Brazes, & Low melting alloys	Structural foams	TCP (thermally conductive polymers)	Thermal coatings
Thermal insulation materials	Thermocouple alloys	Thermoelectrics	Titanium alloys
Tool steels	TPC (thermoplastic copolyester elastomer)	UR, PU, & TPU (thermoset polyurethanes)	Woods
Zinc alloys

Elements	Property : Condition // Data range
Hydrogen	D : liquid \|\| normal H₂ \|\| 14 K to 33 K (-259.1 °C to -240.1 °C) D : liquid \|\| para H₂ \|\| 14 K to 32 K (-259.1 °C to -241.1 °C) D : gas \|\| normal H₂ \|\| 20 K to 3000 K (-253.1 °C to 2726.8 °C) DLL : liquid \|\| normal H₂ \|\| 14 K to 33 K (-259.1 °C to -240.1 °C) DLL : liquid \|\| para H₂ \|\| 14 K to 32 K (-259.1 °C to -241.1 °C) MTE : liquid \|\| normal H₂ \|\| 14 K to 33 K (-259.1 °C to -240.1 °C) MTE : liquid \|\| para H₂ \|\| 14 K to 32 K (-259.1 °C to -241.1 °C) TC : solid \|\| 5 K to 17 K (-268.1 °C to -256.1 °C) TC : liquid \|\| normal H₂ \|\| 15 K to 33 K (-258.1 °C to -240.1 °C) TC : liquid \|\| para H₂ \|\| 15 K to 33 K (-258.1 °C to -240.1 °C) TC : gas \|\| normal H₂ \|\| 20 K to 1000 K (-253.1 °C to 726.9 °C) TC : vapor \|\| normal H₂ \|\| 15 K to 33 K (-258.1 °C to -240.1 °C) TD : liquid \|\| para H₂ \|\| 15 K to 32 K (-258.1 °C to -241.6 °C) TD : gas \|\| normal H₂ \|\| 20 K to 1000 K (-253.1 °C to 726.9 °C) SH : liquid \|\| para H₂ \|\| 15 K to 32 K (-258.1 °C to -241.6 °C) SH : gas \|\| normal H₂ \|\| 0 K to 20000 K (-273.1 °C to 19726.8 °C) HC : liquid \|\| para H₂ \|\| 15 K to 32 K (-258.1 °C to -241.6 °C) HC : gas \|\| normal H₂ \|\| 0 K to 20000 K (-273.1 °C to 19726.8 °C) VP : liquid \|\| normal H₂ \|\| 14 K to 33 K (-259.1 °C to -240.6 °C) VP : liquid \|\| para H₂ \|\| 14 K to 33 K (-259.1 °C to -240.2 °C) Vis : liquid \|\| 15 K to 21 K (-258.5 °C to -252.1 °C) ST : liquid \|\| normal H₂ \|\| 15 K to 20 K (-258.1 °C to -253.1 °C)
Helium	D : solid \|\| 0 K to 27 K (-273.1 °C to -246.1 °C) D : saturated liquid \|\| 2 K to 5 K (-270.9 °C to -267.9 °C) D : gas \|\| 4 K to 3000 K (-269.1 °C to 2726.8 °C) DLL : solid \|\| 0 K to 27 K (-273.1 °C to -246.1 °C) DLL : saturated liquid \|\| 2 K to 5 K (-270.9 °C to -267.9 °C) MTE : solid \|\| 0 K to 27 K (-273.1 °C to -246.1 °C) MTE : saturated liquid \|\| 2 K to 5 K (-270.9 °C to -267.9 °C) TC : liquid \|\| 3 K to 5 K (-270.6 °C to -268.1 °C) TC : gas \|\| 1 K to 2500 K (-272.1 °C to 2226.8 °C) TD : liquid \|\| 3 K to 5 K (-270.6 °C to -268.1 °C) TD : gas \|\| 50 K to 3273 K (-223.1 °C to 3000 °C) SH : liquid \|\| 2 K to 5 K (-270.9 °C to -268.1 °C) SH : gas \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) HC : liquid \|\| 2 K to 5 K (-270.9 °C to -268.1 °C) HC : gas \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) VP : liquid \|\| 2 K to 5 K (-270.9 °C to -268 °C) Vis : liquid \|\| 2 K to 4 K (-270.9 °C to -269.1 °C) Vis : gas \|\| 50 K to 3273 K (-223.1 °C to 3000 °C) ST : liquid \|\| helium I \|\| 1 K to 5 K (-272.1 °C to -268.1 °C)
Lithium	D : solid \|\| 0 K to 388 K (-273.1 °C to 115 °C) DLL : solid \|\| 0 K to 388 K (-273.1 °C to 115 °C) MTE : solid \|\| 0 K to 388 K (-273.1 °C to 115 °C) E : solid \|\| 78 K to 298 K (-195.1 °C to 25 °C) G : solid \|\| 78 K to 298 K (-195.1 °C to 25 °C) v : solid \|\| 78 K to 298 K (-195.1 °C to 25 °C) K : solid \|\| 78 K to 298 K (-195.1 °C to 25 °C) TC : solid \|\| 0 K to 454 K (-273.1 °C to 180.9 °C) TD : solid \|\| 3 K to 388 K (-270.1 °C to 115 °C) SH : solid \|\| 0 K to 454 K (-273.1 °C to 180.5 °C) HC : solid \|\| 0 K to 454 K (-273.1 °C to 180.5 °C) RHO : solid \|\| 1 K to 454 K (-272.1 °C to 180.9 °C) SIGMA : solid \|\| 1 K to 454 K (-272.1 °C to 180.9 °C)
Beryllium	D : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) DLL : solid \|\| polycrystal \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) DLL : solid \|\| a-axis \|\| 80 K to 1273 K (-193.1 °C to 1000 °C) DLL : solid \|\| c-axis \|\| 80 K to 1273 K (-193.1 °C to 1000 °C) DLL : solid \|\| hot-pressed, longitudinal \|\| 120 K to 300 K (-153.1 °C to 26.9 °C) DLL : solid \|\| hot-pressed, transverse \|\| 90 K to 300 K (-183.1 °C to 26.9 °C) MTE : solid \|\| polycrystal \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) MTE : solid \|\| a-axis \|\| 80 K to 1273 K (-193.1 °C to 1000 °C) MTE : solid \|\| c-axis \|\| 80 K to 1273 K (-193.1 °C to 1000 °C) MTE : solid \|\| hot-pressed, longitudinal \|\| 120 K to 300 K (-153.1 °C to 26.9 °C) MTE : solid \|\| hot-pressed, transverse \|\| 90 K to 300 K (-183.1 °C to 26.9 °C) E : solid \|\| 93 K to 1023 K (-180.1 °C to 750 °C) TC : solid \|\| annealed \|\| 0 K to 1400 K (-273.1 °C to 1126.8 °C) TD : solid \|\| annealed \|\| 1 K to 1273 K (-272.1 °C to 1000 °C) SH : solid \|\| 0 K to 1543 K (-273.1 °C to 1270 °C) HC : solid \|\| 0 K to 1543 K (-273.1 °C to 1270 °C) RHO : solid \|\| 1 K to 1500 K (-272.1 °C to 1226.8 °C) SIGMA : solid \|\| 1 K to 1500 K (-272.1 °C to 1226.8 °C)
Boron	D : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) DLL : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) MTE : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) TC : solid \|\| annealed \|\| 0 K to 1100 K (-273.1 °C to 826.9 °C) TD : solid \|\| annealed \|\| 100 K to 300 K (-173.1 °C to 26.9 °C) SH : solid \|\| 100 K to 2350 K (-173.1 °C to 2076.8 °C) HC : solid \|\| 100 K to 2350 K (-173.1 °C to 2076.8 °C)
Nitrogen	D : saturated liquid \|\| 63 K to 126 K (-210 °C to -147.1 °C) D : gas \|\| 77 K to 3000 K (-196.1 °C to 2726.8 °C) DLL : saturated liquid \|\| 63 K to 126 K (-210 °C to -147.1 °C) MTE : saturated liquid \|\| 63 K to 126 K (-210 °C to -147.1 °C) CTE : saturated liquid \|\| 63 K to 112 K (-210 °C to -161.1 °C) TC : solid \|\| 4 K to 26 K (-269.1 °C to -247.1 °C) TC : liquid \|\| 63 K to 125 K (-210.1 °C to -148.1 °C) TC : gas \|\| 78 K to 3273 K (-195.1 °C to 3000 °C) TC : vapor \|\| 60 K to 125 K (-213.1 °C to -148.1 °C) TD : liquid \|\| 64 K to 78 K (-209.1 °C to -195.1 °C) TD : gas \|\| 100 K to 3000 K (-173.1 °C to 2726.8 °C) SH : solid \|\| 15 K to 63 K (-258.1 °C to -210.1 °C) SH : liquid \|\| 64 K to 78 K (-209.1 °C to -195.1 °C) SH : gas \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) HC : solid \|\| 15 K to 63 K (-258.1 °C to -210.1 °C) HC : liquid \|\| 64 K to 78 K (-209.1 °C to -195.1 °C) HC : gas \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) VP : solid \|\| 50 K to 60 K (-223.1 °C to -213.1 °C) VP : liquid \|\| 65 K to 125 K (-208.1 °C to -148.1 °C) Vis : liquid \|\| 67 K to 121 K (-206.6 °C to -152 °C) Vis : gas \|\| 80 K to 2150 K (-193.1 °C to 1876.8 °C) ST : liquid \|\| 64 K to 126 K (-209.1 °C to -147.1 °C) DCRPT : solid \|\| 0 K (-273.1 °C) \|\| 59.5 Hz to 63 Hz
Oxygen	D : liquid \|\| 55 K to 153 K (-218.1 °C to -120 °C) D : gas \|\| 80 K to 3000 K (-193.1 °C to 2726.8 °C) DLL : liquid \|\| 55 K to 153 K (-218.1 °C to -120 °C) MTE : liquid \|\| 55 K to 153 K (-218.1 °C to -120 °C) CTE : liquid \|\| 55 K to 149 K (-218.1 °C to -124.1 °C) TC : liquid \|\| 55 K to 155 K (-218.1 °C to -118.1 °C) TC : gas \|\| O₂ \|\| 50 K to 3273 K (-223.1 °C to 3000 °C) TC : vapor \|\| 90 K to 155 K (-183.1 °C to -118.1 °C) TD : liquid \|\| 55 K to 90 K (-218.1 °C to -183.1 °C) TD : gas \|\| O₂ \|\| 100 K to 3000 K (-173.1 °C to 2726.8 °C) SH : solid \|\| 13 K to 54 K (-260.1 °C to -219.1 °C) SH : liquid \|\| O₂ \|\| 54 K to 90 K (-219.1 °C to -183.1 °C) SH : gas \|\| O₂ \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) HC : solid \|\| 13 K to 54 K (-260.1 °C to -219.1 °C) HC : liquid \|\| O₂ \|\| 54 K to 90 K (-219.1 °C to -183.1 °C) HC : gas \|\| O₂ \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) VP : liquid \|\| 55 K to 85 K (-218.1 °C to -188.1 °C) Vis : liquid \|\| 70 K to 154 K (-203.1 °C to -119.1 °C) Vis : gas \|\| O₂ \|\| 70 K to 2600 K (-203.1 °C to 2326.8 °C) Vis : saturated vapor \|\| 70 K to 154 K (-203.1 °C to -119.1 °C) ST : liquid \|\| 71 K to 89 K (-202.1 °C to -184.1 °C)
Fluorine	D : saturated liquid \|\| 65 K to 105 K (-208.1 °C to -168.1 °C) D : gas \|\| 85 K to 3000 K (-188.1 °C to 2726.8 °C) DLL : saturated liquid \|\| 65 K to 105 K (-208.1 °C to -168.1 °C) MTE : saturated liquid \|\| 65 K to 105 K (-208.1 °C to -168.1 °C) TC : liquid \|\| 50 K to 144 K (-223.1 °C to -129.1 °C) TC : gas \|\| 80 K to 800 K (-193.1 °C to 526.9 °C) TC : vapor \|\| 50 K to 144 K (-223.1 °C to -129.1 °C) VP : liquid \|\| F₂ \|\| 57 K to 85 K (-216.1 °C to -188.1 °C) Vis : liquid \|\| 69 K to 84 K (-204.1 °C to -189.1 °C) ST : liquid \|\| 71 K to 85 K (-202.1 °C to -188.1 °C)
Neon	D : saturated liquid \|\| 25 K to 44 K (-248.6 °C to -228.7 °C) D : gas \|\| 27 K to 3000 K (-246.1 °C to 2726.8 °C) DLL : saturated liquid \|\| 25 K to 44 K (-248.6 °C to -228.7 °C) MTE : saturated liquid \|\| 25 K to 44 K (-248.6 °C to -228.7 °C) E : solid \|\| 8 K to 23 K (-265.1 °C to -250.1 °C) TC : solid \|\| 1 K to 24 K (-272.1 °C to -249.1 °C) TC : liquid \|\| 24 K to 44 K (-249.1 °C to -229.1 °C) TC : gas \|\| 27 K to 2500 K (-246.1 °C to 2226.8 °C) TC : vapor \|\| 27 K to 44 K (-246.1 °C to -229.1 °C) TD : liquid \|\| 25 K to 43 K (-248.1 °C to -230.1 °C) TD : gas \|\| 50 K to 3273 K (-223.1 °C to 3000 °C) SH : solid \|\| 11 K to 24 K (-262.1 °C to -249.4 °C) SH : saturated liquid \|\| 25 K to 43 K (-248.1 °C to -230.1 °C) SH : gas \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) HC : solid \|\| 11 K to 24 K (-262.1 °C to -249.4 °C) HC : saturated liquid \|\| 25 K to 43 K (-248.1 °C to -230.1 °C) HC : gas \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) VP : solid \|\| 14 K to 25 K (-259.3 °C to -248.6 °C) VP : liquid \|\| 25 K to 44 K (-248.6 °C to -229.1 °C) Vis : liquid \|\| 25 K to 44 K (-248.1 °C to -229 °C) Vis : gas \|\| 50 K to 3273 K (-223.1 °C to 3000 °C) ST : liquid \|\| 24 K to 28 K (-249.1 °C to -245.1 °C)
Sodium	D : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) DLL : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) MTE : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) E : solid \|\| 78 K to 300 K (-195.1 °C to 26.9 °C) G : solid \|\| 78 K to 300 K (-195.1 °C to 26.9 °C) v : solid \|\| 78 K to 300 K (-195.1 °C to 26.9 °C) K : solid \|\| 78 K to 300 K (-195.1 °C to 26.9 °C) TC : solid \|\| 0 K to 371 K (-273.1 °C to 97.9 °C) TD : solid \|\| 1 K to 300 K (-272.1 °C to 26.9 °C) SH : solid \|\| 0 K to 371 K (-273.1 °C to 97.9 °C) HC : solid \|\| 0 K to 371 K (-273.1 °C to 97.9 °C) RHO : solid \|\| 1 K to 371 K (-272.1 °C to 97.9 °C) SIGMA : solid \|\| 1 K to 371 K (-272.1 °C to 97.9 °C)
Magnesium	D : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) DLL : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) MTE : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) E : solid \|\| 0 K to 423 K (-273.1 °C to 150 °C) G : solid \|\| 0 K to 423 K (-273.1 °C to 150 °C) v : solid \|\| 0 K to 423 K (-273.1 °C to 150 °C) K : solid \|\| 0 K to 423 K (-273.1 °C to 150 °C) TC : solid \|\| annealed \|\| 0 K to 923 K (-273.1 °C to 650 °C) TD : solid \|\| annealed \|\| 1 K to 773 K (-272.1 °C to 500 °C) SH : solid \|\| 0 K to 923 K (-273.1 °C to 650 °C) HC : solid \|\| 0 K to 923 K (-273.1 °C to 650 °C) SSC : annealed \|\| tested at 78.1 °K (-195 °C), 2.8x10^-⁴/s, 180 micron grain size \|\| 0 to 0.14 mm/mm strain SSC : annealed \|\| tested at 4 °K (-269.1 °C), 2.8x10^-⁴/s, 180 micron grain size \|\| 0 to 0.47 mm/mm strain SSCC : annealed \|\| tested at 78.1 °K (-195 °C), 2.8x10^-⁴/s, 180 micron grain size \|\| 0 to 0.18 mm/mm strain SSCC : annealed \|\| tested at 4 °K (-269.1 °C), 2.8x10^-⁴/s, 180 micron grain size \|\| 0 to 0.174 mm/mm strain UTS : annealed \|\| 2.8x10^-⁴/s, 180 micron grain size \|\| 4 K to 298 K (-269.1 °C to 25 °C) YS : annealed \|\| 2.8x10^-⁴/s, 180 micron grain size \|\| 4 K to 298 K (-269.1 °C to 25 °C) UCS : annealed \|\| 2.8x10^-⁴/s, 180 micron grain size \|\| 4 K to 298 K (-269.1 °C to 25 °C) YSC : annealed \|\| 2.8x10^-⁴/s, 180 micron grain size \|\| 4 K to 298 K (-269.1 °C to 25 °C) %El : annealed, in tension \|\| 2.8x10^-⁴/s, 180 micron grain size \|\| 4 K to 298 K (-269.1 °C to 25 °C) %El : annealed, in compression \|\| 2.8x10^-⁴/s, 180 micron grain size \|\| 4 K to 298 K (-269.1 °C to 25 °C) FSN : in liquid helium \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 1.1x10⁴ cycles to 3x10⁶ cycles FSN : in liquid hydrogen \|\| tested at 4.2 °K (-268.9 °C), R = -1, axial, maximum stress \|\| 1.1x10⁴ cycles to 2x10⁶ cycles FSN : in liquid oxygen \|\| tested at 90 °K (-183.1 °C), R = -1, axial, maximum stress \|\| 2.4x10⁴ cycles to 2x10⁶ cycles RHO : solid \|\| 1 K to 923 K (-272.1 °C to 650 °C) SIGMA : solid \|\| 1 K to 923 K (-272.1 °C to 650 °C)
Aluminum	D : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) DLL : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) MTE : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) CTE : solid \|\| 10 K to 900 K (-263.1 °C to 626.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| bulk \|\| 0 K to 934 K (-273.1 °C to 660.4 °C) TD : solid \|\| bulk \|\| 20 K to 933 K (-253.1 °C to 660 °C) SH : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) HC : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) UTS : annealed \|\| 21 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) UTS : annealed \|\| 27 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) UTS : annealed \|\| 39 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) UTS : annealed \|\| 46 micron grain size \|\| 20 K to 873 K (-253.1 °C to 600 °C) UTS : annealed \|\| 65 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) UTS : annealed \|\| 105 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) UTS : annealed \|\| 118 micron grain size \|\| 20 K to 873 K (-253.1 °C to 600 °C) UTS : annealed \|\| 143 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) YS : annealed \|\| 21 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) YS : annealed \|\| 27 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) YS : annealed \|\| 39 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) YS : annealed \|\| 46 micron grain size \|\| 20 K to 873 K (-253.1 °C to 600 °C) YS : annealed \|\| 65 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) YS : annealed \|\| 105 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) YS : annealed \|\| 118 micron grain size \|\| 20 K to 873 K (-253.1 °C to 600 °C) YS : annealed \|\| 143 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) %El : annealed \|\| 21 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) %El : annealed \|\| 27 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) %El : annealed \|\| 39 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) %El : annealed \|\| 46 micron grain size \|\| 20 K to 873 K (-253.1 °C to 600 °C) %El : annealed \|\| 65 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) %El : annealed \|\| 105 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) %El : annealed \|\| 118 micron grain size \|\| 20 K to 873 K (-253.1 °C to 600 °C) %El : annealed \|\| 143 micron grain size \|\| 20 K to 400 K (-253.1 °C to 126.9 °C) HE : solid \|\| electropolished \|\| 175 K to 700 K (-98.1 °C to 426.9 °C) HE : solid \|\| grit blasted black anodized \|\| 175 K to 300 K (-98.1 °C to 26.9 °C) RHO : solid \|\| 1 K to 933 K (-272.1 °C to 660 °C) SIGMA : solid \|\| 1 K to 933 K (-272.1 °C to 660 °C)
Silicon	D : solid \|\| 0 K to 1000 K (-273.1 °C to 726.9 °C) DLL : solid \|\| 0 K to 1000 K (-273.1 °C to 726.9 °C) MTE : solid \|\| 0 K to 1000 K (-273.1 °C to 726.9 °C) CTE : solid \|\| 0 K to 1000 K (-273.1 °C to 726.9 °C) E : solid \|\| polycrystal \|\| 73 K to 923 K (-200.1 °C to 650 °C) E : solid \|\| <100> axis \|\| 73 K to 923 K (-200.1 °C to 650 °C) E : solid \|\| <111> axis \|\| 73 K to 923 K (-200.1 °C to 650 °C) G : solid \|\| polycrystal \|\| 73 K to 923 K (-200.1 °C to 650 °C) G : solid \|\| <100> axis \|\| 73 K to 923 K (-200.1 °C to 650 °C) G : solid \|\| <111> axis \|\| 73 K to 923 K (-200.1 °C to 650 °C) v : solid \|\| polycrystal \|\| 73 K to 923 K (-200.1 °C to 650 °C) v : solid \|\| <100> axis \|\| 73 K to 923 K (-200.1 °C to 650 °C) v : solid \|\| <111> axis \|\| 73 K to 923 K (-200.1 °C to 650 °C) K : solid \|\| polycrystal \|\| 73 K to 923 K (-200.1 °C to 650 °C) TC : bulk \|\| 0 K to 1685 K (-273.1 °C to 1411.8 °C) TC : nanowire \|\| 115 nm \|\| 25 K to 325 K (-248.1 °C to 51.9 °C) TC : nanowire \|\| 56 nm \|\| 25 K to 325 K (-248.1 °C to 51.9 °C) TC : nanowire \|\| 37 nm \|\| 25 K to 325 K (-248.1 °C to 51.9 °C) TC : nanowire \|\| 22 nm \|\| 25 K to 325 K (-248.1 °C to 51.9 °C) TC : nanocrystalline film \|\| PECVD, 495 nm thick film, 1x10²² B/cm³ to 2x10²² B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) TC : nanocrystalline film \|\| PECVD, 382 nm thick film, 3x10²¹ B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) TC : nanocrystalline film \|\| HWCVD, 594 nm thick film, no boron \|\| 85 K to 300 K (-188.1 °C to 27 °C) TD : solid \|\| bulk \|\| 1 K to 1000 K (-272.1 °C to 726.9 °C) SH : solid \|\| 1 K to 1685 K (-272.1 °C to 1411.8 °C) HC : solid \|\| 1 K to 1685 K (-272.1 °C to 1411.8 °C) RHO : solid \|\| ideally pure \|\| 79 K to 1073 K (-194.1 °C to 800 °C) RHO : solid \|\| 0.0005% B \|\| 83 K to 766 K (-190.1 °C to 492.9 °C) RHO : solid \|\| 0.001% B \|\| 83 K to 821 K (-190.1 °C to 547.9 °C) RHO : solid \|\| 0.002% B \|\| 83 K to 905 K (-190.1 °C to 631.9 °C) RHO : solid \|\| 0.005% B \|\| 83 K to 998 K (-190.1 °C to 725 °C) RHO : solid \|\| 0.01% B \|\| 83 K to 907 K (-190.1 °C to 633.9 °C) RHO : solid \|\| 0.1% B \|\| 83 K to 336 K (-190.1 °C to 62.9 °C) RHO : solid \|\| 1% B \|\| 83 K to 436 K (-190.1 °C to 162.9 °C) RHO : solid \|\| 0.001% P \|\| 83 K to 1000 K (-190.1 °C to 726.9 °C) RHO : solid \|\| 0.0057% P \|\| 83 K to 821 K (-190.1 °C to 547.9 °C) RHO : solid \|\| 0.1% P \|\| 83 K to 303 K (-190.1 °C to 30 °C) RHO : solid \|\| 1% P \|\| 83 K to 506 K (-190.1 °C to 232.9 °C) RHO : nanocrystalline film \|\| PECVD, 495 nm thick film, 1x10²² B/cm³ to 2x10²² B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) RHO : nanocrystalline film \|\| PECVD, 80 nm thick film, 3x10²¹ B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) RHO : nanocrystalline film \|\| HWCVD, 594 nm thick film, 1x10²¹ B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) RHO : nanocrystalline film \|\| HWCVD, 594 nm thick film, 3x10²⁰ B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) SIGMA : solid \|\| ideally pure \|\| 79 K to 1073 K (-194.1 °C to 800 °C) SIGMA : solid \|\| 0.0005% B \|\| 83 K to 766 K (-190.1 °C to 492.9 °C) SIGMA : solid \|\| 0.001% B \|\| 83 K to 821 K (-190.1 °C to 547.9 °C) SIGMA : solid \|\| 0.002% B \|\| 83 K to 905 K (-190.1 °C to 631.9 °C) SIGMA : solid \|\| 0.005% B \|\| 83 K to 998 K (-190.1 °C to 725 °C) SIGMA : solid \|\| 0.01% B \|\| 83 K to 907 K (-190.1 °C to 633.9 °C) SIGMA : solid \|\| 0.1% B \|\| 83 K to 336 K (-190.1 °C to 62.9 °C) SIGMA : solid \|\| 1% B \|\| 83 K to 436 K (-190.1 °C to 162.9 °C) SIGMA : solid \|\| 0.001% P \|\| 83 K to 1000 K (-190.1 °C to 726.9 °C) SIGMA : solid \|\| 0.0057% P \|\| 83 K to 821 K (-190.1 °C to 547.9 °C) SIGMA : solid \|\| 0.1% P \|\| 83 K to 303 K (-190.1 °C to 30 °C) SIGMA : solid \|\| 1% P \|\| 83 K to 506 K (-190.1 °C to 232.9 °C) SIGMA : nanocrystalline film \|\| PECVD, 495 nm thick film, 1x10²² B/cm³ to 2x10²² B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) SIGMA : nanocrystalline film \|\| PECVD, 80 nm thick film, 3x10²¹ B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) SIGMA : nanocrystalline film \|\| HWCVD, 594 nm thick film, 1x10²¹ B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) SIGMA : nanocrystalline film \|\| HWCVD, 594 nm thick film, 3x10²⁰ B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) RIW : measured in vacuum \|\| tested at 30 °K (-243.1 °C) RIW : measured in vacuum \|\| tested at 40 °K (-233.1 °C) RIW : measured in vacuum \|\| tested at 50 °K (-223.1 °C) RIW : measured in vacuum \|\| tested at 60 °K (-213.1 °C) RIW : measured in vacuum \|\| tested at 70 °K (-203.1 °C) RIW : measured in vacuum \|\| tested at 80 °K (-193.1 °C) RIW : measured in vacuum \|\| tested at 90 °K (-183.1 °C) RIW : measured in vacuum \|\| tested at 100 °K (-173 °C) RIW : measured in vacuum \|\| tested at 150 °K (-123 °C) RIW : measured in vacuum \|\| tested at 200 °K (-73 °C) RIT : measured in vacuum \|\| measured at 1100 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 1200 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 1300 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 1400 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 1500 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 2000 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 2500 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 3000 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 3500 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 4000 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 4500 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 5000 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 5500 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) S : nanocrystalline film \|\| PECVD, 495 nm thick film, 1x10²² B/cm³ to 2x10²² B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) S : nanocrystalline film \|\| PECVD, 80 nm thick film, 3x10²¹ B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) S : nanocrystalline film \|\| HWCVD, 594 nm thick film, 1x10²¹ B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C) S : nanocrystalline film \|\| HWCVD, 594 nm thick film, 3x10²⁰ B/cm³ \|\| 85 K to 300 K (-188.1 °C to 27 °C)
Sulfur	D : solid \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) DLL : orthorhombic \|\| a-axis \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) DLL : orthorhombic \|\| b-axis \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) DLL : orthorhombic \|\| c-axis \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) DLL : orthorhombic \|\| polycrystal \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) MTE : orthorhombic \|\| a-axis \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) MTE : orthorhombic \|\| b-axis \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) MTE : orthorhombic \|\| c-axis \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) MTE : orthorhombic \|\| polycrystal \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) CTE : orthorhombic \|\| a-axis \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) CTE : orthorhombic \|\| b-axis \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) CTE : orthorhombic \|\| c-axis \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) CTE : orthorhombic \|\| polycrystal \|\| 98 K to 297 K (-175.1 °C to 23.9 °C) TC : solid \|\| crystalline \|\| 0 K to 392 K (-273.1 °C to 118.9 °C) TC : solid \|\| amorphous \|\| 90 K to 350 K (-183.1 °C to 76.9 °C)
Chlorine	TC : liquid \|\| 172 K to 417 K (-101.1 °C to 143.9 °C) TC : vapor \|\| 200 K to 417 K (-73.1 °C to 143.9 °C) VP : solid \|\| Cl₂ \|\| 138 K to 172 K (-135.1 °C to -101.1 °C) VP : liquid \|\| Cl₂ \|\| 172 K to 238 K (-101.1 °C to -35 °C) ST : liquid \|\| 193 K to 243 K (-80.1 °C to -30 °C)
Argon	D : solid \|\| 4 K to 83 K (-269.1 °C to -190.1 °C) D : saturated liquid \|\| 84 K to 90 K (-189.1 °C to -183.1 °C) D : gas \|\| 87 K to 3000 K (-186.1 °C to 2726.8 °C) DLL : solid \|\| 4 K to 83 K (-269.1 °C to -190.1 °C) DLL : saturated liquid \|\| 84 K to 90 K (-189.1 °C to -183.1 °C) MTE : solid \|\| 4 K to 83 K (-269.1 °C to -190.1 °C) MTE : saturated liquid \|\| 84 K to 90 K (-189.1 °C to -183.1 °C) K : solid \|\| 4 K to 83 K (-269.1 °C to -190.1 °C) TC : solid \|\| 8 K to 80 K (-265.1 °C to -193.1 °C) TC : liquid \|\| 84 K to 151 K (-189.1 °C to -122.1 °C) TC : gas \|\| 88 K to 2500 K (-185.1 °C to 2226.8 °C) TC : vapor \|\| 85 K to 151 K (-188.1 °C to -122.1 °C) TD : solid \|\| 8 K to 80 K (-265.1 °C to -193.1 °C) TD : gas \|\| 50 K to 3273 K (-223.1 °C to 3000 °C) SH : solid \|\| 4 K to 83 K (-269.1 °C to -190.1 °C) SH : gas \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) HC : solid \|\| 4 K to 83 K (-269.1 °C to -190.1 °C) HC : gas \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) VP : solid \|\| 50 K to 80 K (-223.1 °C to -193.1 °C) VP : liquid \|\| 85 K to 150 K (-188.1 °C to -123.1 °C) Vis : saturated liquid \|\| 84 K to 149 K (-189.1 °C to -124.1 °C) Vis : gas \|\| 50 K to 3273 K (-223.1 °C to 3000 °C) ST : liquid \|\| 84 K to 92 K (-189.1 °C to -181.1 °C)
Potassium	E : solid \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) G : solid \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) v : solid \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) K : solid \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) TC : solid \|\| 0 K to 337 K (-273.1 °C to 63.9 °C) SH : solid \|\| 0 K to 337 K (-273.1 °C to 63.5 °C) HC : solid \|\| 0 K to 337 K (-273.1 °C to 63.5 °C) SSC : unknown strain rate \|\| tested at 7.5 °K (-265.6 °C) \|\| 0 to 0.26 mm/mm strain SSC : unknown strain rate \|\| tested at 16.5 °K (-256.6 °C) \|\| 0 to 0.22 mm/mm strain SSC : unknown strain rate \|\| tested at 21.7 °K (-251.4 °C) \|\| 0 to 0.22 mm/mm strain SSC : unknown strain rate \|\| tested at 12 °K (-261.1 °C) \|\| 0 to 0.26 mm/mm strain SSC : unknown strain rate \|\| tested at 40 °K (-233.1 °C) \|\| 0 to 0.22 mm/mm strain SSC : unknown strain rate \|\| tested at 30 °K (-243.1 °C) \|\| 0 to 0.3 mm/mm strain SSC : unknown strain rate \|\| tested at 77 °K (-196.1 °C) \|\| 0 to 0.22 mm/mm strain SSC : unknown strain rate \|\| tested at 195 °K (-78 °C) \|\| 0 to 0.26 mm/mm strain UTS : solid \|\| 5 K to 195 K (-268.1 °C to -78.1 °C) YS : solid \|\| 5 K to 195 K (-268.1 °C to -78.1 °C) %El : solid \|\| 5 K to 195 K (-268.1 °C to -78.1 °C) RHO : solid \|\| 1 K to 336 K (-272.1 °C to 62.9 °C) SIGMA : solid \|\| 1 K to 336 K (-272.1 °C to 62.9 °C)
Calcium	D : solid \|\| 77 K to 313 K (-196.1 °C to 40 °C) DLL : solid \|\| 77 K to 313 K (-196.1 °C to 40 °C) MTE : solid \|\| 77 K to 313 K (-196.1 °C to 40 °C) E : solid \|\| 93 K to 873 K (-180.1 °C to 600 °C) TC : solid \|\| 200 K to 1000 K (-73.1 °C to 726.9 °C) TD : solid \|\| 200 K to 313 K (-73.1 °C to 40 °C) SH : solid \|\| 0 K to 1115 K (-273.1 °C to 841.9 °C) HC : solid \|\| 0 K to 1115 K (-273.1 °C to 841.9 °C) RHO : solid \|\| 1 K to 1113 K (-272.1 °C to 840 °C) SIGMA : solid \|\| 1 K to 1113 K (-272.1 °C to 840 °C)
Scandium	TC : solid \|\| annealed \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) SH : solid \|\| 6 K to 1812 K (-267.1 °C to 1538.8 °C) HC : solid \|\| 6 K to 1812 K (-267.1 °C to 1538.8 °C)
Titanium	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 93 K to 1073 K (-180.1 °C to 800 °C) TC : solid \|\| annealed \|\| 0 K to 1950 K (-273.1 °C to 1676.8 °C) TD : solid \|\| 10 K to 1144 K (-263.1 °C to 870.9 °C) SH : solid \|\| 10 K to 1944 K (-263.1 °C to 1670.8 °C) HC : solid \|\| 10 K to 1944 K (-263.1 °C to 1670.8 °C) SSCC : annealed, 0.001/s \|\| tested at 77 °K (-196.1 °C) \|\| 0 to 0.35 mm/mm strain SSCC : annealed, 0.1/s \|\| tested at 77 °K (-196.1 °C) \|\| 0 to 0.35 mm/mm strain SSCC : annealed, 2200/s \|\| tested at 77 °K (-196.1 °C) \|\| 0 to 0.4 mm/mm strain YSC : bar \|\| 0.001/s strain rate \|\| 77 K to 773 K (-196.1 °C to 500 °C) YSC : bar \|\| 0.1/s strain rate \|\| 77 K to 776 K (-196.1 °C to 502.9 °C) YSC : bar \|\| 2200/s strain rate \|\| 77 K to 998 K (-196.1 °C to 725 °C) RHO : solid \|\| alpha, commercially pure \|\| 77 K to 1100 K (-196.1 °C to 826.9 °C) SIGMA : solid \|\| alpha, commercially pure \|\| 77 K to 1100 K (-196.1 °C to 826.9 °C)
Vanadium	D : solid \|\| 77 K to 1589 K (-196.1 °C to 1315.6 °C) DLL : solid \|\| 77 K to 1589 K (-196.1 °C to 1315.6 °C) MTE : solid \|\| 77 K to 1589 K (-196.1 °C to 1315.6 °C) E : annealed \|\| 4 K to 2100 K (-269.1 °C to 1826.8 °C) G : annealed \|\| 4 K to 1873 K (-269.1 °C to 1600 °C) v : annealed \|\| 4 K to 1873 K (-269.1 °C to 1600 °C) K : annealed \|\| 4 K to 1873 K (-269.1 °C to 1600 °C) TC : solid \|\| annealed \|\| 0 K to 2000 K (-273.1 °C to 1726.8 °C) TD : solid \|\| annealed \|\| 77 K to 1589 K (-196.1 °C to 1315.6 °C) SH : solid \|\| superconducting phase \|\| 1 K to 2190 K (-272.1 °C to 1916.8 °C) SH : solid \|\| non-superconducting phase \|\| 1 K to 2190 K (-272.1 °C to 1916.8 °C) HC : solid \|\| superconducting phase \|\| 1 K to 2190 K (-272.1 °C to 1916.8 °C) HC : solid \|\| non-superconducting phase \|\| 1 K to 2190 K (-272.1 °C to 1916.8 °C) SSCC : as-received \|\| tested at 77 °K (-196.1 °C), 2500/s \|\| 0 to 0.5 mm/mm strain SSCC : annealed \|\| tested at 77 °K (-196.1 °C), 2500/s \|\| 0 to 0.5 mm/mm strain RHO : solid \|\| 1 K to 2202 K (-272.1 °C to 1928.8 °C) SIGMA : solid \|\| 1 K to 2202 K (-272.1 °C to 1928.8 °C)
Chromium	D : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) DLL : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) MTE : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) TC : solid \|\| annealed \|\| 0 K to 2118 K (-273.1 °C to 1845 °C) TD : solid \|\| annealed \|\| 20 K to 1273 K (-253.1 °C to 1000 °C) SH : solid \|\| 20 K to 2130 K (-253.1 °C to 1856.8 °C) HC : solid \|\| 20 K to 2130 K (-253.1 °C to 1856.8 °C) HE : solid \|\| plated coating \|\| 100 K to 1000 K (-173.1 °C to 726.9 °C) RHO : solid \|\| 200 K to 1000 K (-73.1 °C to 726.9 °C) SIGMA : solid \|\| 200 K to 1000 K (-73.1 °C to 726.9 °C)
Manganese	D : solid \|\| 85 K to 1221 K (-188.1 °C to 947.9 °C) DLL : solid \|\| 85 K to 1221 K (-188.1 °C to 947.9 °C) MTE : solid \|\| 85 K to 1221 K (-188.1 °C to 947.9 °C) TC : solid \|\| annealed \|\| 2 K to 300 K (-271.1 °C to 26.9 °C) TD : solid \|\| 2 K to 300 K (-271.1 °C to 27 °C) SH : solid \|\| 1 K to 1517 K (-272.1 °C to 1243.8 °C) HC : solid \|\| 1 K to 1517 K (-272.1 °C to 1243.8 °C) RHO : solid \|\| 0 K to 700 K (-273.1 °C to 426.9 °C) SIGMA : solid \|\| 0 K to 700 K (-273.1 °C to 426.9 °C)
Iron	D : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) DLL : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) MTE : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) CTE : solid \|\| 91 K to 960 K (-182.1 °C to 686.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) TC : solid \|\| annealed \|\| 1 K to 1810 K (-272.1 °C to 1536.8 °C) TD : solid \|\| annealed \|\| 1 K to 960 K (-272.1 °C to 686.9 °C) SH : solid \|\| 1 K to 1809 K (-272.1 °C to 1535.8 °C) HC : solid \|\| 1 K to 1809 K (-272.1 °C to 1535.8 °C) YS : solid \|\| 2.5x10^-⁴/s strain rate \|\| 77 K to 973 K (-196.1 °C to 700 °C) NE : solid \|\| polished \|\| 200 K to 1093 K (-73.1 °C to 820 °C) RHO : solid \|\| annealed \|\| 100 K to 1500 K (-173.1 °C to 1226.8 °C) SIGMA : solid \|\| annealed \|\| 100 K to 1500 K (-173.1 °C to 1226.8 °C)
Cobalt	D : solid \|\| polycrystal \|\| 140 K to 1768 K (-133.1 °C to 1494.8 °C) DLL : solid \|\| polycrystal \|\| 140 K to 1768 K (-133.1 °C to 1494.8 °C) MTE : solid \|\| polycrystal \|\| 140 K to 1768 K (-133.1 °C to 1494.8 °C) CTE : solid \|\| polycrystal \|\| 140 K to 1768 K (-133.1 °C to 1494.8 °C) E : solid \|\| 4 K to 523 K (-269.1 °C to 250 °C) G : solid \|\| 4 K to 523 K (-269.1 °C to 250 °C) v : solid \|\| 4 K to 523 K (-269.1 °C to 250 °C) K : solid \|\| 4 K to 523 K (-269.1 °C to 250 °C) TC : solid \|\| annealed \|\| 0 K to 1767 K (-273.1 °C to 1493.8 °C) SH : solid \|\| 14 K to 690 K (-259.1 °C to 416.9 °C) HC : solid \|\| 14 K to 690 K (-259.1 °C to 416.9 °C)
Nickel	D : solid \|\| 0 K to 1173 K (-273.1 °C to 900 °C) DLL : solid \|\| 0 K to 1173 K (-273.1 °C to 900 °C) MTE : solid \|\| 0 K to 1173 K (-273.1 °C to 900 °C) CTE : solid \|\| 50 K to 800 K (-223.1 °C to 526.9 °C) E : solid \|\| 0 K to 1323 K (-273.1 °C to 1050 °C) TC : solid \|\| annealed \|\| 0 K to 1500 K (-273.1 °C to 1226.8 °C) TD : solid \|\| 2 K to 1173 K (-271.1 °C to 900 °C) SH : solid \|\| 1 K to 1728 K (-272.1 °C to 1455 °C) HC : solid \|\| 1 K to 1728 K (-272.1 °C to 1455 °C) UTS : solid \|\| annealed \|\| 77 K to 1089 K (-196.1 °C to 815.6 °C) YS : solid \|\| annealed \|\| 77 K to 1089 K (-196.1 °C to 815.6 °C) %El : solid \|\| annealed \|\| 77 K to 1089 K (-196.1 °C to 815.6 °C) FEN : hot finished \|\| tested at 4 °K (-269.1 °C), R = -1, axial, total strain range \|\| 190 cycles to 7x10⁴ cycles FEN : hot finished \|\| tested at 78 °K (-195.1 °C), R = -1, axial, total strain range \|\| 140 cycles to 2.73x10⁵ cycles NE : solid \|\| plated \|\| 22 K to 78 K (-251.1 °C to -195 °C) RHO : solid \|\| annealed \|\| 100 K to 1715 K (-173.1 °C to 1441.8 °C) SIGMA : solid \|\| annealed \|\| 100 K to 1715 K (-173.1 °C to 1441.8 °C)
Copper	D : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) DLL : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) MTE : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) CTE : solid \|\| 4 K to 800 K (-269.1 °C to 526.9 °C) E : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) G : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) v : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) K : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) TC : solid \|\| residual resistivity ratio of 30 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| residual resistivity ratio of 100 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| residual resistivity ratio of 300 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| residual resistivity ratio of 1000 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| residual resistivity ratio of 3000 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| 120 nm thin film \|\| 100 K to 475 K (-173.1 °C to 201.9 °C) TC : solid \|\| 181 nm thin film \|\| 100 K to 475 K (-173.1 °C to 201.9 °C) TC : solid \|\| 300 nm thin film \|\| 100 K to 475 K (-173.1 °C to 201.9 °C) TD : solid \|\| residual resistivity ratio of 30 \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) TD : solid \|\| residual resistivity ratio of 100 \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) TD : solid \|\| residual resistivity ratio of 300 \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) TD : solid \|\| residual resistivity ratio of 1000 \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) TD : solid \|\| residual resistivity ratio of 3000 \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) TD : solid \|\| 120 nm thin film \|\| 100 K to 475 K (-173.1 °C to 201.9 °C) TD : solid \|\| 181 nm thin film \|\| 100 K to 475 K (-173.1 °C to 201.9 °C) TD : solid \|\| 300 nm thin film \|\| 100 K to 475 K (-173.1 °C to 201.9 °C) SH : solid \|\| 1 K to 1300 K (-272.1 °C to 1026.8 °C) HC : solid \|\| 1 K to 1300 K (-272.1 °C to 1026.8 °C) UTS : annealed \|\| 10 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : annealed \|\| 20 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : annealed \|\| 30 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : annealed \|\| 40 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : annealed \|\| 50 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : annealed \|\| 65 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) YS : annealed \|\| 10 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) YS : annealed \|\| 20 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) YS : annealed \|\| 30 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) YS : annealed \|\| 40 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) YS : annealed \|\| 50 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) YS : annealed \|\| 65 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) RHO : solid \|\| residual resistivity ratio of 860 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) SIGMA : solid \|\| residual resistivity ratio of 860 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) S : solid \|\| 100 K to 1300 K (-173.1 °C to 1026.8 °C)
Zinc	D : solid \|\| 0 K to 890 K (-273.1 °C to 616.9 °C) DLL : solid \|\| polycrystal \|\| 0 K to 890 K (-273.1 °C to 616.9 °C) MTE : solid \|\| polycrystal \|\| 0 K to 890 K (-273.1 °C to 616.9 °C) E : solid \|\| 0 K to 650 K (-273.1 °C to 376.9 °C) G : solid \|\| 0 K to 650 K (-273.1 °C to 376.9 °C) v : solid \|\| 0 K to 650 K (-273.1 °C to 376.9 °C) K : solid \|\| 0 K to 650 K (-273.1 °C to 376.9 °C) TC : solid \|\| annealed \|\| 0 K to 693 K (-273.1 °C to 420 °C) TD : solid \|\| annealed \|\| 10 K to 693 K (-263.1 °C to 420 °C) SH : solid \|\| 1 K to 693 K (-272.1 °C to 420 °C) SH : gas \|\| 200 K to 6000 K (-73.1 °C to 5726.9 °C) HC : solid \|\| 1 K to 693 K (-272.1 °C to 420 °C) HC : gas \|\| 200 K to 6000 K (-73.1 °C to 5726.9 °C) RHO : solid \|\| 1 K to 693 K (-272.1 °C to 420 °C) SIGMA : solid \|\| 1 K to 693 K (-272.1 °C to 420 °C)
Gallium	TC : solid \|\| 0 K to 303 K (-273.1 °C to 30 °C)
Germanium	D : solid \|\| 40 K to 1085 K (-233.1 °C to 811.9 °C) DLL : solid \|\| 40 K to 1085 K (-233.1 °C to 811.9 °C) MTE : solid \|\| 40 K to 1085 K (-233.1 °C to 811.9 °C) CTE : solid \|\| 40 K to 300 K (-233.1 °C to 26.9 °C) E : solid \|\| polycrystal \|\| 73 K to 573 K (-200.1 °C to 300 °C) E : solid \|\| <111> axis \|\| 116 K to 560 K (-157.1 °C to 286.9 °C) E : solid \|\| <100> axis \|\| 116 K to 560 K (-157.1 °C to 286.9 °C) G : solid \|\| polycrystal \|\| 73 K to 573 K (-200.1 °C to 300 °C) v : solid \|\| polycrystal \|\| 73 K to 573 K (-200.1 °C to 300 °C) K : solid \|\| polycrystal \|\| 73 K to 573 K (-200.1 °C to 300 °C) TC : solid \|\| annealed \|\| 0 K to 1200 K (-273.1 °C to 926.9 °C) TD : solid \|\| annealed \|\| 100 K to 1085 K (-173.1 °C to 811.9 °C) SH : solid \|\| 100 K to 1211 K (-173.1 °C to 937.9 °C) HC : solid \|\| 100 K to 1211 K (-173.1 °C to 937.9 °C) RIW : measured in vacuum \|\| tested at 30 °K (-243.1 °C) RIW : measured in vacuum \|\| tested at 40 °K (-233.1 °C) RIW : measured in vacuum \|\| tested at 50 °K (-223.1 °C) RIW : measured in vacuum \|\| tested at 60 °K (-213.1 °C) RIW : measured in vacuum \|\| tested at 70 °K (-203.1 °C) RIW : measured in vacuum \|\| tested at 80 °K (-193.1 °C) RIW : measured in vacuum \|\| tested at 90 °K (-183.1 °C) RIW : measured in vacuum \|\| tested at 100 °K (-173 °C) RIW : measured in vacuum \|\| tested at 150 °K (-123 °C) RIW : measured in vacuum \|\| tested at 200 °K (-73 °C) RIT : measured in vacuum \|\| measured at 1800 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 2000 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 2500 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 3000 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 3500 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 4000 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 4500 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 5000 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C) RIT : measured in vacuum \|\| measured at 5500 nm \|\| 30 K to 295 K (-243.1 °C to 22 °C)
Arsenic	TC : solid \|\| 200 K to 500 K (-73.1 °C to 226.9 °C)
Selenium	D : trigonal \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) D : glassy, amorphous \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) DLL : trigonal \|\| polycrystal \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) DLL : trigonal \|\| a-axis \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) DLL : trigonal \|\| c-axis \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) DLL : glassy, amorphous \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) MTE : trigonal \|\| polycrystal \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) MTE : trigonal \|\| a-axis \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) MTE : trigonal \|\| c-axis \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) MTE : glassy, amorphous \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) CTE : trigonal \|\| polycrystal \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) CTE : trigonal \|\| a-axis \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) CTE : trigonal \|\| c-axis \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) CTE : glassy, amorphous \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) TC : trigonal \|\| polycrystal \|\| 40 K to 178 K (-233.1 °C to -95.1 °C) TC : trigonal \|\| a-axis \|\| 20 K to 178 K (-253.1 °C to -95.1 °C) TC : trigonal \|\| c-axis \|\| 20 K to 178 K (-253.1 °C to -95.1 °C) TC : glassy, amorphous \|\| 100 K to 300 K (-173.1 °C to 26.9 °C) TD : trigonal \|\| polycrystal \|\| 40 K to 178 K (-233.1 °C to -95.1 °C) TD : trigonal \|\| a-axis \|\| 40 K to 178 K (-233.1 °C to -95.1 °C) TD : trigonal \|\| c-axis \|\| 40 K to 178 K (-233.1 °C to -95.1 °C) TD : glassy, amorphous \|\| 155 K to 300 K (-118.1 °C to 26.9 °C) SH : solid \|\| trigonal \|\| 10 K to 494 K (-263.1 °C to 220.9 °C) SH : solid \|\| glassy, amorphous \|\| 0 K to 494 K (-273.1 °C to 220.9 °C) HC : solid \|\| trigonal \|\| 10 K to 494 K (-263.1 °C to 220.9 °C) HC : solid \|\| glassy, amorphous \|\| 0 K to 494 K (-273.1 °C to 220.9 °C)
Bromine	SH : solid \|\| Br₂ \|\| 1 K to 265 K (-272.1 °C to -8.1 °C) HC : solid \|\| Br₂ \|\| 1 K to 265 K (-272.1 °C to -8.1 °C)
Krypton	D : solid \|\| 4 K to 115 K (-269.1 °C to -158.1 °C) D : gas \|\| 120 K to 3000 K (-153.1 °C to 2726.8 °C) DLL : solid \|\| 4 K to 115 K (-269.1 °C to -158.1 °C) MTE : solid \|\| 4 K to 115 K (-269.1 °C to -158.1 °C) K : solid \|\| 4 K to 115 K (-269.1 °C to -158.1 °C) TC : solid \|\| 1 K to 116 K (-272.1 °C to -157.1 °C) TC : liquid \|\| 116 K to 210 K (-157.1 °C to -63.1 °C) TC : gas \|\| 120 K to 2000 K (-153.1 °C to 1726.8 °C) TC : vapor \|\| 120 K to 210 K (-153.1 °C to -63.1 °C) TD : solid \|\| 4 K to 115 K (-269.1 °C to -158.1 °C) TD : gas \|\| 50 K to 3273 K (-223.1 °C to 3000 °C) SH : solid \|\| 4 K to 115 K (-269.1 °C to -158.1 °C) SH : gas \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) HC : solid \|\| 4 K to 115 K (-269.1 °C to -158.1 °C) HC : gas \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) VP : solid \|\| 75 K to 115 K (-198.1 °C to -158.1 °C) VP : liquid \|\| 120 K to 205 K (-153.1 °C to -68.1 °C) Vis : gas \|\| 50 K to 3273 K (-223.1 °C to 3000 °C) ST : liquid \|\| 115 K to 124 K (-158.1 °C to -149.1 °C)
Rubidium	TC : solid \|\| 0 K to 312 K (-273.1 °C to 38.9 °C) SH : solid \|\| 0 K to 313 K (-273.1 °C to 39.4 °C) HC : solid \|\| 0 K to 313 K (-273.1 °C to 39.4 °C) RHO : solid \|\| 1 K to 313 K (-272.1 °C to 40 °C) SIGMA : solid \|\| 1 K to 313 K (-272.1 °C to 40 °C)
Strontium	TC : solid \|\| 150 K to 1000 K (-123.1 °C to 726.9 °C) SH : solid \|\| 0 K to 1041 K (-273.1 °C to 767.9 °C) HC : solid \|\| 0 K to 1041 K (-273.1 °C to 767.9 °C) RHO : solid \|\| 1 K to 1042 K (-272.1 °C to 768.9 °C) SIGMA : solid \|\| 1 K to 1042 K (-272.1 °C to 768.9 °C)
Yttrium	TC : solid \|\| annealed \|\| 0 K to 1100 K (-273.1 °C to 826.9 °C) YS : solid \|\| 0.23 H, annealed \|\| 78 K to 473 K (-195.1 °C to 200 °C) YS : solid \|\| 5.03 H, annealed \|\| 78 K to 473 K (-195.1 °C to 200 °C) YS : solid \|\| 11.7 H, annealed \|\| 200 K to 473 K (-73.1 °C to 200 °C)
Zirconium	D : solid \|\| 57 K to 1830 K (-216.1 °C to 1556.8 °C) DLL : solid \|\| 57 K to 1830 K (-216.1 °C to 1556.8 °C) MTE : solid \|\| 57 K to 1830 K (-216.1 °C to 1556.8 °C) TC : solid \|\| annealed \|\| 0 K to 2000 K (-273.1 °C to 1726.8 °C) TD : solid \|\| annealed \|\| 57 K to 1830 K (-216.1 °C to 1556.8 °C) SH : solid \|\| 20 K to 2125 K (-253.1 °C to 1851.8 °C) HC : solid \|\| 20 K to 2125 K (-253.1 °C to 1851.8 °C) SSC : annealed, 10 micron grains \|\| tested at 77 °K (-196.1 °C), 4.2x10^-⁴/s \|\| 0 to 0.16 mm/mm strain SSC : annealed, 47 micron grains \|\| tested at 77 °K (-196.1 °C), 4.2x10^-⁴/s \|\| 0 to 0.124 mm/mm strain UTS : annealed \|\| 83 K to 773 K (-190.1 °C to 500 °C) UTS : cold worked 50% \|\| 83 K to 300 K (-190.1 °C to 26.9 °C) %El : cold worked 50% \|\| 83 K to 300 K (-190.1 °C to 26.9 °C) RHO : solid \|\| high purity \|\| 1 K to 2127 K (-272.1 °C to 1853.8 °C) RHO : solid \|\| 0.33% O₂ \|\| 66 K to 1292 K (-207.1 °C to 1018.9 °C) SIGMA : solid \|\| high purity \|\| 1 K to 2127 K (-272.1 °C to 1853.8 °C) SIGMA : solid \|\| 0.33% O₂ \|\| 66 K to 1292 K (-207.1 °C to 1018.9 °C)
Niobium	D : solid \|\| 0 K to 2600 K (-273.1 °C to 2326.8 °C) DLL : solid \|\| 0 K to 2600 K (-273.1 °C to 2326.8 °C) MTE : solid \|\| 0 K to 2600 K (-273.1 °C to 2326.8 °C) E : solid \|\| polycrystal \|\| 123 K to 1950 K (-150.1 °C to 1676.8 °C) E : solid \|\| <100> axis \|\| 123 K to 923 K (-150.1 °C to 650 °C) E : solid \|\| <110> axis \|\| 123 K to 923 K (-150.1 °C to 650 °C) E : solid \|\| <111> axis \|\| 123 K to 923 K (-150.1 °C to 650 °C) G : solid \|\| polycrystal \|\| 123 K to 750 K (-150.1 °C to 476.9 °C) G : solid \|\| <100> axis \|\| 123 K to 923 K (-150.1 °C to 650 °C) G : solid \|\| <110> axis \|\| 123 K to 923 K (-150.1 °C to 650 °C) G : solid \|\| <111> axis \|\| 123 K to 923 K (-150.1 °C to 650 °C) v : solid \|\| polycrystal \|\| 123 K to 750 K (-150.1 °C to 476.9 °C) K : solid \|\| polycrystal \|\| 123 K to 750 K (-150.1 °C to 476.9 °C) TC : solid \|\| annealed \|\| 0 K to 2200 K (-273.1 °C to 1926.8 °C) TD : solid \|\| annealed \|\| 11 K to 2200 K (-262.1 °C to 1926.8 °C) SH : solid \|\| 11 K to 2700 K (-262.1 °C to 2426.8 °C) HC : solid \|\| 11 K to 2700 K (-262.1 °C to 2426.8 °C) SSC : electron beam melted, annealed, 0.001/s \|\| tested at 77 °K (-196.1 °C) \|\| 0 to 0.6 mm/mm strain SSC : electron beam melted, annealed, 0.001/s \|\| tested at 190 °K (-83 °C) \|\| 0 to 0.7 mm/mm strain SSC : electron beam melted, annealed, 3300/s \|\| tested at 77 °K (-196.1 °C) \|\| 0 to 0.6 mm/mm strain SSC : electron beam melted, annealed, 3300/s \|\| tested at 190 °K (-83 °C) \|\| 0 to 0.55 mm/mm strain UTS : effect of H and strain rate \|\| 1 ppm H, as-received, 8.33x10^-⁵/s \|\| 77 K to 298 K (-196.1 °C to 25 °C) UTS : effect of H and strain rate \|\| 1 ppm H, as-received, 0.00167/s \|\| 77 K to 298 K (-196.1 °C to 25 °C) UTS : effect of H and strain rate \|\| 1 ppm H, as-received, 0.1/s \|\| 77 K to 298 K (-196.1 °C to 25 °C) UTS : effect of H and strain rate \|\| 9 ppm H, annealed for 3 h at 673 °K (400 °C), 8.33x10^-⁵/s \|\| 77 K to 298 K (-196.1 °C to 25 °C) UTS : effect of H and strain rate \|\| 30 ppm H, annealed for 6 h at 673 °K (400 °C), 8.33x10^-⁵/s \|\| 77 K to 298 K (-196.1 °C to 25 °C) YS : solid \|\| 6x10^-⁴/s strain rate \|\| 77 K to 1473 K (-196.1 °C to 1200 °C) YS : solid \|\| 2.8/s strain rate \|\| 77 K to 298 K (-196.1 °C to 25 °C) YS : effect of H and strain rate \|\| 1 ppm H, as-received, 8.33x10^-⁵/s \|\| 123 K to 298 K (-150.1 °C to 25 °C) YS : effect of H and strain rate \|\| 1 ppm H, as-received, 0.1/s \|\| 77 K to 298 K (-196.1 °C to 25 °C) YS : effect of H and strain rate \|\| 9 ppm H, annealed for 3 h at 673 °K (400 °C), 8.33x10^-⁵/s \|\| 77 K to 298 K (-196.1 °C to 25 °C) YS : effect of H and strain rate \|\| 30 ppm H, annealed for 6 h at 673 °K (400 °C), 8.33x10^-⁵/s \|\| 77 K to 298 K (-196.1 °C to 25 °C) YSC : solid \|\| 3300/s strain rate \|\| 77 K to 800 K (-196.1 °C to 526.9 °C) %El : effect of H and strain rate \|\| 1 ppm H, as-received, 8.33x10^-⁵/s \|\| 77 K to 298 K (-196.1 °C to 25 °C) %El : effect of H and strain rate \|\| 1 ppm H, as-received, 0.00167/s \|\| 77 K to 298 K (-196.1 °C to 25 °C) %El : effect of H and strain rate \|\| 1 ppm H, as-received, 0.1/s \|\| 77 K to 298 K (-196.1 °C to 25 °C) %El : effect of H and strain rate \|\| 9 ppm H, annealed for 3 h at 673 °K (400 °C), 8.33x10^-⁵/s \|\| 77 K to 298 K (-196.1 °C to 25 °C) %El : effect of H and strain rate \|\| 30 ppm H, annealed for 6 h at 673 °K (400 °C), 8.33x10^-⁵/s \|\| 123 K to 298 K (-150.1 °C to 25 °C) RHO : solid \|\| annealed \|\| 12 K to 2700 K (-261.1 °C to 2426.8 °C) SIGMA : solid \|\| annealed \|\| 12 K to 2700 K (-261.1 °C to 2426.8 °C)
Molybdenum	D : solid \|\| 0 K to 2500 K (-273.1 °C to 2226.8 °C) DLL : solid \|\| 0 K to 2500 K (-273.1 °C to 2226.8 °C) MTE : solid \|\| 0 K to 2500 K (-273.1 °C to 2226.8 °C) E : solid \|\| polycrystal \|\| 93 K to 2273 K (-180.1 °C to 2000 °C) E : solid \|\| [100] \|\| 73 K to 973 K (-200.1 °C to 700 °C) E : solid \|\| [111] \|\| 73 K to 973 K (-200.1 °C to 700 °C) E : solid \|\| [110] \|\| 73 K to 973 K (-200.1 °C to 700 °C) TC : solid \|\| annealed \|\| 0 K to 2800 K (-273.1 °C to 2526.8 °C) TD : solid \|\| annealed \|\| 200 K to 2500 K (-73.1 °C to 2226.8 °C) SH : solid \|\| 0 K to 2897 K (-272.8 °C to 2623.8 °C) HC : solid \|\| 0 K to 2897 K (-272.8 °C to 2623.8 °C) SSCC : annealed, 0.001/s \|\| tested at 77 °K (-196.1 °C) \|\| 0 to 0.2 mm/mm strain YS : arc-cast \|\| forgings, annealed 2 h at 1673 °K (1400 °C) \|\| 183 K to 313 K (-90.1 °C to 40 °C) YSC : powder metallurgy \|\| recrystallized bar \|\| 70 K to 683 K (-203.1 °C to 410 °C) RHO : solid \|\| 1 K to 2894 K (-272.1 °C to 2620.8 °C) SIGMA : solid \|\| 1 K to 2894 K (-272.1 °C to 2620.8 °C)
Ruthenium	E : solid \|\| 4 K to 923 K (-269.1 °C to 650 °C) G : solid \|\| 4 K to 923 K (-269.1 °C to 650 °C) v : solid \|\| 4 K to 923 K (-269.1 °C to 650 °C) K : solid \|\| 4 K to 923 K (-269.1 °C to 650 °C) TC : solid \|\| annealed \|\| 0 K to 2500 K (-273.1 °C to 2226.8 °C) SH : solid \|\| 0 K to 2607 K (-273.1 °C to 2333.8 °C) HC : solid \|\| 0 K to 2607 K (-273.1 °C to 2333.8 °C)
Rhodium	D : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) DLL : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) MTE : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) E : solid \|\| 93 K to 1173 K (-180.1 °C to 900 °C) TC : solid \|\| annealed \|\| 0 K to 2000 K (-273.1 °C to 1726.8 °C) TD : solid \|\| annealed \|\| 1 K to 773 K (-272.1 °C to 500 °C) SH : solid \|\| 0 K to 2237 K (-273.1 °C to 1963.8 °C) HC : solid \|\| 0 K to 2237 K (-273.1 °C to 1963.8 °C) RHO : solid \|\| 20 K to 2236 K (-253.1 °C to 1962.8 °C) SIGMA : solid \|\| 20 K to 2236 K (-253.1 °C to 1962.8 °C)
Palladium	D : solid \|\| 0 K to 1828 K (-273.1 °C to 1555 °C) DLL : solid \|\| 0 K to 1828 K (-273.1 °C to 1555 °C) MTE : solid \|\| 0 K to 1828 K (-273.1 °C to 1555 °C) CTE : solid \|\| 30 K to 300 K (-243.1 °C to 26.9 °C) E : solid \|\| 30 K to 1200 K (-243.1 °C to 926.9 °C) TC : solid \|\| annealed \|\| 0 K to 1800 K (-273.1 °C to 1526.8 °C) TD : solid \|\| annealed \|\| 1 K to 1800 K (-272.1 °C to 1526.8 °C) SH : solid \|\| 0 K to 1827 K (-273.1 °C to 1553.8 °C) HC : solid \|\| 0 K to 1827 K (-273.1 °C to 1553.8 °C) RHO : solid \|\| 1 K to 1827 K (-272.1 °C to 1553.8 °C) SIGMA : solid \|\| 1 K to 1827 K (-272.1 °C to 1553.8 °C) S : solid \|\| 100 K to 2000 K (-173.1 °C to 1726.8 °C)
Silver	D : solid \|\| 0 K to 873 K (-273.1 °C to 600 °C) DLL : solid \|\| 0 K to 873 K (-273.1 °C to 600 °C) MTE : solid \|\| 0 K to 873 K (-273.1 °C to 600 °C) CTE : solid \|\| 30 K to 300 K (-243.1 °C to 26.9 °C) E : solid \|\| 0 K to 1173 K (-273.1 °C to 900 °C) G : solid \|\| 0 K to 1173 K (-273.1 °C to 900 °C) v : solid \|\| 0 K to 1173 K (-273.1 °C to 900 °C) K : solid \|\| 0 K to 1173 K (-273.1 °C to 900 °C) TC : solid \|\| annealed \|\| 0 K to 1235 K (-273.1 °C to 961.9 °C) TC : solid \|\| nanowire \|\| 36 K to 293 K (-237.1 °C to 19.9 °C) TD : solid \|\| bulk, annealed \|\| 1 K to 873 K (-272.1 °C to 600 °C) TD : solid \|\| nanowire \|\| 36 K to 293 K (-237.1 °C to 19.9 °C) SH : solid \|\| 1 K to 1235 K (-272.1 °C to 961.9 °C) HC : solid \|\| 1 K to 1235 K (-272.1 °C to 961.9 °C) SSC : annealed at 973 °K (700 °C) \|\| tested at 20 °K (-253.1 °C), 6.67x10^-⁴/s \|\| 0 to 0.51 mm/mm strain SSC : annealed at 973 °K (700 °C) \|\| tested at 78 °K (-195.1 °C), 6.67x10^-⁴/s \|\| 0 to 0.46 mm/mm strain SSC : annealed at 973 °K (700 °C) \|\| tested at 195 °K (-78 °C), 6.67x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : annealed at 1073 °K (800 °C) \|\| tested at 20 °K (-253.1 °C), 6.67x10^-⁴/s \|\| 0 to 0.41 mm/mm strain SSC : annealed at 1073 °K (800 °C) \|\| tested at 77 °K (-196.1 °C), 6.67x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1073 °K (800 °C) \|\| tested at 195 °K (-78 °C), 6.67x10^-⁴/s \|\| 0 to 0.24 mm/mm strain SSC : annealed at 1173 °K (900 °C) \|\| tested at 20 °K (-253.1 °C), 6.67x10^-⁴/s \|\| 0 to 0.275 mm/mm strain SSC : annealed at 1173 °K (900 °C) \|\| tested at 77 °K (-196.1 °C), 6.67x10^-⁴/s \|\| 0 to 0.28 mm/mm strain SSC : annealed at 1173 °K (900 °C) \|\| tested at 195 °K (-78 °C), 6.67x10^-⁴/s \|\| 0 to 0.11 mm/mm strain UTS : annealing temperature \|\| annealed at 973 °K (700 °C) \|\| 20 K to 1150 K (-253.1 °C to 876.9 °C) UTS : annealing temperature \|\| annealed at 1073 °K (800 °C) \|\| 20 K to 1150 K (-253.1 °C to 876.9 °C) UTS : annealing temperature \|\| annealed at 1173 °K (900 °C) \|\| 20 K to 1150 K (-253.1 °C to 876.9 °C) YS : annealing temperature \|\| annealed at 973 °K (700 °C) \|\| 0 K to 900 K (-273.1 °C to 626.9 °C) YS : annealing temperature \|\| annealed at 1073 °K (800 °C) \|\| 0 K to 900 K (-273.1 °C to 626.9 °C) YS : annealing temperature \|\| annealed at 1173 °K (900 °C) \|\| 0 K to 1150 K (-273.1 °C to 876.9 °C) RHO : solid \|\| bulk \|\| 1 K to 1235 K (-272.1 °C to 961.9 °C) RHO : solid \|\| nanowire \|\| 10 K to 293 K (-263.1 °C to 19.9 °C) SIGMA : solid \|\| bulk \|\| 1 K to 1235 K (-272.1 °C to 961.9 °C) SIGMA : solid \|\| nanowire \|\| 10 K to 293 K (-263.1 °C to 19.9 °C) S : solid \|\| 100 K to 1200 K (-173.1 °C to 926.9 °C)
Cadmium	D : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) DLL : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) MTE : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) E : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) G : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) v : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) K : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) TC : solid \|\| 0 K to 594 K (-273.1 °C to 320.9 °C) TD : solid \|\| 10 K to 594 K (-263.1 °C to 320.9 °C) SH : solid \|\| 1 K to 594 K (-272.1 °C to 320.9 °C) HC : solid \|\| 1 K to 594 K (-272.1 °C to 320.9 °C) UTS : 0.508 mm (0.02 inch) grain size \|\| 4 K to 297 K (-269.1 °C to 23.9 °C) YS : 0.508 mm (0.02 inch) grain size \|\| 4 K to 297 K (-269.1 °C to 23.9 °C)
Indium	D : solid \|\| 0 K to 379 K (-273.1 °C to 105.9 °C) DLL : solid \|\| 0 K to 379 K (-273.1 °C to 105.9 °C) MTE : solid \|\| 0 K to 379 K (-273.1 °C to 105.9 °C) CTE : solid \|\| 60 K to 379 K (-213.1 °C to 105.9 °C) E : solid \|\| 0 K to 423 K (-273.1 °C to 150 °C) G : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) v : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) K : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) TC : solid \|\| annealed \|\| 0 K to 430 K (-273.1 °C to 156.9 °C) TD : solid \|\| 73 K to 379 K (-200.1 °C to 105.9 °C) SH : solid \|\| 4 K to 430 K (-269.1 °C to 156.9 °C) HC : solid \|\| 4 K to 430 K (-269.1 °C to 156.9 °C) UTS : solid \|\| 4 K to 300 K (-269.1 °C to 26.9 °C)
Tin (UNS L13008)	E : solid \|\| 143 K to 423 K (-130.1 °C to 150 °C) G : solid \|\| 143 K to 423 K (-130.1 °C to 150 °C) v : solid \|\| 143 K to 423 K (-130.1 °C to 150 °C) K : solid \|\| 143 K to 423 K (-130.1 °C to 150 °C) TC : solid \|\| annealed \|\| 0 K to 505 K (-273.1 °C to 231.9 °C) SH : solid \|\| 10 K to 505 K (-263.1 °C to 231.9 °C) HC : solid \|\| 10 K to 505 K (-263.1 °C to 231.9 °C) RHO : solid \|\| 175 K to 504 K (-98.1 °C to 230.9 °C) SIGMA : solid \|\| 175 K to 504 K (-98.1 °C to 230.9 °C)
Antimony (UNS M00998)	D : solid \|\| 0 K to 823 K (-273.1 °C to 550 °C) DLL : solid \|\| 0 K to 823 K (-273.1 °C to 550 °C) MTE : solid \|\| 0 K to 823 K (-273.1 °C to 550 °C) E : solid \|\| 93 K to 898 K (-180.1 °C to 625 °C) TC : solid \|\| annealed \|\| 0 K to 904 K (-273.1 °C to 630.9 °C)
Tellurium	TC : solid \|\| polycrystal \|\| 20 K to 178 K (-253.1 °C to -95.1 °C) TC : solid \|\| a-axis \|\| 20 K to 178 K (-253.1 °C to -95.1 °C) TC : solid \|\| c-axis \|\| 20 K to 178 K (-253.1 °C to -95.1 °C)
Iodine	VP : solid \|\| 177 K to 387 K (-96.1 °C to 113.9 °C)
Xenon	D : solid \|\| 0 K to 160 K (-273.1 °C to -113.1 °C) D : gas \|\| 165 K to 3000 K (-108.1 °C to 2726.8 °C) DLL : solid \|\| 0 K to 160 K (-273.1 °C to -113.1 °C) MTE : solid \|\| 0 K to 160 K (-273.1 °C to -113.1 °C) K : solid \|\| 0 K to 160 K (-273.1 °C to -113.1 °C) TC : solid \|\| 50 K to 160 K (-223.1 °C to -113.1 °C) TC : liquid \|\| 161 K to 290 K (-112.1 °C to 16.9 °C) TC : gas \|\| 165 K to 1500 K (-108.1 °C to 1226.8 °C) TC : vapor \|\| 165 K to 290 K (-108.1 °C to 16.9 °C) TD : gas \|\| 50 K to 3273 K (-223.1 °C to 3000 °C) SH : gas \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) HC : gas \|\| 100 K to 20000 K (-173.1 °C to 19726.8 °C) VP : solid \|\| 100 K to 155 K (-173.1 °C to -118.1 °C) VP : liquid \|\| 160 K to 280 K (-113.1 °C to 6.9 °C) Vis : gas \|\| 50 K to 3273 K (-223.1 °C to 3000 °C) ST : liquid \|\| 165 K to 285 K (-108.1 °C to 11.9 °C)
Caesium	TC : solid \|\| 0 K to 302 K (-273.1 °C to 28.9 °C) SH : solid \|\| 0 K to 302 K (-273.1 °C to 28.5 °C) HC : solid \|\| 0 K to 302 K (-273.1 °C to 28.5 °C) RHO : solid \|\| 1 K to 302 K (-272.1 °C to 28.9 °C) SIGMA : solid \|\| 1 K to 302 K (-272.1 °C to 28.9 °C)
Barium	E : solid \|\| 93 K to 723 K (-180.1 °C to 450 °C) SH : solid \|\| 0 K to 1000 K (-273.1 °C to 726.9 °C) HC : solid \|\| 0 K to 1000 K (-273.1 °C to 726.9 °C) RHO : solid \|\| 1 K to 1002 K (-272.1 °C to 728.9 °C) SIGMA : solid \|\| 1 K to 1002 K (-272.1 °C to 728.9 °C)
Lanthanum	E : solid \|\| 93 K to 723 K (-180.1 °C to 450 °C) TC : solid \|\| annealed \|\| 0 K to 1100 K (-273.1 °C to 826.9 °C) RHO : solid \|\| 25 K to 333 K (-248.1 °C to 60 °C) SIGMA : solid \|\| 25 K to 333 K (-248.1 °C to 60 °C)
Cerium	TC : solid \|\| 0 K to 1000 K (-273.1 °C to 726.9 °C)
Praseodymium	E : solid \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) G : solid \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) v : solid \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) K : solid \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) TC : solid \|\| annealed \|\| 80 K to 1000 K (-193.1 °C to 726.9 °C)
Neodymium	TC : solid \|\| 200 K to 1135 K (-73.1 °C to 861.9 °C) RHO : solid \|\| 25 K to 360 K (-248.1 °C to 86.9 °C) SIGMA : solid \|\| 25 K to 360 K (-248.1 °C to 86.9 °C)
Samarium	TC : solid \|\| annealed \|\| 0 K to 600 K (-273.1 °C to 326.9 °C)
Europium	E : solid \|\| 100 K to 400 K (-173.1 °C to 126.9 °C) TC : solid \|\| annealed \|\| 123 K to 300 K (-150.1 °C to 26.9 °C)
Gadolinium	TC : solid \|\| annealed \|\| 0 K to 310 K (-273.1 °C to 36.9 °C) RHO : solid \|\| 25 K to 444 K (-248.1 °C to 170.9 °C) SIGMA : solid \|\| 25 K to 444 K (-248.1 °C to 170.9 °C)
Terbium	TC : solid \|\| annealed \|\| 0 K to 300 K (-273.1 °C to 26.9 °C)
Dysprosium	TC : solid \|\| annealed \|\| 0 K to 1500 K (-273.1 °C to 1226.8 °C) RHO : solid \|\| 10 K to 350 K (-263.1 °C to 76.9 °C) SIGMA : solid \|\| 10 K to 350 K (-263.1 °C to 76.9 °C)
Holmium	TC : solid \|\| annealed \|\| 0 K to 500 K (-273.1 °C to 226.9 °C)
Erbium	E : solid \|\| 81 K to 298 K (-192.1 °C to 25 °C) G : solid \|\| 81 K to 298 K (-192.1 °C to 25 °C) v : solid \|\| 81 K to 298 K (-192.1 °C to 25 °C) K : solid \|\| 81 K to 298 K (-192.1 °C to 25 °C) TC : solid \|\| annealed \|\| 0 K to 1500 K (-273.1 °C to 1226.8 °C) RHO : solid \|\| 10 K to 350 K (-263.1 °C to 76.9 °C) SIGMA : solid \|\| 10 K to 350 K (-263.1 °C to 76.9 °C)
Thulium	TC : solid \|\| annealed \|\| 0 K to 300 K (-273.1 °C to 26.9 °C)
Ytterbium	TC : solid \|\| 123 K to 500 K (-150.1 °C to 226.9 °C)
Lutetium	TC : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) SH : solid \|\| 6 K to 1936 K (-267.1 °C to 1662.8 °C) HC : solid \|\| 6 K to 1936 K (-267.1 °C to 1662.8 °C) SSC : 0.48 at% H, annealed \|\| tested at 78 °K (-195.1 °C), 3.3x10^-⁵/s \|\| 0 to 0.1 mm/mm strain SSC : 7.1 at% H, annealed \|\| tested at 78 °K (-195.1 °C), 3.3x10^-⁵/s \|\| 0 to 0.7 mm/mm strain YS : annealed \|\| 0.48 at% H \|\| 78 K to 473 K (-195.1 °C to 200 °C) YS : annealed \|\| 12.8 at% H \|\| 200 K to 473 K (-73.1 °C to 200 °C) YS : annealed \|\| 7.1 at% H \|\| 78 K to 473 K (-195.1 °C to 200 °C)
Hafnium	TC : solid \|\| annealed \|\| 0 K to 2000 K (-273.1 °C to 1726.8 °C) SH : solid \|\| 10 K to 2470 K (-263.1 °C to 2196.8 °C) HC : solid \|\| 10 K to 2470 K (-263.1 °C to 2196.8 °C) RHO : solid \|\| 1 K to 2015 K (-272.1 °C to 1741.8 °C) SIGMA : solid \|\| 1 K to 2015 K (-272.1 °C to 1741.8 °C)
Tantalum	D : solid \|\| 90 K to 2800 K (-183.1 °C to 2526.8 °C) DLL : solid \|\| 90 K to 2800 K (-183.1 °C to 2526.8 °C) E : solid \|\| 0 K to 2673 K (-273.1 °C to 2400 °C) TC : solid \|\| annealed \|\| 0 K to 3200 K (-273.1 °C to 2926.8 °C) TD : solid \|\| calculated \|\| 90 K to 2800 K (-183.1 °C to 2526.8 °C) SH : solid \|\| 10 K to 3258 K (-263.1 °C to 2985 °C) HC : solid \|\| 10 K to 3258 K (-263.1 °C to 2985 °C) FSN : wire annealed at 1672 °K (1399 °C) \|\| tested at 200 °K (-73 °C), R = -1, maximum stress \|\| 4x10⁴ cycles to 1x10⁷ cycles NE : solid \|\| polished, Wood \|\| 65 K to 1570 K (-208.1 °C to 1296.8 °C) RHO : solid \|\| 4 K to 3258 K (-269.1 °C to 2985 °C) SIGMA : solid \|\| 4 K to 3258 K (-269.1 °C to 2985 °C)
Tungsten	D : solid \|\| 0 K to 3400 K (-273.1 °C to 3126.8 °C) DLL : solid \|\| 0 K to 3400 K (-273.1 °C to 3126.8 °C) MTE : solid \|\| 0 K to 3400 K (-273.1 °C to 3126.8 °C) E : solid \|\| 93 K to 2673 K (-180.1 °C to 2400 °C) TC : solid \|\| Ho et. al. \|\| 0 K to 3660 K (-273.1 °C to 3386.8 °C) TD : solid \|\| 1 K to 3400 K (-272.1 °C to 3126.8 °C) SH : solid \|\| 1 K to 3600 K (-272.1 °C to 3326.8 °C) HC : solid \|\| 1 K to 3600 K (-272.1 °C to 3326.8 °C) RHO : solid \|\| pure \|\| 0 K to 3660 K (-273.1 °C to 3386.8 °C) SIGMA : solid \|\| pure \|\| 0 K to 3660 K (-273.1 °C to 3386.8 °C)
Rhenium	E : solid \|\| 4 K to 1173 K (-269.1 °C to 900 °C) G : solid \|\| 4 K to 923 K (-269.1 °C to 650 °C) v : solid \|\| 4 K to 923 K (-269.1 °C to 650 °C) K : solid \|\| 4 K to 923 K (-269.1 °C to 650 °C) TC : solid \|\| annealed \|\| 0 K to 2600 K (-273.1 °C to 2326.8 °C) %El : solid \|\| 15% worked \|\| 0 K to 2673 K (-273.1 °C to 2400 °C) RHO : solid \|\| annealed \|\| 200 K to 2600 K (-73.1 °C to 2326.8 °C) SIGMA : solid \|\| annealed \|\| 200 K to 2600 K (-73.1 °C to 2326.8 °C)
Osmium	D : solid \|\| 0 K to 1300 K (-273.1 °C to 1026.8 °C) DLL : solid \|\| polycrystal \|\| 0 K to 1300 K (-273.1 °C to 1026.8 °C) DLL : solid \|\| a-axis \|\| 0 K to 1300 K (-273.1 °C to 1026.8 °C) DLL : solid \|\| c-axis \|\| 0 K to 1300 K (-273.1 °C to 1026.8 °C) MTE : solid \|\| polycrystal \|\| 0 K to 1300 K (-273.1 °C to 1026.8 °C) MTE : solid \|\| a-axis \|\| 0 K to 1300 K (-273.1 °C to 1026.8 °C) MTE : solid \|\| c-axis \|\| 0 K to 1300 K (-273.1 °C to 1026.8 °C) CTE : solid \|\| polycrystal \|\| 0 K to 1300 K (-273.1 °C to 1026.8 °C) CTE : solid \|\| a-axis \|\| 0 K to 1300 K (-273.1 °C to 1026.8 °C) CTE : solid \|\| c-axis \|\| 0 K to 1300 K (-273.1 °C to 1026.8 °C) TC : solid \|\| annealed \|\| 0 K to 1673 K (-273.1 °C to 1400 °C)
Iridium	D : solid \|\| 0 K to 2719 K (-273.1 °C to 2445.8 °C) DLL : solid \|\| 0 K to 2719 K (-273.1 °C to 2445.8 °C) MTE : solid \|\| 0 K to 2719 K (-273.1 °C to 2445.8 °C) E : solid \|\| 93 K to 1273 K (-180.1 °C to 1000 °C) TC : solid \|\| annealed \|\| 0 K to 1500 K (-273.1 °C to 1226.8 °C) TD : solid \|\| annealed \|\| 1 K to 1500 K (-272.1 °C to 1226.8 °C) SH : solid \|\| 0 K to 2000 K (-273.1 °C to 1726.8 °C) HC : solid \|\| 0 K to 2000 K (-273.1 °C to 1726.8 °C)
Platinum	D : solid \|\| 0 K to 1973 K (-273.1 °C to 1700 °C) DLL : solid \|\| 0 K to 1973 K (-273.1 °C to 1700 °C) MTE : solid \|\| 0 K to 1973 K (-273.1 °C to 1700 °C) E : solid \|\| 93 K to 1478 K (-180.1 °C to 1204.5 °C) TC : solid \|\| annealed \|\| 0 K to 2045 K (-273.1 °C to 1771.8 °C) TD : solid \|\| annealed \|\| 1 K to 1973 K (-272.1 °C to 1700 °C) SH : solid \|\| 0 K to 2000 K (-273.1 °C to 1726.8 °C) HC : solid \|\| 0 K to 2000 K (-273.1 °C to 1726.8 °C) RHO : solid \|\| 14 K to 2000 K (-259.1 °C to 1726.8 °C) SIGMA : solid \|\| 14 K to 2000 K (-259.1 °C to 1726.8 °C) S : solid \|\| 100 K to 2000 K (-173.1 °C to 1726.8 °C)
Gold	D : solid \|\| 0 K to 1003 K (-273.1 °C to 730 °C) DLL : solid \|\| 0 K to 1003 K (-273.1 °C to 730 °C) MTE : solid \|\| 0 K to 1003 K (-273.1 °C to 730 °C) CTE : solid \|\| 86 K to 1003 K (-187.1 °C to 730 °C) E : solid \|\| 0 K to 1280 K (-273.1 °C to 1006.9 °C) TC : solid \|\| annealed \|\| 0 K to 1338 K (-273.1 °C to 1065 °C) SH : solid \|\| 1 K to 1338 K (-272.1 °C to 1065 °C) HC : solid \|\| 1 K to 1338 K (-272.1 °C to 1065 °C) RHO : solid \|\| 1 K to 1338 K (-272.1 °C to 1065 °C) SIGMA : solid \|\| 1 K to 1338 K (-272.1 °C to 1065 °C) S : solid \|\| 100 K to 1300 K (-173.1 °C to 1026.8 °C)
Mercury	D : solid \|\| 0 K to 234 K (-273.1 °C to -39.1 °C) DLL : solid \|\| 0 K to 234 K (-273.1 °C to -39.1 °C) MTE : solid \|\| 0 K to 234 K (-273.1 °C to -39.1 °C) CTE : solid \|\| 0 K to 234 K (-273.1 °C to -39.1 °C) TC : solid \|\| 0 K to 234 K (-273.1 °C to -39.1 °C) TD : solid \|\| 5 K to 234 K (-268.1 °C to -39.1 °C) SH : solid \|\| 5 K to 234 K (-268.1 °C to -39.1 °C) HC : solid \|\| 5 K to 234 K (-268.1 °C to -39.1 °C)
Thallium	E : solid \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) G : solid \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) v : solid \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) K : solid \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) TC : solid \|\| annealed \|\| 0 K to 500 K (-273.1 °C to 226.9 °C)
Lead	D : solid \|\| 0 K to 593 K (-273.1 °C to 320 °C) DLL : solid \|\| 0 K to 593 K (-273.1 °C to 320 °C) MTE : solid \|\| 0 K to 593 K (-273.1 °C to 320 °C) E : solid \|\| 143 K to 423 K (-130.1 °C to 150 °C) G : solid \|\| 143 K to 423 K (-130.1 °C to 150 °C) v : solid \|\| 143 K to 423 K (-130.1 °C to 150 °C) K : solid \|\| 143 K to 423 K (-130.1 °C to 150 °C) TC : solid \|\| annealed \|\| 0 K to 600 K (-273.1 °C to 326.9 °C) TD : solid \|\| annealed \|\| 10 K to 593 K (-263.1 °C to 320 °C) SH : solid \|\| 10 K to 601 K (-263.1 °C to 327.9 °C) HC : solid \|\| 10 K to 601 K (-263.1 °C to 327.9 °C) UTS : as-cast \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : as-cast \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) RHO : solid \|\| 7 K to 550 K (-266.1 °C to 276.9 °C) SIGMA : solid \|\| 7 K to 550 K (-266.1 °C to 276.9 °C)
Bismuth	D : solid \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) DLL : solid \|\| polycrystal \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) DLL : solid \|\| a-axis \|\| 58 K to 300 K (-215.1 °C to 26.9 °C) DLL : solid \|\| c-axis \|\| 58 K to 300 K (-215.1 °C to 26.9 °C) MTE : solid \|\| polycrystal \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) MTE : solid \|\| a-axis \|\| 58 K to 300 K (-215.1 °C to 26.9 °C) MTE : solid \|\| c-axis \|\| 58 K to 300 K (-215.1 °C to 26.9 °C) CTE : solid \|\| polycrystal \|\| 58 K to 300 K (-215.1 °C to 26.9 °C) CTE : solid \|\| a-axis \|\| 58 K to 300 K (-215.1 °C to 26.9 °C) CTE : solid \|\| c-axis \|\| 58 K to 300 K (-215.1 °C to 26.9 °C) E : solid \|\| 4 K to 544 K (-269.1 °C to 270.9 °C) G : solid \|\| 4 K to 544 K (-269.1 °C to 270.9 °C) v : solid \|\| 4 K to 544 K (-269.1 °C to 270.9 °C) K : solid \|\| 4 K to 544 K (-269.1 °C to 270.9 °C) TC : solid \|\| polycrystal, annealed \|\| 20 K to 544 K (-253.1 °C to 270.9 °C) TC : solid \|\| perpendicular to the trigonal axis \|\| 100 K to 300 K (-173.1 °C to 27 °C) TC : solid \|\| parallel to the trigonal axis \|\| 100 K to 300 K (-173.1 °C to 27 °C) TD : solid \|\| polycrystal, annealed \|\| 10 K to 544 K (-263.1 °C to 270.9 °C) TD : solid \|\| perpendicular to the trigonal axis \|\| 100 K to 300 K (-173.1 °C to 26.9 °C) TD : solid \|\| parallel to the trigonal axis \|\| 100 K to 300 K (-173.1 °C to 26.9 °C) SH : solid \|\| 10 K to 544 K (-263.1 °C to 270.9 °C) HC : solid \|\| 10 K to 544 K (-263.1 °C to 270.9 °C) RHO : solid \|\| perpendicular to the trigonal axis \|\| 80 K to 300 K (-193.1 °C to 27 °C) RHO : solid \|\| parallel to the trigonal axis \|\| 75 K to 300 K (-198.1 °C to 27 °C) SIGMA : solid \|\| perpendicular to the trigonal axis \|\| 80 K to 300 K (-193.1 °C to 27 °C) SIGMA : solid \|\| parallel to the trigonal axis \|\| 75 K to 300 K (-198.1 °C to 27 °C) S : single crystal \|\| perpendicular to the trigonal axis \|\| 80 K to 300 K (-193.1 °C to 27 °C) S : single crystal \|\| parallel to the trigonal axis \|\| 20 K to 300 K (-253.1 °C to 27 °C) S : polycrystal \|\| -325 to +400 mesh powder, annealed \|\| 100 K to 303 K (-173.1 °C to 30 °C) S : polycrystal \|\| -50 to +100 mesh powder, annealed \|\| 100 K to 303 K (-173.1 °C to 30 °C)
Radon	VP : liquid \|\| 130 K to 225 K (-143.1 °C to -48.1 °C)
Francium	VP : solid \|\| 198 K to 281 K (-75.1 °C to 7.9 °C) RHO : solid \|\| 100 K to 281 K (-173.1 °C to 7.9 °C) SIGMA : solid \|\| 100 K to 281 K (-173.1 °C to 7.9 °C)
Radium	RHO : solid \|\| 200 K to 500 K (-73.1 °C to 227 °C) SIGMA : solid \|\| 200 K to 500 K (-73.1 °C to 227 °C)
Thorium	D : solid \|\| 0 K to 400 K (-273.1 °C to 126.9 °C) DLL : solid \|\| 0 K to 400 K (-273.1 °C to 126.9 °C) MTE : solid \|\| 0 K to 400 K (-273.1 °C to 126.9 °C) E : solid \|\| 93 K to 773 K (-180.1 °C to 500 °C) TC : solid \|\| annealed \|\| 0 K to 1300 K (-273.1 °C to 1026.8 °C) TD : solid \|\| 100 K to 400 K (-173.1 °C to 126.9 °C) SH : solid \|\| 100 K to 2023 K (-173.1 °C to 1750 °C) HC : solid \|\| 100 K to 2023 K (-173.1 °C to 1750 °C)
Protactinium	RHO : solid \|\| 25 K to 295 K (-248.1 °C to 21.9 °C) SIGMA : solid \|\| 25 K to 295 K (-248.1 °C to 21.9 °C)
Uranium	TC : solid \|\| 0 K to 1200 K (-273.1 °C to 926.9 °C)
Neptunium	RHO : solid \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) SIGMA : solid \|\| 20 K to 300 K (-253.1 °C to 26.9 °C)
Plutonium	TC : solid \|\| annealed \|\| 80 K to 350 K (-193.1 °C to 76.9 °C)
Iron alloys	Property : Condition // Data range
ARMCO iron	D : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) DLL : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) MTE : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) CTE : solid \|\| 91 K to 960 K (-182.1 °C to 686.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) TC : solid \|\| 77 K to 1255 K (-196.1 °C to 982.3 °C) TD : solid \|\| 77 K to 960 K (-196.1 °C to 686.9 °C) SH : solid \|\| 1 K to 1809 K (-272.1 °C to 1535.8 °C) YS : solid \|\| 2.5x10^-⁴/s strain rate \|\| 77 K to 973 K (-196.1 °C to 700 °C) HE : solid \|\| polished \|\| 200 K to 1093 K (-73.1 °C to 820 °C)
1006 (UNS G10060) (ASTM A29/A510/A545) (AISI 1006) (SAE J403/J412/J414) (GB & GB/T 05/05F/06TIL/08AI/ML04AI)	D : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) DLL : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) MTE : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) CTE : solid \|\| 91 K to 960 K (-182.1 °C to 686.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) TC : solid \|\| 77 K to 1255 K (-196.1 °C to 982.3 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1008 (UNS G10080) (WNr 1.0204) (ISO/EN/DIN 2A/C10/C5) (JIS SWRCH8A) (ASTM A108/A510/A519/A545/A549/A575/A576) (AISI 1008) (SAE J403/J412/J414) (GB & GB/T 08/08AI/08F/B1/B1F/BY1/BY1F/Q195-F/Q195-Z/Q195-b)	D : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) DLL : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) MTE : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) CTE : solid \|\| 91 K to 960 K (-182.1 °C to 686.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1010 (UNS G10100) (WNr 1.1121) (ISO/EN/DIN C10/CK10) (JIS S10C) (ASTM A510/A519/A545/A549/A575/A576) (AISI 1010) (SAE J403/J412/J414) (AMS 5040/5042/5044/5050/5053) (GB & GB/T 08MnREL/08TIL/09OIVL/10/10A/10F/10TIL/ER49-1/ER50-4/ML10/ML10AI)	D : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) DLL : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) MTE : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) CTE : solid \|\| 91 K to 960 K (-182.1 °C to 686.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) TC : solid \|\| 122 K to 1200 K (-151.1 °C to 926.9 °C) TD : solid \|\| 116 K to 1122 K (-157.1 °C to 848.9 °C) SH : solid \|\| 73 K to 1000 K (-200.1 °C to 726.9 °C) UTS : annealed and as-received conditions \|\| 77 K to 1034 K (-196.1 °C to 760.9 °C) YS : annealed and as-received conditions \|\| 77 K to 1034 K (-196.1 °C to 760.9 °C) %El : annealed and as-received conditions \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1015 (UNS G10150) (WNr 1.1141) (ISO/EN/DIN C14/C15/C15E/Ck15) (JIS S15C) (ASTM C18RR/XC12/XC15) (AISI 1015) (SAE J403/J412/J414) (AMS 5060) (GB & GB/T 15/15F/15Mn/H15A/H15Mn/H15Mn/ML15/Q235C-Z/Q235D-TZ)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) TC : solid \|\| 123 K to 813 K (-150.1 °C to 540 °C) TD : solid \|\| 123 K to 813 K (-150.1 °C to 540 °C) SH : solid \|\| 73 K to 1000 K (-200.1 °C to 726.9 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1018 (UNS G10180) (WNr 1.0453) (ISO/EN/DIN C14/CK15) (JIS SEV295/SEV345) (ASTM A108/A510/A513/A519/A544/A545/A548/A549/A576/A659) (AISI 1018) (SAE J403/J412/J414) (AMS 5069) (GB & GB/T 410/5312/712/D)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) TC : solid \|\| 123 K to 813 K (-150.1 °C to 540 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1020 (UNS G10200) (WNr 1.0402) (ISO/EN/DIN C22/CK22) (JIS S20C/S22C/SWRCH20A) (ASTM A510/A519/A544/A576/A659) (AISI 1020) (SAE J403/J412/J414) (AMS 5032/5045) (GB & GB/T 20/20A/20F/20G/A/ML20/ML20AI/Q235q-C)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) TC : solid \|\| 26 K to 1073 K (-247.1 °C to 800 °C) UTS : as-received \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) YS : as-received \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1020 + 0.23 Si	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
1023 (UNS G10230) (WNr 1.1151) (ASTM A510/A575/A576) (AISI 1023) (SAE J403/J412/J414) (GB & GB/T Q235A-F/Q235A-b/Q255/Q255A-Z/Q255B-F/Q255B-F/Q255B-Z/Q255B-b)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1030 (UNS G10300) (WNr 1.1172) (ISO/EN/DIN C30) (JIS S30C/SWRH32B) (ASTM A510/A512/A519/A544/A546/A576/A682) (AISI 1030) (SAE J403/J412/J414) (AFNOR AF50C30/XC32) (GB & GB/T 30)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1035 (UNS G10350) (ISO/EN/DIN 35C8/C35/C35Mn75) (JIS S35C/SWRH37B) (ASTM A510/A519/A544/A545/A546/A576/A682) (AISI 1035) (SAE J403/J412/J414) (AMS 5080/5082)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1040 (UNS G10400) (WNr 1.1186) (ISO/EN/DIN 45C8/CK45/Ck40) (JIS G4051S40C/SWRH42B) (ASTM A108/A29/A449/A510/A519/A546/A576/A682) (AISI 1040) (SAE J403/J412/J414)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) UTS : as-received \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) YS : as-received \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : as-received \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
10B46 (AISI 10B46) (SAE J403)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1045 (UNS G10450) (WNr 1.1192/1.1730) (ISO/EN/DIN 45C8/C45/C45E/C45U/Ck45) (JIS S45C/SWRH47B) (ASTM A29/A510/A519/A576/A682) (AISI 1045) (SAE J403/J412/J414) (AFNOR XC48) (GB & GB/T 45/45H)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1065 (UNS G10650) (WNr 1.1230) (ISO/EN/DIN 65C6/C67) (JIS S65C/SWRH67B) (AISI 1065) (GB & GB/T 1222/3078/3522/4354/4357/65/6725/6819/699/711)	D : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) DLL : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) MTE : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1070 (UNS G10700) (WNr 1.1520) (JIS SWRH72B) (ASTM A510/A576/A682) (AISI 1070) (SAE J403/J412/J414) (AMS 5115) (AFNOR C70E2U) (GB & GB/T 70/70-E/70-F/70-G/CRB1170)	D : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) DLL : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) MTE : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1075 (UNS G10750) (WNr 1.0614) (JIS G4801SUP3/SWRH77B) (AISI 1075) (GB & GB/T 4354/4357/6725/699/75/8919)	D : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) DLL : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) MTE : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) SSC : quenched & tempered \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.7 mm/mm strain SSC : quenched & tempered \|\| tested at 77.6 °K (-195.6 °C), 3.3x10^-⁴/s \|\| 0 to 0.7 mm/mm strain SSC : quenched & tempered \|\| tested at 20.4 °K (-252.7 °C), 3.3x10^-⁴/s \|\| 0 to 0.01 mm/mm strain UTS : bar \|\| quenched & tempered \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar \|\| quenched & tempered \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar \|\| quenched & tempered \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) FEN : hardened & tempered \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum strain \|\| 3x10⁴ cycles to 8.3x10⁵ cycles FEN : hardened & tempered \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum strain \|\| 2.3x10⁴ cycles to 1x10⁷ cycles FEN : hardened & tempered \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum strain \|\| 6.8x10³ cycles to 1x10⁷ cycles FSN : hardened & tempered \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 3x10⁴ cycles to 1x10⁶ cycles FSN : hardened & tempered \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : hardened & tempered \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 7x10³ cycles to 1x10⁶ cycles FSN : hardened & tempered, K_t = 3.2 \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : hardened & tempered, K_t = 3.2 \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : hardened & tempered, K_t = 3.2 \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1080 (UNS G10800) (WNr 1.1248) (ISO/EN/DIN Ck75) (JIS SWRH82B) (ASTM A29/A510/A576/A682) (AISI 1080) (SAE J403/J412/J414) (AMS 5110) (GB & GB/T 4357/5354/6725/699/80/8919)	D : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) DLL : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) MTE : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1086 (UNS G10860) (WNr 1.0628) (AISI 1086) (GB & GB/T T8MnA-E/T8MnA-F/T8MnA-G/T9A-E/T9A-F/T9A-G)	D : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) DLL : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) MTE : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
1095 (UNS G10950) (WNr 1.0618) (ISO/EN/DIN Ck101) (ASTM A290/A510/A576/A682) (AISI 1095) (SAE J403/J412/J414) (AMS 5121/5122/5132/7304)	D : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) DLL : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) MTE : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) TC : solid \|\| 24 K to 1105 K (-249.1 °C to 831.9 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
EN08 (WNr 1.0511/1.1186/1.1189) (JIS S40C) (AFNOR AF60C40/AF60C45/XC42HI) (GB & GB/T 40)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
LZ45CrV	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
LZ50	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) HE : solid \|\| polished \|\| 68 K to 1467 K (-205.1 °C to 1193.4 °C)
G4802 SK5-CSP (JIS G4802SK5-CSP)	D : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) DLL : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) MTE : solid \|\| 20 K to 973 K (-253.1 °C to 700 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
1110 (UNS G11090/G11100) (WNr 1.0702/1.0703) (JIS SUM11/SUM12) (AISI 1110)	D : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) DLL : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) MTE : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) CTE : solid \|\| 91 K to 960 K (-182.1 °C to 686.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
1112 (AISI 1112)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) SH : solid \|\| 73 K to 1000 K (-200.1 °C to 726.9 °C)
1141 (UNS G11410) (AISI 1141) (AFNOR 45MF4)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
1144 (UNS G11440) (ASTM A29/A311/A510) (AISI 1144) (GB & GB/T Y40Mn)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
1151 (UNS G11510) (WNr 1.0728) (ISO/EN/DIN 60S20) (AISI 1151) (SAE J1397/J403/J935)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
API X60 pipeline steel	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) SH : solid \|\| 73 K to 1000 K (-200.1 °C to 726.9 °C)
API X65 pipeline steel	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) SH : solid \|\| 73 K to 1000 K (-200.1 °C to 726.9 °C)
API X80 pipeline steel	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) SH : solid \|\| 73 K to 1000 K (-200.1 °C to 726.9 °C) FSN : rotary bending fatigue \|\| tested at 193 °K (-80 °C), R = -1, maximum stress \|\| 2x10⁴ cycles to 1x10⁷ cycles
API X90 pipeline steel	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) SH : solid \|\| 73 K to 1000 K (-200.1 °C to 726.9 °C)
3140 (UNS G31400)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
4037 (UNS G40370) (WNr 1.5432) (ISO/EN/DIN 42MnMo7) (ASTM A322/A331/A519/A547) (AISI 4037) (SAE J404/J412/J770) (AMS 6300)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
4130 (UNS G41300) (WNr 1.7218) (ISO/EN/DIN 25CrMo4/G26CrMo4) (JIS SCM420/SCM430) (ASTM A322/A331/A505/A513) (AISI 4130) (SAE J404/J412/J770) (AMS 6350/6356/6360) (AFNOR 25CD4) (GB & GB/T 30CrMo/ZG20CrMo)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) CTE : solid \|\| 0 K to 977 K (-273.1 °C to 703.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) TC : solid \|\| hardened & tempered \|\| 24 K to 1473 K (-249.1 °C to 1200 °C)
4135 (UNS G41350) (WNr 1.7220) (ISO/EN/DIN 34CrMo4/35CrMo4) (JIS SCM435H) (ASTM A29/A331/A355/A519/A519/A711/A829) (AISI 4135) (SAE J1397/J404/J412/J770) (AMS 6352/6365/6372/6372C/6372D) (AFNOR 34CD4/35CD4) (GB & GB/T 35CrMo/ZG35CrMo)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) CTE : solid \|\| 0 K to 977 K (-273.1 °C to 703.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) TC : solid \|\| hardened & tempered \|\| 24 K to 1473 K (-249.1 °C to 1200 °C)
4140 (UNS G41400) (WNr 1.3563/1.7223/1.7225/1.7227) (ISO/EN/DIN 40Cr4Mo3/42CrMo4/42CrMoS4) (JIS SCM440/SCM440H) (ASTM A193/A194/A29/A320/A322/A331/A505/A506/A513/A519/A547/A646/A711/A752/A829) (AISI 4140) (SAE J404/J412/J770) (AMS 6349/6381/6382/6390/6395/6529) (AFNOR 42CD4) (GB & GB/T 42CrMo)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) CTE : solid \|\| 0 K to 977 K (-273.1 °C to 703.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
4142 (UNS G41420) (WNr 1.3563/1.7223/1.7225/1.7227) (ISO/EN/DIN 40Cr4Mo3/42Cr4Mo2) (AISI 4142) (AFNOR 40CD4/42CD4/42CDTS) (GB & GB/T 40CrMnMo/42CrMn/42CrMnMo)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
4150 (WNr 1.7228) (ISO/EN/DIN 49CrMo4/50CrMo4) (AISI 4150) (AFNOR 50CD4) (GB & GB/T 50CrMo)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
SCM 415 (WNr 1.7262) (ISO/EN/DIN 15CrMo) (JIS SCM415) (AFNOR 15CD4.05)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
4310 (UNS G43100) (AISI 4310) (SAE 4310)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 871.1 °C) CTE : solid \|\| 0 K to 977 K (-273.1 °C to 703.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
4320 (UNS G43200) (WNr 1.8988) (ISO/EN/DIN 15NiVCr1Mo15) (AISI 4320) (SAE 4320) (GB & GB/T G20CrNi2Mo/G20CrNiMo)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 871.1 °C) CTE : solid \|\| 0 K to 977 K (-273.1 °C to 703.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
4340 (UNS G43400) (WNr 1.6565) (ISO/EN/DIN 36CrNiMo6/40NiCr4Mo3/40NiCrMo6) (JIS G4103SNCM439) (ASTM A322/A331/A505/A519/A547/A646) (AISI 4340) (SAE J404/J412/J770) (AMS 5331/6359/6414/6415) (AFNOR 35NCD6) (GB & GB/T 34CrNi1Mo/40CrNiMo/40CrNiMoA)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 871.1 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 871.1 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 871.1 °C) CTE : solid \|\| 0 K to 977 K (-273.1 °C to 703.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) TC : solid \|\| oil quenched \|\| 123 K to 813 K (-150.1 °C to 540 °C) TC : solid \|\| normalized \|\| 123 K to 813 K (-150.1 °C to 540 °C) FSN : UTS 1.59 GPa (231 ksi), hardened & tempered \|\| tested at 77 °K (-196.1 °C), R = -1, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : UTS 1.59 GPa (231 ksi), hardened & tempered \|\| tested at 77 °K (-196.1 °C), R = -1, K_t = 2.75, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles RHO : solid \|\| cold-drawn, annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| cold-drawn, annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C)
4350 (UNS G43500) (AISI 4350) (SAE 4350)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 871.1 °C) CTE : solid \|\| 0 K to 977 K (-273.1 °C to 703.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
4615 (UNS G46150) (AISI 4615) (SAE 4615)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
5115 (UNS G51150) (WNr 1.7131) (ISO/EN/DIN 16MnCr5/17Mn1Cr95) (AISI 5115) (AFNOR 16MC5) (GB & GB/T 15Cr/15CrMn/16MnCr/20Cr)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
5132 (UNS G51320) (WNr 1.7033/1.7037/1.8401) (ISO/EN/DIN 34Cr4/34CrS4) (ASTM A331/A332/A505/A519) (AISI 5132) (SAE J404/J412/J770) (AFNOR 32C4) (GB & GB/T 30Cr/30CrMnSi)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
5140 (UNS G51400) (WNr 1.7035/1.7039/1.7045) (ISO/EN/DIN 37Cr4/40Cr/40Cr1/41Cr4) (JIS SCR440) (ASTM A331/A332/A505/A519) (AISI 5140) (SAE J404/J412/J770) (AFNOR 42C4) (GB & GB/T 38CrA/40Cr)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
5160 (UNS G51600) (ASTM A29/A322/A331/A505/A519/A752/A829) (AISI 5160) (SAE J1397/J404/J412/J770)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
6140 (UNS G61400) (AISI 6140) (SAE J1249)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
6150 (UNS G61500) (WNr 1.8159) (ISO/EN/DIN 50CrV2/50CrV4/51CrV4) (JIS G4801SUP10) (AISI 6150) (SAE 6150) (AFNOR 50CV4/50CrV4/51CrV4) (GB & GB/T 50CrVA)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
8620 (WNr 1.7321) (ISO/EN/DIN 20MoCr4/20NiCrMo2) (SAE 8620)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
8630 (UNS G86300) (WNr 1.6545) (ISO/EN/DIN 30NiCrMo2) (ASTM A322/A505) (AISI 8630) (AMS 5333)	UTS : normalized \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : normalized \|\| 77 K to 300 K (-196.1 °C to 26.9 °C)
S690QL (WNr 1.8928)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
JIS G 4801 SUP12 (JIS G4801SUP12)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
9255 (UNS G92550) (WNr 1.0904) (ISO/EN/DIN 55Si2Mn90/55Si7) (AISI 9255) (SAE J404/J412/J770)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A36 (UNS K02600) (ASTM A36)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A106 Grade B (UNS K03006) (WNr 1.0405) (ISO/EN/DIN P265GH) (JIS G3454STPG410) (ASTM A106B)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A182 Grade F1 (WNr 1.5415) (ISO/EN/DIN 15Mo3/16Mo3) (SAE A182GradeF1) (AMS A182GradeF1)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A182 Grade F11 (WNr 1.7335) (ISO/EN/DIN 13CrMo44/13CrMo45) (JIS SFVAF12) (SAE A182GradeF11) (AMS A182GradeF11) (GB & GB/T 12CrMo)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A201 Grade B	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A302 Grade B	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A283C (S235)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A333 Grade 6	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A441 (UNS K12211) (ASTM A441)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A500 Grade A	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) TC : solid \|\| 77 K to 1255 K (-196.1 °C to 982.3 °C) SSC : 8.33x10^-⁴/s \|\| tested at 153 °K (-120 °C) in liquid N₂ \|\| 0 to 0.15 mm/mm strain UTS : solid \|\| 113 K to 293 K (-160.1 °C to 20 °C) YS : solid \|\| 113 K to 293 K (-160.1 °C to 20 °C) %El : solid \|\| 113 K to 293 K (-160.1 °C to 20 °C)
A508 Cl.3	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A508 Gr.1A	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A514 (UNS K11872) (JIS ADC6) (ASTM G4A) (AFNOR A-G3T)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A529 (WNr 1.0044) (JIS SS400) (ASTM A529) (AFNOR E28-2) (GB & GB/T Q225A/Q275Z)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A537 Gr 1 & 2 (S185) (UNS K02400) (ASTM A537)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A533 Grade B (WNr 1.7703) (ISO/EN/DIN 13CrMoV9-10)	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A572 Grade 50 (WNr 1.0045) (JIS SM490A/SS490) (ASTM A572) (AFNOR E36-2) (GB & GB/T Q345B/Q345C)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A572 Grade 65	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A992	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A633 Grade C (UNS K12000)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
ASTM A723 (UNS K25550)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
500C rebar	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
BS 460B (steel reinforcing bar)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
BS B500B (steel reinforcing bar)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
B500SP (steel reinforcing bar)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
A881/A881M rebar	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
P690Q (WNr 1.8879)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) SSC : quenched & tempered \|\| tested at 77 °K (-196.1 °C), unknown strain rate \|\| 0 to 0.12 mm/mm strain SSC : quenched & tempered \|\| tested at 156 °K (-117 °C), unknown strain rate \|\| 0 to 0.8 mm/mm strain SSC : quenched & tempered \|\| tested at 179 °K (-94 °C), unknown strain rate \|\| 0 to 0.67 mm/mm strain
10GN2MFA	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) UTS : unknown condition \|\| 153 K to 293 K (-120.1 °C to 20 °C) YS : unknown condition \|\| 153 K to 293 K (-120.1 °C to 20 °C) %El : unknown condition \|\| 153 K to 293 K (-120.1 °C to 20 °C) FSN : unknown condition \|\| tested at 153 °K (-120 °C), R = -1, rotating beam, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles
JIS G4053-SMn443 (JIS G4053SMn443)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
P500QL2 (WNr 1.8865)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DIROS 500 S	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
Fe - 2 Mn - 1.3 Si - 0.7 Cr - 0.4 C (wt %)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
Strenx 700	D : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) DLL : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) MTE : solid \|\| 0 K to 960 K (-273.1 °C to 686.9 °C) CTE : solid \|\| 91 K to 960 K (-182.1 °C to 686.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
Strenx 960 Plus	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
Docol S355	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
D6a/D6ac (UNS K24728) (ASTM A355/A579) (AMS 5027/5028/6431/6438/6439)	UTS : normalized at 1200 °K (927 °C), austenitized at 1172 °K (899 °C), tempered at 811 °K (538 °C) \|\| air melted \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : normalized at 1200 °K (927 °C), austenitized at 1172 °K (899 °C), tempered at 811 °K (538 °C) \|\| ESR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : normalized at 1200 °K (927 °C), austenitized at 1172 °K (899 °C), tempered at 811 °K (538 °C) \|\| VAR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : normalized at 1200 °K (927 °C), austenitized at 1172 °K (899 °C), tempered at 811 °K (538 °C) \|\| average of the 3 different processing types \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : normalized at 1200 °K (927 °C), austenitized at 1172 °K (899 °C), tempered at 811 °K (538 °C) \|\| air melted \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : normalized at 1200 °K (927 °C), austenitized at 1172 °K (899 °C), tempered at 811 °K (538 °C) \|\| ESR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : normalized at 1200 °K (927 °C), austenitized at 1172 °K (899 °C), tempered at 811 °K (538 °C) \|\| VAR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : normalized at 1200 °K (927 °C), austenitized at 1172 °K (899 °C), tempered at 811 °K (538 °C) \|\| average of the 3 different processing types \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : normalized at 1200 °K (927 °C), austenitized at 1172 °K (899 °C), tempered at 811 °K (538 °C) \|\| air melted \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : normalized at 1200 °K (927 °C), austenitized at 1172 °K (899 °C), tempered at 811 °K (538 °C) \|\| ESR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : normalized at 1200 °K (927 °C), austenitized at 1172 °K (899 °C), tempered at 811 °K (538 °C) \|\| VAR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : normalized at 1200 °K (927 °C), austenitized at 1172 °K (899 °C), tempered at 811 °K (538 °C) \|\| average of the 3 different processing types \|\| 77 K to 293 K (-196.1 °C to 20 °C)
SIQUAL 8509 (WNr 1.8509) (ISO/EN/DIN 41CrAlMo7/41CrAlMo7-10)	D : solid \|\| 82 K to 773 K (-191.1 °C to 500 °C) DLL : solid \|\| 82 K to 773 K (-191.1 °C to 500 °C) MTE : solid \|\| 82 K to 773 K (-191.1 °C to 500 °C)
SIQUAL 8519 (WNr 1.8519) (ISO/EN/DIN 31CrMoV9)	D : solid \|\| 82 K to 773 K (-191.1 °C to 500 °C) DLL : solid \|\| 82 K to 773 K (-191.1 °C to 500 °C) MTE : solid \|\| 82 K to 773 K (-191.1 °C to 500 °C)
SIQUAL 8550 (WNr 1.8550) (ISO/EN/DIN 34CrAlNi7/34CrAlNi7-10)	D : solid \|\| 82 K to 773 K (-191.1 °C to 500 °C) DLL : solid \|\| 82 K to 773 K (-191.1 °C to 500 °C) MTE : solid \|\| 82 K to 773 K (-191.1 °C to 500 °C)
HY-130	UTS : as-received \|\| plates \|\| 81 K to 421 K (-192.1 °C to 147.9 °C) UTS : normalized at 1144 °K (871 °C), austenitized at 1089 °K (816 °C), tempered at 811 °K (538 °C) \|\| air melted \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : normalized at 1144 °K (871 °C), austenitized at 1089 °K (816 °C), tempered at 811 °K (538 °C) \|\| ESR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : normalized at 1144 °K (871 °C), austenitized at 1089 °K (816 °C), tempered at 811 °K (538 °C) \|\| VAR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : normalized at 1144 °K (871 °C), austenitized at 1089 °K (816 °C), tempered at 811 °K (538 °C) \|\| average of the 3 different processing types \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : plates \|\| as-received \|\| 81 K to 421 K (-192.1 °C to 147.9 °C) YS : normalized at 1144 °K (871 °C), austenitized at 1089 °K (816 °C), tempered at 811 °K (538 °C) \|\| air melted \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : normalized at 1144 °K (871 °C), austenitized at 1089 °K (816 °C), tempered at 811 °K (538 °C) \|\| ESR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : normalized at 1144 °K (871 °C), austenitized at 1089 °K (816 °C), tempered at 811 °K (538 °C) \|\| VAR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : normalized at 1144 °K (871 °C), austenitized at 1089 °K (816 °C), tempered at 811 °K (538 °C) \|\| average of the 3 different processing types \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : plates \|\| as-received \|\| 81 K to 293 K (-192.1 °C to 20 °C) %El : normalized at 1144 °K (871 °C), austenitized at 1089 °K (816 °C), tempered at 811 °K (538 °C) \|\| air melted \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : normalized at 1144 °K (871 °C), austenitized at 1089 °K (816 °C), tempered at 811 °K (538 °C) \|\| ESR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : normalized at 1144 °K (871 °C), austenitized at 1089 °K (816 °C), tempered at 811 °K (538 °C) \|\| VAR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : normalized at 1144 °K (871 °C), austenitized at 1089 °K (816 °C), tempered at 811 °K (538 °C) \|\| average of the 3 different processing types \|\| 77 K to 293 K (-196.1 °C to 20 °C)
CA15 (UNS J91150) (ASTM A217/A426/A487/A743) (SAE 60410) (AMS 5351B)	E : solid \|\| 20 K to 1173 K (-253.1 °C to 900 °C)
CC50 (UNS J92615) (ASTM A743) (SAE 60446)	NE : solid \|\| surface finish #1 \|\| 100 K to 1200 K (-173.1 °C to 926.9 °C) NE : solid \|\| surface finish #8 \|\| 100 K to 1200 K (-173.1 °C to 926.9 °C)
CF3 (UNS J92500) (WNr 1.4306/1.4307) (ISO/EN/DIN X2CrNi18-9/X2CrNi19-11) (ASTM A351/A451/A743/A744) (AMS 5511/5639/5647/5697) (AFNOR Z2CN18-10/Z3CN18-10/Z3CN19-10M) (GB & GB/T 00Cr19Ni10)	E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) UTS : as-cast \|\| 173 K to 673 K (-100.1 °C to 400 °C) YS : as-cast \|\| 173 K to 673 K (-100.1 °C to 400 °C) %El : as-cast \|\| 173 K to 673 K (-100.1 °C to 400 °C)
CF3M (UNS J92800) (ISO/EN/DIN X2CrNiMo17-12-2) (JIS SUS316/SUS316L) (ASTM A351/A451/A743/A744) (GB & GB/T 00Cr17Ni14Mo2/0Cr18Ni12Mo2Ti)	D : solid \|\| 75 K to 923 K (-198.1 °C to 650 °C) DLL : solid \|\| 75 K to 923 K (-198.1 °C to 650 °C) MTE : solid \|\| 75 K to 923 K (-198.1 °C to 650 °C) CTE : solid \|\| 75 K to 923 K (-198.1 °C to 650 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) K : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) UTS : as-cast \|\| 173 K to 673 K (-100.1 °C to 400 °C) YS : as-cast \|\| 173 K to 673 K (-100.1 °C to 400 °C) %El : as-cast \|\| 173 K to 673 K (-100.1 °C to 400 °C)
CF8 (UNS J92600) (ASTM A351/A451/A743/A743/A744) (SAE 60304)	D : solid \|\| 75 K to 923 K (-198.1 °C to 650 °C) DLL : solid \|\| 75 K to 923 K (-198.1 °C to 650 °C) MTE : solid \|\| 75 K to 923 K (-198.1 °C to 650 °C) CTE : solid \|\| 75 K to 923 K (-198.1 °C to 650 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) K : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) UTS : as-cast \|\| 173 K to 673 K (-100.1 °C to 400 °C) YS : as-cast \|\| 173 K to 673 K (-100.1 °C to 400 °C) %El : as-cast \|\| 173 K to 673 K (-100.1 °C to 400 °C) HE : solid \|\| grit blasted black oxidized \|\| 175 K to 350 K (-98.1 °C to 76.9 °C)
CF8C (UNS J92710) (ASTM A351/A451/A743/A744) (SAE 60347) (AMS 5363B)	E : solid \|\| 80 K to 1144 K (-193.1 °C to 870.9 °C) SH : solid \|\| 4 K to 1255 K (-269.1 °C to 982.3 °C)
CF8M (UNS J92900) (ASTM A351/A743/A744) (SAE 60316)	E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) K : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) SH : solid \|\| 4 K to 1255 K (-269.1 °C to 982.3 °C) UTS : as-cast \|\| 173 K to 673 K (-100.1 °C to 400 °C) YS : as-cast \|\| 173 K to 673 K (-100.1 °C to 400 °C) %El : as-cast \|\| 173 K to 673 K (-100.1 °C to 400 °C)
CF12M (ASTM A451) (SAE 60316)	E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) K : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) SH : solid \|\| 4 K to 1255 K (-269.1 °C to 982.3 °C)
CF16F (UNS J92701) (WNr 1.4305) (ISO/EN/DIN X8CrNiS18-9) (ASTM A743) (SAE 60303/60303a) (AFNOR Z10CNF18-09/Z8CNF18-09) (GB & GB/T Y1Cr18Ni9/Y1Cr18Ni9)	E : solid \|\| 0 K to 593 K (-273.1 °C to 320 °C)
CF20 (UNS J92602) (ASTM A743) (SAE 60302) (AFNOR Z10CN18.09) (GB & GB/T 1Cr18Ni9)	E : solid \|\| 33 K to 1089 K (-240.1 °C to 815.6 °C) G : solid \|\| 33 K to 1089 K (-240.1 °C to 815.6 °C) v : solid \|\| 33 K to 1089 K (-240.1 °C to 815.6 °C) K : solid \|\| 33 K to 1089 K (-240.1 °C to 815.6 °C)
CG8M (UNS J93000) (ASTM A743/A744) (AFNOR Z8CND18.10.3M) (GB & GB/T 0Cr19Ni13Mo3)	SH : solid \|\| 4 K to 873 K (-269.1 °C to 600 °C)
CK20 (UNS J94202) (ASTM A351/A451/A743) (SAE 60310) (AMS 5365A)	E : solid \|\| 5 K to 1144 K (-268.1 °C to 870.9 °C) G : solid \|\| 5 K to 1144 K (-268.1 °C to 870.9 °C) v : solid \|\| 5 K to 1144 K (-268.1 °C to 870.9 °C) K : solid \|\| 5 K to 1144 K (-268.1 °C to 870.9 °C) SH : solid \|\| 4 K to 1173 K (-269.1 °C to 900 °C)
Hardox 400	E : solid \|\| 173 K to 293 K (-100.1 °C to 20 °C) SSC : tempered martensite-bainite \|\| tested at 193 °K (-80 °C), unknown strain rate \|\| 0 to 0.56 mm/mm strain SSC : tempered martensite-bainite \|\| tested at 173 °K (-100 °C), unknown strain rate \|\| 0 to 0.67 mm/mm strain UTS : solution annealed & aged \|\| 173 K to 293 K (-100.1 °C to 20 °C) YS : solution annealed & aged \|\| 173 K to 293 K (-100.1 °C to 20 °C) %El : solution annealed & aged \|\| 173 K to 293 K (-100.1 °C to 20 °C)
300M (UNS K44220) (ASTM A579) (AMS 6419)	D : solid \|\| 0 K to 977 K (-273.1 °C to 703.9 °C) DLL : solid \|\| 0 K to 977 K (-273.1 °C to 703.9 °C) MTE : solid \|\| 0 K to 977 K (-273.1 °C to 703.9 °C) CTE : solid \|\| 0 K to 977 K (-273.1 °C to 703.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
9 Ni steel (UNS K81340) (ASTM A1334/A333/A353M/A522/A553M)	D : solid \|\| 52 K to 811 K (-221.1 °C to 537.9 °C) DLL : solid \|\| 52 K to 811 K (-221.1 °C to 537.9 °C) MTE : solid \|\| 52 K to 811 K (-221.1 °C to 537.9 °C) CTE : solid \|\| 52 K to 811 K (-221.1 °C to 537.9 °C) E : solid \|\| 75 K to 311 K (-198.1 °C to 37.9 °C) TC : solid \|\| heat-treated \|\| 52 K to 811 K (-221.1 °C to 537.9 °C) SSC : double normalized & stress relieved \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.1 mm/mm strain SSC : double normalized & stress relieved \|\| tested at 77.6 °K (-195.6 °C), 3.3x10^-⁴/s \|\| 0 to 0.18 mm/mm strain SSC : double normalized & stress relieved \|\| tested at 20.4 °K (-252.7 °C), 3.3x10^-⁴/s \|\| 0 to 0.2 mm/mm strain UTS : solid \|\| heat-treated at 1172 °K (899 °C) \|\| 20 K to 755 K (-253.1 °C to 482.3 °C) YS : solid \|\| heat-treated at 1172 °K (899 °C) \|\| 20 K to 755 K (-253.1 °C to 482.3 °C) %El : solid \|\| heat-treated at 1172 °K (899 °C) \|\| 20 K to 755 K (-253.1 °C to 482.3 °C) FEN : normalized & aged \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum strain \|\| 1x10⁴ cycles to 7.7x10⁵ cycles FEN : normalized & aged \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum strain \|\| 2.4x10⁴ cycles to 1x10⁷ cycles FEN : normalized & aged \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum strain \|\| 1.3x10⁴ cycles to 1x10⁶ cycles FSN : normalized & aged \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : normalized & aged \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : normalized & aged \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : normalized & aged, K_t = 3.1 \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 6x10⁵ cycles FSN : normalized & aged, K_t = 3.1 \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : normalized & aged, K_t = 3.1 \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 4x10⁵ cycles
HP 9-4-20 (UNS K91461/K91472) (AMS 6468/6523/6525)	D : solid \|\| 22 K to 1275 K (-251.1 °C to 1001.9 °C) DLL : solid \|\| 22 K to 1275 K (-251.1 °C to 1001.9 °C) MTE : solid \|\| 22 K to 1275 K (-251.1 °C to 1001.9 °C)
HP 9-4-25 (UNS K91122) (AMS 6546)	D : solid \|\| 22 K to 366 K (-251.1 °C to 92.9 °C) DLL : solid \|\| 22 K to 366 K (-251.1 °C to 92.9 °C) MTE : solid \|\| 22 K to 366 K (-251.1 °C to 92.9 °C) CTE : solid \|\| 22 K to 366 K (-251.1 °C to 92.9 °C)
HP 9-4-30 (UNS K91283)	D : solid \|\| 22 K to 366 K (-251.1 °C to 92.9 °C) DLL : solid \|\| 22 K to 366 K (-251.1 °C to 92.9 °C) MTE : solid \|\| 22 K to 366 K (-251.1 °C to 92.9 °C) CTE : solid \|\| 22 K to 366 K (-251.1 °C to 92.9 °C) E : solid \|\| in tension \|\| 188 K to 533 K (-85.1 °C to 260 °C) E : solid \|\| in compression \|\| 188 K to 533 K (-85.1 °C to 260 °C) SSC : long transverse \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : short transverse \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : longitudinal \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.4 mm/mm strain UTS : unknown condition \|\| hand forging \|\| 200 K to 533 K (-73.1 °C to 260 °C) UTS : normalized at 1172 °K (899 °C), austenitized at 1103 °K (829 °C), tempered at 811 °K (538 °C) \|\| air melted \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : normalized at 1172 °K (899 °C), austenitized at 1103 °K (829 °C), tempered at 811 °K (538 °C) \|\| ESR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : normalized at 1172 °K (899 °C), austenitized at 1103 °K (829 °C), tempered at 811 °K (538 °C) \|\| VAR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : normalized at 1172 °K (899 °C), austenitized at 1103 °K (829 °C), tempered at 811 °K (538 °C) \|\| average of the 3 different processing types \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : unknown condition \|\| hand forging \|\| 200 K to 533 K (-73.1 °C to 260 °C) YS : normalized at 1172 °K (899 °C), austenitized at 1103 °K (829 °C), tempered at 811 °K (538 °C) \|\| air melted \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : normalized at 1172 °K (899 °C), austenitized at 1103 °K (829 °C), tempered at 811 °K (538 °C) \|\| ESR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : normalized at 1172 °K (899 °C), austenitized at 1103 °K (829 °C), tempered at 811 °K (538 °C) \|\| VAR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : normalized at 1172 °K (899 °C), austenitized at 1103 °K (829 °C), tempered at 811 °K (538 °C) \|\| average of the 3 different processing types \|\| 77 K to 293 K (-196.1 °C to 20 °C) YSC : unknown condition \|\| hand forging \|\| 200 K to 533 K (-73.1 °C to 260 °C) %El : normalized at 1172 °K (899 °C), austenitized at 1103 °K (829 °C), tempered at 811 °K (538 °C) \|\| air melted \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : normalized at 1172 °K (899 °C), austenitized at 1103 °K (829 °C), tempered at 811 °K (538 °C) \|\| ESR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : normalized at 1172 °K (899 °C), austenitized at 1103 °K (829 °C), tempered at 811 °K (538 °C) \|\| VAR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : normalized at 1172 °K (899 °C), austenitized at 1103 °K (829 °C), tempered at 811 °K (538 °C) \|\| average of the 3 different processing types \|\| 77 K to 293 K (-196.1 °C to 20 °C)
AL-6XN (UNS N08367) (WNr 1.4529) (ISO/EN/DIN X1NiCrMoCuN25-20-7) (JIS SUS836L) (ASTM A182/A194/A240/A249/A269/A270/A351/A358/A409/A479/A688/A743/A744/A813/A814/B366/B462/B472/B472/B564/B675/B676/B688/B690/B691/B804/B834)	SSCC : as-received plate \|\| tested at 77 °K (-196.1 °C), 0.001/s \|\| 0 to 0.45 mm/mm strain SSCC : as-received plate \|\| tested at 77 °K (-196.1 °C), 3500/s \|\| 0 to 0.34 mm/mm strain SSCC : as-received plate \|\| tested at 77 °K (-196.1 °C), 8300/s \|\| 0 to 0.35 mm/mm strain UTS : annealed \|\| 5 K to 811 K (-268.1 °C to 537.9 °C) YS : annealed \|\| 5 K to 811 K (-268.1 °C to 537.9 °C) %El : annealed \|\| 5 K to 811 K (-268.1 °C to 537.9 °C)
201LN (UNS S20153) (WNr 1.4371) (ISO/EN/DIN X2CrMnNiN17-7-5) (ASTM A240)	UTS : annealed \|\| 67 K to 1073 K (-206.1 °C to 800 °C) YS : annealed \|\| 67 K to 1073 K (-206.1 °C to 800 °C) %El : annealed \|\| 89 K to 1073 K (-184.1 °C to 800 °C)
301 (UNS S30100) (WNr 1.4310) (ISO/EN/DIN X10CrNi18-8) (JIS SUS301) (ASTM A167/A177/A554/A666) (AISI 301) (SAE J405) (AMS 5517/5518/5519) (AFNOR Z11CN18-08/Z12CN17-07) (GB & GB/T 1Cr17Ni7/1Cr17Ni8)	D : solid \|\| 22 K to 1144 K (-251.1 °C to 870.9 °C) DLL : solid \|\| 22 K to 1144 K (-251.1 °C to 870.9 °C) MTE : solid \|\| 22 K to 1144 K (-251.1 °C to 870.9 °C) E : average \|\| 20 K to 773 K (-253.1 °C to 500 °C) E : 60% cold reduction \|\| longitudinal \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) E : 60% cold reduction \|\| transverse \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) E : extra hard sheet \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) E : full hard rod \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) G : average \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) v : average \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) K : average \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) TC : solid \|\| 136 K to 1216 K (-137.1 °C to 942.9 °C) TD : solid \|\| annealed \|\| 116 K to 1255 K (-157.1 °C to 982.3 °C) SH : solid \|\| 73 K to 1255 K (-200.1 °C to 982.3 °C) UTS : annealed \|\| 4 K to 1144 K (-269.1 °C to 870.9 °C) UTS : extra hard \|\| 20 K to 293 K (-253.1 °C to 20 °C) UTS : 60% cold-rolled \|\| unnotched, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 60% cold-rolled \|\| unnotched, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 60% cold-rolled \|\| notched, K_t = 3.2, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 60% cold-rolled \|\| notched, K_t = 3.2, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 60% cold-rolled \|\| notched, K_t = 6.3, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 60% cold-rolled \|\| notched, K_t = 6.3, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 60% cold-rolled \|\| notched, K_t = 19, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 60% cold-rolled \|\| notched, K_t = 19, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 60% cold-rolled \|\| weld joint, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 60% cold-rolled \|\| weld joint, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) YS : annealed \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C) YS : extra hard \|\| 20 K to 293 K (-253.1 °C to 20 °C) YS : 60% cold-rolled \|\| unnotched, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) YS : 60% cold-rolled \|\| unnotched, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) %El : annealed \|\| 4 K to 1144 K (-269.1 °C to 870.9 °C) %El : extra hard \|\| 20 K to 293 K (-253.1 °C to 20 °C) %El : 60% cold-rolled \|\| unnotched, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) %El : 60% cold-rolled \|\| unnotched, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) %El : 60% cold-rolled \|\| weld joint, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) %El : 60% cold-rolled \|\| weld joint, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) FSN : extra full hard 1 mm (0.0394 inch) sheet \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : extra full hard 1 mm (0.0394 inch) sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : extra full hard 1 mm (0.0394 inch) sheet \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 8x10³ cycles to 1x10⁶ cycles FSN : extra full hard 1 mm (0.0394 inch) sheet, K_t = 3.1 \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : extra full hard 1 mm (0.0394 inch) sheet, K_t = 3.1 \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : extra full hard 1 mm (0.0394 inch) sheet, K_t = 3.1 \|\| tested at 20.4 °K (-252.7 °C), R = -1, flexure, maximum stress \|\| 4x10³ cycles to 8x10⁴ cycles NE : solid \|\| polished \|\| 88 K to 1114 K (-185.1 °C to 840.9 °C) NE : solid \|\| clean & smooth \|\| 88 K to 1090 K (-185.1 °C to 816.9 °C)
302 (UNS S30200) (WNr 1.4300) (ISO/EN/DIN X12CrNi18-8) (JIS SUS302) (ASTM A167/A240/A276/A313/A479/A580) (AISI 302) (SAE J230/J405) (AMS 5515/5516/5600) (AFNOR Z10CN18.09) (GB & GB/T 1Cr18Ni9)	D : solid \|\| 22 K to 1144 K (-251.1 °C to 870.9 °C) DLL : solid \|\| 22 K to 1144 K (-251.1 °C to 870.9 °C) MTE : solid \|\| 22 K to 1144 K (-251.1 °C to 870.9 °C) E : solid \|\| 33 K to 1089 K (-240.1 °C to 815.6 °C) G : solid \|\| 33 K to 1089 K (-240.1 °C to 815.6 °C) v : solid \|\| 33 K to 1089 K (-240.1 °C to 815.6 °C) K : solid \|\| 33 K to 1089 K (-240.1 °C to 815.6 °C) UTS : annealed \|\| 20 K to 1089 K (-253.1 °C to 815.6 °C) UTS : cold-drawn \|\| 20 K to 293 K (-253.1 °C to 20 °C) YS : annealed \|\| 20 K to 1089 K (-253.1 °C to 815.6 °C) YS : cold-drawn \|\| 20 K to 293 K (-253.1 °C to 20 °C) %El : annealed \|\| 20 K to 1089 K (-253.1 °C to 815.6 °C) %El : cold-drawn \|\| 20 K to 293 K (-253.1 °C to 20 °C) RHO : solid \|\| 4 K to 1173 K (-269.1 °C to 900 °C) SIGMA : solid \|\| 4 K to 1173 K (-269.1 °C to 900 °C)
302HQ (UNS S30430) (JIS SUSXM7) (ASTM A276/A493/F593)	UTS : annealed \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) YS : annealed \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : annealed \|\| 77 K to 300 K (-196.1 °C to 26.9 °C)
303 (UNS S30300) (WNr 1.4305) (ISO/EN/DIN X8CrNiS18-9) (JIS SUS303) (ASTM A194/A314/A320/A473/A473/A581/A582/A895) (AISI 303) (SAE J405) (AMS 5640) (AFNOR Z10CNF18-09/Z8CNF18-09) (GB & GB/T Y1Cr18Ni9/Y1Cr18Ni9)	D : solid \|\| 0 K to 923 K (-273.1 °C to 650 °C) DLL : solid \|\| 0 K to 923 K (-273.1 °C to 650 °C) MTE : solid \|\| 0 K to 923 K (-273.1 °C to 650 °C) E : solid \|\| 0 K to 593 K (-273.1 °C to 320 °C) TC : solid \|\| 4 K to 1173 K (-269.1 °C to 900 °C) RHO : solid \|\| 4 K to 1175 K (-269.1 °C to 901.9 °C) SIGMA : solid \|\| 4 K to 1175 K (-269.1 °C to 901.9 °C)
304 (UNS S30400) (WNr 1.4301) (ISO/EN/DIN X5CrNi18-10/X5CrNi18-9) (JIS SUS304) (ASTM A167/A182/A193/A276/A314/A320/A479) (AISI 304) (SAE J405) (AMS 5501/5513/5639/5647/5697) (AFNOR Z6CN18-09/Z7CN18-09) (GB & GB/T 0Cr18Ni9)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) TC : solid \|\| 1 K to 1700 K (-272.1 °C to 1426.8 °C) TD : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) SSC : annealed at 1323 °K (1050 °C), water quenched \|\| tested at 77 °K (-196.1 °C), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : annealed at 1323 °K (1050 °C), water quenched \|\| tested at 153 °K (-120 °C), unknown strain rate \|\| 0 to 0.35 mm/mm strain SSC : annealed at 1323 °K (1050 °C), water quenched \|\| tested at 193 °K (-80 °C), unknown strain rate \|\| 0 to 0.4 mm/mm strain UTS : annealed \|\| 20 K to 1089 K (-253.1 °C to 815.6 °C) UTS : 50% cold-rolled, extra low carbon grade \|\| longitudinal \|\| 20 K to 298 K (-253.1 °C to 25 °C) UTS : 50% cold-rolled, extra low carbon grade \|\| transverse \|\| 20 K to 298 K (-253.1 °C to 25 °C) YS : annealed \|\| 20 K to 1089 K (-253.1 °C to 815.6 °C) YS : 50% cold-rolled, extra low carbon grade \|\| longitudinal \|\| 20 K to 298 K (-253.1 °C to 25 °C) YS : 50% cold-rolled, extra low carbon grade \|\| transverse \|\| 20 K to 298 K (-253.1 °C to 25 °C) %El : annealed \|\| 20 K to 1089 K (-253.1 °C to 815.6 °C) %El : 50% cold-rolled, extra low carbon grade \|\| longitudinal \|\| 20 K to 298 K (-253.1 °C to 25 °C) %El : 50% cold-rolled, extra low carbon grade \|\| transverse \|\| 20 K to 298 K (-253.1 °C to 25 °C) FSN : cold reduced bar \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 4x10³ cycles to 6x10⁶ cycles FSN : cold reduced bar \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 6x10³ cycles to 1x10⁶ cycles FSN : cold reduced bar \|\| tested at 77.6 °K (-195.6 °C) R = -1, K_t = 2.75, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles FSN : cold reduced bar \|\| tested at 20 °K (-253.1 °C) R = -1, K_t = 2.75, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : cold reduced bar \|\| tested at 77.6 °K (-195.6 °C) R = -1, K_t = 3.9, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁷ cycles HE : solid \|\| grit blasted black oxidized \|\| 175 K to 350 K (-98.1 °C to 76.9 °C) RHO : solid \|\| 4 K to 1173 K (-269.1 °C to 900 °C) SIGMA : solid \|\| 4 K to 1173 K (-269.1 °C to 900 °C)
304 Cu (WNr 1.4567) (ISO/EN/DIN X3CrNiCu1894) (JIS SUSXM7) (AISI 304Cu) (AFNOR Z3CNU18-10) (GB & GB/T 0Cr18Ni9Cu3)	TC : solid \|\| 1 K to 1700 K (-272.1 °C to 1426.8 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C)
304L (UNS S30403) (WNr 1.4306/1.4307) (ISO/EN/DIN X2CrNi18-9/X2CrNi19-11) (JIS SUS304L) (ASTM A167/A182/A193/A213/A276/A314/A320/A479) (SAE J405) (AMS 5511/5639/5647/5697) (AFNOR Z2CN18-10/Z3CN18-10/Z3CN19-10M) (GB & GB/T 00Cr19Ni10)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) TC : solid \|\| 1 K to 1700 K (-272.1 °C to 1426.8 °C) TD : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) UTS : 50% cold-rolled \|\| unnotched, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 50% cold-rolled \|\| unnotched, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 50% cold-rolled \|\| notched, K_t = 3.2, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 50% cold-rolled \|\| notched, K_t = 3.2, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 50% cold-rolled \|\| notched, K_t = 6.3, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 50% cold-rolled \|\| notched, K_t = 6.3, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 50% cold-rolled \|\| notched, K_t = 19, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 50% cold-rolled \|\| notched, K_t = 19, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 50% cold-rolled \|\| weld joint, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) UTS : 50% cold-rolled \|\| weld joint, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) YS : 50% cold-rolled \|\| unnotched, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) YS : 50% cold-rolled \|\| unnotched, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) %El : 60% cold-rolled \|\| unnotched, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) %El : 60% cold-rolled \|\| unnotched, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) %El : 60% cold-rolled \|\| weld joint, longitudinal \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) %El : 60% cold-rolled \|\| weld joint, transverse \|\| 20 K to 299 K (-253.1 °C to 25.4 °C) FEN : solution annealed at mill \|\| tested at 4 °K (-269.1 °C), R = -1, axial, total strain range \|\| 200 cycles to 4x10⁴ cycles FEN : solution annealed at mill \|\| tested at 78 °K (-195.1 °C), R = -1, axial, total strain range \|\| 100 cycles to 1.6x10⁵ cycles FSN : butt weld \|\| tested at 110 °K (-163 °C), PS=2.3%, R = 0.1, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : butt weld \|\| tested at 110 °K (-163 °C), PS=50%, R = 0.1, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles FSN : butt weld \|\| tested at 110 °K (-163 °C), PS=97.7%, R = 0.1, maximum stress \|\| 5x10³ cycles to 2x10⁶ cycles RHO : solid \|\| 1 K to 1672 K (-272.1 °C to 1398.8 °C) SIGMA : solid \|\| 1 K to 1672 K (-272.1 °C to 1398.8 °C)
304LN (UNS S30453) (WNr 1.4311) (ISO/EN/DIN X2CrNiN18-10) (JIS SUS304LN) (AFNOR Z2CN18-10Az/Z3CN18-10Az) (GB & GB/T 00Cr18Ni10N)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) TC : solid \|\| 1 K to 1700 K (-272.1 °C to 1426.8 °C) TD : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) HE : solid \|\| grit blasted black oxidized \|\| 175 K to 350 K (-98.1 °C to 76.9 °C)
304H (UNS S30409) (WNr 1.4301/1.4948) (ISO/EN/DIN X5CrNi18-10) (JIS SUS304) (AFNOR Z6CN18-09) (GB & GB/T 1Cr18Ni9)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) TC : solid \|\| 1 K to 1700 K (-272.1 °C to 1426.8 °C) TD : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) HE : solid \|\| grit blasted black oxidized \|\| 175 K to 350 K (-98.1 °C to 76.9 °C)
Super 304H (304HCu) (UNS S30432) (WNr 1.4907) (ISO/EN/DIN X10CrNiCuNb189) (ASTM A213)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) TC : solid \|\| 1 K to 1700 K (-272.1 °C to 1426.8 °C) TD : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) HE : solid \|\| grit blasted black oxidized \|\| 175 K to 350 K (-98.1 °C to 76.9 °C)
305 (UNS S30500) (WNr 1.4303) (ISO/EN/DIN X4CrNi18-12) (JIS SUS305J1) (ASTM A167/A193/A240/A249/A314/A320/A473/A580) (AISI 305) (SAE J405) (AMS 5514/5685) (AFNOR Z1CN18-12) (GB & GB/T 1Cr18Ni12)	SH : solid \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : annealed \|\| 20 K to 1089 K (-253.1 °C to 815.6 °C) YS : annealed \|\| 20 K to 1089 K (-253.1 °C to 815.6 °C) %El : annealed \|\| 20 K to 1089 K (-253.1 °C to 815.6 °C)
308 (UNS S30800) (WNr 1.4303) (AISI 308) (AFNOR Z1CN18-12) (GB & GB/T 1Cr18Ni12)	UTS : 15% cold-drawn \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : 15% cold-drawn \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : 15% cold-drawn \|\| 20 K to 300 K (-253.1 °C to 26.9 °C)
310 (UNS S31000) (WNr 1.4841/1.4845) (ISO/EN/DIN X12CrNi25-20/X12CrNi25-21) (JIS SUH310) (ASTM A167) (AISI 310) (SAE 303010) (AFNOR Z12CN25.20) (GB & GB/T 0Cr25Ni20/2Cr25Ni20)	D : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) DLL : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) MTE : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1144 K (-268.1 °C to 870.9 °C) G : solid \|\| 5 K to 1144 K (-268.1 °C to 870.9 °C) v : solid \|\| 5 K to 1144 K (-268.1 °C to 870.9 °C) K : solid \|\| 5 K to 1144 K (-268.1 °C to 870.9 °C) TC : solid \|\| 1 K to 1023 K (-272.1 °C to 750 °C) SH : solid \|\| 4 K to 1173 K (-269.1 °C to 900 °C) SSC : annealed at 1422 °K (1149 °C), plates \|\| tested at 4 °K (-269.1 °C), 1.67x10^-⁴/s \|\| 0 to 0.8 mm/mm strain SSC : annealed at 1422 °K (1149 °C), plates \|\| tested at 77 °K (-196.1 °C), 1.67x10^-⁴/s \|\| 0 to 1.18 mm/mm strain SSC : annealed at 1422 °K (1149 °C), plates \|\| tested at 168 °K (-105 °C), 1.67x10^-⁴/s \|\| 0 to 1.4 mm/mm strain UTS : annealed \|\| 4 K to 1144 K (-269.1 °C to 870.9 °C) UTS : 75% cold-rolled \|\| longitudinal \|\| 20 K to 298 K (-253.1 °C to 25 °C) UTS : 75% cold-rolled \|\| transverse \|\| 20 K to 298 K (-253.1 °C to 25 °C) YS : annealed \|\| 20 K to 1144 K (-253.1 °C to 870.9 °C) YS : 75% cold-rolled \|\| longitudinal \|\| 20 K to 298 K (-253.1 °C to 25 °C) YS : 75% cold-rolled \|\| transverse \|\| 20 K to 298 K (-253.1 °C to 25 °C) %El : annealed \|\| 4 K to 1253 K (-269.1 °C to 980 °C) %El : 75% cold-rolled \|\| longitudinal \|\| 20 K to 298 K (-253.1 °C to 25 °C) %El : 75% cold-rolled \|\| transverse \|\| 20 K to 298 K (-253.1 °C to 25 °C) FEN : mill annealed & pickled \|\| tested at 4 °K (-269.1 °C), R = -1, axial, total strain range \|\| 40 cycles to 6x10⁴ cycles FEN : mill annealed & pickled \|\| tested at 78 °K (-195.1 °C), R = -1, axial, total strain range \|\| 100 cycles to 6x10⁵ cycles RHO : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) SIGMA : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C)
310S (UNS S31008) (WNr 1.4842/1.4845) (ISO/EN/DIN X12CrNi25-20/X8CrNi25-21) (JIS SUS310/SUS310S) (ASTM A167/A240/A240M/A276/A314) (AISI 310S) (SAE 30310S/J405) (AMS 5521/5572/5577/5651) (AFNOR Z12CN25-20/Z8CN25-20) (GB & GB/T 0Cr25Ni20)	SH : solid \|\| 4 K to 1367 K (-269.1 °C to 1093.4 °C) RHO : solid \|\| 10 K to 1144 K (-263.1 °C to 870.9 °C) SIGMA : solid \|\| 10 K to 1144 K (-263.1 °C to 870.9 °C)
316 (UNS S31600) (WNr 1.4401/1.4436) (ISO/EN/DIN X3CrNiMo17-13-3/X5CrNiMo17-12-2) (JIS SUS316) (ASTM A182/A276/A314/A479) (AISI 316) (AMS 5648/5653) (AFNOR Z6CND17-11/Z6CND17-12/Z7CND17-11-02/Z7CND18-12-03) (GB & GB/T 0Cr17Ni12Mo2)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) K : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) TC : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) TD : solid \|\| annealed \|\| 116 K to 1255 K (-157.1 °C to 982.3 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) SSC : annealed at 1366 °K (1093 °C), plates \|\| tested at 4 °K (-269.1 °C), 1.67x10^-⁴/s \|\| 0 to 0.8 mm/mm strain SSC : annealed at 1366 °K (1093 °C), plates \|\| tested at 77 °K (-196.1 °C), 1.67x10^-⁴/s \|\| 0 to 1.15 mm/mm strain SSC : annealed at 1366 °K (1093 °C), plates \|\| tested at 168 °K (-105 °C), 1.67x10^-⁴/s \|\| 0 to 1.38 mm/mm strain SSC : annealed at 1323 °K (1050 °C), sheet \|\| tested at 123 °K (-150 °C), 0.001/s \|\| 0 to 0.4 mm/mm strain SSC : annealed at 1323 °K (1050 °C), sheet \|\| tested at 173 °K (-100 °C), 0.001/s \|\| 0 to 0.4 mm/mm strain UTS : annealed \|\| 4 K to 1144 K (-269.1 °C to 870.9 °C) YS : annealed \|\| 21 K to 923 K (-252.1 °C to 650 °C) %El : annealed \|\| 4 K to 1144 K (-269.1 °C to 870.9 °C) RHO : solid \|\| 4 K to 873 K (-269.1 °C to 600 °C) SIGMA : solid \|\| 4 K to 873 K (-269.1 °C to 600 °C)
316H (UNS S31609) (WNr 1.4401) (ASTM A213/A269/A312/A358) (GB & GB/T 0Cr17Ni12Mo2)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) K : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) TC : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) TD : solid \|\| annealed \|\| 116 K to 1255 K (-157.1 °C to 982.3 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) RHO : solid \|\| 4 K to 873 K (-269.1 °C to 600 °C) SIGMA : solid \|\| 4 K to 873 K (-269.1 °C to 600 °C)
316L (UNS S31603) (WNr 1.4404/1.4432/1.4435) (ISO/EN/DIN X2CrNiMo17-12-2/X2CrNiMo17-12-3/X2CrNiMo18-14-3) (JIS SUS316L) (ASTM A240/A666) (AISI 316L) (AMS 5507) (AFNOR Z2CND17-12/Z2CND17-13/Z2CND18-13/Z3CND17-11-02/Z3CND17-12-03/Z3CND18-14-03) (GB & GB/T 00Cr17Ni14Mo2/0Cr18Ni12Mo2Ti)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) K : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) TC : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) TD : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) RHO : solid \|\| 4 K to 873 K (-269.1 °C to 600 °C) SIGMA : solid \|\| 4 K to 873 K (-269.1 °C to 600 °C)
316LN (UNS S31653) (WNr 1.4406/1.4429) (ISO/EN/DIN X2CrNiMoN17-11-2/X2CrNiMoN17-13-3) (JIS SUS316LN) (ASTM A240) (AFNOR Z2CND17-13/Z3CND17-11Az/Z3CND17-12Az) (GB & GB/T 00Cr17Ni12Mo2N/00Cr17Ni13Mo2N)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) K : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) TC : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) TD : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) SSC : annealed \|\| tested at 123 °K (-150 °C), 0.001/s \|\| 0 to 0.4 mm/mm strain SSC : annealed \|\| tested at 173 °K (-100 °C), 0.001/s \|\| 0 to 0.4 mm/mm strain UTS : annealed \|\| annealed at 1339 °K (1066 °C) for 1 h, water quenched \|\| 200 K to 478 K (-73.1 °C to 204.5 °C) UTS : annealed \|\| annealed at 1323 °K (1050 °C) for 0.5 h \|\| 123 K to 823 K (-150.1 °C to 550 °C) UTS : as-rolled \|\| 12.7 mm (0.5 inch) diameter bar \|\| 200 K to 478 K (-73.1 °C to 204.5 °C) UTS : 20% cold-rolled \|\| 1 mm (0.0394 inch) thick sheet \|\| 123 K to 823 K (-150.1 °C to 550 °C) YS : annealed \|\| annealed at 1339 °K (1066 °C) for 1 h, water quenched \|\| 200 K to 478 K (-73.1 °C to 204.5 °C) YS : annealed \|\| annealed at 1323 °K (1050 °C) for 0.5 h \|\| 123 K to 823 K (-150.1 °C to 550 °C) YS : as-rolled \|\| 12.7 mm (0.5 inch) diameter bar \|\| 200 K to 478 K (-73.1 °C to 204.5 °C) YS : 20% cold-rolled \|\| 1 mm (0.0394 inch) thick sheet \|\| 123 K to 823 K (-150.1 °C to 550 °C) %El : annealed \|\| annealed at 1339 °K (1066 °C) for 1 h, water quenched \|\| 200 K to 478 K (-73.1 °C to 204.5 °C) %El : as-rolled \|\| 12.7 mm (0.5 inch) diameter bar \|\| 200 K to 478 K (-73.1 °C to 204.5 °C) RHO : solid \|\| 4 K to 873 K (-269.1 °C to 600 °C) SIGMA : solid \|\| 4 K to 873 K (-269.1 °C to 600 °C)
316LS / 316LVM (UNS S31653) (WNr 1.4406/1.4429) (ISO/EN/DIN X2CrNiMoN17-11-2/X2CrNiMoN17-13-3) (ASTM A240/F138) (AFNOR Z2CND17-13/Z3CND17-11Az) (GB & GB/T 00Cr17Ni12Mo2N/00Cr17Ni13Mo2N)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) K : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) TC : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) TD : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C)
316NG (UNS S31600) (WNr 1.4401) (ISO/EN/DIN X5CrNiMo17-12-2) (GB & GB/T 0Cr17Ni12Mo2)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) K : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) TC : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) TD : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C)
316 Ti (UNS S31635) (WNr 1.4571) (ISO/EN/DIN X6CrNiMoTi17-12-2) (JIS SUS316Ti) (AFNOR Z6CNDT17-12) (GB & GB/T 0Cr18Ni12Mo2Ti/1Cr18Ni12Mo3Ti)	SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C)
Alloy D9	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) K : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C)
CF-8M (UNS S31600) (WNr 1.4401) (ISO/EN/DIN X5CrNiMo17-12-2) (GB & GB/T 0Cr17Ni12Mo2)	CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) E : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) G : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) v : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) K : solid \|\| 5 K to 1173 K (-268.1 °C to 900 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C)
317 (UNS S31700) (WNr 1.4449) (ISO/EN/DIN X5CrNiMo17-13/X5CrNiMo18-15-4) (JIS SUS317) (ASTM A182/A213/A240/A249/A276/A312/A358/A376/A403/A430) (AISI 317) (AFNOR Z8CND18.10.3M) (GB & GB/T 0Cr19Ni13Mo3)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) TC : solid \|\| 1 K to 1644 K (-272.1 °C to 1370.8 °C) SH : solid \|\| 4 K to 873 K (-269.1 °C to 600 °C) RHO : solid \|\| 1 K to 1644 K (-272.1 °C to 1370.8 °C) SIGMA : solid \|\| 1 K to 1644 K (-272.1 °C to 1370.8 °C)
317L (UNS S31703) (WNr 1.4438) (ISO/EN/DIN X2CrNiMo18-15-4/X2CrNiMoN18-15-4) (JIS SUS317L) (ASTM A167/A240) (AISI 317L) (AFNOR Z2CND19-15/Z3CND19-15-04) (GB & GB/T 00Cr19Ni13Mo3)	D : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) DLL : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) MTE : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) CTE : solid \|\| 10 K to 300 K (-263.1 °C to 26.9 °C) SH : solid \|\| 4 K to 873 K (-269.1 °C to 600 °C)
321 (UNS S32100) (WNr 1.4541) (ISO/EN/DIN X6CrNiTi18-10) (JIS SUS321) (ASTM A167/A182/A193) (AISI 321) (SAE J405) (AMS 5510/5557/5570) (AFNOR Z6CNT18-10) (GB & GB/T 0Cr18Ni10Ti/1Cr18Ni11Ti/H0Cr20Ni10Ti)	D : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) DLL : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) MTE : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) E : solid \|\| 0 K to 1089 K (-273.1 °C to 815.6 °C) TC : solid \|\| 1 K to 1672 K (-272.1 °C to 1398.8 °C) UTS : mill annealed \|\| 20 K to 293 K (-253.1 °C to 20 °C) YS : mill annealed \|\| 20 K to 293 K (-253.1 °C to 20 °C) %El : mill annealed \|\| 20 K to 293 K (-253.1 °C to 20 °C) FSN : annealed \|\| tested at 77 °K (-196.1 °C), R = -1, axial, maximum stress \|\| 1x10⁴ cycles to 4x10⁶ cycles FSN : annealed \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 800 cycles to 2x10⁶ cycles FSN : annealed \|\| tested at 77 °K (-196.1 °C), R = -1, K_t = 3.5, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : annealed \|\| tested at 20 °K (-253.1 °C), R = -1, K_t = 3.5, axial, maximum stress \|\| 400 cycles to 2x10⁶ cycles FSN : annealed \|\| tested at 77 °K (-196.1 °C), R = -1, TIG welded, axial, maximum stress \|\| 1x10³ cycles to 4x10⁶ cycles FSN : annealed \|\| tested at 20 °K (-253.1 °C), R = -1, TIG welded, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles NE : solid \|\| polished to 6 micro-inch RMS \|\| 85 K to 1253 K (-188.1 °C to 980 °C) NE : solid \|\| slightly oxidized \|\| 76 K to 1163 K (-197.1 °C to 890 °C) RHO : solid \|\| 4 K to 1173 K (-269.1 °C to 900 °C) SIGMA : solid \|\| 4 K to 1173 K (-269.1 °C to 900 °C)
321H (UNS S32109) (WNr 1.4541/1.4878) (ISO/EN/DIN X6CrNiTi18-10/Z12CrNiTi189) (JIS SUS321) (AFNOR Z6CNT18-10/Z6CNT18-12(B)) (GB & GB/T 0Cr18Ni10Ti/1Cr18Ni9Ti)	D : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) DLL : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) MTE : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) E : solid \|\| 0 K to 1089 K (-273.1 °C to 815.6 °C)
347 (UNS S34700) (WNr 1.4550) (ISO/EN/DIN X6CrNiNb18-10) (JIS SUS347) (ASTM A167/A182/A193/A479) (AISI 347) (SAE J405) (AMS 55125556) (AFNOR Z6CNNb18-10) (GB & GB/T 0Cr18Ni11Nb)	D : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) DLL : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) MTE : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) E : solid \|\| 80 K to 1144 K (-193.1 °C to 870.9 °C) TC : solid \|\| annealed \|\| 0 K to 1665 K (-273.1 °C to 1392 °C) TD : solid \|\| annealed \|\| 116 K to 1255 K (-157.1 °C to 982.3 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) SSC : annealed at 1366 °K (1093 °C), plates \|\| tested at 4 °K (-269.1 °C), 1.67x10^-⁴/s \|\| 0 to 0.67 mm/mm strain SSC : annealed at 1366 °K (1093 °C), plates \|\| tested at 77 °K (-196.1 °C), 1.67x10^-⁴/s \|\| 0 to 0.87 mm/mm strain SSC : annealed at 1366 °K (1093 °C), plates \|\| tested at 168 °K (-105 °C), 1.67x10^-⁴/s \|\| 0 to 1.1 mm/mm strain UTS : stabilized at 1366 °K (1093 °C) \|\| 20 K to 1089 K (-253.1 °C to 815.6 °C) UTS : mill annealed \|\| 20 K to 527 K (-253.1 °C to 253.9 °C) UTS : 10% cold-drawn \|\| 17 K to 296 K (-256.1 °C to 22.9 °C) YS : stabilized at 1366 °K (1093 °C) \|\| 20 K to 1089 K (-253.1 °C to 815.6 °C) YS : annealed \|\| 20 K to 529 K (-253.1 °C to 255.9 °C) YS : 10% cold-drawn \|\| 20 K to 296 K (-253.1 °C to 22.9 °C) %El : annealed \|\| 20 K to 533 K (-253.1 °C to 260 °C) %El : 10% cold-drawn \|\| 20 K to 296 K (-253.1 °C to 22.9 °C) FEN : annealed sheet \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum strain \|\| 3x10⁴ cycles to 1.1x10⁶ cycles FEN : annealed sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum strain \|\| 2.4x10⁴ cycles to 1.4x10⁶ cycles FEN : annealed sheet \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum strain \|\| 3.7x10⁴ cycles to 6.6x10⁵ cycles FSN : annealed sheet \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 3x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 3x10⁴ cycles to 2x10⁶ cycles FSN : annealed sheet \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 5x10⁴ cycles to 8x10⁵ cycles FSN : annealed sheet, K_t = 3.2 \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet, K_t = 3.2 \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet, K_t = 3.2 \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet, K_t = 6.4 \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet, K_t = 6.4 \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet, K_t = 6.4 \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles NE : solid \|\| polished \|\| 88 K to 1083 K (-185.1 °C to 810 °C) RHO : solid \|\| 4 K to 1073 K (-269.1 °C to 800 °C) SIGMA : solid \|\| 4 K to 1073 K (-269.1 °C to 800 °C)
348 (UNS S34800) (ASTM A167/A182/A213/A240/A249/A269/A276/A312/A314) (AISI 348) (AFNOR Z6CNNb18.10) (GB & GB/T 1Cr19Ni11Nb)	E : solid \|\| 80 K to 1089 K (-193.1 °C to 815.6 °C) SH : solid \|\| 4 K to 1255 K (-269.1 °C to 982.3 °C)
403 (UNS S40300) (WNr 1.4004/1.4024) (ISO/EN/DIN X10Cr12/X15Cr13) (JIS SUS403) (ASTM A176/A276/A314/A473) (AISI 403/614) (AFNOR Z12C13M) (GB & GB/T 1Cr12)	SH : solid \|\| 100 K to 1500 K (-173.1 °C to 1226.8 °C)
410 (UNS S41000) (WNr 1.4006) (ISO/EN/DIN X10Cr13/X12Cr13) (JIS SUS410) (ASTM A176/A182/A276/A479/A493/A580/F899) (AISI 410) (SAE J405) (AMS 5504/5505/5613) (AFNOR Z10C13/Z13C13) (GB & GB/T 1Cr12)	D : solid \|\| 0 K to 921 K (-273.1 °C to 647.9 °C) DLL : solid \|\| 0 K to 921 K (-273.1 °C to 647.9 °C) MTE : solid \|\| 0 K to 921 K (-273.1 °C to 647.9 °C) E : solid \|\| 20 K to 1173 K (-253.1 °C to 900 °C) TC : solid \|\| 1 K to 1600 K (-272.1 °C to 1326.8 °C) RHO : solid \|\| 4 K to 973 K (-269.1 °C to 700 °C) SIGMA : solid \|\| 4 K to 973 K (-269.1 °C to 700 °C)
416 (UNS S41600) (WNr 1.4005) (ISO/EN/DIN X12CrS13) (JIS SUS416) (ASTM A194/A314/A473/A581/A582) (AISI 416) (SAE J405) (AMS 5610) (AFNOR Z12C13/Z6C13) (GB & GB/T 1Cr13/Y1Cr13)	D : solid \|\| 0 K to 780 K (-273.1 °C to 506.9 °C) DLL : solid \|\| 0 K to 780 K (-273.1 °C to 506.9 °C) MTE : solid \|\| 0 K to 780 K (-273.1 °C to 506.9 °C) UTS : heat-treated \|\| 20 K to 293 K (-253.1 °C to 20 °C) YS : heat-treated \|\| 20 K to 293 K (-253.1 °C to 20 °C) %El : heat-treated \|\| 20 K to 293 K (-253.1 °C to 20 °C) RHO : solid \|\| 4 K to 1173 K (-269.1 °C to 900 °C) SIGMA : solid \|\| 4 K to 1173 K (-269.1 °C to 900 °C)
420 (UNS S42000) (WNr 1.4021/1.4028/1.4031/1.4034) (ISO/EN/DIN X20Cr13/X30Cr13/X39Cr13/X39Cr13/X40Cr14/X46Cr13) (JIS SUS420J1/SUS420J1/SUS420J2) (ASTM A276/A314/A473/A580) (AISI 420) (SAE J405) (AMS 5506/5621/7207) (AFNOR X20Cr13/Z20C13/Z33C13/Z40C14) (GB & GB/T 2Cr13/3Cr13/4C13/X20Cr13)	D : solid \|\| 20 K to 1273 K (-253.1 °C to 1000 °C) DLL : solid \|\| 20 K to 1273 K (-253.1 °C to 1000 °C) MTE : solid \|\| 20 K to 1273 K (-253.1 °C to 1000 °C) TC : solid \|\| annealed \|\| 10 K to 1200 K (-263.1 °C to 926.9 °C) TC : solid \|\| hardened \|\| 10 K to 1500 K (-263.1 °C to 1226.8 °C)
430 (UNS S43000) (WNr 1.4016) (ISO/EN/DIN X6Cr17) (JIS SUS430) (ASTM A176/A182/A240/A276/A314/A473/A479/A493/A580) (AISI 430) (SAE J405) (AMS 5503/5627) (AFNOR Z8C17) (GB & GB/T 1Cr15/1Cr17)	TC : solid \|\| annealed \|\| 1 K to 1750 K (-272.1 °C to 1476.8 °C) UTS : solid \|\| annealed \|\| 77 K to 1033 K (-196.1 °C to 760 °C) YS : solid \|\| annealed \|\| 77 K to 1033 K (-196.1 °C to 760 °C) %El : solid \|\| annealed \|\| 77 K to 1033 K (-196.1 °C to 760 °C) RHO : solid \|\| 1 K to 1750 K (-272.1 °C to 1476.8 °C) SIGMA : solid \|\| 1 K to 1750 K (-272.1 °C to 1476.8 °C)
440C (UNS S44004) (WNr 1.3544/1.4125) (ISO/EN/DIN X105CrMo17) (JIS SUS440C) (ASTM A276/A314/A473/A493/A580/A756) (AISI 440C) (SAE J405) (AMS 5618/5630/5880/7445) (AFNOR Z100CD17) (GB & GB/T 11Cr17)	D : solid \|\| 0 K to 973 K (-273.1 °C to 700 °C) DLL : solid \|\| 0 K to 973 K (-273.1 °C to 700 °C) MTE : solid \|\| 0 K to 973 K (-273.1 °C to 700 °C) RHO : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| hardened \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| hardened \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Cronidur 30 (WNr 1.4108) (ISO/EN/DIN X30CrMoN151) (SAE 5898) (AMS 5659/5898)	D : solid \|\| annealed \|\| 77 K to 394 K (-196.1 °C to 120.9 °C) D : solid \|\| as-hardened \|\| 77 K to 394 K (-196.1 °C to 120.9 °C) DLL : solid \|\| 77 K to 394 K (-196.1 °C to 120.9 °C) MTE : solid \|\| 77 K to 394 K (-196.1 °C to 120.9 °C) TC : solid \|\| high tempered \|\| 116 K to 394 K (-157.1 °C to 120.9 °C) TC : solid \|\| as-hardened \|\| 116 K to 394 K (-157.1 °C to 120.9 °C) TD : solid \|\| high tempered \|\| 116 K to 394 K (-157.1 °C to 120.9 °C) TD : solid \|\| as-hardened \|\| 116 K to 394 K (-157.1 °C to 120.9 °C) SH : solid \|\| 77 K to 394 K (-196.1 °C to 120.9 °C)
446 (UNS S44600) (WNr 1.4749/1.4762/1.4763) (ISO/EN/DIN X10CrAlSi25/X18CrN28/X8Cr24) (JIS SUH446) (ASTM A268) (AFNOR Z10C24) (GB & GB/T 2Cr25N)	NE : solid \|\| surface finish #1 \|\| 100 K to 1200 K (-173.1 °C to 926.9 °C) NE : solid \|\| surface finish #8 \|\| 100 K to 1200 K (-173.1 °C to 926.9 °C) NE : solid \|\| polished \|\| 86 K to 1153 K (-187.1 °C to 880 °C)
AM-350 (UNS S35000) (ASTM A579/A693) (AISI 633) (SAE J467) (AMS 5546/5548/5554/5745)	RHO : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| solution annealed & aged \|\| 4 K to 923 K (-269.1 °C to 650 °C) SIGMA : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| solution annealed & aged \|\| 4 K to 923 K (-269.1 °C to 650 °C)
AM-355 (UNS S35500) (ASTM A564/A579/A693/A705) (AISI 634) (SAE J467) (AMS 5547/5549/5594/5743/5744/5780)	D : solid \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C) DLL : solid \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C) MTE : solid \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C) CTE : solid \|\| 77 K to 866 K (-196.1 °C to 592.9 °C) UTS : cold-rolled & tempered, 95% martensite \|\| longitudinal \|\| 20 K to 298 K (-253.1 °C to 25 °C) UTS : cold-rolled & tempered, 95% martensite \|\| transverse \|\| 20 K to 298 K (-253.1 °C to 25 °C) YS : cold-rolled & tempered, 95% martensite \|\| longitudinal \|\| 20 K to 298 K (-253.1 °C to 25 °C) YS : cold-rolled & tempered, 95% martensite \|\| transverse \|\| 20 K to 298 K (-253.1 °C to 25 °C) %El : cold-rolled & tempered, 95% martensite \|\| longitudinal \|\| 20 K to 298 K (-253.1 °C to 25 °C) %El : cold-rolled & tempered, 95% martensite \|\| transverse \|\| 20 K to 298 K (-253.1 °C to 25 °C)
13-8 Mo PH (UNS S13800) (WNr 1.4534) (ISO/EN/DIN X3CrNiMoAl13-8-2) (ASTM A564/A693/A705/XM-13) (AMS 5629/5840/5864/5934)	E : solid \|\| in tension \|\| 199 K to 811 K (-74.1 °C to 537.9 °C) UTS : solid \|\| H1000 condition \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solid \|\| H1000 condition \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) %El : solid \|\| H1000 condition \|\| 77 K to 811 K (-196.1 °C to 537.9 °C)
15-5 PH (UNS S15500) (WNr 1.4594) (ISO/EN/DIN X5CrNiMoCuNb14-5) (ASTM A564/A693/A705/F899/XM-12) (AMS 5658/5659/5826)	D : solid \|\| 200 K to 700 K (-73.1 °C to 426.9 °C) DLL : solid \|\| H900 \|\| 200 K to 700 K (-73.1 °C to 426.9 °C) DLL : solid \|\| H1150 \|\| 200 K to 775 K (-73.1 °C to 501.9 °C) MTE : solid \|\| H900 \|\| 200 K to 700 K (-73.1 °C to 426.9 °C) MTE : solid \|\| H1150 \|\| 200 K to 775 K (-73.1 °C to 501.9 °C) CTE : solid \|\| H900 \|\| 200 K to 700 K (-73.1 °C to 426.9 °C) CTE : solid \|\| H1150 \|\| 200 K to 775 K (-73.1 °C to 501.9 °C) UTS : bar/forging \|\| H900 \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) UTS : bar/forging \|\| H925 \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) UTS : bar/forging \|\| H1025 \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) UTS : bar/forging \|\| H1075 \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) UTS : bar/forging \|\| H1100 \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) UTS : bar/forging \|\| H1150 \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) UTS : plate \|\| H1025, 4.76 mm to 15.9 mm (0.1875 inch to 0.625 inch) \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) UTS : plate \|\| H1025, 15.9 mm to 50.8 mm (0.625 inch to 2 inch) \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) UTS : plate \|\| H1025, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) YS : bar/forging \|\| H900 \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) YS : bar/forging \|\| H925 \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) YS : bar/forging \|\| H1025 \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) YS : bar/forging \|\| H1075 \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) YS : bar/forging \|\| H1100 \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) YS : bar/forging \|\| H1150 \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) YS : plate \|\| H1025, 4.76 mm to 15.9 mm (0.1875 inch to 0.625 inch) \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) YS : plate \|\| H1025, 15.9 mm to 50.8 mm (0.625 inch to 2 inch) \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) YS : plate \|\| H1025, 50.8 mm to 76.2 mm (2 inch to 3 inch) \|\| 77 K to 700 K (-196.1 °C to 426.9 °C)
15-7 Mo PH (UNS S15700) (WNr 1.4532/1.4574) (ASTM A461/A564/A579/A693/A705) (AISI 632) (SAE J476) (AMS 5520/5657/5812/5813)	NE : solid \|\| polished \|\| 44 K to 1043 K (-229.1 °C to 770 °C)
17-4 PH (UNS S17400) (WNr 1.4542/1.4548) (ISO/EN/DIN X5CrNiCuNb16-4) (JIS SUS630) (ASTM A564/A693/A705) (AISI 630) (AMS 5604/5622/5643/5825/5827/7474) (AFNOR Z6CNU17.04) (GB & GB/T 0Cr17Ni4Cu4Nb)	D : solid \|\| H900 \|\| 200 K to 700 K (-73.1 °C to 426.9 °C) D : solid \|\| H1100 \|\| 1 K to 300 K (-272.1 °C to 26.9 °C) D : solid \|\| H1150 \|\| 200 K to 700 K (-73.1 °C to 426.9 °C) DLL : solid \|\| H900 \|\| 200 K to 700 K (-73.1 °C to 426.9 °C) DLL : solid \|\| H1100 \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) DLL : solid \|\| H1150 \|\| 200 K to 700 K (-73.1 °C to 426.9 °C) MTE : solid \|\| H900 \|\| 200 K to 700 K (-73.1 °C to 426.9 °C) MTE : solid \|\| H1100 \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) MTE : solid \|\| H1150 \|\| 200 K to 700 K (-73.1 °C to 426.9 °C) CTE : solid \|\| H900 \|\| 200 K to 700 K (-73.1 °C to 426.9 °C) CTE : solid \|\| H1100 \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) CTE : solid \|\| H1150 \|\| 200 K to 700 K (-73.1 °C to 426.9 °C) SSC : H1100 \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.6 mm/mm strain SSC : H1100 \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate \|\| 0 to 0.3 mm/mm strain UTS : wrought \|\| H1100 \|\| 20 K to 293 K (-253.1 °C to 20 °C) YS : wrought \|\| H1100 \|\| 20 K to 293 K (-253.1 °C to 20 °C) %El : wrought \|\| H1100 \|\| 20 K to 293 K (-253.1 °C to 20 °C) RHO : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C)
17-7 PH (UNS S17700) (WNr 1.4568) (ISO/EN/DIN X7CrNiAl17-7) (JIS SUS631) (ASTM A313/A564/A579/A693/A705) (AISI 631) (AMS 5528/5529/5568/5644/5678/5824) (AFNOR Z3CNU18-09FF) (GB & GB/T 0Cr17Ni7Al)	D : solid \|\| 0 K to 589 K (-273.1 °C to 315.6 °C) DLL : solid \|\| 0 K to 589 K (-273.1 °C to 315.6 °C) MTE : solid \|\| 0 K to 589 K (-273.1 °C to 315.6 °C) UTS : solid \|\| TH 1050 \|\| 20 K to 923 K (-253.1 °C to 650 °C) YS : solid \|\| TH 1050 \|\| 76 K to 923 K (-197.1 °C to 650 °C) %El : solid \|\| TH 1050 \|\| 20 K to 923 K (-253.1 °C to 650 °C) FSN : TH 1050 \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : TH 1050 \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : TH 1050 \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : RH 950 \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : RH 950 \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : RH 950 \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 6x10³ cycles to 1x10⁶ cycles FSN : RH 950, K_t = 3 \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 1x10⁶ cycles FSN : RH 950, K_t = 3 \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 6x10³ cycles to 1x10⁶ cycles FSN : RH 950, K_t = 3 \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles NE : solid \|\| polished to 2 micro-inch RMS \|\| 55 K to 993 K (-218.1 °C to 720 °C) NE : solid \|\| polished to 15 micro-inch RMS \|\| 55 K to 973 K (-218.1 °C to 700 °C)
Gall-tough (UNS S20161)	UTS : annealed & quenched \|\| 200 K to 1144 K (-73.1 °C to 870.9 °C) YS : annealed & quenched \|\| 200 K to 1144 K (-73.1 °C to 870.9 °C) %El : annealed & quenched \|\| 200 K to 1144 K (-73.1 °C to 870.9 °C)
Gall-tough Plus (UNS S20162/S21800)	UTS : annealed & quenched \|\| 200 K to 1144 K (-73.1 °C to 870.9 °C) YS : annealed & quenched \|\| 200 K to 1144 K (-73.1 °C to 870.9 °C) %El : annealed & quenched \|\| 200 K to 1144 K (-73.1 °C to 870.9 °C)
ATI S240 alloy (UNS S11900) (AMS 5929)	UTS : 102 mm (4 inch) round forged bar \|\| H950 \|\| 200 K to 713 K (-73.1 °C to 440 °C) UTS : 102 mm (4 inch) round forged bar \|\| H1000 \|\| 200 K to 840 K (-73.1 °C to 566.9 °C) YS : 102 mm (4 inch) round forged bar \|\| H950 \|\| 200 K to 713 K (-73.1 °C to 440 °C) YS : 102 mm (4 inch) round forged bar \|\| H1000 \|\| 200 K to 840 K (-73.1 °C to 566.9 °C) %El : 102 mm (4 inch) round forged bar \|\| H950 \|\| 200 K to 713 K (-73.1 °C to 440 °C) %El : 102 mm (4 inch) round forged bar \|\| H1000 \|\| 200 K to 840 K (-73.1 °C to 566.9 °C)
Custom 450 (UNS S45000) (ASTM A564/A693/A705/A959/XM-25) (AMS 5763/5773/5863)	UTS : solid \|\| solution treated \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : solid \|\| condition H900 \|\| 77 K to 839 K (-196.1 °C to 565.9 °C) UTS : solid \|\| condition H1150 \|\| 77 K to 839 K (-196.1 °C to 565.9 °C) YS : solid \|\| solution treated \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : solid \|\| condition H900 \|\| 77 K to 839 K (-196.1 °C to 565.9 °C) YS : solid \|\| condition H1150 \|\| 77 K to 839 K (-196.1 °C to 565.9 °C) %El : solid \|\| solution treated \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : solid \|\| condition H900 \|\| 77 K to 839 K (-196.1 °C to 565.9 °C) %El : solid \|\| condition H1150 \|\| 77 K to 839 K (-196.1 °C to 565.9 °C)
Custom 455 (UNS S45500) (ASTM A313/A564/A693/A705/XM-16) (AMS 5578/5647/5860)	UTS : solid \|\| H900 \|\| 89 K to 698 K (-184.1 °C to 425 °C) UTS : solid \|\| H950 \|\| 89 K to 811 K (-184.1 °C to 537.9 °C) UTS : solid \|\| H1000 \|\| 89 K to 811 K (-184.1 °C to 537.9 °C) %El : solid \|\| H900 \|\| 89 K to 698 K (-184.1 °C to 425 °C) %El : solid \|\| H950 \|\| 89 K to 811 K (-184.1 °C to 537.9 °C) %El : solid \|\| H1000 \|\| 89 K to 811 K (-184.1 °C to 537.9 °C)
Nitronic 33 (UNS S24000) (ASTM XM-29)	D : solid \|\| 88 K to 1255 K (-185.1 °C to 982.3 °C) DLL : solid \|\| 88 K to 1255 K (-185.1 °C to 982.3 °C) MTE : solid \|\| 88 K to 1255 K (-185.1 °C to 982.3 °C) CTE : solid \|\| 88 K to 1255 K (-185.1 °C to 982.3 °C) UTS : annealed \|\| 77 K to 298 K (-196.1 °C to 25 °C) UTS : 60% cold-rolled sheet \|\| 77 K to 298 K (-196.1 °C to 25 °C) YS : annealed \|\| 77 K to 298 K (-196.1 °C to 25 °C) YS : 60% cold rolled sheet \|\| 77 K to 298 K (-196.1 °C to 25 °C) %El : annealed \|\| 77 K to 298 K (-196.1 °C to 25 °C) %El : 60% cold rolled sheet \|\| 77 K to 298 K (-196.1 °C to 25 °C)
Nitronic 40 (UNS S21900/S21904) (ASTM A276/A314/A412/A429/A473/A580) (AMS 5561)	TC : solid \|\| 118 °K (-155 °C) and below \|\| 5 K to 118 K (-268.1 °C to -155 °C) UTS : annealed \|\| sheet, strip & slab \|\| 20 K to 977 K (-253.1 °C to 704 °C) UTS : cold reduced \|\| 60% cold reduction \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) UTS : hot-rolled, rack cooled \|\| air melted \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : hot-rolled, rack cooled \|\| ESR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : hot-rolled, rack cooled \|\| VAR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : hot-rolled, rack cooled \|\| average of the 3 different processing types \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : hot-rolled, annealed, water quenched \|\| 102 mm (4 inch) square bar \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : annealed \|\| sheet, strip & slab \|\| 20 K to 977 K (-253.1 °C to 704 °C) YS : hot-rolled, rack cooled \|\| air melted \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : hot-rolled, rack cooled \|\| ESR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : hot-rolled, rack cooled \|\| VAR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : hot-rolled, rack cooled \|\| average of the 3 different processing types \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : hot-rolled, annealed, water quenched \|\| 102 mm (4 inch) square bar \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) %El : annealed \|\| sheet, strip & slab \|\| 20 K to 977 K (-253.1 °C to 704 °C) %El : hot-rolled, rack cooled \|\| air melted \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : hot-rolled, rack cooled \|\| ESR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : hot-rolled, rack cooled \|\| VAR processed \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : hot-rolled, rack cooled \|\| average of the 3 different processing types \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : hot-rolled, annealed, water quenched \|\| 102 mm (4 inch) square bar \|\| 77 K to 811 K (-196.1 °C to 537.9 °C)
Nitronic 50 (UNS S20910) (WNr 1.3964) (ISO/EN/DIN X2CrNiMnMoN25-18-6-5/X3CrNiMnMoNbN23-17-5-3) (ASTM A240/A276/A412/A479/F1314/X580/XM-19) (AMS 5764/5861)	D : solid \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C) DLL : solid \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C) MTE : solid \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C) CTE : solid \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C) SSCC : 0.001/s \|\| tested at 77 °K (-196.1 °C) \|\| 0 to 0.41 mm/mm strain SSCC : 3500/s \|\| tested at 77 °K (-196.1 °C) \|\| 0 to 0.3 mm/mm strain UTS : annealed at 1394 °K (1121 °C) \|\| 77 K to 1089 K (-196.1 °C to 815.6 °C) UTS : hot-rolled, unannealed high-strength bars \|\| 77 K to 867 K (-196.1 °C to 593.4 °C) YS : annealed at 1394 °K (1121 °C) \|\| 77 K to 1089 K (-196.1 °C to 815.6 °C) YS : hot-rolled, unannealed high-strength bars \|\| 77 K to 867 K (-196.1 °C to 593.4 °C) %El : annealed at 1394 °K (1121 °C) \|\| 77 K to 1089 K (-196.1 °C to 815.6 °C) %El : hot-rolled, unannealed high-strength bars \|\| 77 K to 867 K (-196.1 °C to 593.4 °C)
Nitronic 60 (UNS S21800) (ASTM A193/A276/A314/A351/A479/A580/A743) (AMS 5848)	E : solid \|\| 20 K to 293 K (-253.1 °C to 20 °C) UTS : bar \|\| annealed \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C) UTS : bar \|\| cold swaged 54% \|\| 77 K to 923 K (-196.1 °C to 650 °C) YS : bar \|\| annealed \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C) YS : bar \|\| cold swaged 54% \|\| 77 K to 923 K (-196.1 °C to 650 °C) %El : bar \|\| annealed \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C) %El : bar \|\| cold swaged 54% \|\| 77 K to 923 K (-196.1 °C to 650 °C)
SINOXX 4580 (WNr 1.4580) (ISO/EN/DIN X2CrNiMoN17-13-5/X6CrNiMoNb17-12-2) (JIS SUS316) (AISI 316/316Cb) (AFNOR Z6CNDNb17-12/Z6CNDNb19-13) (GB & GB/T 0Cr17Ni12Mo2)	TC : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) TD : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C) SH : solid \|\| 4 K to 1700 K (-269.1 °C to 1426.8 °C)
21 Cr - 6 Ni - 9 Mn (wt %) (UNS S21904) (ISO/EN/DIN X11CrNiMnN19-8-6) (ASTM A182/A269/A276/A312/A314/A412/A473/A479/A580/A666/A813/A814/A965) (AMS 5561/5562/5595/5656)	UTS : annealed \|\| 77 K to 977 K (-196.1 °C to 703.9 °C) YS : annealed \|\| 77 K to 977 K (-196.1 °C to 703.9 °C) %El : annealed \|\| 77 K to 977 K (-196.1 °C to 703.9 °C)
S04	SSC : as-received \|\| tested at 93.2 °K (-180 °C), 0.00167/s \|\| 0 to 0.8 mm/mm strain SSC : after 10 cycles to 1.20 GPa (174 ksi) \|\| tested at 93.2 °K (-180 °C), 0.00167/s \|\| 0 to 0.62 mm/mm strain SSC : after 10 cycles to 1.27 GPa (184 ksi) \|\| tested at 93.2 °K (-180 °C), 0.00167/s \|\| 0 to 0.54 mm/mm strain
Ni-SPAN C alloy 902 (Low expansion 43-PH) (UNS N09902) (AMS 5221C/5223C/5225C)	D : solid \|\| 0 K to 533 K (-273.1 °C to 260 °C) DLL : bar \|\| 5 h at 755 °K (482 °C) \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) DLL : average value \|\| 0 K to 533 K (-273.1 °C to 260 °C) MTE : bar \|\| 5 h at 755 °K (482 °C) \|\| 0 K to 300 K (-273.1 °C to 26.9 °C) MTE : average value \|\| 0 K to 533 K (-273.1 °C to 260 °C) E : bar \|\| 5 h at 922 °K (649 °C) \|\| 20 K to 311 K (-253.1 °C to 37.9 °C) G : bar \|\| 5 h at 922 °K (649 °C) \|\| 20 K to 311 K (-253.1 °C to 37.9 °C) v : bar \|\| 5 h at 922 °K (649 °C) \|\| 20 K to 311 K (-253.1 °C to 37.9 °C) K : bar \|\| 20 K to 311 K (-253.1 °C to 37.9 °C) TC : solid \|\| solution treated & aged \|\| 123 K to 813 K (-150.1 °C to 540 °C) SSC : solution treated & aged \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.2 mm/mm strain SSC : solution treated & aged \|\| tested at 77.6 °K (-195.6 °C), 3.3x10^-⁴/s \|\| 0 to 0.23 mm/mm strain SSC : solution treated & aged \|\| tested at 20.4 °K (-252.7 °C), 3.3x10^-⁴/s \|\| 0 to 0.25 mm/mm strain UTS : solid \|\| solution treated & aged \|\| 20 K to 311 K (-253.1 °C to 37.9 °C) YS : solid \|\| solution treated & aged \|\| 20 K to 311 K (-253.1 °C to 37.9 °C) %El : solid \|\| solution treated & aged \|\| 20 K to 311 K (-253.1 °C to 37.9 °C) FSN : solution treated & aged \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : solution treated & aged \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : solution treated & aged \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : solution treated & aged, K_t = 3.1 \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 8x10³ cycles to 1x10⁶ cycles FSN : solution treated & aged, K_t = 3.1 \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : solution treated & aged, K_t = 3.1 \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles
2003 (UNS S32003) (ASTM A240/A270/A480/A789/A790/A928)	D : solid \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 171 K to 478 K (-102.1 °C to 205 °C) DLL : solid \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 171 K to 478 K (-102.1 °C to 205 °C) MTE : solid \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 171 K to 478 K (-102.1 °C to 205 °C) CTE : solid \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 171 K to 478 K (-102.1 °C to 205 °C) UTS : sheet, strip, plate \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 183 K to 533 K (-90.1 °C to 260 °C) YS : sheet, strip, plate \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 183 K to 533 K (-90.1 °C to 260 °C) %El : sheet, strip, plate \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 183 K to 533 K (-90.1 °C to 260 °C)
2102 (UNS S82001) (ASTM A240/A480/A789/A790)	D : solid \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 163 K to 673 K (-110.1 °C to 400 °C) DLL : solid \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 163 K to 673 K (-110.1 °C to 400 °C) MTE : solid \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 163 K to 673 K (-110.1 °C to 400 °C) CTE : solid \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 163 K to 673 K (-110.1 °C to 400 °C) UTS : plate \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 182 K to 803 K (-91.1 °C to 530 °C) YS : plate \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 182 K to 803 K (-91.1 °C to 530 °C) %El : plate \|\| annealed between 1283 °K (1010 °C) & 1372 °K (1099 °C) \|\| 182 K to 803 K (-91.1 °C to 530 °C)
2205 (UNS S31803/S32205) (WNr 1.4462) (ISO/EN/DIN X2CrNiMoN22-5-3) (JIS SUS329J3L) (ASTM A240/A276/A479/A955M) (AFNOR Z2CND22-05Az) (GB & GB/T 00Cr22Ni5Mo3N)	SSC : fine grain, 0.0167/s \|\| tested at 200 °K (-73 °C), annealed \|\| 0 to 0.224 mm/mm strain UTS : rebar \|\| as-rolled \|\| 199 K to 478 K (-74.1 °C to 205 °C) UTS : rebar \|\| annealed \|\| 199 K to 478 K (-74.1 °C to 205 °C) UTS : fine grain sheet \|\| annealed \|\| 195 K to 435 K (-78.1 °C to 161.9 °C) YS : rebar \|\| as-rolled \|\| 199 K to 478 K (-74.1 °C to 205 °C) YS : rebar \|\| annealed \|\| 199 K to 478 K (-74.1 °C to 205 °C) YS : fine grain sheet \|\| annealed \|\| 195 K to 435 K (-78.1 °C to 161.9 °C) %El : rebar \|\| as-rolled \|\| 199 K to 478 K (-74.1 °C to 205 °C) %El : rebar \|\| annealed \|\| 199 K to 478 K (-74.1 °C to 205 °C) %El : fine grain sheet \|\| annealed \|\| 195 K to 435 K (-78.1 °C to 161.9 °C)
2315 (ASTM A203)	D : solid \|\| 172 K to 366 K (-101.1 °C to 92.9 °C) DLL : solid \|\| 172 K to 366 K (-101.1 °C to 92.9 °C) MTE : solid \|\| 172 K to 366 K (-101.1 °C to 92.9 °C) CTE : solid \|\| 172 K to 366 K (-101.1 °C to 92.9 °C) TC : solid \|\| normalized & tempered \|\| 123 K to 813 K (-150.1 °C to 540 °C) UTS : as-rolled \|\| 110 K to 308 K (-163.1 °C to 35 °C) UTS : normalized \|\| 110 K to 311 K (-163.1 °C to 37.9 °C) UTS : quenched & tempered \|\| 110 K to 315 K (-163.1 °C to 41.9 °C) YS : as-rolled \|\| 84 K to 312 K (-189.1 °C to 38.9 °C) YS : normalized \|\| 110 K to 308 K (-163.1 °C to 35 °C) YS : quenched & tempered \|\| 110 K to 311 K (-163.1 °C to 37.9 °C)
2330 (ASTM A203)	UTS : annealed \|\| 90 K to 300 K (-183.1 °C to 26.9 °C) UTS : normalized \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) UTS : oil quenched & tempered \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : annealed \|\| 90 K to 300 K (-183.1 °C to 26.9 °C) %El : normalized \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : oil quenched & tempered \|\| 77 K to 300 K (-196.1 °C to 26.9 °C)
2515	TC : solid \|\| normalized & tempered \|\| 125 K to 696 K (-148.1 °C to 422.9 °C)
Maraging 200 (C-type) (UNS K92810) (ASTM A538/A538M)	E : solid \|\| 75 K to 400 K (-198.1 °C to 126.9 °C) G : solid \|\| 75 K to 400 K (-198.1 °C to 126.9 °C) v : solid \|\| 75 K to 400 K (-198.1 °C to 126.9 °C) K : solid \|\| 75 K to 400 K (-198.1 °C to 126.9 °C)
Maraging 250 (C-type) (UNS K92890) (ASTM A538/A538M) (AMS 6512/6520)	D : solid \|\| 16 K to 1144 K (-257.1 °C to 870.9 °C) DLL : solid \|\| 16 K to 1144 K (-257.1 °C to 870.9 °C) MTE : solid \|\| 16 K to 1144 K (-257.1 °C to 870.9 °C) CTE : solid \|\| 16 K to 1033 K (-257.1 °C to 760 °C) E : in tension \|\| 75 K to 811 K (-198.1 °C to 537.9 °C) G : solid \|\| 75 K to 400 K (-198.1 °C to 126.9 °C) v : solid \|\| 75 K to 400 K (-198.1 °C to 126.9 °C) K : solid \|\| 75 K to 400 K (-198.1 °C to 126.9 °C) UTS : solution annealed & aged, plate \|\| longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, plate \|\| transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, sheet \|\| transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, sheet \|\| longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, bar \|\| < 102 mm (4 inch), transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, bar \|\| < 102 mm (4 inch), longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, plate \|\| longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, plate \|\| transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, sheet \|\| transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, sheet \|\| longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, bar \|\| < 102 mm (4 inch), transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, bar \|\| 102 mm (4 inch), longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C)
Maraging 300 (C-type) (UNS K93120) (ISO/EN/DIN X3NiCoMo18-8-5) (ASTM A538/A538M) (AMS 6514/6521)	D : solid \|\| 16 K to 1144 K (-257.1 °C to 870.9 °C) DLL : solid \|\| 16 K to 1144 K (-257.1 °C to 870.9 °C) MTE : solid \|\| 16 K to 1144 K (-257.1 °C to 870.9 °C) E : in tension \|\| 75 K to 811 K (-198.1 °C to 537.9 °C) G : solid \|\| 75 K to 400 K (-198.1 °C to 126.9 °C) v : solid \|\| 75 K to 400 K (-198.1 °C to 126.9 °C) K : solid \|\| 75 K to 400 K (-198.1 °C to 126.9 °C) UTS : solution annealed & aged, plate \|\| longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, plate \|\| transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, sheet \|\| longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, sheet \|\| transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, bar \|\| < 102 mm (4 inch), transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, bar \|\| < 102 mm (4 inch), longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, plate \|\| longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, plate \|\| transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, sheet \|\| longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, sheet \|\| transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, bar \|\| < 102 mm (4 inch), transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, bar \|\| < 102 mm (4 inch), longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), longitudinal \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : solution annealed & aged, bar \|\| 102 mm to 254 mm (4 inch to 10 inch), transverse \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) FEN : annealed & aged \|\| tested at 4 °K (-269.1 °C), R = -1, axial, total strain range \|\| 20 cycles to 7.3x10⁴ cycles FEN : annealed & aged \|\| tested at 78 °K (-195.1 °C), R = -1, axial, total strain range \|\| 80 cycles to 8.9x10⁴ cycles
Maraging 350 (C-type)	TC : solid \|\| data from Koniorczyk et. al., hardness HRC 37 \|\| 200 K to 1378 K (-73.1 °C to 1105 °C) SH : solid \|\| 200 K to 753 K (-73.1 °C to 480 °C)
Incoloy 330 (RA 330) (UNS N08330) (WNr 1.4864/1.4886) (ISO/EN/DIN X12NiCrSi36-16) (JIS SUH330) (ASTM B511/B512/B535/B536/B546) (AISI 330) (SAE J405/J412) (AMS 5592/5716) (AFNOR Z12NC37-18/Z12NCS35-16/Z12NCS37-18) (GB & GB/T 1Cr16Ni35)	UTS : annealed \|\| 77 K to 1433 K (-196.1 °C to 1160 °C) YS : annealed \|\| 77 K to 1477 K (-196.1 °C to 1203.8 °C) %El : annealed \|\| 77 K to 1367 K (-196.1 °C to 1093.4 °C)
Incoloy 800 (UNS N08800) (WNr 1.4876) (ISO/EN/DIN FeNi32Cr21AlTi/NW8800/X10NiCrAlTi32-20/X10NiCrAlTi32-21) (JIS NCF800) (ASTM B163/B366/B407/B408/B409/B514/B515/B564) (AMS 5871) (AFNOR Z8NC32-21)	E : solid \|\| 83 K to 1073 K (-190.1 °C to 800 °C) G : solid \|\| 83 K to 1073 K (-190.1 °C to 800 °C) v : solid \|\| 83 K to 1073 K (-190.1 °C to 800 °C) K : solid \|\| 83 K to 1073 K (-190.1 °C to 800 °C)
Incoloy 800H & 800HT (UNS N08810/N08811) (WNr 1.4958/1.4959) (ISO/EN/DIN FeNi32Cr21AlTi4/NW8810/NW8811/X10NiCrAlTi32-20/X5NiCrAlTi31-20/X8NiCrAlTi32-21) (JIS NCF800H) (ASTM B163/B407/B408/B409/B564)	E : solid \|\| 83 K to 1073 K (-190.1 °C to 800 °C) G : solid \|\| 83 K to 1073 K (-190.1 °C to 800 °C) v : solid \|\| 83 K to 1073 K (-190.1 °C to 800 °C) K : solid \|\| 83 K to 1073 K (-190.1 °C to 800 °C)
Incoloy 27-7MO (UNS S31277)	D : solid \|\| 83 K to 973 K (-190.1 °C to 700 °C) DLL : solid \|\| 83 K to 973 K (-190.1 °C to 700 °C) MTE : solid \|\| 83 K to 973 K (-190.1 °C to 700 °C) UTS : annealed \|\| 77 K to 727 K (-196.1 °C to 453.9 °C) YS : annealed \|\| 77 K to 727 K (-196.1 °C to 453.9 °C) %El : annealed \|\| 77 K to 727 K (-196.1 °C to 453.9 °C)
Incoloy A-286 (UNS S66286) (WNr 1.4980) (ISO/EN/DIN X5NiCrTi2615) (JIS SUH660) (ASTM A453/A638) (AISI 660) (SAE J467) (AMS 5525/5728/5731/5732/5734/5735/5736/5737/5804/5805/5858/5895)	D : solid \|\| 22 K to 1144 K (-251.1 °C to 870.9 °C) DLL : solid \|\| 22 K to 1144 K (-251.1 °C to 870.9 °C) MTE : solid \|\| 22 K to 1144 K (-251.1 °C to 870.9 °C) CTE : solid \|\| 144 K to 1144 K (-129.1 °C to 870.9 °C) E : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) G : solid \|\| 0 K to 1089 K (-273.1 °C to 815.6 °C) v : solid \|\| 0 K to 1089 K (-273.1 °C to 815.6 °C) K : solid \|\| 0 K to 1089 K (-273.1 °C to 815.6 °C) TC : solid \|\| precipitation hardened \|\| 4 K to 1000 K (-269.1 °C to 726.9 °C) TC : solid \|\| solution annealed \|\| 4 K to 1600 K (-269.1 °C to 1326.8 °C) SSC : solution treated at 1255 °K (982 °C), air cooled, aged at 1005 °K (732 °C) \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.22 mm/mm strain SSC : solution treated at 1255 °K (982 °C), air cooled, aged at 1005 °K (732 °C) \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate \|\| 0 to 0.28 mm/mm strain SSC : solution treated at 1255 °K (982 °C), air cooled, aged at 1005 °K (732 °C) \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate \|\| 0 to 0.29 mm/mm strain UTS : solution treated at 1255 °K (982 °C), oil quenched, aged at 991 °K (718 °C) \|\| bar \|\| 22 K to 1089 K (-251.1 °C to 815.6 °C) UTS : solution treated at 1255 °K (982 °C), oil quenched, aged at 991 °K (718 °C) \|\| sheet \|\| 22 K to 923 K (-251.1 °C to 650 °C) YS : solution treated at 1255 °K (982 °C), oil quenched, aged at 991 °K (718 °C) \|\| bar \|\| 22 K to 923 K (-251.1 °C to 650 °C) YS : solution treated at 1255 °K (982 °C), oil quenched, aged at 991 °K (718 °C) \|\| sheet \|\| 22 K to 923 K (-251.1 °C to 650 °C) FSN : solution treated, unnotched \|\| tested at 77 °K (-196.1 °C), R = -1, axial, maximum stress \|\| 100 cycles to 4x10⁶ cycles FSN : solution treated, unnotched \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 400 cycles to 2x10⁶ cycles FSN : solution treated, TIG welded \|\| tested at 77 °K (-196.1 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : solution treated, TIG welded \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : solution treated & aged, K_t = 2 \|\| tested at 77 °K (-196.1 °C), R = 0, axial, maximum stress \|\| 2x10³ cycles to 2x10⁵ cycles FSN : solution treated, K_t = 3.5 \|\| tested at 77 °K (-196.1 °C), R = -1, axial, maximum stress \|\| 2x10³ cycles to 4x10⁶ cycles FSN : solution treated, K_t = 3.5 \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles
Incoloy DS (WNr 1.4862)	UTS : solid \|\| hot-rolled plate + HT & welded \|\| 77 K to 1273 K (-196.1 °C to 1000 °C) UTS : solid \|\| hot-rolled plate (HT 1020) \|\| 77 K to 1273 K (-196.1 °C to 1000 °C) UTS : solid \|\| hot-rolled plate (HT 1150) \|\| 77 K to 1273 K (-196.1 °C to 1000 °C) YS : solid \|\| hot-rolled plate + HT & welded \|\| 77 K to 1273 K (-196.1 °C to 1000 °C) YS : solid \|\| hot-rolled plate (HT 1020) \|\| 77 K to 1273 K (-196.1 °C to 1000 °C) YS : solid \|\| hot-rolled plate (HT 1150) \|\| 77 K to 1273 K (-196.1 °C to 1000 °C) %El : solid \|\| hot-rolled plate + HT & welded \|\| 77 K to 1273 K (-196.1 °C to 1000 °C) %El : solid \|\| hot-rolled plate (HT 1020) \|\| 77 K to 1273 K (-196.1 °C to 1000 °C) %El : solid \|\| hot-rolled plate (HT 1150) \|\| 77 K to 1273 K (-196.1 °C to 1000 °C)
Haynes Multimet (N-155) (UNS R30155) (WNr 1.4971) (JIS SUH661) (ASTM A567/A639) (AISI 661) (AMS 5376/5531/5532/5585/5769/5794/5795)	NE : solid \|\| polished \|\| 85 K to 1243 K (-188.1 °C to 970 °C) NE : solid \|\| oxidized \|\| 85 K to 1193 K (-188.1 °C to 920 °C)
38MnVS (ISO/EN/DIN 38MnVS)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
25MnCrVS (ISO/EN/DIN 25MnCrVS)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) SH : solid \|\| 73 K to 1000 K (-200.1 °C to 726.9 °C)
25MnCrSiVB6 (ISO/EN/DIN 25MnCrSiVB6)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) SH : solid \|\| 73 K to 1000 K (-200.1 °C to 726.9 °C)
Fe - 3 Mn (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
TRIP/TWIP 15 Cr - 6 Mn - 6 Ni (wt %)	UTS : cast & homogenized \|\| 77 K to 573 K (-196.1 °C to 300 °C) YS : cast & homogenized \|\| 77 K to 573 K (-196.1 °C to 300 °C) %El : cast & homogenized \|\| 77 K to 573 K (-196.1 °C to 300 °C)
A128-E2 Hadfield steel (Fe - 13 Mn (wt %)) (WNr 1.3401) (ISO/EN/DIN X120Mn12)	SSC : austenitized & quenched \|\| tested at 77 °K (-196.1 °C), 8.33x10^-⁴/s \|\| 0 to 0.7 mm/mm strain SSC : austenitized & quenched \|\| tested at 173 °K (-100 °C), 8.33x10^-⁴/s \|\| 0 to 0.27 mm/mm strain SSC : austenitized & quenched \|\| tested at 194 °K (-79 °C), 8.33x10^-⁴/s \|\| 0 to 0.28 mm/mm strain SSCC : austenitized & quenched \|\| tested at 173 °K (-100 °C), 6.67x10^-⁴/s \|\| 0 to 0.24 mm/mm strain YS : solid \|\| 77 K to 523 K (-196.1 °C to 250 °C) YSC : solid \|\| 173 K to 523 K (-100.1 °C to 250 °C)
Fe - 22 Mn (wt %)	FSN : axial fatigue \|\| tested at 110 °K (-163 °C), R = 0.1, stress range \|\| 2.4x10⁴ cycles to 1x10⁷ cycles
Fe - 24 Mn (wt %)	FSN : axial fatigue \|\| tested at 110 °K (-163 °C), R = 0.1, stress range \|\| 2.4x10⁴ cycles to 1x10⁷ cycles
Fe - 30 Mn - 1 C (wt %)	D : solid \|\| 4 K to 300 K (-269.1 °C to 27 °C) DLL : solid \|\| 4 K to 300 K (-269.1 °C to 27 °C) MTE : solid \|\| 4 K to 300 K (-269.1 °C to 27 °C) CTE : solid \|\| 4 K to 300 K (-269.1 °C to 27 °C) TC : solid \|\| 4 K to 300 K (-269.1 °C to 27 °C) TD : solid \|\| 4 K to 300 K (-268.9 °C to 27 °C) SH : solid \|\| 4 K to 300 K (-268.9 °C to 27 °C)
Fe - 35 Mn (wt %)	SSC : 0.45 microns \|\| tested at 93.2 °K (-180 °C), 0.001/s \|\| 0 to 0.178 mm/mm strain SSC : 2 microns \|\| tested at 93.2 °K (-180 °C), 0.001/s \|\| 0 to 0.373 mm/mm strain SSC : 2.3 microns \|\| tested at 93.2 °K (-180 °C), 0.001/s \|\| 0 to 0.47 mm/mm strain SSC : 3.8 microns \|\| tested at 93.2 °K (-180 °C), 0.001/s \|\| 0 to 0.161 mm/mm strain SSC : 10.8 microns \|\| tested at 93.2 °K (-180 °C), 0.001/s \|\| 0 to 0.6 mm/mm strain SSC : 21 microns \|\| tested at 93.2 °K (-180 °C), 0.001/s \|\| 0 to 0.58 mm/mm strain
Fe - 0.5 Au (at %)	YS : quenched from 1273 °K (1000 °C) \|\| 78 K to 300 K (-195.1 °C to 27 °C)
Fe - 8 Co (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 50 Co (at %)	SSCC : disordered \|\| tested at 77 °K (-196.1 °C), 7.6x10^-⁵/s \|\| 0 to 0.68 mm/mm strain SSCC : disordered \|\| tested at 100 °K (-173 °C), 7.6x10^-⁵/s \|\| 0 to 0.68 mm/mm strain SSCC : disordered \|\| tested at 123 °K (-150 °C), 7.6x10^-⁵/s \|\| 0 to 0.68 mm/mm strain SSCC : disordered \|\| tested at 170 °K (-103 °C), 7.6x10^-⁵/s \|\| 0 to 0.68 mm/mm strain SSCC : ordered \|\| tested at 77 °K (-196.1 °C), 7.6x10^-⁵/s \|\| 0 to 0.49 mm/mm strain SSCC : ordered \|\| tested at 100 °K (-173 °C), 7.6x10^-⁵/s \|\| 0 to 0.415 mm/mm strain SSCC : ordered \|\| tested at 123 °K (-150 °C), 7.6x10^-⁵/s \|\| 0 to 0.42 mm/mm strain SSCC : ordered \|\| tested at 170 °K (-103 °C), 7.6x10^-⁵/s \|\| 0 to 0.43 mm/mm strain YSC : disordered \|\| 77 K to 443 K (-196.1 °C to 170 °C) YSC : ordered \|\| 77 K to 588 K (-196.1 °C to 315 °C)
Fe - 10 Cr (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 1.67 Cu (at %)	YS : quenched from 1273 °K (1000 °C), aged at 748 °K (475 °C) \|\| not aged \|\| 77 K to 300 K (-196.1 °C to 27 °C) YS : quenched from 1273 °K (1000 °C), aged at 748 °K (475 °C) \|\| aged 0.5 h \|\| 77 K to 300 K (-196.1 °C to 27 °C) YS : quenched from 1273 °K (1000 °C), aged at 748 °K (475 °C) \|\| aged 1 h \|\| 77 K to 300 K (-196.1 °C to 27 °C) YS : quenched from 1273 °K (1000 °C), aged at 748 °K (475 °C) \|\| aged 2 h \|\| 77 K to 300 K (-196.1 °C to 27 °C) YS : quenched from 1273 °K (1000 °C), aged at 748 °K (475 °C) \|\| aged 3 h \|\| 77 K to 300 K (-196.1 °C to 27 °C) YS : quenched from 1273 °K (1000 °C), aged at 748 °K (475 °C) \|\| aged 6.5 h \|\| 77 K to 300 K (-196.1 °C to 27 °C)
Fe - 3 Ir (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 0.5 Ni (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1808 K (-272.1 °C to 1535 °C) SIGMA : solid \|\| 1 K to 1808 K (-272.1 °C to 1535 °C)
Fe - 1 Ni (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1803 K (-272.1 °C to 1530 °C) SIGMA : solid \|\| 1 K to 1803 K (-272.1 °C to 1530 °C)
Fe - 3 Ni (wt %)	E : solid \|\| ferrite \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| ferrite \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| ferrite \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| ferrite \|\| 76 K to 473 K (-197.1 °C to 200 °C) TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| martensite \|\| 1 K to 600 K (-272.1 °C to 327 °C) SIGMA : solid \|\| martensite \|\| 1 K to 600 K (-272.1 °C to 327 °C)
Fe - 5 Ni (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| martensite \|\| 1 K to 1035 K (-272.1 °C to 762 °C) SIGMA : solid \|\| martensite \|\| 1 K to 1035 K (-272.1 °C to 762 °C)
Fe - 10 Ni (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| martensite \|\| 1 K to 965 K (-272.1 °C to 692 °C) SIGMA : solid \|\| martensite \|\| 1 K to 965 K (-272.1 °C to 692 °C)
Fe - 15 Ni (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| martensite \|\| 1 K to 920 K (-272.1 °C to 647 °C) SIGMA : solid \|\| martensite \|\| 1 K to 920 K (-272.1 °C to 647 °C)
Fe - 20 Ni (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| martensite \|\| 1 K to 875 K (-272.1 °C to 602 °C) SIGMA : solid \|\| martensite \|\| 1 K to 875 K (-272.1 °C to 602 °C)
Fe - 25 Ni (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| martensite \|\| 1 K to 810 K (-272.1 °C to 537 °C) SIGMA : solid \|\| martensite \|\| 1 K to 810 K (-272.1 °C to 537 °C)
Fe - 30 Ni (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| martensite \|\| 1 K to 740 K (-272.1 °C to 467 °C) SIGMA : solid \|\| martensite \|\| 1 K to 740 K (-272.1 °C to 467 °C)
Fe - 34 Ni (wt %)	SSC : deformed 70% at 298 °K (25 °C) \|\| tested at 195 °K (-78 °C), 6.7x10^-⁴/s \|\| 0 to 0.11 mm/mm strain SSC : deformed 70% at 723 °K (450 °C) \|\| tested at 77.2 °K (-196 °C), 6.7x10^-⁴/s \|\| 0 to 0.115 mm/mm strain
Fe - 35 Ni (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1600 K (-272.1 °C to 1327 °C) SIGMA : solid \|\| 1 K to 1600 K (-272.1 °C to 1327 °C)
Fe - 40 Ni (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1600 K (-272.1 °C to 1327 °C) SIGMA : solid \|\| 1 K to 1600 K (-272.1 °C to 1327 °C)
Fe - 45 Ni (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1706 K (-272.1 °C to 1433 °C) SIGMA : solid \|\| 1 K to 1706 K (-272.1 °C to 1433 °C)
Fe - 50 Ni (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1704 K (-272.1 °C to 1431 °C) SIGMA : solid \|\| 1 K to 1704 K (-272.1 °C to 1431 °C)
Fe - 3 Pt (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 5 Pt (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 10 Pt (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 3 Re (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 6 Re (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 3 Rh (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 6 Rh (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 8 Rh (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 6 Ru (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 9 Ru (at %)	E : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) G : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) v : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C) K : solid \|\| 76 K to 473 K (-197.1 °C to 200 °C)
Fe - 1 Si (wt %)	D : solid \|\| 200 K to 973 K (-73.1 °C to 700 °C) DLL : solid \|\| 200 K to 973 K (-73.1 °C to 700 °C) MTE : solid \|\| 200 K to 973 K (-73.1 °C to 700 °C) CTE : solid \|\| 200 K to 973 K (-73.1 °C to 700 °C) RHO : solid \|\| 25 K to 738 K (-248.1 °C to 465 °C) SIGMA : solid \|\| 25 K to 738 K (-248.1 °C to 465 °C)
Fe - 1.8 Si (wt %)	D : solid \|\| 200 K to 948 K (-73.1 °C to 675 °C) DLL : solid \|\| 200 K to 948 K (-73.1 °C to 675 °C) MTE : solid \|\| 200 K to 948 K (-73.1 °C to 675 °C) CTE : solid \|\| 200 K to 948 K (-73.1 °C to 675 °C)
Fe - 2.8 Si (wt %)	D : solid \|\| 200 K to 1033 K (-73.1 °C to 760 °C) DLL : solid \|\| 200 K to 1033 K (-73.1 °C to 760 °C) MTE : solid \|\| 200 K to 1033 K (-73.1 °C to 760 °C) CTE : solid \|\| 200 K to 1033 K (-73.1 °C to 760 °C)
Fe - 3.9 Si (wt %)	D : solid \|\| 200 K to 1048 K (-73.1 °C to 775 °C) DLL : solid \|\| 200 K to 1048 K (-73.1 °C to 775 °C) MTE : solid \|\| 200 K to 1048 K (-73.1 °C to 775 °C) CTE : solid \|\| 200 K to 1048 K (-73.1 °C to 775 °C)
Fe - 4.4 Si (wt %)	D : solid \|\| 200 K to 1043 K (-73.1 °C to 770 °C) DLL : solid \|\| 200 K to 1043 K (-73.1 °C to 770 °C) MTE : solid \|\| 200 K to 1043 K (-73.1 °C to 770 °C) CTE : solid \|\| 200 K to 1043 K (-73.1 °C to 770 °C)
Fe - 8 Si (wt %)	D : solid \|\| 200 K to 978 K (-73.1 °C to 705 °C) DLL : solid \|\| 200 K to 978 K (-73.1 °C to 705 °C) MTE : solid \|\| 200 K to 978 K (-73.1 °C to 705 °C) CTE : solid \|\| 200 K to 978 K (-73.1 °C to 705 °C)
Fe - 6 Ni - 0.2 C (wt %)	YS : tempered martensite \|\| tempered at 523 °K (250 °C) \|\| 77 K to 295 K (-196.1 °C to 22 °C) YSC : tempered martensite \|\| tempered at 523 °K (250 °C) \|\| 77 K to 295 K (-196.1 °C to 22 °C)
TRIP 590	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
TRIP 600	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
TRIP 700	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
TRIP 780	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
TRIP 800	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
TRIP 1000	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DUAL-TEN 590	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DUAL-TEN 600	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DUAL-TEN 780	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DUAL-TEN 800	E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
H220LAD	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
HSLA 280	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
HSLA 340	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
H380LAD	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
HSLA 550	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DP 450	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C)
DP 500	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DP 550	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DP 590	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DP 600	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DP 690	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DP 780	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DP 800	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DP 820	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DP 965	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DP 980	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
QP 980 (3GAHSS)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DQSK	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
EDDS	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DDS	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
DS Type B	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
API 5ST CT80	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
S350	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
S420	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
G500	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) G : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) v : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C) K : solid \|\| 4 K to 1500 K (-269.1 °C to 1226.8 °C)
Nickel alloys	Property : Condition // Data range
Nickel (commercially pure)	D : solid \|\| 0 K to 1173 K (-273.1 °C to 900 °C) DLL : solid \|\| 0 K to 1173 K (-273.1 °C to 900 °C) MTE : solid \|\| 0 K to 1173 K (-273.1 °C to 900 °C) E : solid \|\| 0 K to 1323 K (-273.1 °C to 1050 °C) SH : solid \|\| 100 K to 1728 K (-173.1 °C to 1455 °C) SSC : annealed \|\| tested at 195 °K (-78 °C), 3.3x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SSC : annealed \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.45 mm/mm strain SSC : annealed \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.4 mm/mm strain FEN : hot finished \|\| tested at 4 °K (-269.1 °C), R = -1, axial, total strain range \|\| 190 cycles to 7x10⁴ cycles FEN : hot finished \|\| tested at 78 °K (-195.1 °C), R = -1, axial, total strain range \|\| 140 cycles to 2.73x10⁵ cycles FSN : annealed \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 4x10⁶ cycles FSN : annealed \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 6x10⁴ cycles to 1x10⁶ cycles FSN : annealed, K_t = 3 \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles FSN : annealed, K_t = 3 \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed, K_t = 3 \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 1x10⁶ cycles
Nickel D (211) (UNS N02211) (WNr 2.4116)	D : solid \|\| 81 K to 1173 K (-192.1 °C to 900 °C) DLL : solid \|\| 81 K to 1173 K (-192.1 °C to 900 °C) MTE : solid \|\| 81 K to 1173 K (-192.1 °C to 900 °C) CTE : solid \|\| 50 K to 800 K (-223.1 °C to 526.9 °C)
Nickel 200 (UNS N02200) (WNr 2.4036/2.4040) (ISO/EN/DIN Ni99.0) (ASTM B160/B161/B162)	D : solid \|\| 73 K to 1373 K (-200.1 °C to 1100 °C) DLL : solid \|\| 73 K to 1373 K (-200.1 °C to 1100 °C) MTE : solid \|\| 73 K to 1373 K (-200.1 °C to 1100 °C) E : solid \|\| 0 K to 1323 K (-273.1 °C to 1050 °C) TC : solid \|\| annealed \|\| 173 K to 1273 K (-100.1 °C to 1000 °C) SSC : annealed bar \|\| tested at 195 °K (-78 °C), 3.3x10^-⁴/s \|\| 0 to 0.37 mm/mm strain SSC : annealed bar \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.438 mm/mm strain SSC : annealed bar \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.438 mm/mm strain FEN : hot finished \|\| tested at 4 °K (-269.1 °C), R = -1, axial, total strain range \|\| 190 cycles to 7x10⁴ cycles FEN : hot finished \|\| tested at 78 °K (-195.1 °C), R = -1, axial, total strain range \|\| 140 cycles to 2.73x10⁵ cycles FSN : annealed sheet \|\| tested at 194 °K (-79 °C), reverse bending, R = -1, maximum stress \|\| 1.49x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet \|\| tested at 77 °K (-196.1 °C), reverse bending, R = -1, maximum stress \|\| 2.93x10⁴ cycles to 1x10⁶ cycles FSN : annealed sheet \|\| tested at 20 °K (-253.1 °C), reverse bending, R = -1, maximum stress \|\| 6x10⁴ cycles to 1x10⁶ cycles RHO : solid \|\| 173 K to 1373 K (-100.1 °C to 1100 °C) SIGMA : solid \|\| 173 K to 1373 K (-100.1 °C to 1100 °C)
Nickel 201 (UNS N02201) (WNr 2.4068) (ISO/EN/DIN LC-Ni99) (JIS NW2201) (ASTM B160/B161/B162) (SAE 5553) (AMS 5553)	TC : solid \|\| annealed \|\| 173 K to 1273 K (-100.1 °C to 1000 °C) RHO : solid \|\| 173 K to 1273 K (-100.1 °C to 1000 °C) SIGMA : solid \|\| 173 K to 1273 K (-100.1 °C to 1000 °C)
Nickel TD (UNS N03260)	RHO : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Monel 400 (UNS N04400) (WNr 2.4360) (ISO/EN/DIN NW4400/NiCu30/NiCu30Fe) (JIS NW4400)	D : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) DLL : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) MTE : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) CTE : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) TC : solid \|\| annealed \|\| 4 K to 1255 K (-269.1 °C to 982.3 °C) TC : solid \|\| hard-drawn, cold-rolled \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) TD : solid \|\| annealed \|\| 88 K to 589 K (-185.1 °C to 315.6 °C) TD : solid \|\| hard-drawn, cold-rolled \|\| 88 K to 300 K (-185.1 °C to 26.9 °C) SH : solid \|\| 88 K to 589 K (-185.1 °C to 315.6 °C) RHO : solid \|\| 77 K to 1367 K (-196.1 °C to 1093.4 °C) SIGMA : solid \|\| 77 K to 1367 K (-196.1 °C to 1093.4 °C)
Monel 401 (UNS N04401)	D : solid \|\| 77 K to 1367 K (-196.1 °C to 1093.4 °C) DLL : solid \|\| 77 K to 1367 K (-196.1 °C to 1093.4 °C) MTE : solid \|\| 77 K to 1367 K (-196.1 °C to 1093.4 °C) CTE : solid \|\| 77 K to 1367 K (-196.1 °C to 1093.4 °C)
Monel K-500 (UNS N05500) (WNr 2.4374/2.4375) (ISO/EN/DIN NW5500/NiCu30Al/NiCu30Al3Ti) (ASTM B865) (AMS 4676)	D : solid \|\| annealed, hot-rolled, cast & cold-rolled materials \|\| 0 K to 1289 K (-273.1 °C to 1015.9 °C) D : solid \|\| age hardened \|\| 73 K to 1073 K (-200.1 °C to 800 °C) DLL : solid \|\| annealed, hot-rolled, cast & cold-rolled materials \|\| 0 K to 1289 K (-273.1 °C to 1015.9 °C) DLL : solid \|\| age hardened \|\| 73 K to 1073 K (-200.1 °C to 800 °C) MTE : solid \|\| annealed, hot-rolled, cast & cold-rolled materials \|\| 0 K to 1289 K (-273.1 °C to 1015.9 °C) MTE : solid \|\| age hardened \|\| 73 K to 1073 K (-200.1 °C to 800 °C) CTE : solid \|\| annealed, hot-rolled, cast & cold-rolled materials \|\| 0 K to 1289 K (-273.1 °C to 1015.9 °C) CTE : solid \|\| age hardened \|\| 73 K to 1073 K (-200.1 °C to 800 °C) TC : solid \|\| annealed & quenched \|\| 131 K to 1185 K (-142.1 °C to 911.9 °C) TD : solid \|\| annealed & quenched \|\| 116 K to 1144 K (-157.1 °C to 870.9 °C) SH : solid \|\| 73 K to 1144 K (-200.1 °C to 870.9 °C) SSC : bar aged at 866 °K (593 °C) \|\| tested at 195 °K (-78 °C), 3.3x10^-⁴/s \|\| 0 to 0.22 mm/mm strain SSC : bar aged at 866 °K (593 °C) \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.28 mm/mm strain SSC : bar aged at 866 °K (593 °C) \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.28 mm/mm strain SSC : wire aged at 800 °K (527 °C) \|\| tested at 77 °K (-196.1 °C), 2.2x10^-⁴/s \|\| 0 to 0.111 mm/mm strain SSC : wire aged at 800 °K (527 °C) \|\| tested at 77 °K (-196.1 °C), 2.2x10^-⁴/s, 300 ppm H₂ \|\| 0 to 0.113 mm/mm strain FSN : sheet \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 2.7x10⁴ cycles to 1x10⁶ cycles FSN : sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 1.7x10⁴ cycles to 1x10⁶ cycles FSN : sheet \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 3.3x10⁴ cycles to 1x10⁶ cycles FSN : sheet \|\| tested at 194 °K (-79 °C), R = -1, K_t = 3.2, flexure, maximum stress \|\| 1.9x10⁴ cycles to 1x10⁶ cycles FSN : sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 3.2, flexure, maximum stress \|\| 1.75x10⁴ cycles to 1.34x10⁶ cycles FSN : sheet \|\| tested at 20.4 °K (-252.8 °C), R = -1, K_t = 3.2, flexure, maximum stress \|\| 4x10⁴ cycles to 1.33x10⁶ cycles NE : polished \|\| 88 K to 1255 K (-185.1 °C to 982.3 °C) NE : clean & smooth \|\| 88 K to 1089 K (-185.1 °C to 815.6 °C) NE : as-received \|\| 88 K to 1089 K (-185.1 °C to 815.6 °C) RHO : solid \|\| 77 K to 1255 K (-196.1 °C to 982.3 °C) SIGMA : solid \|\| 77 K to 1255 K (-196.1 °C to 982.3 °C)
Monel R-405 (UNS N04405)	D : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) DLL : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) MTE : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) CTE : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) TC : solid \|\| annealed \|\| 4 K to 1255 K (-269.1 °C to 982.3 °C) SH : solid \|\| 88 K to 589 K (-185.1 °C to 315.6 °C) RHO : solid \|\| 77 K to 1367 K (-196.1 °C to 1093.4 °C) SIGMA : solid \|\| 77 K to 1367 K (-196.1 °C to 1093.4 °C)
20Cb-3 (Incoloy 020) (UNS N08020) (WNr 2.4660) (ISO/EN/DIN FeNi35Cr20Cu4Mo2/NW8020/NiCr20CuMo) (ASTM B366/B462/B463/B464/B468/B471/B472/B473/B475/B747)	UTS : annealed \|\| 21 K to 1144 K (-252.1 °C to 870.9 °C) YS : annealed \|\| 21 K to 1144 K (-252.1 °C to 870.9 °C) %El : annealed \|\| 21 K to 1144 K (-252.1 °C to 870.9 °C)
Inconel 600 (UNS N06600) (WNr 2.4640/2.4816) (ISO/EN/DIN NW6600/NiCr15Fe/NiCr15Fe8) (JIS NCF600) (AMS 5540/5580/5665)	D : solid \|\| 148 K to 1273 K (-125.1 °C to 1000 °C) DLL : solid \|\| 148 K to 1273 K (-125.1 °C to 1000 °C) MTE : solid \|\| 148 K to 1273 K (-125.1 °C to 1000 °C) E : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) G : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) v : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) K : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) TC : solid \|\| annealed \|\| 4 K to 1073 K (-269.1 °C to 800 °C) TC : solid \|\| drawn \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) TD : solid \|\| annealed \|\| 148 K to 1273 K (-125.1 °C to 1000 °C) SH : solid \|\| 73 K to 1273 K (-200.1 °C to 1000 °C) UTS : annealed \|\| hot-rolled rod \|\| 194 K to 1255 K (-79.1 °C to 982.3 °C) UTS : cold-drawn \|\| rod \|\| 23 K to 973 K (-250.1 °C to 700 °C) YS : annealed \|\| hot-rolled rod \|\| 194 K to 1255 K (-79.1 °C to 982.3 °C) YS : annealed \|\| hot-rolled plate \|\| 194 K to 1255 K (-79.1 °C to 982.3 °C) YS : cold-drawn \|\| rod \|\| 23 K to 973 K (-250.1 °C to 700 °C) %El : annealed \|\| hot-rolled rod \|\| 194 K to 1255 K (-79.1 °C to 982.3 °C) %El : annealed \|\| hot-rolled plate \|\| 194 K to 1255 K (-79.1 °C to 982.3 °C) %El : cold-drawn \|\| rod \|\| 23 K to 973 K (-250.1 °C to 700 °C) FEN : sheet \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum strain \|\| 1.1x10⁴ cycles to 1x10⁷ cycles FEN : sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum strain \|\| 1.34x10⁴ cycles to 1x10⁸ cycles FEN : sheet \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum strain \|\| 3.13x10⁴ cycles to 8.4x10⁵ cycles FSN : sheet \|\| tested at 194 °K (-79 °C), R = -1, K_t = 3.2, flexure, maximum stress \|\| 6.1x10³ cycles to 1x10⁶ cycles FSN : sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 3.2, flexure, maximum stress \|\| 7.7x10³ cycles to 1x10⁶ cycles FSN : sheet \|\| tested at 20.4 °K (-252.8 °C), R = -1, K_t = 3.2, flexure, maximum stress \|\| 4.4x10⁴ cycles to 1x10⁶ cycles
Inconel 625 (UNS N06625) (WNr 2.4856) (ISO/EN/DIN NW6625/NiCr22Mo9Nb) (JIS NCF625) (AMS 5599/5666/5837)	D : solid \|\| 19 K to 1200 K (-254.1 °C to 926.9 °C) DLL : solid \|\| 19 K to 1200 K (-254.1 °C to 926.9 °C) MTE : solid \|\| 19 K to 1200 K (-254.1 °C to 926.9 °C) CTE : solid \|\| 19 K to 1200 K (-254.1 °C to 926.9 °C) TC : solid \|\| annealed \|\| 116 K to 1255 K (-157.1 °C to 982.3 °C) RHO : solid \|\| 4 K to 973 K (-269.1 °C to 700 °C) SIGMA : solid \|\| 4 K to 973 K (-269.1 °C to 700 °C)
Inconel 625LCF (UNS N06626) (WNr 2.4856) (JIS DNiCrMo-3) (ASTM B443/SB443) (AMS 5879)	TC : solid \|\| 123 K to 1273 K (-150.1 °C to 1000 °C)
Inconel 702 (UNS N07702)	TC : solid \|\| solution annealed \|\| 123 K to 1473 K (-150.1 °C to 1200 °C) TC : solid \|\| age-hardened \|\| 123 K to 1073 K (-150.1 °C to 800 °C)
Inconel 706 (UNS N09706)	D : solid \|\| 77 K to 1089 K (-196.1 °C to 815.6 °C) DLL : solid \|\| 77 K to 1089 K (-196.1 °C to 815.6 °C) MTE : solid \|\| 77 K to 1089 K (-196.1 °C to 815.6 °C) CTE : solid \|\| 77 K to 1089 K (-196.1 °C to 815.6 °C) E : solid \|\| 77 K to 973 K (-196.1 °C to 700 °C) G : solid \|\| 77 K to 973 K (-196.1 °C to 700 °C) v : solid \|\| 77 K to 973 K (-196.1 °C to 700 °C) K : solid \|\| 77 K to 973 K (-196.1 °C to 700 °C) TC : solid \|\| precipitation hardened \|\| 77 K to 873 K (-196.1 °C to 600 °C) UTS : cold-rolled sheet \|\| heat-treated, 1200 °K (927 °C) to 1283 °K (1010 °C)/933 °K (660 °C)/894 °K (621 °C) \|\| 77 K to 1033 K (-196.1 °C to 760 °C) UTS : cold-rolled sheet \|\| heat-treated, 1200 °K (927 °C) to 1283 °K (1010 °C)/1116 °K (843 °C)/933 °K (660 °C)/894 °K (621 °C) \|\| 77 K to 1033 K (-196.1 °C to 760 °C) YS : cold-rolled sheet \|\| heat-treated, 1200 °K (927 °C) to 1283 °K (1010 °C)/933 °K (660 °C)/894 °K (621 °C) \|\| 77 K to 1033 K (-196.1 °C to 760 °C) YS : cold-rolled sheet \|\| heat-treated, 1200 °K (927 °C) to 1283 °K (1010 °C)/1116 °K (843 °C)/933 °K (660 °C)/894 °K (621 °C) \|\| 77 K to 1033 K (-196.1 °C to 760 °C) %El : cold-rolled sheet \|\| heat-treated, 1200 °K (927 °C) to 1283 °K (1010 °C)/933 °K (660 °C)/894 °K (621 °C) \|\| 77 K to 1033 K (-196.1 °C to 760 °C) %El : cold-rolled sheet \|\| heat-treated, 1200 °K (927 °C) to 1283 °K (1010 °C)/1116 °K (843 °C)/933 °K (660 °C)/894 °K (621 °C) \|\| 77 K to 1033 K (-196.1 °C to 760 °C) RHO : solid \|\| 77 K to 873 K (-196.1 °C to 600 °C) SIGMA : solid \|\| 77 K to 873 K (-196.1 °C to 600 °C)
Inconel 718 (UNS N07718) (WNr 2.4668) (ISO/EN/DIN NiCr19Fe19Nb5Mo3/NiCr19NbMo) (ASTM B637/B670)	D : solid \|\| 33 K to 1144 K (-240.1 °C to 870.9 °C) DLL : solid \|\| 33 K to 1144 K (-240.1 °C to 870.9 °C) MTE : solid \|\| 33 K to 1144 K (-240.1 °C to 870.9 °C) CTE : solid \|\| 33 K to 1144 K (-240.1 °C to 870.9 °C) E : conventionally processed \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) G : conventionally processed \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) v : conventionally processed \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) K : conventionally processed \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) TC : solid \|\| 7 K to 1367 K (-266.1 °C to 1093.4 °C) UTS : other conditions \|\| cold-rolled & aged sheet \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) UTS : other conditions \|\| cold-rolled, annealed & aged sheet \|\| 195 K to 810 K (-78.1 °C to 536.9 °C) YS : other conditions \|\| cold-rolled & aged sheet \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) YS : other conditions \|\| cold-rolled, annealed & aged sheet \|\| 195 K to 811 K (-78.1 °C to 537.9 °C) %El : other conditions \|\| cold-rolled & aged sheet \|\| 77 K to 811 K (-196.1 °C to 537.9 °C) %El : other conditions \|\| cold-rolled, annealed & aged sheet \|\| 195 K to 811 K (-78.1 °C to 537.9 °C) FEN : solution annealed at 1339 °K (1066 °C) for 1 h, aged at 1005 °K (732 °C) & 922 °K (649 °C) \|\| tested at 4 °K (-269.1 °C), R = -1, axial, total strain range \|\| 100 cycles to 5.1x10⁴ cycles FEN : solution annealed at 1339 °K (1066 °C) for 1 h, aged at 1005 °K (732 °C) & 922 °K (649 °C) \|\| tested at 78 °K (-195.1 °C), R = -1, axial, total strain range \|\| 80 cycles to 1.7x10⁵ cycles FSN : annealed & aged, UTS at 293 °K (20 °C) of 1.33 GPa (193 ksi) \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 1.3x10⁴ cycles to 1x10⁷ cycles FSN : annealed & aged, UTS at 293 °K (20 °C) of 1.33 GPa (193 ksi) \|\| tested at 20.4 °K (-252.7 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : solution treated, UTS at 293 °K (20 °C) of 517 MPa (75 ksi) \|\| tested at 77 °K (-196.1 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : solution treated, UTS at 293 °K (20 °C) of 517 MPa (75 ksi) \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 800 cycles to 4x10⁶ cycles FSN : solution treated, UTS at 293 °K (20 °C) of 517 MPa (75 ksi) \|\| tested at 77 °K (-196.1 °C), K_t = 3.5, R = -1, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : solution treated, UTS at 293 °K (20 °C) of 517 MPa (75 ksi) \|\| tested at 20 °K (-253.1 °C), K_t = 3.5, R = -1, axial, maximum stress \|\| 3x10³ cycles to 1x10⁶ cycles FSN : solution treated, TIG welded \|\| tested at 77 °K (-196.1 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : solution treated, TIG welded \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles RHO : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| aged \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| aged \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Inconel 718SPF (UNS N07719) (AMS 5596G)	D : solid \|\| 33 K to 1144 K (-240.1 °C to 870.9 °C) DLL : solid \|\| 33 K to 1144 K (-240.1 °C to 870.9 °C) MTE : solid \|\| 33 K to 1144 K (-240.1 °C to 870.9 °C) CTE : solid \|\| 33 K to 1144 K (-240.1 °C to 870.9 °C) E : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) G : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) v : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) K : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) TC : solid \|\| 7 K to 1367 K (-266.1 °C to 1093.4 °C) RHO : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| aged \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| aged \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Inconel X-750 (UNS N07750) (WNr 2.4669) (ISO/EN/DIN NW7750/NiCr15Fe7Ti2Al/NiCr15Fe7TiAl) (JIS NCF750) (ASTM B637) (AMS 5542/5598/5667/5668/5669/5670/5671/5747)	D : solid \|\| heat-treated \|\| 0 K to 1590 K (-273.1 °C to 1316.8 °C) DLL : solid \|\| heat-treated \|\| 0 K to 1590 K (-273.1 °C to 1316.8 °C) MTE : solid \|\| heat-treated \|\| 0 K to 1590 K (-273.1 °C to 1316.8 °C) CTE : solid \|\| heat-treated \|\| 0 K to 1590 K (-273.1 °C to 1316.8 °C) E : solid \|\| 0 K to 1255 K (-273.1 °C to 982.3 °C) TC : solid \|\| annealed \|\| 7 K to 300 K (-266.1 °C to 26.9 °C) TC : solid \|\| heat-treated \|\| 116 K to 1665 K (-157.1 °C to 1391.8 °C) TD : solid \|\| heat-treated \|\| 116 K to 1255 K (-157.1 °C to 981.9 °C) SH : solid \|\| 1 K to 1255 K (-272.1 °C to 982.3 °C) SSC : aged 20 h at 978 °K (704 °C) and air cooled, 3.3x10^-⁴/s \|\| tested at 195 °K (-78 °C) \|\| 0 to 0.23 mm/mm strain SSC : aged 20 h at 978 °K (704 °C) and air cooled, 3.3x10^-⁴/s \|\| tested at 76 °K (-197.1 °C) \|\| 0 to 0.25 mm/mm strain SSC : aged 20 h at 978 °K (704 °C) and air cooled, 3.3x10^-⁴/s \|\| tested at 20 °K (-253.1 °C) \|\| 0 to 0.28 mm/mm strain UTS : bar \|\| aged 20 h at 978 °K (704 °C) & air cooled \|\| 20 K to 293 K (-253.1 °C to 20 °C) YS : bar \|\| aged 20 h at 978 °K (704 °C) & air cooled \|\| 20 K to 293 K (-253.1 °C to 20 °C) %El : bar \|\| aged 20 h at 978 °K (704 °C) & air cooled \|\| 20 K to 293 K (-253.1 °C to 20 °C) FEN : cold-rolled sheet \|\| tested at 194 °K (-79 °C), R = -1, flexure, aged 978 °K (704 °C) for 20 h, maximum strain \|\| 1.3x10⁴ cycles to 1.35x10⁶ cycles FEN : cold-rolled sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, aged 978 °K (704 °C) for 20 h, maximum strain \|\| 2.5x10⁴ cycles to 9x10⁵ cycles FEN : cold-rolled sheet \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, aged 978 °K (704 °C) for 20 h, maximum strain \|\| 4.5x10⁴ cycles to 1x10⁶ cycles FSN : cold-rolled sheet \|\| tested at 194 °K (-79 °C), R = -1, K_t = 3.2, flexure, aged 978 °K (704 °C) for 20 h, maximum stress \|\| 1.5x10⁴ cycles to 1x10⁷ cycles FSN : cold-rolled sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 3.2, flexure, aged 978 °K (704 °C) for 20 h, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : cold-rolled sheet \|\| tested at 20.4 °K (-252.8 °C), R = -1, K_t = 3.2, flexure, aged 978 °K (704 °C) for 20 h, maximum stress \|\| 2.7x10⁴ cycles to 1.25x10⁶ cycles FSN : cold-rolled sheet \|\| tested at 194 °K (-79 °C), R = -1, K_t = 6.4, flexure, aged 978 °K (704 °C) for 20 h, maximum stress \|\| 2.8x10⁴ cycles to 1.1x10⁶ cycles FSN : cold-rolled sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 6.4, flexure, aged 978 °K (704 °C) for 20 h, maximum stress \|\| 2.4x10⁴ cycles to 1x10⁶ cycles NE : solid \|\| polished \|\| 88 K to 1183 K (-185.1 °C to 910 °C) RHO : solid \|\| hot-rolled & direct aged \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| hot-rolled & direct aged \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Inconel C-276 (UNS N10276) (WNr 2.4375/2.4537/2.4819) (ISO/EN/DIN NW0276/NiMo16Cr/NiMo16Cr15Fe6W4/NiMo16Cr15W) (JIS NW0276)	TC : solid \|\| 105 K to 1373 K (-168.1 °C to 1100 °C)
Inconel HX / Hastelloy X / Nimonic PE13 (UNS N06002) (WNr 2.4665) (ISO/EN/DIN NW6002/NiCr21Fe18Mo9/NiCr22Fe18Mo) (JIS NW6002) (AMS 5536/5588/5754/5798)	D : solid \|\| 0 K to 1590 K (-273.1 °C to 1316.8 °C) DLL : solid \|\| 0 K to 1590 K (-273.1 °C to 1316.8 °C) MTE : solid \|\| 0 K to 1590 K (-273.1 °C to 1316.8 °C) CTE : solid \|\| 0 K to 1590 K (-273.1 °C to 1316.8 °C) TC : solid \|\| annealed \|\| 7 K to 1273 K (-266.1 °C to 1000 °C) RHO : solid \|\| 7 K to 1273 K (-266.1 °C to 1000 °C) SIGMA : solid \|\| 7 K to 1273 K (-266.1 °C to 1000 °C)
Incoloy 825 (UNS N08825) (WNr 2.4858) (ISO/EN/DIN NW8825/NiCr21Mo/NiCr2Mo/NiFe30Cr21Mo3) (JIS NCF825)	TC : solid \|\| 123 K to 1173 K (-150.1 °C to 900 °C)
Hastelloy A	UTS : rolled & annealed \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) YS : rolled & annealed \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : rolled & annealed \|\| 77 K to 300 K (-196.1 °C to 26.9 °C)
Hastelloy B (UNS N10001) (WNr 2.4600) (JIS NW0001) (AFNOR Ni-Mo28)	D : solid \|\| 20 K to 1513 K (-253.1 °C to 1240 °C) DLL : solid \|\| 20 K to 1513 K (-253.1 °C to 1240 °C) MTE : solid \|\| 20 K to 1513 K (-253.1 °C to 1240 °C) CTE : solid \|\| 20 K to 1513 K (-253.1 °C to 1240 °C) NE : solid \|\| 2 micro-inch RMS finish \|\| 86 K to 1263 K (-187.1 °C to 990 °C) NE : solid \|\| 15 micro-inch RMS finish \|\| 86 K to 1263 K (-187.1 °C to 990 °C)
Hastelloy C (UNS N10002) (WNr 2.4602) (AFNOR NiMo16Cr15C)	UTS : rolled & annealed \|\| 73 K to 300 K (-200.1 °C to 26.9 °C) YS : rolled & annealed \|\| 73 K to 300 K (-200.1 °C to 26.9 °C) %El : rolled & annealed \|\| 73 K to 300 K (-200.1 °C to 26.9 °C) FSN : solution treated \|\| tested at 77 °K (-196.1 °C), R = -1, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : solution treated \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 400 cycles to 1x10⁶ cycles FSN : TIG welded \|\| tested at 77 °K (-196.1 °C), R = -1, axial, maximum stress \|\| 4x10³ cycles to 4x10⁶ cycles FSN : TIG welded \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : solution treated, K_t = 3.8 \|\| tested at 77 °K (-196.1 °C), R = -1, axial, maximum stress \|\| 2x10³ cycles to 4x10⁶ cycles FSN : solution treated, K_t = 3.8 \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 2x10³ cycles to 4x10⁶ cycles NE : solid \|\| 2 micro-inch RMS finish \|\| 77 K to 1100 K (-196.1 °C to 826.9 °C) NE : solid \|\| 15 micro-inch RMS finish \|\| 77 K to 1100 K (-196.1 °C to 826.9 °C) RHO : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Hastelloy HYBRID-BC1 (UNS N10362) (WNr 2.4708) (ISO/EN/DIN NiMo22Cr15)	D : solution annealed \|\| 123 K to 873 K (-150.1 °C to 600 °C) DLL : solution annealed \|\| 123 K to 873 K (-150.1 °C to 600 °C) MTE : solution annealed \|\| 123 K to 873 K (-150.1 °C to 600 °C) CTE : solution annealed \|\| 123 K to 873 K (-150.1 °C to 600 °C) E : solution annealed \|\| values for 19 mm (0.75 inch) sheet below RT \|\| 116 K to 297 K (-157.1 °C to 23.9 °C) E : solution annealed \|\| combined values below/above RT \|\| 116 K to 873 K (-157.1 °C to 600 °C)
Hastelloy N (UNS N10003)	RHO : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Haynes R-41 (Rene 41) (UNS N07041) (WNr 2.4973) (AISI 683) (AMS 5545/5712/5800)	D : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) DLL : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) MTE : solid \|\| 0 K to 1367 K (-273.1 °C to 1093.4 °C) E : solid \|\| 77 K to 1273 K (-196.1 °C to 1000 °C) G : solid \|\| 77 K to 1005 K (-196.1 °C to 731.9 °C) v : solid \|\| 77 K to 1005 K (-196.1 °C to 731.9 °C) K : solid \|\| 77 K to 1005 K (-196.1 °C to 731.9 °C) SSC : annealed \|\| tested at 195 °K (-78 °C), 3.3x10^-⁴/s \|\| 0 to 0.23 mm/mm strain SSC : annealed \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.23 mm/mm strain SSC : annealed \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.23 mm/mm strain UTS : bar \|\| solution treated at 1353 °K (1079 °C) \|\| 20 K to 293 K (-253.1 °C to 20 °C) YS : bar \|\| solution treated at 1353 °K (1079 °C) \|\| 20 K to 293 K (-253.1 °C to 20 °C) %El : bar \|\| solution treated at 1353 °K (1079 °C) & aged \|\| 20 K to 293 K (-253.1 °C to 20 °C) RHO : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Udimet 630	RHO : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Udimet 700	RHO : solid \|\| hot-rolled \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| hot-rolled \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Udimet D-979 (UNS N09979) (AISI 664) (SAE J467) (AMS 5509/5746)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) UTS : solution annealed & aged \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C) YS : solution annealed & aged \|\| 77 K to 1144 K (-196.1 °C to 870.9 °C)
AEREX 350	TC : solid \|\| 84 K to 963 K (-189.1 °C to 690 °C) RHO : solid \|\| 87 K to 973 K (-186.1 °C to 700 °C) SIGMA : solid \|\| 87 K to 973 K (-186.1 °C to 700 °C)
Waspaloy (UNS N07001) (WNr 2.4654) (ISO/EN/DIN NW7001/NiCr20Co13Mo4Ti3Al) (AISI 685) (AMS 5544/5704/5706/5707/5708/5709/5728/7471)	RHO : solid \|\| aged \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| aged \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C)
CY40 (UNS N06040) (ISO/EN/DIN C-NiCr15Fe/NC6040) (ASTM A494/A743/A744/CY-40)	D : solid \|\| 148 K to 1273 K (-125.1 °C to 1000 °C) DLL : solid \|\| 148 K to 1273 K (-125.1 °C to 1000 °C) MTE : solid \|\| 148 K to 1273 K (-125.1 °C to 1000 °C) E : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) G : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) v : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) K : solid \|\| 0 K to 1273 K (-273.1 °C to 1000 °C) SH : solid \|\| 73 K to 1273 K (-200.1 °C to 1000 °C)
Ni-Ti (Nitinol)	E : solid \|\| annealed at 1200 °K (927 °C), Ms = 227 °K (-46 °C) \|\| 100 K to 350 K (-173.1 °C to 76.9 °C)
Ni - 0.5 Cu (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Ni - 1 Cu (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Ni - 3 Cu (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Ni - 5 Cu (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Ni - 10 Cu (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Ni - 15 Cu (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Ni - 20 Cu (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Ni - 25 Cu (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Ni - 30 Cu (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Ni - 35 Cu (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Ni - 40 Cu (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Ni - 45 Cu (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Ni - 45 Fe (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1703 K (-272.1 °C to 1430 °C) SIGMA : solid \|\| 1 K to 1703 K (-272.1 °C to 1430 °C)
Ni - 40 Fe (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1600 K (-272.1 °C to 1327 °C) SIGMA : solid \|\| 1 K to 1600 K (-272.1 °C to 1327 °C)
Ni - 35 Fe (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1702 K (-272.1 °C to 1429 °C) SIGMA : solid \|\| 1 K to 1702 K (-272.1 °C to 1429 °C)
Ni - 30 Fe (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1702 K (-272.1 °C to 1429 °C) SIGMA : solid \|\| 1 K to 1702 K (-272.1 °C to 1429 °C)
Ni - 25 Fe (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1703 K (-272.1 °C to 1430 °C) SIGMA : solid \|\| 1 K to 1703 K (-272.1 °C to 1430 °C)
Ni - 20 Fe (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1703 K (-272.1 °C to 1430 °C) SIGMA : solid \|\| 1 K to 1703 K (-272.1 °C to 1430 °C)
Ni - 15 Fe (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1707 K (-272.1 °C to 1434 °C) SIGMA : solid \|\| 1 K to 1707 K (-272.1 °C to 1434 °C)
Ni - 10 Fe (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1710 K (-272.1 °C to 1437 °C) SIGMA : solid \|\| 1 K to 1710 K (-272.1 °C to 1437 °C)
Ni - 5 Fe (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1600 K (-272.1 °C to 1327 °C) SIGMA : solid \|\| 1 K to 1600 K (-272.1 °C to 1327 °C)
Ni - 3 Fe (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1720 K (-272.1 °C to 1447 °C) SIGMA : solid \|\| 1 K to 1720 K (-272.1 °C to 1447 °C)
Ni - 1 Fe (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1725 K (-272.1 °C to 1452 °C) SIGMA : solid \|\| 1 K to 1725 K (-272.1 °C to 1452 °C)
Ni - 0.5 Fe (wt %)	TC : solid \|\| 4 K to 1100 K (-269.1 °C to 827 °C) RHO : solid \|\| 1 K to 1727 K (-272.1 °C to 1454 °C) SIGMA : solid \|\| 1 K to 1727 K (-272.1 °C to 1454 °C)
Aluminum alloys	Property : Condition // Data range
1050 (UNS A91050) (WNr 3.0255) (ISO/EN/DIN Al99.5) (JIS A1050/A199.5) (AFNOR A5) (GB & GB/T T3880-2018)	D : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) DLL : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) MTE : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) CTE : solid \|\| 10 K to 900 K (-263.1 °C to 626.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TD : solid \|\| 20 K to 933 K (-253.1 °C to 660 °C) SH : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) HE : solid \|\| 175 K to 700 K (-98.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 933 K (-272.1 °C to 660 °C) SIGMA : solid \|\| 1 K to 933 K (-272.1 °C to 660 °C)
1060 (UNS A91060) (ISO/EN/DIN Al99.6) (JIS A1060PB/A1060SB/A1060SBC)	D : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) DLL : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) MTE : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) CTE : solid \|\| 10 K to 900 K (-263.1 °C to 626.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TD : solid \|\| 20 K to 933 K (-253.1 °C to 660 °C) SH : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) UTS : 10,000 h hold \|\| O temper \|\| 75 K to 533 K (-198.1 °C to 260 °C) YS : 10,000 h hold \|\| O temper \|\| 75 K to 533 K (-198.1 °C to 260 °C) HE : solid \|\| 175 K to 700 K (-98.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 933 K (-272.1 °C to 660 °C) SIGMA : solid \|\| 1 K to 933 K (-272.1 °C to 660 °C)
1085 (UNS A91085) (ISO/EN/DIN Al99.85) (JIS 1085H/A1085P)	D : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) DLL : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) MTE : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) CTE : solid \|\| 10 K to 900 K (-263.1 °C to 626.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TD : solid \|\| 20 K to 933 K (-253.1 °C to 660 °C) SH : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) SSC : annealed \|\| tested at 77 °K (-196.1 °C), 0.008/s \|\| 0 to 0.52 mm/mm strain HE : solid \|\| 175 K to 700 K (-98.1 °C to 426.9 °C)
1100 (UNS A91100) (ISO/EN/DIN Al99.0Cu) (AFNOR A45)	D : solid \|\| O temper \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) DLL : solid \|\| O temper \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) MTE : solid \|\| O temper \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| F temper \|\| 4 K to 366 K (-269.1 °C to 92.9 °C) TD : solid \|\| F temper \|\| 20 K to 713 K (-253.1 °C to 440 °C) SH : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) SSC : O temper \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.371 mm/mm strain SSC : O temper \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.38 mm/mm strain SSC : O temper \|\| tested at 195 °K (-78 °C), 3.3x10^-⁴/s \|\| 0 to 0.37 mm/mm strain UTS : 10,000 h hold \|\| O temper \|\| 19 K to 533 K (-254.1 °C to 260 °C) UTS : 10,000 h hold \|\| H12 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| H14 temper \|\| 4 K to 643 K (-269.1 °C to 370 °C) UTS : 10,000 h hold \|\| H18 temper \|\| 77 K to 698 K (-196.1 °C to 425 °C) YS : 10,000 h hold \|\| O temper \|\| 19 K to 533 K (-254.1 °C to 260 °C) YS : 10,000 h hold \|\| H12 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| H14 temper \|\| 4 K to 643 K (-269.1 °C to 370 °C) YS : 10,000 h hold \|\| H18 temper \|\| 77 K to 698 K (-196.1 °C to 425 °C) FSN : H16 temper \|\| tested at 77 °K (-196.1 °C), R = -1, flexure, maximum stress \|\| 3x10³ cycles to 2x10⁶ cycles FSN : H16 temper \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles RHO : solid \|\| O temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| O temper \|\| 4 K to 293 K (-269.1 °C to 20 °C)
1145 (UNS A91145)	D : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) DLL : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) MTE : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) CTE : solid \|\| 10 K to 900 K (-263.1 °C to 626.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TD : solid \|\| 20 K to 933 K (-253.1 °C to 660 °C) SH : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) HE : solid \|\| 175 K to 700 K (-98.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 933 K (-272.1 °C to 660 °C) SIGMA : solid \|\| 1 K to 933 K (-272.1 °C to 660 °C)
1199 (UNS A91199)	D : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) DLL : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) MTE : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) CTE : solid \|\| 10 K to 900 K (-263.1 °C to 626.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| bulk \|\| 0 K to 933 K (-273.1 °C to 660 °C) TD : solid \|\| 20 K to 933 K (-253.1 °C to 660 °C) SH : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) HE : solid \|\| 175 K to 700 K (-98.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 933 K (-272.1 °C to 660 °C) SIGMA : solid \|\| 1 K to 933 K (-272.1 °C to 660 °C)
1350 (UNS A91350) (ISO/EN/DIN E-Al99.5)	D : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) DLL : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) MTE : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) CTE : solid \|\| 10 K to 900 K (-263.1 °C to 626.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| annealed \|\| 6 K to 933 K (-267.6 °C to 660 °C) TD : solid \|\| annealed \|\| 10 K to 933 K (-263.1 °C to 660 °C) SH : solid \|\| 10 K to 933 K (-263.1 °C to 660 °C) HE : solid \|\| 175 K to 700 K (-98.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 933 K (-272.1 °C to 660 °C) SIGMA : solid \|\| 1 K to 933 K (-272.1 °C to 660 °C)
2011 (UNS A92011) (WNr 3.1056/3.1655) (ISO/EN/DIN AlCu4PbMg/AlCu6BiPb) (JIS A2011) (ASTM B210/B211) (SAE J454) (AFNOR A-U5PbBi)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
2014 (UNS A92014) (ISO/EN/DIN AlCu4SiMg/AlCuSiMn) (JIS A2014) (AFNOR A-U4SG)	D : solid \|\| 55 K to 589 K (-218.1 °C to 315.6 °C) DLL : solid \|\| 55 K to 589 K (-218.1 °C to 315.6 °C) MTE : solid \|\| 55 K to 589 K (-218.1 °C to 315.6 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| T6 temper \|\| 20 K to 573 K (-253.1 °C to 300 °C) UTS : 10,000 h hold \|\| T6 & T652 tempers, forgings \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : 10,000 h hold \|\| T4 temper, extrusions \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| T6 temper, extrusions \|\| 77 K to 813 K (-196.1 °C to 540 °C) UTS : 10,000 h hold \|\| T6 temper sheet & T651 temper plate \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| T61 temper, forgings \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| O temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| T6 & T652 tempers, forgings \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : 10,000 h hold \|\| T4 temper, extrusions \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| T6 temper, extrusions \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : 10,000 h hold \|\| T6 temper sheet & T651 temper plate \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| T61 temper, forgings \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| O temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) %El : 10,000 hold \|\| T6 temper \|\| 14 K to 644 K (-259.1 °C to 371.2 °C) FEN : T6 temper \|\| tested at 4 °K (-269.1 °C), R = -1, axial, total strain range \|\| 10 cycles to 7.1x10⁴ cycles FEN : T6 temper \|\| tested at 78 °K (-195.1 °C), R = -1, axial, total strain range \|\| 30 cycles to 4.3x10⁴ cycles FSN : T6 temper, sheet \|\| tested at 77 °K (-196.1 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 4x10⁶ cycles FSN : T6 temper, sheet \|\| tested at 77 °K (-196.1 °C), R = 0.01, axial, maximum stress \|\| 1x10³ cycles to 4x10⁶ cycles FSN : T6 temper, sheet \|\| tested at 77 °K (-196.1 °C), R = -1, K_t = 3.5, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : T6 temper, sheet \|\| tested at 77 °K (-196.1 °C), R = -1, K_t = 8.0, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : T6 temper, sheet \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : T6 temper, sheet \|\| tested at 20 °K (-253.1 °C), R = 0.01, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : T6 temper, TIG welded \|\| tested at 77 °K (-196.1 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 6x10⁶ cycles FSN : T6 temper, TIG welded \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 600 cycles to 1x10⁶ cycles FSN : T6 temper, notched, K_t = 3.5 \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 400 cycles to 1x10⁶ cycles FSN : T6 temper, notched, K_t = 8.0 \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles RHO : solid \|\| T651 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| T651 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C)
2017 (UNS A92017) (WNr 3.1325) (ISO/EN/DIN AlCu4MgSi/AlCuMg1) (AFNOR A-U4G)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : 0.5 h hold \|\| T4 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : 10 h hold \|\| T4 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : 100 h hold \|\| T4 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : 1000 h hold \|\| T4 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : 10,000 h hold \|\| T4 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 0.5 h hold \|\| T4 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 10 h hold \|\| T4 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 100 h hold \|\| T4 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 1000 h hold \|\| T4 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 10,000 h hold \|\| T4 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C)
2018 (UNS A92018)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : 0.5 h hold \|\| T61 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10 h hold \|\| T61 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 100 h hold \|\| T61 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 1000 h hold \|\| T61 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| T61 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 0.5 h hold \|\| T61 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10 h hold \|\| T61 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 100 h hold \|\| T61 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 1000 h hold \|\| T61 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| T61 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C)
2020 (UNS A92020)	D : solid \|\| T6 temper \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) DLL : solid \|\| T6 temper \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) MTE : solid \|\| T6 temper \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) SSC : T6 temper \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.6 mm/mm strain SSC : T6 temper \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : T6 temper \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate \|\| 0 to 0.6 mm/mm strain UTS : 0.5 h hold \|\| T6 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : 10 h hold \|\| T6 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : 100 h hold \|\| T6 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : 1000 h hold \|\| T6 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : 10,000 h hold \|\| T6 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 0.5 h hold \|\| T6 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 10 h hold \|\| T6 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 100 h hold \|\| T6 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 1000 h hold \|\| T6 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 10,000 h hold \|\| T6 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) FSN : T6 temper, sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, axial, maximum stress \|\| 800 cycles to 1x10⁷ cycles FSN : T6 temper, sheet \|\| tested at 20.4 °K (-252.7 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles
2021 (UNS A92021)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : 0.1 h hold \|\| T81 temper, plate \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : 0.5 h hold \|\| T81 temper, plate \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : 10 h hold \|\| T81 temper, plate \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : 100 h hold \|\| T81 temper, plate \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : 1000 h hold \|\| T81 temper, plate \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : 10,000 h hold \|\| T81 temper, plate \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : 0.1 h hold \|\| T81 temper, plate \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : 0.5 h hold \|\| T81 temper, plate \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : 10 h hold \|\| T81 temper, plate \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : 100 h hold \|\| T81 temper, plate \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : 1000 h hold \|\| T81 temper, plate \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : 10,000 h hold \|\| T81 temper, plate \|\| 4 K to 813 K (-269.1 °C to 540 °C)
2024 (UNS A92024) (WNr 3.1355) (ISO/EN/DIN AlCu4Mg1/AlCu4Mg1.5/AlCuMg2) (JIS A2024) (AFNOR A-U4G1)	D : solid \|\| 0 K to 755 K (-273.1 °C to 482.3 °C) DLL : solid \|\| 0 K to 755 K (-273.1 °C to 482.3 °C) MTE : solid \|\| 0 K to 755 K (-273.1 °C to 482.3 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| T4 temper, as-received \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) TC : solid \|\| T4 temper, annealed \|\| 116 K to 700 K (-157.1 °C to 426.9 °C) TC : solid \|\| T8xx temper \|\| 88 K to 589 K (-185.1 °C to 315.8 °C) TD : solid \|\| T4 temper, as-received \|\| 88 K to 703 K (-185.1 °C to 430 °C) TD : solid \|\| T4 temper, annealed \|\| 116 K to 700 K (-157.1 °C to 426.9 °C) TD : solid \|\| T8xx temper \|\| 88 K to 589 K (-185.1 °C to 315.8 °C) SH : solid \|\| 22 K to 700 K (-251.1 °C to 427 °C) SSC : T86 temper \|\| tested at 195 °K (-78 °C), 3.3x10^-⁴/s \|\| 0 to 0.35 mm/mm strain SSC : T86 temper \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.6 mm/mm strain SSC : T86 temper \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.9 mm/mm strain UTS : 10,000 h hold \|\| T3 temper \|\| 20 K to 813 K (-253.1 °C to 540 °C) UTS : 10,000 h hold \|\| T4 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| T6 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| T36 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| T86 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 10,000 h hold \|\| T3 temper \|\| 20 K to 813 K (-253.1 °C to 540 °C) YS : 10,000 h hold \|\| T4 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| T6 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| T36 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| T86 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) FSN : T4 temper \|\| tested at 20 °K (-253.1 °C), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 4x10⁶ cycles FSN : T4 temper \|\| tested at 77 °K (-196.1 °C), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 6x10⁷ cycles NE : solid \|\| as-received & polished samples \|\| 55 K to 822 K (-218.1 °C to 548.9 °C) RHO : solid \|\| O temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| T4 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| T6 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| T86 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| O temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| T4 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| T6 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| T86 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C)
2025 (UNS A92025) (JIS A2025FD/A2025FH)	D : solid \|\| 200 K to 589 K (-73.1 °C to 315.6 °C) DLL : solid \|\| 200 K to 589 K (-73.1 °C to 315.6 °C) MTE : solid \|\| 200 K to 589 K (-73.1 °C to 315.6 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
2036 (UNS A92036)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
2090 (UNS A92090)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| T81 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) TC : solid \|\| unknown condition \|\| 80 K to 531 K (-193.1 °C to 257.9 °C) TD : solid \|\| T81 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) TD : solid \|\| unknown condition \|\| 80 K to 531 K (-193.1 °C to 257.9 °C) SH : solid \|\| 123 K to 598 K (-150.1 °C to 325 °C) SSC : T4 temper \|\| tested at 77 °K (-196.1 °C), 8x10^-⁴/s \|\| 0 to 0.25 mm/mm strain SSC : T4 temper \|\| tested at 4 °K (-269.1 °C), 8x10^-⁴/s \|\| 0 to 0.225 mm/mm strain SSC : T81 temper \|\| tested at 77 °K (-196.1 °C), 8x10^-⁴/s \|\| 0 to 0.125 mm/mm strain SSC : T81 temper \|\| tested at 4 °K (-269.1 °C), 8x10^-⁴/s \|\| 0 to 0.175 mm/mm strain UTS : plate, T4 temper \|\| longitudinal \|\| 4 K to 298 K (-269.1 °C to 25 °C) UTS : plate, T8xxx tempers \|\| longitudinal \|\| 4 K to 533 K (-269.1 °C to 260 °C) UTS : plate, T8xxx tempers \|\| transverse \|\| 4 K to 533 K (-269.1 °C to 260 °C) UTS : plate, T8xxx tempers \|\| 45 degrees \|\| 4 K to 295 K (-269.1 °C to 22 °C) UTS : plate, T81 temper \|\| longitudinal \|\| 4 K to 298 K (-269.1 °C to 25 °C) YS : plate, T4 temper \|\| longitudinal \|\| 4 K to 298 K (-269.1 °C to 25 °C) YS : plate, T8xxx tempers \|\| longitudinal \|\| 4 K to 533 K (-269.1 °C to 260 °C) YS : plate, T8xxx tempers \|\| transverse \|\| 4 K to 533 K (-269.1 °C to 260 °C) YS : plate, T8xxx tempers \|\| 45 degrees \|\| 4 K to 295 K (-269.1 °C to 22 °C) YS : plate, T81 temper \|\| longitudinal \|\| 4 K to 298 K (-269.1 °C to 25 °C) %El : plate, T4 temper \|\| longitudinal \|\| 4 K to 298 K (-269.1 °C to 25 °C) %El : plate, T8xxx tempers \|\| longitudinal \|\| 4 K to 533 K (-269.1 °C to 260 °C) %El : plate, T8xxx tempers \|\| transverse \|\| 4 K to 533 K (-269.1 °C to 260 °C) %El : plate, T8xxx tempers \|\| 45 degrees \|\| 4 K to 295 K (-269.1 °C to 22 °C) %El : plate, T81 temper \|\| longitudinal \|\| 4 K to 298 K (-269.1 °C to 25 °C)
2117 (UNS A92117) (WNr 3.1325) (ISO/EN/DIN AlCu2.5Mg/AlCu2.5Mg0.5/AlCuMg0.5/AlCuMg1) (JIS A2017P) (AFNOR A-U2G)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T4 temper \|\| 0.5 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : T4 temper \|\| 10 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : T4 temper \|\| 100 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : T4 temper \|\| 1000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : T4 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T4 temper \|\| 0.5 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T4 temper \|\| 10 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T4 temper \|\| 100 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T4 temper \|\| 1000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T4 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C)
2124 (UNS A92124) (WNr 3.1355) (ISO/EN/DIN AlCu4Mg1/AlCuMg2) (JIS 2024P)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
2198 (UNS A92198)	SSC : T8 temper, base material \|\| tested at 90 °K (-183.1 °C), 0.001/s \|\| 0 to 0.116 mm/mm strain SSC : T8 temper, base material \|\| tested at 173 °K (-100 °C), 0.001/s \|\| 0 to 0.75 mm/mm strain SSC : T8 temper, friction stir weld at 400 rpm \|\| tested at 77 °K (-196.1 °C), 0.001/s \|\| 0 to 0.14 mm/mm strain SSC : T8 temper, friction stir weld at 400 rpm \|\| tested at 173 °K (-100 °C), 0.001/s \|\| 0 to 0.12 mm/mm strain SSC : T8 temper, friction stir weld at 600 rpm \|\| tested at 20 °K (-253.1 °C), 0.001/s \|\| 0 to 0.13 mm/mm strain SSC : T8 temper, friction stir weld at 600 rpm \|\| tested at 77 °K (-196.1 °C), 0.001/s \|\| 0 to 0.12 mm/mm strain SSC : T8 temper, friction stir weld at 600 rpm \|\| tested at 173 °K (-100 °C), 0.001/s \|\| 0 to 0.1 mm/mm strain SSC : T8 temper, friction stir weld at 800 rpm \|\| tested at 20 °K (-253.1 °C), 0.001/s \|\| 0 to 0.15 mm/mm strain SSC : T8 temper, friction stir weld at 800 rpm \|\| tested at 77 °K (-196.1 °C), 0.001/s \|\| 0 to 0.11 mm/mm strain SSC : T8 temper, friction stir weld at 800 rpm \|\| tested at 173 °K (-100 °C), 0.001/s \|\| 0 to 0.11 mm/mm strain UTS : T8 temper \|\| base material \|\| 90 K to 298 K (-183.1 °C to 25 °C) UTS : T8 temper \|\| friction stir weld at 400 rpm \|\| 77 K to 298 K (-196.1 °C to 25 °C) UTS : T8 temper \|\| friction stir weld at 600 rpm \|\| 20 K to 298 K (-253.1 °C to 25 °C) UTS : T8 temper \|\| friction stir weld at 800 rpm \|\| 20 K to 298 K (-253.1 °C to 25 °C) YS : T8 temper \|\| base material \|\| 90 K to 298 K (-183.1 °C to 25 °C) YS : T8 temper \|\| friction stir weld at 400 rpm \|\| 77 K to 298 K (-196.1 °C to 25 °C) YS : T8 temper \|\| friction stir weld at 600 rpm \|\| 20 K to 298 K (-253.1 °C to 25 °C) YS : T8 temper \|\| friction stir weld at 800 rpm \|\| 20 K to 298 K (-253.1 °C to 25 °C) %El : T8 temper \|\| base material \|\| 90 K to 298 K (-183.1 °C to 25 °C) %El : T8 temper \|\| friction stir weld at 400 rpm \|\| 77 K to 298 K (-196.1 °C to 25 °C) %El : T8 temper \|\| friction stir weld at 600 rpm \|\| 20 K to 298 K (-253.1 °C to 25 °C) %El : T8 temper \|\| friction stir weld at 800 rpm \|\| 20 K to 298 K (-253.1 °C to 25 °C)
2214 (UNS A92214)	D : solid \|\| 55 K to 589 K (-218.1 °C to 315.6 °C) DLL : solid \|\| 55 K to 589 K (-218.1 °C to 315.6 °C) MTE : solid \|\| 55 K to 589 K (-218.1 °C to 315.6 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
2218 (UNS A92218)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T61 temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T61 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T61 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T61 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T61 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T61 temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T61 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T61 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T61 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T61 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
2219 (UNS A92219) (ISO/EN/DIN AlCu6Mn)	D : solid \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) DLL : solid \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) MTE : solid \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) CTE : solid \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| T81 temper \|\| 48 K to 573 K (-225.1 °C to 300 °C) TC : solid \|\| T852 temper \|\| 0 K to 833 K (-273.1 °C to 560 °C) TD : solid \|\| T81 temper \|\| 48 K to 573 K (-225.1 °C to 300 °C) TD : solid \|\| T852 temper \|\| 22 K to 811 K (-251.1 °C to 538 °C) SH : solid \|\| T852 temper \|\| 1 K to 900 K (-272.1 °C to 627 °C) SSC : T62 temper \|\| tested at 194 °K (-79 °C), unknown strain rate, longitudinal \|\| 0 to 0.6 mm/mm strain SSC : T62 temper \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate, longitudinal \|\| 0 to 0.1 mm/mm strain SSC : T62 temper \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate, longitudinal \|\| 0 to 0.16 mm/mm strain SSC : T62 temper \|\| tested at 194 °K (-79 °C), unknown strain rate, transverse \|\| 0 to 0.6 mm/mm strain SSC : T62 temper \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate, transverse \|\| 0 to 0.85 mm/mm strain SSC : T62 temper \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate, transverse \|\| 0 to 0.12 mm/mm strain SSC : T81 temper \|\| tested at 194 °K (-79 °C), unknown strain rate, longitudinal \|\| 0 to 0.9 mm/mm strain SSC : T81 temper \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate, longitudinal \|\| 0 to 0.1 mm/mm strain SSC : T81 temper \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate, longitudinal \|\| 0 to 0.11 mm/mm strain SSC : T81 temper \|\| tested at 194 °K (-79 °C), unknown strain rate, transverse \|\| 0 to 0.7 mm/mm strain SSC : T81 temper \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate, transverse \|\| 0 to 0.75 mm/mm strain SSC : T81 temper \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate, transverse \|\| 0 to 0.11 mm/mm strain SSC : T87 temper \|\| tested at 194 °K (-79 °C), unknown strain rate, longitudinal \|\| 0 to 0.9 mm/mm strain SSC : T87 temper \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate, longitudinal \|\| 0 to 0.9 mm/mm strain SSC : T87 temper \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate, longitudinal \|\| 0 to 0.11 mm/mm strain SSC : T87 temper \|\| tested at 194 °K (-79 °C), unknown strain rate, transverse \|\| 0 to 0.7 mm/mm strain SSC : T87 temper \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate, transverse \|\| 0 to 0.8 mm/mm strain SSC : T87 temper \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate, transverse \|\| 0 to 0.11 mm/mm strain SSC : T87 temper, friction stir weld \|\| tested at 77 °K (-196.1 °C), unknown strain rate \|\| 0 to 0.92 mm/mm strain SSC : T87 temper, friction stir weld \|\| tested at 20 °K (-253.1 °C), unknown strain rate \|\| 0 to 0.96 mm/mm strain UTS : 10,000 h hold \|\| T37 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : 10,000 h hold \|\| T851 temper \|\| 4 K to 643 K (-269.1 °C to 370 °C) UTS : 10,000 h hold \|\| T81 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : 10,000 h hold \|\| T8511 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| T62 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : friction stir weld \|\| T87 temper \|\| 20 K to 298 K (-253.1 °C to 25 °C) YS : 10,000 h hold \|\| T37 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 10,000 h hold \|\| T851 temper \|\| 4 K to 643 K (-269.1 °C to 370 °C) YS : 10,000 h hold \|\| T81 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : 10,000 h hold \|\| T8511 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| T62 temper \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : friction stir weld \|\| T87 temper \|\| 20 K to 298 K (-253.1 °C to 25 °C) YSC : sheet & plate \|\| T62 temper \|\| 70 K to 649 K (-203.1 °C to 375.9 °C) %El : friction stir weld \|\| T87 temper \|\| 20 K to 298 K (-253.1 °C to 25 °C) FEN : T851 temper \|\| tested at 4 °K (-269.1 °C), R = -1, axial, total strain range \|\| 180 cycles to 7.1x10⁴ cycles FEN : T851 temper \|\| tested at 78 °K (-195.1 °C), R = -1, axial, total strain range \|\| 90 cycles to 2x10⁵ cycles FSN : T62 temper \|\| tested at 77.6 °K (-195.6 °C), R = -1, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : T62 temper \|\| tested at 20.4 °K (-252.7 °C), R = -1, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : T62 temper \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 3.5, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : T62 temper \|\| tested at 20.4 °K (-252.7 °C), R = -1, K_t = 3.5, axial, maximum stress \|\| 800 cycles to 2x10⁶ cycles FSN : T62 temper \|\| tested at 77.6 °K (-195.6 °C), R = -1, TIG welded, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : T62 temper \|\| tested at 20.4 °K (-252.7 °C), R = -1, TIG welded, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : T87 temper \|\| tested at 77.6 °K (-195.6 °C), R = -1, axial, maximum stress \|\| 600 cycles to 6x10⁴ cycles FSN : T87 temper \|\| tested at 20.4 °K (-252.7 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : T87 temper \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 3.5, axial, maximum stress \|\| 400 cycles to 1x10⁷ cycles FSN : T87 temper \|\| tested at 20.4 °K (-252.7 °C), R = -1, K_t = 3.5, axial, maximum stress \|\| 400 cycles to 2x10⁶ cycles FSN : T87 temper \|\| tested at 77.6 °K (-195.6 °C), R = -1, TIG welded, axial, maximum stress \|\| 1x10³ cycles to 6x10⁶ cycles FSN : T87 temper \|\| tested at 20.4 °K (-252.7 °C), R = -1, TIG welded, axial, maximum stress \|\| 1x10³ cycles to 4x10⁶ cycles
2319 (UNS A92319)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
2618 (UNS A92618)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T61 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T61 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T651 temper \|\| 1000 h hold \|\| 4 K to 643 K (-269.1 °C to 370 °C) UTS : T651 temper \|\| 10,000 h hold \|\| 4 K to 643 K (-269.1 °C to 370 °C) UTS : T6511 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6511 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T61 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T61 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T651 temper \|\| 1000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T651 temper \|\| 10,000 h hold \|\| 4 K to 643 K (-269.1 °C to 370 °C) YS : T6511 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6511 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
3003 (UNS A93003) (WNr 3.0517) (ISO/EN/DIN AlMn1Cu/AlMnCu) (JIS A3003) (AFNOR A-M1)	D : solid \|\| F temper \|\| 4 K to 775 K (-269.1 °C to 501.9 °C) DLL : solid \|\| F temper \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) MTE : solid \|\| F temper \|\| 4 K to 775 K (-269.1 °C to 501.9 °C) CTE : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| F temper \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) TD : solid \|\| F temper \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) SH : solid \|\| F temper \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : O temper \|\| 0.5 h to 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) UTS : H12 temper \|\| 0.5 h to 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H14 temper \|\| 100 h hold \|\| 4 K to 643 K (-269.1 °C to 370 °C) UTS : H14 temper \|\| 1000 h at T \|\| 4 K to 643 K (-269.1 °C to 370 °C) UTS : H14 temper \|\| 10,000 h at T \|\| 4 K to 643 K (-269.1 °C to 370 °C) UTS : H18 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : O temper \|\| 0.5 h to 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : H12 temper \|\| 0.5 h to 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H14 temper \|\| 100 h hold \|\| 4 K to 643 K (-269.1 °C to 370 °C) YS : H14 temper \|\| 1000 h hold \|\| 4 K to 643 K (-269.1 °C to 370 °C) YS : H14 temper \|\| 10,000 h hold \|\| 4 K to 643 K (-269.1 °C to 370 °C) YS : H18 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
3004 (UNS A93004) (WNr 3.0526) (ISO/EN/DIN AlMn1Mg1) (AFNOR A-M1G/A-MG1)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : 10,000 h hold \|\| O temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| H32 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| H34 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| H38 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| O temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| H32 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| H34 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| H38 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C)
3105 (UNS A93105) (WNr 3.0505) (ISO/EN/DIN AlMn0.5Mg0.5/AlMn0.5Mg0.6) (JIS A3105P)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
4032 (UNS A94032) (WNr 1.5411) (JIS A4032FD)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T6 temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
5005 (UNS A95005) (WNr 3.3315/3.3317/3.3318/3.3319) (ISO/EN/DIN Al99.85Mg1/Al99.9Mg1/AlMg1/AlRMg1) (JIS A5005P) (AFNOR A-G0.6)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : 10,000 h hold \|\| O temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| H14 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : 10,000 h hold \|\| H18 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| O temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| H14 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : 10,000 h hold \|\| H18 temper \|\| 77 K to 643 K (-196.1 °C to 370 °C)
5050 (UNS A95050) (WNr 3.3316) (ISO/EN/DIN AlMg1.5) (AFNOR A-G1.5)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : O temper \|\| 1 h to 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H34 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H34 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H38 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H38 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : O temper \|\| 1 h to 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H34 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H34 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H38 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H38 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
5052 (UNS A95052) (WNr 3.3523) (ISO/EN/DIN AlMg2.5) (JIS A5052P) (AFNOR A-G2.5C)	D : solid \|\| 200 K to 773 K (-73.1 °C to 500 °C) DLL : solid \|\| 200 K to 773 K (-73.1 °C to 500 °C) MTE : solid \|\| 200 K to 773 K (-73.1 °C to 500 °C) CTE : solid \|\| 200 K to 773 K (-73.1 °C to 500 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| O temper \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : O temper \|\| 1 h to 100,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) UTS : H32 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : H34 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H38 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : O temper \|\| 1 h to 100,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : H32 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : H34 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H38 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) RHO : solid \|\| annealed \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) SIGMA : solid \|\| annealed \|\| 4 K to 300 K (-269.1 °C to 26.9 °C)
5056 (UNS A95056) (WNr 3.3556) (ISO/EN/DIN AlMg5/AlMg5Cr) (AFNOR A-G5)	CTE : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : O temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) UTS : H32 temper \|\| 10,000 h hold \|\| 20 K to 813 K (-253.1 °C to 540 °C) UTS : H34 temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) UTS : H38 temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : O temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : H32 temper \|\| 10,000 h hold \|\| 20 K to 813 K (-253.1 °C to 540 °C) YS : H34 temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : H38 temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C)
5083 (UNS A95083) (WNr 3.3546/3.3547/3.3548) (ISO/EN/DIN AlMg4.5Mn/AlMg4.5Mn0.7) (JIS A5083) (AFNOR A-G4.5MC)	D : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) DLL : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) MTE : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) CTE : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| O temper \|\| 4 K to 849 K (-269.1 °C to 575.9 °C) TD : solid \|\| O temper \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) SH : solid \|\| O temper \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : O temper \|\| 10 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : O temper \|\| 1000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : O temper \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : H321 temper \|\| 10 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : H321 temper \|\| 1000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : H321 temper \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : O temper \|\| 10 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : O temper \|\| 1000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : O temper \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : H321 temper \|\| 10 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : H321 temper \|\| 1000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : H321 temper \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) FSN : H113 \|\| tested at 88.7 °K (-184.4 °C), R = -1, flexure, maximum stress \|\| 1x10⁵ cycles to 1x10⁷ cycles RHO : solid \|\| H113 temper, across grain \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| H113 temper, with grain \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| H113 temper, across grain \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| H113 temper, with grain \|\| 4 K to 293 K (-269.1 °C to 20 °C)
5086 (UNS A95086) (WNr 3.3545) (ISO/EN/DIN AlMg4/AlMg4Mn) (JIS A5086P/A5086S) (AFNOR A-G4MC)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| F temper \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : O temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : H32 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H32 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H34 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H34 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : O temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : H32 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H32 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H34 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H34 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
5154 (UNS A95154) (ISO/EN/DIN AlMg3.5) (AFNOR A-G3C)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| O temper \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : O temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H32 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H34 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H38 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : O temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H32 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H34 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H38 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) RHO : solid \|\| annealed \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) SIGMA : solid \|\| annealed \|\| 4 K to 300 K (-269.1 °C to 26.9 °C)
5182 (UNS A95182) (ISO/EN/DIN AlMg4.5Mn0.4/AlMg5Mn)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) SSC : annealed \|\| tested at 77 °K (-196.1 °C), 0.008/s \|\| 0 to 0.37 mm/mm strain
5252 (UNS A95252)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
5254 (UNS A95254)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
5356 (UNS A95356) (ISO/EN/DIN AlMg5Cr)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : O temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : H321 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : O temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : H321 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
5454 (UNS A95454) (WNr 3.3537) (ISO/EN/DIN AlMg2.7Mn/AlMg3Mn) (JIS A5454) (AFNOR A-G2.5MC)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : O temper \|\| 10,000 h hold \|\| 4 K to 643 K (-269.1 °C to 370 °C) UTS : H32 temper \|\| 10,000 h hold \|\| 4 K to 643 K (-269.1 °C to 370 °C) UTS : H34 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : O temper \|\| 10,000 h hold \|\| 4 K to 643 K (-269.1 °C to 370 °C) YS : H32 temper \|\| 10,000 h hold \|\| 4 K to 643 K (-269.1 °C to 370 °C) YS : H34 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C)
5456 (UNS A95456) (ISO/EN/DIN AlMg5Mn)	D : solid \|\| 0 K to 589 K (-273.1 °C to 315.6 °C) DLL : solid \|\| 0 K to 589 K (-273.1 °C to 315.6 °C) MTE : solid \|\| 0 K to 589 K (-273.1 °C to 315.6 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| H343 temper \|\| 20 K to 573 K (-253.1 °C to 300 °C) SSC : H343 temper \|\| tested at 194 °K (-79 °C), unknown strain rate, longitudinal \|\| 0 to 0.1 mm/mm strain SSC : H343 temper \|\| tested at 77 °K (-196.1 °C), unknown strain rate, longitudinal \|\| 0 to 0.1 mm/mm strain SSC : H343 temper \|\| tested at 20 °K (-253.1 °C), unknown strain rate, longitudinal \|\| 0 to 0.1 mm/mm strain UTS : O temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : H321 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : H323 temper \|\| 10,000 h hold \|\| 20 K to 298 K (-253.1 °C to 25 °C) YS : O temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : H321 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : H323 temper \|\| 10,000 h hold \|\| 20 K to 298 K (-253.1 °C to 25 °C) FSN : H343 temper \|\| tested at 77 °K (-196.1 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : H343 temper \|\| tested at 20 °K (-253.1 °C), R = -1, axial, maximum stress \|\| 2x10³ cycles to 1x10⁷ cycles
5457 (UNS A95457)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
5652 (UNS A95652)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
5657 (UNS A95657)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
5754 (UNS A95754) (WNr 3.3535) (ISO/EN/DIN AlMg3) (AFNOR A-G3M)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
6005 (UNS A96005) (WNr 3.3210) (ISO/EN/DIN AlSiMg/AlSiMg0.7) (AFNOR A-GS0.5/A-SG0.5)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
6009 (UNS A96009)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
6010 (UNS A96010)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
6013 (UNS A96013) (ISO/EN/DIN AlMg1Si0.8CuMn) (AMS 4216)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
6016 (UNS A96016) (ISO/EN/DIN AlMgSi)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) SSC : natural aged \|\| tested at 77 °K (-196.1 °C), 0.008/s \|\| 0 to 0.32 mm/mm strain
6053 (UNS A96053)	D : solid \|\| 200 K to 589 K (-73.1 °C to 315.6 °C) DLL : solid \|\| 60 K to 589 K (-213.1 °C to 315.6 °C) MTE : solid \|\| 60 K to 589 K (-213.1 °C to 315.6 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
6060 (UNS A96060/A96063) (WNr 3.3206) (ISO/EN/DIN AlMg1SiCu/AlMgSi/AlMgSi0.5) (JIS A6060) (AFNOR AGS)	D : solid \|\| 22 K to 589 K (-251.1 °C to 315.6 °C) DLL : solid \|\| 22 K to 589 K (-251.1 °C to 315.6 °C) MTE : solid \|\| 22 K to 589 K (-251.1 °C to 315.6 °C) CTE : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) SH : solid \|\| 4 K to 811 K (-269.1 °C to 537.9 °C)
6061 (UNS A96061) (WNr 3.3211) (ISO/EN/DIN AlMg0.7Si/AlMg1SiCu) (JIS A6061) (AFNOR A-GSUC)	D : solid \|\| 22 K to 588 K (-251.1 °C to 314.9 °C) DLL : solid \|\| 22 K to 588 K (-251.1 °C to 314.9 °C) MTE : solid \|\| 22 K to 588 K (-251.1 °C to 314.9 °C) CTE : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 499.9 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 499.9 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 499.9 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 499.9 °C) TC : solid \|\| T6 temper \|\| 4 K to 811 K (-269.1 °C to 537.9 °C) TD : solid \|\| T6 temper \|\| 22 K to 811 K (-251.1 °C to 538 °C) SH : solid \|\| T6 temper \|\| 4 K to 900 K (-269.1 °C to 627 °C) SSC : T6 temper \|\| tested at 194 °K (-79 °C), unknown strain rate, longitudinal \|\| 0 to 0.12 mm/mm strain SSC : T6 temper \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate, longitudinal \|\| 0 to 0.17 mm/mm strain SSC : T6 temper \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate, longitudinal \|\| 0 to 0.23 mm/mm strain SSC : T6 temper \|\| tested at 194 °K (-79 °C), unknown strain rate, transverse \|\| 0 to 0.1 mm/mm strain SSC : T6 temper \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate, transverse \|\| 0 to 0.15 mm/mm strain SSC : T6 temper \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate, transverse \|\| 0 to 0.23 mm/mm strain UTS : O temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 539.9 °C) UTS : T4 & T451 tempers \|\| 10,000 h hold \|\| 20 K to 813 K (-253.1 °C to 539.9 °C) UTS : T6 temper \|\| sheet & rolled-and-drawn, 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 539.9 °C) UTS : T6, T651 & T6511 tempers \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 539.9 °C) YS : O temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 539.9 °C) YS : T4 & T451 tempers \|\| 10,000 h hold \|\| 20 K to 813 K (-253.1 °C to 539.9 °C) YS : T6 temper \|\| sheet & rolled-and-drawn, 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 539.9 °C) YS : T6, T651 & T6511 tempers \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 539.9 °C) FSN : T6 temper \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 2x10³ cycles to 6x10⁶ cycles FSN : T6 temper \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 1x10³ cycles to 1x10⁸ cycles HE : solid \|\| T6 temper, grit blasted black anodized \|\| 175 K to 300 K (-98.1 °C to 26.9 °C) RHO : solid \|\| T6 temper \|\| 4 K to 293 K (-269.1 °C to 19.9 °C) SIGMA : solid \|\| T6 temper \|\| 4 K to 293 K (-269.1 °C to 19.9 °C)
6063 (UNS A96063) (WNr 3.3206) (ISO/EN/DIN AlMg0.7Si/AlMgSi0.5/AlSiMgMn) (JIS A6063) (AFNOR AGS)	E : solid \|\| 0 K to 773 K (-273.1 °C to 499.9 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 499.9 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 499.9 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 499.9 °C) TC : solid \|\| as-fabricated \|\| 4 K to 478 K (-269.1 °C to 204.5 °C) UTS : O temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 539.9 °C) UTS : T5 temper \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 539.9 °C) UTS : T6 temper, extrusions \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 369.9 °C) YS : O temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 539.9 °C) YS : T5 temper \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 539.9 °C) YS : T6 temper, except extrusions \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 369.9 °C) RHO : solid \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) SIGMA : solid \|\| 4 K to 300 K (-269.1 °C to 26.9 °C)
6066 (UNS A96066)	D : solid \|\| 200 K to 589 K (-73.1 °C to 315.6 °C) DLL : solid \|\| 60 K to 589 K (-213.1 °C to 315.6 °C) MTE : solid \|\| 60 K to 589 K (-213.1 °C to 315.6 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
6070 (UNS A96070)	D : solid \|\| 200 K to 589 K (-73.1 °C to 315.6 °C) DLL : solid \|\| 60 K to 589 K (-213.1 °C to 315.6 °C) MTE : solid \|\| 60 K to 589 K (-213.1 °C to 315.6 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T6 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
6101 (UNS A96101) (WNr 3.2307) (ISO/EN/DIN E-Al1MgSi0.5/E-AlMgSi/EAlMgSi) (JIS A6101PB/A6101SB/A6101SBC/A6101TB)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T6 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T61 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T63 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T64 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T8 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T61 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T63 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T64 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T8 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
6110 (UNS A96110)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
6151 (UNS A96165) (ISO/EN/DIN AlSiMg0.5Mn) (JIS A6151FD/A6151FH)	D : solid \|\| 200 K to 644 K (-73.1 °C to 370.9 °C) DLL : solid \|\| 200 K to 644 K (-73.1 °C to 370.9 °C) MTE : solid \|\| 200 K to 644 K (-73.1 °C to 370.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T6 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
6201 (UNS A96201)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T81 temper \|\| 10 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) UTS : T81 temper \|\| 1000 h hold \|\| 77 K to 478 K (-196.1 °C to 205 °C) UTS : T81 temper \|\| 10,000 h hold \|\| 77 K to 478 K (-196.1 °C to 205 °C) YS : T81 temper \|\| 10 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) YS : T81 temper \|\| 1000 h hold \|\| 77 K to 478 K (-196.1 °C to 205 °C) YS : T81 temper \|\| 10,000 h hold \|\| 77 K to 478 K (-196.1 °C to 205 °C)
6262 (UNS A96262) (ISO/EN/DIN AlMg1SiPb)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T9 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T9 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T9 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T9 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T9 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T9 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
6351 (UNS A96351) (ISO/EN/DIN AlSi1Mg/AlSi1Mg0.5Mn) (JIS A6151FD/A6151FH)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T5 temper \|\| 10 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) UTS : T5 temper \|\| 10,000 h hold \|\| 77 K to 478 K (-196.1 °C to 205 °C) UTS : T6 temper \|\| 10 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) UTS : T6 temper \|\| 10,000 h hold \|\| 77 K to 423 K (-196.1 °C to 150 °C) YS : T5 temper \|\| 10 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) YS : T5 temper \|\| 10,000 h hold \|\| 77 K to 478 K (-196.1 °C to 205 °C) YS : T6 temper \|\| 10 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) YS : T6 temper \|\| 10,000 h hold \|\| 77 K to 423 K (-196.1 °C to 150 °C)
7005 (UNS A97005) (ISO/EN/DIN AlZn4.5Mg1.5Mn)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T53 temper \|\| 100 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : T53 temper \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : T6 temper \|\| sheet \|\| 77 K to 298 K (-196.1 °C to 25 °C) UTS : T63 & T6351 tempers \|\| 100 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : T63 & T6351 tempers \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : T53 temper \|\| 100 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : T53 temper \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : T6 temper \|\| sheet \|\| 77 K to 298 K (-196.1 °C to 25 °C) YS : T63 & T6351 tempers \|\| 100 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : T63 & T6351 tempers \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C)
7010 (UNS A97010) (ISO/EN/DIN AlZn6MgCu)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
7039 (UNS A97039)	D : solid \|\| 0 K to 700 K (-273.1 °C to 426.9 °C) DLL : solid \|\| 0 K to 700 K (-273.1 °C to 426.9 °C) MTE : solid \|\| 0 K to 700 K (-273.1 °C to 426.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| T61 temper \|\| 6 K to 300 K (-267.1 °C to 26.9 °C) SSC : T6 temper \|\| tested at 194 °K (-79 °C), unknown strain rate, longitudinal \|\| 0 to 0.1 mm/mm strain SSC : T6 temper \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate, longitudinal \|\| 0 to 0.13 mm/mm strain SSC : T6 temper \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate, longitudinal \|\| 0 to 0.15 mm/mm strain SSC : T6 temper \|\| tested at 194 °K (-79 °C), unknown strain rate, transverse \|\| 0 to 0.1 mm/mm strain SSC : T6 temper \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate, transverse \|\| 0 to 0.11 mm/mm strain SSC : T6 temper \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate, transverse \|\| 0 to 0.13 mm/mm strain UTS : T6 & T6151 tempers \|\| sheet & plate \|\| 4 K to 298 K (-269.1 °C to 25 °C) UTS : T63 & T6351 tempers \|\| 10 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) UTS : T63 & T6351 tempers \|\| 100 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) UTS : T63 & T6351 tempers \|\| 1000 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) UTS : T63 & T6351 tempers \|\| 10,000 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) YS : T6 & T6151 tempers \|\| sheet & plate \|\| 4 K to 298 K (-269.1 °C to 25 °C) YS : T63 & T6351 tempers \|\| 10 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) YS : T63 & T6351 tempers \|\| 100 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) YS : T63 & T6351 tempers \|\| 1000 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) YS : T63 & T6351 tempers \|\| 10,000 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) FSN : T6 temper, smooth \|\| tested at 194 °K (-79 °C), R = -1, axial, maximum stress \|\| 400 cycles to 1x10⁶ cycles FSN : T6 temper, smooth \|\| tested at 77.6 °K (-195.6 °C), R = -1, axial, maximum stress \|\| 2x10³ cycles to 1x10⁶ cycles FSN : T6 temper, smooth \|\| tested at 194 °K (-79 °C), R = 0.01, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : T6 temper, smooth \|\| tested at 77.6 °K (-195.6 °C), R = 0.01, axial, maximum stress \|\| 400 cycles to 2x10⁶ cycles FSN : T6 temper, notched \|\| tested at 194 °K (-79 °C), K_t = 3.5, R = -1, axial, maximum stress \|\| 400 cycles to 4x10⁶ cycles FSN : T6 temper, notched \|\| tested at 77.6 °K (-195.6 °C), K_t = 3.5, R = -1, axial, maximum stress \|\| 600 cycles to 1x10⁶ cycles FSN : T6 temper, notched \|\| tested at 194 °K (-79 °C), K_t = 8.0, R = -1, axial, maximum stress \|\| 400 cycles to 2x10⁶ cycles FSN : T6 temper, notched \|\| tested at 77.6 °K (-195.6 °C), K_t = 8.0, R = -1, axial, maximum stress \|\| 1x10³ cycles to 2x10⁶ cycles FSN : T6 temper, TIG weld \|\| tested at 194 °K (-79 °C), R = -1, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : T6 temper, TIG weld \|\| tested at 77.6 °K (-195.6 °C), R = -1, axial, maximum stress \|\| 600 cycles to 2x10⁶ cycles FSN : T6151 temper, plate, smooth \|\| tested at 77.6 °K (-195.6 °C), R = 0.1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T6151 temper, plate, notched \|\| tested at 77.6 °K (-195.6 °C), R = 0.1, axial, K_t = 3.0, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles RHO : solid \|\| O temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| T61 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| O temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| T61 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C)
7050 (UNS A97050) (ISO/EN/DIN AlZn6CuMgZr)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T7452 temper \|\| forgings, 10 h hold \|\| 77 K to 478 K (-196.1 °C to 205 °C) UTS : T7452 temper \|\| forgings, 100 h hold \|\| 77 K to 478 K (-196.1 °C to 205 °C) UTS : T7452 temper \|\| forgings, 10,000 h hold \|\| 77 K to 478 K (-196.1 °C to 205 °C) YS : T7452 temper \|\| forgings, 10 h hold \|\| 77 K to 478 K (-196.1 °C to 205 °C) YS : T7452 temper \|\| forgings, 100 h hold \|\| 77 K to 478 K (-196.1 °C to 205 °C) YS : T7452 temper \|\| forgings, 10,000 h hold \|\| 77 K to 478 K (-196.1 °C to 205 °C)
7072 (UNS A97072)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
7075 (UNS A97075) (WNr 3.4365) (ISO/EN/DIN AlZn5.5MgCu/AlZn6MgCu1.5/AlZnMgCu1.5) (JIS A7075) (ASTM B316) (AMS 22771/4149/4179/4344) (AFNOR A-Z5GU)	D : solid \|\| 0 K to 700 K (-273.1 °C to 426.9 °C) DLL : solid \|\| 0 K to 700 K (-273.1 °C to 426.9 °C) MTE : solid \|\| 0 K to 700 K (-273.1 °C to 426.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| T6 temper, as-received \|\| 0 K to 700 K (-273.1 °C to 427 °C) TC : solid \|\| T6 temper, annealed \|\| 0 K to 700 K (-273.1 °C to 427 °C) TD : solid \|\| T6 temper, as-received \|\| 116 K to 700 K (-157.1 °C to 426.9 °C) TD : solid \|\| T6 temper, annealed \|\| 116 K to 700 K (-157.1 °C to 426.9 °C) SH : solid \|\| 1 K to 793 K (-272.1 °C to 520 °C) SSC : T6 temper \|\| tested at 195 °K (-78 °C), 3.3x10^-⁴/s \|\| 0 to 0.1 mm/mm strain SSC : T6 temper \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.1 mm/mm strain SSC : T6 temper \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.13 mm/mm strain UTS : O temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 & T6511 tempers \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) UTS : T73 temper \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) UTS : T76 & T651 tempers \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : O temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 & T6511 tempers \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : T73 temper \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) YS : T76 & T651 tempers \|\| 10,000 h hold \|\| 4 K to 813 K (-269.1 °C to 540 °C) %El : 0.635 mm (0.025 inch) sheet \|\| T6 temper, longitudinal \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : 3.17 mm (0.125 inch) sheet \|\| T6 temper, longitudinal \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : 19 mm (0.75 inch) bar \|\| T6 temper, longitudinal \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : average of all \|\| T6 temper, longitudinal \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) FSN : T6 temper, bar \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 2x10³ cycles to 4x10⁶ cycles FSN : T6 temper, bar \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁶ cycles FSN : T6 temper, bar \|\| tested at 194 °K (-79 °C), R = -1, K_t = 3.2, flexure, maximum stress \|\| 8x10³ cycles to 1x10⁷ cycles FSN : T6 temper, bar \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 3.2, flexure, maximum stress \|\| 8x10³ cycles to 1x10⁷ cycles FSN : T6 temper, bar \|\| tested at 20.4 °K (-252.7 °C), R = -1, K_t = 3.2, flexure, maximum stress \|\| 4x10³ cycles to 1x10⁶ cycles FSN : T6 temper, sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, axial, maximum stress \|\| 2x10³ cycles to 1x10⁷ cycles FSN : T6 temper, sheet \|\| tested at 20.4 °K (-252.7 °C), R = -1, axial, maximum stress \|\| 1x10³ cycles to 1x10⁷ cycles FSN : T6 temper, sheet \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 3.5, axial, maximum stress \|\| 400 cycles to 4x10⁶ cycles FSN : T6 temper, sheet \|\| tested at 20.4 °K (-252.7 °C), R = -1, K_t = 3.5, axial, maximum stress \|\| 400 cycles to 2x10⁶ cycles NE : solid \|\| polished \|\| 75 K to 803 K (-198.1 °C to 530 °C) RHO : solid \|\| T6 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| T73 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| T6 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| T73 temper \|\| 4 K to 293 K (-269.1 °C to 20 °C)
7079 (UNS A97079)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T6 & T651 tempers \|\| 0.5 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : T6 & T651 tempers \|\| 10 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : T6 & T651 tempers \|\| 100 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : T6 & T651 tempers \|\| 1000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : T6 & T651 tempers \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T6 & T651 tempers \|\| 0.5 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T6 & T651 tempers \|\| 10 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T6 & T651 tempers \|\| 100 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T6 & T651 tempers \|\| 1000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T6 & T651 tempers \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C)
7175 (UNS A97175) (ISO/EN/DIN AlZn5.5MgCu) (ASTM B316) (AMS 22771/4149/4179/4344)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T74 & T736 tempers \|\| 10 h hold \|\| 20 K to 503 K (-253.1 °C to 230 °C) UTS : T74 & T736 tempers \|\| 1000 h hold \|\| 20 K to 503 K (-253.1 °C to 230 °C) UTS : T74 & T736 tempers \|\| 10,000 h hold \|\| 20 K to 503 K (-253.1 °C to 230 °C) YS : T74 & T736 tempers \|\| 10 h hold \|\| 20 K to 503 K (-253.1 °C to 230 °C) YS : T74 & T736 tempers \|\| 1000 h hold \|\| 20 K to 503 K (-253.1 °C to 230 °C) YS : T74 & T736 tempers \|\| 10,000 h hold \|\| 20 K to 503 K (-253.1 °C to 230 °C)
7178 (UNS A97178) (ISO/EN/DIN AlZn7MgCu)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T6 temper \|\| 10 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : T6 temper \|\| 1000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : T6 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T6 temper \|\| 10 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T6 temper \|\| 1000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T6 temper \|\| 10,000 h hold \|\| 20 K to 643 K (-253.1 °C to 370 °C)
7249 (UNS A97249) (ISO/EN/DIN AlZn8MgCu)	SH : solid \|\| T76511 temper \|\| 22 K to 304 K (-251.1 °C to 30.9 °C)
7475 (UNS A97475) (WNr 3.4365) (ISO/EN/DIN AlZn5.5MgCu/AlZnMgCu1.5)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T61 temper \|\| 10 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) UTS : T61 temper \|\| 1000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) UTS : T61 temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) UTS : T761 temper \|\| 10 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) UTS : T761 temper \|\| 1000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) UTS : T761 temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : T61 temper \|\| 10 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : T61 temper \|\| 1000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : T61 temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : T761 temper \|\| 10 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : T761 temper \|\| 1000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C) YS : T761 temper \|\| 10,000 h hold \|\| 77 K to 813 K (-196.1 °C to 540 °C)
8090 (UNS A98090)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TC : solid \|\| T352 temper, forging \|\| 4 K to 293 K (-269.1 °C to 20 °C) TC : solid \|\| T8771 temper, rolled plate \|\| 140 K to 403 K (-133.1 °C to 130 °C) TD : solid \|\| T352 temper forging \|\| 155 K to 293 K (-118.1 °C to 20 °C) TD : solid \|\| T8771 temper, rolled plate \|\| 155 K to 403 K (-118.1 °C to 130 °C) SH : solid \|\| 155 K to 673 K (-118.1 °C to 400 °C) UTS : sheet \|\| T6 temper \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) UTS : plate, T3 temper \|\| longitudinal \|\| 4 K to 295 K (-269.1 °C to 22 °C) UTS : plate, T3 temper \|\| transverse \|\| 4 K to 295 K (-269.1 °C to 22 °C) UTS : plate, T8xxx tempers \|\| longitudinal \|\| 4 K to 533 K (-269.1 °C to 260 °C) UTS : plate, T8xxx tempers \|\| transverse \|\| 4 K to 533 K (-269.1 °C to 260 °C) UTS : plate, T8xxx tempers \|\| 45 degrees \|\| 4 K to 533 K (-269.1 °C to 260 °C) UTS : plate, T8xxx tempers \|\| through thickness \|\| 4 K to 533 K (-269.1 °C to 260 °C) YS : sheet \|\| T6 temper \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) YS : plate, T3 temper \|\| longitudinal \|\| 4 K to 295 K (-269.1 °C to 22 °C) YS : plate, T3 temper \|\| transverse \|\| 4 K to 295 K (-269.1 °C to 22 °C) YS : plate, T8xxx tempers \|\| longitudinal \|\| 4 K to 533 K (-269.1 °C to 260 °C) YS : plate, T8xxx tempers \|\| transverse \|\| 4 K to 533 K (-269.1 °C to 260 °C) YS : plate, T8xxx tempers \|\| 45 degrees \|\| 4 K to 533 K (-269.1 °C to 260 °C) YS : plate, T8xxx tempers \|\| through thickness \|\| 4 K to 533 K (-269.1 °C to 260 °C) %El : sheet \|\| T6 temper \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : plate, T3 temper \|\| longitudinal \|\| 4 K to 295 K (-269.1 °C to 22 °C) %El : plate, T3 temper \|\| transverse \|\| 4 K to 295 K (-269.1 °C to 22 °C) %El : plate, T8xxx tempers \|\| longitudinal \|\| 4 K to 533 K (-269.1 °C to 260 °C) %El : plate, T8xxx tempers \|\| transverse \|\| 4 K to 533 K (-269.1 °C to 260 °C) %El : plate, T8xxx tempers \|\| 45 degrees \|\| 4 K to 533 K (-269.1 °C to 260 °C) %El : plate, T8xxx tempers \|\| through thickness \|\| 4 K to 533 K (-269.1 °C to 260 °C) FSN : T6 temper \|\| tested at 77 °K (-196.1 °C), R = 0, axial, stress amplitude \|\| 1.8x10⁴ cycles to 2.2x10⁶ cycles
201.0 (UNS A02010)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
208.0 (UNS A02080)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
224.0 (UNS A02240)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
242.0 (UNS A02420) (JIS AC5A/AC5A.1AC5A.2/C5AS) (AFNOR A-U4NT)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T571 temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T571 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T571 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T77 temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T77 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T77 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T571 temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T571 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T571 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T77 temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T77 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T77 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
249.0 (UNS A02490)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T7 temper \|\| 0.5 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) UTS : T7 temper \|\| 10 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) UTS : T7 temper \|\| 100 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) UTS : T7 temper \|\| 1000 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) UTS : T7 temper \|\| 10,000 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) YS : T7 temper \|\| 0.5 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) YS : T7 temper \|\| 10 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) YS : T7 temper \|\| 100 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) YS : T7 temper \|\| 1000 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) YS : T7 temper \|\| 10,000 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C)
295.0 (UNS A02950) (ISO/EN/DIN AlCu4S/AlCu4Ti) (JIS AC1A/C1AS) (GB & GB/T ZAlCu4)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
319.0 (UNS A03190) (ISO/EN/DIN AlSi6Cu4) (JIS AC2B) (GB & GB/T ZAlSi7Cu4)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : F temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T5 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T5 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T5 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T5 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T5 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T5 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
332.0 (UNS A03320) (JIS C8CS)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
333.0 (UNS A03330) (WNr 3.2163) (ISO/EN/DIN AlSi9Cu3) (JIS AC4B) (AFNOR A-S9U3)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T5 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T5 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T5 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T7 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T7 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T7 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T5 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T5 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T5 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T7 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T7 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T7 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
336.0 (UNS A03360) (JIS AC8A/C8AS)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T551 temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T551 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T551 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T551 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T551 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T551 temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T551 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T551 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T551 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T551 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
354.0 (UNS A03540) (GB & GB/T ZAlSi9Cu2Mg)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T6 temper \|\| 0.5 h hold \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) UTS : T6 temper \|\| 10 h hold \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) UTS : T6 temper \|\| 100 h hold \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) UTS : T6 temper \|\| 1000 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) UTS : T6 temper \|\| 10,000 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) YS : T6 temper \|\| 0.5 h hold \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) YS : T6 temper \|\| 10 h hold \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) YS : T6 temper \|\| 100 h hold \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) YS : T6 temper \|\| 1000 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) YS : T6 temper \|\| 10,000 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C)
355.0 (UNS A03550) (ISO/EN/DIN AlSi5Cu1Mg) (JIS AC4D/C4DS) (GB & GB/T ZAlSi5CulMg)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) TD : solid \|\| 20 K to 573 K (-253.1 °C to 300 °C) UTS : T51 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T51 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T51 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T51 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
356.0 (UNS A03560) (WNr 3.2371) (ISO/EN/DIN AlSi7Mg) (JIS AC4C/AC4CH/C4CS) (SAE J452323) (AMS 4217/4260/4261/4284/4285/4286) (AFNOR A-S7G) (GB & GB/T ZAlSi7Mg/ZAlSi7MgA)	D : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) DLL : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) MTE : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) SSC : T6 temper \|\| tested at 195 °K (-78 °C), 3.3x10^-⁴/s \|\| 0 to 0.9 mm/mm strain SSC : T6 temper \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.1 mm/mm strain SSC : T6 temper \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.9 mm/mm strain UTS : T51 temper \|\| sand cast \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| sand cast \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| permanent mold \|\| 20 K to 643 K (-253.1 °C to 370 °C) UTS : T7 temper \|\| sand cast \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T7 temper \|\| permanent mold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T51 temper \|\| sand cast \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| sand cast \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| permanent mold \|\| 20 K to 643 K (-253.1 °C to 370 °C) YS : T7 temper \|\| sand cast \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T7 temper \|\| permanent mold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
359.0 (UNS A03590) (AFNOR A-S9)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T6 temper \|\| 10 h hold \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) UTS : T6 temper \|\| 1000 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) UTS : T6 temper \|\| 10,000 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) UTS : T62 temper \|\| 10 h hold \|\| 77 K to 298 K (-196.1 °C to 25 °C) UTS : T62 temper \|\| 1000 h hold \|\| 77 K to 423 K (-196.1 °C to 150 °C) UTS : T62 temper \|\| 10,000 h hold \|\| 77 K to 423 K (-196.1 °C to 150 °C) YS : T6 temper \|\| 10 h hold \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) YS : T6 temper \|\| 1000 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) YS : T6 temper \|\| 10,000 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) YS : T62 temper \|\| 10 h hold \|\| 77 K to 298 K (-196.1 °C to 25 °C) YS : T62 temper \|\| 1000 h hold \|\| 77 K to 423 K (-196.1 °C to 150 °C) YS : T62 temper \|\| 10,000 h hold \|\| 77 K to 423 K (-196.1 °C to 150 °C)
360.0 (UNS A03600) (WNr 3.2381/3.2385) (ISO/EN/DIN AlSi10Mg) (JIS AC4A/ADC3/C4AS) (AFNOR A-S9G) (GB & GB/T ZAlSi9Mg)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : F temper \|\| 0.5 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) UTS : F temper \|\| 10 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) UTS : F temper \|\| 100 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) UTS : F temper \|\| 1000 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) UTS : F temper \|\| 10,000 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) YS : F temper \|\| 0.5 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) YS : F temper \|\| 10 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) YS : F temper \|\| 100 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) YS : F temper \|\| 1000 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) YS : F temper \|\| 10,000 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C)
380.0 (UNS A03800) (ISO/EN/DIN AlSi8Cu3Fe)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : F temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
384.0 (UNS A03840)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : F temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
518.0 (UNS A05180) (WNr 3.3292) (ISO/EN/DIN AlMg9) (JIS ADC5)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
520.0 (UNS A05200) (ISO/EN/DIN AlMg10) (JIS AC7B) (GB & GB/T ZAlMg10)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
710.0 (UNS A07100)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : F temper \|\| 0.5 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) UTS : F temper \|\| 10 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) UTS : F temper \|\| 100 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) UTS : F temper \|\| 1000 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) UTS : F temper \|\| 10,000 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) YS : F temper \|\| 0.5 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) YS : F temper \|\| 10 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) YS : F temper \|\| 100 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) YS : F temper \|\| 1000 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C) YS : F temper \|\| 10,000 h hold \|\| 77 K to 533 K (-196.1 °C to 260 °C)
A201.0 (UNS A12010/A12011)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T7 temper \|\| sand castings 100 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) UTS : T7 temper \|\| sand castings 1000 h hold \|\| 4 K to 589 K (-269.1 °C to 315.6 °C) UTS : T7 temper \|\| sand castings 10,000 h hold \|\| 4 K to 589 K (-269.1 °C to 315.6 °C) YS : T7 temper \|\| sand castings 100 h hold \|\| 4 K to 478 K (-269.1 °C to 205 °C) YS : T7 temper \|\| sand castings 1000 h hold \|\| 4 K to 589 K (-269.1 °C to 315.6 °C) YS : T7 temper \|\| sand castings 10,000 h hold \|\| 4 K to 589 K (-269.1 °C to 315.6 °C)
A206.0 (UNS A12060)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
A240.0 (UNS A12400)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
A319 (UNS A13190)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
A355.0 (UNS A13550)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
A356.0 (UNS A13560) (ISO/EN/DIN AlSi7Mg) (JIS AC4C/AC4CH) (AMS 4218) (GB & GB/T ZAlSi7Mg/ZAlSi7MgA)	D : solid \|\| 22 K to 842 K (-251.1 °C to 568.9 °C) DLL : solid \|\| 22 K to 842 K (-251.1 °C to 568.9 °C) MTE : solid \|\| 22 K to 842 K (-251.1 °C to 568.9 °C) E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
A357	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
A360.0 (UNS A03600) (ISO/EN/DIN AlSi10Mg) (JIS AC4A/ADC3) (ASTM SG100A) (GB & GB/T ZAlSi9Mg)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : F temper \|\| 0.5 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) UTS : F temper \|\| 10 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) UTS : F temper \|\| 100 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) UTS : F temper \|\| 1000 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) UTS : F temper \|\| 10,000 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) YS : F temper \|\| 0.5 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) YS : F temper \|\| 10 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) YS : F temper \|\| 100 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) YS : F temper \|\| 1000 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C) YS : F temper \|\| 10,000 h hold \|\| 193 K to 643 K (-80.1 °C to 370 °C)
A380.0 (UNS A13800) (JIS ADC10) (ASTM SC84A) (AFNOR A-S10U4)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : F temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
A390 (UNS A13900)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
B443.0 (UNS A24430)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : F temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : F temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : F temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
C355.0 (UNS A33350)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) UTS : T6 temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) UTS : T6 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 0.5 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 10 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 100 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 1000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C) YS : T6 temper \|\| 10,000 h hold \|\| 77 K to 643 K (-196.1 °C to 370 °C)
E319	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
AlCu4TiMg	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
CZ42	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
Al - 1 Li (3.8 a/o Li)	SSC : 1x10^-⁴/s, equal-channel angular hydro-extrusion (ECAH) \|\| tested at 4.2 °K (-268.9 °C) \|\| 0 to 0.257 mm/mm strain SSC : 1x10^-⁴/s, equal-channel angular hydro-extrusion (ECAH) \|\| tested at 77 °K (-196.1 °C) \|\| 0 to 0.11 mm/mm strain UTS : equal-channel angular hydro-extrusion (ECAH) \|\| 77 K to 400 K (-196.1 °C to 126.9 °C) YS : equal-channel angular hydro-extrusion (ECAH) \|\| 4 K to 400 K (-268.9 °C to 126.9 °C) %El : equal-channel angular hydro-extrusion (ECAH) \|\| 77 K to 400 K (-196.1 °C to 126.9 °C)
Al - 1.3 Li (4.9 a/o Li)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
Al - 2.8 Li (wt %) (10 a/o Li)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
Al - 3.37 Li (wt %) (12 a/o Li)	E : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) G : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) v : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C) K : solid \|\| 0 K to 773 K (-273.1 °C to 500 °C)
Al - 0.5 Cu (wt %)	TC : solid \|\| 4 K to 923 K (-269.1 °C to 650 °C) RHO : solid \|\| 1 K to 923 K (-272.1 °C to 650 °C) SIGMA : solid \|\| 1 K to 923 K (-272.1 °C to 650 °C)
Al - 1 Cu (wt %)	TC : solid \|\| 4 K to 913 K (-269.1 °C to 639.9 °C) RHO : solid \|\| 1 K to 900 K (-272.1 °C to 627 °C) SIGMA : solid \|\| 1 K to 900 K (-272.1 °C to 627 °C)
Al - 1.5 Cu (wt %)	TC : solid \|\| 4 K to 873 K (-269.1 °C to 599.9 °C)
Al - 3 Cu (wt %)	TC : solid \|\| 4 K to 873 K (-269.1 °C to 599.9 °C) RHO : solid \|\| 1 K to 875 K (-272.1 °C to 602 °C) SIGMA : solid \|\| 1 K to 875 K (-272.1 °C to 602 °C)
Al - 4 Cu (wt %)	TC : solid \|\| 4 K to 833 K (-269.1 °C to 559.9 °C)
Al - 5 Cu (wt %)	TC : solid \|\| 4 K to 833 K (-269.1 °C to 559.9 °C) RHO : solid \|\| 1 K to 835 K (-272.1 °C to 562 °C) SIGMA : solid \|\| 1 K to 835 K (-272.1 °C to 562 °C)
Al - 10 Cu (wt %)	TC : solid \|\| 4 K to 821 K (-269.1 °C to 547.9 °C) RHO : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C) SIGMA : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C)
Al - 15 Cu (wt %)	TC : solid \|\| 4 K to 821 K (-269.1 °C to 547.9 °C) RHO : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C) SIGMA : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C)
Al - 20 Cu (wt %)	TC : solid \|\| 4 K to 821 K (-269.1 °C to 547.9 °C) RHO : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C) SIGMA : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C)
Al - 21 Cu (wt %)	TC : solid \|\| 4 K to 821 K (-269.1 °C to 547.9 °C)
Al - 25 Cu (wt %)	TC : solid \|\| 4 K to 821 K (-269.1 °C to 547.9 °C) RHO : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C) SIGMA : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C)
Al - 30 Cu (wt %)	TC : solid \|\| 4 K to 821 K (-269.1 °C to 547.9 °C) RHO : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C) SIGMA : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C)
Al - 33 Cu (wt %)	TC : solid \|\| 4 K to 821 K (-269.1 °C to 547.9 °C)
Al - 35 Cu (wt %)	TC : solid \|\| 4 K to 821 K (-269.1 °C to 547.9 °C) RHO : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C) SIGMA : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C)
Al - 37 Cu (wt %)	TC : solid \|\| 4 K to 821 K (-269.1 °C to 547.9 °C)
Al - 40 Cu (wt %)	TC : solid \|\| 4 K to 821 K (-269.1 °C to 547.9 °C)
Al - 45 Cu (wt %)	TC : solid \|\| 4 K to 821 K (-269.1 °C to 547.9 °C) RHO : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C) SIGMA : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C)
Al - 0.5 Mg (wt %)	TC : solid \|\| 4 K to 922 K (-269.1 °C to 648.9 °C) RHO : solid \|\| 1 K to 923 K (-272.1 °C to 650 °C) SIGMA : solid \|\| 1 K to 923 K (-272.1 °C to 650 °C)
Al - 1 Mg (wt %)	TC : solid \|\| 4 K to 913 K (-269.1 °C to 639.9 °C) RHO : solid \|\| 1 K to 800 K (-272.1 °C to 527 °C) SIGMA : solid \|\| 1 K to 800 K (-272.1 °C to 527 °C)
Al - 3 Mg (wt %)	TC : solid \|\| 4 K to 881 K (-269.1 °C to 607.9 °C) RHO : solid \|\| 1 K to 800 K (-272.1 °C to 527 °C) SIGMA : solid \|\| 1 K to 800 K (-272.1 °C to 527 °C)
Al - 5 Mg (wt %)	TC : solid \|\| 4 K to 849 K (-269.1 °C to 575.9 °C) RHO : solid \|\| not cold worked \|\| 1 K to 849 K (-272.1 °C to 576 °C) SIGMA : solid \|\| not cold worked \|\| 1 K to 849 K (-272.1 °C to 576 °C)
Al - 7 Mg (wt %)	RHO : solid \|\| not cold worked \|\| 1 K to 700 K (-272.1 °C to 427 °C) SIGMA : solid \|\| not cold worked \|\| 1 K to 700 K (-272.1 °C to 427 °C)
Al - 8 Mg (wt %)	RHO : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C) SIGMA : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C)
Al - 10 Mg (wt %)	TC : solid \|\| 4 K to 788 K (-269.1 °C to 514.9 °C) RHO : solid \|\| 1 K to 789 K (-272.1 °C to 516 °C) SIGMA : solid \|\| 1 K to 789 K (-272.1 °C to 516 °C)
Copper alloys	Property : Condition // Data range
UNS C10100 (OFE) (UNS C10100) (ISO/EN/DIN Cu-OFE) (ASTM F68)	D : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) DLL : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) MTE : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) CTE : solid \|\| 4 K to 800 K (-269.1 °C to 526.9 °C) E : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) G : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) v : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) K : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) TC : solid \|\| residual resistivity ratio of 30 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| residual resistivity ratio of 100 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| residual resistivity ratio of 300 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| residual resistivity ratio of 1000 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| residual resistivity ratio of 3000 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) SH : solid \|\| 1 K to 1300 K (-272.1 °C to 1026.8 °C) FEN : annealed \|\| tested at 4 °K (-269.1 °C), R = -1, axial, total strain range \|\| 150 cycles to 9.2x10⁴ cycles FEN : annealed \|\| tested at 78 °K (-195.1 °C), R = -1, axial, total strain range \|\| 80 cycles to 2.2x10⁵ cycles S : solid \|\| 100 K to 1300 K (-173.1 °C to 1026.8 °C)
UNS C10200 (OFHC/OF) (UNS C10200) (ISO/EN/DIN CW008A/Cu-OF)	D : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) DLL : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) MTE : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) CTE : solid \|\| 4 K to 800 K (-269.1 °C to 526.9 °C) E : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) G : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) v : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) K : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) TC : solid \|\| residual resistivity ratio of 30 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| residual resistivity ratio of 100 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| residual resistivity ratio of 300 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| residual resistivity ratio of 1000 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) TC : solid \|\| residual resistivity ratio of 3000 \|\| 1 K to 1358 K (-272.1 °C to 1085 °C) SH : solid \|\| 1 K to 1300 K (-272.1 °C to 1026.8 °C) SSC : cold-drawn 60%, 3.3x10^-⁴/s \|\| tested at 20 °K (-253.1 °C), 60% reduction \|\| 0 to 0.26 mm/mm strain SSC : cold-drawn 60%, 3.3x10^-⁴/s \|\| tested at 76 °K (-197.1 °C), 60% reduction \|\| 0 to 0.18 mm/mm strain SSC : cold-drawn 60%, 3.3x10^-⁴/s \|\| tested at 194 °K (-79 °C), 60% reduction \|\| 0 to 0.5 mm/mm strain SSC : unknown strain rate \|\| tested at 4 °K (-269.1 °C), 60% reduction \|\| 0 to 0.26 mm/mm strain SSCC : as-received \|\| tested at 77 °K (-196.1 °C), 4000/s \|\| 0 to 0.89 mm/mm strain SSCC : as-received \|\| tested at 77 °K (-196.1 °C), 8000/s \|\| 0 to 0.39 mm/mm strain SSCC : annealed \|\| tested at 77 °K (-196.1 °C), 4000/s \|\| 0 to 0.82 mm/mm strain SSCC : annealed \|\| tested at 77 °K (-196.1 °C), 8000/s \|\| 0 to 0.55 mm/mm strain UTS : annealed \|\| 10 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : annealed \|\| 20 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : annealed \|\| 30 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : annealed \|\| 40 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : annealed \|\| 50 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) UTS : annealed \|\| 65 micron GS \|\| 4 K to 755 K (-269.1 °C to 482.3 °C) YS : annealed \|\| 10 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) YS : annealed \|\| 20 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) YS : annealed \|\| 30 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) YS : annealed \|\| 40 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) YS : annealed \|\| 50 micron GS \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) FSN : annealed \|\| tested at 20 °K (-253.1 °C), R = -1, maximum stress \|\| 1.3x10⁴ cycles to 5x10⁶ cycles FSN : annealed \|\| tested at 4 °K (-269.1 °C), R = -1, maximum stress \|\| 1.3x10⁴ cycles to 3x10⁶ cycles RHO : solid \|\| annealed \|\| 4 K to 740 K (-269.1 °C to 466.9 °C) RHO : solid \|\| 60% cold-drawn \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| annealed \|\| 4 K to 740 K (-269.1 °C to 466.9 °C) SIGMA : solid \|\| 60% cold-drawn \|\| 4 K to 293 K (-269.1 °C to 20 °C) S : solid \|\| 100 K to 1300 K (-173.1 °C to 1026.8 °C)
UNS C10300 (UNS C10300) (ISO/EN/DIN CW021A/Cu-PHC)	D : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) DLL : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) MTE : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) CTE : solid \|\| 4 K to 800 K (-269.1 °C to 526.9 °C) E : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) G : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) v : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) K : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C)
UNS C10400 (UNS C10400) (WNr 2.0040) (ISO/EN/DIN CuAg0.05(OF)/OF-Cu)	D : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) DLL : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) MTE : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) CTE : solid \|\| 4 K to 800 K (-269.1 °C to 526.9 °C) E : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) G : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) v : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) K : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) TC : solid \|\| 73 K to 573 K (-200.1 °C to 300 °C) SSC : annealed \|\| tested at 4 °K (-269.1 °C), unknown strain rate \|\| 0 to 0.47 mm/mm strain SSC : annealed \|\| tested at 76 °K (-197.1 °C), unknown strain rate \|\| 0 to 0.4 mm/mm strain SSC : hard \|\| tested at 4 °K (-269.1 °C), unknown strain rate \|\| 0 to 0.18 mm/mm strain SSC : hard \|\| tested at 76 °K (-197.1 °C), unknown strain rate \|\| 0 to 0.7 mm/mm strain SSC : half hard \|\| tested at 4 °K (-269.1 °C), unknown strain rate \|\| 0 to 0.37 mm/mm strain SSC : half hard \|\| tested at 76 °K (-197.1 °C), unknown strain rate \|\| 0 to 0.18 mm/mm strain UTS : annealed \|\| 80 micron grain size \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) UTS : half hard \|\| 77 micron grain size \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) UTS : hard \|\| unknown grain size \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) YS : annealed \|\| 80 micron grain size \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) YS : half hard \|\| 77 micron grain size \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) YS : hard \|\| unknown grain size \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) %El : annealed \|\| 80 micron grain size \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) %El : half hard \|\| 77 micron grain size \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) %El : hard \|\| unknown grain size \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) RHO : solid \|\| annealed \|\| 73 K to 473 K (-200.1 °C to 200 °C) SIGMA : solid \|\| annealed \|\| 73 K to 473 K (-200.1 °C to 200 °C)
UNS C10500 (UNS C10500) (ISO/EN/DIN CuAg0.05(OF))	D : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) DLL : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) MTE : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) CTE : solid \|\| 4 K to 800 K (-269.1 °C to 526.9 °C) E : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) G : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) v : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) K : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) TC : solid \|\| 73 K to 573 K (-200.1 °C to 300 °C) RHO : solid \|\| annealed \|\| 73 K to 473 K (-200.1 °C to 200 °C) SIGMA : solid \|\| annealed \|\| 73 K to 473 K (-200.1 °C to 200 °C)
UNS C10700 (UNS C10700)	D : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) DLL : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) MTE : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) CTE : solid \|\| 4 K to 800 K (-269.1 °C to 526.9 °C) E : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) G : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) v : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) K : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) TC : solid \|\| 73 K to 573 K (-200.1 °C to 300 °C) RHO : solid \|\| annealed \|\| 73 K to 473 K (-200.1 °C to 200 °C) SIGMA : solid \|\| annealed \|\| 73 K to 473 K (-200.1 °C to 200 °C)
UNS C10800 (UNS C10800)	D : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) DLL : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) MTE : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) CTE : solid \|\| 4 K to 800 K (-269.1 °C to 526.9 °C) E : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) G : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) v : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) K : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C)
UNS C11000 (ETP) (UNS C11000) (WNr 2.0060/2.0065/2.0070/2.0076/2.0090) (ISO/EN/DIN CW004A/Cu-ETP) (JIS C1100B)	D : solid \|\| 83 K to 1373 K (-190.1 °C to 1100 °C) DLL : solid \|\| 83 K to 1373 K (-190.1 °C to 1100 °C) MTE : solid \|\| 83 K to 1373 K (-190.1 °C to 1100 °C) CTE : solid \|\| 83 K to 1373 K (-190.1 °C to 1100 °C) E : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) G : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) v : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) K : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) TC : solid \|\| 4 K to 973 K (-268.9 °C to 700 °C) SSC : soft anneal, hardness RH86 \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.35 mm/mm strain SSC : soft anneal, hardness RH86 \|\| tested at 77.6 °K (-195.6 °C), 3.3x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SSC : soft anneal, hardness RH86 \|\| tested at 20.4 °K (-252.8 °C), 3.3x10^-⁴/s \|\| 0 to 0.45 mm/mm strain UTS : annealed \|\| soft anneal RH86, 19 mm (0.75 inch) diameter bar \|\| 20 K to 311 K (-253.1 °C to 37.9 °C) UTS : annealed \|\| 3.17 mm (0.125 inch) sheet, 0.04 mm (0.00157 inch) grain size \|\| 77 K to 478 K (-196.1 °C to 204.5 °C) UTS : annealed \|\| 4.5 mm (0.177 inch) rod \|\| 90 K to 297 K (-183.1 °C to 23.9 °C) UTS : annealed \|\| 6.35 mm (0.25 inch) rod \|\| 93 K to 294 K (-180.1 °C to 20.9 °C) UTS : cold worked \|\| 3.17 mm (0.125 inch) sheet cold worked 5% to 7% \|\| 77 K to 478 K (-196.1 °C to 204.5 °C) UTS : cold worked \|\| 4.5 mm (0.177 inch) sheet cold worked 50% \|\| 90 K to 297 K (-183.1 °C to 23.9 °C) UTS : hot worked \|\| rod \|\| 196 K to 977 K (-77.1 °C to 703.9 °C) YS : annealed \|\| soft anneal RH86, 19 mm (0.75 inch) diameter bar \|\| 20 K to 311 K (-253.1 °C to 37.9 °C) YS : annealed \|\| 3.17 mm (0.125 inch) sheet, 0.04 mm (0.00157 inch) grain size \|\| 77 K to 478 K (-196.1 °C to 204.5 °C) YS : annealed \|\| 4.5 mm (0.177 inch) rod \|\| 90 K to 297 K (-183.1 °C to 23.9 °C) YS : annealed \|\| 6.35 mm (0.25 inch) rod \|\| 93 K to 294 K (-180.1 °C to 20.9 °C) YS : cold worked \|\| 3.17 mm (0.125 inch) sheet cold worked 5% to 7% \|\| 77 K to 478 K (-196.1 °C to 204.5 °C) YS : cold worked \|\| 4.5 mm (0.177 inch) sheet cold worked 50% \|\| 90 K to 297 K (-183.1 °C to 23.9 °C) YS : hot worked \|\| rod \|\| 196 K to 293 K (-77.1 °C to 20 °C) %El : annealed \|\| soft anneal RH86, 19 mm (0.75 inch) diameter bar \|\| 20 K to 311 K (-253.1 °C to 37.9 °C) %El : annealed \|\| 3.17 mm (0.125 inch) sheet, 0.04 mm (0.00157 inch) grain size \|\| 77 K to 478 K (-196.1 °C to 204.5 °C) %El : annealed \|\| 4.5 mm (0.177 inch) rod \|\| 90 K to 297 K (-183.1 °C to 23.9 °C) %El : annealed \|\| 6.35 mm (0.25 inch) rod \|\| 93 K to 294 K (-180.1 °C to 20.9 °C) %El : cold worked \|\| 3.17 mm (0.125 inch) sheet cold worked 5% to 7% \|\| 77 K to 478 K (-196.1 °C to 204.5 °C) %El : cold worked \|\| 4.5 mm (0.177 inch) sheet cold worked 50% \|\| 90 K to 297 K (-183.1 °C to 23.9 °C) %El : hot worked \|\| rod \|\| 196 K to 977 K (-77.1 °C to 703.9 °C) RHO : solid \|\| annealed \|\| 73 K to 740 K (-200.1 °C to 466.9 °C) SIGMA : solid \|\| annealed \|\| 73 K to 740 K (-200.1 °C to 466.9 °C)
UNS C11100 (UNS C11100)	D : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) DLL : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) MTE : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) CTE : solid \|\| 4 K to 800 K (-269.1 °C to 526.9 °C) E : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) G : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) v : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C) K : solid \|\| 4 K to 1330 K (-269.1 °C to 1056.8 °C)
UNS C11400 (UNS C11400) (WNr 1.7666) (ISO/EN/DIN CuAg0.03)	D : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) DLL : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) MTE : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) CTE : solid \|\| 4 K to 800 K (-269.1 °C to 526.9 °C) TC : solid \|\| 73 K to 573 K (-200.1 °C to 300 °C) RHO : solid \|\| annealed \|\| 73 K to 473 K (-200.1 °C to 200 °C) SIGMA : solid \|\| annealed \|\| 73 K to 473 K (-200.1 °C to 200 °C)
UNS C12000 (UNS C12000) (ISO/EN/DIN CW023A/Cu-DLP) (JIS C1220B)	D : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) DLL : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) MTE : solid \|\| 4 K to 1273 K (-269.1 °C to 1000 °C) CTE : solid \|\| 4 K to 800 K (-269.1 °C to 526.9 °C) UTS : annealed \|\| 77 K to 298 K (-196.1 °C to 25 °C) UTS : cold worked 5% to 7% \|\| 77 K to 298 K (-196.1 °C to 25 °C) YS : annealed \|\| 77 K to 298 K (-196.1 °C to 25 °C) YS : cold worked 5% to 7% \|\| 77 K to 298 K (-196.1 °C to 25 °C) %El : annealed \|\| 77 K to 298 K (-196.1 °C to 25 °C) %El : cold worked 5% to 7% \|\| 77 K to 298 K (-196.1 °C to 25 °C)
UNS C12200 (UNS C12200) (WNr 1.7672) (ISO/EN/DIN CW024A/Cu-DHP)	E : solid \|\| annealed \|\| 4 K to 298 K (-269.1 °C to 25 °C) E : solid \|\| cold-drawn 26% \|\| 4 K to 298 K (-269.1 °C to 25 °C) SSC : annealed \|\| tested at 4 °K (-269.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.46 mm/mm strain SSC : annealed \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.46 mm/mm strain SSC : annealed \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.43 mm/mm strain SSC : annealed \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.37 mm/mm strain SSC : cold-drawn & aged \|\| tested at 4 °K (-269.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : cold-drawn & aged \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : cold-drawn & aged \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.19 mm/mm strain SSC : cold-drawn & aged \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.1 mm/mm strain UTS : solid \|\| annealed \|\| 4 K to 478 K (-269.1 °C to 204.6 °C) UTS : solid \|\| cold-drawn 26% \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) UTS : solid \|\| cold worked 5% to 7% \|\| 77 K to 922 K (-196.1 °C to 648.9 °C) YS : solid \|\| annealed \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) YS : solid \|\| cold-drawn 26% \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) YS : solid \|\| cold worked 5% to 7% \|\| 77 K to 728 K (-196.1 °C to 454.6 °C) %El : solid \|\| annealed \|\| 4 K to 478 K (-269.1 °C to 204.6 °C) %El : solid \|\| cold-drawn 26% \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) %El : solid \|\| cold worked 5% to 7% \|\| 77 K to 922 K (-196.1 °C to 648.9 °C)
UNS C14200 (UNS C14200) (ISO/EN/DIN CuAs(P))	UTS : plate \|\| annealed \|\| 77 K to 478 K (-196.1 °C to 204.5 °C) %El : plate \|\| annealed \|\| 77 K to 478 K (-196.1 °C to 204.5 °C)
UNS C15000 (UNS C15000) (WNr 2.1580) (ISO/EN/DIN CW119C/CW120C/CuZr) (ASTM B224) (SAE J461/J463)	E : cold-drawn 85% to 90% & aged \|\| 4 K to 298 K (-269.1 °C to 25 °C) SSC : cold-drawn & aged 19 mm (0.75 inch) diameter bar \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.1 mm/mm strain SSC : cold-drawn & aged 19 mm (0.75 inch) diameter bar \|\| tested at 76 °K (-197.1 °C), unknown strain rate \|\| 0 to 0.135 mm/mm strain SSC : cold-drawn & aged 19 mm (0.75 inch) diameter bar \|\| tested at 20 °K (-253.1 °C), unknown strain rate \|\| 0 to 0.216 mm/mm strain SSC : cold-drawn & aged 19 mm (0.75 inch) diameter bar \|\| tested at 4 °K (-269.1 °C), unknown strain rate \|\| 0 to 0.216 mm/mm strain UTS : cold-drawn & aged \|\| unknown reduction \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) YS : cold-drawn & aged \|\| unknown reduction \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) %El : cold-drawn & aged \|\| unknown reduction \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) RHO : solid \|\| cold-drawn & aged \|\| 4 K to 788 K (-269.1 °C to 515 °C) SIGMA : solid \|\| cold-drawn & aged \|\| 4 K to 788 K (-269.1 °C to 515 °C)
UNS C17000 (UNS C17000) (WNr 2.1245) (ISO/EN/DIN CW101C/CuBe1.7CoNi/CuBe2) (AFNOR CuBe1.7)	D : solid \|\| 27 K to 573 K (-246.1 °C to 300 °C) DLL : solid \|\| 27 K to 573 K (-246.1 °C to 300 °C) MTE : solid \|\| 27 K to 573 K (-246.1 °C to 300 °C) CTE : solid \|\| 27 K to 573 K (-246.1 °C to 300 °C) TC : solid \|\| precipitation hardened \|\| 4 K to 473 K (-269.1 °C to 200 °C) UTS : solution treated \|\| 14 mm (0.551 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) UTS : solution treated \|\| 19 mm (0.748 inch) rod \|\| 20 K to 293 K (-253.1 °C to 20 °C) UTS : solution treated \|\| average \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : solution treated & cold worked \|\| 14 mm (0.551 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) UTS : solution treated & cold worked \|\| 19 mm (0.748 inch) rod \|\| 20 K to 293 K (-253.1 °C to 20 °C) UTS : solution treated & cold worked \|\| average \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : precipitation hardened \|\| 14 mm (0.551 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) UTS : cold worked & precipitation hardened \|\| 14 mm (0.551 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) YS : solution treated \|\| 14 mm (0.551 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) YS : solution treated \|\| 19 mm (0.748 inch) rod \|\| 20 K to 293 K (-253.1 °C to 20 °C) YS : solution treated \|\| average \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : solution treated & cold worked \|\| 14 mm (0.551 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) YS : solution treated & cold worked \|\| 19 mm (0.748 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) YS : solution treated & cold worked \|\| average \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : precipitation hardened \|\| 14 mm (0.551 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) YS : cold worked & precipitation hardened \|\| 14 mm (0.551 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) %El : solution treated \|\| 14 mm (0.551 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) %El : solution treated \|\| 19 mm (0.748 inch) rod \|\| 20 K to 293 K (-253.1 °C to 20 °C) %El : solution treated \|\| average \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : solution treated & cold worked \|\| 14 mm (0.551 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) %El : solution treated & cold worked \|\| 19 mm (0.748 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) %El : solution treated & cold worked \|\| average \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : precipitation hardened \|\| 14 mm (0.551 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C) %El : cold worked & precipitation hardened \|\| 14 mm (0.551 inch) rod \|\| 89 K to 300 K (-184.1 °C to 26.9 °C)
UNS C17200 (UNS C17200) (WNr 2.1247) (ISO/EN/DIN CuBe2/CuBe2CoNi) (ASTM B194/B196/B197/B570/B643) (AFNOR CuBe1.9)	D : solid \|\| 6 K to 573 K (-267.1 °C to 300 °C) DLL : solid \|\| 6 K to 573 K (-267.1 °C to 300 °C) MTE : solid \|\| 6 K to 573 K (-267.1 °C to 300 °C) CTE : solid \|\| 6 K to 320 K (-267.1 °C to 46.9 °C) E : solid \|\| 20 K to 589 K (-253.1 °C to 315.6 °C) TC : solid \|\| 2 K to 1100 K (-271.1 °C to 826.9 °C) TD : solid \|\| 83 K to 573 K (-190.1 °C to 300 °C) SH : solid \|\| 83 K to 811 K (-190.1 °C to 537.9 °C) SSC : 37% cold worked \|\| tested at 20 °K (-253.1 °C), 1x10^-⁴/s \|\| 0 to 0.22 mm/mm strain SSC : 37% cold worked \|\| tested at 194 °K (-79 °C), 1x10^-⁴/s \|\| 0 to 0.8 mm/mm strain SSC : 37% cold worked \|\| tested at 76 °K (-197.1 °C), 1x10^-⁴/s \|\| 0 to 0.25 mm/mm strain SSC : annealed \|\| tested at 20 °K (-253.1 °C), 1x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : annealed \|\| tested at 194 °K (-79 °C), 1x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : annealed \|\| tested at 76 °K (-197.1 °C), 1x10^-⁴/s \|\| 0 to 0.5 mm/mm strain UTS : solid \|\| annealed \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : solid \|\| aged at 672 °K (399 °C) for 1.5 h \|\| 88 K to 300 K (-185.1 °C to 26.9 °C) UTS : solid \|\| aged at 589 °K (316 °C) for 3 h \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : solid \|\| annealed \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : solid \|\| aged at 672 °K (399 °C) for 1.5 h \|\| 88 K to 300 K (-185.1 °C to 26.9 °C) YS : solid \|\| aged at 589 °K (316 °C) for 3 h \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : solid \|\| aged at 408 °K (135 °C) for 48 h \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : solid \|\| annealed \|\| 20 K to 295 K (-253.1 °C to 21.9 °C) %El : solid \|\| 37% cold worked \|\| 20 K to 295 K (-253.1 °C to 21.9 °C) FSN : AT \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 1.5x10⁴ cycles to 6.8x10⁵ cycles FSN : AT \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 6.5x10⁴ cycles to 1x10⁷ cycles FSN : AT \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 1.3x10⁵ cycles to 3.4x10⁶ cycles FSN : AT \|\| tested at 194 °K (-79 °C), R = -1, K_t = 3.2, flexure, maximum stress \|\| 1.55x10⁴ cycles to 1.26x10⁶ cycles FSN : AT \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 3.2, flexure, maximum stress \|\| 1.8x10⁴ cycles to 1x10⁷ cycles FSN : AT \|\| tested at 20.4 °K (-252.8 °C), R = -1, K_t = 3.2, flexure, maximum stress \|\| 3.3x10⁴ cycles to 1.3x10⁶ cycles FSN : 1/2 HT \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 2.1x10⁴ cycles to 1.36x10⁶ cycles FSN : 1/2 HT \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 2.4x10⁴ cycles to 1x10⁶ cycles FSN : 1/2 HT \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 2.3x10⁴ cycles to 1x10⁷ cycles FSN : 1/2 HT \|\| tested at 194 °K (-79 °C), R = -1, K_t = 3.1, flexure, maximum stress \|\| 4.15x10⁴ cycles to 1x10⁶ cycles FSN : 1/2 HT \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 3.1, flexure, maximum stress \|\| 1.25x10⁴ cycles to 1.05x10⁶ cycles FSN : 1/2 HT \|\| tested at 20.4 °K (-252.8 °C), R = -1, K_t = 3.1, flexure, maximum stress \|\| 8.6x10⁴ cycles to 1x10⁷ cycles FSN : 1/2 HT \|\| tested at 194 °K (-79 °C), R = -1, K_t = 6.6, flexure, maximum stress \|\| 6x10³ cycles to 1.06x10⁶ cycles FSN : 1/2 HT \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 6.6, flexure, maximum stress \|\| 2.4x10⁴ cycles to 1.08x10⁶ cycles FSN : 1/2 HT \|\| tested at 20.4 °K (-252.8 °C), R = -1, K_t = 6.6, flexure, maximum stress \|\| 5.1x10⁴ cycles to 1.07x10⁶ cycles
UNS C17500 (UNS C17500) (WNr 2.1285) (ISO/EN/DIN CW104C/CuCo2Be) (ASTM B441/B534) (SAE J461/J463)	D : solid \|\| 6 K to 573 K (-267.1 °C to 300 °C) DLL : solid \|\| 6 K to 573 K (-267.1 °C to 300 °C) MTE : solid \|\| 6 K to 573 K (-267.1 °C to 300 °C) CTE : solid \|\| 6 K to 320 K (-267.1 °C to 46.9 °C) E : solid \|\| 20 K to 298 K (-253.1 °C to 25 °C) SH : solid \|\| 83 K to 811 K (-190.1 °C to 537.9 °C) UTS : half hard sheet \|\| 20 K to 297 K (-253.1 °C to 23.9 °C) YS : half hard sheet \|\| 20 K to 297 K (-253.1 °C to 23.9 °C) %El : half hard sheet \|\| 20 K to 297 K (-253.1 °C to 23.9 °C)
UNS C17510 (UNS C17510) (WNr 2.0850) (ISO/EN/DIN CW110C/CuNi2Be) (ASTM B441/B534)	TC : solid \|\| 77 K to 573 K (-196.1 °C to 300 °C) SH : solid \|\| 83 K to 811 K (-190.1 °C to 537.9 °C) SSC : cold-rolled & aged plate \|\| tested at 76 °K (-197.1 °C), 8.8x10^-⁴/s \|\| 0 to 0.1 mm/mm strain SSC : cold-rolled & aged plate \|\| tested at 4 °K (-269.1 °C), 8.8x10^-⁴/s \|\| 0 to 0.12 mm/mm strain UTS : solid \|\| cold-rolled 37% & aged 2 h at 755 °K (482 °C) \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) YS : solid \|\| cold-rolled 37% & aged 2 h at 755 °K (482 °C) \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) %El : solid \|\| cold-rolled 37% & aged 2 h at 755 °K (482 °C) \|\| 4 K to 295 K (-269.1 °C to 21.9 °C)
UNS C18150 (UNS C18150) (WNr 2.1293) (ISO/EN/DIN CW106C/CuCr1Zr/CuCrZr) (AFNOR UC1Zr)	D : solid \|\| 93 K to 1173 K (-180.1 °C to 900 °C) DLL : solid \|\| 93 K to 1173 K (-180.1 °C to 900 °C) MTE : solid \|\| 93 K to 1173 K (-180.1 °C to 900 °C)
UNS C21000 (UNS C21000) (WNr 2.0220) (ISO/EN/DIN CuZn5)	RHO : solid \|\| annealed \|\| 77 K to 473 K (-196.1 °C to 200 °C) RHO : solid \|\| fully cold worked \|\| 77 K to 373 K (-196.1 °C to 100 °C) SIGMA : solid \|\| annealed \|\| 77 K to 473 K (-196.1 °C to 200 °C) SIGMA : solid \|\| fully cold worked \|\| 77 K to 373 K (-196.1 °C to 100 °C)
UNS C22000 (UNS C22000) (WNr 2.0230) (ISO/EN/DIN CuZn10) (ASTM B130/B131/B134/B135/B36/B372/B587)	E : solid \|\| 4 K to 298 K (-269.1 °C to 25 °C) TC : solid \|\| annealed \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) SSC : annealed \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.367 mm/mm strain SSC : annealed \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.58 mm/mm strain SSC : annealed \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.63 mm/mm strain SSC : annealed \|\| tested at 4 °K (-269.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.61 mm/mm strain UTS : annealed \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) YS : annealed \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) %El : annealed \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) FSN : annealed \|\| tested at 100 °K (-173 °C), R = -1, axial, maximum stress \|\| 3x10³ cycles to 1.5x10⁶ cycles RHO : solid \|\| annealed \|\| 4 K to 473 K (-269.1 °C to 200 °C) SIGMA : solid \|\| annealed \|\| 4 K to 473 K (-269.1 °C to 200 °C)
UNS C23000 (UNS C23000) (WNr 2.0240) (ISO/EN/DIN CuZn15) (ASTM B111/B134/B135/B359/B36/B395/B43) (SAE J461/J463)	E : solid \|\| 4 K to 298 K (-269.1 °C to 25 °C) TC : solid \|\| annealed \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) SSC : cold-drawn 14% \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.465 mm/mm strain SSC : cold-drawn 14% \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.58 mm/mm strain SSC : cold-drawn 14% \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.55 mm/mm strain SSC : cold-drawn 14% \|\| tested at 4 °K (-269.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.61 mm/mm strain UTS : annealed \|\| 4 K to 773 K (-269.1 °C to 500 °C) UTS : cold worked 14% \|\| 4 K to 295 K (-269.1 °C to 22 °C) YS : annealed \|\| 4 K to 773 K (-269.1 °C to 500 °C) YS : cold worked 14% \|\| 4 K to 295 K (-269.1 °C to 22 °C) %El : annealed \|\| 4 K to 505 K (-269.1 °C to 232.3 °C) %El : cold worked 14% \|\| 4 K to 295 K (-269.1 °C to 22 °C) FSN : annealed \|\| tested at 100 °K (-173 °C), R = -1, axial, maximum stress \|\| 600 cycles to 4.4x10⁶ cycles RHO : solid \|\| annealed \|\| 77 K to 473 K (-196.1 °C to 200 °C) RHO : solid \|\| cold-drawn \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| annealed \|\| 77 K to 473 K (-196.1 °C to 200 °C) SIGMA : solid \|\| cold-drawn \|\| 4 K to 293 K (-269.1 °C to 20 °C)
UNS C24000 (UNS C24000) (WNr 2.0250) (ISO/EN/DIN CuZn20)	RHO : solid \|\| annealed \|\| 77 K to 473 K (-196.1 °C to 200 °C) RHO : solid \|\| fully cold worked \|\| 77 K to 373 K (-196.1 °C to 100 °C) SIGMA : solid \|\| annealed \|\| 77 K to 473 K (-196.1 °C to 200 °C) SIGMA : solid \|\| fully cold worked \|\| 77 K to 373 K (-196.1 °C to 100 °C)
UNS C26000 (UNS C26000) (WNr 2.0265) (ISO/EN/DIN CuZn30) (ASTM B129/B134/B135/B19/B36/B569/B587)	D : solid \|\| 20 K to 573 K (-253.1 °C to 300 °C) DLL : solid \|\| 20 K to 573 K (-253.1 °C to 300 °C) MTE : solid \|\| 20 K to 573 K (-253.1 °C to 300 °C) TC : solid \|\| annealed \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) SSC : annealed \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.37 mm/mm strain SSC : annealed \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.37 mm/mm strain SSC : annealed \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.41 mm/mm strain SSC : annealed \|\| tested at 4 °K (-269.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.37 mm/mm strain UTS : 3/4 hard \|\| 19 mm (0.75 inch) bar \|\| 20 K to 297 K (-253.1 °C to 23.9 °C) YS : 3/4 hard \|\| 19 mm (0.75 inch) bar \|\| 20 K to 297 K (-253.1 °C to 23.9 °C) %El : 3/4 hard \|\| 19 mm (0.75 inch) bar \|\| 20 K to 297 K (-253.1 °C to 23.9 °C) FSN : annealed \|\| tested at 100 °K (-173 °C), R = -1, axial, maximum stress \|\| 3x10³ cycles to 1.4x10⁶ cycles FSN : cold-rolled & stress relieved \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : cold-rolled & stress relieved \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : cold-rolled & stress relieved \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 1x10⁵ cycles to 1x10⁶ cycles FSN : cold-rolled & stress relieved, K_t = 3.2 \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles FSN : cold-rolled & stress relieved, K_t = 3.2 \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : cold-rolled & stress relieved, K_t = 3.2 \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : cold-rolled & stress relieved, K_t = 6.4 \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : cold-rolled & stress relieved, K_t = 6.4 \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : cold-rolled & stress relieved, K_t = 6.4 \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles RHO : solid \|\| annealed \|\| 77 K to 473 K (-196.1 °C to 200 °C) RHO : solid \|\| 3/4 hard \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| fully cold worked \|\| 77 K to 373 K (-196.1 °C to 100 °C) SIGMA : solid \|\| annealed \|\| 77 K to 473 K (-196.1 °C to 200 °C) SIGMA : solid \|\| 3/4 hard \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| fully cold worked \|\| 77 K to 373 K (-196.1 °C to 100 °C)
UNS C26800 (UNS C26800) (ISO/EN/DIN CuZn33)	TC : solid \|\| 73 K to 473 K (-200.1 °C to 200 °C) UTS : annealed \|\| 90 K to 970 K (-183.1 °C to 696.9 °C) %El : annealed \|\| 90 K to 970 K (-183.1 °C to 696.9 °C) RHO : solid \|\| annealed \|\| 77 K to 473 K (-196.1 °C to 200 °C) SIGMA : solid \|\| annealed \|\| 77 K to 473 K (-196.1 °C to 200 °C)
UNS C28000 (UNS C28000) (WNr 2.0550) (ISO/EN/DIN CW509L/CuZn40) (ASTM B111/B135/B36/B395) (AFNOR CuZn40/UZ40)	TC : solid \|\| annealed \|\| 73 K to 513 K (-200.1 °C to 240 °C)
UNS C28580 (UNS C28580)	RHO : solid \|\| 66 K to 1183 K (-207.1 °C to 910 °C) SIGMA : solid \|\| 66 K to 1183 K (-207.1 °C to 910 °C)
UNS C36500 (UNS C36500) (ISO/EN/DIN CW610N/CuZn40Pb)	UTS : annealed \|\| 90 K to 293 K (-183.1 °C to 20 °C) UTS : cold worked 12% \|\| 90 K to 293 K (-183.1 °C to 20 °C) %El : annealed \|\| 90 K to 293 K (-183.1 °C to 20 °C) %El : cold worked 12% \|\| 90 K to 293 K (-183.1 °C to 20 °C)
UNS C37000 (UNS C37000) (WNr 2.0372) (ISO/EN/DIN CW607N/CW611N/CuZn38Pb/CuZn38Pb1/CuZn39Pb0.5)	UTS : annealed \|\| 90 K to 973 K (-183.1 °C to 700 °C) UTS : cold worked 12% \|\| 90 K to 778 K (-183.1 °C to 505 °C) %El : annealed \|\| 90 K to 973 K (-183.1 °C to 700 °C) %El : cold worked 12% \|\| 90 K to 778 K (-183.1 °C to 505 °C)
UNS C37700 (UNS C37700) (WNr 2.0380) (ISO/EN/DIN CW608N/CuZn38Pb2/CuZn39Pb2/CuZn40Pb2) (JIS C3603/C3771) (ASTM B124/B283) (SAE J461/J463)	UTS : annealed \|\| 90 K to 973 K (-183.1 °C to 700 °C) UTS : cold worked 12% \|\| 90 K to 778 K (-183.1 °C to 505 °C) %El : annealed \|\| 90 K to 973 K (-183.1 °C to 700 °C) %El : cold worked 12% \|\| 90 K to 778 K (-183.1 °C to 505 °C)
UNS C38500 (UNS C38500) (WNr 2.0401) (ISO/EN/DIN CW614N/CuZn39Pb3) (AFNOR CuZn40Pb3/UZ39)	UTS : annealed \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) UTS : cold worked, hard \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : annealed \|\| 77 K to 700 K (-196.1 °C to 426.9 °C) %El : cold worked, hard \|\| 77 K to 293 K (-196.1 °C to 20 °C)
UNS C44300 (UNS C44300) (WNr 2.0470) (ISO/EN/DIN CW706R/CuZn28Sn/CuZn28Sn1) (ASTM B111/B171/B359/B395/B432)	E : solid \|\| 4 K to 505 K (-269.1 °C to 231.9 °C) SSC : annealed 19 mm (0.75 inch) diameter bar \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.63 mm/mm strain SSC : annealed 19 mm (0.75 inch) diameter bar \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.66 mm/mm strain SSC : annealed 19 mm (0.75 inch) diameter bar \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.66 mm/mm strain SSC : annealed 19 mm (0.75 inch) diameter bar \|\| tested at 4 °K (-269.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.61 mm/mm strain UTS : annealed \|\| 4 K to 505 K (-269.1 °C to 231.9 °C) YS : annealed \|\| 4 K to 505 K (-269.1 °C to 231.9 °C) %El : annealed \|\| 4 K to 505 K (-269.1 °C to 231.9 °C) RHO : solid \|\| annealed \|\| 77 K to 473 K (-196.1 °C to 200 °C) RHO : solid \|\| fully cold worked \|\| 77 K to 373 K (-196.1 °C to 100 °C) SIGMA : solid \|\| annealed \|\| 77 K to 473 K (-196.1 °C to 200 °C) SIGMA : solid \|\| fully cold worked \|\| 77 K to 373 K (-196.1 °C to 100 °C)
UNS C46400 (UNS C46400) (WNr 1.7660) (ISO/EN/DIN CuZn38Sn1/CuZn39Sn1) (ASTM B124/B171/B21/B283/B432)	E : solid \|\| 4 K to 298 K (-269.1 °C to 25 °C) SSC : annealed \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : annealed \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.329 mm/mm strain SSC : annealed \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.327 mm/mm strain SSC : annealed \|\| tested at 4 °K (-269.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.29 mm/mm strain UTS : annealed \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) YS : annealed \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) %El : annealed \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) RHO : solid \|\| annealed \|\| 4 K to 473 K (-269.1 °C to 200 °C) SIGMA : solid \|\| annealed \|\| 4 K to 473 K (-269.1 °C to 200 °C)
UNS C50500 (UNS C50500) (ISO/EN/DIN CuSn2) (ASTM B105/B508/B9)	E : cold worked \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) TC : solid \|\| 4 K to 473 K (-269.1 °C to 200 °C) RHO : solid \|\| annealed \|\| 4 K to 300 K (-269.1 °C to 26.9 °C) SIGMA : solid \|\| annealed \|\| 4 K to 300 K (-269.1 °C to 26.9 °C)
UNS C51000 (UNS C51000) (ISO/EN/DIN CW451K/CuSn4/CuSn5) (ASTM B100/B103/B139/B159)	D : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) DLL : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) MTE : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) CTE : solid \|\| 0 K to 573 K (-273.1 °C to 300 °C) E : spring temper \|\| 4 K to 298 K (-269.1 °C to 25 °C) TC : solid \|\| 4 K to 473 K (-269.1 °C to 200 °C) SSC : cold-drawn 85% \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.43 mm/mm strain SSC : cold-drawn 85% \|\| tested at 76 °K (-197.1 °C), unknown strain rate \|\| 0 to 0.42 mm/mm strain SSC : cold-drawn 85% \|\| tested at 20 °K (-253.1 °C), unknown strain rate \|\| 0 to 0.25 mm/mm strain SSC : cold-drawn 85% \|\| tested at 4 °K (-269.1 °C), unknown strain rate \|\| 0 to 0.25 mm/mm strain UTS : annealed \|\| 1.6 mm (0.063 inch) sheet, unknown grain size \|\| 200 K to 300 K (-73.1 °C to 27 °C) UTS : cold worked 61% \|\| 1.6 mm (0.063 inch) sheet \|\| 200 K to 300 K (-73.1 °C to 27 °C) UTS : cold-drawn 85% \|\| 19 mm (0.748 inch) rod \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) YS : annealed \|\| 1.6 mm (0.063 inch) sheet, unknown grain size \|\| 200 K to 300 K (-73.1 °C to 27 °C) YS : cold worked 61% \|\| 1.6 mm (0.063 inch) sheet \|\| 200 K to 300 K (-73.1 °C to 27 °C) YS : cold-drawn 85% \|\| 19 mm (0.748 inch) rod \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) %El : annealed \|\| 1.6 mm (0.063 inch) sheet, unknown grain size \|\| 200 K to 300 K (-73.1 °C to 27 °C) %El : cold worked 61% \|\| 1.6 mm (0.063 inch) sheet \|\| 200 K to 300 K (-73.1 °C to 27 °C) %El : cold-drawn 85% \|\| 19 mm (0.748 inch) rod \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) RHO : solid \|\| annealed \|\| 4 K to 473 K (-269.1 °C to 200 °C) RHO : solid \|\| spring cold-drawn 85% \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| annealed \|\| 4 K to 473 K (-269.1 °C to 200 °C) SIGMA : solid \|\| spring cold-drawn 85% \|\| 4 K to 293 K (-269.1 °C to 20 °C)
UNS C51100 (UNS C51100) (WNr 2.1016) (ISO/EN/DIN CuSn4) (ASTM B100/B103) (AFNOR CuSn4P)	SSC : cold-drawn 85% \|\| tested at 4 °K (-269.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.26 mm/mm strain SSC : cold-drawn 85% \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.26 mm/mm strain SSC : cold-drawn 85% \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.23 mm/mm strain SSC : cold-drawn 85% \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.5 mm/mm strain
UNS C52100 (UNS C52100) (WNr 2.1010/2.1030) (ISO/EN/DIN CW453K/CuSn8) (ASTM B103/B139/B159) (AFNOR CuSn8P/UE9P)	E : solid \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) TC : solid \|\| 4 K to 473 K (-269.1 °C to 200 °C) UTS : hard drawn \|\| 19 mm (0.75 inch) diameter bar \|\| 20 K to 297 K (-253.1 °C to 23.9 °C) YS : hard drawn \|\| 19 mm (0.75 inch) diameter bar \|\| 20 K to 297 K (-253.1 °C to 23.9 °C) %El : hard drawn \|\| 19 mm (0.75 inch) diameter bar \|\| 20 K to 297 K (-253.1 °C to 23.9 °C) RHO : solid \|\| annealed \|\| 4 K to 473 K (-269.1 °C to 200 °C) SIGMA : solid \|\| annealed \|\| 4 K to 473 K (-269.1 °C to 200 °C)
UNS C52400 (UNS C52400) (ISO/EN/DIN CuSn10) (ASTM B103/B139/B159)	D : solid \|\| 4 K to 573 K (-269.1 °C to 300 °C) DLL : solid \|\| 4 K to 573 K (-269.1 °C to 300 °C) MTE : solid \|\| 4 K to 573 K (-269.1 °C to 300 °C) CTE : solid \|\| 4 K to 573 K (-269.1 °C to 300 °C)
UNS C61000 (UNS C61000) (WNr 2.0920) (ISO/EN/DIN CuAl7/CuAl8)	UTS : annealed \|\| 3 mm (0.118 inch) rod \|\| 4 K to 293 K (-269.1 °C to 20 °C) YS : annealed \|\| 3 mm (0.118 inch) rod \|\| 4 K to 293 K (-269.1 °C to 20 °C)
UNS C61300 (UNS C61300) (ISO/EN/DIN CuAl7Fe3Sn) (ASTM B111/B150/B169/B171/B315/B432/B608)	E : solid \|\| annealed \|\| 4 K to 811 K (-269.1 °C to 537.9 °C) E : solid \|\| cold worked \|\| 91 K to 811 K (-182.1 °C to 537.9 °C)
UNS C61400 (UNS C61400) (WNr 2.0932) (ISO/EN/DIN CW303G/CuAl7Fe2/CuAl8Fe/CuAl8Fe3/CuAl8Fe3) (ASTM B111/B150/B169/B171/B315/B432/B608)	E : solid \|\| annealed \|\| 4 K to 811 K (-269.1 °C to 537.9 °C) E : solid \|\| cold worked \|\| 91 K to 811 K (-182.1 °C to 537.9 °C) SSC : annealed \|\| tested at 4 °K (-269.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.325 mm/mm strain SSC : annealed \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.36 mm/mm strain SSC : annealed \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.36 mm/mm strain SSC : annealed \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.328 mm/mm strain UTS : annealed \|\| 36 micron grain size \|\| 4 K to 295 K (-269.1 °C to 22 °C) UTS : annealed \|\| 25 micron grain size \|\| 90 K to 293 K (-183.1 °C to 20 °C) YS : annealed \|\| 36 micron grain size \|\| 4 K to 295 K (-269.1 °C to 22 °C) YS : annealed \|\| 25 micron grain size \|\| 90 K to 293 K (-183.1 °C to 20 °C) %El : annealed \|\| 36 micron grain size \|\| 4 K to 295 K (-269.1 °C to 22 °C) %El : annealed \|\| 25 micron grain size \|\| 90 K to 293 K (-183.1 °C to 20 °C) RHO : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C)
UNS C62300 (UNS C62300) (ISO/EN/DIN CuAl10Fe/CuAl10Fe3) (ASTM B124/B150/B283)	E : solid \|\| annealed \|\| 91 K to 811 K (-182.1 °C to 537.9 °C) E : solid \|\| cold worked \|\| 91 K to 811 K (-182.1 °C to 537.9 °C) E : solid \|\| average \|\| 91 K to 811 K (-182.1 °C to 537.9 °C) UTS : annealed \|\| 49 mm (1.93 inch) bar \|\| 90 K to 811 K (-183.1 °C to 537.9 °C) UTS : 0.4% cold worked \|\| 49 mm (1.93 inch) bar \|\| 90 K to 811 K (-183.1 °C to 537.9 °C) YS : annealed \|\| 49 mm (1.93 inch) bar \|\| 90 K to 293 K (-183.1 °C to 20 °C) YS : 0.4% cold worked \|\| 49 mm (1.93 inch) bar \|\| 90 K to 293 K (-183.1 °C to 20 °C) %El : annealed \|\| 49 mm (1.93 inch) bar \|\| 90 K to 811 K (-183.1 °C to 537.9 °C) %El : 0.4% cold worked \|\| 49 mm (1.93 inch) bar \|\| 90 K to 811 K (-183.1 °C to 537.9 °C)
UNS C63000 (UNS C63000) (WNr 2.0966) (ISO/EN/DIN CuAl10Ni/CuAl10Ni5Fe4/CuAl9Ni6Fe3) (ASTM B124/B150/B171/B283/F468/SB150/SB171) (AMS 4640)	E : solid \|\| annealed \|\| 91 K to 811 K (-182.1 °C to 537.9 °C) E : solid \|\| cold worked \|\| 91 K to 811 K (-182.1 °C to 537.9 °C) E : solid \|\| sand cast \|\| 4 K to 298 K (-269.1 °C to 25 °C) E : solid \|\| average of all \|\| 91 K to 300 K (-182.1 °C to 27 °C) SSC : sand cast \|\| tested at 4 °K (-269.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : sand cast \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : sand cast \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.5 mm/mm strain SSC : sand cast \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.77 mm/mm strain SSC : as-cast \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.8 mm/mm strain SSC : as-cast \|\| tested at 76 °K (-197.1 °C), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : as-cast \|\| tested at 20 °K (-253.1 °C), unknown strain rate \|\| 0 to 0.5 mm/mm strain SSC : as-cast \|\| tested at 4 °K (-269.1 °C), unknown strain rate \|\| 0 to 0.5 mm/mm strain UTS : annealed at 893 °K (620 °C) \|\| 50 mm (1.97 inch) rod \|\| 90 K to 293 K (-183.1 °C to 20 °C) YS : annealed at 893 °K (620 °C) \|\| 50 mm (1.97 inch) rod \|\| 90 K to 293 K (-183.1 °C to 20 °C) %El : annealed at 893 °K (620 °C) \|\| 50 mm (1.97 inch) rod \|\| 90 K to 293 K (-183.1 °C to 20 °C) RHO : solid \|\| sand cast \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| sand cast \|\| 4 K to 293 K (-269.1 °C to 20 °C)
UNS C64700 (UNS C64700) (WNr 2.0853/2.0855) (ISO/EN/DIN CW111C/CuNi2Si) (JIS Ni2Si) (ASTM B411/B412)	E : solid \|\| precipitation hardened \|\| 4 K to 298 K (-269.1 °C to 25 °C) SSC : aged \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.13 mm/mm strain SSC : aged \|\| tested at 76 °K (-197.1 °C), unknown strain rate \|\| 0 to 0.17 mm/mm strain SSC : aged \|\| tested at 20 °K (-253.1 °C), unknown strain rate \|\| 0 to 0.25 mm/mm strain SSC : aged \|\| tested at 4 °K (-269.1 °C), unknown strain rate \|\| 0 to 0.21 mm/mm strain UTS : aged \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) UTS : aged after cold working 75% \|\| 103 K to 295 K (-170.1 °C to 22 °C) YS : aged \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) YS : aged after cold working 75% \|\| 103 K to 295 K (-170.1 °C to 22 °C) %El : aged \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) %El : aged after cold working 75% \|\| 103 K to 295 K (-170.1 °C to 22 °C) RHO : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) RHO : solid \|\| aged, Rockwell hardness B93 \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| aged, Rockwell hardness B93 \|\| 4 K to 293 K (-269.1 °C to 20 °C)
UNS C65500 (UNS C65500) (WNr 2.1525) (ISO/EN/DIN CW116C/CuSi3Mn/CuSi3Mn1) (ASTM B100/B124/B283/B315/B432/B96/B98/B99/F467/SB315/SB96/SB98)	D : solid \|\| 90 K to 573 K (-183.1 °C to 300 °C) DLL : solid \|\| 90 K to 573 K (-183.1 °C to 300 °C) MTE : solid \|\| 90 K to 573 K (-183.1 °C to 300 °C) CTE : solid \|\| 90 K to 573 K (-183.1 °C to 300 °C) E : solid \|\| annealed \|\| 4 K to 450 K (-269.1 °C to 176.9 °C) E : solid \|\| cold worked \|\| 20 K to 298 K (-253.1 °C to 25 °C) TC : solid \|\| below RT, hard temper \|\| 15 K to 90 K (-258.1 °C to -183.1 °C) SSC : annealed \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.46 mm/mm strain SSC : annealed \|\| tested at 76 °K (-197.1 °C), unknown strain rate \|\| 0 to 0.52 mm/mm strain SSC : annealed \|\| tested at 20 °K (-253.1 °C), unknown strain rate \|\| 0 to 0.52 mm/mm strain SSC : annealed \|\| tested at 4 °K (-269.1 °C), unknown strain rate \|\| 0 to 0.43 mm/mm strain UTS : solid \|\| annealed \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) UTS : solid \|\| quarter hard \|\| 20 K to 297 K (-253.1 °C to 23.9 °C) UTS : solid \|\| cold worked 42% \|\| 83 K to 813 K (-190.1 °C to 540 °C) YS : solid \|\| annealed \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) YS : solid \|\| quarter hard \|\| 20 K to 297 K (-253.1 °C to 23.9 °C) %El : solid \|\| annealed \|\| 4 K to 295 K (-269.1 °C to 21.9 °C) %El : solid \|\| quarter hard \|\| 20 K to 297 K (-253.1 °C to 23.9 °C) %El : solid \|\| cold worked 42% \|\| 83 K to 813 K (-190.1 °C to 540 °C) RHO : solid \|\| soft annealed \|\| 4 K to 473 K (-269.1 °C to 200 °C) SIGMA : solid \|\| soft annealed \|\| 4 K to 473 K (-269.1 °C to 200 °C)
UNS C70600 (UNS C70600) (WNr 2.0872/2.0877) (ISO/EN/DIN CW352H/CuNi10Fe/CuNi10Fe1Mn) (ASTM B111/B121/B122/B151/B171/B359/B395/B402/B432/B466/B467/B543/B552/B608) (SAE J461/J463)	E : solid \|\| 4 K to 533 K (-269.1 °C to 260 °C) SSC : annealed \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.3 mm/mm strain SSC : annealed \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.33 mm/mm strain SSC : annealed \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.37 mm/mm strain SSC : annealed \|\| tested at 4 °K (-269.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.4 mm/mm strain UTS : solid \|\| annealed \|\| 4 K to 673 K (-269.1 °C to 400 °C) YS : solid \|\| annealed \|\| 4 K to 673 K (-269.1 °C to 400 °C) %El : solid \|\| annealed \|\| 4 K to 673 K (-269.1 °C to 400 °C) RHO : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| annealed \|\| 4 K to 293 K (-269.1 °C to 20 °C)
UNS C71500 (UNS C71500) (WNr 2.0820) (ISO/EN/DIN CW354H/CuNi30Fe/CuNi30Mn1Fe) (ASTM B111/B122/B151/B171/B359/B395/B402/B432/B466/B467/B522/B543/B608)	E : solid \|\| 4 K to 623 K (-269.1 °C to 350 °C) SSC : annealed \|\| tested at 194 °K (-79 °C), 3.3x10^-⁴/s \|\| 0 to 0.37 mm/mm strain SSC : annealed \|\| tested at 76 °K (-197.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.36 mm/mm strain SSC : annealed \|\| tested at 20 °K (-253.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.4 mm/mm strain SSC : annealed \|\| tested at 4 °K (-269.1 °C), 3.3x10^-⁴/s \|\| 0 to 0.36 mm/mm strain UTS : annealed \|\| 4 K to 1173 K (-269.1 °C to 900 °C) YS : annealed \|\| 4 K to 1173 K (-269.1 °C to 900 °C) %El : annealed \|\| 4 K to 1173 K (-269.1 °C to 900 °C) RHO : solid \|\| annealed \|\| 4 K to 473 K (-269.1 °C to 200 °C) SIGMA : solid \|\| annealed \|\| 4 K to 473 K (-269.1 °C to 200 °C)
UNS C83600 (UNS C83600) (WNr 2.1096/2.1097) (ISO/EN/DIN CC491K/CuPb5Sn5Zn5/CuSn5Pb5Zn5) (JIS BC6/CAC406/CAC406C/H2203/H5111)	D : solid \|\| 170 K to 1000 K (-103.1 °C to 726.9 °C) DLL : solid \|\| 170 K to 1000 K (-103.1 °C to 726.9 °C) MTE : solid \|\| 170 K to 1000 K (-103.1 °C to 726.9 °C) CTE : solid \|\| 170 K to 1000 K (-103.1 °C to 726.9 °C)
UNS C95300 (UNS C95300) (ISO/EN/DIN G-CuAl9Fe2) (ASTM B148/B271/B505) (SAE 688/68b/J461/J462)	UTS : chill cast \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : chill cast \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : chill cast \|\| 77 K to 293 K (-196.1 °C to 20 °C)
GRCop-84 (ISO/EN/DIN Cu8Cr4Nb)	D : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) DLL : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) MTE : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) TC : solid \|\| powder metallurgy, 200 ppm Fe \|\| 80 K to 1093 K (-193.1 °C to 820 °C) SH : powder metallurgy \|\| 175 K to 1173 K (-98.1 °C to 900 °C) UTS : as-extruded \|\| 4 K to 1000 K (-269.1 °C to 726.9 °C) UTS : brazed \|\| as-extruded \|\| 20 K to 1089 K (-253.1 °C to 815.6 °C) YS : as-extruded \|\| 4 K to 1073 K (-269.1 °C to 800 °C) YS : brazed \|\| as-extruded \|\| 14 K to 1089 K (-259.1 °C to 815.6 °C) %El : as-extruded \|\| 4 K to 1073 K (-269.1 °C to 800 °C) %El : brazed \|\| as-extruded \|\| 14 K to 1089 K (-259.1 °C to 815.6 °C) RHO : solid \|\| 30 K to 473 K (-243.1 °C to 200 °C) SIGMA : solid \|\| 30 K to 473 K (-243.1 °C to 200 °C)
NARloy-Z	UTS : solid \|\| solution annealed & aged \|\| 30 K to 773 K (-243.1 °C to 500 °C) YS : solid \|\| solution annealed & aged \|\| 37 K to 920 K (-236.1 °C to 646.9 °C)
Cu - 0.5 Al (wt %)	TC : solid \|\| 4 K to 1354 K (-269.1 °C to 1080.8 °C) RHO : solid \|\| 1 K to 1354 K (-272.1 °C to 1081 °C) SIGMA : solid \|\| 1 K to 1354 K (-272.1 °C to 1081 °C)
Cu - 1 Al (wt %)	TC : solid \|\| 4 K to 1352 K (-269.1 °C to 1078.8 °C) RHO : solid \|\| 1 K to 1353 K (-272.1 °C to 1080 °C) SIGMA : solid \|\| 1 K to 1353 K (-272.1 °C to 1080 °C)
Cu - 3 Al (wt %)	TC : solid \|\| 4 K to 1343 K (-269.1 °C to 1069.8 °C) RHO : solid \|\| 1 K to 1343 K (-272.1 °C to 1070 °C) SIGMA : solid \|\| 1 K to 1343 K (-272.1 °C to 1070 °C)
Cu - 4.5 Al (wt %)	RHO : solid \|\| 1 K to 1313 K (-272.1 °C to 1040 °C) SIGMA : solid \|\| 1 K to 1313 K (-272.1 °C to 1040 °C)
Cu - 10 Al (wt %)	RHO : solid \|\| 1 K to 1313 K (-272.1 °C to 1040 °C) SIGMA : solid \|\| 1 K to 1313 K (-272.1 °C to 1040 °C)
Cu - 25 Al (wt %)	TC : solid \|\| 4 K to 939 K (-269.1 °C to 665.9 °C)
Cu - 30 Al (wt %)	TC : solid \|\| 4 K to 864 K (-269.1 °C to 590.9 °C)
Cu - 35 Al (wt %)	TC : solid \|\| 4 K to 864 K (-269.1 °C to 590.9 °C)
Cu - 39 Al (wt %)	TC : solid \|\| 4 K to 864 K (-269.1 °C to 590.9 °C)
Cu - 45 Al (wt %)	TC : solid \|\| 4 K to 864 K (-269.1 °C to 590.9 °C)
Cu - 50 Al (wt %)	TC : solid \|\| 4 K to 821 K (-269.1 °C to 547.9 °C) RHO : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C) SIGMA : solid \|\| 1 K to 821 K (-272.1 °C to 548 °C)
Cu - 8 Cr - 1 Al (wt %)	TC : solid \|\| vacuum plasma sprayed & HIPed, bulk density of 8.546 g/cm³ \|\| 93 K to 1223 K (-180.1 °C to 950 °C) RHO : solid \|\| vacuum plasma sprayed & HIPed \|\| 93 K to 393 K (-180.1 °C to 120 °C) SIGMA : solid \|\| vacuum plasma sprayed & HIPed \|\| 93 K to 393 K (-180.1 °C to 120 °C)
Cu - 17 Cr - 5 Al (wt %)	TC : solid \|\| as-cast, bulk density of 7.688 g/cm³ \|\| 93 K to 1223 K (-180.1 °C to 950 °C)
Cu - 23 Cr - 5 Al (wt %)	TC : solid \|\| cold sprayed, bulk density of 7.575 g/cm³ \|\| 93 K to 1223 K (-180.1 °C to 950 °C) RHO : solid \|\| cold sprayed, bulk density of 7.575 g/cm³ \|\| 83 K to 413 K (-190.1 °C to 140 °C) SIGMA : solid \|\| cold sprayed, bulk density of 7.575 g/cm³ \|\| 83 K to 413 K (-190.1 °C to 140 °C)
Cu - 0.5 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 1 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 3 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 5 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 10 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 15 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 20 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 25 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 30 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 35 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 40 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 45 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 50 Ni (wt %)	TC : solid \|\| 4 K to 1200 K (-269.1 °C to 926.9 °C) RHO : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C) SIGMA : solid \|\| 1 K to 1100 K (-272.1 °C to 827 °C)
Cu - 1.7 Pd (wt %)	RHO : solid \|\| annealed \|\| 55 K to 833 K (-218.1 °C to 560 °C) SIGMA : solid \|\| annealed \|\| 55 K to 833 K (-218.1 °C to 560 °C)
Cu - 3.3 Pd (wt %)	RHO : solid \|\| annealed \|\| 55 K to 833 K (-218.1 °C to 560 °C) SIGMA : solid \|\| annealed \|\| 55 K to 833 K (-218.1 °C to 560 °C)
Cu - 5 Pd (wt %)	RHO : solid \|\| annealed \|\| 55 K to 833 K (-218.1 °C to 560 °C) SIGMA : solid \|\| annealed \|\| 55 K to 833 K (-218.1 °C to 560 °C)
Cu - 6.7 Pd (wt %)	RHO : solid \|\| annealed \|\| 55 K to 833 K (-218.1 °C to 560 °C) SIGMA : solid \|\| annealed \|\| 55 K to 833 K (-218.1 °C to 560 °C)
Cu - 1 Pt (wt %)	RHO : solid \|\| annealed \|\| 70 K to 770 K (-203.1 °C to 496.9 °C) SIGMA : solid \|\| annealed \|\| 70 K to 770 K (-203.1 °C to 496.9 °C)
Cu - 2 Pt (wt %)	RHO : solid \|\| annealed \|\| 70 K to 770 K (-203.1 °C to 496.9 °C) SIGMA : solid \|\| annealed \|\| 70 K to 770 K (-203.1 °C to 496.9 °C)
Cu - 3 Pt (wt %)	RHO : solid \|\| annealed \|\| 70 K to 770 K (-203.1 °C to 496.9 °C) SIGMA : solid \|\| annealed \|\| 70 K to 770 K (-203.1 °C to 496.9 °C)
Cu - 4 Pt (wt %)	RHO : solid \|\| annealed \|\| 70 K to 770 K (-203.1 °C to 496.9 °C) SIGMA : solid \|\| annealed \|\| 70 K to 770 K (-203.1 °C to 496.9 °C)
Cu - 0.5 Zn (wt %)	TC : solid \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C) SIGMA : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C)
Cu - 1 Zn (wt %)	TC : solid \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C) SIGMA : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C)
Cu - 3 Zn (wt %)	TC : solid \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C) SIGMA : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C)
Cu - 5 Zn (wt %)	TC : solid \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C) SIGMA : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C)
Cu - 10 Zn (wt %)	TC : solid \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C) SIGMA : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C)
Cu - 15 Zn (wt %)	TC : solid \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C) SIGMA : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C)
Cu - 20 Zn (wt %)	TC : solid \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C) SIGMA : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C)
Cu - 25 Zn (wt %)	TC : solid \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C) SIGMA : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C)
Cu - 30 Zn (wt %)	TC : solid \|\| 4 K to 700 K (-269.1 °C to 426.9 °C) RHO : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C) SIGMA : solid \|\| 1 K to 700 K (-272.1 °C to 427 °C)
AZ31 (UNS M11311) (WNr 3.5312) (ISO/EN/DIN Mg-Al3Zn1Mn/MgAl3Zn)	TC : solid \|\| all tempers \|\| 173 K to 523 K (-100.1 °C to 250 °C) TD : solid \|\| 116 K to 590 K (-157.1 °C to 316.9 °C) UTS : AZ31B \|\| as-extruded \|\| 85 K to 300 K (-188.1 °C to 26.9 °C) UTS : AZ31B \|\| hot-rolled \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) UTS : AZ31B \|\| annealed \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : AZ31B \|\| as-extruded \|\| 85 K to 300 K (-188.1 °C to 26.9 °C) YS : AZ31B \|\| hot-rolled \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) YS : AZ31B \|\| annealed \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : AZ31B \|\| as-extruded \|\| 85 K to 300 K (-188.1 °C to 26.9 °C) %El : AZ31B \|\| hot-rolled \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : AZ31B \|\| annealed \|\| 20 K to 300 K (-253.1 °C to 26.9 °C)
AZ61 (UNS M11610) (WNr 3.5612) (ISO/EN/DIN Mg-Al6Zn1Mn/MgAl6Zn)	UTS : as-extruded \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) UTS : cold-drawn 13% RA \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) YS : as-extruded \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) YS : cold-drawn 13% RA \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : as-extruded \|\| 77 K to 589 K (-196.1 °C to 315.6 °C)
AZ80 (UNS M11800) (WNr 3.5812) (ISO/EN/DIN Mg-Al8ZnMn/MgAl8Zn) (AFNOR G-A8Z)	UTS : extruded \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) UTS : T5 temper, extruded \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) UTS : T51 temper, extruded \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) YS : extruded \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) YS : T5 temper, extruded \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) YS : T51 temper, extruded \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : extruded \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : T5 temper, extruded \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : T51 temper, extruded \|\| 77 K to 300 K (-196.1 °C to 26.9 °C)
AZ81 (UNS M11810) (WNr 3.5812) (ISO/EN/DIN MgAl8Zn1)	D : solid \|\| 4 K to 682 K (-269.1 °C to 408.9 °C) DLL : solid \|\| 4 K to 682 K (-269.1 °C to 408.9 °C) MTE : solid \|\| 4 K to 682 K (-269.1 °C to 408.9 °C) CTE : solid \|\| 4 K to 682 K (-269.1 °C to 408.9 °C)
AZ91 (UNS M11910/M11912/M11914/M11916/M11921) (WNr 3.5912) (ISO/EN/DIN Mg-Al8Zn/MgAl9Zn1)	UTS : T6 temper \|\| 77 K to 422 K (-196.1 °C to 148.9 °C) YS : T6 temper \|\| 77 K to 422 K (-196.1 °C to 148.9 °C) %El : T6 temper \|\| 77 K to 422 K (-196.1 °C to 148.9 °C)
AZ92 (UNS M11920) (ISO/EN/DIN Mg-Al9Zn2)	D : solid \|\| T6 temper \|\| 88 K to 811 K (-185.1 °C to 537.9 °C) DLL : solid \|\| T6 temper \|\| 88 K to 811 K (-185.1 °C to 537.9 °C) MTE : solid \|\| T6 temper \|\| 88 K to 811 K (-185.1 °C to 537.9 °C) UTS : T6 temper \|\| 77 K to 422 K (-196.1 °C to 148.9 °C) YS : T6 temper \|\| 77 K to 422 K (-196.1 °C to 148.9 °C) %El : T6 temper \|\| 77 K to 422 K (-196.1 °C to 148.9 °C)
EZ33 (UNS M12330) (WNr 3.5103) (ISO/EN/DIN MgRE3Zn2Zr) (AMS 4442)	UTS : T5 temper \|\| 77 K to 623 K (-196.1 °C to 350 °C) YS : T5 temper \|\| 77 K to 623 K (-196.1 °C to 350 °C) %El : T5 temper \|\| 77 K to 623 K (-196.1 °C to 350 °C)
HK31 (UNS M13310)	UTS : T6 temper, HK31A \|\| 0.5 h at temperature \|\| 77 K to 625 K (-196.1 °C to 351.9 °C) UTS : T6 temper, HK31A \|\| 100 h at temperature \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) UTS : T6 temper, HK31A \|\| 500 h or 1,000 h at temperature \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) YS : T6 temper, HK31A \|\| 0.5 h at temperature \|\| 77 K to 625 K (-196.1 °C to 351.9 °C) YS : T6 temper, HK31A \|\| 100 h at temperature \|\| 77 K to 590 K (-196.1 °C to 316.9 °C) YS : T6 temper, HK31A \|\| 500 h at temperature \|\| 77 K to 590 K (-196.1 °C to 316.9 °C) YS : T6 temper, HK31A \|\| 1,000 h at temperature \|\| 77 K to 590 K (-196.1 °C to 316.9 °C) %El : T6 temper \|\| 77 K to 422 K (-196.1 °C to 148.9 °C)
HM31 (UNS M13312)	UTS : F temper, extruded \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) YS : F temper, extruded \|\| 77 K to 300 K (-196.1 °C to 26.9 °C) %El : F temper, extruded \|\| 77 K to 300 K (-196.1 °C to 26.9 °C)
QE22 (MSR-B) (UNS M18220) (WNr 3.5164) (ISO/EN/DIN MgAg2RE2Zr)	E : solid \|\| 195 K to 673 K (-78.1 °C to 400 °C) UTS : sand casting \|\| T6 temper \|\| 61 K to 644 K (-212.1 °C to 370.9 °C) YS : sand casting \|\| T6 temper \|\| 61 K to 644 K (-212.1 °C to 370.9 °C) %El : sand casting \|\| T6 temper \|\| 61 K to 644 K (-212.1 °C to 370.9 °C)
ZE10 (UNS M16100) (ISO/EN/DIN Mg-Zn1Zr)	UTS : H11 temper \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : H11 temper \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : H11 temper \|\| 20 K to 300 K (-253.1 °C to 26.9 °C)
ZH62 (UNS M16620) (WNr 3.5102)	UTS : sand casting \|\| T5 temper \|\| 77 K to 422 K (-196.1 °C to 148.9 °C) YS : sand casting \|\| T5 temper \|\| 77 K to 422 K (-196.1 °C to 148.9 °C) %El : sand casting \|\| T5 temper \|\| 77 K to 422 K (-196.1 °C to 148.9 °C)
ZK60 (UNS M16600) (ISO/EN/DIN Mg-Zn6Zr) (AFNOR G-Z55Zr)	UTS : solution treated at 773 °K (500 °C) \|\| 123 K to 296 K (-150.1 °C to 22.9 °C) YS : solution treated at 773 °K (500 °C) \|\| 123 K to 296 K (-150.1 °C to 22.9 °C) %El : solution treated at 773 °K (500 °C) \|\| 123 K to 296 K (-150.1 °C to 22.9 °C)
Mg - 0.5 Al (wt %)	TC : solid \|\| 100 K to 914 K (-173.1 °C to 640.9 °C) RHO : solid \|\| 1 K to 913 K (-272.1 °C to 640 °C) SIGMA : solid \|\| 1 K to 913 K (-272.1 °C to 640 °C)
Mg - 1 Al (wt %)	TC : solid \|\| 100 K to 906 K (-173.1 °C to 632.9 °C) RHO : solid \|\| 1 K to 913 K (-272.1 °C to 640 °C) SIGMA : solid \|\| 1 K to 913 K (-272.1 °C to 640 °C)
Mg - 3 Al (wt %)	TC : solid \|\| 100 K to 872 K (-173.1 °C to 598.9 °C) RHO : solid \|\| 1 K to 872 K (-272.1 °C to 599 °C) SIGMA : solid \|\| 1 K to 872 K (-272.1 °C to 599 °C)
Mg - 5 Al (wt %)	RHO : solid \|\| 1 K to 839 K (-272.1 °C to 566 °C) SIGMA : solid \|\| 1 K to 839 K (-272.1 °C to 566 °C)
Mg - 10 Al (wt %)	RHO : solid \|\| 1 K to 756 K (-272.1 °C to 483 °C) SIGMA : solid \|\| 1 K to 756 K (-272.1 °C to 483 °C)
Mg - 1.8 Gd (wt %)	SSC : annealed \|\| tested at 78.1 °K (-195 °C), 2.8x10^-⁴/s \|\| 0 to 0.53 mm/mm strain SSC : annealed \|\| tested at 4 °K (-269.1 °C), 2.8x10^-⁴/s \|\| 0 to 0.125 mm/mm strain SSCC : annealed \|\| tested at 78.1 °K (-195 °C), 2.8x10^-⁴/s \|\| 0 to 0.18 mm/mm strain SSCC : annealed \|\| tested at 4 °K (-269.1 °C), 2.8x10^-⁴/s \|\| 0 to 0.173 mm/mm strain UTS : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C) YS : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C) UCS : annealed \|\| 2.8x10^-⁴/s \|\| 78 K to 298 K (-195.1 °C to 25 °C) YSC : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C) %El : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C)
Mg - 2.9 Gd (wt %)	SSC : annealed \|\| tested at 78.1 °K (-195 °C), 2.8x10^-⁴/s \|\| 0 to 0.16 mm/mm strain SSC : annealed \|\| tested at 4 °K (-269.1 °C), 2.8x10^-⁴/s \|\| 0 to 0.14 mm/mm strain SSCC : annealed \|\| tested at 78.1 °K (-195 °C), 2.8x10^-⁴/s \|\| 0 to 0.212 mm/mm strain SSCC : annealed \|\| tested at 4 °K (-269.1 °C), 2.8x10^-⁴/s \|\| 0 to 0.193 mm/mm strain UTS : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C) YS : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C) UCS : annealed \|\| 2.8x10^-⁴/s \|\| 78 K to 298 K (-195.1 °C to 25 °C) YSC : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C) %El : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C)
Mg - 1.1 Y (wt %)	SSC : annealed \|\| tested at 78.1 °K (-195 °C), 2.8x10^-⁴/s \|\| 0 to 0.79 mm/mm strain SSC : annealed \|\| tested at 4 °K (-269.1 °C), 2.8x10^-⁴/s \|\| 0 to 0.75 mm/mm strain SSCC : annealed \|\| tested at 78.1 °K (-195 °C), 2.8x10^-⁴/s \|\| 0 to 0.18 mm/mm strain SSCC : annealed \|\| tested at 4 °K (-269.1 °C), 2.8x10^-⁴/s \|\| 0 to 0.124 mm/mm strain UTS : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C) YS : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C) YSC : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C) %El : annealed, in tension \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C)
Mg - 2 Y (wt %)	SSC : annealed \|\| tested at 78.1 °K (-195 °C), 2.8x10^-⁴/s \|\| 0 to 0.73 mm/mm strain SSC : annealed \|\| tested at 4 °K (-269.1 °C), 2.8x10^-⁴/s \|\| 0 to 0.88 mm/mm strain SSCC : annealed \|\| tested at 78.1 °K (-195 °C), 2.8x10^-⁴/s \|\| 0 to 0.11 mm/mm strain SSCC : annealed \|\| tested at 4 °K (-269.1 °C), 2.8x10^-⁴/s \|\| 0 to 0.116 mm/mm strain UTS : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C) YS : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C) YSC : annealed \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C) %El : annealed, in tension \|\| 2.8x10^-⁴/s \|\| 4 K to 298 K (-269.1 °C to 25 °C)
Titanium alloys	Property : Condition // Data range
Ti Grade 1 (UNS R50250) (WNr 3.7025) (ISO/EN/DIN Ti-P01/Ti-P11) (ASTM B265/B337/B338/B363/B381/B861/B862/F67) (GB & GB/T TA-1)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 93 K to 1073 K (-180.1 °C to 800 °C) TC : solid \|\| annealed \|\| 0 K to 1950 K (-273.1 °C to 1676.8 °C) TD : solid \|\| annealed \|\| 100 K to 1144 K (-173.1 °C to 870.9 °C) SH : solid \|\| 100 K to 1944 K (-173.1 °C to 1670.8 °C) UTS : solid \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) YS : solid \|\| 77 K to 589 K (-196.1 °C to 315.6 °C) FSN : annealed bar, 9 micron grain size \|\| tested at 77.2 °K (-196 °C), R = -1, axial, maximum stress \|\| 2.3x10⁵ cycles to 1x10⁷ cycles
Ti Grade 2 (UNS R50400) (WNr 3.7035) (ISO/EN/DIN Ti-P02) (JIS TP340H) (ASTM B265/B337/B338/B348/B363/B367/B381/B861/B862/F67) (AMS 4902/4941/4942/4951) (GB & GB/T TA-2)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 93 K to 1073 K (-180.1 °C to 800 °C) TC : solid \|\| annealed \|\| 0 K to 1950 K (-273.1 °C to 1676.8 °C) TD : solid \|\| annealed \|\| 100 K to 1144 K (-173.1 °C to 870.9 °C) SH : solid \|\| 100 K to 1944 K (-173.1 °C to 1670.8 °C) SSC : low impurities, hot-rolled & annealed 15.9 mm (0.625 inch) diameter rounds \|\| tested at 77.2 °K (-196 °C), 1.67x10^-⁴/s \|\| 0 to 0.8 mm/mm strain SSC : low impurities, hot-rolled & annealed 15.9 mm (0.625 inch) diameter rounds \|\| tested at 123 °K (-150 °C), 1.67x10^-⁴/s \|\| 0 to 0.88 mm/mm strain SSC : low impurities, hot-rolled & annealed 15.9 mm (0.625 inch) diameter rounds \|\| tested at 195 °K (-78 °C), 1.67x10^-⁴/s \|\| 0 to 0.7 mm/mm strain SSC : high impurities, hot-rolled and annealed 25.4 mm (1 inch) diameter bar \|\| tested at 77.2 °K (-196 °C), 1.67x10^-⁴/s \|\| 0 to 0.34 mm/mm strain SSC : high impurities, hot-rolled and annealed 25.4 mm (1 inch) diameter bar \|\| tested at 195 °K (-78 °C), 1.67x10^-⁴/s \|\| 0 to 0.5 mm/mm strain UTS : low impurities, hot-rolled and annealed 15.9 mm (0.625 inch) diameter bar \|\| 77 K to 373 K (-196.1 °C to 100 °C) UTS : high impurities, hot-rolled and annealed 25.4 mm (1 inch) diameter bar \|\| 77 K to 423 K (-196.1 °C to 150 °C) UTS : annealed 2 h at 978 °K (704 °C) \|\| 2.5x10^-⁵/s \|\| 17 K to 300 K (-256.1 °C to 26.9 °C) UTS : 1.5 mm (0.0591 inch) sheet, cold-rolled & annealed \|\| 0.001/s \|\| 20 K to 298 K (-253.1 °C to 24.9 °C) UTS : average of all \|\| 17 K to 873 K (-256.1 °C to 600 °C) YS : low impurities, hot-rolled and annealed 15.9 mm (0.625 inch) diameter bar \|\| 77 K to 373 K (-196.1 °C to 100 °C) YS : high impurities, hot-rolled and annealed 25.4 mm (1 inch) diameter bar \|\| 77 K to 423 K (-196.1 °C to 150 °C) YS : annealed 2 h at 978 °K (704 °C) \|\| 2.5x10^-⁵/s \|\| 17 K to 300 K (-256.1 °C to 26.9 °C) YS : 1.5 mm (0.0591 inch) sheet, cold-rolled & annealed \|\| 0.001/s \|\| 20 K to 298 K (-253.1 °C to 24.9 °C) YS : average of all \|\| 17 K to 873 K (-256.1 °C to 600 °C) %El : low impurities, hot-rolled and annealed 15.9 mm (0.625 inch) diameter bar \|\| 77 K to 373 K (-196.1 °C to 100 °C) %El : high impurities, hot-rolled and annealed 25.4 mm (1 inch) diameter bar \|\| 77 K to 423 K (-196.1 °C to 150 °C) %El : annealed 2 h at 978 °K (704 °C) \|\| 2.5x10^-⁵/s \|\| 17 K to 300 K (-256.1 °C to 26.9 °C) %El : 1.5 mm (0.0591 inch) sheet, cold-rolled & annealed \|\| 0.001/s \|\| 20 K to 298 K (-253.1 °C to 24.9 °C) %El : average of all \|\| 17 K to 873 K (-256.1 °C to 600 °C)
Ti Grade 3 (UNS R50500) (WNr 3.7055) (ASTM B265/B337/B338/B348/B363/B381/B861/B862/F67) (AMS 4900)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 93 K to 1073 K (-180.1 °C to 800 °C) TC : solid \|\| annealed \|\| 0 K to 1950 K (-273.1 °C to 1676.8 °C) TD : solid \|\| annealed \|\| 100 K to 1144 K (-173.1 °C to 870.9 °C) SH : solid \|\| 100 K to 1944 K (-173.1 °C to 1670.8 °C)
Ti Grade 4 (UNS R50700) (WNr 3.7065) (ASTM B265/B348/B367/B381/F1341/F67) (AMS 4901/4902/4921)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 93 K to 1073 K (-180.1 °C to 800 °C) TC : solid \|\| annealed \|\| 0 K to 1950 K (-273.1 °C to 1676.8 °C) TD : solid \|\| annealed \|\| 100 K to 1144 K (-173.1 °C to 870.9 °C) SH : solid \|\| 100 K to 1944 K (-173.1 °C to 1670.8 °C) UTS : 1.5 mm (0.0591 inch) sheet, cold-rolled & annealed \|\| 0.001/s \|\| 20 K to 298 K (-253.1 °C to 25 °C) UTS : combination of as-received, hot-rolled and annealed bar and cold-rolled & annealed sheet \|\| 20 K to 811 K (-253.1 °C to 537.9 °C) YS : 1.5 mm (0.0591 inch) sheet, cold-rolled & annealed \|\| 0.001/s \|\| 20 K to 298 K (-253.1 °C to 25 °C) YS : combination of as-received, hot-rolled and annealed bar and cold-rolled & annealed sheet \|\| 20 K to 811 K (-253.1 °C to 537.9 °C) %El : 1.5 mm (0.0591 inch) sheet, cold-rolled & annealed \|\| 0.001/s \|\| 20 K to 298 K (-253.1 °C to 25 °C) %El : combination of as-received, hot-rolled and annealed bar and cold-rolled & annealed sheet \|\| 20 K to 811 K (-253.1 °C to 537.9 °C) RHO : solid \|\| alpha \|\| 77 K to 1100 K (-196.1 °C to 826.9 °C) SIGMA : solid \|\| alpha \|\| 77 K to 1100 K (-196.1 °C to 826.9 °C)
Ti - 6 Al - 4 V (UNS R56400)	D : solid \|\| 4 K to 1033 K (-269.1 °C to 760 °C) DLL : solid \|\| 4 K to 1033 K (-269.1 °C to 760 °C) MTE : solid \|\| 4 K to 1033 K (-269.1 °C to 760 °C) E : solid \|\| 33 K to 1200 K (-240.1 °C to 926.9 °C) TC : solid \|\| annealed \|\| 4 K to 1863 K (-269.1 °C to 1590 °C) TD : solid \|\| 21 K to 1220 K (-252.1 °C to 946.9 °C) SH : solid \|\| 21 K to 1900 K (-252.1 °C to 1626.8 °C) SSCC : annealed commercial rod \|\| tested at 77 °K (-196.1 °C), 1900/s \|\| 0 to 0.13 mm/mm strain UTS : bar \|\| hot-rolled at 973 °K (700 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar \|\| hot-rolled at 1023 °K (750 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar \|\| hot-rolled at 1073 °K (800 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar \|\| hot-rolled at 1123 °K (850 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar \|\| hot-rolled at 1223 °K (950 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar \|\| annealed \|\| 20 K to 293 K (-253.1 °C to 20 °C) UTS : bar, extra low interstitial \|\| hot-rolled at 1023 °K (750 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar, extra low interstitial \|\| hot-rolled at 1073 °K (800 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar, extra low interstitial \|\| hot-rolled at 1123 °K (850 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar, extra low interstitial \|\| hot-rolled at 1173 °K (900 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar, extra low interstitial \|\| hot-rolled at 1223 °K (950 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : annealed, combined datasets \|\| 20 K to 800 K (-253.1 °C to 526.9 °C) YS : bar \|\| hot-rolled at 973 °K (700 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar \|\| hot-rolled at 1023 °K (750 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar \|\| hot-rolled at 1073 °K (800 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar \|\| hot-rolled at 1123 °K (850 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar \|\| hot-rolled at 1223 °K (950 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar \|\| annealed \|\| 20 K to 293 K (-253.1 °C to 20 °C) YS : bar, extra low interstitial \|\| hot-rolled at 1023 °K (750 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar, extra low interstitial \|\| hot-rolled at 1073 °K (800 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar, extra low interstitial \|\| hot-rolled at 1123 °K (850 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar, extra low interstitial \|\| hot-rolled at 1173 °K (900 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar, extra low interstitial \|\| hot-rolled at 1223 °K (950 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : annealed, combined datasets \|\| 20 K to 800 K (-253.1 °C to 526.9 °C) %El : bar \|\| hot-rolled at 973 °K (700 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar \|\| hot-rolled at 1023 °K (750 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar \|\| hot-rolled at 1073 °K (800 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar \|\| hot-rolled at 1123 °K (850 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar \|\| hot-rolled at 1223 °K (950 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar \|\| annealed \|\| 20 K to 293 K (-253.1 °C to 20 °C) %El : bar, extra low interstitial \|\| hot-rolled at 1023 °K (750 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar, extra low interstitial \|\| hot-rolled at 1073 °K (800 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar, extra low interstitial \|\| hot-rolled at 1123 °K (850 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar, extra low interstitial \|\| hot-rolled at 1173 °K (900 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar, extra low interstitial \|\| hot-rolled at 1223 °K (950 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) FEN : vacuum annealed bar \|\| tested at 4 °K (-269.1 °C), R = -1, axial, total strain range \|\| 80 cycles to 2.2x10⁴ cycles FEN : vacuum annealed bar \|\| tested at 78 °K (-195.1 °C), R = -1, axial, total strain range \|\| 40 cycles to 3.5x10⁴ cycles FSN : annealed \|\| tested at 194 °K (-79 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 2x10⁶ cycles FSN : annealed \|\| tested at 77.6 °K (-195.6 °C), R = -1, flexure, maximum stress \|\| 4x10⁴ cycles to 1x10⁶ cycles FSN : annealed \|\| tested at 20.4 °K (-252.8 °C), R = -1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed \|\| tested at 194 °K (-79 °C), R = -1, K_t = 3.1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : annealed \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 3.1, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : annealed \|\| tested at 20.4 °K (-252.8 °C), R = -1, K_t = 3.1, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : annealed \|\| tested at 194 °K (-79 °C), R = -1, K_t = 6.4, flexure, maximum stress \|\| 1x10⁴ cycles to 4x10⁴ cycles FSN : annealed \|\| tested at 77.6 °K (-195.6 °C), R = -1, K_t = 6.4, flexure, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles FSN : annealed \|\| tested at 20.4 °K (-252.8 °C), R = -1, K_t = 6.4, flexure, maximum stress \|\| 2x10⁴ cycles to 1x10⁶ cycles FSN : low-interstitial \|\| tested at 77 °K (-196.1 °C), R = 0.01, axial, maximum stress \|\| 2x10³ cycles to 2x10⁶ cycles FSN : low-interstitial \|\| tested at 20 °K (-253.1 °C), R = 0.01, axial, maximum stress \|\| 1x10⁴ cycles to 1x10⁶ cycles NE : solid \|\| polished \|\| 33 K to 923 K (-240.1 °C to 650 °C) RHO : solid \|\| 19 K to 1900 K (-254.1 °C to 1626.8 °C) SIGMA : solid \|\| 19 K to 1900 K (-254.1 °C to 1626.8 °C)
Ti - 6 Al - 4 V (Grade 5) (UNS R56400) (ASTM B265/B348/B381/B861/F467/F468) (AMS 4911/4928/4935/4965/4967)	E : solid \|\| 33 K to 1200 K (-240.1 °C to 926.9 °C) TC : solid \|\| heat-treated at 1200 °K (927 °C) & 755 °K (482 °C) \|\| 14 K to 907 K (-259.1 °C to 633.9 °C) UTS : annealed, combined datasets \|\| 20 K to 800 K (-253.1 °C to 526.9 °C) YS : annealed, combined datasets \|\| 20 K to 800 K (-253.1 °C to 526.9 °C)
Ti - 6 Al - 4 V ELI (Grade 23) (UNS R56407) (ASTM B265/B348/B362/B363/B381/F136/F620) (AMS 4905/4907/4930/4931/4956/4996/4998)	D : solid \|\| 4 K to 1033 K (-269.1 °C to 760 °C) DLL : solid \|\| 4 K to 1033 K (-269.1 °C to 760 °C) MTE : solid \|\| 4 K to 1033 K (-269.1 °C to 760 °C) E : solid \|\| 33 K to 1200 K (-240.1 °C to 926.9 °C) TC : solid \|\| heat-treated at 1200 °K (927 °C) & 755 °K (482 °C) \|\| 14 K to 907 K (-259.1 °C to 633.9 °C) UTS : annealed \|\| un-notched \|\| 22 K to 311 K (-251.1 °C to 37.9 °C) UTS : annealed \|\| notched, K_t = 6.3 \|\| 22 K to 311 K (-251.1 °C to 37.9 °C) YS : annealed \|\| un-notched \|\| 22 K to 311 K (-251.1 °C to 37.9 °C) %El : annealed \|\| un-notched \|\| 22 K to 311 K (-251.1 °C to 37.9 °C) NE : solid \|\| polished \|\| 33 K to 923 K (-240.1 °C to 650 °C)
Ti - 5 Al - 2.5 Sn (Grade 6) (UNS R54520) (WNr 3.7115) (ISO/EN/DIN TiAl5Sn2.5) (ASTM B265/B348/B381) (AMS 4910/4926/4953/4966) (GB & GB/T TA-7)	TC : solid \|\| 0 K to 1888 K (-273.1 °C to 1615 °C) SH : solid \|\| 1 K to 1218 K (-272.1 °C to 945 °C) UTS : mill annealed \|\| 2 K to 811 K (-271.1 °C to 537.9 °C) NE : solid \|\| polished \|\| 53 K to 1089 K (-220.1 °C to 815.4 °C) NE : solid \|\| oxidized \|\| 48 K to 1178 K (-225.1 °C to 904.9 °C)
Ti - 5 Al - 2.5 Sn ELI (AMS 4909/4924)	UTS : solid \|\| 20 K to 293 K (-253.1 °C to 20 °C) YS : solid \|\| 20 K to 293 K (-253.1 °C to 20 °C) %El : solid \|\| 20 K to 293 K (-253.1 °C to 20 °C)
Ti - 0.15 Pd (Grade 7) (UNS R52400) (ASTM B265/B337/B338/B348/B363/B381/B861/B862)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 93 K to 1073 K (-180.1 °C to 800 °C) TC : solid \|\| annealed \|\| 0 K to 1950 K (-273.1 °C to 1676.8 °C) TD : solid \|\| annealed \|\| 100 K to 1144 K (-173.1 °C to 870.9 °C) SH : solid \|\| 100 K to 1944 K (-173.1 °C to 1670.8 °C)
Ti - 0.15 Pd (Grade 11) (UNS R52250) (WNr 3.7235) (ISO/EN/DIN Ti2Pd) (ASTM B265/B337/B338/B348/B363/B381/B861/B862)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 93 K to 1073 K (-180.1 °C to 800 °C) TC : solid \|\| annealed \|\| 0 K to 1950 K (-273.1 °C to 1676.8 °C) TD : solid \|\| annealed \|\| 100 K to 1144 K (-173.1 °C to 870.9 °C) SH : solid \|\| 100 K to 1944 K (-173.1 °C to 1670.8 °C)
Ti - 0.3 Mo - 0.8 Ni (Grade 12) (UNS R53400) (WNr 3.7101/3.7105) (ISO/EN/DIN TiNi0.8Mo0.3) (ASTM B265/B337/B338/B348/B381/B861/B862) (AMS 4902)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 93 K to 1073 K (-180.1 °C to 800 °C) TC : solid \|\| annealed \|\| 0 K to 1950 K (-273.1 °C to 1676.8 °C) TD : solid \|\| annealed \|\| 100 K to 1144 K (-173.1 °C to 870.9 °C) SH : solid \|\| 100 K to 1944 K (-173.1 °C to 1670.8 °C)
Ti - 0.05 Pd (Grade 16) (UNS R52402) (ASTM B265/B337/B338/B348/B381/B861/B862)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 93 K to 1073 K (-180.1 °C to 800 °C) TC : solid \|\| annealed \|\| 0 K to 1950 K (-273.1 °C to 1676.8 °C) TD : solid \|\| annealed \|\| 100 K to 1144 K (-173.1 °C to 870.9 °C) SH : solid \|\| 100 K to 1944 K (-173.1 °C to 1670.8 °C)
Ti - 0.05 Pd (Grade 17) (UNS R52252) (ASTM B265/B337/B338/B348/B363/B363/B861/B862/F-17)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 93 K to 1073 K (-180.1 °C to 800 °C) TC : solid \|\| annealed \|\| 0 K to 1950 K (-273.1 °C to 1676.8 °C) TD : solid \|\| annealed \|\| 100 K to 1144 K (-173.1 °C to 870.9 °C) SH : solid \|\| 100 K to 1944 K (-173.1 °C to 1670.8 °C)
Ti - 8 V - 6 Cr - 4 Mo - 4 Zr - 3 Al (Grade 19) (UNS R58640) (ASTM B265/B348/B363/B381/B861/F-19) (AMS 4957/4958)	RHO : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Ti - 3 Al - 8 V - 6 Cr - 4 Mo - 4 Zr - 0.05 Pd (Grade 20) (UNS R58645) (ASTM B265/B337/B348/B363/B381/B861/F-20/WPT20)	RHO : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Ti - 0.1 Ru (Grade 26) (UNS R52404) (ASTM B265/B337/B338/B348/B363/B381/B861/B862)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 93 K to 1073 K (-180.1 °C to 800 °C) TC : solid \|\| annealed \|\| 0 K to 1950 K (-273.1 °C to 1676.8 °C) TD : solid \|\| annealed \|\| 100 K to 1144 K (-173.1 °C to 870.9 °C) SH : solid \|\| 100 K to 1944 K (-173.1 °C to 1670.8 °C)
Ti - 0.1 Ru (Grade 27) (UNS R52254) (ASTM B265/B337/B338/B348/B363/B381/B861/B862)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| 93 K to 1073 K (-180.1 °C to 800 °C) TC : solid \|\| annealed \|\| 0 K to 1950 K (-273.1 °C to 1676.8 °C) TD : solid \|\| annealed \|\| 100 K to 1144 K (-173.1 °C to 870.9 °C) SH : solid \|\| 100 K to 1944 K (-173.1 °C to 1670.8 °C)
Ti - 5.3 Al - 3 Mo - 1.5 V (wt %)	UTS : bar \|\| hot-rolled at 1023 °K (750 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar \|\| hot-rolled at 1073 °K (800 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar \|\| hot-rolled at 1123 °K (850 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar \|\| hot-rolled at 1173 °K (900 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) UTS : bar \|\| hot-rolled at 1223 °K (950 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar \|\| hot-rolled at 1023 °K (750 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar \|\| hot-rolled at 1073 °K (800 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar \|\| hot-rolled at 1123 °K (850 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar \|\| hot-rolled at 1173 °K (900 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) YS : bar \|\| hot-rolled at 1223 °K (950 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar \|\| hot-rolled at 1023 °K (750 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar \|\| hot-rolled at 1073 °K (800 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar \|\| hot-rolled at 1123 °K (850 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar \|\| hot-rolled at 1173 °K (900 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C) %El : bar \|\| hot-rolled at 1223 °K (950 °C) \|\| 20 K to 300 K (-253.1 °C to 26.9 °C)
UNS R54520 (Ti - 5 Al - 2.5 Sn (wt%)) (UNS R54520)	D : solid \|\| 22 K to 1144 K (-251.1 °C to 870.9 °C) DLL : solid \|\| 22 K to 1144 K (-251.1 °C to 870.9 °C) MTE : solid \|\| 22 K to 1144 K (-251.1 °C to 870.9 °C) E : solid \|\| in tension \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) E : solid \|\| in compression \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) TC : solid \|\| annealed \|\| 4 K to 1089 K (-269.1 °C to 815.6 °C) SSC : normal interstitial \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.6 mm/mm strain SSC : normal interstitial \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate \|\| 0 to 0.3 mm/mm strain SSC : normal interstitial \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate \|\| 0 to 0.1 mm/mm strain SSC : annealed, extra-low interstitial, longitudinal \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.1 mm/mm strain SSC : annealed, extra-low interstitial, longitudinal \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate \|\| 0 to 0.1 mm/mm strain SSC : annealed, extra-low interstitial, longitudinal \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate \|\| 0 to 0.1 mm/mm strain SSC : annealed, extra-low interstitial, transverse \|\| tested at 194 °K (-79 °C), unknown strain rate \|\| 0 to 0.8 mm/mm strain SSC : annealed, extra-low interstitial, transverse \|\| tested at 77.6 °K (-195.6 °C), unknown strain rate \|\| 0 to 0.13 mm/mm strain SSC : annealed, extra-low interstitial, transverse \|\| tested at 20.4 °K (-252.7 °C), unknown strain rate \|\| 0 to 0.17 mm/mm strain UTS : annealed sheet \|\| longitudinal, 0.381 mm to 2.03 mm (0.015 inch to 0.08 inch) \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) UTS : annealed sheet \|\| longitudinal, 2.03 mm to 4.76 mm (0.08 inch to 0.1875 inch) \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) UTS : annealed sheet \|\| long transverse, 2.03 mm to 4.76 mm (0.08 inch to 0.1875 inch) \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) UTS : annealed sheet \|\| long transverse, 0.381 mm to 2.03 mm (0.015 inch to 0.08 inch) \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) YS : annealed sheet \|\| longitudinal, 0.381 mm to 2.03 mm (0.015 inch to 0.08 inch) \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) YS : annealed sheet \|\| longitudinal, 2.03 mm to 4.76 mm (0.08 inch to 0.1875 inch) \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) YS : annealed sheet \|\| long transverse, 2.03 mm to 4.76 mm (0.08 inch to 0.1875 inch) \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) YS : annealed sheet \|\| long transverse, 0.381 mm to 2.03 mm (0.015 inch to 0.08 inch) \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) %El : annealed sheet \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) FEN : vacuum annealed \|\| tested at 4 °K (-269.1 °C), R = -1, axial, total strain range \|\| 50 cycles to 6.5x10⁴ cycles FEN : vacuum annealed \|\| tested at 78 °K (-195.1 °C), R = -1, axial, total strain range \|\| 40 cycles to 6.1x10⁴ cycles FSN : annealed \|\| tested at 77.6 °K (-195.6 °C), R = 0.01, axial, maximum stress \|\| 1x10³ cycles to 6x10⁶ cycles FSN : annealed \|\| tested at 20.4 °K (-252.7 °C), R = 0.01, axial, maximum stress \|\| 1x10³ cycles to 6x10⁶ cycles FSN : TIG welded \|\| tested at 77.6 °K (-195.6 °C), R = 0.01, axial, maximum stress \|\| 4x10³ cycles to 4x10⁶ cycles FSN : TIG welded \|\| tested at 20.4 °K (-252.7 °C), R = 0.01, axial, maximum stress \|\| 8x10³ cycles to 4x10⁶ cycles RHO : solid \|\| 6 K to 811 K (-267.1 °C to 537.9 °C) SIGMA : solid \|\| 6 K to 811 K (-267.1 °C to 537.9 °C)
C-110M (Ti - 8 Mn (wt %)) (UNS R56080) (SAE 8Mn) (AMS 4908A)	NE : solid \|\| polished \|\| 76 K to 993 K (-197.1 °C to 720 °C)
Ti - 4 Al - 4 Mn (wt %)	TC : solid \|\| annealed \|\| 15 K to 811 K (-258.1 °C to 537.9 °C)
Ti-150A (Ti - 3 Cr - 2 Fe (wt %))	D : solid \|\| 88 K to 923 K (-185.1 °C to 650 °C) DLL : solid \|\| 88 K to 923 K (-185.1 °C to 650 °C) MTE : solid \|\| 88 K to 923 K (-185.1 °C to 650 °C) CTE : solid \|\| 88 K to 923 K (-185.1 °C to 650 °C) TC : solid \|\| 88 K to 1367 K (-185.1 °C to 1093.4 °C)
TA16 (Ti - 2 Al - 2.5 Zr (wt %))	SSC : extruded bar \|\| tested at 77 °K (-196.1 °C), 6.67x10^-⁴/s, fine grain \|\| 0 to 0.2 mm/mm strain
Ti - 4 Al - 3 Mo - 1 V (wt %)	SH : solid \|\| solution treated & aged \|\| 21 K to 923 K (-252.1 °C to 650 °C) UTS : mill-annealed \|\| sheet \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C) YS : mill-annealed \|\| sheet \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C) %El : mill-annealed \|\| sheet \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Ti - 4 Al - 4 Mo - 2 Sn (wt %) (IMI550)	E : solid \|\| 77 K to 293 K (-196.1 °C to 20 °C)
Ti - 6.5 Al - 3 Mo - 1 V (wt %)	UTS : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C) YS : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C) %El : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Ti - 7 Al - 3 Mo (wt %)	UTS : mill-annealed \|\| sheet \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C) YS : mill-annealed \|\| sheet \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C) %El : mill-annealed \|\| sheet \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Ti - 7 Al - 4 Mo (wt %) (UNS R56740) (AMS 7Al-4Mo)	UTS : mill-annealed \|\| sheet \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C) YS : mill-annealed \|\| sheet \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C) %El : mill-annealed \|\| sheet \|\| 77 K to 293 K (-196.1 °C to 20 °C) %El : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Ti - 7 Al - 4 V (wt %)	UTS : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C) YS : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C) %El : mill-annealed \|\| bar \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Ti - 8 Al - 1 Mo - 1 V (wt %) (UNS R54810) (AMS 4915/4916/4972/4973)	D : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) DLL : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) MTE : solid \|\| 0 K to 1144 K (-273.1 °C to 870.9 °C) E : solid \|\| in tension \|\| 200 K to 811 K (-73.1 °C to 537.9 °C) E : solid \|\| in compression \|\| 200 K to 811 K (-73.1 °C to 537.9 °C) UTS : single annealed \|\| longitudinal, less than 4.76 mm (0.1875 inch) \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) UTS : single annealed \|\| transverse, less than 4.76 mm (0.1875 inch) \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) UTS : duplex annealed \|\| longitudinal, 0.381 mm (0.015 inch) \|\| 200 K to 644 K (-73.1 °C to 370.9 °C) UTS : duplex annealed \|\| transverse, 0.381 mm (0.015 inch) \|\| 200 K to 644 K (-73.1 °C to 370.9 °C) UTS : duplex annealed \|\| longitudinal, 0.635 mm (0.025 inch) \|\| 200 K to 644 K (-73.1 °C to 370.9 °C) UTS : duplex annealed \|\| transverse, 0.635 mm (0.025 inch) \|\| 200 K to 644 K (-73.1 °C to 370.9 °C) YS : single annealed \|\| longitudinal, less than 4.76 mm (0.1875 inch) \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) YS : single annealed \|\| transverse, less than 4.76 mm (0.1875 inch) \|\| 22 K to 811 K (-251.1 °C to 537.9 °C) YS : duplex annealed \|\| longitudinal, 0.381 mm (0.015 inch) \|\| 200 K to 644 K (-73.1 °C to 370.9 °C) YS : duplex annealed \|\| transverse, 0.381 mm (0.015 inch) \|\| 200 K to 644 K (-73.1 °C to 370.9 °C) YS : duplex annealed \|\| longitudinal, 0.635 mm (0.025 inch) \|\| 200 K to 644 K (-73.1 °C to 370.9 °C) YS : duplex annealed \|\| transverse, 0.635 mm (0.025 inch) \|\| 200 K to 644 K (-73.1 °C to 370.9 °C)
Ti - 13 V - 11 Cr - 3 Al (wt %) (UNS R58010) (AMS 4917/4959)	D : solid \|\| 4 K to 923 K (-269.1 °C to 650 °C) DLL : solid \|\| 4 K to 923 K (-269.1 °C to 650 °C) MTE : solid \|\| 4 K to 923 K (-269.1 °C to 650 °C) CTE : solid \|\| 4 K to 923 K (-269.1 °C to 650 °C) TC : solid \|\| 20 K to 923 K (-253.1 °C to 650 °C) TD : solid \|\| 20 K to 923 K (-253.1 °C to 650 °C) SH : solid \|\| 20 K to 923 K (-253.1 °C to 650 °C) UTS : mill-annealed \|\| sheet \|\| 77 K to 293 K (-196.1 °C to 20 °C) UTS : mill-annealed \|\| bar \|\| 120 K to 293 K (-153.1 °C to 20 °C) YS : mill-annealed \|\| sheet \|\| 77 K to 293 K (-196.1 °C to 20 °C) YS : mill-annealed \|\| bar \|\| 120 K to 293 K (-153.1 °C to 20 °C) %El : mill-annealed \|\| sheet \|\| 120 K to 293 K (-153.1 °C to 20 °C) %El : mill-annealed \|\| bar \|\| 120 K to 293 K (-153.1 °C to 20 °C) RHO : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C) SIGMA : solid \|\| 4 K to 293 K (-269.1 °C to 20 °C)
Ti - 16 V - 2.5 Al (wt %)	D : solution treated & aged sheet \|\| 4 K to 923 K (-269.1 °C to 650 °C) DLL : solution treated & aged sheet \|\| 4 K to 923 K (-269.1 °C to 650 °C) MTE : solution treated & aged sheet \|\| 4 K to 923 K (-269.1 °C to 650 °C) CTE : solution treated & aged sheet \|\| 4 K to 923 K (-269.1 °C to 650 °C) TC : solution treated & aged sheet \|\| 20 K to 923 K (-253.1 °C to 650 °C) TD : solution treated & aged sheet \|\| 20 K to 923 K (-253.1 °C to 650 °C) SH : solution treated & aged sheet \|\| 20 K to 923 K (-253.1 °C to 650 °C) UTS : mill-annealed \|\| sheet \|\| 120 K to 293 K (-153.1 °C to 20 °C) UTS : mill-annealed \|\| bar \|\| 120 K to 293 K (-153.1 °C to 20 °C) YS : mill-annealed \|\| sheet \|\| 120 K to 293 K (-153.1 °C to 20 °C) YS : mill-annealed \|\| bar \|\| 120 K to 293 K (-153.1 °C to 20 °C) %El : mill-annealed \|\| sheet \|\| 120 K to 293 K (-153.1 °C to 20 °C) %El : mill-annealed \|\| bar \|\| 120 K to 293 K (-153.1 °C to 20 °C)
Oxides	Property : Condition // Data range
Ag₂O	D : solid \|\| 173 K to 573 K (-100.1 °C to 300 °C) DLL : solid \|\| 173 K to 573 K (-100.1 °C to 300 °C) MTE : solid \|\| 173 K to 573 K (-100.1 °C to 300 °C)
Al₂O₃ (alpha)	D : solid \|\| 20 K to 2000 K (-253.1 °C to 1726.8 °C) DLL : solid \|\| polycrystal \|\| 20 K to 2000 K (-253.1 °C to 1726.8 °C) DLL : solid \|\| a-axis \|\| 70 K to 2300 K (-203.1 °C to 2026.8 °C) DLL : solid \|\| c-axis \|\| 70 K to 2300 K (-203.1 °C to 2026.8 °C) MTE : solid \|\| polycrystal \|\| 20 K to 2000 K (-253.1 °C to 1726.8 °C) E : solid \|\| polycrystal \|\| 0 K to 1873 K (-273.1 °C to 1600 °C) E : solid \|\| sapphire (a-axis) \|\| 0 K to 1825 K (-273.1 °C to 1551.8 °C) E : solid \|\| sapphire (c-axis) \|\| 0 K to 1825 K (-273.1 °C to 1551.8 °C) TC : solid \|\| 6 K to 2073 K (-267.1 °C to 1800 °C) SH : solid \|\| 10 K to 2250 K (-263.1 °C to 1976.8 °C) HC : solid \|\| 10 K to 2250 K (-263.1 °C to 1976.8 °C)
B₂O₃	SH : solid \|\| 178 K to 723 K (-95.1 °C to 450 °C) HC : solid \|\| 178 K to 723 K (-95.1 °C to 450 °C)
BaO	D : solid \|\| 73 K to 2023 K (-200.1 °C to 1750 °C) DLL : solid \|\| 73 K to 2023 K (-200.1 °C to 1750 °C) MTE : solid \|\| 73 K to 2023 K (-200.1 °C to 1750 °C) SH : solid \|\| 10 K to 2000 K (-263.1 °C to 1726.8 °C) HC : solid \|\| 10 K to 2000 K (-263.1 °C to 1726.8 °C)
BeO	TC : solid \|\| 0 K to 2673 K (-273.1 °C to 2400 °C) SH : solid \|\| 5 K to 2373 K (-268.1 °C to 2100 °C) HC : solid \|\| 5 K to 2373 K (-268.1 °C to 2100 °C)
CO	D : saturated liquid \|\| 67 K to 133 K (-206.1 °C to -140 °C) D : gas \|\| 135 K to 2000 K (-138.1 °C to 1726.8 °C) DLL : saturated liquid \|\| 67 K to 133 K (-206.1 °C to -140 °C) MTE : saturated liquid \|\| 67 K to 133 K (-206.1 °C to -140 °C) TC : liquid \|\| 78 K to 112 K (-195.1 °C to -161.1 °C) TC : gas \|\| 80 K to 3273 K (-193.1 °C to 3000 °C) SH : solid \|\| 13 K to 67 K (-260.1 °C to -206.1 °C) HC : solid \|\| 13 K to 67 K (-260.1 °C to -206.1 °C) VP : gas \|\| 75 K to 130 K (-198.1 °C to -143.1 °C) Vis : liquid \|\| 68 K to 81 K (-205 °C to -192.1 °C) Vis : gas \|\| 75 K to 1000 K (-198.1 °C to 726.9 °C) ST : liquid \|\| 81 K to 91 K (-192.1 °C to -182.1 °C)
CO₂	D : solid \|\| 177 K to 216 K (-96.1 °C to -56.8 °C) DLL : solid \|\| 177 K to 216 K (-96.1 °C to -56.8 °C) MTE : solid \|\| 177 K to 216 K (-96.1 °C to -56.8 °C) SH : solid \|\| 23 K to 198 K (-250.1 °C to -75 °C) HC : solid \|\| 23 K to 198 K (-250.1 °C to -75 °C) VP : solid \|\| 128 K to 195 K (-145.1 °C to -78.1 °C)
CaO	D : solid \|\| 73 K to 2800 K (-200.1 °C to 2526.8 °C) DLL : solid \|\| 73 K to 2800 K (-200.1 °C to 2526.8 °C) MTE : solid \|\| 73 K to 2800 K (-200.1 °C to 2526.8 °C)
CdO	D : solid \|\| 73 K to 1773 K (-200.1 °C to 1500 °C) DLL : solid \|\| 73 K to 1773 K (-200.1 °C to 1500 °C) MTE : solid \|\| 73 K to 1773 K (-200.1 °C to 1500 °C)
CeO₂	D : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) DLL : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) MTE : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C)
Co₃O₄	D : solid \|\| 73 K to 1773 K (-200.1 °C to 1500 °C) DLL : solid \|\| 73 K to 1773 K (-200.1 °C to 1500 °C) MTE : solid \|\| 73 K to 1773 K (-200.1 °C to 1500 °C)
Cr₂O₃	SH : solid \|\| 50 K to 2000 K (-223.1 °C to 1726.8 °C) HC : solid \|\| 50 K to 2000 K (-223.1 °C to 1726.8 °C)
CuO	SH : solid \|\| 10 K to 1250 K (-263.1 °C to 976.9 °C) HC : solid \|\| 10 K to 1250 K (-263.1 °C to 976.9 °C)
Cu₂O	D : solid \|\| 73 K to 1573 K (-200.1 °C to 1300 °C) DLL : solid \|\| 73 K to 1573 K (-200.1 °C to 1300 °C) MTE : solid \|\| 73 K to 1573 K (-200.1 °C to 1300 °C) SH : solid \|\| 1 K to 1516 K (-272.1 °C to 1242.8 °C) HC : solid \|\| 1 K to 1516 K (-272.1 °C to 1242.8 °C)
Dy₂O₃	D : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) DLL : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) MTE : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) CTE : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C)
Er₂O₃	D : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) DLL : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) MTE : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C)
Eu₂O₃	D : solid \|\| 73 K to 1473 K (-200.1 °C to 1200 °C) DLL : solid \|\| 73 K to 1473 K (-200.1 °C to 1200 °C) MTE : solid \|\| 73 K to 1473 K (-200.1 °C to 1200 °C) CTE : solid \|\| 73 K to 1473 K (-200.1 °C to 1200 °C)
Fe₂O₃ (hematite)	SH : solid \|\| 5 K to 1800 K (-268.1 °C to 1526.8 °C) HC : solid \|\| 5 K to 1800 K (-268.1 °C to 1526.8 °C)
Fe₃O₄ (magnetite)	D : solid \|\| 73 K to 1773 K (-200.1 °C to 1500 °C) DLL : solid \|\| 73 K to 1773 K (-200.1 °C to 1500 °C) MTE : solid \|\| 73 K to 1773 K (-200.1 °C to 1500 °C) TC : solid \|\| single crystal \|\| 0 K to 300 K (-273.1 °C to 27 °C) TD : solid \|\| single crystal \|\| 73 K to 300 K (-200.1 °C to 27 °C) SH : solid \|\| 2 K to 1815 K (-271.6 °C to 1541.8 °C) HC : solid \|\| 2 K to 1815 K (-271.6 °C to 1541.8 °C)
Fe₃O₄ (Co, Mn, & Zn doped)	D : undoped \|\| 73 K to 1773 K (-200.1 °C to 1500 °C) DLL : undoped \|\| 73 K to 1773 K (-200.1 °C to 1500 °C) MTE : undoped \|\| 73 K to 1773 K (-200.1 °C to 1500 °C) TC : solid \|\| single crystal \|\| 0 K to 300 K (-273.1 °C to 27 °C) TD : solid \|\| single crystal \|\| 73 K to 300 K (-200.1 °C to 27 °C) SH : undoped \|\| 2 K to 1815 K (-271.6 °C to 1541.8 °C) HC : undoped \|\| 2 K to 1815 K (-271.6 °C to 1541.8 °C)
Ga₂O₃	TC : beta \|\| a-axis \|\| 84 K to 490 K (-189.1 °C to 216.9 °C) TC : beta \|\| b-axis \|\| 84 K to 490 K (-189.1 °C to 216.9 °C) TC : beta \|\| c-axis \|\| 84 K to 490 K (-189.1 °C to 216.9 °C) TC : beta \|\| [-201] axis \|\| 84 K to 490 K (-189.1 °C to 216.9 °C)
Gd₂O₃	D : solid \|\| 73 K to 1673 K (-200.1 °C to 1400 °C) DLL : solid \|\| 73 K to 1673 K (-200.1 °C to 1400 °C) MTE : solid \|\| 73 K to 1673 K (-200.1 °C to 1400 °C)
GeO₂ (vitreous)	D : solid \|\| 93 K to 873 K (-180.1 °C to 600 °C) DLL : solid \|\| 93 K to 873 K (-180.1 °C to 600 °C) MTE : solid \|\| 93 K to 873 K (-180.1 °C to 600 °C) CTE : solid \|\| 93 K to 673 K (-180.1 °C to 400 °C) E : solid \|\| 73 K to 823 K (-200.1 °C to 550 °C)
H₂O (water)	D : solid \|\| 73 K to 273 K (-200.1 °C to 0 °C) DLL : solid \|\| 73 K to 273 K (-200.1 °C to 0 °C) MTE : solid \|\| 73 K to 273 K (-200.1 °C to 0 °C) CTE : solid \|\| 73 K to 273 K (-200.1 °C to 0 °C) E : solid \|\| 0 K to 273 K (-273.1 °C to -0.1 °C) G : solid \|\| 0 K to 273 K (-273.1 °C to -0.1 °C) v : solid \|\| 0 K to 273 K (-273.1 °C to -0.1 °C) K : solid \|\| 0 K to 273 K (-273.1 °C to -0.1 °C) TC : solid \|\| 4 K to 273 K (-269.1 °C to 0 °C) TD : solid \|\| 73 K to 273 K (-200.1 °C to 0 °C) SH : solid \|\| 1 K to 273 K (-272.1 °C to 0 °C) HC : solid \|\| 1 K to 273 K (-272.1 °C to 0 °C) VP : solid \|\| 200 K to 270 K (-73.1 °C to -3.1 °C)
In₂O₃	D : solid \|\| 73 K to 2273 K (-200.1 °C to 2000 °C) DLL : solid \|\| 73 K to 2273 K (-200.1 °C to 2000 °C) MTE : solid \|\| 73 K to 2273 K (-200.1 °C to 2000 °C) CTE : solid \|\| 73 K to 2273 K (-200.1 °C to 2000 °C) SH : solid \|\| 0 K to 1600 K (-273.1 °C to 1326.8 °C) HC : solid \|\| 0 K to 1600 K (-273.1 °C to 1326.8 °C)
La₂O₃	D : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) DLL : solid \|\| polycrystal \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) DLL : solid \|\| a-axis \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) DLL : solid \|\| c-axis \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) MTE : solid \|\| polycrystal \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) MTE : solid \|\| a-axis \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) MTE : solid \|\| c-axis \|\| 73 K to 2523 K (-200.1 °C to 2250 °C)
Lu₂O₃	D : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) DLL : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C) MTE : solid \|\| 73 K to 2523 K (-200.1 °C to 2250 °C)
MgO	D : solid \|\| 73 K to 3000 K (-200.1 °C to 2726.8 °C) DLL : solid \|\| 73 K to 3000 K (-200.1 °C to 2726.8 °C) MTE : solid \|\| 73 K to 3000 K (-200.1 °C to 2726.8 °C) E : solid \|\| polycrystal \|\| 80 K to 1100 K (-193.1 °C to 826.9 °C) G : solid \|\| polycrystal \|\| 80 K to 1100 K (-193.1 °C to 826.9 °C) v : solid \|\| polycrystal \|\| 80 K to 1100 K (-193.1 °C to 826.9 °C) K : solid \|\| polycrystal \|\| 80 K to 1050 K (-193.1 °C to 776.9 °C) TC : solid \|\| polycrystal \|\| 100 K to 2973 K (-173.1 °C to 2700 °C) TC : solid \|\| single crystal \|\| 0 K to 500 K (-273.1 °C to 227 °C) TD : solid \|\| polycrystal \|\| 100 K to 2000 K (-173.1 °C to 1727 °C) TD : solid \|\| single crystal \|\| 20 K to 500 K (-253.1 °C to 227 °C) SH : solid \|\| 20 K to 2000 K (-253.1 °C to 1726.8 °C) HC : solid \|\| 20 K to 2000 K (-253.1 °C to 1726.8 °C) NE : solid \|\| 88 K to 1755 K (-185.1 °C to 1481.8 °C)
MnO	D : solid \|\| 173 K to 2023 K (-100.1 °C to 1750 °C) DLL : solid \|\| 173 K to 2023 K (-100.1 °C to 1750 °C) MTE : solid \|\| 173 K to 2023 K (-100.1 °C to 1750 °C) TC : solid \|\| single crystal \|\| 0 K to 500 K (-273.1 °C to 227 °C) TD : solid \|\| single crystal \|\| 10 K to 500 K (-263.1 °C to 227 °C) SH : solid \|\| 10 K to 1800 K (-263.1 °C to 1526.8 °C) HC : solid \|\| 10 K to 1800 K (-263.1 °C to 1526.8 °C)
MnO₂	SH : solid \|\| 10 K to 800 K (-263.1 °C to 526.9 °C) HC : solid \|\| 10 K to 800 K (-263.1 °C to 526.9 °C)
Mn₂O₃	SH : solid \|\| 10 K to 1350 K (-263.1 °C to 1076.8 °C) HC : solid \|\| 10 K to 1350 K (-263.1 °C to 1076.8 °C)
Mn₃O₄	D : solid \|\| 73 K to 1373 K (-200.1 °C to 1100 °C) DLL : solid \|\| polycrystal \|\| 73 K to 1373 K (-200.1 °C to 1100 °C) DLL : solid \|\| a-axis \|\| 73 K to 1373 K (-200.1 °C to 1100 °C) DLL : solid \|\| c-axis \|\| 73 K to 1373 K (-200.1 °C to 1100 °C) MTE : solid \|\| polycrystal \|\| 73 K to 1373 K (-200.1 °C to 1100 °C) MTE : solid \|\| a-axis \|\| 73 K to 1373 K (-200.1 °C to 1100 °C) MTE : solid \|\| c-axis \|\| 73 K to 1373 K (-200.1 °C to 1100 °C) SH : solid \|\| 10 K to 1800 K (-263.1 °C to 1526.8 °C) HC : solid \|\| 10 K to 1800 K (-263.1 °C to 1526.8 °C)
MoO₃	SH : solid \|\| 20 K to 1111 K (-253.1 °C to 837.9 °C) HC : solid \|\| 20 K to 1111 K (-253.1 °C to 837.9 °C)
NO	D : gas \|\| 125 K to 2000 K (-148.1 °C to 1726.8 °C) TC : gas \|\| 150 K to 3273 K (-123.1 °C to 3000 °C) TD : gas \|\| 200 K to 3273 K (-73.1 °C to 3000 °C) SH : gas \|\| 200 K to 6000 K (-73.1 °C to 5726.9 °C) HC : gas \|\| 200 K to 6000 K (-73.1 °C to 5726.9 °C) VP : solid \|\| 77 K to 109 K (-196.1 °C to -164.1 °C) VP : liquid \|\| 109 K to 121 K (-164.1 °C to -152.1 °C) Vis : gas \|\| 200 K to 1000 K (-73.1 °C to 726.9 °C) ST : liquid \|\| 113 K to 121 K (-160.1 °C to -152.1 °C)
N₂O	D : gas \|\| 190 K to 2000 K (-83.1 °C to 1726.8 °C) TC : gas \|\| 180 K to 3273 K (-93.1 °C to 3000 °C) TD : gas \|\| 200 K to 2000 K (-73.1 °C to 1726.8 °C) SH : gas \|\| 200 K to 5900 K (-73.1 °C to 5626.9 °C) HC : gas \|\| 200 K to 5900 K (-73.1 °C to 5626.9 °C) VP : solid \|\| 117 K to 182 K (-156.1 °C to -90.8 °C) VP : liquid \|\| 182 K to 184 K (-90.8 °C to -89.1 °C) VP : gas \|\| 200 K to 290 K (-73.1 °C to 16.9 °C) Vis : gas \|\| 200 K to 470 K (-73.1 °C to 196.9 °C) ST : liquid \|\| 173 K to 263 K (-100.1 °C to -10 °C)
NbO	D : solid \|\| 73 K to 1473 K (-200.1 °C to 1200 °C) DLL : solid \|\| 73 K to 1473 K (-200.1 °C to 1200 °C) MTE : solid \|\| 73 K to 1473 K (-200.1 °C to 1200 °C)
NbO₂	D : solid \|\| 73 K to 2023 K (-200.1 °C to 1750 °C) DLL : solid \|\| polycrystal \|\| 73 K to 2

Dataset listing below 200 K by material