Changes

Contact Us
title banner
Changes


New and revised materials and properties in MPDB v9.79 as compared to v9.77


Key to property symbols (number of datasets):

D     = Density
 DLL   = Linear thermal expansion (ΔL/L)
MTE   = Mean coefficient of thermal expansion
 CTE   = Coefficient of thermal expansion (CTE)
E     = Elastic/Young's modulus
 G     = Shear modulus
v     = Poisson's ratio
 K     = Bulk modulus
TC    = Thermal conductivity
 TD    = Thermal diffusivity
SH    = Specific heat
 HC    = Heat capacity
SSC   = True stress-strain curve (tension)
 SSCC  = True stress-strain curve (compression)
UTS   = Tensile strength
 YS    = Yield strength (tension)
UCS   = Compressive strength
 YSC   = Yield strength (compression)
%El   = Elongation
 SR    = Stress rupture
FEN   = Fatigue ε-N curve
 FSN   = Fatigue S-N curve
CRS   = Creep strength
 IC    = Isochronous creep
HE    = Hemispherical total emissivity
 NE    = Normal total emissivity
VP    = Vapor pressure
 Vis   = Viscosity
ST    = Surface tension
 RHO   = Electrical resistivity
SIGMA = Electrical conductivity
 SV    = Specific volume
AV    = Apparent viscosity
 FM    = Flexural modulus
FS    = Flexural strength
 ESSC  = Engineering stress-strain curve (tension)
ESSCC = Engineering stress-strain curve (compression)
 CRM   = Creep modulus
RPB   = Relative permeability
 AP    = Absolute permeability
BH    = B-H curve
 HB    = H-B curve
CL    = Core loss
 EP    = Exciting Power
DCRPT = Relative permittivity
 DF    = Dissipation factor
RIW   = Refractive index vs λ
 RIT   = Refractive index vs T
S     = Seebeck coefficient


"(N)" indicates the data is new, "(R)" indicates the data has been revised, * indicates the data is the RT value only

659 new materials, 2708 new property sets, 142 revised properties, and 1861 new RT values


97% sunflower - 3% Olive oil (New) 70% sunflower - 30% Olive oil (New) 304 430 7055 (New)
316 (Revised) A357 7A85 A356.0 Ag - 42 Te (at %) (New)
Ag2S Ag2Te Al - 10 Cu (wt %) Al - 15 Cu (wt %) Al - 25 Cu (wt %)
Al - 0.5 Cu (wt %) Al - 1 Cu (wt %) Al - 1.5 Cu (wt %) Al - 3 Cu (wt %) Al - 5 Cu (wt %)
Al - 22.5 Cu (wt %) (New) Al - 33 Cu (wt %) (Revised) Al - 21 Cu (wt %) (Revised) Al - 7 Si (wt %) Al - 1 Si (wt %) (New)
Al - 8 Si (wt %) (New) Al - 9 Si (wt %) (New) Al - 10 Si (wt %) (New) Al - 11 Si (wt %) (New) Al - 11.5 Si (wt %) (New)
Al - 12 Si (wt %) (New) Al - 12.6 Si (wt %) (New) Al - 2 Si (wt %) (New) Al - 3 Si (wt %) (New) Al - 4 Si (wt %) (New)
Al - 5 Si (wt %) (New) Al - 6 Si (wt %) (New) 3.8 Al2O3 - 55.67 SiO2 - 35.53 CaO - 5 K2O (mol %) slag (New) 9.9 Al2O3 - 54.35 SiO2 - 34.75 CaO - 1 K2O (mol %) slag (New) 9.7 Al2O3 - 53.25 SiO2 - 34.05 CaO - 3 K2O (mol %) slag (New)
9.5 Al2O3 - 52.16 SiO2 - 33.35 CaO - 5 K2O (mol %) slag (New) 1.98 Al2O3 - 59.2 SiO2 - 37.82 CaO - 1 K2O (mol %) slag (New) 1.94 Al2O3 - 58.01 SiO2 - 37.05 CaO - 3 K2O (mol %) slag (New) 1.9 Al2O3 - 56.81 SiO2 - 36.29 CaO - 5 K2O (mol %) slag (New) 3.96 Al2O3 - 58.01 SiO2 - 37.03 CaO - 1 K2O (mol %) slag (New)
3.88 Al2O3 - 56.84 SiO2 - 36.28 CaO - 3 K2O (mol %) slag (New) 34 Al2O3 - 18 SiO2 - 39 CaO - 9 MgO (mol %) slag (New) 34 Al2O3 - 14 SiO2 - 45 CaO - 7 MgO (mol %) slag (New) 43 Al2O3 - 9 SiO2 - 43 CaO - 5 MgO (mol %) slag (New) 25.7 Al2O3 - 58.4 SiO2 - 10.7 CaO - 61.6 MgO (mol %) slag (New)
29 Al2O3 - 60 SiO2 - 11.6 CaO - 57.1 MgO (mol %) slag (New) 29.7 Al2O3 - 65.2 SiO2 - 28.5 CaO - 39.5 MgO (mol %) slag (New) 31.8 Al2O3 - 64.6 SiO2 - 23.3 CaO - 42.4 MgO (mol %) slag (New) 32.2 Al2O3 - 62.9 SiO2 - 12.8 CaO - 42.9 MgO (mol %) slag (New) 32.4 Al2O3 - 61.7 SiO2 - 12.9 CaO - 52.2 MgO (mol %) slag (New)
33.4 Al2O3 - 63.1 SiO2 - 13.3 CaO - 44.6 MgO (mol %) slag (New) 33.7 Al2O3 - 64.1 SiO2 - 18.8 CaO - 44.9 MgO (mol %) slag (New) 34.4 Al2O3 - 63.3 SiO2 - 13.9 CaO - 45.8 MgO (mol %) slag (New) 35.6 Al2O3 - 63.5 SiO2 - 14.2 CaO - 47.4 MgO (mol %) slag (New) 36.2 Al2O3 - 65.3 SiO2 - 16 CaO - 37.4 MgO (mol %) slag (New)
39 Al2O3 - 64.8 SiO2 - 13.5 CaO - 44.9 MgO (mol %) slag (New) 39.3 Al2O3 - 64.6 SiO2 - 8.8 CaO - 40.6 MgO (mol %) slag (New) 42.2 Al2O3 - 66.1 SiO2 - 12.8 CaO - 42.5 MgO (mol %) slag (New) 46.4 Al2O3 - 67.8 SiO2 - 11.8 CaO - 39.5 MgO (mol %) slag (New) 20 Al2O3 - 38 SiO2 - 38 CaO - 4 MgO (mol %) slag (New)
20 Al2O3 - 36 SiO2 - 36 CaO - 8 MgO (mol %) slag (New) 26 Al2O3 - 35 SiO2 - 35 CaO - 4 MgO (mol %) slag (New) 26 Al2O3 - 33 SiO2 - 33 CaO - 8 MgO (mol %) slag (New) 32 Al2O3 - 20 SiO2 - 38 CaO - 9 MgO (mol %) slag (New) 2 Al2O3 - 59.8 SiO2 - 38.2 CaO (mol %) slag (New)
26 Al2O3 - 37 SiO2 - 37 CaO (mol %) slag (New) 10 Al2O3 - 54.9 SiO2 - 35.1 CaO (mol %) slag (New) 8 Al2O3 - 58 SiO2 - 34 CaO (mol %) slag (New) 13.1 Al2O3 - 55.4 SiO2 - 31.5 CaO (mol %) slag (New) 10.1 Al2O3 - 48.5 SiO2 - 41.5 CaO (mol %) slag (New)
16 Al2O3 - 45 SiO2 - 39 CaO (mol %) slag (New) 21 Al2O3 - 43 SiO2 - 36 CaO (mol %) slag (New) 11.5 Al2O3 - 48.8 SiO2 - 39.7 CaO (mol %) slag (New) 11.8 Al2O3 - 48.6 SiO2 - 39.6 CaO (mol %) slag (New) 12 Al2O3 - 42.8 SiO2 - 45.2 CaO (mol %) slag (New)
12 Al2O3 - 46.4 SiO2 - 41.6 CaO (mol %) slag (New) 12.3 Al2O3 - 31.5 SiO2 - 56.2 CaO (mol %) slag (New) 12.4 Al2O3 - 36.9 SiO2 - 50.8 CaO (mol %) slag (New) 12.4 Al2O3 - 42.3 SiO2 - 45.3 CaO (mol %) slag (New) 12.5 Al2O3 - 44.5 SiO2 - 43.1 CaO (mol %) slag (New)
12.5 Al2O3 - 47.7 SiO2 - 39.8 CaO (mol %) slag (New) 12.5 Al2O3 - 53.2 SiO2 - 34.2 CaO (mol %) slag (New) 13.8 Al2O3 - 40.5 SiO2 - 45.7 CaO (mol %) slag (New) 13.8 Al2O3 - 44.9 SiO2 - 41.2 CaO (mol %) slag (New) 13.9 Al2O3 - 49.3 SiO2 - 36.8 CaO (mol %) slag (New)
16.6 Al2O3 - 42.4 SiO2 - 41.1 CaO (mol %) slag (New) 19.4 Al2O3 - 40.9 SiO2 - 39.7 CaO (mol %) slag (New) 2.9 Al2O3 - 44.3 SiO2 - 52.8 CaO (mol %) slag (New) 2.9 Al2O3 - 49.4 SiO2 - 47.7 CaO (mol %) slag (New) 2.9 Al2O3 - 54.6 SiO2 - 42.5 CaO (mol %) slag (New)
2.9 Al2O3 - 59.7 SiO2 - 37.3 CaO (mol %) slag (New) 3.5 Al2O3 - 48.6 SiO2 - 47.9 CaO (mol %) slag (New) 4.7 Al2O3 - 47 SiO2 - 48.3 CaO (mol %) slag (New) 5.3 Al2O3 - 46.2 SiO2 - 48.5 CaO (mol %) slag (New) 5.9 Al2O3 - 40.2 SiO2 - 53.9 CaO (mol %) slag (New)
5.9 Al2O3 - 45.4 SiO2 - 48.7 CaO (mol %) slag (New) 6 Al2O3 - 50.6 SiO2 - 43.4 CaO (mol %) slag (New) 6 Al2O3 - 55.9 SiO2 - 38.1 CaO (mol %) slag (New) 6.8 Al2O3 - 45.7 SiO2 - 47.5 CaO (mol %) slag (New) 6.8 Al2O3 - 46.8 SiO2 - 46.4 CaO (mol %) slag (New)
6.8 Al2O3 - 47.8 SiO2 - 45.4 CaO (mol %) slag (New) 7.8 Al2O3 - 42.9 SiO2 - 49.3 CaO (mol %) slag (New) 7.8 Al2O3 - 48.2 SiO2 - 44 CaO (mol %) slag (New) 8.5 Al2O3 - 47.4 SiO2 - 44.1 CaO (mol %) slag (New) 9.1 Al2O3 - 35.9 SiO2 - 55 CaO (mol %) slag (New)
9.1 Al2O3 - 41.2 SiO2 - 49.7 CaO (mol %) slag (New) 9.1 Al2O3 - 46.5 SiO2 - 44.3 CaO (mol %) slag (New) 9.2 Al2O3 - 51.9 SiO2 - 38.9 CaO (mol %) slag (New) 9.5 Al2O3 - 57.6 SiO2 - 32.9 CaO (mol %) slag (New) 10.4 Al2O3 - 39.5 SiO2 - 50.1 CaO (mol %) slag (New)
10.6 Al2O3 - 52.5 SiO2 - 36.9 CaO (mol %) slag (New) 10.8 Al2O3 - 38.7 SiO2 - 50.6 CaO (mol %) slag (New) 11.1 Al2O3 - 49.4 SiO2 - 39.4 CaO (mol %) slag (New) 11.2 Al2O3 - 39.9 SiO2 - 48.9 CaO (mol %) slag (New) 11.5 Al2O3 - 41.3 SiO2 - 47.1 CaO (mol %) slag (New)
22.1 Al2O3 - 39.5 SiO2 - 38.4 CaO (mol %) slag (New) 25 Al2O3 - 38 SiO2 - 37 CaO (mol %) slag (New) 11 Al2O3 - 50 SiO2 - 39 CaO (mol %) slag (New) 20 Al2O3 - 40 SiO2 - 40 CaO (mol %) slag (New) 4 Al2O3 - 58.6 SiO2 - 37.4 CaO (mol %) slag (New)
7 Al2O3 - 65.1 SiO2 - 27.9 Na2O (mol %) slag (New) Antimony (Revised) 8 Au - 6 Ag - 86 Cu (at %) (New) 10 Au - 25 Ag - 65 Cu (at %) (New) 14 Au - 34 Ag - 52 Cu (at %) (New)
15 Au - 10 Ag - 75 Cu (at %) (New) 17 Au - 42 Ag - 41 Cu (at %) (New) 20 Au - 50 Ag - 30 Cu (at %) (New) 21 Au - 14 Ag - 65 Cu (at %) (New) 22 Au - 55 Ag - 23 Cu (at %) (New)
24 Au - 61 Ag - 15 Cu (at %) (New) 26 Au - 66 Ag - 8 Cu (at %) (New) 29 Au - 19 Ag - 52 Cu (at %) (New) 35 Au - 24 Ag - 41 Cu (at %) (New) 42 Au - 28 Ag - 30 Cu (at %) (New)
47 Au - 31 Ag - 22 Cu (at %) (New) 51 Au - 34 Ag - 15 Cu (at %) (New) 56 Au - 37 Ag - 7 Cu (at %) (New) 4 Au - 3 Ag - 93 Cu (at %) (New) 4 Au - 10 Ag - 86 Cu (at %) (New)
7 Au - 18 Ag - 75 Cu (at %) (New) Au - 20 Cu (wt %) 50 BaO - 50 P2O5 (mol %) (New) B4C (Revised) Bi - 60 In (wt %) (New)
Bi - 52 In (wt %) (New) Bi - 35 In (wt %) (New) Bi - 15 In (wt %) (New) Bi - 85 In (wt %) (New) Bi - 66 In (wt %) (New)
Bi - 12 Sb (at %) (New) Bi - 60 Sb (wt %) (New) Bi - 20 Sb (wt %) (New) Bi - 40 Sb (wt %) (New) Bi - 27.5 Sn (wt %) (New)
Bi - 12.4 Sn (wt %) (New) Bi - 46 Sn (wt %) (Revised) Bi - 30 Te (wt %) (New) Bi - 40 Te (wt %) (New) Bi - 50 Te (wt %) (New)
Bi - 60 Te (wt %) (New) Bi - 70 Te (wt %) (New) Bi - 80 Te (wt %) (New) Bi - 90 Te (wt %) (New) Bi - 10 Te (wt %) (New)
Bi - 20 Te (wt %) (New) Bismuth Bromine Ca1-xErxF2+x (New) 20 CaF2 - 28.8 CaO - 36.8 Al2O3 - 5 SiO2 - 1.5 B2O3 - 8 BaO (wt %) slag (New)
20 CaF2 - 32.8 CaO - 36.8 Al2O3 - 5 SiO2 - 1.5 B2O3 - 4 BaO (wt %) slag (New) 20 CaF2 - 31.8 CaO - 31.8 Al2O3 - 15 SiO2 - 1.5 B2O3 slag (New) 20 CaF2 - 36.8 CaO - 36.8 Al2O3 - 5 SiO2 - 1.5 B2O3 (wt %) slag (New) 20 CaF2 - 34.3 CaO - 34.3 Al2O3 - 10 SiO2 - 1.5 B2O3 (wt %) slag (New) 20 CaF2 - 39.3 CaO - 39.3 Al2O3 - 0 SiO2 - 1.5 B2O3 (wt %) slag (New)
50 CaF2 - 40 SiO2 - 10 MnO (wt %) flux (New) 40 CaF2 - 40 SiO2 - 20 MnO (wt %) flux (New) 30 CaF2 - 40 SiO2 - 30 MnO (wt %) flux (New) 20 CaF2 - 40 SiO2 - 40 MnO (wt %) flux (New) 10 CaF2 - 40 SiO2 - 50 MnO (wt %) flux (New)
Canola/rapeseed oil 40.5 CaO - 40.5 Al2O3 - 14.3 B2O3 - 4.8 La2O3 (wt %) slag (New) 38.6 CaO - 38.6 Al2O3 - 13.6 B2O3 - 9.1 La2O3 (wt %) slag (New) 37.0 CaO - 37.0 Al2O3 - 13.0 B2O3 - 13.0 La2O3 (wt %) slag (New) 42.5 CaO - 42.5 Al2O3 - 15.0 B2O3 (wt %) slag (New)
23.5 CaO - 10 Al2O3 - 66.5 Fe2O3 (wt %) slag (New) 22.2 CaO - 15 Al2O3 - 62.8 Fe2O3 (wt %) slag (New) 14.2 CaO - 5 Al2O3 - 80.8 Fe2O3 (wt %) slag (New) 13.4 CaO - 10 Al2O3 - 76.6 Fe2O3 (wt %) slag (New) 12.7 CaO - 15 Al2O3 - 72.3 Fe2O3 (wt %) slag (New)
24.8 CaO - 5 Al2O3 - 70.2 Fe2O3 (wt %) slag (New) 50 CaO - 50 Al2O3 (wt %) slag 14.9 CaO - 85.1 Fe2O3 (wt %) slag (New) 24.8 CaO - 75.2 Fe2O3 (wt %) slag (New) 26.1 CaO - 73.9 Fe2O3 (wt %) slag (New)
32 CaO - 32 SiO2 - 16 Al2O3 - 20 Fe2O3 (wt %) slag (New) 28 CaO - 28 SiO2 - 14 Al2O3 - 30 Fe2O3 (wt %) slag (New) 24 CaO - 24 SiO2 - 12 Al2O3 - 40 Fe2O3 (wt %) slag (New) 36 CaO - 36 SiO2 - 18 Al2O3 - 10 Fe2O3 (wt %) slag (New) 43 CaO - 43 SiO2 - 8 Al2O3 - 2 Li2O - 0 Na2O - 4 K2O (mol %) slag (New)
43 CaO - 43 SiO2 - 8 Al2O3 - 4 Li2O - 0 Na2O - 2 K2O (mol %) slag (New) 43 CaO - 43 SiO2 - 8 Al2O3 - 0 Li2O - 2 Na2O - 4 K2O (mol %) slag (New) 43 CaO - 43 SiO2 - 8 Al2O3 - 0 Li2O - 4 Na2O - 2 K2O (mol %) slag (New) 43 CaO - 43 SiO2 - 8 Al2O3 - 2 Li2O - 2 Na2O - 2 K2O (mol %) slag (New) 45 CaO - 45 SiO2 - 4 Al2O3 - 0 Li2O - 0 Na2O - 6 K2O (mol %) slag (New)
45 CaO - 45 SiO2 - 4 Al2O3 - 2 Li2O - 0 Na2O - 4 K2O (mol %) slag (New) 45 CaO - 45 SiO2 - 4 Al2O3 - 4 Li2O - 0 Na2O - 2 K2O (mol %) slag (New) 45 CaO - 45 SiO2 - 4 Al2O3 - 0 Li2O - 2 Na2O - 4 K2O (mol %) slag (New) 45 CaO - 45 SiO2 - 4 Al2O3 - 0 Li2O - 4 Na2O - 2 K2O (mol %) slag (New) 45 CaO - 45 SiO2 - 4 Al2O3 - 2 Li2O - 2 Na2O - 2 K2O (mol %) slag (New)
43 CaO - 43 SiO2 - 8 Al2O3 - 0 Li2O - 0 Na2O - 6 K2O (mol %) slag (New) 45 CaO - 45 SiO2 - 4 Al2O3 - 0 Li2O - 6 Na2O (mol %) slag (New) 45 CaO - 45 SiO2 - 4 Al2O3 - 2 Li2O - 4 Na2O (mol %) slag (New) 43 CaO - 43 SiO2 - 8 Al2O3 - 0 Li2O - 6 Na2O (mol %) slag (New) 45 CaO - 45 SiO2 - 4 Al2O3 - 4 Li2O - 2 Na2O (mol %) slag (New)
43 CaO - 43 SiO2 - 8 Al2O3 - 2 Li2O - 4 Na2O (mol %) slag (New) 43 CaO - 43 SiO2 - 8 Al2O3 - 4 Li2O - 2 Na2O (mol %) slag (New) 45 CaO - 45 SiO2 - 4 Al2O3 - 6 Li2O (mol %) slag (New) 43 CaO - 43 SiO2 - 8 Al2O3 - 6 Li2O (mol %) slag (New) 23.8 CaO - 55.2 SiO2 - 13 Al2O3 - 3 MgO - 5 Cr2O3 (wt %) slag (New)
30.2 CaO - 48.8 SiO2 - 13 Al2O3 - 3 MgO - 5 Cr2O3 (wt %) slag (New) 37.4 CaO - 41.6 SiO2 - 13 Al2O3 - 3 MgO - 5 Cr2O3 (wt %) slag (New) 38.4 CaO - 42.6 SiO2 - 13 Al2O3 - 3 MgO - 3 Cr2O3 (wt %) slag (New) 39.3 CaO - 43.7 SiO2 - 13 Al2O3 - 3 MgO - 1 Cr2O3 (wt %) slag (New) 39.8 CaO - 44.2 SiO2 - 13 Al2O3 - 3 MgO - 0 Cr2O3 (wt %) slag (New)
41.0 CaO - 38.0 SiO2 - 13 Al2O3 - 3 MgO - 5 Cr2O3 (wt %) slag (New) 41.3 CaO - 37.0 SiO2 - 6.0 Al2O3 - 3.0 MgO - 5.8 F - 6.4 Na2O - 0.5 Li2O (wt %) slag (New) 35.6 CaO - 42.8 SiO2 - 5.9 Al2O3 - 3.0 MgO - 5.8 F - 6.4 Na2O - 0.5 Li2O (wt %) slag (New) 37.1 CaO - 41.0 SiO2 - 6.0 Al2O3 - 3.0 MgO - 5.9 F - 6.4 Na2O - 0.5 Li2O (wt %) slag (New) 39.9 CaO - 38.5 SiO2 - 5.9 Al2O3 - 3.0 MgO - 5.8 F - 6.4 Na2O - 0.5 Li2O (wt %) slag (New)
27.5 CaO - 23.7 SiO2 - 14.4 Al2O3 - 7.7 MgO - 22.5 FetO - 4.4 P2O5 (wt %) slag (New) 25.1 CaO - 21.4 SiO2 - 14.3 Al2O3 - 7.6 MgO - 22.4 FetO - 9.2 P2O5 (wt %) slag (New) 32.6 CaO - 28.2 SiO2 - 14.4 Al2O3 - 7.7 MgO - 12.9 FetO - 4.2 P2O5 (wt %) slag (New) 37.3 CaO - 31.9 SiO2 - 14.3 Al2O3 - 7.7 MgO - 4.6 FetO - 4.2 P2O5 (wt %) slag (New) 28.4 CaO - 24.3 SiO2 - 14.2 Al2O3 - 7.5 MgO - 22.8 FetO - 2.7 P2O5 (wt %) slag (New)
30.0 CaO - 25.5 SiO2 - 14.3 Al2O3 - 7.6 MgO - 22.6 FetO (wt %) slag (New) 39.5 CaO - 34.1 SiO2 - 14.3 Al2O3 - 7.8 MgO - 4.4 P2O5 (wt %) slag (New) 24.6 CaO - 20.5 SiO2 - 13 Al2O3 - 8 MgO - 25 TiO2 - 9 FeO (wt %) slag (New) 21.8 CaO - 18.2 SiO2 - 13 Al2O3 - 8 MgO - 30 TiO2 - 9 FeO (wt %) slag (New) 32.7 CaO - 27.3 SiO2 - 13 Al2O3 - 8 MgO - 10 TiO2 - 9 FeO (wt %) slag (New)
30.0 CaO - 25.0 SiO2 - 13 Al2O3 - 8 MgO - 15 TiO2 - 9 FeO (wt %) slag (New) 27.3 CaO - 22.7 SiO2 - 13 Al2O3 - 8 MgO - 20 TiO2 - 9 FeO (wt %) slag (New) 40.0 CaO - 20 SiO2 - 30 Al2O3 - 5 MgO - 5 TiO2 (wt %) slag (New) 53.3 CaO - 6.7 SiO2 - 30 Al2O3 - 5 MgO - 5 TiO2 (wt %) slag (New) 54.6 CaO - 5.5 SiO2 - 30 Al2O3 - 5 MgO - 5 TiO2 (wt %) slag (New)
34 CaO - 40 SiO2 - 16 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New) 32 CaO - 40 SiO2 - 18 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New) 30 CaO - 40 SiO2 - 20 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New) 28 CaO - 40 SiO2 - 22 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New) 26 CaO - 40 SiO2 - 24 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)
24 CaO - 40 SiO2 - 26 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New) 22 CaO - 40 SiO2 - 28 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New) 20 CaO - 40 SiO2 - 30 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New) 33.6 CaO - 40.4 SiO2 - 16 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New) 32.7 CaO - 39.3 SiO2 - 18 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)
31.8 CaO - 38.2 SiO2 - 20 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New) 30.9 CaO - 37.1 SiO2 - 22 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New) 30 CaO - 36 SiO2 - 24 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New) 29.1 CaO - 34.9 SiO2 - 26 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New) 28.2 CaO - 33.8 SiO2 - 28 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)
54.0 CaO - 9.0 SiO2 - 30 Al2O3 - 5 MgO - 2 TiO2 (wt %) slag (New) 51.4 CaO - 8.6 SiO2 - 30 Al2O3 - 5 MgO - 5 TiO2 (wt %) slag (New) 49.7 CaO - 8.3 SiO2 - 30 Al2O3 - 5 MgO - 7 TiO2 (wt %) slag (New) 47.1 CaO - 7.9 SiO2 - 30 Al2O3 - 5 MgO - 10 TiO2 (wt %) slag (New) 34 CaO - 34 SiO2 - 17 Al2O3 - 15 MgO (wt %) slag (New)
32 CaO - 32 SiO2 - 16 Al2O3 - 20 MgO (wt %) slag (New) 38 CaO - 38 SiO2 - 19 Al2O3 - 5 MgO (wt %) slag (New) 36 CaO - 36 SiO2 - 18 Al2O3 - 10 MgO (wt %) slag (New) 55.7 CaO - 9.3 SiO2 - 30 Al2O3 - 5 MgO (wt %) slag (New) 41.4 CaO - 41.8 SiO2 - 10.7 Al2O3 - 5.7 MoO3 (wt %) slag (New)
43.6 CaO - 43.6 SiO2 - 11.0 Al2O3 - 1.7 MoO3 (wt %) slag (New) 42.5 CaO - 42.7 SiO2 - 10.8 Al2O3 - 3.9 MoO3 (wt %) slag (New) 22.2 CaO - 23.8 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 8 Na2O - 4 BaO - 3 MgO - 8 Li2O (wt %) (New) 25.1 CaO - 26.9 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 8 Na2O - 4 BaO - 3 MgO - 2 Li2O (wt %) (New) 24.1 CaO - 25.9 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 8 Na2O - 4 BaO - 3 MgO - 4 Li2O (wt %) (New)
23.1 CaO - 24.9 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 8 Na2O - 4 BaO - 3 MgO - 6 Li2O (wt %) (New) 27.0 CaO - 29.0 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 6 Na2O - 4 BaO - 3 MgO (wt %) (New) 25.0 CaO - 27.0 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 10 Na2O - 4 BaO - 3 MgO (wt %) (New) 26.0 CaO - 28.0 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 8 Na2O - 4 BaO - 3 MgO (wt %) (New) 28.9 CaO - 31.1 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 2 Na2O - 4 BaO - 3 MgO (wt %) (New)
27.9 CaO - 30.1 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 4 Na2O - 4 BaO - 3 MgO (wt %) (New) 32 CaO - 32 SiO2 - 16 Al2O3 - 20 TiO2 (wt %) slag (New) 36 CaO - 36 SiO2 - 18 Al2O3 - 10 TiO2 (wt %) slag (New) 46 CaO - 46 SiO2 - 8 Al2O3 (mol %) slag (New) 48 CaO - 48 SiO2 - 4 Al2O3 (mol %) slag (New)
26 CaO - 42 SiO2 - 18 CaF2 - 14 Na2O (wt %) slag (New) 31 CaO - 38 SiO2 - 18 CaF2 - 13 Na2O (wt %) slag (New) 33 CaO - 33 SiO2 - 19 CaF2 - 15 Na2O (wt %) slag (New) 37 CaO - 32 SiO2 - 18 CaF2 - 13 Na2O (wt %) slag (New) 13.4 CaO - 10 SiO2 - 76.6 Fe2O3 (wt %) slag (New)
12.7 CaO - 15 SiO2 - 72.3 Fe2O3 (wt %) slag (New) 23.5 CaO - 10 SiO2 - 66.5 Fe2O3 (wt %) slag (New) 22.2 CaO - 15 SiO2 - 62.8 Fe2O3 (wt %) slag (New) 14.2 CaO - 5 SiO2 - 80.8 Fe2O3 (wt %) slag (New) 22.9 CaO - 37.3 SiO2 - 4.9 MgO - 20.1 Al2O3 - 14.8 MnO (wt %) slag (New)
19.3 CaO - 30.4 SiO2 - 4.8 MgO - 19.1 Al2O3 - 26.4 MnO (wt %) slag (New) 15.2 CaO - 25.6 SiO2 - 4.4 MgO - 20.7 Al2O3 - 34.1 MnO (wt %) slag (New) 12.1 CaO - 21.4 SiO2 - 4.5 MgO - 17.0 Al2O3 - 45.0 MnO (wt %) slag (New) 7.2 CaO - 12.9 SiO2 - 5.1 MgO - 20.2 Al2O3 - 54.6 MnO (wt %) slag (New) 37.5 CaO - 38.1 SiO2 - 5.0 MgO - 19.4 Al2O3 - 0.0 MnO (wt %) slag (New)
35.6 CaO - 35.1 SiO2 - 5.0 MgO - 19.2 Al2O3 - 5.1 MnO (wt %) slag (New) 30.4 CaO - 30.6 SiO2 - 4.5 MgO - 20.3 Al2O3 - 14.2 MnO (wt %) slag (New) 25.6 CaO - 27.0 SiO2 - 4.6 MgO - 19.2 Al2O3 - 23.6 MnO (wt %) slag (New) 19.8 CaO - 20.4 SiO2 - 5.1 MgO - 19.8 Al2O3 - 34.9 MnO (wt %) slag (New) 15.5 CaO - 14.9 SiO2 - 4.8 MgO - 19.2 Al2O3 - 45.6 MnO (wt %) slag (New)
10.6 CaO - 10.9 SiO2 - 4.4 MgO - 19.9 Al2O3 - 54.2 MnO (wt %) slag (New) 45.4 CaO - 29.8 SiO2 - 5.3 MgO - 19.5 Al2O3 - 0.0 MnO (wt %) slag (New) 42.0 CaO - 28.1 SiO2 - 4.5 MgO - 20.5 Al2O3 - 4.9 MnO (wt %) slag (New) 35.3 CaO - 24.5 SiO2 - 4.8 MgO - 20.6 Al2O3 - 14.8 MnO (wt %) slag (New) 30.3 CaO - 20.4 SiO2 - 5.1 MgO - 20.1 Al2O3 - 24.1 MnO (wt %) slag (New)
23.8 CaO - 16.4 SiO2 - 5.0 MgO - 20.6 Al2O3 - 34.2 MnO (wt %) slag (New) 18.3 CaO - 12.4 SiO2 - 4.7 MgO - 20.3 Al2O3 - 44.3 MnO (wt %) slag (New) 28.3 CaO - 47.5 SiO2 - 4.7 MgO - 19.5 Al2O3 - 0.0 MnO (wt %) slag (New) 26.8 CaO - 43.5 SiO2 - 5.1 MgO - 19.3 Al2O3 - 5.3 MnO (wt %) slag (New) 29.2 CaO - 25.5 SiO2 - 7.3 MgO - 14.0 Al2O3 - 22.0 TiO2 - 2.0 CaCl2 (wt %) slag (New)
28.9 CaO - 25.2 SiO2 - 7.2 MgO - 13.9 Al2O3 - 21.8 TiO2 - 3.0 CaCl2 (wt %) slag (New) 28.0 CaO - 24.4 SiO2 - 7.0 MgO - 13.5 Al2O3 - 21.1 TiO2 - 6.0 CaCl2 (wt %) slag (New) 26.8 CaO - 23.4 SiO2 - 6.7 MgO - 12.9 Al2O3 - 20.2 TiO2 - 10.0 CaCl2 (wt %) slag (New) 29.8 CaO - 26.0 SiO2 - 7.4 MgO - 14.3 Al2O3 - 22.5 TiO2 - 0.0 CaCl2 (wt %) slag (New) 29.5 CaO - 25.7 SiO2 - 7.3 MgO - 14.2 Al2O3 - 22.2 TiO2 - 1.0 CaCl2 (wt %) slag (New)
47.7 CaO - 40.5 SiO2 - 1.8 MgO - 10 CaF2 (wt %) slag (New) 51.9 CaO - 44.1 SiO2 - 2 MgO - 2 CaF2 (wt %) slag (New) 49.8 CaO - 42.3 SiO2 - 1.9 MgO - 6 CaF2 (wt %) slag (New) 51.4 CaO - 43.7 SiO2 - 1.9 MgO - 3 KOH (wt %) slag (New) 51.4 CaO - 43.7 SiO2 - 1.9 MgO - 3 Li2O (wt %) slag (New)
51 CaO - 43 SiO2 - 6 MgO (wt %) slag (New) 51.7 CaO - 46.8 SiO2 - 1.5 MgO (wt %) slag (New) 53 CaO - 45 SiO2 - 2 MgO (wt %) slag (New) 15 CaO - 30 SiO2 - 40.9 MnO - 14.1 CaF2 (wt %) slag (New) 28 CaO - 56.1 SiO2 - 11.1 MnO - 4.8 CaF2 (wt %) slag (New)
26.6 CaO - 53.1 SiO2 - 10.7 MnO - 9.6 CaF2 (wt %) slag (New) 25.1 CaO - 50.2 SiO2 - 10.2 MnO - 14.5 CaF2 (wt %) slag (New) 18.4 CaO - 36.8 SiO2 - 40.1 MnO - 4.7 CaF2 (wt %) slag (New) 16.3 CaO - 32.6 SiO2 - 41.7 MnO - 9.4 CaF2 (wt %) slag (New) 47.5 CaO - 47.5 SiO2 - 5 MnO (mol %) slag (New)
45 CaO - 45 SiO2 - 10 MnO (mol %) slag (New) 40 CaO - 40 SiO2 - 20 MnO (mol %) slag (New) 35 CaO - 35 SiO2 - 30 MnO (mol %) slag (New) 30.3 CaO - 60.5 SiO2 - 9.2 MnO (wt %) slag (New) 20.5 CaO - 41.1 SiO2 - 38.4 MnO (wt %) slag (New)
55.8 CaO - 44.2 SiO2 (mol %) slag (New) 37.7 CaO - 62.3 SiO2 (mol %) slag (New) 48.3 CaO - 51.7 SiO2 (mol %) slag (New) CaO CaSiO3
Ca1-xTmxF2+x (New) Cd - 50 Pb (at %) (New) Cd - 64.5 Pb (at %) (New) Cd - 71.9 Pb (at %) (New) Cd - 75 Pb (at %) (New)
Cd - 90 Pb (at %) (New) Cd - 2.8 Pb (at %) (New) Cd - 10 Pb (at %) (New) Cd - 25 Pb (at %) (New) Cd - 35.2 Pb (at %) (New)
Cd - 85 Sn (at %) (New) Cd - 11 Sn (at %) (New) Cd - 25 Sn (at %) (New) Cd - 50 Sn (at %) (New) Cd - 66.5 Sn (at %) (New)
Cd - 3.3 Tl (at %) (New) Cd - 6.6 Tl (at %) (New) CdTe Chromel CM 186 LC (Revised)
CMSX-10 (Revised) Co - 20 Cu (at %) (New) Co - 40 Cu (at %) (New) Co - 20 Fe (at %) (New) Co - 40 Fe (at %) (New)
Co - 20 Ni (at %) (New) Co - 40 Ni (at %) (New) Cobalt Corn oil Corning 7740 (Pyrex) (Revised)
Cr - 40 Fe (wt %) (New) Cr - 43 Ni (wt %) (New) Cu - 4 Ag (wt %) Cu - 6 Ag (wt %) Cu - 7 Ag (wt %)
Cu - 8 Ag (wt %) Cu - 90 Ce (at %) (New) Cu - 80 Ce (at %) (New) Cu - 71 Ce (at %) (New) Cu - 61 Ce (at %) (New)
Cu - 50 Ce (at %) (New) Cu - 41 Ce (at %) (New) Cu - 30 Ce (at %) (New) Cu - 20 Ce (at %) (New) Cu - 20 Co (at %) (New)
Cu - 20 Fe (at %) (New) Cu - 40 Fe (at %) (New) Cu - 20 Ni (wt %) Cu - 40 Ni (wt %) CuAl9Mn2 (New)
CuAsSe2 (New) CuGe2P3 CuSbS2 (New) CuSbSe2 (Cd doped) (New) Cu3SbSe4
CuSbTe2 (Revised) Dy(Fe1-xAlx)2 (New) E glass fiber Fe - 0.5 Au (at %) (New) Fe - 20 Co (at %) (New)
Fe - 30 Co (at %) (New) Fe - 40 Co (at %) (New) Fe - 50 Co (at %) (New) Fe - 8 Co (at %) (New) Fe - 40 Cr (at %) (New)
Fe - 10 Cr (at %) (New) Fe - 20 Cr (at %) (New) Fe - 40 Cu (at %) (New) Fe - 1.67 Cu (at %) (New) Fe - 20 Cu (at %) (New)
Fe - 3 Ir (at %) (New) Fe - 10 Mn - 1.6 C (wt %) (New) Fe - 10 Mn - 4.1 C (wt %) (New) Fe - 5 Mn - 1.5 C (wt %) (New) Fe - 5 Mn - 4.2 C (wt %) (New)
Fe - 3 Mn (at %) (New) Fe - 10 Mn (wt %) Fe - 3 Mn (wt %) Fe - 5 Mn (wt %) Fe - 6 Ni - 0.2 C (wt %) (New)
Fe - 3 Ni (wt %) Fe - 5 Ni (wt %) Fe - 10 Ni (wt %) Fe - 20 Ni (wt %) Fe - 30 Ni (wt %)
Fe - 40 Ni (wt %) Fe - 0.5 Ni (wt %) Fe - 1 Ni (wt %) Fe - 34 Ni (wt %) (New) Fe - 3 Pt (at %) (New)
Fe - 5 Pt (at %) (New) Fe - 10 Pt (at %) (New) Fe - 3 Re (at %) (New) Fe - 6 Re (at %) (New) Fe - 3 Rh (at %) (New)
Fe - 6 Rh (at %) (New) Fe - 8 Rh (at %) (New) Fe - 6 Ru (at %) (New) Fe - 9 Ru (at %) (New) Fe65Cu20Ni15 (New)
Fe48Cu20Ni32 (New) 29.6 FeO - 36.9 CaO - 33.5 SiO2 (mol %) slag (New) 27 FeO - 26.5 CaO - 46.5 SiO2 (mol %) slag (New) 26 FeO - 38 CaO - 36 SiO2 (mol %) slag (New) 25 FeO - 51 CaO - 24 SiO2 (mol %) slag (New)
62.3 FeO - 4.5 CaO - 33.2 SiO2 (mol %) slag (New) 62.2 FeO - 5.2 CaO - 32.6 SiO2 (mol %) slag (New) 57.4 FeO - 9.3 CaO - 33.3 SiO2 (mol %) slag (New) 51.5 FeO - 13.5 CaO - 35 SiO2 (mol %) slag (New) 46 FeO - 9.6 CaO - 44.4 SiO2 (mol %) slag (New)
39 FeO - 28.5 CaO - 32.5 SiO2 (mol %) slag (New) 37.1 FeO - 18.2 CaO - 44.7 SiO2 (mol %) slag (New) 65.1 FeO - 5.2 Fe2O3 - 29.7 CaO (mol %) (New) 57.3 FeO - 5.6 Fe2O3 - 37.1 CaO (mol %) (New) 90.7 FeO - 4.1 Fe2O3 - 5.2 CaO (mol %) (New)
85.7 FeO - 4.3 Fe2O3 - 10 CaO (mol %) (New) 80.1 FeO - 4.5 Fe2O3 - 15.4 CaO (mol %) (New) 74.4 FeO - 4.8 Fe2O3 - 20.8 CaO (mol %) (New) 69.9 FeO - 5 Fe2O3 - 25.1 CaO (mol %) (New) 35.6 FeO - 20.2 Fe2O3 - 34.22 SiO2 - 10 Al2O3 (wt %) slag (New)
35.7 FeO - 17 Fe2O3 - 32.32 SiO2 - 15 Al2O3 (wt %) slag (New) 42.1 FeO - 26.3 Fe2O3 - 26.6 SiO2 - 5 Al2O3 (wt %) slag (New) 39.6 FeO - 25.2 Fe2O3 - 25.2 SiO2 - 10 Al2O3 (wt %) slag (New) 35.5 FeO - 29.2 Fe2O3 - 30.35 SiO2 - 5 Al2O3 (wt %) slag (New) 35.7 FeO - 25.6 Fe2O3 - 28.75 SiO2 - 10 Al2O3 (wt %) slag (New)
31.8 FeO - 27.1 Fe2O3 - 36.12 SiO2 - 5 Al2O3 (wt %) slag (New) 42.6 FeO - 29.4 Fe2O3 - 28 SiO2 (wt %) slag (New) 41.4 FeO - 26.6 Fe2O3 - 32 SiO2 (wt %) slag (New) 44.2 FeO - 17.8 Fe2O3 - 38 SiO2 (wt %) slag (New) 96.2 FeO - 3.8 Fe2O3 (mol %) (New)
49.46 FeO - 40.54 SiO2 - 10 Al2O3 (wt %) slag (New) 46.71 FeO - 38.29 SiO2 - 15 Al2O3 (wt %) slag (New) 43.96 FeO - 36.04 SiO2 - 20 Al2O3 (wt %) slag (New) 52.21 FeO - 42.79 SiO2 - 5 Al2O3 (wt %) slag (New) 61 FeO - 29 SiO2 - 6 Fe2O3 - 2.5 Al2O3 (wt %) slag (New)
59 FeO - 29 SiO2 - 8 Fe2O3 - 2.6 Al2O3 (wt %) slag (New) 63 FeO - 29 SiO2 - 4.6 Fe2O3 - 2.6 Al2O3 (wt %) slag (New) 64 FeO - 29 SiO2 - 4 Fe2O3 - 2.5 Al2O3 (wt %) slag (New) 56.6 FeO - 43.4 SiO2 (mol %) slag (New) 66 FeO - 34 SiO2 (mol %) slag (New)
Fe2VAl (Si, Sn, Ta, Ti, & W doped) GaFeO3 (Sm doped) (New) Ge26InxSe74-x glass (New) Ge20Sb10Se70 glass (New) Ge15Sb15Se70 glass (New)
Ge10Sb20Se70 glass (New) Ge5Sb25Se70 glass (New) H13 HfC In - 3 Ag (wt %)
In - 19 Ag (wt %) (New) In - 40.5 Ag (wt %) (New) In - 53 Ag (wt %) (New) In - 63.6 Ag (wt %) (New) In - 79 Ag (wt %) (New)
In - 48.1 Sn (at %) In - 55 Sn (at %) In - 75 Sn (at %) In - 83 Sn (at %) In - 14.7 Sn (at %)
In - 21.3 Sn (at %) In - 25.3 Sn (at %) In - 30.24 Sn (at %) In - 36 Sn (at %) In - 42 Sn (at %)
In - 42.5 Sn (at %) In - 47.22 Sn (at %) In - 70 Sn (at %) (New) In - 50 Sn (at %) (New) In - 10 Sn (at %) (New)
In - 90 Sn (at %) (New) IN-100 Inconel 625 Iron (Revised) K - 43.5 Na (wt%) (New)
K2Ba3(P2O7)2 (New) 71.8 KF - 23.9 AlF3 - 4.2 Al2O3 (wt %) electrolyte (New) 71.4 KF - 28.6 AlF3 - 0.0 Al2O3 (wt %) electrolyte (New) 70.9 KF - 28.4 AlF3 - 0.7 Al2O3 (wt %) electrolyte (New) 70.4 KF - 28.1 AlF3 - 1.5 Al2O3 (wt %) electrolyte (New)
69.2 KF - 27.7 AlF3 - 3.1 Al2O3 (wt %) electrolyte (New) 66.7 KF - 33.3 AlF3 - 0.0 Al2O3 (wt %) electrolyte (New) 65.5 KF - 32.8 AlF3 - 1.7 Al2O3 (wt %) electrolyte (New) 64.3 KF - 32.1 AlF3 - 3.6 Al2O3 (wt %) electrolyte (New) 64.0 KF - 32.0 AlF3 - 4.0 Al2O3 (wt %) electrolyte (New)
60.0 KF - 40.0 AlF3 - 0.0 Al2O3 (wt %) electrolyte (New) 59.0 KF - 39.3 AlF3 - 1.6 Al2O3 (wt %) electrolyte (New) 58.8 KF - 39.2 AlF3 - 2.1 Al2O3 (wt %) electrolyte (New) 58.0 KF - 38.7 AlF3 - 3.4 Al2O3 (wt %) electrolyte (New) 75.0 KF - 25.0 AlF3 - 0.0 Al2O3 (wt %) electrolyte (New)
74.0 KF - 24.7 AlF3 - 1.3 Al2O3 (wt %) electrolyte (New) 73.0 KF - 24.3 AlF3 - 2.7 Al2O3 (wt %) electrolyte (New) 68.8 KF - 22.9 AlF3 - 8.2 AlPO4 (wt %) electrolyte (New) 71.4 KF - 28.6 AlF3 - 0.0 AlPO4 (wt %) electrolyte (New) 69.6 KF - 27.8 AlF3 - 2.6 AlPO4 (wt %) electrolyte (New)
67.4 KF - 27.0 AlF3 - 5.6 AlPO4 (wt %) electrolyte (New) 64.8 KF - 25.9 AlF3 - 9.3 AlPO4 (wt %) electrolyte (New) 66.7 KF - 33.3 AlF3 - 0.0 AlPO4 (wt %) electrolyte (New) 65.7 KF - 32.9 AlF3 - 1.4 AlPO4 (wt %) electrolyte (New) 64.7 KF - 32.3 AlF3 - 3.0 AlPO4 (wt %) electrolyte (New)
63.5 KF - 31.8 AlF3 - 4.7 AlPO4 (wt %) electrolyte (New) 62.3 KF - 31.2 AlF3 - 6.5 AlPO4 (wt %) electrolyte (New) 72.3 KF - 27.7 AlF3 - 0.0 AlPO4 (wt %) electrolyte (New) 71.4 KF - 27.4 AlF3 - 1.2 AlPO4 (wt %) electrolyte (New) 71.0 KF - 27.2 AlF3 - 1.8 AlPO4 (wt %) electrolyte (New)
69.4 KF - 26.6 AlF3 - 3.9 AlPO4 (wt %) electrolyte (New) 75.0 KF - 25.0 AlF3 - 0.0 AlPO4 (wt %) electrolyte (New) 73.3 KF - 24.4 AlF3 - 2.3 AlPO4 (wt %) electrolyte (New) 71.3 KF - 23.8 AlF3 - 5.0 AlPO4 (wt %) electrolyte (New) 304L
316L LaAl2 (Revised) Lead (Revised) 85 LiF - 15 Li2S (mol %) (New) 316LN
Magnesium Manganese MAR-M200 Maraging 350 (C-type) Mg - 2.9 Gd (wt %) (New)
Mg - 1.8 Gd (wt %) (New) Mg - 2 Y (wt %) (New) Mg - 1.1 Y (wt %) (New) 34.5 MnO - 34.5 SiO2 - 6.0 MgO - 25.0 Al2O3 (wt %) flux (New) 47.0 MnO - 47.0 SiO2 - 6.0 MgO - 0.0 Al2O3 (wt %) flux (New)
44.5 MnO - 44.5 SiO2 - 6.0 MgO - 5.0 Al2O3 (wt %) flux (New) 42.0 MnO - 42.0 SiO2 - 6.0 MgO - 10.0 Al2O3 (wt %) flux (New) 39.5 MnO - 39.5 SiO2 - 6.0 MgO - 15.0 Al2O3 (wt %) flux (New) 37.0 MnO - 37.0 SiO2 - 6.0 MgO - 20.0 Al2O3 (wt %) flux (New) Na - 44 K (wt%) (New)
Ni - 20 Co (at %) (New) Ni - 40 Co (at %) (New) Ni - 20 Cr (at %) (New) Ni - 40 Cr (at %) (New) Ni - 10 Cr (at %) (New)
Ni - 40 Cu (wt %) Ni - 20 Cu (wt %) Ni - 20 Fe (wt %) Ni - 40 Fe (wt %) Ni - 34 S (at %) (New)
Ni-Ti (Nitinol) Ni45Cu20Fe35 (New) Ni70Cu20Fe10 (New) Ni60Cu20Fe20 (New) Ni3Zr2P3 (New)
Olive oil Pb - 40 In (at %) (New) Pb - 60 In (at %) (New) Pb - 80 In (at %) (New) Pb - 20 In (at %) (New)
Pb - 50 In (wt %) Pb - 13 Sb (wt %) (New) 80.75 PbCl2 - 4.25 PbS - 15 PbO (mol %) (New) 93.1 PbCl2 - 4.9 PbS - 2 PbO (mol %) (New) 90.25 PbCl2 - 4.75 PbS - 5 PbO (mol %) (New)
85.5 PbCl2 - 4.5 PbS - 10 PbO (mol %) (New) 33.3 PbO - 66.7 B2O3 (mol %) (New) 27 PbO - 73 B2O3 (mol %) (New) 42 PbO - 58 B2O3 (mol %) (New) 80 PbO - 20 SiO2 (wt %)
81.34 PbO - 18.66 SiO2 (wt %) (New) 82.54 PbO - 17.46 SiO2 (wt %) (New) 83.68 PbO - 16.32 SiO2 (wt %) (New) 84.6 PbO - 15.4 SiO2 (wt %) (New) 85.31 PbO - 14.69 SiO2 (wt %) (New)
85.84 PbO - 14.16 SiO2 (wt %) (New) 86.35 PbO - 13.65 SiO2 (wt %) (New) 86.85 PbO - 13.15 SiO2 (wt %) (New) 87.34 PbO - 12.66 SiO2 (wt %) (New) 87.82 PbO - 12.18 SiO2 (wt %) (New)
88.14 PbO - 11.86 SiO2 (wt %) (New) 88.75 PbO - 11.25 SiO2 (wt %) (New) 89.21 PbO - 10.79 SiO2 (wt %) (New) 91.78 PbO - 8.22 SiO2 (wt %) (New) 79.58 PbO - 20.42 SiO2 (wt %) (New)
PMMA (Revised) 48 P2O5 - 16 Na2O - 14.4 CaO - 1.6 Al2O3 - 20 CoO (wt %) (New) 60 P2O5 - 20 Na2O - 18 CaO - 2 Al2O3 (wt %) (New) Pyroceram 9608 Pyroceram 9606 (Revised)
Rene 95 Rene 80 (Revised) Rhenium Rice bran (New) S-2 glass fiber
SbCl3 Schott N-BK7 (Revised) SiC (alpha) (Revised) 30 SiO2 - 20 Al2O3 - 26 CaO - 2 MgO - 8 Na2O - 6 F2 - 8 MnO (wt %) (New) 21 SiO2 - 8 Al2O3 - 35 CaO - 5 MgO - 6 Na2O - 2 K2O - 14 F2 - 4 FeO - 5 B2O3 (wt %) (New)
17 SiO2 - 26 Al2O3 - 28 CaO - 4 MgO - 5 Na2O - 2 K2O - 11 F2 - 3 FeO - 4 B2O3 (wt %) (New) 30 SiO2 - 11 Al2O3 - 30 CaO - 12 Na2O - 4 F2 - 1 FeO - 12 MnO (wt %) (New) 23 SiO2 - 32 Al2O3 - 23 CaO - 9 Na2O - 3 F2 - 10 MnO (wt %) (New) 39 SiO2 - 11 Al2O3 - 25 CaO - 14 Na2O - 1 K2O - 5 F2 - 4 FeO - 1 B2O3 (wt %) (New) 35 SiO2 - 19 Al2O3 - 23 CaO - 13 Na2O - 1 K2O - 5 F2 - 3 FeO - 1 B2O3 (wt %) (New)
32 SiO2 - 26 Al2O3 - 21 CaO - 12 Na2O - 1 K2O - 4 F2 - 3 FeO - 1 B2O3 (wt %) (New) 37 SiO2 - 9 Al2O3 - 32 CaO - 5 Na2O - 2 K2O - 8.5 F2 - 3 FeO - 3.5 B2O3 (wt %) (New) 34 SiO2 - 14 Al2O3 - 31 CaO - 5 Na2O - 2 K2O - 8 F2 - 3 FeO - 3 B2O3 (wt %) (New) 32 SiO2 - 19 Al2O3 - 29 CaO - 4 Na2O - 2 K2O - 8 F2 - 3 FeO - 3 B2O3 (wt %) (New) 30 SiO2 - 26 Al2O3 - 26 CaO - 4 Na2O - 1 K2O - 7 F2 - 3 FeO - 3 B2O3 (wt %) (New)
28 SiO2 - 32 Al2O3 - 24 CaO - 4 Na2O - 1 K2O - 6 F2 - 2 FeO - 3 B2O3 (wt %) (New) 41 SiO2 - 5 Al2O3 - 26 CaO - 15 Na2O - 1 K2O - 6 F2 - 4 FeO - 2 B2O3 (wt %) (New) 30 SiO2 - 21 Al2O3- 28 CaO - 1 MgO - 6 Na2O - 12 F2 - 1 FeO - 1 MnO (wt %) (New) 39.2 SiO2 - 39.6 CaO - 21.2 Al2O3 (wt %) slag (New) 72.7 SiO2 - 8.9 CaO - 18.4 Al2O3 (wt %) slag (New)
59.1 SiO2 - 15.1 CaO - 25.8 Al2O3 (wt %) slag (New) 68.2 SiO2 - 21.2 CaO - 10.6 Al2O3 (wt %) slag (New) 63.1 SiO2 - 21.1 CaO - 15.8 Al2O3 (wt %) slag (New) 58.4 SiO2 - 20.7 CaO - 20.9 Al2O3 (wt %) slag (New) 53.4 SiO2 - 20.5 CaO - 26.1 Al2O3 (wt %) slag (New)
59.4 SiO2 - 24.6 CaO - 16.0 Al2O3 (wt %) slag (New) 35.8 SiO2 - 24.1 CaO - 40.1 Al2O3 (wt %) slag (New) 64.7 SiO2 - 29.6 CaO - 5.7 Al2O3 (wt %) slag (New) 59.9 SiO2 - 29.3 CaO - 10.8 Al2O3 (wt %) slag (New) 54.8 SiO2 - 28.9 CaO - 16.3 Al2O3 (wt %) slag (New)
49.9 SiO2 - 29.4 CaO - 20.7 Al2O3 (wt %) slag (New) 45.2 SiO2 - 29.2 CaO - 25.6 Al2O3 (wt %) slag (New) 58.8 SiO2 - 34.8 CaO - 6.4 Al2O3 (wt %) slag (New) 48.6 SiO2 - 41.0 CaO - 10.4 Al2O3 (wt %) slag (New) 43.7 SiO2 - 40.7 CaO - 15.6 Al2O3 (wt %) slag (New)
38 SiO2 - 35 CaO - 1 MgO - 7 Na2O - 15 F2 - 1 FeO - 2 MnO (wt %) (New) 37 SiO2 - 33 CaO - 2 MgO - 10 Na2O - 7 F2 - 11 MnO (wt %) (New) 43 SiO2 - 28 CaO - 16 Na2O - 1 K2O - 6 F2 - 4 FeO - 2 B2O3 (wt %) (New) 42.3 SiO2 - 23.1 CaO - 34.6 Na2O (mol %) slag (New) 77.1 SiO2 - 9.1 CaO - 13.6 Na2O (mol %) slag (New)
69.4 SiO2 - 18.4 CaO - 12.2 Na2O (mol %) slag (New) 58.3 SiO2 - 16.7 CaO - 25 Na2O (mol %) slag (New) 49.4 SiO2 - 10.1 CaO - 40.5 Na2O (mol %) slag (New) 61 SiO2 - 39 CaO (mol %) slag (New) 25 SiO2 - 29 FeO - 15 ZnO - 12 CaO - 6 MgO - 5 CaS - 4 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New)
25 SiO2 - 30 FeO - 16 ZnO - 8 CaO - 8 MgO - 5 CaS - 4 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New) 25 SiO2 - 29 FeO - 12 ZnO - 12 CaO - 9 MgO - 5 CaS - 4 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New) 24 SiO2 - 28 FeO - 24 ZnO - 7 CaO - 5 MgO - 4 CaS - 4 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New) 24 SiO2 - 28 FeO - 11 ZnO - 20 CaO - 5 MgO - 4 CaS - 4 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New) 37 SiO2 - 28 FeO - 11 ZnO - 7 CaO - 5 MgO - 4 CaS - 4 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New)
31 SiO2 - 28 FeO - 11 ZnO - 7 CaO - 5 MgO - 4 CaS - 10 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New) 25 SiO2 - 29 FeO - 12 ZnO - 8 CaO - 5 MgO - 5 CaS - 12 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New) 27 SiO2 - 32 FeO - 13 ZnO - 8 CaO - 6 MgO - 5 CaS - 4 Al2O3 - 3 Fe2O3 - 2 PbO (wt %) (New) 73 SiO2 - 12 K2O - 6 Na2O - 5 CaO - 4 MgO (wt %) (New) 67 SiO2 - 12 K2O - 8 ZrO2 - 6 Na2O - 4 TiO2 - 1 CaO - 1 Al2O3 - 1 MgO (wt %) (New)
67 SiO2 - 12 K2O - 8 ZrO2 - 6 Na2O - 4 ZnO - 1 CaO - 1 Al2O3 - 1 MgO (wt %) (New) 47 SiO2 - 8 MgO - 17 CaO - 14 Al2O3 - 4 K2O - 1.1 Na2O - 4.5 Fe - 1.4 Cr2O3 (wt %) (New) 47 SiO2 - 8 MgO - 18 CaO - 14 Al2O3 - 4 K2O - 1.1 Na2O - 5 Fe - 0.9 Cr2O3 (wt %) (New) 40 SiO2 - 8 MgO - 14 CaO - 11 Al2O3 - 3.2 K2O - 1.3 Na2O - 4 Fe - 15 Cu (wt %) (New) 46 SiO2 - 9 MgO - 15 CaO - 12 Al2O3 - 4 K2O - 1.5 Na2O - 5 Fe - 3.6 Cu (wt %) (New)
45 SiO2 - 9 MgO - 15 CaO - 11 Al2O3 - 3.6 K2O - 1.4 Na2O - 5 Fe - 6 Cu (wt %) (New) 43 SiO2 - 8 MgO - 15 CaO - 11 Al2O3 - 3.5 K2O - 1.4 Na2O - 5 Fe - 9 Cu (wt %) (New) 49 SiO2 - 8 MgO - 16 CaO - 14 Al2O3 - 4 K2O - 1 Na2O - 4.5 Fe (wt %) (New) 52 SiO2 - 8 MgO - 16 CaO - 13 Al2O3 - 3 K2O - 1 Na2O - 3.8 Fe (wt %) (New) 55 SiO2 - 7 MgO - 14 CaO - 13 Al2O3 - 3.3 K2O - 0.8 Na2O - 4 Fe (wt %) (New)
30 SiO2 - 8 MgO - 42 CaO - 9 Al2O3 - 2.3 K2O - 1 Na2O - 3.8 Fe (wt %) (New) 41 SiO2 - 19 MgO - 16 CaO - 11 Al2O3 - 3.2 K2O - 1.2 Na2O - 5 Fe (wt %) (New) 48 SiO2 - 8 MgO - 16 CaO - 12 Al2O3 - 4 K2O - 1.5 Na2O - 5.6 Fe (wt %) (New) 43 SiO2 - 12 MgO - 21 CaO - 12 Al2O3 - 3 K2O - 1.3 Na2O - 5 Fe (wt %) (New) 40 SiO2 - 10 MgO - 25 CaO - 13 Al2O3 - 3 K2O - 1.2 Na2O - 4.7 Fe (wt %) (New)
36 SiO2 - 9 MgO - 32 CaO - 12 Al2O3 - 3 K2O - 1 Na2O - 4.5 Fe (wt %) (New) 44 SiO2 - 7.6 MgO - 15 CaO - 10 Al2O3 - 3.5 K2O - 1.4 Na2O - 12 Fe2O3 - 12 Fe (wt %) (New) 41 SiO2 - 7.2 MgO - 14 CaO - 9 Al2O3 - 3 K2O - 1.3 Na2O - 20 Fe2O3 - 16 Fe (wt %) (New) 46 SiO2 - 8 MgO - 16 CaO - 11 Al2O3 - 4 K2O - 1.1 Na2O - 6 Fe2O3 - 9 Fe (wt %) (New) 59 SiO2 - 35 Na2O - 6 Al2O3 (mol %)
60 SiO2 - 20 Na2O - 20 Al2O3 (mol %) (New) 50 SiO2 - 25 Na2O - 25 Al2O3 (mol %) (New) 75 SiO2 - 12.5 Na2O - 12.5 Al2O3 (mol %) (New) 60 SiO2 - 28 Na2O - 12 Al2O3 (mol %) (New) 60 SiO2 - 26.7 Na2O - 13.3 Al2O3 (mol %) (New)
70 SiO2 - 25 Na2O - 3 CaO - 1 Al2O3 - 1 TiO2 (wt %) (New) 65 SiO2 - 25 Na2O - 5 ZnO - 3 CaO - 1 Al2O3 - 1 TiO2 (wt %) (New) 60 SiO2 - 25 Na2O - 10 ZnO - 3 CaO - 1 Al2O3 - 1 TiO2 (wt %) (New) 55 SiO2 - 25 Na2O - 15 ZnO - 3 CaO - 1 Al2O3 - 1 TiO2 (wt %) (New) 55 SiO2 - 45 Na2O (mol %) slag (New)
70 SiO2 - 30 Na2O (mol %) slag (New) 60 SiO2 - 40 Na2O (mol %) (New) Sn - 30.6 Bi (wt %) (New) 63 Sn - 37 Pb (wt %) 70 Sn - 30 Pb (wt %)
10 Sn - 90 Pb (wt %) 20 Sn - 80 Pb (wt %) 25 Sn - 75 Pb (wt %) 60 Sn - 40 Pb (wt %) 36 Sn - 64 Pb (wt %) (New)
48 Sn - 52 Pb (wt %) (New) 52 Sn - 48 Pb (wt %) (New) 74 Sn - 26 Pb (wt %) (New) 88 Sn - 12 Pb (wt %) (New) 5 Sn - 95 Pb (wt %) (Revised)
Sn - 62 Zn (wt %) (New) Sn - 83 Zn (wt %) (New) Sn - 5 Zn (wt %) (New) Sn - 8 Zn (wt %) (New) Sn - 35 Zn (wt %) (New)
Sn - 9 Zn (wt %) (Revised) Soderberg electrode paste (New) Soybean oil Sunflower oil Ta - 8 W - 2 Hf (wt %) (T-111)
Ta - 10 W (wt %) (Revised) Tantalum Tellurium (Revised) Thallium (Revised) Ti - 6 Al - 2 Sn - 4 Zr - 2 Mo (wt %)
Ti - 6 Al - 4 V (Grade 5) Ti - 6 Al - 4 V Ti - 6 Al - 4 Zr - 4 Nb (wt %) (New) Ti3Al (Revised) TiC
86 TiO2 - 6 FeO - 0.0 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New) 72.1 TiO2 - 6 FeO - 13.9 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New) 69.6 TiO2 - 9 FeO - 13.4 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New) 67.1 TiO2 - 12 FeO - 12.9 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New) 64.6 TiO2 - 15 FeO - 12.4 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)
75.0 TiO2 - 9.5 FeO - 7.5 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New) 67.3 TiO2 - 9.6 FeO - 15.1 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New) 59.4 TiO2 - 9.7 FeO - 22.9 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New) 51.4 TiO2 - 9.8 FeO - 30.8 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New) 77 TiO2 - 15 FeO - 0.0 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)
80 TiO2 - 12 FeO - 0.0 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New) 83 TiO2 - 9 FeO - 0.0 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New) 81 Tl - 17 Cd - 2 Bi (wt %) (New) 13 Tl - 26 Cd - 61 Bi (wt %) (New) 44 Tl - 11 Cd - 45 Bi (wt %) (New)
TRIP 9 Cr - 8 Ni - 4 Mo - 3 Mn - 3 Si (wt %) (New) Tritan FX200 (New) Tritan HX100 (New) Tritan MP100 (New) Tritan MX711
Udimet 500 UNS C11000 (ETP) (Revised) UNS C43000 UNS C43400 UNS C43500
UNS C44300 UNS C46500 UNS C46600 UNS C46700 UNS C48200
UNS C48500 UNS C50500 UNS C52100 UNS C52400 UNS C60600
UNS C60800 UNS C61000 UNS C61300 UNS C61800 UNS C61900
UNS C62300 UNS C62400 UNS C62500 UNS C63000 UNS C63600
UNS C63800 UNS C64200 UNS C64400 UNS C64700 UNS C65100
UNS C66700 UNS C67400 UNS C67500 UNS C69000 UNS C69400
UNS C70400 UNS C72200 UNS C72800 UNS C72900 UNS C74500
UNS C75700 UNS C76390 UNS C78200 UNS C95200 UNS C95300
UNS C95500 UNS C10800 UNS C11100 UNS C12000 UNS C12100
UNS C12500 UNS C12700 UNS C12800 UNS C12900 UNS C13000
UNS C14300 UNS C14310 UNS C14700 UNS C14710 UNS C14720
UNS C15000 UNS C15500 UNS C15715 UNS C15720 UNS C15760
UNS C16500 UNS C17200 UNS C18090 UNS C18150 UNS C18700
UNS C19000 UNS C19200 UNS C19220 UNS C19280 UNS C22000
UNS C26000 UNS C26100 UNS C26130 UNS C26200 UNS C27200
UNS C27400 UNS C31600 UNS C32000 UNS C33000 UNS C33100
UNS C33200 UNS C33500 UNS C34000 UNS C34200 UNS C35000
UNS C35600 UNS C36200 UNS C36500 UNS C36600 UNS C36700
UNS C36800 UNS C37000 UNS C37100 UNS C38500 UNS C40800
UNS C41100 UNS C41300 UNS C41500 UNS C63020 (New) UNS C76300 (New)
UNS C24000 (Revised) UNS C61400 (Revised) UNS C10400 (Revised) UNS C10500 (Revised) UNS C12200 (Revised)
UNS C14200 (Revised) UNS C36000 (Revised) UNS C46400 (Revised) UNS C26800 (Revised) UNS C63200 (Revised)
UNS C10700 (Revised) UNS C95800 (Revised) UNS C11400 (Revised) UNS C28000 (Revised) UNS C31400 (Revised)
UNS C14500 (Revised) UNS C51000 (Revised) UNS C65500 (Revised) UNS C14510 (Revised) UNS C37700 (Revised)
UNS C54400 (Revised) UNS C68700 (Revised) UNS C21000 (Revised) UNS C14520 (Revised) UNS C23000 (Revised)
V - H (beta) (New) Vespel TP-8395 (Revised) Vespel TP-8549 (Revised) Vespel TP-8792 (Revised) Vespel TP-8054 (Revised)
Vespel TP-8130 (Revised) Vespel TP-8212 (Revised) Vespel TP-8311 (Revised) W - 20 Ta - 12 Mo (wt %) WC - 13 Co (wt %)
WC - 15 Co (wt %) WC - 8 Co (wt %) (New) WC - 10 Co (wt %) (New) WC - 20 Co (wt %) (New) WC - 3 Co (wt %) (Revised)
WC - 25 Co (wt %) (Revised) WC - 9 Co (wt %) (Revised) WC - 5 Co (wt %) (Revised) WC - 11 Co (wt %) (Revised) WC - 12 Co (wt %) (Revised)
WC - 6 Co (wt %) (Revised) WC - 7 Co (wt %) (Revised) WSe2 Y3Fe5O12 (YIG) Zinc
Zircaloy-2 Zirconium Zn - 0.16 Pb (at %) (New) Zn - 0.52 Pb (at %) (New) ZnTe
ZrC Zr2Ni (New) Zytel 101 Zytel 70G30HSL Zytel ST801

97% sunflower - 3% Olive oil (New)

    SH        :    liquid  ||  16974|9|1|-1

return to listing



70% sunflower - 30% Olive oil (New)

    SH        :    liquid  ||  16975|9|1|-1

return to listing



304

    FEN    (N):    annealed  ||  tested at 21 °C (70 °F), R = -1, axial, 0.004/s strain rate, elastic strain range  ||  1250|14|2|3
    FEN    (N):    annealed  ||  tested at 430 °C (806 °F), R = -1, axial, 0.004/s strain rate, elastic strain range  ||  1250|14|2|4
    FEN    (N):    annealed  ||  tested at 649 °C (1200 °F), R = -1, axial, 0.004/s strain rate, elastic strain range  ||  1250|14|2|5
    FEN    (N):    annealed  ||  tested at 649 °C (1200 °F), R = -1, axial, 4 x 10-5/s strain rate, elastic strain range  ||  1250|14|2|6
    FEN    (N):    annealed  ||  tested at 816 °C (1500 °F), R = -1, axial, 0.004/s strain rate, elastic strain range  ||  1250|14|2|7
    FEN    (N):    annealed  ||  tested at 816 °C (1500 °F), R = -1, axial, 4 x 10-5/s strain rate, elastic strain range  ||  1250|14|2|8
    VP     (N):    liquid  ||  1250|18|1|-1

return to listing



430

    DLL    (N):    liquid  ||  1005|0|1|-1
    MTE    (N):    liquid  ||  1005|8|1|-1
    CTE    (N):    liquid  ||  1005|16|1|-1
    D      (N):    liquid  ||  1005|24|1|-1

return to listing



7055 (New)

    SSCC      :    0.001/s  ||  tested at 250 °C (482 °F)  ||  16364|12|0|0
    SSCC      :    0.001/s  ||  tested at 300 °C (572 °F)  ||  16364|12|0|1
    SSCC      :    0.001/s  ||  tested at 350 °C (662 °F)  ||  16364|12|0|2
    SSCC      :    0.001/s  ||  tested at 400 °C (752 °F)  ||  16364|12|0|3
    SSCC      :    0.001/s  ||  tested at 450 °C (842 °F)  ||  16364|12|0|4
    SSCC      :    0.01/s  ||  tested at 250 °C (482 °F)  ||  16364|12|1|0
    SSCC      :    0.01/s  ||  tested at 300 °C (572 °F)  ||  16364|12|1|1
    SSCC      :    0.01/s  ||  tested at 350 °C (662 °F)  ||  16364|12|1|2
    SSCC      :    0.01/s  ||  tested at 400 °C (752 °F)  ||  16364|12|1|3
    SSCC      :    0.01/s  ||  tested at 450 °C (842 °F)  ||  16364|12|1|4
    SSCC      :    0.1/s  ||  tested at 250 °C (482 °F)  ||  16364|12|2|0
    SSCC      :    0.1/s  ||  tested at 300 °C (572 °F)  ||  16364|12|2|1
    SSCC      :    0.1/s  ||  tested at 350 °C (662 °F)  ||  16364|12|2|2
    SSCC      :    0.1/s  ||  tested at 400 °C (752 °F)  ||  16364|12|2|3
    SSCC      :    0.1/s  ||  tested at 450 °C (842 °F)  ||  16364|12|2|4
    SSCC      :    1/s  ||  tested at 250 °C (482 °F)  ||  16364|12|3|0
    SSCC      :    1/s  ||  tested at 300 °C (572 °F)  ||  16364|12|3|1
    SSCC      :    1/s  ||  tested at 350 °C (662 °F)  ||  16364|12|3|2
    SSCC      :    1/s  ||  tested at 400 °C (752 °F)  ||  16364|12|3|3
    SSCC      :    1/s  ||  tested at 450 °C (842 °F)  ||  16364|12|3|4
    D     (*):    solid  ||  16364|24|0|-1

return to listing



316

    FEN    (R):    annealed  ||  tested at 600 °C (1112 °F), R = -1, total strain range  ||  1259|14|0|1
    FEN    (N):    annealed  ||  tested at 593 °C (1100 °F), R = -1, total strain range  ||  1259|14|0|2
    FEN    (N):    annealed  ||  tested at 593 °C (1100 °F), R = -1, plastic strain range  ||  1259|14|0|3
    FEN    (N):    annealed  ||  tested at 593 °C (1100 °F), R = -1, elastic strain range  ||  1259|14|0|4
    FEN    (N):    solution annealed, aged 5040 h at 593 °C (1100 °F)  ||  tested at 593 °C (1100 °F), R = -1, total strain range  ||  1259|14|2|0
    FEN    (N):    solution annealed, aged 5040 h at 593 °C (1100 °F)  ||  tested at 593 °C (1100 °F), R = -1, plastic strain range  ||  1259|14|2|1
    FEN    (N):    solution annealed, aged 5040 h at 593 °C (1100 °F)  ||  tested at 593 °C (1100 °F), R = -1, elastic strain range  ||  1259|14|2|2
    FEN    (N):    solution annealed at 1050 °C (1922 °F)  ||  tested at 600 °C (1112 °F), R = -1, axial, 6.7 x 10-3/s, total strain range  ||  1259|14|3|0
    FEN    (N):    solution annealed at 1050 °C (1922 °F)  ||  tested at 600 °C (1112 °F), R = -1, axial, 6.7 x 10-5/s, total strain range  ||  1259|14|3|1
    FEN    (N):    solution annealed at 1050 °C (1922 °F)  ||  tested at 700 °C (1292 °F), R = -1, axial, 6.7 x 10-3/s, total strain range  ||  1259|14|3|2
    FEN    (N):    solution annealed at 1050 °C (1922 °F)  ||  tested at 700 °C (1292 °F), R = -1, axial, 6.7 x 10-5/s, total strain range  ||  1259|14|3|3
    VP     (N):    liquid  ||  1259|18|1|-1
    SR     (N):    annealed at 1050 °C (1922 °F)  ||  tested at 704 °C (1300 °F)  ||  1259|22|0|5
    SR     (R):    annealed at 1050 °C (1922 °F)  ||  Master curve (LMP)  ||  1259|22|0|6

return to listing



A357

    YSC    (N):    semi-solid  ||  grain refined  ||  120|21|1|0
    YSC    (N):    semi-solid  ||  magnetohydrodynamically stirred  ||  120|21|1|1

return to listing



7A85

    FSN    (N):    T7452 temper  ||  tested at 24 °C (75 °F) in air, R = -1, axial, maximum stress  ||  3142|6|0|0
    FSN    (N):    T7452 temper  ||  tested at 24 °C (75 °F) in 3.5% NaCl, R = -1, axial, maximum stress  ||  3142|6|0|1

return to listing



A356.0

    FSN    (N):    T6 temper  ||  tested at 20 °C (68 °F), R = -1, axial, coarse grain, stress amplitude  ||  119|6|1|0
    FSN    (N):    T6 temper  ||  tested at 20 °C (68 °F), R = -1, axial, fine grain, stress amplitude  ||  119|6|1|1
    FSN    (N):    T6 temper  ||  tested at 20 °C (68 °F), R = -1, axial, coarse grain, HIPed, stress amplitude  ||  119|6|1|2
    FSN    (N):    T6 temper  ||  tested at 20 °C (68 °F), R = -1, axial, fine grain, HIPed, stress amplitude  ||  119|6|1|3
    YSC    (N):    semi-solid  ||  grain refined  ||  119|21|1|0
    YSC    (N):    semi-solid  ||  magnetohydrodynamically stirred  ||  119|21|1|1
    YSC    (N):    semi-solid  ||  rheocast  ||  119|21|1|2

return to listing



Ag - 42 Te (at %) (New)

    TC        :    liquid  ||  16553|1|1|-1

return to listing



Ag2S

    TC     (N):    liquid  ||  3582|1|1|-1
    TD     (N):    liquid  ||  3582|25|1|-1

return to listing



Ag2Te

    TC     (N):    liquid  ||  3558|1|1|-1

return to listing



Al - 10 Cu (wt %)

    Vis    (N):    liquid  ||  15357|26|1|-1

return to listing



Al - 15 Cu (wt %)

    Vis    (N):    liquid  ||  15356|26|1|-1

return to listing



Al - 25 Cu (wt %)

    Vis    (N):    liquid  ||  15355|26|1|-1

return to listing



Al - 0.5 Cu (wt %)

    Vis    (N):    liquid  ||  15354|26|1|-1

return to listing



Al - 1 Cu (wt %)

    Vis    (N):    liquid  ||  15360|26|1|-1

return to listing



Al - 1.5 Cu (wt %)

    Vis    (N):    liquid  ||  8928|26|1|-1

return to listing



Al - 3 Cu (wt %)

    Vis    (N):    liquid  ||  15359|26|1|-1

return to listing



Al - 5 Cu (wt %)

    Vis    (N):    liquid  ||  15358|26|1|-1

return to listing



Al - 22.5 Cu (wt %) (New)

    DLL       :    liquid  ||  16376|0|1|-1
    MTE       :    liquid  ||  16376|8|1|-1
    CTE       :    liquid  ||  16376|16|1|-1
    D         :    liquid  ||  16376|24|1|-1
    Vis       :    liquid  ||  16376|26|1|-1
    ST        :    liquid  ||  16376|38|1|-1

return to listing



Al - 33 Cu (wt %)

    DLL    (R):    liquid  ||  9502|0|1|-1
    MTE    (R):    liquid  ||  9502|8|1|-1
    CTE    (R):    liquid  ||  9502|16|1|-1
    D      (R):    liquid  ||  9502|24|1|-1

return to listing



Al - 21 Cu (wt %)

    DLL    (R):    liquid  ||  9503|0|1|-1
    MTE    (R):    liquid  ||  9503|8|1|-1
    CTE    (R):    liquid  ||  9503|16|1|-1
    D      (R):    liquid  ||  9503|24|1|-1

return to listing



Al - 7 Si (wt %)

    DLL    (N):    liquid  ||  9043|0|1|-1
    MTE    (N):    liquid  ||  9043|8|1|-1
    CTE    (N):    liquid  ||  9043|16|1|-1
    D      (N):    liquid  ||  9043|24|1|-1
    Vis    (N):    liquid  ||  9043|26|1|-1

return to listing



Al - 1 Si (wt %) (New)

    DLL       :    liquid  ||  16731|0|1|-1
    MTE       :    liquid  ||  16731|8|1|-1
    CTE       :    liquid  ||  16731|16|1|-1
    D         :    liquid  ||  16731|24|1|-1
    Vis       :    liquid  ||  16731|26|1|-1

return to listing



Al - 8 Si (wt %) (New)

    DLL       :    liquid  ||  16737|0|1|-1
    MTE       :    liquid  ||  16737|8|1|-1
    CTE       :    liquid  ||  16737|16|1|-1
    D         :    liquid  ||  16737|24|1|-1
    Vis       :    liquid  ||  16737|26|1|-1

return to listing



Al - 9 Si (wt %) (New)

    DLL       :    liquid  ||  16738|0|1|-1
    MTE       :    liquid  ||  16738|8|1|-1
    CTE       :    liquid  ||  16738|16|1|-1
    D         :    liquid  ||  16738|24|1|-1
    Vis       :    liquid  ||  16738|26|1|-1

return to listing



Al - 10 Si (wt %) (New)

    DLL       :    liquid  ||  16739|0|1|-1
    MTE       :    liquid  ||  16739|8|1|-1
    CTE       :    liquid  ||  16739|16|1|-1
    D         :    liquid  ||  16739|24|1|-1
    Vis       :    liquid  ||  16739|26|1|-1

return to listing



Al - 11 Si (wt %) (New)

    DLL       :    liquid  ||  16740|0|1|-1
    MTE       :    liquid  ||  16740|8|1|-1
    CTE       :    liquid  ||  16740|16|1|-1
    D         :    liquid  ||  16740|24|1|-1
    Vis       :    liquid  ||  16740|26|1|-1

return to listing



Al - 11.5 Si (wt %) (New)

    DLL       :    liquid  ||  16352|0|1|-1
    E         :    solid  ||  16352|3|0|-1
    MTE       :    liquid  ||  16352|8|1|-1
    CTE       :    liquid  ||  16352|16|1|-1
    D     (*):    solid  ||  16352|24|0|-1
    D         :    liquid  ||  16352|24|1|-1
    Vis       :    liquid  ||  16352|26|1|-1

return to listing



Al - 12 Si (wt %) (New)

    DLL       :    liquid  ||  16741|0|1|-1
    MTE       :    liquid  ||  16741|8|1|-1
    CTE       :    liquid  ||  16741|16|1|-1
    D         :    liquid  ||  16741|24|1|-1
    Vis       :    liquid  ||  16741|26|1|-1

return to listing



Al - 12.6 Si (wt %) (New)

    DLL       :    liquid  ||  16742|0|1|-1
    MTE       :    liquid  ||  16742|8|1|-1
    CTE       :    liquid  ||  16742|16|1|-1
    D         :    liquid  ||  16742|24|1|-1
    Vis       :    liquid  ||  16742|26|1|-1

return to listing



Al - 2 Si (wt %) (New)

    DLL       :    liquid  ||  16732|0|1|-1
    MTE       :    liquid  ||  16732|8|1|-1
    CTE       :    liquid  ||  16732|16|1|-1
    D         :    liquid  ||  16732|24|1|-1
    Vis       :    liquid  ||  16732|26|1|-1

return to listing



Al - 3 Si (wt %) (New)

    DLL       :    liquid  ||  16733|0|1|-1
    MTE       :    liquid  ||  16733|8|1|-1
    CTE       :    liquid  ||  16733|16|1|-1
    D         :    liquid  ||  16733|24|1|-1
    Vis       :    liquid  ||  16733|26|1|-1

return to listing



Al - 4 Si (wt %) (New)

    DLL       :    liquid  ||  16734|0|1|-1
    MTE       :    liquid  ||  16734|8|1|-1
    CTE       :    liquid  ||  16734|16|1|-1
    D         :    liquid  ||  16734|24|1|-1
    Vis       :    liquid  ||  16734|26|1|-1

return to listing



Al - 5 Si (wt %) (New)

    DLL       :    liquid  ||  16735|0|1|-1
    MTE       :    liquid  ||  16735|8|1|-1
    CTE       :    liquid  ||  16735|16|1|-1
    D         :    liquid  ||  16735|24|1|-1
    Vis       :    liquid  ||  16735|26|1|-1

return to listing



Al - 6 Si (wt %) (New)

    DLL       :    liquid  ||  16736|0|1|-1
    MTE       :    liquid  ||  16736|8|1|-1
    CTE       :    liquid  ||  16736|16|1|-1
    D         :    liquid  ||  16736|24|1|-1
    Vis       :    liquid  ||  16736|26|1|-1

return to listing



3.8 Al2O3 - 55.67 SiO2 - 35.53 CaO - 5 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16709|26|1|-1

return to listing



9.9 Al2O3 - 54.35 SiO2 - 34.75 CaO - 1 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16711|26|1|-1

return to listing



9.7 Al2O3 - 53.25 SiO2 - 34.05 CaO - 3 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16712|26|1|-1

return to listing



9.5 Al2O3 - 52.16 SiO2 - 33.35 CaO - 5 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16713|26|1|-1

return to listing



1.98 Al2O3 - 59.2 SiO2 - 37.82 CaO - 1 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16703|26|1|-1

return to listing



1.94 Al2O3 - 58.01 SiO2 - 37.05 CaO - 3 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16704|26|1|-1

return to listing



1.9 Al2O3 - 56.81 SiO2 - 36.29 CaO - 5 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16705|26|1|-1

return to listing



3.96 Al2O3 - 58.01 SiO2 - 37.03 CaO - 1 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16707|26|1|-1

return to listing



3.88 Al2O3 - 56.84 SiO2 - 36.28 CaO - 3 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16708|26|1|-1

return to listing



34 Al2O3 - 18 SiO2 - 39 CaO - 9 MgO (mol %) slag (New)

    TC        :    liquid  ||  16728|1|1|-1

return to listing



34 Al2O3 - 14 SiO2 - 45 CaO - 7 MgO (mol %) slag (New)

    TC        :    liquid  ||  16729|1|1|-1

return to listing



43 Al2O3 - 9 SiO2 - 43 CaO - 5 MgO (mol %) slag (New)

    TC        :    liquid  ||  16730|1|1|-1

return to listing



25.7 Al2O3 - 58.4 SiO2 - 10.7 CaO - 61.6 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16665|2|1|-1
    SIGMA     :    liquid  ||  16665|10|1|-1

return to listing



29 Al2O3 - 60 SiO2 - 11.6 CaO - 57.1 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16666|2|1|-1
    SIGMA     :    liquid  ||  16666|10|1|-1

return to listing



29.7 Al2O3 - 65.2 SiO2 - 28.5 CaO - 39.5 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16667|2|1|-1
    SIGMA     :    liquid  ||  16667|10|1|-1

return to listing



31.8 Al2O3 - 64.6 SiO2 - 23.3 CaO - 42.4 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16668|2|1|-1
    SIGMA     :    liquid  ||  16668|10|1|-1

return to listing



32.2 Al2O3 - 62.9 SiO2 - 12.8 CaO - 42.9 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16669|2|1|-1
    SIGMA     :    liquid  ||  16669|10|1|-1

return to listing



32.4 Al2O3 - 61.7 SiO2 - 12.9 CaO - 52.2 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16670|2|1|-1
    SIGMA     :    liquid  ||  16670|10|1|-1

return to listing



33.4 Al2O3 - 63.1 SiO2 - 13.3 CaO - 44.6 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16671|2|1|-1
    SIGMA     :    liquid  ||  16671|10|1|-1

return to listing



33.7 Al2O3 - 64.1 SiO2 - 18.8 CaO - 44.9 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16672|2|1|-1
    SIGMA     :    liquid  ||  16672|10|1|-1

return to listing



34.4 Al2O3 - 63.3 SiO2 - 13.9 CaO - 45.8 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16673|2|1|-1
    SIGMA     :    liquid  ||  16673|10|1|-1

return to listing



35.6 Al2O3 - 63.5 SiO2 - 14.2 CaO - 47.4 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16674|2|1|-1
    SIGMA     :    liquid  ||  16674|10|1|-1

return to listing



36.2 Al2O3 - 65.3 SiO2 - 16 CaO - 37.4 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16675|2|1|-1
    SIGMA     :    liquid  ||  16675|10|1|-1

return to listing



39 Al2O3 - 64.8 SiO2 - 13.5 CaO - 44.9 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16676|2|1|-1
    SIGMA     :    liquid  ||  16676|10|1|-1

return to listing



39.3 Al2O3 - 64.6 SiO2 - 8.8 CaO - 40.6 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16677|2|1|-1
    SIGMA     :    liquid  ||  16677|10|1|-1

return to listing



42.2 Al2O3 - 66.1 SiO2 - 12.8 CaO - 42.5 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16678|2|1|-1
    SIGMA     :    liquid  ||  16678|10|1|-1

return to listing



46.4 Al2O3 - 67.8 SiO2 - 11.8 CaO - 39.5 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16679|2|1|-1
    SIGMA     :    liquid  ||  16679|10|1|-1

return to listing



20 Al2O3 - 38 SiO2 - 38 CaO - 4 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16660|2|1|-1
    SIGMA     :    liquid  ||  16660|10|1|-1

return to listing



20 Al2O3 - 36 SiO2 - 36 CaO - 8 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16661|2|1|-1
    SIGMA     :    liquid  ||  16661|10|1|-1

return to listing



26 Al2O3 - 35 SiO2 - 35 CaO - 4 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16663|2|1|-1
    SIGMA     :    liquid  ||  16663|10|1|-1

return to listing



26 Al2O3 - 33 SiO2 - 33 CaO - 8 MgO (mol %) slag (New)

    RHO       :    liquid  ||  16664|2|1|-1
    SIGMA     :    liquid  ||  16664|10|1|-1

return to listing



32 Al2O3 - 20 SiO2 - 38 CaO - 9 MgO (mol %) slag (New)

    TC        :    liquid  ||  16727|1|1|-1

return to listing



2 Al2O3 - 59.8 SiO2 - 38.2 CaO (mol %) slag (New)

    Vis       :    liquid  ||  16702|26|1|-1

return to listing



26 Al2O3 - 37 SiO2 - 37 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16662|2|1|-1
    SIGMA     :    liquid  ||  16662|10|1|-1

return to listing



10 Al2O3 - 54.9 SiO2 - 35.1 CaO (mol %) slag (New)

    Vis       :    liquid  ||  16710|26|1|-1

return to listing



8 Al2O3 - 58 SiO2 - 34 CaO (mol %) slag (New)

    TC        :    liquid  ||  16714|1|1|-1
    SH    (*):    solid  ||  16714|9|0|-1
    D     (*):    solid  ||  16714|24|0|-1

return to listing



13.1 Al2O3 - 55.4 SiO2 - 31.5 CaO (mol %) slag (New)

    TC        :    liquid  ||  16715|1|1|-1
    SH    (*):    solid  ||  16715|9|0|-1
    D     (*):    solid  ||  16715|24|0|-1

return to listing



10.1 Al2O3 - 48.5 SiO2 - 41.5 CaO (mol %) slag (New)

    TC        :    liquid  ||  16716|1|1|-1
    SH    (*):    solid  ||  16716|9|0|-1
    D     (*):    solid  ||  16716|24|0|-1

return to listing



16 Al2O3 - 45 SiO2 - 39 CaO (mol %) slag (New)

    TC        :    liquid  ||  16717|1|1|-1
    SH    (*):    solid  ||  16717|9|0|-1
    D     (*):    solid  ||  16717|24|0|-1

return to listing



21 Al2O3 - 43 SiO2 - 36 CaO (mol %) slag (New)

    TC        :    liquid  ||  16718|1|1|-1
    SH    (*):    solid  ||  16718|9|0|-1
    D     (*):    solid  ||  16718|24|0|-1

return to listing



11.5 Al2O3 - 48.8 SiO2 - 39.7 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16642|2|1|-1
    SIGMA     :    liquid  ||  16642|10|1|-1

return to listing



11.8 Al2O3 - 48.6 SiO2 - 39.6 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16643|2|1|-1
    SIGMA     :    liquid  ||  16643|10|1|-1

return to listing



12 Al2O3 - 42.8 SiO2 - 45.2 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16644|2|1|-1
    SIGMA     :    liquid  ||  16644|10|1|-1

return to listing



12 Al2O3 - 46.4 SiO2 - 41.6 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16645|2|1|-1
    SIGMA     :    liquid  ||  16645|10|1|-1

return to listing



12.3 Al2O3 - 31.5 SiO2 - 56.2 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16646|2|1|-1
    SIGMA     :    liquid  ||  16646|10|1|-1

return to listing



12.4 Al2O3 - 36.9 SiO2 - 50.8 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16647|2|1|-1
    SIGMA     :    liquid  ||  16647|10|1|-1

return to listing



12.4 Al2O3 - 42.3 SiO2 - 45.3 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16648|2|1|-1
    SIGMA     :    liquid  ||  16648|10|1|-1

return to listing



12.5 Al2O3 - 44.5 SiO2 - 43.1 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16649|2|1|-1
    SIGMA     :    liquid  ||  16649|10|1|-1

return to listing



12.5 Al2O3 - 47.7 SiO2 - 39.8 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16650|2|1|-1
    SIGMA     :    liquid  ||  16650|10|1|-1

return to listing



12.5 Al2O3 - 53.2 SiO2 - 34.2 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16651|2|1|-1
    SIGMA     :    liquid  ||  16651|10|1|-1

return to listing



13.8 Al2O3 - 40.5 SiO2 - 45.7 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16652|2|1|-1
    SIGMA     :    liquid  ||  16652|10|1|-1

return to listing



13.8 Al2O3 - 44.9 SiO2 - 41.2 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16653|2|1|-1
    SIGMA     :    liquid  ||  16653|10|1|-1

return to listing



13.9 Al2O3 - 49.3 SiO2 - 36.8 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16654|2|1|-1
    SIGMA     :    liquid  ||  16654|10|1|-1

return to listing



16.6 Al2O3 - 42.4 SiO2 - 41.1 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16655|2|1|-1
    SIGMA     :    liquid  ||  16655|10|1|-1

return to listing



19.4 Al2O3 - 40.9 SiO2 - 39.7 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16656|2|1|-1
    SIGMA     :    liquid  ||  16656|10|1|-1

return to listing



2.9 Al2O3 - 44.3 SiO2 - 52.8 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16614|2|1|-1
    SIGMA     :    liquid  ||  16614|10|1|-1

return to listing



2.9 Al2O3 - 49.4 SiO2 - 47.7 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16615|2|1|-1
    SIGMA     :    liquid  ||  16615|10|1|-1

return to listing



2.9 Al2O3 - 54.6 SiO2 - 42.5 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16616|2|1|-1
    SIGMA     :    liquid  ||  16616|10|1|-1
    Vis       :    liquid  ||  16616|26|1|-1

return to listing



2.9 Al2O3 - 59.7 SiO2 - 37.3 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16617|2|1|-1
    SIGMA     :    liquid  ||  16617|10|1|-1

return to listing



3.5 Al2O3 - 48.6 SiO2 - 47.9 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16618|2|1|-1
    SIGMA     :    liquid  ||  16618|10|1|-1

return to listing



4.7 Al2O3 - 47 SiO2 - 48.3 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16619|2|1|-1
    SIGMA     :    liquid  ||  16619|10|1|-1

return to listing



5.3 Al2O3 - 46.2 SiO2 - 48.5 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16620|2|1|-1
    SIGMA     :    liquid  ||  16620|10|1|-1

return to listing



5.9 Al2O3 - 40.2 SiO2 - 53.9 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16621|2|1|-1
    SIGMA     :    liquid  ||  16621|10|1|-1

return to listing



5.9 Al2O3 - 45.4 SiO2 - 48.7 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16622|2|1|-1
    SIGMA     :    liquid  ||  16622|10|1|-1
    Vis       :    liquid  ||  16622|26|1|-1

return to listing



6 Al2O3 - 50.6 SiO2 - 43.4 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16623|2|1|-1
    SIGMA     :    liquid  ||  16623|10|1|-1

return to listing



6 Al2O3 - 55.9 SiO2 - 38.1 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16624|2|1|-1
    SIGMA     :    liquid  ||  16624|10|1|-1

return to listing



6.8 Al2O3 - 45.7 SiO2 - 47.5 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16625|2|1|-1
    SIGMA     :    liquid  ||  16625|10|1|-1

return to listing



6.8 Al2O3 - 46.8 SiO2 - 46.4 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16626|2|1|-1
    SIGMA     :    liquid  ||  16626|10|1|-1

return to listing



6.8 Al2O3 - 47.8 SiO2 - 45.4 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16627|2|1|-1
    SIGMA     :    liquid  ||  16627|10|1|-1

return to listing



7.8 Al2O3 - 42.9 SiO2 - 49.3 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16628|2|1|-1
    SIGMA     :    liquid  ||  16628|10|1|-1

return to listing



7.8 Al2O3 - 48.2 SiO2 - 44 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16629|2|1|-1
    SIGMA     :    liquid  ||  16629|10|1|-1

return to listing



8.5 Al2O3 - 47.4 SiO2 - 44.1 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16630|2|1|-1
    SIGMA     :    liquid  ||  16630|10|1|-1

return to listing



9.1 Al2O3 - 35.9 SiO2 - 55 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16631|2|1|-1
    SIGMA     :    liquid  ||  16631|10|1|-1

return to listing



9.1 Al2O3 - 41.2 SiO2 - 49.7 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16632|2|1|-1
    SIGMA     :    liquid  ||  16632|10|1|-1

return to listing



9.1 Al2O3 - 46.5 SiO2 - 44.3 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16633|2|1|-1
    SIGMA     :    liquid  ||  16633|10|1|-1

return to listing



9.2 Al2O3 - 51.9 SiO2 - 38.9 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16634|2|1|-1
    SIGMA     :    liquid  ||  16634|10|1|-1

return to listing



9.5 Al2O3 - 57.6 SiO2 - 32.9 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16635|2|1|-1
    SIGMA     :    liquid  ||  16635|10|1|-1

return to listing



10.4 Al2O3 - 39.5 SiO2 - 50.1 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16636|2|1|-1
    SIGMA     :    liquid  ||  16636|10|1|-1

return to listing



10.6 Al2O3 - 52.5 SiO2 - 36.9 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16637|2|1|-1
    SIGMA     :    liquid  ||  16637|10|1|-1

return to listing



10.8 Al2O3 - 38.7 SiO2 - 50.6 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16638|2|1|-1
    SIGMA     :    liquid  ||  16638|10|1|-1

return to listing



11.1 Al2O3 - 49.4 SiO2 - 39.4 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16639|2|1|-1
    SIGMA     :    liquid  ||  16639|10|1|-1

return to listing



11.2 Al2O3 - 39.9 SiO2 - 48.9 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16640|2|1|-1
    SIGMA     :    liquid  ||  16640|10|1|-1

return to listing



11.5 Al2O3 - 41.3 SiO2 - 47.1 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16641|2|1|-1
    SIGMA     :    liquid  ||  16641|10|1|-1

return to listing



22.1 Al2O3 - 39.5 SiO2 - 38.4 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16657|2|1|-1
    SIGMA     :    liquid  ||  16657|10|1|-1

return to listing



25 Al2O3 - 38 SiO2 - 37 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16658|2|1|-1
    SIGMA     :    liquid  ||  16658|10|1|-1

return to listing



11 Al2O3 - 50 SiO2 - 39 CaO (mol %) slag (New)

    Vis       :    liquid  ||  16581|26|1|-1

return to listing



20 Al2O3 - 40 SiO2 - 40 CaO (mol %) slag (New)

    RHO       :    liquid  ||  16659|2|1|-1
    SIGMA     :    liquid  ||  16659|10|1|-1

return to listing



4 Al2O3 - 58.6 SiO2 - 37.4 CaO (mol %) slag (New)

    Vis       :    liquid  ||  16706|26|1|-1

return to listing



7 Al2O3 - 65.1 SiO2 - 27.9 Na2O (mol %) slag (New)

    TC        :    liquid  ||  16721|1|1|-1
    SH    (*):    solid  ||  16721|9|0|-1
    D     (*):    solid  ||  16721|24|0|-1

return to listing



Antimony

    Vis    (R):    liquid  ||  885|26|1|-1

return to listing



8 Au - 6 Ag - 86 Cu (at %) (New)

    DLL       :    liquid  ||  16481|0|1|-1
    MTE       :    liquid  ||  16481|8|1|-1
    CTE       :    liquid  ||  16481|16|1|-1
    D         :    liquid  ||  16481|24|1|-1
    ST        :    liquid  ||  16481|38|1|-1

return to listing



10 Au - 25 Ag - 65 Cu (at %) (New)

    DLL       :    liquid  ||  16482|0|1|-1
    MTE       :    liquid  ||  16482|8|1|-1
    CTE       :    liquid  ||  16482|16|1|-1
    D         :    liquid  ||  16482|24|1|-1
    ST        :    liquid  ||  16482|38|1|-1

return to listing



14 Au - 34 Ag - 52 Cu (at %) (New)

    DLL       :    liquid  ||  16483|0|1|-1
    MTE       :    liquid  ||  16483|8|1|-1
    CTE       :    liquid  ||  16483|16|1|-1
    D         :    liquid  ||  16483|24|1|-1
    ST        :    liquid  ||  16483|38|1|-1

return to listing



15 Au - 10 Ag - 75 Cu (at %) (New)

    DLL       :    liquid  ||  16484|0|1|-1
    MTE       :    liquid  ||  16484|8|1|-1
    CTE       :    liquid  ||  16484|16|1|-1
    D         :    liquid  ||  16484|24|1|-1
    ST        :    liquid  ||  16484|38|1|-1

return to listing



17 Au - 42 Ag - 41 Cu (at %) (New)

    DLL       :    liquid  ||  16485|0|1|-1
    MTE       :    liquid  ||  16485|8|1|-1
    CTE       :    liquid  ||  16485|16|1|-1
    D         :    liquid  ||  16485|24|1|-1
    ST        :    liquid  ||  16485|38|1|-1

return to listing



20 Au - 50 Ag - 30 Cu (at %) (New)

    DLL       :    liquid  ||  16486|0|1|-1
    MTE       :    liquid  ||  16486|8|1|-1
    CTE       :    liquid  ||  16486|16|1|-1
    D         :    liquid  ||  16486|24|1|-1
    ST        :    liquid  ||  16486|38|1|-1

return to listing



21 Au - 14 Ag - 65 Cu (at %) (New)

    DLL       :    liquid  ||  16487|0|1|-1
    MTE       :    liquid  ||  16487|8|1|-1
    CTE       :    liquid  ||  16487|16|1|-1
    D         :    liquid  ||  16487|24|1|-1
    ST        :    liquid  ||  16487|38|1|-1

return to listing



22 Au - 55 Ag - 23 Cu (at %) (New)

    DLL       :    liquid  ||  16488|0|1|-1
    MTE       :    liquid  ||  16488|8|1|-1
    CTE       :    liquid  ||  16488|16|1|-1
    D         :    liquid  ||  16488|24|1|-1
    ST        :    liquid  ||  16488|38|1|-1

return to listing



24 Au - 61 Ag - 15 Cu (at %) (New)

    DLL       :    liquid  ||  16489|0|1|-1
    MTE       :    liquid  ||  16489|8|1|-1
    CTE       :    liquid  ||  16489|16|1|-1
    D         :    liquid  ||  16489|24|1|-1
    ST        :    liquid  ||  16489|38|1|-1

return to listing



26 Au - 66 Ag - 8 Cu (at %) (New)

    DLL       :    liquid  ||  16490|0|1|-1
    MTE       :    liquid  ||  16490|8|1|-1
    CTE       :    liquid  ||  16490|16|1|-1
    D         :    liquid  ||  16490|24|1|-1
    ST        :    liquid  ||  16490|38|1|-1

return to listing



29 Au - 19 Ag - 52 Cu (at %) (New)

    DLL       :    liquid  ||  16491|0|1|-1
    MTE       :    liquid  ||  16491|8|1|-1
    CTE       :    liquid  ||  16491|16|1|-1
    D         :    liquid  ||  16491|24|1|-1
    ST        :    liquid  ||  16491|38|1|-1

return to listing



35 Au - 24 Ag - 41 Cu (at %) (New)

    DLL       :    liquid  ||  16492|0|1|-1
    MTE       :    liquid  ||  16492|8|1|-1
    CTE       :    liquid  ||  16492|16|1|-1
    D         :    liquid  ||  16492|24|1|-1
    ST        :    liquid  ||  16492|38|1|-1

return to listing



42 Au - 28 Ag - 30 Cu (at %) (New)

    DLL       :    liquid  ||  16493|0|1|-1
    MTE       :    liquid  ||  16493|8|1|-1
    CTE       :    liquid  ||  16493|16|1|-1
    D         :    liquid  ||  16493|24|1|-1
    ST        :    liquid  ||  16493|38|1|-1

return to listing



47 Au - 31 Ag - 22 Cu (at %) (New)

    DLL       :    liquid  ||  16494|0|1|-1
    MTE       :    liquid  ||  16494|8|1|-1
    CTE       :    liquid  ||  16494|16|1|-1
    D         :    liquid  ||  16494|24|1|-1
    ST        :    liquid  ||  16494|38|1|-1

return to listing



51 Au - 34 Ag - 15 Cu (at %) (New)

    DLL       :    liquid  ||  16495|0|1|-1
    MTE       :    liquid  ||  16495|8|1|-1
    CTE       :    liquid  ||  16495|16|1|-1
    D         :    liquid  ||  16495|24|1|-1
    ST        :    liquid  ||  16495|38|1|-1

return to listing



56 Au - 37 Ag - 7 Cu (at %) (New)

    DLL       :    liquid  ||  16496|0|1|-1
    MTE       :    liquid  ||  16496|8|1|-1
    CTE       :    liquid  ||  16496|16|1|-1
    D         :    liquid  ||  16496|24|1|-1
    ST        :    liquid  ||  16496|38|1|-1

return to listing



4 Au - 3 Ag - 93 Cu (at %) (New)

    DLL       :    liquid  ||  16478|0|1|-1
    MTE       :    liquid  ||  16478|8|1|-1
    CTE       :    liquid  ||  16478|16|1|-1
    D         :    liquid  ||  16478|24|1|-1

return to listing



4 Au - 10 Ag - 86 Cu (at %) (New)

    DLL       :    liquid  ||  16479|0|1|-1
    MTE       :    liquid  ||  16479|8|1|-1
    CTE       :    liquid  ||  16479|16|1|-1
    D         :    liquid  ||  16479|24|1|-1
    ST        :    liquid  ||  16479|38|1|-1

return to listing



7 Au - 18 Ag - 75 Cu (at %) (New)

    DLL       :    liquid  ||  16480|0|1|-1
    MTE       :    liquid  ||  16480|8|1|-1
    CTE       :    liquid  ||  16480|16|1|-1
    D         :    liquid  ||  16480|24|1|-1
    ST        :    liquid  ||  16480|38|1|-1

return to listing



Au - 20 Cu (wt %)

    ST     (N):    liquid  ||  15316|38|1|-1

return to listing



50 BaO - 50 P2O5 (mol %) (New)

    DLL       :    glass  ||  16972|0|0|-1
    MTE       :    glass  ||  16972|8|0|-1
    CTE       :    glass  ||  16972|16|0|-1
    D         :    glass  ||  16972|24|0|-1

return to listing



B4C

    TC     (N):    solid  ||  spark plasma sintered, 96.8% dense, Ozer et. al.  ||  182|1|0|1
    RHO    (N):    spark plasma sintered, 96.8% dense, Ozer et. al.  ||  182|2|0|-1
    SH     (R):    solid  ||  Medwick et. al.  ||  182|9|0|0
    SH     (N):    solid  ||  spark plasma sintered, Ozer et. al.  ||  182|9|0|1
    SIGMA  (N):    spark plasma sintered, 96.8% dense, Ozer et. al.  ||  182|10|0|-1
    HC     (R):    solid  ||  Medwick et. al.  ||  182|17|0|0
    HC     (N):    solid  ||  spark plasma sintered, Ozer et. al.  ||  182|17|0|1
    TD     (N):    Ozer et. al.  ||  spark plasma sintered, 96.8% dense  ||  182|25|1|0
    S      (N):    Ozer et. al.  ||  spark plasma sintered  ||  182|48|0|0

return to listing



Bi - 60 In (wt %) (New)

    DLL       :    liquid  ||  16573|0|1|-1
    MTE       :    liquid  ||  16573|8|1|-1
    CTE       :    liquid  ||  16573|16|1|-1
    D         :    liquid  ||  16573|24|1|-1

return to listing



Bi - 52 In (wt %) (New)

    DLL       :    liquid  ||  16574|0|1|-1
    MTE       :    liquid  ||  16574|8|1|-1
    CTE       :    liquid  ||  16574|16|1|-1
    D         :    liquid  ||  16574|24|1|-1

return to listing



Bi - 35 In (wt %) (New)

    DLL       :    liquid  ||  16575|0|1|-1
    MTE       :    liquid  ||  16575|8|1|-1
    CTE       :    liquid  ||  16575|16|1|-1
    D         :    liquid  ||  16575|24|1|-1

return to listing



Bi - 15 In (wt %) (New)

    DLL       :    liquid  ||  16576|0|1|-1
    MTE       :    liquid  ||  16576|8|1|-1
    CTE       :    liquid  ||  16576|16|1|-1
    D         :    liquid  ||  16576|24|1|-1

return to listing



Bi - 85 In (wt %) (New)

    DLL       :    liquid  ||  16571|0|1|-1
    MTE       :    liquid  ||  16571|8|1|-1
    CTE       :    liquid  ||  16571|16|1|-1
    D         :    liquid  ||  16571|24|1|-1

return to listing



Bi - 66 In (wt %) (New)

    DLL       :    liquid  ||  16572|0|1|-1
    MTE       :    liquid  ||  16572|8|1|-1
    CTE       :    liquid  ||  16572|16|1|-1
    D         :    liquid  ||  16572|24|1|-1

return to listing



Bi - 12 Sb (at %) (New)

    DLL       :    liquid  ||  16459|0|1|-1
    TC        :    annealed  ||  -325 to +400 mesh powder  ||  16459|1|0|0
    TC        :    annealed  ||  -50 to +100 mesh powder  ||  16459|1|0|1
    RHO       :    annealed  ||  -325 to +400 mesh powder  ||  16459|2|0|0
    RHO       :    annealed  ||  -50 to +100 mesh powder  ||  16459|2|0|1
    MTE       :    liquid  ||  16459|8|1|-1
    SIGMA     :    annealed  ||  -325 to +400 mesh powder  ||  16459|10|0|0
    SIGMA     :    annealed  ||  -50 to +100 mesh powder  ||  16459|10|0|1
    CTE       :    liquid  ||  16459|16|1|-1
    D         :    liquid  ||  16459|24|1|-1
    S         :    annealed  ||  -325 to +400 mesh powder  ||  16459|48|0|0
    S         :    annealed  ||  -50 to +100 mesh powder  ||  16459|48|0|1

return to listing



Bi - 60 Sb (wt %) (New)

    DLL       :    liquid  ||  16570|0|1|-1
    MTE       :    liquid  ||  16570|8|1|-1
    CTE       :    liquid  ||  16570|16|1|-1
    D         :    liquid  ||  16570|24|1|-1

return to listing



Bi - 20 Sb (wt %) (New)

    DLL       :    liquid  ||  16568|0|1|-1
    MTE       :    liquid  ||  16568|8|1|-1
    CTE       :    liquid  ||  16568|16|1|-1
    D         :    liquid  ||  16568|24|1|-1

return to listing



Bi - 40 Sb (wt %) (New)

    DLL       :    liquid  ||  16569|0|1|-1
    MTE       :    liquid  ||  16569|8|1|-1
    CTE       :    liquid  ||  16569|16|1|-1
    D         :    liquid  ||  16569|24|1|-1

return to listing



Bi - 27.5 Sn (wt %) (New)

    DLL       :    liquid  ||  16360|0|1|-1
    MTE       :    liquid  ||  16360|8|1|-1
    CTE       :    liquid  ||  16360|16|1|-1
    D         :    liquid  ||  16360|24|1|-1
    ST        :    liquid  ||  16360|38|1|-1

return to listing



Bi - 12.4 Sn (wt %) (New)

    DLL       :    liquid  ||  16361|0|1|-1
    MTE       :    liquid  ||  16361|8|1|-1
    CTE       :    liquid  ||  16361|16|1|-1
    D         :    liquid  ||  16361|24|1|-1
    ST        :    liquid  ||  16361|38|1|-1

return to listing



Bi - 46 Sn (wt %)

    DLL    (N):    liquid  ||  Moser et. al.  ||  9631|0|1|1
    DLL    (N):    liquid  ||  average of Moser et. al. and Plevachuk et. al.  ||  9631|0|1|2
    MTE    (N):    liquid  ||  Moser et. al.  ||  9631|8|1|1
    MTE    (N):    liquid  ||  average of Moser et. al. and Plevachuk et. al.  ||  9631|8|1|2
    CTE    (N):    liquid  ||  Moser et. al.  ||  9631|16|1|1
    CTE    (N):    liquid  ||  average of Moser et. al. and Plevachuk et. al.  ||  9631|16|1|2
    D      (N):    liquid  ||  Moser et. al.  ||  9631|24|1|1
    D      (N):    liquid  ||  average of Moser et. al. and Plevachuk et. al.  ||  9631|24|1|2
    ST     (R):    liquid  ||  9631|38|1|-1

return to listing



Bi - 30 Te (wt %) (New)

    DLL       :    liquid  ||  16423|0|1|-1
    MTE       :    liquid  ||  16423|8|1|-1
    CTE       :    liquid  ||  16423|16|1|-1
    D         :    liquid  ||  16423|24|1|-1

return to listing



Bi - 40 Te (wt %) (New)

    DLL       :    liquid  ||  16424|0|1|-1
    MTE       :    liquid  ||  16424|8|1|-1
    CTE       :    liquid  ||  16424|16|1|-1
    D         :    liquid  ||  16424|24|1|-1

return to listing



Bi - 50 Te (wt %) (New)

    DLL       :    liquid  ||  16425|0|1|-1
    MTE       :    liquid  ||  16425|8|1|-1
    CTE       :    liquid  ||  16425|16|1|-1
    D         :    liquid  ||  16425|24|1|-1

return to listing



Bi - 60 Te (wt %) (New)

    DLL       :    liquid  ||  16426|0|1|-1
    MTE       :    liquid  ||  16426|8|1|-1
    CTE       :    liquid  ||  16426|16|1|-1
    D         :    liquid  ||  16426|24|1|-1

return to listing



Bi - 70 Te (wt %) (New)

    DLL       :    liquid  ||  16427|0|1|-1
    MTE       :    liquid  ||  16427|8|1|-1
    CTE       :    liquid  ||  16427|16|1|-1
    D         :    liquid  ||  16427|24|1|-1

return to listing



Bi - 80 Te (wt %) (New)

    DLL       :    liquid  ||  16428|0|1|-1
    MTE       :    liquid  ||  16428|8|1|-1
    CTE       :    liquid  ||  16428|16|1|-1
    D         :    liquid  ||  16428|24|1|-1

return to listing



Bi - 90 Te (wt %) (New)

    DLL       :    liquid  ||  16429|0|1|-1
    MTE       :    liquid  ||  16429|8|1|-1
    CTE       :    liquid  ||  16429|16|1|-1
    D         :    liquid  ||  16429|24|1|-1

return to listing



Bi - 10 Te (wt %) (New)

    DLL       :    liquid  ||  16421|0|1|-1
    MTE       :    liquid  ||  16421|8|1|-1
    CTE       :    liquid  ||  16421|16|1|-1
    D         :    liquid  ||  16421|24|1|-1

return to listing



Bi - 20 Te (wt %) (New)

    DLL       :    liquid  ||  16422|0|1|-1
    MTE       :    liquid  ||  16422|8|1|-1
    CTE       :    liquid  ||  16422|16|1|-1
    D         :    liquid  ||  16422|24|1|-1

return to listing



Bismuth

    S      (N):    polycrystal  ||  -325 to +400 mesh powder, annealed  ||  917|48|1|0
    S      (N):    polycrystal  ||  -50 to +100 mesh powder, annealed  ||  917|48|1|1

return to listing



Bromine

    ST     (N):    liquid  ||  869|38|1|-1

return to listing



Ca1-xErxF2+x (New)

    TC        :    single crystal  ||  x = 0.0, CaF2  ||  16362|1|0|0
    TC        :    single crystal  ||  x = 0.01, Ca0.99Er0.01F2.01  ||  16362|1|0|1
    TC        :    single crystal  ||  x = 0.05, Ca0.95Er0.05F2.05  ||  16362|1|0|2
    TC        :    single crystal  ||  x = 0.075, Ca0.925Er0.075F2.075  ||  16362|1|0|3
    TC        :    single crystal  ||  x = 0.1, Ca0.9Er0.1F2.1  ||  16362|1|0|4

return to listing



20 CaF2 - 28.8 CaO - 36.8 Al2O3 - 5 SiO2 - 1.5 B2O3 - 8 BaO (wt %) slag (New)

    Vis       :    liquid  ||  16941|26|1|-1

return to listing



20 CaF2 - 32.8 CaO - 36.8 Al2O3 - 5 SiO2 - 1.5 B2O3 - 4 BaO (wt %) slag (New)

    Vis       :    liquid  ||  16940|26|1|-1

return to listing



20 CaF2 - 31.8 CaO - 31.8 Al2O3 - 15 SiO2 - 1.5 B2O3 slag (New)

    Vis       :    liquid  ||  16939|26|1|-1

return to listing



20 CaF2 - 36.8 CaO - 36.8 Al2O3 - 5 SiO2 - 1.5 B2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16937|26|1|-1

return to listing



20 CaF2 - 34.3 CaO - 34.3 Al2O3 - 10 SiO2 - 1.5 B2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16938|26|1|-1

return to listing



20 CaF2 - 39.3 CaO - 39.3 Al2O3 - 0 SiO2 - 1.5 B2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16936|26|1|-1

return to listing



50 CaF2 - 40 SiO2 - 10 MnO (wt %) flux (New)

    Vis       :    liquid  ||  16925|26|1|-1

return to listing



40 CaF2 - 40 SiO2 - 20 MnO (wt %) flux (New)

    Vis       :    liquid  ||  16926|26|1|-1

return to listing



30 CaF2 - 40 SiO2 - 30 MnO (wt %) flux (New)

    Vis       :    liquid  ||  16927|26|1|-1

return to listing



20 CaF2 - 40 SiO2 - 40 MnO (wt %) flux (New)

    Vis       :    liquid  ||  16928|26|1|-1

return to listing



10 CaF2 - 40 SiO2 - 50 MnO (wt %) flux (New)

    Vis       :    liquid  ||  16929|26|1|-1

return to listing



Canola/rapeseed oil

    SH     (N):    liquid  ||  3411|9|1|-1

return to listing



40.5 CaO - 40.5 Al2O3 - 14.3 B2O3 - 4.8 La2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16899|26|1|-1

return to listing



38.6 CaO - 38.6 Al2O3 - 13.6 B2O3 - 9.1 La2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16900|26|1|-1

return to listing



37.0 CaO - 37.0 Al2O3 - 13.0 B2O3 - 13.0 La2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16901|26|1|-1

return to listing



42.5 CaO - 42.5 Al2O3 - 15.0 B2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16898|26|1|-1

return to listing



23.5 CaO - 10 Al2O3 - 66.5 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16597|26|1|-1

return to listing



22.2 CaO - 15 Al2O3 - 62.8 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16598|26|1|-1

return to listing



14.2 CaO - 5 Al2O3 - 80.8 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16603|26|1|-1

return to listing



13.4 CaO - 10 Al2O3 - 76.6 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16604|26|1|-1

return to listing



12.7 CaO - 15 Al2O3 - 72.3 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16605|26|1|-1

return to listing



24.8 CaO - 5 Al2O3 - 70.2 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16596|26|1|-1

return to listing



50 CaO - 50 Al2O3 (wt %) slag

    ST     (N):    liquid  ||  16751|38|1|-1

return to listing



14.9 CaO - 85.1 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16599|26|1|-1

return to listing



24.8 CaO - 75.2 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16593|26|1|-1

return to listing



26.1 CaO - 73.9 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16592|26|1|-1

return to listing



32 CaO - 32 SiO2 - 16 Al2O3 - 20 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16589|26|1|-1

return to listing



28 CaO - 28 SiO2 - 14 Al2O3 - 30 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16590|26|1|-1

return to listing



24 CaO - 24 SiO2 - 12 Al2O3 - 40 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16591|26|1|-1

return to listing



36 CaO - 36 SiO2 - 18 Al2O3 - 10 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16588|26|1|-1

return to listing



43 CaO - 43 SiO2 - 8 Al2O3 - 2 Li2O - 0 Na2O - 4 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16884|26|1|-1

return to listing



43 CaO - 43 SiO2 - 8 Al2O3 - 4 Li2O - 0 Na2O - 2 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16885|26|1|-1

return to listing



43 CaO - 43 SiO2 - 8 Al2O3 - 0 Li2O - 2 Na2O - 4 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16886|26|1|-1

return to listing



43 CaO - 43 SiO2 - 8 Al2O3 - 0 Li2O - 4 Na2O - 2 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16887|26|1|-1

return to listing



43 CaO - 43 SiO2 - 8 Al2O3 - 2 Li2O - 2 Na2O - 2 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16888|26|1|-1

return to listing



45 CaO - 45 SiO2 - 4 Al2O3 - 0 Li2O - 0 Na2O - 6 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16870|26|1|-1

return to listing



45 CaO - 45 SiO2 - 4 Al2O3 - 2 Li2O - 0 Na2O - 4 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16873|26|1|-1

return to listing



45 CaO - 45 SiO2 - 4 Al2O3 - 4 Li2O - 0 Na2O - 2 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16874|26|1|-1

return to listing



45 CaO - 45 SiO2 - 4 Al2O3 - 0 Li2O - 2 Na2O - 4 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16875|26|1|-1

return to listing



45 CaO - 45 SiO2 - 4 Al2O3 - 0 Li2O - 4 Na2O - 2 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16876|26|1|-1

return to listing



45 CaO - 45 SiO2 - 4 Al2O3 - 2 Li2O - 2 Na2O - 2 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16877|26|1|-1

return to listing



43 CaO - 43 SiO2 - 8 Al2O3 - 0 Li2O - 0 Na2O - 6 K2O (mol %) slag (New)

    Vis       :    liquid  ||  16881|26|1|-1

return to listing



45 CaO - 45 SiO2 - 4 Al2O3 - 0 Li2O - 6 Na2O (mol %) slag (New)

    Vis       :    liquid  ||  16889|26|1|-1

return to listing



45 CaO - 45 SiO2 - 4 Al2O3 - 2 Li2O - 4 Na2O (mol %) slag (New)

    Vis       :    liquid  ||  16871|26|1|-1

return to listing



43 CaO - 43 SiO2 - 8 Al2O3 - 0 Li2O - 6 Na2O (mol %) slag (New)

    Vis       :    liquid  ||  16880|26|1|-1

return to listing



45 CaO - 45 SiO2 - 4 Al2O3 - 4 Li2O - 2 Na2O (mol %) slag (New)

    Vis       :    liquid  ||  16872|26|1|-1

return to listing



43 CaO - 43 SiO2 - 8 Al2O3 - 2 Li2O - 4 Na2O (mol %) slag (New)

    Vis       :    liquid  ||  16882|26|1|-1

return to listing



43 CaO - 43 SiO2 - 8 Al2O3 - 4 Li2O - 2 Na2O (mol %) slag (New)

    Vis       :    liquid  ||  16883|26|1|-1

return to listing



45 CaO - 45 SiO2 - 4 Al2O3 - 6 Li2O (mol %) slag (New)

    Vis       :    liquid  ||  16869|26|1|-1

return to listing



43 CaO - 43 SiO2 - 8 Al2O3 - 6 Li2O (mol %) slag (New)

    Vis       :    liquid  ||  16879|26|1|-1

return to listing



23.8 CaO - 55.2 SiO2 - 13 Al2O3 - 3 MgO - 5 Cr2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16806|26|1|-1

return to listing



30.2 CaO - 48.8 SiO2 - 13 Al2O3 - 3 MgO - 5 Cr2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16807|26|1|-1

return to listing



37.4 CaO - 41.6 SiO2 - 13 Al2O3 - 3 MgO - 5 Cr2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16808|26|1|-1

return to listing



38.4 CaO - 42.6 SiO2 - 13 Al2O3 - 3 MgO - 3 Cr2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16809|26|1|-1

return to listing



39.3 CaO - 43.7 SiO2 - 13 Al2O3 - 3 MgO - 1 Cr2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16810|26|1|-1

return to listing



39.8 CaO - 44.2 SiO2 - 13 Al2O3 - 3 MgO - 0 Cr2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16811|26|1|-1

return to listing



41.0 CaO - 38.0 SiO2 - 13 Al2O3 - 3 MgO - 5 Cr2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16812|26|1|-1

return to listing



41.3 CaO - 37.0 SiO2 - 6.0 Al2O3 - 3.0 MgO - 5.8 F - 6.4 Na2O - 0.5 Li2O (wt %) slag (New)

    RHO       :    liquid  ||  16897|2|1|-1
    SIGMA     :    liquid  ||  16897|10|1|-1

return to listing



35.6 CaO - 42.8 SiO2 - 5.9 Al2O3 - 3.0 MgO - 5.8 F - 6.4 Na2O - 0.5 Li2O (wt %) slag (New)

    RHO       :    liquid  ||  16894|2|1|-1
    SIGMA     :    liquid  ||  16894|10|1|-1

return to listing



37.1 CaO - 41.0 SiO2 - 6.0 Al2O3 - 3.0 MgO - 5.9 F - 6.4 Na2O - 0.5 Li2O (wt %) slag (New)

    RHO       :    liquid  ||  16895|2|1|-1
    SIGMA     :    liquid  ||  16895|10|1|-1

return to listing



39.9 CaO - 38.5 SiO2 - 5.9 Al2O3 - 3.0 MgO - 5.8 F - 6.4 Na2O - 0.5 Li2O (wt %) slag (New)

    RHO       :    liquid  ||  16896|2|1|-1
    SIGMA     :    liquid  ||  16896|10|1|-1

return to listing



27.5 CaO - 23.7 SiO2 - 14.4 Al2O3 - 7.7 MgO - 22.5 FetO - 4.4 P2O5 (wt %) slag (New)

    Vis       :    liquid  ||  16795|26|1|-1

return to listing



25.1 CaO - 21.4 SiO2 - 14.3 Al2O3 - 7.6 MgO - 22.4 FetO - 9.2 P2O5 (wt %) slag (New)

    Vis       :    liquid  ||  16796|26|1|-1

return to listing



32.6 CaO - 28.2 SiO2 - 14.4 Al2O3 - 7.7 MgO - 12.9 FetO - 4.2 P2O5 (wt %) slag (New)

    Vis       :    liquid  ||  16797|26|1|-1

return to listing



37.3 CaO - 31.9 SiO2 - 14.3 Al2O3 - 7.7 MgO - 4.6 FetO - 4.2 P2O5 (wt %) slag (New)

    Vis       :    liquid  ||  16798|26|1|-1

return to listing



28.4 CaO - 24.3 SiO2 - 14.2 Al2O3 - 7.5 MgO - 22.8 FetO - 2.7 P2O5 (wt %) slag (New)

    Vis       :    liquid  ||  16794|26|1|-1

return to listing



30.0 CaO - 25.5 SiO2 - 14.3 Al2O3 - 7.6 MgO - 22.6 FetO (wt %) slag (New)

    Vis       :    liquid  ||  16793|26|1|-1

return to listing



39.5 CaO - 34.1 SiO2 - 14.3 Al2O3 - 7.8 MgO - 4.4 P2O5 (wt %) slag (New)

    Vis       :    liquid  ||  16799|26|1|-1

return to listing



24.6 CaO - 20.5 SiO2 - 13 Al2O3 - 8 MgO - 25 TiO2 - 9 FeO (wt %) slag (New)

    Vis       :    liquid  ||  16945|26|1|-1

return to listing



21.8 CaO - 18.2 SiO2 - 13 Al2O3 - 8 MgO - 30 TiO2 - 9 FeO (wt %) slag (New)

    Vis       :    liquid  ||  16946|26|1|-1

return to listing



32.7 CaO - 27.3 SiO2 - 13 Al2O3 - 8 MgO - 10 TiO2 - 9 FeO (wt %) slag (New)

    Vis       :    liquid  ||  16942|26|1|-1

return to listing



30.0 CaO - 25.0 SiO2 - 13 Al2O3 - 8 MgO - 15 TiO2 - 9 FeO (wt %) slag (New)

    Vis       :    liquid  ||  16943|26|1|-1

return to listing



27.3 CaO - 22.7 SiO2 - 13 Al2O3 - 8 MgO - 20 TiO2 - 9 FeO (wt %) slag (New)

    Vis       :    liquid  ||  16944|26|1|-1

return to listing



40.0 CaO - 20 SiO2 - 30 Al2O3 - 5 MgO - 5 TiO2 (wt %) slag (New)

    Vis       :    liquid  ||  16956|26|1|-1

return to listing



53.3 CaO - 6.7 SiO2 - 30 Al2O3 - 5 MgO - 5 TiO2 (wt %) slag (New)

    Vis       :    liquid  ||  16957|26|1|-1

return to listing



54.6 CaO - 5.5 SiO2 - 30 Al2O3 - 5 MgO - 5 TiO2 (wt %) slag (New)

    Vis       :    liquid  ||  16958|26|1|-1

return to listing



34 CaO - 40 SiO2 - 16 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16828|0|1|-1
    MTE       :    liquid  ||  16828|8|1|-1
    CTE       :    liquid  ||  16828|16|1|-1
    D         :    liquid  ||  16828|24|1|-1
    ST        :    liquid  ||  16828|38|1|-1

return to listing



32 CaO - 40 SiO2 - 18 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16829|0|1|-1
    MTE       :    liquid  ||  16829|8|1|-1
    CTE       :    liquid  ||  16829|16|1|-1
    D         :    liquid  ||  16829|24|1|-1
    ST        :    liquid  ||  16829|38|1|-1

return to listing



30 CaO - 40 SiO2 - 20 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16830|0|1|-1
    MTE       :    liquid  ||  16830|8|1|-1
    CTE       :    liquid  ||  16830|16|1|-1
    D         :    liquid  ||  16830|24|1|-1
    ST        :    liquid  ||  16830|38|1|-1

return to listing



28 CaO - 40 SiO2 - 22 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16831|0|1|-1
    MTE       :    liquid  ||  16831|8|1|-1
    CTE       :    liquid  ||  16831|16|1|-1
    D         :    liquid  ||  16831|24|1|-1
    ST        :    liquid  ||  16831|38|1|-1

return to listing



26 CaO - 40 SiO2 - 24 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16832|0|1|-1
    MTE       :    liquid  ||  16832|8|1|-1
    CTE       :    liquid  ||  16832|16|1|-1
    D         :    liquid  ||  16832|24|1|-1
    ST        :    liquid  ||  16832|38|1|-1

return to listing



24 CaO - 40 SiO2 - 26 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16833|0|1|-1
    MTE       :    liquid  ||  16833|8|1|-1
    CTE       :    liquid  ||  16833|16|1|-1
    D         :    liquid  ||  16833|24|1|-1
    ST        :    liquid  ||  16833|38|1|-1

return to listing



22 CaO - 40 SiO2 - 28 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16834|0|1|-1
    MTE       :    liquid  ||  16834|8|1|-1
    CTE       :    liquid  ||  16834|16|1|-1
    D         :    liquid  ||  16834|24|1|-1
    ST        :    liquid  ||  16834|38|1|-1

return to listing



20 CaO - 40 SiO2 - 30 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16835|0|1|-1
    MTE       :    liquid  ||  16835|8|1|-1
    CTE       :    liquid  ||  16835|16|1|-1
    D         :    liquid  ||  16835|24|1|-1
    ST        :    liquid  ||  16835|38|1|-1

return to listing



33.6 CaO - 40.4 SiO2 - 16 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16821|0|1|-1
    MTE       :    liquid  ||  16821|8|1|-1
    CTE       :    liquid  ||  16821|16|1|-1
    D         :    liquid  ||  16821|24|1|-1
    ST        :    liquid  ||  16821|38|1|-1

return to listing



32.7 CaO - 39.3 SiO2 - 18 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16822|0|1|-1
    MTE       :    liquid  ||  16822|8|1|-1
    CTE       :    liquid  ||  16822|16|1|-1
    D         :    liquid  ||  16822|24|1|-1
    ST        :    liquid  ||  16822|38|1|-1

return to listing



31.8 CaO - 38.2 SiO2 - 20 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16823|0|1|-1
    MTE       :    liquid  ||  16823|8|1|-1
    CTE       :    liquid  ||  16823|16|1|-1
    D         :    liquid  ||  16823|24|1|-1
    ST        :    liquid  ||  16823|38|1|-1

return to listing



30.9 CaO - 37.1 SiO2 - 22 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16824|0|1|-1
    MTE       :    liquid  ||  16824|8|1|-1
    CTE       :    liquid  ||  16824|16|1|-1
    D         :    liquid  ||  16824|24|1|-1
    ST        :    liquid  ||  16824|38|1|-1

return to listing



30 CaO - 36 SiO2 - 24 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16825|0|1|-1
    MTE       :    liquid  ||  16825|8|1|-1
    CTE       :    liquid  ||  16825|16|1|-1
    D         :    liquid  ||  16825|24|1|-1
    ST        :    liquid  ||  16825|38|1|-1

return to listing



29.1 CaO - 34.9 SiO2 - 26 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16826|0|1|-1
    MTE       :    liquid  ||  16826|8|1|-1
    CTE       :    liquid  ||  16826|16|1|-1
    D         :    liquid  ||  16826|24|1|-1
    ST        :    liquid  ||  16826|38|1|-1

return to listing



28.2 CaO - 33.8 SiO2 - 28 Al2O3 - 9 MgO - 1 TiO2 (wt %) slag (New)

    DLL       :    liquid  ||  16827|0|1|-1
    MTE       :    liquid  ||  16827|8|1|-1
    CTE       :    liquid  ||  16827|16|1|-1
    D         :    liquid  ||  16827|24|1|-1
    ST        :    liquid  ||  16827|38|1|-1

return to listing



54.0 CaO - 9.0 SiO2 - 30 Al2O3 - 5 MgO - 2 TiO2 (wt %) slag (New)

    Vis       :    liquid  ||  16952|26|1|-1

return to listing



51.4 CaO - 8.6 SiO2 - 30 Al2O3 - 5 MgO - 5 TiO2 (wt %) slag (New)

    Vis       :    liquid  ||  16953|26|1|-1

return to listing



49.7 CaO - 8.3 SiO2 - 30 Al2O3 - 5 MgO - 7 TiO2 (wt %) slag (New)

    Vis       :    liquid  ||  16954|26|1|-1

return to listing



47.1 CaO - 7.9 SiO2 - 30 Al2O3 - 5 MgO - 10 TiO2 (wt %) slag (New)

    Vis       :    liquid  ||  16955|26|1|-1

return to listing



34 CaO - 34 SiO2 - 17 Al2O3 - 15 MgO (wt %) slag (New)

    Vis       :    liquid  ||  16584|26|1|-1

return to listing



32 CaO - 32 SiO2 - 16 Al2O3 - 20 MgO (wt %) slag (New)

    Vis       :    liquid  ||  16585|26|1|-1

return to listing



38 CaO - 38 SiO2 - 19 Al2O3 - 5 MgO (wt %) slag (New)

    Vis       :    liquid  ||  16582|26|1|-1

return to listing



36 CaO - 36 SiO2 - 18 Al2O3 - 10 MgO (wt %) slag (New)

    Vis       :    liquid  ||  16583|26|1|-1

return to listing



55.7 CaO - 9.3 SiO2 - 30 Al2O3 - 5 MgO (wt %) slag (New)

    Vis       :    liquid  ||  16951|26|1|-1

return to listing



41.4 CaO - 41.8 SiO2 - 10.7 Al2O3 - 5.7 MoO3 (wt %) slag (New)

    Vis       :    liquid  ||  16893|26|1|-1

return to listing



43.6 CaO - 43.6 SiO2 - 11.0 Al2O3 - 1.7 MoO3 (wt %) slag (New)

    Vis       :    liquid  ||  16891|26|1|-1

return to listing



42.5 CaO - 42.7 SiO2 - 10.8 Al2O3 - 3.9 MoO3 (wt %) slag (New)

    Vis       :    liquid  ||  16892|26|1|-1

return to listing



22.2 CaO - 23.8 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 8 Na2O - 4 BaO - 3 MgO - 8 Li2O (wt %) (New)

    Vis       :    liquid  ||  16963|26|1|-1

return to listing



25.1 CaO - 26.9 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 8 Na2O - 4 BaO - 3 MgO - 2 Li2O (wt %) (New)

    Vis       :    liquid  ||  16960|26|1|-1

return to listing



24.1 CaO - 25.9 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 8 Na2O - 4 BaO - 3 MgO - 4 Li2O (wt %) (New)

    Vis       :    liquid  ||  16961|26|1|-1

return to listing



23.1 CaO - 24.9 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 8 Na2O - 4 BaO - 3 MgO - 6 Li2O (wt %) (New)

    Vis       :    liquid  ||  16962|26|1|-1

return to listing



27.0 CaO - 29.0 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 6 Na2O - 4 BaO - 3 MgO (wt %) (New)

    Vis       :    liquid  ||  16966|26|1|-1

return to listing



25.0 CaO - 27.0 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 10 Na2O - 4 BaO - 3 MgO (wt %) (New)

    Vis       :    liquid  ||  16967|26|1|-1

return to listing



26.0 CaO - 28.0 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 8 Na2O - 4 BaO - 3 MgO (wt %) (New)

    Vis       :    liquid  ||  16959|26|1|-1

return to listing



28.9 CaO - 31.1 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 2 Na2O - 4 BaO - 3 MgO (wt %) (New)

    Vis       :    liquid  ||  16964|26|1|-1

return to listing



27.9 CaO - 30.1 SiO2 - 8 Al2O3 - 12 TiO2 - 11 CaF2 - 4 Na2O - 4 BaO - 3 MgO (wt %) (New)

    Vis       :    liquid  ||  16965|26|1|-1

return to listing



32 CaO - 32 SiO2 - 16 Al2O3 - 20 TiO2 (wt %) slag (New)

    Vis       :    liquid  ||  16587|26|1|-1

return to listing



36 CaO - 36 SiO2 - 18 Al2O3 - 10 TiO2 (wt %) slag (New)

    Vis       :    liquid  ||  16586|26|1|-1

return to listing



46 CaO - 46 SiO2 - 8 Al2O3 (mol %) slag (New)

    Vis       :    liquid  ||  16878|26|1|-1

return to listing



48 CaO - 48 SiO2 - 4 Al2O3 (mol %) slag (New)

    Vis       :    liquid  ||  16868|26|1|-1

return to listing



26 CaO - 42 SiO2 - 18 CaF2 - 14 Na2O (wt %) slag (New)

    ST        :    liquid  ||  16817|38|1|-1

return to listing



31 CaO - 38 SiO2 - 18 CaF2 - 13 Na2O (wt %) slag (New)

    ST        :    liquid  ||  16818|38|1|-1

return to listing



33 CaO - 33 SiO2 - 19 CaF2 - 15 Na2O (wt %) slag (New)

    ST        :    liquid  ||  16819|38|1|-1

return to listing



37 CaO - 32 SiO2 - 18 CaF2 - 13 Na2O (wt %) slag (New)

    ST        :    liquid  ||  16820|38|1|-1

return to listing



13.4 CaO - 10 SiO2 - 76.6 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16601|26|1|-1

return to listing



12.7 CaO - 15 SiO2 - 72.3 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16602|26|1|-1

return to listing



23.5 CaO - 10 SiO2 - 66.5 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16594|26|1|-1

return to listing



22.2 CaO - 15 SiO2 - 62.8 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16595|26|1|-1

return to listing



14.2 CaO - 5 SiO2 - 80.8 Fe2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16600|26|1|-1

return to listing



22.9 CaO - 37.3 SiO2 - 4.9 MgO - 20.1 Al2O3 - 14.8 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16838|26|1|-1

return to listing



19.3 CaO - 30.4 SiO2 - 4.8 MgO - 19.1 Al2O3 - 26.4 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16839|26|1|-1

return to listing



15.2 CaO - 25.6 SiO2 - 4.4 MgO - 20.7 Al2O3 - 34.1 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16840|26|1|-1

return to listing



12.1 CaO - 21.4 SiO2 - 4.5 MgO - 17.0 Al2O3 - 45.0 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16841|26|1|-1

return to listing



7.2 CaO - 12.9 SiO2 - 5.1 MgO - 20.2 Al2O3 - 54.6 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16842|26|1|-1

return to listing



37.5 CaO - 38.1 SiO2 - 5.0 MgO - 19.4 Al2O3 - 0.0 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16843|26|1|-1

return to listing



35.6 CaO - 35.1 SiO2 - 5.0 MgO - 19.2 Al2O3 - 5.1 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16844|26|1|-1

return to listing



30.4 CaO - 30.6 SiO2 - 4.5 MgO - 20.3 Al2O3 - 14.2 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16845|26|1|-1

return to listing



25.6 CaO - 27.0 SiO2 - 4.6 MgO - 19.2 Al2O3 - 23.6 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16846|26|1|-1

return to listing



19.8 CaO - 20.4 SiO2 - 5.1 MgO - 19.8 Al2O3 - 34.9 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16847|26|1|-1

return to listing



15.5 CaO - 14.9 SiO2 - 4.8 MgO - 19.2 Al2O3 - 45.6 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16848|26|1|-1

return to listing



10.6 CaO - 10.9 SiO2 - 4.4 MgO - 19.9 Al2O3 - 54.2 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16849|26|1|-1

return to listing



45.4 CaO - 29.8 SiO2 - 5.3 MgO - 19.5 Al2O3 - 0.0 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16850|26|1|-1

return to listing



42.0 CaO - 28.1 SiO2 - 4.5 MgO - 20.5 Al2O3 - 4.9 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16851|26|1|-1

return to listing



35.3 CaO - 24.5 SiO2 - 4.8 MgO - 20.6 Al2O3 - 14.8 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16852|26|1|-1

return to listing



30.3 CaO - 20.4 SiO2 - 5.1 MgO - 20.1 Al2O3 - 24.1 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16853|26|1|-1

return to listing



23.8 CaO - 16.4 SiO2 - 5.0 MgO - 20.6 Al2O3 - 34.2 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16854|26|1|-1

return to listing



18.3 CaO - 12.4 SiO2 - 4.7 MgO - 20.3 Al2O3 - 44.3 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16855|26|1|-1

return to listing



28.3 CaO - 47.5 SiO2 - 4.7 MgO - 19.5 Al2O3 - 0.0 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16836|26|1|-1

return to listing



26.8 CaO - 43.5 SiO2 - 5.1 MgO - 19.3 Al2O3 - 5.3 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16837|26|1|-1

return to listing



29.2 CaO - 25.5 SiO2 - 7.3 MgO - 14.0 Al2O3 - 22.0 TiO2 - 2.0 CaCl2 (wt %) slag (New)

    Vis       :    liquid  ||  16932|26|1|-1

return to listing



28.9 CaO - 25.2 SiO2 - 7.2 MgO - 13.9 Al2O3 - 21.8 TiO2 - 3.0 CaCl2 (wt %) slag (New)

    Vis       :    liquid  ||  16933|26|1|-1

return to listing



28.0 CaO - 24.4 SiO2 - 7.0 MgO - 13.5 Al2O3 - 21.1 TiO2 - 6.0 CaCl2 (wt %) slag (New)

    Vis       :    liquid  ||  16934|26|1|-1

return to listing



26.8 CaO - 23.4 SiO2 - 6.7 MgO - 12.9 Al2O3 - 20.2 TiO2 - 10.0 CaCl2 (wt %) slag (New)

    Vis       :    liquid  ||  16935|26|1|-1

return to listing



29.8 CaO - 26.0 SiO2 - 7.4 MgO - 14.3 Al2O3 - 22.5 TiO2 - 0.0 CaCl2 (wt %) slag (New)

    Vis       :    liquid  ||  16930|26|1|-1

return to listing



29.5 CaO - 25.7 SiO2 - 7.3 MgO - 14.2 Al2O3 - 22.2 TiO2 - 1.0 CaCl2 (wt %) slag (New)

    Vis       :    liquid  ||  16931|26|1|-1

return to listing



47.7 CaO - 40.5 SiO2 - 1.8 MgO - 10 CaF2 (wt %) slag (New)

    Vis       :    liquid  ||  16748|26|1|-1

return to listing



51.9 CaO - 44.1 SiO2 - 2 MgO - 2 CaF2 (wt %) slag (New)

    Vis       :    liquid  ||  16746|26|1|-1

return to listing



49.8 CaO - 42.3 SiO2 - 1.9 MgO - 6 CaF2 (wt %) slag (New)

    Vis       :    liquid  ||  16747|26|1|-1

return to listing



51.4 CaO - 43.7 SiO2 - 1.9 MgO - 3 KOH (wt %) slag (New)

    Vis       :    liquid  ||  16749|26|1|-1

return to listing



51.4 CaO - 43.7 SiO2 - 1.9 MgO - 3 Li2O (wt %) slag (New)

    Vis       :    liquid  ||  16750|26|1|-1

return to listing



51 CaO - 43 SiO2 - 6 MgO (wt %) slag (New)

    Vis       :    liquid  ||  16744|26|1|-1

return to listing



51.7 CaO - 46.8 SiO2 - 1.5 MgO (wt %) slag (New)

    Vis       :    liquid  ||  16745|26|1|-1

return to listing



53 CaO - 45 SiO2 - 2 MgO (wt %) slag (New)

    Vis       :    liquid  ||  16743|26|1|-1

return to listing



15 CaO - 30 SiO2 - 40.9 MnO - 14.1 CaF2 (wt %) slag (New)

    Vis       :    liquid  ||  16788|26|1|-1

return to listing



28 CaO - 56.1 SiO2 - 11.1 MnO - 4.8 CaF2 (wt %) slag (New)

    Vis       :    liquid  ||  16790|26|1|-1

return to listing



26.6 CaO - 53.1 SiO2 - 10.7 MnO - 9.6 CaF2 (wt %) slag (New)

    Vis       :    liquid  ||  16791|26|1|-1

return to listing



25.1 CaO - 50.2 SiO2 - 10.2 MnO - 14.5 CaF2 (wt %) slag (New)

    Vis       :    liquid  ||  16792|26|1|-1

return to listing



18.4 CaO - 36.8 SiO2 - 40.1 MnO - 4.7 CaF2 (wt %) slag (New)

    Vis       :    liquid  ||  16786|26|1|-1

return to listing



16.3 CaO - 32.6 SiO2 - 41.7 MnO - 9.4 CaF2 (wt %) slag (New)

    Vis       :    liquid  ||  16787|26|1|-1

return to listing



47.5 CaO - 47.5 SiO2 - 5 MnO (mol %) slag (New)

    RHO       :    solid  ||  16813|2|0|-1
    SIGMA     :    solid  ||  16813|10|0|-1

return to listing



45 CaO - 45 SiO2 - 10 MnO (mol %) slag (New)

    RHO       :    solid  ||  16814|2|0|-1
    SIGMA     :    solid  ||  16814|10|0|-1

return to listing



40 CaO - 40 SiO2 - 20 MnO (mol %) slag (New)

    RHO       :    solid  ||  16815|2|0|-1
    SIGMA     :    solid  ||  16815|10|0|-1

return to listing



35 CaO - 35 SiO2 - 30 MnO (mol %) slag (New)

    RHO       :    solid  ||  16816|2|0|-1
    SIGMA     :    solid  ||  16816|10|0|-1

return to listing



30.3 CaO - 60.5 SiO2 - 9.2 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16789|26|1|-1

return to listing



20.5 CaO - 41.1 SiO2 - 38.4 MnO (wt %) slag (New)

    Vis       :    liquid  ||  16785|26|1|-1

return to listing



55.8 CaO - 44.2 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16387|0|1|-1
    MTE       :    liquid  ||  16387|8|1|-1
    CTE       :    liquid  ||  16387|16|1|-1
    D         :    liquid  ||  16387|24|1|-1

return to listing



37.7 CaO - 62.3 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16385|0|1|-1
    MTE       :    liquid  ||  16385|8|1|-1
    CTE       :    liquid  ||  16385|16|1|-1
    D         :    liquid  ||  16385|24|1|-1

return to listing



48.3 CaO - 51.7 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16386|0|1|-1
    MTE       :    liquid  ||  16386|8|1|-1
    CTE       :    liquid  ||  16386|16|1|-1
    D         :    liquid  ||  16386|24|1|-1

return to listing



CaO

    ST     (N):    liquid  ||  2659|38|1|-1

return to listing



CaSiO3

    RHO    (N):    liquid  ||  6248|2|1|-1
    SIGMA  (N):    liquid  ||  6248|10|1|-1

return to listing



Ca1-xTmxF2+x (New)

    TC        :    single crystal  ||  x = 0.02, Ca0.98Tm0.02F2.02  ||  16363|1|0|0
    TC        :    single crystal  ||  x = 0.04, Ca0.96Tm0.04F2.04  ||  16363|1|0|1
    TC        :    single crystal  ||  x = 0.06, Ca0.94Er0.06F2.06  ||  16363|1|0|2

return to listing



Cd - 50 Pb (at %) (New)

    DLL       :    liquid  ||  16453|0|1|-1
    MTE       :    liquid  ||  16453|8|1|-1
    CTE       :    liquid  ||  16453|16|1|-1
    D         :    liquid  ||  16453|24|1|-1
    Vis       :    liquid  ||  16453|26|1|-1

return to listing



Cd - 64.5 Pb (at %) (New)

    DLL       :    liquid  ||  16454|0|1|-1
    MTE       :    liquid  ||  16454|8|1|-1
    CTE       :    liquid  ||  16454|16|1|-1
    D         :    liquid  ||  16454|24|1|-1
    Vis       :    liquid  ||  16454|26|1|-1

return to listing



Cd - 71.9 Pb (at %) (New)

    DLL       :    liquid  ||  16455|0|1|-1
    MTE       :    liquid  ||  16455|8|1|-1
    CTE       :    liquid  ||  16455|16|1|-1
    D         :    liquid  ||  16455|24|1|-1
    Vis       :    liquid  ||  16455|26|1|-1

return to listing



Cd - 75 Pb (at %) (New)

    DLL       :    liquid  ||  16456|0|1|-1
    MTE       :    liquid  ||  16456|8|1|-1
    CTE       :    liquid  ||  16456|16|1|-1
    D         :    liquid  ||  16456|24|1|-1
    Vis       :    liquid  ||  16456|26|1|-1

return to listing



Cd - 90 Pb (at %) (New)

    DLL       :    liquid  ||  16457|0|1|-1
    MTE       :    liquid  ||  16457|8|1|-1
    CTE       :    liquid  ||  16457|16|1|-1
    D         :    liquid  ||  16457|24|1|-1
    Vis       :    liquid  ||  16457|26|1|-1

return to listing



Cd - 2.8 Pb (at %) (New)

    DLL       :    liquid  ||  16450|0|1|-1
    MTE       :    liquid  ||  16450|8|1|-1
    CTE       :    liquid  ||  16450|16|1|-1
    D         :    liquid  ||  16450|24|1|-1
    Vis       :    liquid  ||  16450|26|1|-1

return to listing



Cd - 10 Pb (at %) (New)

    DLL       :    liquid  ||  16451|0|1|-1
    MTE       :    liquid  ||  16451|8|1|-1
    CTE       :    liquid  ||  16451|16|1|-1
    D         :    liquid  ||  16451|24|1|-1
    Vis       :    liquid  ||  16451|26|1|-1

return to listing



Cd - 25 Pb (at %) (New)

    DLL       :    liquid  ||  16452|0|1|-1
    MTE       :    liquid  ||  16452|8|1|-1
    CTE       :    liquid  ||  16452|16|1|-1
    D         :    liquid  ||  16452|24|1|-1
    Vis       :    liquid  ||  16452|26|1|-1

return to listing



Cd - 35.2 Pb (at %) (New)

    DLL       :    liquid  ||  16458|0|1|-1
    MTE       :    liquid  ||  16458|8|1|-1
    CTE       :    liquid  ||  16458|16|1|-1
    D         :    liquid  ||  16458|24|1|-1
    Vis       :    liquid  ||  16458|26|1|-1

return to listing



Cd - 85 Sn (at %) (New)

    DLL       :    liquid  ||  16445|0|1|-1
    MTE       :    liquid  ||  16445|8|1|-1
    CTE       :    liquid  ||  16445|16|1|-1
    D         :    liquid  ||  16445|24|1|-1
    Vis       :    liquid  ||  16445|26|1|-1

return to listing



Cd - 11 Sn (at %) (New)

    DLL       :    liquid  ||  16441|0|1|-1
    MTE       :    liquid  ||  16441|8|1|-1
    CTE       :    liquid  ||  16441|16|1|-1
    D         :    liquid  ||  16441|24|1|-1
    Vis       :    liquid  ||  16441|26|1|-1

return to listing



Cd - 25 Sn (at %) (New)

    DLL       :    liquid  ||  16442|0|1|-1
    MTE       :    liquid  ||  16442|8|1|-1
    CTE       :    liquid  ||  16442|16|1|-1
    D         :    liquid  ||  16442|24|1|-1
    Vis       :    liquid  ||  16442|26|1|-1

return to listing



Cd - 50 Sn (at %) (New)

    DLL       :    liquid  ||  16443|0|1|-1
    MTE       :    liquid  ||  16443|8|1|-1
    CTE       :    liquid  ||  16443|16|1|-1
    D         :    liquid  ||  16443|24|1|-1
    Vis       :    liquid  ||  16443|26|1|-1

return to listing



Cd - 66.5 Sn (at %) (New)

    DLL       :    liquid  ||  16444|0|1|-1
    MTE       :    liquid  ||  16444|8|1|-1
    CTE       :    liquid  ||  16444|16|1|-1
    D         :    liquid  ||  16444|24|1|-1
    Vis       :    liquid  ||  16444|26|1|-1

return to listing



Cd - 3.3 Tl (at %) (New)

    DLL       :    liquid  ||  16448|0|1|-1
    MTE       :    liquid  ||  16448|8|1|-1
    CTE       :    liquid  ||  16448|16|1|-1
    D         :    liquid  ||  16448|24|1|-1
    Vis       :    liquid  ||  16448|26|1|-1

return to listing



Cd - 6.6 Tl (at %) (New)

    DLL       :    liquid  ||  16449|0|1|-1
    MTE       :    liquid  ||  16449|8|1|-1
    CTE       :    liquid  ||  16449|16|1|-1
    D         :    liquid  ||  16449|24|1|-1
    Vis       :    liquid  ||  16449|26|1|-1

return to listing



CdTe

    VP     (N):    solid  ||  partial pressure of Te2  ||  2474|18|0|0
    VP     (N):    solid  ||  partial pressure of Cd  ||  2474|18|0|1

return to listing



Chromel

    UTS   (N*):    annealed  ||  2827|5|0|-1
    YS    (N*):    annealed  ||  2827|13|0|-1
    %El   (N*):    annealed  ||  2827|29|0|-1

return to listing



CM 186 LC

    DLL    (N):    solid  ||  14926|0|0|-1
    TC     (N):    solid  ||  14926|1|0|-1
    MTE    (N):    solid  ||  14926|8|0|-1
    SH     (N):    solid  ||  14926|9|0|-1
    SH     (N):    liquid  ||  14926|9|1|-1
    D      (R):    solid  ||  14926|24|0|-1
    TD     (N):    solid  ||  14926|25|0|-1

return to listing



CMSX-10

    DLL    (N):    solid  ||  3363|0|0|-1
    DLL    (N):    liquid  ||  3363|0|1|-1
    TC     (N):    solid  ||  3363|1|0|-1
    MTE    (N):    solid  ||  3363|8|0|-1
    MTE    (N):    liquid  ||  3363|8|1|-1
    SH     (N):    solid  ||  3363|9|0|-1
    SH     (N):    liquid  ||  3363|9|1|-1
    D      (R):    solid  ||  3363|24|0|-1
    D      (N):    liquid  ||  3363|24|1|-1
    TD     (N):    solid  ||  3363|25|0|-1

return to listing



Co - 20 Cu (at %) (New)

    DLL       :    liquid  ||  16982|0|1|-1
    MTE       :    liquid  ||  16982|8|1|-1
    CTE       :    liquid  ||  16982|16|1|-1
    D         :    liquid  ||  16982|24|1|-1

return to listing



Co - 40 Cu (at %) (New)

    DLL       :    liquid  ||  16983|0|1|-1
    MTE       :    liquid  ||  16983|8|1|-1
    CTE       :    liquid  ||  16983|16|1|-1
    D         :    liquid  ||  16983|24|1|-1

return to listing



Co - 20 Fe (at %) (New)

    DLL       :    liquid  ||  16986|0|1|-1
    MTE       :    liquid  ||  16986|8|1|-1
    CTE       :    liquid  ||  16986|16|1|-1
    D         :    liquid  ||  16986|24|1|-1

return to listing



Co - 40 Fe (at %) (New)

    DLL       :    liquid  ||  16987|0|1|-1
    MTE       :    liquid  ||  16987|8|1|-1
    CTE       :    liquid  ||  16987|16|1|-1
    D         :    liquid  ||  16987|24|1|-1

return to listing



Co - 20 Ni (at %) (New)

    DLL       :    liquid  ||  16989|0|1|-1
    MTE       :    liquid  ||  16989|8|1|-1
    CTE       :    liquid  ||  16989|16|1|-1
    D         :    liquid  ||  16989|24|1|-1

return to listing



Co - 40 Ni (at %) (New)

    DLL       :    liquid  ||  16990|0|1|-1
    MTE       :    liquid  ||  16990|8|1|-1
    CTE       :    liquid  ||  16990|16|1|-1
    D         :    liquid  ||  16990|24|1|-1

return to listing



Cobalt

    SSCC   (N):    sintered rod  ||  tested at 1250 °C (2282 °F), 0.001/s  ||  861|12|0|0
    SSCC   (N):    sintered rod  ||  tested at 1250 °C (2282 °F), 3.2/s  ||  861|12|0|1

return to listing



Corn oil

    SH     (N):    liquid  ||  3410|9|1|-1

return to listing



Corning 7740 (Pyrex)

    TC     (R):    solid  ||  1419|1|0|-1

return to listing



Cr - 40 Fe (wt %) (New)

    DLL       :    liquid  ||  16351|0|1|-1
    MTE       :    liquid  ||  16351|8|1|-1
    CTE       :    liquid  ||  16351|16|1|-1
    D         :    liquid  ||  16351|24|1|-1

return to listing



Cr - 43 Ni (wt %) (New)

    DLL       :    liquid  ||  16347|0|1|-1
    MTE       :    liquid  ||  16347|8|1|-1
    CTE       :    liquid  ||  16347|16|1|-1
    D         :    liquid  ||  16347|24|1|-1

return to listing



Cu - 4 Ag (wt %)

    Vis    (N):    liquid  ||  16250|26|1|-1

return to listing



Cu - 6 Ag (wt %)

    Vis    (N):    liquid  ||  16251|26|1|-1

return to listing



Cu - 7 Ag (wt %)

    Vis    (N):    liquid  ||  854|26|1|-1

return to listing



Cu - 8 Ag (wt %)

    Vis    (N):    liquid  ||  16252|26|1|-1

return to listing



Cu - 90 Ce (at %) (New)

    SH        :    liquid  ||  16544|9|1|-1
    HC        :    liquid  ||  16544|17|1|-1

return to listing



Cu - 80 Ce (at %) (New)

    SH        :    liquid  ||  16545|9|1|-1
    HC        :    liquid  ||  16545|17|1|-1

return to listing



Cu - 71 Ce (at %) (New)

    SH        :    liquid  ||  16546|9|1|-1
    HC        :    liquid  ||  16546|17|1|-1

return to listing



Cu - 61 Ce (at %) (New)

    SH        :    liquid  ||  16547|9|1|-1
    HC        :    liquid  ||  16547|17|1|-1

return to listing



Cu - 50 Ce (at %) (New)

    SH        :    liquid  ||  16548|9|1|-1
    HC        :    liquid  ||  16548|17|1|-1

return to listing



Cu - 41 Ce (at %) (New)

    SH        :    liquid  ||  16549|9|1|-1
    HC        :    liquid  ||  16549|17|1|-1

return to listing



Cu - 30 Ce (at %) (New)

    SH        :    liquid  ||  16550|9|1|-1
    HC        :    liquid  ||  16550|17|1|-1

return to listing



Cu - 20 Ce (at %) (New)

    SH        :    liquid  ||  16551|9|1|-1
    HC        :    liquid  ||  16551|17|1|-1

return to listing



Cu - 20 Co (at %) (New)

    DLL       :    liquid  ||  16985|0|1|-1
    MTE       :    liquid  ||  16985|8|1|-1
    CTE       :    liquid  ||  16985|16|1|-1
    D         :    liquid  ||  16985|24|1|-1

return to listing



Cu - 20 Fe (at %) (New)

    DLL       :    liquid  ||  16992|0|1|-1
    MTE       :    liquid  ||  16992|8|1|-1
    CTE       :    liquid  ||  16992|16|1|-1
    D         :    liquid  ||  16992|24|1|-1

return to listing



Cu - 40 Fe (at %) (New)

    DLL       :    liquid  ||  16993|0|1|-1
    MTE       :    liquid  ||  16993|8|1|-1
    CTE       :    liquid  ||  16993|16|1|-1
    D         :    liquid  ||  16993|24|1|-1

return to listing



Cu - 20 Ni (wt %)

    DLL    (N):    liquid  ||  15293|0|1|-1
    MTE    (N):    liquid  ||  15293|8|1|-1
    CTE    (N):    liquid  ||  15293|16|1|-1
    D      (N):    liquid  ||  15293|24|1|-1

return to listing



Cu - 40 Ni (wt %)

    DLL    (N):    liquid  ||  15297|0|1|-1
    MTE    (N):    liquid  ||  15297|8|1|-1
    CTE    (N):    liquid  ||  15297|16|1|-1
    D      (N):    liquid  ||  15297|24|1|-1

return to listing



CuAl9Mn2 (New)

    DLL       :    solid  ||  16372|0|0|-1
    TC    (*):    solid  ||  16372|1|0|-1
    RHO   (*):    solid  ||  16372|2|0|-1
    E     (*):    solid  ||  16372|3|0|-1
    UTS       :    hot-rolled  ||  12 mm (0.472 inch) bar  ||  16372|5|0|0
    UTS       :    forged  ||  25 mm (0.984 inch) bar  ||  16372|5|1|0
    MTE       :    solid  ||  16372|8|0|-1
    SH    (*):    solid  ||  16372|9|0|-1
    SIGMA (*):    solid  ||  16372|10|0|-1
    G     (*):    solid  ||  16372|11|0|-1
    YS        :    forged  ||  25 mm (0.984 inch) bar  ||  16372|13|1|0
    CTE       :    solid  ||  16372|16|0|-1
    v     (*):    solid  ||  16372|19|0|-1
    D         :    solid  ||  16372|24|0|-1
    TD    (*):    solid  ||  16372|25|0|-1
    K     (*):    solid  ||  16372|27|0|-1
    %El       :    hot-rolled  ||  12 mm (0.472 inch) bar  ||  16372|29|0|0
    %El       :    forged  ||  25 mm (0.984 inch) bar  ||  16372|29|1|0

return to listing



CuAsSe2 (New)

    TC        :    solid  ||  16375|1|0|-1
    TC        :    liquid  ||  16375|1|1|-1
    D     (*):    solid  ||  tetragonal  ||  16375|24|0|0

return to listing



CuGe2P3

    DLL    (N):    solid  ||  stoichiometric  ||  15398|0|0|0
    MTE    (N):    solid  ||  stoichiometric  ||  15398|8|0|0
    CTE    (N):    solid  ||  stoichiometric  ||  15398|16|0|0
    D      (N):    solid  ||  stoichiometric  ||  15398|24|0|0

return to listing



CuSbS2 (New)

    TC        :    solid  ||  16374|1|0|-1
    TC        :    liquid  ||  16374|1|1|-1
    D     (*):    solid  ||  orthorhombic  ||  16374|24|0|0

return to listing



CuSbSe2 (Cd doped) (New)

    TC        :    undoped  ||  16430|1|0|-1
    TC        :    Cd-doped  ||  x = 0.02, CuSb0.98Cd0.02Se2  ||  16430|1|1|0
    TC        :    Cd-doped  ||  x = 0.04, CuSb0.96Cd0.04Se2  ||  16430|1|1|1
    TC        :    Cd-doped  ||  x = 0.06, CuSb0.94Cd0.05Se2  ||  16430|1|1|2
    TC        :    Cd-doped  ||  x = 0.08, CuSb0.92Cd0.08Se2  ||  16430|1|1|3
    RHO       :    undoped  ||  bulk  ||  16430|2|0|0
    RHO       :    undoped  ||  thin film, annealed 10 minutes at 420 °C (788 °F)  ||  16430|2|0|1
    RHO       :    Cd-doped  ||  x = 0.02, CuSb0.98Cd0.02Se2  ||  16430|2|1|0
    RHO       :    Cd-doped  ||  x = 0.04, CuSb0.96Cd0.04Se2  ||  16430|2|1|1
    RHO       :    Cd-doped  ||  x = 0.06, CuSb0.94Cd0.06Se2  ||  16430|2|1|2
    RHO       :    Cd-doped  ||  x = 0.08, CuSb0.92Cd0.08Se2  ||  16430|2|1|3
    SH    (*):    undoped  ||  16430|9|0|-1
    SH    (*):    Cd-doped  ||  x = 0.02, CuSb0.98Cd0.02Se2  ||  16430|9|1|0
    SH    (*):    Cd-doped  ||  x = 0.04, CuSb0.96Cd0.04Se2  ||  16430|9|1|1
    SH    (*):    Cd-doped  ||  x = 0.06, CuSb0.94Cd0.06Se2  ||  16430|9|1|2
    SH    (*):    Cd-doped  ||  x = 0.08, CuSb0.92Cd0.08Se2  ||  16430|9|1|3
    SIGMA     :    undoped  ||  bulk  ||  16430|10|0|0
    SIGMA     :    undoped  ||  thin film, annealed 10 minutes at 420 °C (788 °F)  ||  16430|10|0|1
    SIGMA     :    Cd-doped  ||  x = 0.02, CuSb0.98Cd0.02Se2  ||  16430|10|1|0
    SIGMA     :    Cd-doped  ||  x = 0.04, CuSb0.96Cd0.04Se2  ||  16430|10|1|1
    SIGMA     :    Cd-doped  ||  x = 0.06, CuSb0.94Cd0.06Se2  ||  16430|10|1|2
    SIGMA     :    Cd-doped  ||  x = 0.08, CuSb0.92Cd0.08Se2  ||  16430|10|1|3
    D     (*):    undoped  ||  16430|24|0|-1
    D     (*):    Cd-doped  ||  x = 0.02, CuSb0.98Cd0.02Se2  ||  16430|24|1|0
    D     (*):    Cd-doped  ||  x = 0.04, CuSb0.96Cd0.04Se2  ||  16430|24|1|1
    D     (*):    Cd-doped  ||  x = 0.06, CuSb0.94Cd0.06Se2  ||  16430|24|1|2
    D     (*):    Cd-doped  ||  x = 0.08, CuSb0.92Cd0.08Se2  ||  16430|24|1|3
    TD        :    undoped  ||  16430|25|0|-1
    TD        :    Cd-doped  ||  x = 0.02, CuSb0.98Cd0.02Se2  ||  16430|25|1|0
    TD        :    Cd-doped  ||  x = 0.04, CuSb0.96Cd0.04Se2  ||  16430|25|1|1
    TD        :    Cd-doped  ||  x = 0.06, CuSb0.94Cd0.05Se2  ||  16430|25|1|2
    TD        :    Cd-doped  ||  x = 0.08, CuSb0.92Cd0.08Se2  ||  16430|25|1|3
    S         :    undoped  ||  16430|48|0|-1
    S         :    Cd-doped  ||  x = 0.02, CuSb0.98Cd0.02Se2  ||  16430|48|1|0
    S         :    Cd-doped  ||  x = 0.04, CuSb0.96Cd0.04Se2  ||  16430|48|1|1
    S         :    Cd-doped  ||  x = 0.06, CuSb0.94Cd0.05Se2  ||  16430|48|1|2
    S         :    Cd-doped  ||  x = 0.08, CuSb0.92Cd0.08Se2  ||  16430|48|1|3

return to listing



Cu3SbSe4

    E     (N*):    solid  ||  2553|3|0|-1
    G     (N*):    solid  ||  2553|11|0|-1
    v     (N*):    solid  ||  2553|19|0|-1
    K     (N*):    solid  ||  2553|27|0|-1

return to listing



CuSbTe2

    TC     (R):    solid  ||  2554|1|0|-1
    TC     (R):    liquid  ||  2554|1|1|-1

return to listing



Dy(Fe1-xAlx)2 (New)

    DLL       :    solid  ||  DyFe2  ||  16563|0|0|0
    DLL       :    solid  ||  DyFe1.8Al0.2  ||  16563|0|0|1
    DLL       :    solid  ||  DyFe1.6Al0.4  ||  16563|0|0|2
    DLL       :    solid  ||  DyFe1.4Al0.6  ||  16563|0|0|3
    MTE       :    solid  ||  DyFe2  ||  16563|8|0|0
    MTE       :    solid  ||  DyFe1.8Al0.2  ||  16563|8|0|1
    MTE       :    solid  ||  DyFe1.6Al0.4  ||  16563|8|0|2
    MTE       :    solid  ||  DyFe1.4Al0.6  ||  16563|8|0|3
    CTE       :    solid  ||  DyFe2  ||  16563|16|0|0
    CTE       :    solid  ||  DyFe1.8Al0.2  ||  16563|16|0|1
    CTE       :    solid  ||  DyFe1.6Al0.4  ||  16563|16|0|2
    CTE       :    solid  ||  DyFe1.4Al0.6  ||  16563|16|0|3
    D         :    solid  ||  DyFe2  ||  16563|24|0|0

return to listing



E glass fiber

    TC    (N*):    solid  ||  3268|1|0|-1
    RHO    (N):    solid  ||  3268|2|0|-1
    SH     (N):    solid  ||  3268|9|0|-1
    SIGMA  (N):    solid  ||  3268|10|0|-1
    TD    (N*):    solid  ||  3268|25|0|-1
    DCRPT  (N):    annealed material  ||  tested at 23 °C (73 °F)  ||  3268|41|0|0
    DF     (N):    annealed material  ||  tested at 23 °C (73 °F)  ||  3268|42|0|0

return to listing



Fe - 0.5 Au (at %) (New)

    YS        :    quenched from 1000 °C (1832 °F)  ||  16378|13|0|-1
    D     (*):    solid  ||  16378|24|0|-1

return to listing



Fe - 20 Co (at %) (New)

    DLL       :    liquid  ||  16988|0|1|-1
    MTE       :    liquid  ||  16988|8|1|-1
    CTE       :    liquid  ||  16988|16|1|-1
    D         :    liquid  ||  16988|24|1|-1

return to listing



Fe - 30 Co (at %) (New)

    DLL       :    liquid  ||  16800|0|1|-1
    MTE       :    liquid  ||  16800|8|1|-1
    CTE       :    liquid  ||  16800|16|1|-1
    D         :    liquid  ||  16800|24|1|-1

return to listing



Fe - 40 Co (at %) (New)

    DLL       :    liquid  ||  16801|0|1|-1
    MTE       :    liquid  ||  16801|8|1|-1
    CTE       :    liquid  ||  16801|16|1|-1
    D         :    liquid  ||  16801|24|1|-1

return to listing



Fe - 50 Co (at %) (New)

    DLL       :    liquid  ||  16436|0|1|-1
    MTE       :    liquid  ||  16436|8|1|-1
    SSCC      :    disordered  ||  tested at -196.1 °C (-321.1 °F), 7.6 x 10-5/s  ||  16436|12|0|0
    SSCC      :    disordered  ||  tested at -173 °C (-280 °F), 7.6 x 10-5/s  ||  16436|12|0|1
    SSCC      :    disordered  ||  tested at -150 °C (-238 °F), 7.6 x 10-5/s  ||  16436|12|0|2
    SSCC      :    disordered  ||  tested at -103 °C (-154 °F), 7.6 x 10-5/s  ||  16436|12|0|3
    SSCC      :    disordered  ||  tested at -65 °C (-85 °F), 7.6 x 10-5/s  ||  16436|12|0|4
    SSCC      :    disordered  ||  tested at 25 °C (77 °F), 7.6 x 10-5/s  ||  16436|12|0|5
    SSCC      :    disordered  ||  tested at 120 °C (248 °F), 7.6 x 10-5/s  ||  16436|12|0|6
    SSCC      :    ordered  ||  tested at -196.1 °C (-321.1 °F), 7.6 x 10-5/s  ||  16436|12|1|0
    SSCC      :    ordered  ||  tested at -173 °C (-280 °F), 7.6 x 10-5/s  ||  16436|12|1|1
    SSCC      :    ordered  ||  tested at -150 °C (-238 °F), 7.6 x 10-5/s  ||  16436|12|1|2
    SSCC      :    ordered  ||  tested at -103 °C (-154 °F), 7.6 x 10-5/s  ||  16436|12|1|3
    SSCC      :    ordered  ||  tested at -65 °C (-85 °F), 7.6 x 10-5/s  ||  16436|12|1|4
    SSCC      :    ordered  ||  tested at 21 °C (70 °F), 7.6 x 10-5/s  ||  16436|12|1|5
    SSCC      :    ordered  ||  tested at 103 °C (217 °F), 7.6 x 10-5/s  ||  16436|12|1|6
    SSCC      :    ordered  ||  tested at 176 °C (349 °F), 7.6 x 10-5/s  ||  16436|12|1|7
    SSCC      :    ordered  ||  tested at 307 °C (584 °F), 7.6 x 10-5/s  ||  16436|12|1|8
    CTE       :    liquid  ||  16436|16|1|-1
    YSC       :    disordered  ||  16436|21|0|-1
    YSC       :    ordered  ||  16436|21|1|-1
    D         :    liquid  ||  16436|24|1|-1

return to listing



Fe - 8 Co (at %) (New)

    E         :    solid  ||  16409|3|0|-1
    G         :    solid  ||  16409|11|0|-1
    v         :    solid  ||  16409|19|0|-1
    D     (*):    solid  ||  16409|24|0|-1
    K         :    solid  ||  16409|27|0|-1

return to listing



Fe - 40 Cr (at %) (New)

    DLL       :    liquid  ||  16350|0|1|-1
    MTE       :    liquid  ||  16350|8|1|-1
    CTE       :    liquid  ||  16350|16|1|-1
    D         :    liquid  ||  16350|24|1|-1

return to listing



Fe - 10 Cr (at %) (New)

    DLL       :    liquid  ||  16348|0|1|-1
    E         :    solid  ||  16348|3|0|-1
    MTE       :    liquid  ||  16348|8|1|-1
    G         :    solid  ||  16348|11|0|-1
    CTE       :    liquid  ||  16348|16|1|-1
    v         :    solid  ||  16348|19|0|-1
    D     (*):    solid  ||  16348|24|0|-1
    D         :    liquid  ||  16348|24|1|-1
    K         :    solid  ||  16348|27|0|-1

return to listing



Fe - 20 Cr (at %) (New)

    DLL       :    liquid  ||  16349|0|1|-1
    MTE       :    liquid  ||  16349|8|1|-1
    CTE       :    liquid  ||  16349|16|1|-1
    D         :    liquid  ||  16349|24|1|-1

return to listing



Fe - 40 Cu (at %) (New)

    DLL       :    liquid  ||  16995|0|1|-1
    MTE       :    liquid  ||  16995|8|1|-1
    CTE       :    liquid  ||  16995|16|1|-1
    D         :    liquid  ||  16995|24|1|-1

return to listing



Fe - 1.67 Cu (at %) (New)

    YS        :    quenched from 1000 °C (1832 °F), aged at 475 °C (887 °F)  ||  not aged  ||  16379|13|0|0
    YS        :    quenched from 1000 °C (1832 °F), aged at 475 °C (887 °F)  ||  aged 0.5 h  ||  16379|13|0|1
    YS        :    quenched from 1000 °C (1832 °F), aged at 475 °C (887 °F)  ||  aged 1 h  ||  16379|13|0|2
    YS        :    quenched from 1000 °C (1832 °F), aged at 475 °C (887 °F)  ||  aged 2 h  ||  16379|13|0|3
    YS        :    quenched from 1000 °C (1832 °F), aged at 475 °C (887 °F)  ||  aged 3 h  ||  16379|13|0|4
    YS        :    quenched from 1000 °C (1832 °F), aged at 475 °C (887 °F)  ||  aged 6.5 h  ||  16379|13|0|5
    D     (*):    solid  ||  16379|24|0|-1

return to listing



Fe - 20 Cu (at %) (New)

    DLL       :    liquid  ||  16994|0|1|-1
    MTE       :    liquid  ||  16994|8|1|-1
    CTE       :    liquid  ||  16994|16|1|-1
    D         :    liquid  ||  16994|24|1|-1

return to listing



Fe - 3 Ir (at %) (New)

    E         :    solid  ||  16412|3|0|-1
    G         :    solid  ||  16412|11|0|-1
    v         :    solid  ||  16412|19|0|-1
    D     (*):    solid  ||  16412|24|0|-1
    K         :    solid  ||  16412|27|0|-1

return to listing



Fe - 10 Mn - 1.6 C (wt %) (New)

    DLL       :    liquid  ||  16699|0|1|-1
    MTE       :    liquid  ||  16699|8|1|-1
    CTE       :    liquid  ||  16699|16|1|-1
    D         :    liquid  ||  16699|24|1|-1

return to listing



Fe - 10 Mn - 4.1 C (wt %) (New)

    DLL       :    liquid  ||  16700|0|1|-1
    MTE       :    liquid  ||  16700|8|1|-1
    CTE       :    liquid  ||  16700|16|1|-1
    D         :    liquid  ||  16700|24|1|-1

return to listing



Fe - 5 Mn - 1.5 C (wt %) (New)

    DLL       :    liquid  ||  16697|0|1|-1
    MTE       :    liquid  ||  16697|8|1|-1
    CTE       :    liquid  ||  16697|16|1|-1
    D         :    liquid  ||  16697|24|1|-1

return to listing



Fe - 5 Mn - 4.2 C (wt %) (New)

    DLL       :    liquid  ||  16698|0|1|-1
    MTE       :    liquid  ||  16698|8|1|-1
    CTE       :    liquid  ||  16698|16|1|-1
    D         :    liquid  ||  16698|24|1|-1

return to listing



Fe - 3 Mn (at %) (New)

    E         :    solid  ||  16414|3|0|-1
    G         :    solid  ||  16414|11|0|-1
    v         :    solid  ||  16414|19|0|-1
    D     (*):    solid  ||  16414|24|0|-1
    K         :    solid  ||  16414|27|0|-1

return to listing



Fe - 10 Mn (wt %)

    DLL    (N):    liquid  ||  16682|0|1|-1
    MTE    (N):    liquid  ||  16682|8|1|-1
    CTE    (N):    liquid  ||  16682|16|1|-1
    D      (N):    liquid  ||  16682|24|1|-1

return to listing



Fe - 3 Mn (wt %)

    DLL    (N):    liquid  ||  16680|0|1|-1
    MTE    (N):    liquid  ||  16680|8|1|-1
    CTE    (N):    liquid  ||  16680|16|1|-1
    D      (N):    liquid  ||  16680|24|1|-1

return to listing



Fe - 5 Mn (wt %)

    DLL    (N):    liquid  ||  16681|0|1|-1
    MTE    (N):    liquid  ||  16681|8|1|-1
    CTE    (N):    liquid  ||  16681|16|1|-1
    D      (N):    liquid  ||  16681|24|1|-1

return to listing



Fe - 6 Ni - 0.2 C (wt %) (New)

    YS        :    tempered martensite  ||  tempered at 250 °C (482 °F)  ||  16407|13|0|0
    YSC       :    tempered martensite  ||  tempered at 250 °C (482 °F)  ||  16407|21|0|0

return to listing



Fe - 3 Ni (wt %)

    E      (N):    solid  ||  ferrite  ||  16104|3|0|0
    E     (N*):    solid  ||  martensite  ||  16104|3|0|1
    G      (N):    solid  ||  ferrite  ||  16104|11|0|0
    G     (N*):    solid  ||  martensite  ||  16104|11|0|1
    v      (N):    solid  ||  ferrite  ||  16104|19|0|0
    v     (N*):    solid  ||  martensite  ||  16104|19|0|1
    K      (N):    solid  ||  ferrite  ||  16104|27|0|0
    K     (N*):    solid  ||  martensite  ||  16104|27|0|1

return to listing



Fe - 5 Ni (wt %)

    E     (N*):    solid  ||  martensite  ||  16105|3|0|0
    G     (N*):    solid  ||  martensite  ||  16105|11|0|0
    v     (N*):    solid  ||  martensite  ||  16105|19|0|0
    K     (N*):    solid  ||  martensite  ||  16105|27|0|0

return to listing



Fe - 10 Ni (wt %)

    E     (N*):    solid  ||  martensite  ||  16106|3|0|0
    G     (N*):    solid  ||  martensite  ||  16106|11|0|0
    v     (N*):    solid  ||  martensite  ||  16106|19|0|0
    K     (N*):    solid  ||  martensite  ||  16106|27|0|0

return to listing



Fe - 20 Ni (wt %)

    DLL    (N):    liquid  ||  16108|0|1|-1
    E     (N*):    solid  ||  martensite  ||  16108|3|0|0
    MTE    (N):    liquid  ||  16108|8|1|-1
    G     (N*):    solid  ||  martensite  ||  16108|11|0|0
    CTE    (N):    liquid  ||  16108|16|1|-1
    v     (N*):    solid  ||  martensite  ||  16108|19|0|0
    D      (N):    liquid  ||  16108|24|1|-1
    K     (N*):    solid  ||  martensite  ||  16108|27|0|0

return to listing



Fe - 30 Ni (wt %)

    DLL    (N):    liquid  ||  16110|0|1|-1
    MTE    (N):    liquid  ||  16110|8|1|-1
    CTE    (N):    liquid  ||  16110|16|1|-1
    D      (N):    liquid  ||  16110|24|1|-1

return to listing



Fe - 40 Ni (wt %)

    DLL    (N):    liquid  ||  16112|0|1|-1
    MTE    (N):    liquid  ||  16112|8|1|-1
    CTE    (N):    liquid  ||  16112|16|1|-1
    D      (N):    liquid  ||  16112|24|1|-1

return to listing



Fe - 0.5 Ni (wt %)

    E     (N*):    solid  ||  martensite  ||  16102|3|0|0
    G     (N*):    solid  ||  martensite  ||  16102|11|0|0
    v     (N*):    solid  ||  martensite  ||  16102|19|0|0
    K     (N*):    solid  ||  martensite  ||  16102|27|0|0

return to listing



Fe - 1 Ni (wt %)

    E     (N*):    solid  ||  ferrite  ||  16103|3|0|0
    E     (N*):    solid  ||  martensite  ||  16103|3|0|1
    G     (N*):    solid  ||  ferrite  ||  16103|11|0|0
    G     (N*):    solid  ||  martensite  ||  16103|11|0|1
    v     (N*):    solid  ||  ferrite  ||  16103|19|0|0
    v     (N*):    solid  ||  martensite  ||  16103|19|0|1
    K     (N*):    solid  ||  ferrite  ||  16103|27|0|0
    K     (N*):    solid  ||  martensite  ||  16103|27|0|1

return to listing



Fe - 34 Ni (wt %) (New)

    SSC       :    deformed 70% at 25 °C (77 °F)  ||  tested at -78 °C (-108 °F), 6.7 x 10-4/s  ||  16435|4|0|0
    SSC       :    deformed 70% at 450 °C (842 °F)  ||  tested at -196 °C (-320.8 °F), 6.7 x 10-4/s  ||  16435|4|1|0
    SSC       :    deformed 70% at 450 °C (842 °F)  ||  tested at 22 °C (72 °F), 6.7 x 10-4/s  ||  16435|4|1|1

return to listing



Fe - 3 Pt (at %) (New)

    E         :    solid  ||  16415|3|0|-1
    G         :    solid  ||  16415|11|0|-1
    v         :    solid  ||  16415|19|0|-1
    D     (*):    solid  ||  16415|24|0|-1
    K         :    solid  ||  16415|27|0|-1

return to listing



Fe - 5 Pt (at %) (New)

    E         :    solid  ||  16416|3|0|-1
    G         :    solid  ||  16416|11|0|-1
    v         :    solid  ||  16416|19|0|-1
    D     (*):    solid  ||  16416|24|0|-1
    K         :    solid  ||  16416|27|0|-1

return to listing



Fe - 10 Pt (at %) (New)

    E         :    solid  ||  16413|3|0|-1
    G         :    solid  ||  16413|11|0|-1
    v         :    solid  ||  16413|19|0|-1
    D     (*):    solid  ||  16413|24|0|-1
    K         :    solid  ||  16413|27|0|-1

return to listing



Fe - 3 Re (at %) (New)

    E         :    solid  ||  16417|3|0|-1
    G         :    solid  ||  16417|11|0|-1
    v         :    solid  ||  16417|19|0|-1
    D     (*):    solid  ||  16417|24|0|-1
    K         :    solid  ||  16417|27|0|-1

return to listing



Fe - 6 Re (at %) (New)

    E         :    solid  ||  16408|3|0|-1
    G         :    solid  ||  16408|11|0|-1
    v         :    solid  ||  16408|19|0|-1
    D     (*):    solid  ||  16408|24|0|-1
    K         :    solid  ||  16408|27|0|-1

return to listing



Fe - 3 Rh (at %) (New)

    E         :    solid  ||  16418|3|0|-1
    G         :    solid  ||  16418|11|0|-1
    v         :    solid  ||  16418|19|0|-1
    D     (*):    solid  ||  16418|24|0|-1
    K         :    solid  ||  16418|27|0|-1

return to listing



Fe - 6 Rh (at %) (New)

    E         :    solid  ||  16419|3|0|-1
    G         :    solid  ||  16419|11|0|-1
    v         :    solid  ||  16419|19|0|-1
    D     (*):    solid  ||  16419|24|0|-1
    K         :    solid  ||  16419|27|0|-1

return to listing



Fe - 8 Rh (at %) (New)

    E         :    solid  ||  16420|3|0|-1
    G         :    solid  ||  16420|11|0|-1
    v         :    solid  ||  16420|19|0|-1
    D     (*):    solid  ||  16420|24|0|-1
    K         :    solid  ||  16420|27|0|-1

return to listing



Fe - 6 Ru (at %) (New)

    E         :    solid  ||  16410|3|0|-1
    G         :    solid  ||  16410|11|0|-1
    v         :    solid  ||  16410|19|0|-1
    D     (*):    solid  ||  16410|24|0|-1
    K         :    solid  ||  16410|27|0|-1

return to listing



Fe - 9 Ru (at %) (New)

    E         :    solid  ||  16411|3|0|-1
    G         :    solid  ||  16411|11|0|-1
    v         :    solid  ||  16411|19|0|-1
    D     (*):    solid  ||  16411|24|0|-1
    K         :    solid  ||  16411|27|0|-1

return to listing



Fe65Cu20Ni15 (New)

    DLL       :    liquid  ||  16999|0|1|-1
    MTE       :    liquid  ||  16999|8|1|-1
    CTE       :    liquid  ||  16999|16|1|-1
    D         :    liquid  ||  16999|24|1|-1

return to listing



Fe48Cu20Ni32 (New)

    DLL       :    liquid  ||  17000|0|1|-1
    MTE       :    liquid  ||  17000|8|1|-1
    CTE       :    liquid  ||  17000|16|1|-1
    D         :    liquid  ||  17000|24|1|-1

return to listing



29.6 FeO - 36.9 CaO - 33.5 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16394|0|1|-1
    MTE       :    liquid  ||  16394|8|1|-1
    CTE       :    liquid  ||  16394|16|1|-1
    D         :    liquid  ||  16394|24|1|-1

return to listing



27 FeO - 26.5 CaO - 46.5 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16397|0|1|-1
    RHO       :    liquid  ||  16397|2|1|-1
    MTE       :    liquid  ||  16397|8|1|-1
    SIGMA     :    liquid  ||  16397|10|1|-1
    CTE       :    liquid  ||  16397|16|1|-1
    D         :    liquid  ||  16397|24|1|-1

return to listing



26 FeO - 38 CaO - 36 SiO2 (mol %) slag (New)

    RHO       :    liquid  ||  16612|2|1|-1
    SIGMA     :    liquid  ||  16612|10|1|-1

return to listing



25 FeO - 51 CaO - 24 SiO2 (mol %) slag (New)

    RHO       :    liquid  ||  16613|2|1|-1
    SIGMA     :    liquid  ||  16613|10|1|-1

return to listing



62.3 FeO - 4.5 CaO - 33.2 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16389|0|1|-1
    MTE       :    liquid  ||  16389|8|1|-1
    CTE       :    liquid  ||  16389|16|1|-1
    D         :    liquid  ||  16389|24|1|-1

return to listing



62.2 FeO - 5.2 CaO - 32.6 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16390|0|1|-1
    MTE       :    liquid  ||  16390|8|1|-1
    CTE       :    liquid  ||  16390|16|1|-1
    D         :    liquid  ||  16390|24|1|-1

return to listing



57.4 FeO - 9.3 CaO - 33.3 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16391|0|1|-1
    MTE       :    liquid  ||  16391|8|1|-1
    CTE       :    liquid  ||  16391|16|1|-1
    D         :    liquid  ||  16391|24|1|-1

return to listing



51.5 FeO - 13.5 CaO - 35 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16392|0|1|-1
    MTE       :    liquid  ||  16392|8|1|-1
    CTE       :    liquid  ||  16392|16|1|-1
    D         :    liquid  ||  16392|24|1|-1

return to listing



46 FeO - 9.6 CaO - 44.4 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16395|0|1|-1
    MTE       :    liquid  ||  16395|8|1|-1
    CTE       :    liquid  ||  16395|16|1|-1
    D         :    liquid  ||  16395|24|1|-1

return to listing



39 FeO - 28.5 CaO - 32.5 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16393|0|1|-1
    MTE       :    liquid  ||  16393|8|1|-1
    CTE       :    liquid  ||  16393|16|1|-1
    D         :    liquid  ||  16393|24|1|-1

return to listing



37.1 FeO - 18.2 CaO - 44.7 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16396|0|1|-1
    MTE       :    liquid  ||  16396|8|1|-1
    CTE       :    liquid  ||  16396|16|1|-1
    D         :    liquid  ||  16396|24|1|-1

return to listing



65.1 FeO - 5.2 Fe2O3 - 29.7 CaO (mol %) (New)

    DLL       :    liquid  ||  16405|0|1|-1
    MTE       :    liquid  ||  16405|8|1|-1
    CTE       :    liquid  ||  16405|16|1|-1
    D         :    liquid  ||  16405|24|1|-1

return to listing



57.3 FeO - 5.6 Fe2O3 - 37.1 CaO (mol %) (New)

    DLL       :    liquid  ||  16406|0|1|-1
    MTE       :    liquid  ||  16406|8|1|-1
    CTE       :    liquid  ||  16406|16|1|-1
    D         :    liquid  ||  16406|24|1|-1

return to listing



90.7 FeO - 4.1 Fe2O3 - 5.2 CaO (mol %) (New)

    DLL       :    liquid  ||  16400|0|1|-1
    MTE       :    liquid  ||  16400|8|1|-1
    CTE       :    liquid  ||  16400|16|1|-1
    D         :    liquid  ||  16400|24|1|-1

return to listing



85.7 FeO - 4.3 Fe2O3 - 10 CaO (mol %) (New)

    DLL       :    liquid  ||  16401|0|1|-1
    MTE       :    liquid  ||  16401|8|1|-1
    CTE       :    liquid  ||  16401|16|1|-1
    D         :    liquid  ||  16401|24|1|-1

return to listing



80.1 FeO - 4.5 Fe2O3 - 15.4 CaO (mol %) (New)

    DLL       :    liquid  ||  16402|0|1|-1
    MTE       :    liquid  ||  16402|8|1|-1
    CTE       :    liquid  ||  16402|16|1|-1
    D         :    liquid  ||  16402|24|1|-1

return to listing



74.4 FeO - 4.8 Fe2O3 - 20.8 CaO (mol %) (New)

    DLL       :    liquid  ||  16403|0|1|-1
    MTE       :    liquid  ||  16403|8|1|-1
    CTE       :    liquid  ||  16403|16|1|-1
    D         :    liquid  ||  16403|24|1|-1

return to listing



69.9 FeO - 5 Fe2O3 - 25.1 CaO (mol %) (New)

    DLL       :    liquid  ||  16404|0|1|-1
    MTE       :    liquid  ||  16404|8|1|-1
    CTE       :    liquid  ||  16404|16|1|-1
    D         :    liquid  ||  16404|24|1|-1

return to listing



35.6 FeO - 20.2 Fe2O3 - 34.22 SiO2 - 10 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16691|26|1|-1

return to listing



35.7 FeO - 17 Fe2O3 - 32.32 SiO2 - 15 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16692|26|1|-1

return to listing



42.1 FeO - 26.3 Fe2O3 - 26.6 SiO2 - 5 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16684|26|1|-1

return to listing



39.6 FeO - 25.2 Fe2O3 - 25.2 SiO2 - 10 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16685|26|1|-1

return to listing



35.5 FeO - 29.2 Fe2O3 - 30.35 SiO2 - 5 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16687|26|1|-1

return to listing



35.7 FeO - 25.6 Fe2O3 - 28.75 SiO2 - 10 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16688|26|1|-1

return to listing



31.8 FeO - 27.1 Fe2O3 - 36.12 SiO2 - 5 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16690|26|1|-1

return to listing



42.6 FeO - 29.4 Fe2O3 - 28 SiO2 (wt %) slag (New)

    Vis       :    liquid  ||  16683|26|1|-1

return to listing



41.4 FeO - 26.6 Fe2O3 - 32 SiO2 (wt %) slag (New)

    Vis       :    liquid  ||  16686|26|1|-1

return to listing



44.2 FeO - 17.8 Fe2O3 - 38 SiO2 (wt %) slag (New)

    Vis       :    liquid  ||  16689|26|1|-1

return to listing



96.2 FeO - 3.8 Fe2O3 (mol %) (New)

    DLL       :    liquid  ||  16399|0|1|-1
    MTE       :    liquid  ||  16399|8|1|-1
    CTE       :    liquid  ||  16399|16|1|-1
    D         :    liquid  ||  16399|24|1|-1

return to listing



49.46 FeO - 40.54 SiO2 - 10 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16694|26|1|-1

return to listing



46.71 FeO - 38.29 SiO2 - 15 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16695|26|1|-1

return to listing



43.96 FeO - 36.04 SiO2 - 20 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16696|26|1|-1

return to listing



52.21 FeO - 42.79 SiO2 - 5 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16693|26|1|-1

return to listing



61 FeO - 29 SiO2 - 6 Fe2O3 - 2.5 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16948|26|1|-1

return to listing



59 FeO - 29 SiO2 - 8 Fe2O3 - 2.6 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16949|26|1|-1

return to listing



63 FeO - 29 SiO2 - 4.6 Fe2O3 - 2.6 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16950|26|1|-1

return to listing



64 FeO - 29 SiO2 - 4 Fe2O3 - 2.5 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16947|26|1|-1

return to listing



56.6 FeO - 43.4 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16398|0|1|-1
    MTE       :    liquid  ||  16398|8|1|-1
    CTE       :    liquid  ||  16398|16|1|-1
    D         :    liquid  ||  16398|24|1|-1

return to listing



66 FeO - 34 SiO2 (mol %) slag (New)

    DLL       :    liquid  ||  16388|0|1|-1
    MTE       :    liquid  ||  16388|8|1|-1
    CTE       :    liquid  ||  16388|16|1|-1
    D         :    liquid  ||  16388|24|1|-1

return to listing



Fe2VAl (Si, Sn, Ta, Ti, & W doped)

    TC     (N):    Ta doped  ||  Fe2V0.98Ta0.1Al0.92  ||  15602|1|2|0
    RHO    (N):    Ta doped  ||  Fe2V0.98Ta0.1Al0.92  ||  15602|2|2|0
    SIGMA  (N):    Ta doped  ||  Fe2V0.98Ta0.1Al0.92  ||  15602|10|2|0
    S      (N):    Ta doped  ||  Fe2V0.98Ta0.1Al0.92  ||  15602|48|2|0

return to listing



GaFeO3 (Sm doped) (New)

    RHO       :    un-doped  ||  GaFeO3  ||  16365|2|0|0
    RHO       :    Sm doped  ||  x = 0.05, GaFe0.95Sm0.05O3  ||  16365|2|1|0
    RHO       :    Sm doped  ||  x = 0.1, GaFe0.9Sm0.1O3  ||  16365|2|1|1
    RHO       :    Sm doped  ||  x = 0.15, GaFe0.85Sm0.15O3  ||  16365|2|1|2
    SIGMA     :    un-doped  ||  GaFeO3  ||  16365|10|0|0
    SIGMA     :    Sm doped  ||  x = 0.05, GaFe0.95Sm0.05O3  ||  16365|10|1|0
    SIGMA     :    Sm doped  ||  x = 0.1, GaFe0.9Sm0.1O3  ||  16365|10|1|1
    SIGMA     :    Sm doped  ||  x = 0.15, GaFe0.85Sm0.15O3  ||  16365|10|1|2

return to listing



Ge26InxSe74-x glass (New)

    RHO       :    glass thin film  ||  x = 0.7, Ge26.6In0.7Se72.7  ||  16366|2|0|0
    RHO       :    glass thin film  ||  x = 2.4, Ge25.4In2.4Se72.2  ||  16366|2|0|1
    RHO       :    glass thin film  ||  x = 2.9, Ge27.8In2.9Se69.3  ||  16366|2|0|2
    RHO       :    glass thin film  ||  x = 4.8, Ge25.8In4.8Se69.4  ||  16366|2|0|3
    SIGMA     :    glass thin film  ||  x = 0.7, Ge26.6In0.7Se72.7  ||  16366|10|0|0
    SIGMA     :    glass thin film  ||  x = 2.4, Ge25.4In2.4Se72.2  ||  16366|10|0|1
    SIGMA     :    glass thin film  ||  x = 2.9, Ge27.8In2.9Se69.3  ||  16366|10|0|2
    SIGMA     :    glass thin film  ||  x = 4.8, Ge25.8In4.8Se69.4  ||  16366|10|0|3

return to listing



Ge20Sb10Se70 glass (New)

    TC        :    glass  ||  17001|1|0|-1
    TD        :    glass  ||  17001|25|0|-1

return to listing



Ge15Sb15Se70 glass (New)

    TC        :    glass  ||  17002|1|0|-1
    TD        :    glass  ||  17002|25|0|-1

return to listing



Ge10Sb20Se70 glass (New)

    TC        :    glass  ||  17003|1|0|-1
    TD        :    glass  ||  17003|25|0|-1

return to listing



Ge5Sb25Se70 glass (New)

    TC        :    glass  ||  17004|1|0|-1
    TD        :    glass  ||  17004|25|0|-1

return to listing



H13

    SSC    (N):    laser powder bed fusion  ||  tested at 600 °C (1112 °F), 7.25 x 10-4/s, as-built, scan direction  ||  2864|4|1|4
    SSC    (N):    laser powder bed fusion  ||  tested at 600 °C (1112 °F), 7.25 x 10-4/s, as-built, build direction  ||  2864|4|1|5
    SSC    (N):    laser powder bed fusion  ||  tested at 600 °C (1112 °F), 7.25 x 10-4/s, tempered at 600 °C (1112 °F), scan direction  ||  2864|4|1|6
    SSC    (N):    laser powder bed fusion  ||  tested at 600 °C (1112 °F), 7.25 x 10-4/s, tempered at 600 °C (1112 °F), build direction  ||  2864|4|1|7

return to listing



HfC

    NE     (N):    solid  ||  Fisenko and Lemberg  ||  187|28|0|1

return to listing



In - 3 Ag (wt %)

    ST     (N):    liquid  ||  2754|38|1|-1

return to listing



In - 19 Ag (wt %) (New)

    DLL       :    liquid  ||  16353|0|1|-1
    MTE       :    liquid  ||  16353|8|1|-1
    CTE       :    liquid  ||  16353|16|1|-1
    D         :    liquid  ||  16353|24|1|-1
    ST        :    liquid  ||  16353|38|1|-1

return to listing



In - 40.5 Ag (wt %) (New)

    DLL       :    liquid  ||  16354|0|1|-1
    MTE       :    liquid  ||  16354|8|1|-1
    CTE       :    liquid  ||  16354|16|1|-1
    D         :    liquid  ||  16354|24|1|-1
    ST        :    liquid  ||  16354|38|1|-1

return to listing



In - 53 Ag (wt %) (New)

    DLL       :    liquid  ||  16355|0|1|-1
    MTE       :    liquid  ||  16355|8|1|-1
    CTE       :    liquid  ||  16355|16|1|-1
    D         :    liquid  ||  16355|24|1|-1
    ST        :    liquid  ||  16355|38|1|-1

return to listing



In - 63.6 Ag (wt %) (New)

    DLL       :    liquid  ||  16356|0|1|-1
    MTE       :    liquid  ||  16356|8|1|-1
    CTE       :    liquid  ||  16356|16|1|-1
    D         :    liquid  ||  16356|24|1|-1
    ST        :    liquid  ||  16356|38|1|-1

return to listing



In - 79 Ag (wt %) (New)

    DLL       :    liquid  ||  16357|0|1|-1
    MTE       :    liquid  ||  16357|8|1|-1
    CTE       :    liquid  ||  16357|16|1|-1
    D         :    liquid  ||  16357|24|1|-1
    ST        :    liquid  ||  16357|38|1|-1

return to listing



In - 48.1 Sn (at %)

    DLL    (N):    liquid  ||  2753|0|1|-1
    MTE    (N):    liquid  ||  2753|8|1|-1
    CTE    (N):    liquid  ||  2753|16|1|-1
    D      (N):    liquid  ||  2753|24|1|-1
    ST     (N):    liquid  ||  2753|38|1|-1

return to listing



In - 55 Sn (at %)

    DLL    (N):    liquid  ||  9574|0|1|-1
    MTE    (N):    liquid  ||  9574|8|1|-1
    CTE    (N):    liquid  ||  9574|16|1|-1
    D      (N):    liquid  ||  9574|24|1|-1
    ST     (N):    liquid  ||  9574|38|1|-1

return to listing



In - 75 Sn (at %)

    DLL    (N):    liquid  ||  9575|0|1|-1
    MTE    (N):    liquid  ||  9575|8|1|-1
    CTE    (N):    liquid  ||  9575|16|1|-1
    D      (N):    liquid  ||  9575|24|1|-1
    ST     (N):    liquid  ||  9575|38|1|-1

return to listing



In - 83 Sn (at %)

    DLL    (N):    liquid  ||  2752|0|1|-1
    MTE    (N):    liquid  ||  2752|8|1|-1
    CTE    (N):    liquid  ||  2752|16|1|-1
    D      (N):    liquid  ||  2752|24|1|-1
    ST     (N):    liquid  ||  2752|38|1|-1

return to listing



In - 14.7 Sn (at %)

    DLL    (N):    liquid  ||  9566|0|1|-1
    MTE    (N):    liquid  ||  9566|8|1|-1
    CTE    (N):    liquid  ||  9566|16|1|-1
    D      (N):    liquid  ||  9566|24|1|-1
    ST     (N):    liquid  ||  9566|38|1|-1

return to listing



In - 21.3 Sn (at %)

    DLL    (N):    liquid  ||  9567|0|1|-1
    MTE    (N):    liquid  ||  9567|8|1|-1
    CTE    (N):    liquid  ||  9567|16|1|-1
    D      (N):    liquid  ||  9567|24|1|-1
    ST     (N):    liquid  ||  9567|38|1|-1

return to listing



In - 25.3 Sn (at %)

    DLL    (N):    liquid  ||  9568|0|1|-1
    MTE    (N):    liquid  ||  9568|8|1|-1
    CTE    (N):    liquid  ||  9568|16|1|-1
    D      (N):    liquid  ||  9568|24|1|-1
    ST     (N):    liquid  ||  9568|38|1|-1

return to listing



In - 30.24 Sn (at %)

    DLL    (N):    liquid  ||  9569|0|1|-1
    MTE    (N):    liquid  ||  9569|8|1|-1
    CTE    (N):    liquid  ||  9569|16|1|-1
    D      (N):    liquid  ||  9569|24|1|-1
    ST     (N):    liquid  ||  9569|38|1|-1

return to listing



In - 36 Sn (at %)

    DLL    (N):    liquid  ||  9570|0|1|-1
    MTE    (N):    liquid  ||  9570|8|1|-1
    CTE    (N):    liquid  ||  9570|16|1|-1
    D      (N):    liquid  ||  9570|24|1|-1
    ST     (N):    liquid  ||  9570|38|1|-1

return to listing



In - 42 Sn (at %)

    DLL    (N):    liquid  ||  9571|0|1|-1
    MTE    (N):    liquid  ||  9571|8|1|-1
    CTE    (N):    liquid  ||  9571|16|1|-1
    D      (N):    liquid  ||  9571|24|1|-1
    ST     (N):    liquid  ||  9571|38|1|-1

return to listing



In - 42.5 Sn (at %)

    DLL    (N):    liquid  ||  9572|0|1|-1
    MTE    (N):    liquid  ||  9572|8|1|-1
    CTE    (N):    liquid  ||  9572|16|1|-1
    D      (N):    liquid  ||  9572|24|1|-1
    ST     (N):    liquid  ||  9572|38|1|-1

return to listing



In - 47.22 Sn (at %)

    DLL    (N):    liquid  ||  9573|0|1|-1
    MTE    (N):    liquid  ||  9573|8|1|-1
    CTE    (N):    liquid  ||  9573|16|1|-1
    D      (N):    liquid  ||  9573|24|1|-1
    ST     (N):    liquid  ||  9573|38|1|-1

return to listing



In - 70 Sn (at %) (New)

    DLL       :    liquid  ||  16566|0|1|-1
    MTE       :    liquid  ||  16566|8|1|-1
    CTE       :    liquid  ||  16566|16|1|-1
    D         :    liquid  ||  16566|24|1|-1
    ST        :    liquid  ||  16566|38|1|-1

return to listing



In - 50 Sn (at %) (New)

    DLL       :    liquid  ||  16565|0|1|-1
    MTE       :    liquid  ||  16565|8|1|-1
    CTE       :    liquid  ||  16565|16|1|-1
    D         :    liquid  ||  16565|24|1|-1
    ST        :    liquid  ||  16565|38|1|-1

return to listing



In - 10 Sn (at %) (New)

    DLL       :    liquid  ||  16564|0|1|-1
    MTE       :    liquid  ||  16564|8|1|-1
    CTE       :    liquid  ||  16564|16|1|-1
    D         :    liquid  ||  16564|24|1|-1
    ST        :    liquid  ||  16564|38|1|-1

return to listing



In - 90 Sn (at %) (New)

    DLL       :    liquid  ||  16567|0|1|-1
    MTE       :    liquid  ||  16567|8|1|-1
    CTE       :    liquid  ||  16567|16|1|-1
    D         :    liquid  ||  16567|24|1|-1
    ST        :    liquid  ||  16567|38|1|-1

return to listing



IN-100

    SSCC   (N):    0.003/s  ||  tested at 900 °C (1652 °F)  ||  1951|12|0|0
    SSCC   (N):    0.003/s  ||  tested at 1000 °C (1832 °F)  ||  1951|12|0|1
    SSCC   (N):    0.003/s  ||  tested at 1050 °C (1922 °F)  ||  1951|12|0|2
    SSCC   (N):    0.003/s  ||  tested at 1100 °C (2012 °F)  ||  1951|12|0|3
    SSCC   (N):    0.003/s  ||  tested at 1200 °C (2192 °F)  ||  1951|12|0|4
    SSCC   (N):    0.01/s  ||  tested at 900 °C (1652 °F)  ||  1951|12|1|0
    SSCC   (N):    0.01/s  ||  tested at 1000 °C (1832 °F)  ||  1951|12|1|1
    SSCC   (N):    0.01/s  ||  tested at 1050 °C (1922 °F)  ||  1951|12|1|2
    SSCC   (N):    0.01/s  ||  tested at 1100 °C (2012 °F)  ||  1951|12|1|3
    SSCC   (N):    0.01/s  ||  tested at 1200 °C (2192 °F)  ||  1951|12|1|4
    SSCC   (N):    0.1/s  ||  tested at 900 °C (1652 °F)  ||  1951|12|2|0
    SSCC   (N):    0.1/s  ||  tested at 1000 °C (1832 °F)  ||  1951|12|2|1
    SSCC   (N):    0.1/s  ||  tested at 1050 °C (1922 °F)  ||  1951|12|2|2
    SSCC   (N):    0.1/s  ||  tested at 1100 °C (2012 °F)  ||  1951|12|2|3
    SSCC   (N):    0.1/s  ||  tested at 1200 °C (2192 °F)  ||  1951|12|2|4
    SSCC   (N):    1/s  ||  tested at 900 °C (1652 °F)  ||  1951|12|3|0
    SSCC   (N):    1/s  ||  tested at 1000 °C (1832 °F)  ||  1951|12|3|1
    SSCC   (N):    1/s  ||  tested at 1050 °C (1922 °F)  ||  1951|12|3|2
    SSCC   (N):    1/s  ||  tested at 1100 °C (2012 °F)  ||  1951|12|3|3
    SSCC   (N):    1/s  ||  tested at 1200 °C (2192 °F)  ||  1951|12|3|4
    SSCC   (N):    10/s  ||  tested at 900 °C (1652 °F)  ||  1951|12|4|0
    SSCC   (N):    10/s  ||  tested at 1000 °C (1832 °F)  ||  1951|12|4|1
    SSCC   (N):    10/s  ||  tested at 1050 °C (1922 °F)  ||  1951|12|4|2
    SSCC   (N):    10/s  ||  tested at 1100 °C (2012 °F)  ||  1951|12|4|3
    SSCC   (N):    10/s  ||  tested at 1200 °C (2192 °F)  ||  1951|12|4|4

return to listing



Inconel 625

    SSC    (N):    laser powder bed fusion  ||  tested at 20 °C (68 °F), 0.0025/s, loaded parallel to the build direction  ||  1860|4|6|0
    SSC    (N):    laser powder bed fusion  ||  tested at 20 °C (68 °F), 0.0025/s, loaded perpendicular to the build direction  ||  1860|4|6|1
    SSC    (N):    laser powder bed fusion  ||  tested at 20 °C (68 °F), 0.0025/s, loaded parallel to the build direction, remelted at 95 W  ||  1860|4|6|2
    SSC    (N):    laser powder bed fusion  ||  tested at 20 °C (68 °F), 0.0025/s, loaded perpendicular to the build direction, remelted at 95 W  ||  1860|4|6|3
    SSC    (N):    laser powder bed fusion  ||  tested at 20 °C (68 °F), 0.0025/s, loaded parallel to the build direction, remelted at 110 W  ||  1860|4|6|4
    SSC    (N):    laser powder bed fusion  ||  tested at 20 °C (68 °F), 0.0025/s, loaded perpendicular to the build direction, remelted at 110 W  ||  1860|4|6|5
    SSC    (N):    laser powder bed fusion  ||  tested at 20 °C (68 °F), 0.0025/s, loaded parallel to the build direction, remelted at 120 W  ||  1860|4|6|6
    SSC    (N):    laser powder bed fusion  ||  tested at 20 °C (68 °F), 0.0025/s, loaded perpendicular to the build direction, remelted at 120 W  ||  1860|4|6|7

return to listing



Iron

    DLL    (R):    liquid  ||  860|0|1|-1
    MTE    (R):    liquid  ||  860|8|1|-1
    CTE    (R):    liquid  ||  860|16|1|-1
    D      (R):    liquid  ||  860|24|1|-1
    ST     (N):    liquid  ||  28 ppm O  ||  860|38|1|0
    ST     (N):    liquid  ||  319 ppm O  ||  860|38|1|1
    ST     (N):    liquid  ||  606 ppm O  ||  860|38|1|2
    ST     (N):    liquid  ||  720 ppm O  ||  860|38|1|3
    ST     (N):    liquid  ||  749 ppm O  ||  860|38|1|4
    ST     (N):    liquid  ||  895 ppm O  ||  860|38|1|5
    ST     (N):    liquid  ||  1213 ppm O  ||  860|38|1|6

return to listing



K - 43.5 Na (wt%) (New)

    TC        :    liquid  ||  16383|1|1|-1

return to listing



K2Ba3(P2O7)2 (New)

    RHO       :    un-doped  ||  GaFeO3  ||  16367|2|0|0
    SIGMA     :    un-doped  ||  GaFeO3  ||  16367|10|0|0

return to listing



71.8 KF - 23.9 AlF3 - 4.2 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16755|0|1|-1
    MTE       :    liquid  ||  16755|8|1|-1
    CTE       :    liquid  ||  16755|16|1|-1
    D         :    liquid  ||  16755|24|1|-1

return to listing



71.4 KF - 28.6 AlF3 - 0.0 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16756|0|1|-1
    MTE       :    liquid  ||  16756|8|1|-1
    CTE       :    liquid  ||  16756|16|1|-1
    D         :    liquid  ||  16756|24|1|-1

return to listing



70.9 KF - 28.4 AlF3 - 0.7 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16757|0|1|-1
    MTE       :    liquid  ||  16757|8|1|-1
    CTE       :    liquid  ||  16757|16|1|-1
    D         :    liquid  ||  16757|24|1|-1

return to listing



70.4 KF - 28.1 AlF3 - 1.5 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16758|0|1|-1
    MTE       :    liquid  ||  16758|8|1|-1
    CTE       :    liquid  ||  16758|16|1|-1
    D         :    liquid  ||  16758|24|1|-1

return to listing



69.2 KF - 27.7 AlF3 - 3.1 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16759|0|1|-1
    MTE       :    liquid  ||  16759|8|1|-1
    CTE       :    liquid  ||  16759|16|1|-1
    D         :    liquid  ||  16759|24|1|-1

return to listing



66.7 KF - 33.3 AlF3 - 0.0 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16760|0|1|-1
    MTE       :    liquid  ||  16760|8|1|-1
    CTE       :    liquid  ||  16760|16|1|-1
    D         :    liquid  ||  16760|24|1|-1

return to listing



65.5 KF - 32.8 AlF3 - 1.7 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16761|0|1|-1
    MTE       :    liquid  ||  16761|8|1|-1
    CTE       :    liquid  ||  16761|16|1|-1
    D         :    liquid  ||  16761|24|1|-1

return to listing



64.3 KF - 32.1 AlF3 - 3.6 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16762|0|1|-1
    MTE       :    liquid  ||  16762|8|1|-1
    CTE       :    liquid  ||  16762|16|1|-1
    D         :    liquid  ||  16762|24|1|-1

return to listing



64.0 KF - 32.0 AlF3 - 4.0 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16763|0|1|-1
    MTE       :    liquid  ||  16763|8|1|-1
    CTE       :    liquid  ||  16763|16|1|-1
    D         :    liquid  ||  16763|24|1|-1

return to listing



60.0 KF - 40.0 AlF3 - 0.0 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16764|0|1|-1
    MTE       :    liquid  ||  16764|8|1|-1
    CTE       :    liquid  ||  16764|16|1|-1
    D         :    liquid  ||  16764|24|1|-1

return to listing



59.0 KF - 39.3 AlF3 - 1.6 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16765|0|1|-1
    MTE       :    liquid  ||  16765|8|1|-1
    CTE       :    liquid  ||  16765|16|1|-1
    D         :    liquid  ||  16765|24|1|-1

return to listing



58.8 KF - 39.2 AlF3 - 2.1 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16766|0|1|-1
    MTE       :    liquid  ||  16766|8|1|-1
    CTE       :    liquid  ||  16766|16|1|-1
    D         :    liquid  ||  16766|24|1|-1

return to listing



58.0 KF - 38.7 AlF3 - 3.4 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16767|0|1|-1
    MTE       :    liquid  ||  16767|8|1|-1
    CTE       :    liquid  ||  16767|16|1|-1
    D         :    liquid  ||  16767|24|1|-1

return to listing



75.0 KF - 25.0 AlF3 - 0.0 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16752|0|1|-1
    MTE       :    liquid  ||  16752|8|1|-1
    CTE       :    liquid  ||  16752|16|1|-1
    D         :    liquid  ||  16752|24|1|-1

return to listing



74.0 KF - 24.7 AlF3 - 1.3 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16753|0|1|-1
    MTE       :    liquid  ||  16753|8|1|-1
    CTE       :    liquid  ||  16753|16|1|-1
    D         :    liquid  ||  16753|24|1|-1

return to listing



73.0 KF - 24.3 AlF3 - 2.7 Al2O3 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16754|0|1|-1
    MTE       :    liquid  ||  16754|8|1|-1
    CTE       :    liquid  ||  16754|16|1|-1
    D         :    liquid  ||  16754|24|1|-1

return to listing



68.8 KF - 22.9 AlF3 - 8.2 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16771|0|1|-1
    MTE       :    liquid  ||  16771|8|1|-1
    CTE       :    liquid  ||  16771|16|1|-1
    D         :    liquid  ||  16771|24|1|-1

return to listing



71.4 KF - 28.6 AlF3 - 0.0 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16772|0|1|-1
    MTE       :    liquid  ||  16772|8|1|-1
    CTE       :    liquid  ||  16772|16|1|-1
    D         :    liquid  ||  16772|24|1|-1

return to listing



69.6 KF - 27.8 AlF3 - 2.6 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16773|0|1|-1
    MTE       :    liquid  ||  16773|8|1|-1
    CTE       :    liquid  ||  16773|16|1|-1
    D         :    liquid  ||  16773|24|1|-1

return to listing



67.4 KF - 27.0 AlF3 - 5.6 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16774|0|1|-1
    MTE       :    liquid  ||  16774|8|1|-1
    CTE       :    liquid  ||  16774|16|1|-1
    D         :    liquid  ||  16774|24|1|-1

return to listing



64.8 KF - 25.9 AlF3 - 9.3 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16775|0|1|-1
    MTE       :    liquid  ||  16775|8|1|-1
    CTE       :    liquid  ||  16775|16|1|-1
    D         :    liquid  ||  16775|24|1|-1

return to listing



66.7 KF - 33.3 AlF3 - 0.0 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16776|0|1|-1
    MTE       :    liquid  ||  16776|8|1|-1
    CTE       :    liquid  ||  16776|16|1|-1
    D         :    liquid  ||  16776|24|1|-1

return to listing



65.7 KF - 32.9 AlF3 - 1.4 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16777|0|1|-1
    MTE       :    liquid  ||  16777|8|1|-1
    CTE       :    liquid  ||  16777|16|1|-1
    D         :    liquid  ||  16777|24|1|-1

return to listing



64.7 KF - 32.3 AlF3 - 3.0 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16778|0|1|-1
    MTE       :    liquid  ||  16778|8|1|-1
    CTE       :    liquid  ||  16778|16|1|-1
    D         :    liquid  ||  16778|24|1|-1

return to listing



63.5 KF - 31.8 AlF3 - 4.7 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16779|0|1|-1
    MTE       :    liquid  ||  16779|8|1|-1
    CTE       :    liquid  ||  16779|16|1|-1
    D         :    liquid  ||  16779|24|1|-1

return to listing



62.3 KF - 31.2 AlF3 - 6.5 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16780|0|1|-1
    MTE       :    liquid  ||  16780|8|1|-1
    CTE       :    liquid  ||  16780|16|1|-1
    D         :    liquid  ||  16780|24|1|-1

return to listing



72.3 KF - 27.7 AlF3 - 0.0 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16781|0|1|-1
    MTE       :    liquid  ||  16781|8|1|-1
    CTE       :    liquid  ||  16781|16|1|-1
    D         :    liquid  ||  16781|24|1|-1

return to listing



71.4 KF - 27.4 AlF3 - 1.2 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16782|0|1|-1
    MTE       :    liquid  ||  16782|8|1|-1
    CTE       :    liquid  ||  16782|16|1|-1
    D         :    liquid  ||  16782|24|1|-1

return to listing



71.0 KF - 27.2 AlF3 - 1.8 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16783|0|1|-1
    MTE       :    liquid  ||  16783|8|1|-1
    CTE       :    liquid  ||  16783|16|1|-1
    D         :    liquid  ||  16783|24|1|-1

return to listing



69.4 KF - 26.6 AlF3 - 3.9 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16784|0|1|-1
    MTE       :    liquid  ||  16784|8|1|-1
    CTE       :    liquid  ||  16784|16|1|-1
    D         :    liquid  ||  16784|24|1|-1

return to listing



75.0 KF - 25.0 AlF3 - 0.0 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16768|0|1|-1
    MTE       :    liquid  ||  16768|8|1|-1
    CTE       :    liquid  ||  16768|16|1|-1
    D         :    liquid  ||  16768|24|1|-1

return to listing



73.3 KF - 24.4 AlF3 - 2.3 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16769|0|1|-1
    MTE       :    liquid  ||  16769|8|1|-1
    CTE       :    liquid  ||  16769|16|1|-1
    D         :    liquid  ||  16769|24|1|-1

return to listing



71.3 KF - 23.8 AlF3 - 5.0 AlPO4 (wt %) electrolyte (New)

    DLL       :    liquid  ||  16770|0|1|-1
    MTE       :    liquid  ||  16770|8|1|-1
    CTE       :    liquid  ||  16770|16|1|-1
    D         :    liquid  ||  16770|24|1|-1

return to listing



304L

    VP     (N):    liquid  ||  1251|18|1|-1

return to listing



316L

    VP     (N):    liquid  ||  1260|18|1|-1

return to listing



LaAl2

    DLL    (R):    solid  ||  1555|0|0|-1
    MTE    (R):    solid  ||  1555|8|0|-1
    CTE    (R):    solid  ||  1555|16|0|-1
    D      (R):    solid  ||  1555|24|0|-1

return to listing



Lead

    Vis    (R):    liquid  ||  916|26|1|-1

return to listing



85 LiF - 15 Li2S (mol %) (New)

    DLL       :    liquid  ||  16497|0|1|-1
    MTE       :    liquid  ||  16497|8|1|-1
    CTE       :    liquid  ||  16497|16|1|-1
    D         :    liquid  ||  16497|24|1|-1

return to listing



316LN

    SR     (N):    effect of welding process  ||  tested at 650 °C (1202 °F), base material  ||  1261|22|1|0
    SR     (N):    effect of welding process  ||  tested at 650 °C (1202 °F), HW-TIG welded  ||  1261|22|1|1
    SR     (N):    effect of welding process  ||  tested at 650 °C (1202 °F), A-TIG welded  ||  1261|22|1|2
    SR     (N):    effect of welding process  ||  tested at 650 °C (1202 °F), HLM welded  ||  1261|22|1|3

return to listing



Magnesium

    SSC    (N):    annealed  ||  tested at 25 °C (77 °F), 2.8 x 10-4/s, 180 micron grain size  ||  843|4|1|0
    SSC    (N):    annealed  ||  tested at -195 °C (-319 °F), 2.8 x 10-4/s, 180 micron grain size  ||  843|4|1|1
    SSC    (N):    annealed  ||  tested at -269.1 °C (-452.5 °F), 2.8 x 10-4/s, 180 micron grain size  ||  843|4|1|2
    UTS    (N):    annealed  ||  2.8 x 10-4/s, 180 micron grain size  ||  843|5|0|0
    SSCC   (N):    annealed  ||  tested at 25 °C (77 °F), 2.8 x 10-4/s, 180 micron grain size  ||  843|12|1|0
    SSCC   (N):    annealed  ||  tested at -195 °C (-319 °F), 2.8 x 10-4/s, 180 micron grain size  ||  843|12|1|1
    SSCC   (N):    annealed  ||  tested at -269.1 °C (-452.5 °F), 2.8 x 10-4/s, 180 micron grain size  ||  843|12|1|2
    YS     (N):    annealed  ||  2.8 x 10-4/s, 180 micron grain size  ||  843|13|0|0
    YSC    (N):    annealed  ||  2.8 x 10-4/s, 180 micron grain size  ||  843|21|0|0
    %El    (N):    annealed, in tension  ||  2.8 x 10-4/s, 180 micron grain size  ||  843|29|0|0
    %El    (N):    annealed, in compression  ||  2.8 x 10-4/s, 180 micron grain size  ||  843|29|1|0
    UCS    (N):    annealed  ||  2.8 x 10-4/s, 180 micron grain size  ||  843|47|0|0

return to listing



Manganese

    DLL    (N):    liquid  ||  859|0|1|-1
    MTE    (N):    liquid  ||  859|8|1|-1
    CTE    (N):    liquid  ||  859|16|1|-1
    D      (N):    liquid  ||  859|24|1|-1
    ST     (N):    liquid  ||  372 ppm O, 528 ppm S  ||  859|38|1|1

return to listing



MAR-M200

    FSN    (N):    single crystal  ||  tested at 20 °C (68 °F), axial, in air, stress range  ||  1879|6|1|0
    FSN    (N):    single crystal  ||  tested at 20 °C (68 °F), axial, in vacuum, stress range  ||  1879|6|1|1
    FEN    (N):    directionally solidified  ||  tested at 21 °C (70 °F), R = -1, ultrasonic, total strain amplitude  ||  1879|14|1|2

return to listing



Maraging 350 (C-type)

    UTS   (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 3 h at 510 °C (950 °F), air cooled  ||  1064|5|2|0
    UTS   (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 25% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F)  ||  1064|5|2|1
    UTS   (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 70% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F)  ||  1064|5|2|2
    UTS   (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 25% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F)  ||  1064|5|2|3
    UTS   (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 70% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F)  ||  1064|5|2|4
    FSN    (N):    1 h at 816 °C (1500 °F), 3 h at 510 °C (950 °F), air cooled  ||  tested at 20 °C (68 °F), R = 0.1, axial, maximum stress  ||  1064|6|1|0
    FSN    (N):    1 h at 816 °C (1500 °F), 25% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F)  ||  tested at 20 °C (68 °F), R = 0.1, axial, maximum stress  ||  1064|6|2|0
    FSN    (N):    1 h at 816 °C (1500 °F), 70% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F)  ||  tested at 20 °C (68 °F), R = 0.1, axial, maximum stress  ||  1064|6|3|0
    FSN    (N):    1 h at 816 °C (1500 °F), 25% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F)  ||  tested at 20 °C (68 °F), R = 0.1, axial, maximum stress  ||  1064|6|4|0
    FSN    (N):    1 h at 816 °C (1500 °F), 70% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F)  ||  tested at 20 °C (68 °F), R = 0.1, axial, maximum stress  ||  1064|6|5|0
    YS    (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 3 h at 510 °C (950 °F), air cooled  ||  1064|13|2|0
    YS    (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 25% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F)  ||  1064|13|2|1
    YS    (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 70% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F)  ||  1064|13|2|2
    YS    (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 25% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F)  ||  1064|13|2|3
    YS    (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 70% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F)  ||  1064|13|2|4
    %El   (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 3 h at 510 °C (950 °F), air cooled  ||  1064|29|2|0
    %El   (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 25% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F)  ||  1064|29|2|1
    %El   (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 70% reduction at 24 °C (75 °F), 3 h at 510 °C (950 °F)  ||  1064|29|2|2
    %El   (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 25% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F)  ||  1064|29|2|3
    %El   (N*):    effect of cold work & anneal on RT value  ||  1 h at 816 °C (1500 °F), 70% reduction at 399 °C (750 °F), 3 h at 510 °C (950 °F)  ||  1064|29|2|4

return to listing



Mg - 2.9 Gd (wt %) (New)

    SSC       :    annealed  ||  tested at 25 °C (77 °F), 2.8 x 10-4/s  ||  16803|4|0|0
    SSC       :    annealed  ||  tested at -195 °C (-319 °F), 2.8 x 10-4/s  ||  16803|4|0|1
    SSC       :    annealed  ||  tested at -269.1 °C (-452.5 °F), 2.8 x 10-4/s  ||  16803|4|0|2
    UTS       :    annealed  ||  2.8 x 10-4/s  ||  16803|5|0|0
    SSCC      :    annealed  ||  tested at 25 °C (77 °F), 2.8 x 10-4/s  ||  16803|12|0|0
    SSCC      :    annealed  ||  tested at -195 °C (-319 °F), 2.8 x 10-4/s  ||  16803|12|0|1
    SSCC      :    annealed  ||  tested at -269.1 °C (-452.5 °F), 2.8 x 10-4/s  ||  16803|12|0|2
    YS        :    annealed  ||  2.8 x 10-4/s  ||  16803|13|0|0
    YSC       :    annealed  ||  2.8 x 10-4/s  ||  16803|21|0|0
    %El       :    annealed  ||  2.8 x 10-4/s  ||  16803|29|0|0
    UCS       :    annealed  ||  2.8 x 10-4/s  ||  16803|47|0|0

return to listing



Mg - 1.8 Gd (wt %) (New)

    SSC       :    annealed  ||  tested at 25 °C (77 °F), 2.8 x 10-4/s  ||  16802|4|0|0
    SSC       :    annealed  ||  tested at -195 °C (-319 °F), 2.8 x 10-4/s  ||  16802|4|0|1
    SSC       :    annealed  ||  tested at -269.1 °C (-452.5 °F), 2.8 x 10-4/s  ||  16802|4|0|2
    UTS       :    annealed  ||  2.8 x 10-4/s  ||  16802|5|0|0
    SSCC      :    annealed  ||  tested at 25 °C (77 °F), 2.8 x 10-4/s  ||  16802|12|0|0
    SSCC      :    annealed  ||  tested at -195 °C (-319 °F), 2.8 x 10-4/s  ||  16802|12|0|1
    SSCC      :    annealed  ||  tested at -269.1 °C (-452.5 °F), 2.8 x 10-4/s  ||  16802|12|0|2
    YS        :    annealed  ||  2.8 x 10-4/s  ||  16802|13|0|0
    YSC       :    annealed  ||  2.8 x 10-4/s  ||  16802|21|0|0
    %El       :    annealed  ||  2.8 x 10-4/s  ||  16802|29|0|0
    UCS       :    annealed  ||  2.8 x 10-4/s  ||  16802|47|0|0

return to listing



Mg - 2 Y (wt %) (New)

    SSC       :    annealed  ||  tested at 25 °C (77 °F), 2.8 x 10-4/s  ||  16805|4|0|0
    SSC       :    annealed  ||  tested at -195 °C (-319 °F), 2.8 x 10-4/s  ||  16805|4|0|1
    SSC       :    annealed  ||  tested at -269.1 °C (-452.5 °F), 2.8 x 10-4/s  ||  16805|4|0|2
    UTS       :    annealed  ||  2.8 x 10-4/s  ||  16805|5|0|0
    SSCC      :    annealed  ||  tested at 25 °C (77 °F), 2.8 x 10-4/s  ||  16805|12|0|0
    SSCC      :    annealed  ||  tested at -195 °C (-319 °F), 2.8 x 10-4/s  ||  16805|12|0|1
    SSCC      :    annealed  ||  tested at -269.1 °C (-452.5 °F), 2.8 x 10-4/s  ||  16805|12|0|2
    YS        :    annealed  ||  2.8 x 10-4/s  ||  16805|13|0|0
    YSC       :    annealed  ||  2.8 x 10-4/s  ||  16805|21|0|0
    %El       :    annealed, in tension  ||  2.8 x 10-4/s  ||  16805|29|0|0
    %El   (*):    annealed, in compression  ||  2.8 x 10-4/s  ||  16805|29|1|0
    UCS   (*):    annealed  ||  2.8 x 10-4/s  ||  16805|47|0|0

return to listing



Mg - 1.1 Y (wt %) (New)

    SSC       :    annealed  ||  tested at 25 °C (77 °F), 2.8 x 10-4/s  ||  16804|4|0|0
    SSC       :    annealed  ||  tested at -195 °C (-319 °F), 2.8 x 10-4/s  ||  16804|4|0|1
    SSC       :    annealed  ||  tested at -269.1 °C (-452.5 °F), 2.8 x 10-4/s  ||  16804|4|0|2
    UTS       :    annealed  ||  2.8 x 10-4/s  ||  16804|5|0|0
    SSCC      :    annealed  ||  tested at 25 °C (77 °F), 2.8 x 10-4/s  ||  16804|12|0|0
    SSCC      :    annealed  ||  tested at -195 °C (-319 °F), 2.8 x 10-4/s  ||  16804|12|0|1
    SSCC      :    annealed  ||  tested at -269.1 °C (-452.5 °F), 2.8 x 10-4/s  ||  16804|12|0|2
    YS        :    annealed  ||  2.8 x 10-4/s  ||  16804|13|0|0
    YSC       :    annealed  ||  2.8 x 10-4/s  ||  16804|21|0|0
    %El       :    annealed, in tension  ||  2.8 x 10-4/s  ||  16804|29|0|0
    %El   (*):    annealed, in compression  ||  2.8 x 10-4/s  ||  16804|29|1|0
    UCS   (*):    annealed  ||  2.8 x 10-4/s  ||  16804|47|0|0

return to listing



34.5 MnO - 34.5 SiO2 - 6.0 MgO - 25.0 Al2O3 (wt %) flux (New)

    Vis       :    liquid  ||  16924|26|1|-1

return to listing



47.0 MnO - 47.0 SiO2 - 6.0 MgO - 0.0 Al2O3 (wt %) flux (New)

    Vis       :    liquid  ||  16919|26|1|-1

return to listing



44.5 MnO - 44.5 SiO2 - 6.0 MgO - 5.0 Al2O3 (wt %) flux (New)

    Vis       :    liquid  ||  16920|26|1|-1

return to listing



42.0 MnO - 42.0 SiO2 - 6.0 MgO - 10.0 Al2O3 (wt %) flux (New)

    Vis       :    liquid  ||  16921|26|1|-1

return to listing



39.5 MnO - 39.5 SiO2 - 6.0 MgO - 15.0 Al2O3 (wt %) flux (New)

    Vis       :    liquid  ||  16922|26|1|-1

return to listing



37.0 MnO - 37.0 SiO2 - 6.0 MgO - 20.0 Al2O3 (wt %) flux (New)

    Vis       :    liquid  ||  16923|26|1|-1

return to listing



Na - 44 K (wt%) (New)

    TC        :    liquid  ||  16382|1|1|-1

return to listing



Ni - 20 Co (at %) (New)

    DLL       :    liquid  ||  16984|0|1|-1
    MTE       :    liquid  ||  16984|8|1|-1
    CTE       :    liquid  ||  16984|16|1|-1
    D         :    liquid  ||  16984|24|1|-1

return to listing



Ni - 40 Co (at %) (New)

    DLL       :    liquid  ||  16991|0|1|-1
    MTE       :    liquid  ||  16991|8|1|-1
    CTE       :    liquid  ||  16991|16|1|-1
    D         :    liquid  ||  16991|24|1|-1

return to listing



Ni - 20 Cr (at %) (New)

    DLL       :    liquid  ||  16345|0|1|-1
    MTE       :    liquid  ||  16345|8|1|-1
    CTE       :    liquid  ||  16345|16|1|-1
    D         :    liquid  ||  16345|24|1|-1

return to listing



Ni - 40 Cr (at %) (New)

    DLL       :    liquid  ||  16346|0|1|-1
    MTE       :    liquid  ||  16346|8|1|-1
    CTE       :    liquid  ||  16346|16|1|-1
    D         :    liquid  ||  16346|24|1|-1

return to listing



Ni - 10 Cr (at %) (New)

    DLL       :    liquid  ||  16344|0|1|-1
    MTE       :    liquid  ||  16344|8|1|-1
    CTE       :    liquid  ||  16344|16|1|-1
    D         :    liquid  ||  16344|24|1|-1

return to listing



Ni - 40 Cu (wt %)

    DLL    (N):    liquid  ||  15301|0|1|-1
    MTE    (N):    liquid  ||  15301|8|1|-1
    CTE    (N):    liquid  ||  15301|16|1|-1
    D      (N):    liquid  ||  15301|24|1|-1

return to listing



Ni - 20 Cu (wt %)

    DLL    (N):    liquid  ||  15305|0|1|-1
    MTE    (N):    liquid  ||  15305|8|1|-1
    CTE    (N):    liquid  ||  15305|16|1|-1
    D      (N):    liquid  ||  15305|24|1|-1

return to listing



Ni - 20 Fe (wt %)

    DLL    (N):    liquid  ||  16120|0|1|-1
    MTE    (N):    liquid  ||  16120|8|1|-1
    CTE    (N):    liquid  ||  16120|16|1|-1
    D      (N):    liquid  ||  16120|24|1|-1

return to listing



Ni - 40 Fe (wt %)

    DLL    (N):    liquid  ||  16116|0|1|-1
    MTE    (N):    liquid  ||  16116|8|1|-1
    CTE    (N):    liquid  ||  16116|16|1|-1
    D      (N):    liquid  ||  16116|24|1|-1

return to listing



Ni - 34 S (at %) (New)

    TC        :    liquid  ||  16552|1|1|-1

return to listing



Ni-Ti (Nitinol)

    RHO    (N):    solid  ||  on heating  ||  2851|2|0|0
    RHO    (N):    solid  ||  on cooling  ||  2851|2|0|1
    SIGMA  (N):    solid  ||  on heating  ||  2851|10|0|0
    SIGMA  (N):    solid  ||  on cooling  ||  2851|10|0|1

return to listing



Ni45Cu20Fe35 (New)

    DLL       :    liquid  ||  16998|0|1|-1
    MTE       :    liquid  ||  16998|8|1|-1
    CTE       :    liquid  ||  16998|16|1|-1
    D         :    liquid  ||  16998|24|1|-1

return to listing



Ni70Cu20Fe10 (New)

    DLL       :    liquid  ||  16996|0|1|-1
    MTE       :    liquid  ||  16996|8|1|-1
    CTE       :    liquid  ||  16996|16|1|-1
    D         :    liquid  ||  16996|24|1|-1

return to listing



Ni60Cu20Fe20 (New)

    DLL       :    liquid  ||  16997|0|1|-1
    MTE       :    liquid  ||  16997|8|1|-1
    CTE       :    liquid  ||  16997|16|1|-1
    D         :    liquid  ||  16997|24|1|-1

return to listing



Ni3Zr2P3 (New)

    RHO       :    solid  ||  [010] direction  ||  16562|2|0|0
    SIGMA     :    solid  ||  [010] direction  ||  16562|10|0|0

return to listing



Olive oil

    SH     (N):    liquid  ||  2143|9|1|-1
    TD     (N):    liquid  ||  2143|25|1|-1

return to listing



Pb - 40 In (at %) (New)

    Vis       :    liquid  ||  16432|26|1|-1

return to listing



Pb - 60 In (at %) (New)

    Vis       :    liquid  ||  16433|26|1|-1

return to listing



Pb - 80 In (at %) (New)

    Vis       :    liquid  ||  16434|26|1|-1

return to listing



Pb - 20 In (at %) (New)

    Vis       :    liquid  ||  16431|26|1|-1

return to listing



Pb - 50 In (wt %)

    Vis    (N):    liquid  ||  2743|26|1|-1

return to listing



Pb - 13 Sb (wt %) (New)

    TC        :    liquid  ||  16380|1|1|-1

return to listing



80.75 PbCl2 - 4.25 PbS - 15 PbO (mol %) (New)

    RHO       :    liquid  ||  16501|2|1|-1
    SIGMA     :    liquid  ||  16501|10|1|-1

return to listing



93.1 PbCl2 - 4.9 PbS - 2 PbO (mol %) (New)

    RHO       :    liquid  ||  16498|2|1|-1
    SIGMA     :    liquid  ||  16498|10|1|-1

return to listing



90.25 PbCl2 - 4.75 PbS - 5 PbO (mol %) (New)

    RHO       :    liquid  ||  16499|2|1|-1
    SIGMA     :    liquid  ||  16499|10|1|-1

return to listing



85.5 PbCl2 - 4.5 PbS - 10 PbO (mol %) (New)

    RHO       :    liquid  ||  16500|2|1|-1
    SIGMA     :    liquid  ||  16500|10|1|-1

return to listing



33.3 PbO - 66.7 B2O3 (mol %) (New)

    DLL       :    glass  ||  16970|0|0|-1
    MTE       :    glass  ||  16970|8|0|-1
    D         :    glass  ||  16970|24|0|-1

return to listing



27 PbO - 73 B2O3 (mol %) (New)

    DLL       :    glass  ||  16971|0|0|-1
    MTE       :    glass  ||  16971|8|0|-1
    D         :    glass  ||  16971|24|0|-1

return to listing



42 PbO - 58 B2O3 (mol %) (New)

    DLL       :    glass  ||  16969|0|0|-1
    MTE       :    glass  ||  16969|8|0|-1
    D         :    glass  ||  16969|24|0|-1

return to listing



80 PbO - 20 SiO2 (wt %)

    Vis    (N):    liquid  ||  1524|26|1|-1

return to listing



81.34 PbO - 18.66 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16521|26|1|-1

return to listing



82.54 PbO - 17.46 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16522|26|1|-1

return to listing



83.68 PbO - 16.32 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16523|26|1|-1

return to listing



84.6 PbO - 15.4 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16524|26|1|-1

return to listing



85.31 PbO - 14.69 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16525|26|1|-1

return to listing



85.84 PbO - 14.16 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16526|26|1|-1

return to listing



86.35 PbO - 13.65 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16527|26|1|-1

return to listing



86.85 PbO - 13.15 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16528|26|1|-1

return to listing



87.34 PbO - 12.66 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16529|26|1|-1

return to listing



87.82 PbO - 12.18 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16530|26|1|-1

return to listing



88.14 PbO - 11.86 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16531|26|1|-1

return to listing



88.75 PbO - 11.25 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16532|26|1|-1

return to listing



89.21 PbO - 10.79 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16533|26|1|-1

return to listing



91.78 PbO - 8.22 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16534|26|1|-1

return to listing



79.58 PbO - 20.42 SiO2 (wt %) (New)

    Vis       :    liquid  ||  16520|26|1|-1

return to listing



PMMA

    TC     (R):    solid  ||  1808|1|0|-1

return to listing



48 P2O5 - 16 Na2O - 14.4 CaO - 1.6 Al2O3 - 20 CoO (wt %) (New)

    TC        :    undoped  ||  16981|1|0|-1
    TC        :    doped  ||  0.5 V2O5  ||  16981|1|1|0
    TC        :    doped  ||  1 V2O5  ||  16981|1|1|1
    TC        :    doped  ||  0.5 CuO  ||  16981|1|1|2
    TC        :    doped  ||  1 CuO  ||  16981|1|1|3
    SH        :    undoped  ||  16981|9|0|-1
    SH        :    doped  ||  0.5 V2O5  ||  16981|9|1|0
    SH        :    doped  ||  1 V2O5  ||  16981|9|1|1
    SH        :    doped  ||  0.5 CuO  ||  16981|9|1|2
    SH        :    doped  ||  1 CuO  ||  16981|9|1|3
    D     (*):    undoped  ||  16981|24|0|-1
    D     (*):    doped  ||  0.5 V2O5  ||  16981|24|1|0
    D     (*):    doped  ||  1 V2O5  ||  16981|24|1|1
    D     (*):    doped  ||  0.5 CuO  ||  16981|24|1|2
    D     (*):    doped  ||  1 CuO  ||  16981|24|1|3
    TD        :    undoped  ||  16981|25|0|-1
    TD        :    doped  ||  0.5 V2O5  ||  16981|25|1|0
    TD        :    doped  ||  1 V2O5  ||  16981|25|1|1
    TD        :    doped  ||  0.5 CuO  ||  16981|25|1|2
    TD        :    doped  ||  1 CuO  ||  16981|25|1|3
    RIW       :    undoped, measured in air  ||  tested at 20 °C (68 °F)  ||  16981|45|0|0
    RIW       :    doped, measured in air  ||  tested at 20 °C (68 °F), 0.5 V2O5  ||  16981|45|1|0
    RIW       :    doped, measured in air  ||  tested at 20 °C (68 °F), 1 V2O5  ||  16981|45|1|1
    RIW       :    doped, measured in air  ||  tested at 20 °C (68 °F), 0.5 CuO  ||  16981|45|1|2
    RIW       :    doped, measured in air  ||  tested at 20 °C (68 °F), 1 CuO  ||  16981|45|1|3

return to listing



60 P2O5 - 20 Na2O - 18 CaO - 2 Al2O3 (wt %) (New)

    TC        :    solid  ||  16980|1|0|-1
    SH        :    solid  ||  16980|9|0|-1
    D     (*):    solid  ||  16980|24|0|-1
    TD        :    solid  ||  16980|25|0|-1
    RIW       :    measured in air  ||  tested at 20 °C (68 °F)  ||  16980|45|0|0

return to listing



Pyroceram 9608

    RHO    (N):    solid  ||  1535|2|0|-1
    E     (N*):    solid  ||  1535|3|0|-1
    SIGMA  (N):    solid  ||  1535|10|0|-1
    G     (N*):    solid  ||  1535|11|0|-1
    v     (N*):    solid  ||  1535|19|0|-1
    K     (N*):    solid  ||  1535|27|0|-1

return to listing



Pyroceram 9606

    DLL    (R):    solid  ||  1534|0|0|-1
    TC     (R):    solid  ||  1534|1|0|-1
    UTS    (N):    solid  ||  1534|5|0|-1
    MTE    (R):    solid  ||  1534|8|0|-1
    D      (R):    solid  ||  1534|24|0|-1
    DCRPT  (N):    tested at 25 °C (77 °F)  ||  1534|41|0|-1
    DCRPT  (N):    tested at 300 °C (572 °F)  ||  1534|41|1|-1
    DCRPT  (N):    tested at 500 °C (932 °F)  ||  1534|41|2|-1
    DF     (N):    tested at 25 °C (77 °F)  ||  1534|42|0|-1
    DF     (N):    tested at 300 °C (572 °F)  ||  1534|42|1|-1
    UCS   (N*):    solid  ||  1534|47|0|-1

return to listing



Rene 95

    FEN    (N):    forged, solution annealed & aged  ||  tested at 649 °C (1200 °F), R = -1, axial, plastic strain range  ||  1910|14|2|0

return to listing



Rene 80

    DLL    (N):    solid  ||  15036|0|0|-1
    DLL    (N):    liquid  ||  15036|0|1|-1
    TC     (N):    solid  ||  15036|1|0|-1
    MTE    (N):    solid  ||  15036|8|0|-1
    MTE    (N):    liquid  ||  15036|8|1|-1
    SH     (N):    solid  ||  15036|9|0|-1
    SH     (N):    liquid  ||  15036|9|1|-1
    FEN    (N):    3-step and 4-step heat treatments, 0.01 cpm  ||  tested at 871 °C (1600 °F), R = -1, axial, total strain range  ||  15036|14|1|0
    FEN    (N):    3-step and 4-step heat treatments, 0.1 cpm  ||  tested at 871 °C (1600 °F), R = -1, axial, total strain range  ||  15036|14|2|0
    FEN    (N):    3-step and 4-step heat treatments, 1 cpm  ||  tested at 871 °C (1600 °F), R = -1, axial, total strain range  ||  15036|14|3|0
    FEN    (N):    3-step and 4-step heat treatments, 1 cpm  ||  tested at 871 °C (1600 °F), R = -1, axial, plastic strain range  ||  15036|14|3|1
    FEN    (N):    3-step and 4-step heat treatments, 1 cpm  ||  tested at 871 °C (1600 °F), R = -1, axial, elastic strain range  ||  15036|14|3|2
    FEN    (N):    3-step and 4-step heat treatments, 10 cpm  ||  tested at 871 °C (1600 °F), R = -1, axial, total strain range  ||  15036|14|4|0
    D      (R):    solid  ||  15036|24|0|-1
    D      (N):    liquid  ||  15036|24|1|-1
    TD     (N):    solid  ||  15036|25|0|-1

return to listing



Rhenium

    SR     (N):    electron beam refined sheet  ||  tested at 1093 °C (2000 °F)  ||  909|22|0|0
    SR     (N):    electron beam refined sheet  ||  tested at 1649 °C (3000 °F)  ||  909|22|0|1
    SR     (N):    electron beam refined sheet  ||  tested at 2204 °C (4000 °F)  ||  909|22|0|2
    SR     (N):    electron beam refined sheet  ||  Master curve (LMP)  ||  909|22|0|3
    SR     (N):    commercial powder metallurgical sheet  ||  tested at 1093 °C (2000 °F)  ||  909|22|1|0
    SR     (N):    commercial powder metallurgical sheet  ||  tested at 1649 °C (3000 °F)  ||  909|22|1|1
    SR     (N):    commercial powder metallurgical sheet  ||  tested at 2204 °C (4000 °F)  ||  909|22|1|2
    SR     (N):    commercial powder metallurgical sheet  ||  Master curve (LMP)  ||  909|22|1|3

return to listing



Rice bran (New)

    SH        :    liquid  ||  16973|9|1|-1

return to listing



S-2 glass fiber

    DLL    (N):    solid  ||  3269|0|0|-1
    MTE    (N):    solid  ||  3269|8|0|-1
    SH    (N*):    solid  ||  3269|9|0|-1
    CTE    (N):    solid  ||  3269|16|0|-1
    D      (N):    solid  ||  3269|24|0|-1
    DCRPT  (N):    annealed material  ||  tested at 23 °C (73 °F)  ||  3269|41|0|0
    DF     (N):    annealed material  ||  tested at 23 °C (73 °F)  ||  3269|42|0|0

return to listing



SbCl3

    ST     (N):    liquid  ||  3447|38|1|-1

return to listing



Schott N-BK7

    TC     (R):    solid  ||  1430|1|0|-1

return to listing



SiC (alpha)

    TC     (N):    solid  ||  spark plasma sintered, Ozer et. al., 96.8% dense  ||  197|1|0|1
    RHO    (N):    solid  ||  spark plasma sintered, Ozer et. al.  ||  197|2|0|1
    SIGMA  (N):    solid  ||  spark plasma sintered, Ozer et. al.  ||  197|10|0|1
    TD     (R):    solid  ||  Hexoloy SA  ||  197|25|0|0
    TD     (N):    solid  ||  spark plasma sintered, Ozer et. al., 96.8% dense  ||  197|25|0|1
    FS     (N):    Hexoloy SA  ||  197|33|0|-1
    UCS   (N*):    Hexoloy SA  ||  197|47|0|-1
    S      (N):    Ozer et. al.  ||  spark plasma sintered  ||  197|48|0|0

return to listing



30 SiO2 - 20 Al2O3 - 26 CaO - 2 MgO - 8 Na2O - 6 F2 - 8 MnO (wt %) (New)

    Vis       :    liquid  ||  16517|26|1|-1

return to listing



21 SiO2 - 8 Al2O3 - 35 CaO - 5 MgO - 6 Na2O - 2 K2O - 14 F2 - 4 FeO - 5 B2O3 (wt %) (New)

    Vis       :    liquid  ||  16514|26|1|-1

return to listing



17 SiO2 - 26 Al2O3 - 28 CaO - 4 MgO - 5 Na2O - 2 K2O - 11 F2 - 3 FeO - 4 B2O3 (wt %) (New)

    Vis       :    liquid  ||  16515|26|1|-1

return to listing



30 SiO2 - 11 Al2O3 - 30 CaO - 12 Na2O - 4 F2 - 1 FeO - 12 MnO (wt %) (New)

    Vis       :    liquid  ||  16518|26|1|-1

return to listing



23 SiO2 - 32 Al2O3 - 23 CaO - 9 Na2O - 3 F2 - 10 MnO (wt %) (New)

    Vis       :    liquid  ||  16519|26|1|-1

return to listing



39 SiO2 - 11 Al2O3 - 25 CaO - 14 Na2O - 1 K2O - 5 F2 - 4 FeO - 1 B2O3 (wt %) (New)

    Vis       :    liquid  ||  16509|26|1|-1

return to listing



35 SiO2 - 19 Al2O3 - 23 CaO - 13 Na2O - 1 K2O - 5 F2 - 3 FeO - 1 B2O3 (wt %) (New)

    Vis       :    liquid  ||  16510|26|1|-1

return to listing



32 SiO2 - 26 Al2O3 - 21 CaO - 12 Na2O - 1 K2O - 4 F2 - 3 FeO - 1 B2O3 (wt %) (New)

    Vis       :    liquid  ||  16511|26|1|-1

return to listing



37 SiO2 - 9 Al2O3 - 32 CaO - 5 Na2O - 2 K2O - 8.5 F2 - 3 FeO - 3.5 B2O3 (wt %) (New)

    Vis       :    liquid  ||  16502|26|1|-1

return to listing



34 SiO2 - 14 Al2O3 - 31 CaO - 5 Na2O - 2 K2O - 8 F2 - 3 FeO - 3 B2O3 (wt %) (New)

    Vis       :    liquid  ||  16503|26|1|-1

return to listing



32 SiO2 - 19 Al2O3 - 29 CaO - 4 Na2O - 2 K2O - 8 F2 - 3 FeO - 3 B2O3 (wt %) (New)

    Vis       :    liquid  ||  16504|26|1|-1

return to listing



30 SiO2 - 26 Al2O3 - 26 CaO - 4 Na2O - 1 K2O - 7 F2 - 3 FeO - 3 B2O3 (wt %) (New)

    Vis       :    liquid  ||  16505|26|1|-1

return to listing



28 SiO2 - 32 Al2O3 - 24 CaO - 4 Na2O - 1 K2O - 6 F2 - 2 FeO - 3 B2O3 (wt %) (New)

    Vis       :    liquid  ||  16506|26|1|-1

return to listing



41 SiO2 - 5 Al2O3 - 26 CaO - 15 Na2O - 1 K2O - 6 F2 - 4 FeO - 2 B2O3 (wt %) (New)

    Vis       :    liquid  ||  16508|26|1|-1

return to listing



30 SiO2 - 21 Al2O3- 28 CaO - 1 MgO - 6 Na2O - 12 F2 - 1 FeO - 1 MnO (wt %) (New)

    Vis       :    liquid  ||  16513|26|1|-1

return to listing



39.2 SiO2 - 39.6 CaO - 21.2 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16918|26|1|-1

return to listing



72.7 SiO2 - 8.9 CaO - 18.4 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16902|26|1|-1

return to listing



59.1 SiO2 - 15.1 CaO - 25.8 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16903|26|1|-1

return to listing



68.2 SiO2 - 21.2 CaO - 10.6 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16904|26|1|-1

return to listing



63.1 SiO2 - 21.1 CaO - 15.8 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16905|26|1|-1

return to listing



58.4 SiO2 - 20.7 CaO - 20.9 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16906|26|1|-1

return to listing



53.4 SiO2 - 20.5 CaO - 26.1 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16907|26|1|-1

return to listing



59.4 SiO2 - 24.6 CaO - 16.0 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16908|26|1|-1

return to listing



35.8 SiO2 - 24.1 CaO - 40.1 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16909|26|1|-1

return to listing



64.7 SiO2 - 29.6 CaO - 5.7 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16910|26|1|-1

return to listing



59.9 SiO2 - 29.3 CaO - 10.8 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16911|26|1|-1

return to listing



54.8 SiO2 - 28.9 CaO - 16.3 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16912|26|1|-1

return to listing



49.9 SiO2 - 29.4 CaO - 20.7 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16913|26|1|-1

return to listing



45.2 SiO2 - 29.2 CaO - 25.6 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16914|26|1|-1

return to listing



58.8 SiO2 - 34.8 CaO - 6.4 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16915|26|1|-1

return to listing



48.6 SiO2 - 41.0 CaO - 10.4 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16916|26|1|-1

return to listing



43.7 SiO2 - 40.7 CaO - 15.6 Al2O3 (wt %) slag (New)

    Vis       :    liquid  ||  16917|26|1|-1

return to listing



38 SiO2 - 35 CaO - 1 MgO - 7 Na2O - 15 F2 - 1 FeO - 2 MnO (wt %) (New)

    Vis       :    liquid  ||  16512|26|1|-1

return to listing



37 SiO2 - 33 CaO - 2 MgO - 10 Na2O - 7 F2 - 11 MnO (wt %) (New)

    Vis       :    liquid  ||  16516|26|1|-1

return to listing



43 SiO2 - 28 CaO - 16 Na2O - 1 K2O - 6 F2 - 4 FeO - 2 B2O3 (wt %) (New)

    Vis       :    liquid  ||  16507|26|1|-1

return to listing



42.3 SiO2 - 23.1 CaO - 34.6 Na2O (mol %) slag (New)

    TC        :    liquid  ||  16726|1|1|-1
    SH    (*):    solid  ||  16726|9|0|-1
    D     (*):    solid  ||  16726|24|0|-1

return to listing



77.1 SiO2 - 9.1 CaO - 13.6 Na2O (mol %) slag (New)

    TC        :    liquid  ||  16722|1|1|-1
    SH    (*):    solid  ||  16722|9|0|-1
    D     (*):    solid  ||  16722|24|0|-1

return to listing



69.4 SiO2 - 18.4 CaO - 12.2 Na2O (mol %) slag (New)

    TC        :    liquid  ||  16723|1|1|-1
    SH    (*):    solid  ||  16723|9|0|-1
    D     (*):    solid  ||  16723|24|0|-1

return to listing



58.3 SiO2 - 16.7 CaO - 25 Na2O (mol %) slag (New)

    TC        :    liquid  ||  16724|1|1|-1
    SH    (*):    solid  ||  16724|9|0|-1
    D     (*):    solid  ||  16724|24|0|-1

return to listing



49.4 SiO2 - 10.1 CaO - 40.5 Na2O (mol %) slag (New)

    TC        :    liquid  ||  16725|1|1|-1
    SH    (*):    solid  ||  16725|9|0|-1
    D     (*):    solid  ||  16725|24|0|-1

return to listing



61 SiO2 - 39 CaO (mol %) slag (New)

    Vis       :    liquid  ||  16701|26|1|-1

return to listing



25 SiO2 - 29 FeO - 15 ZnO - 12 CaO - 6 MgO - 5 CaS - 4 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New)

    Vis       :    liquid  ||  16536|26|1|-1

return to listing



25 SiO2 - 30 FeO - 16 ZnO - 8 CaO - 8 MgO - 5 CaS - 4 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New)

    Vis       :    liquid  ||  16537|26|1|-1

return to listing



25 SiO2 - 29 FeO - 12 ZnO - 12 CaO - 9 MgO - 5 CaS - 4 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New)

    Vis       :    liquid  ||  16538|26|1|-1

return to listing



24 SiO2 - 28 FeO - 24 ZnO - 7 CaO - 5 MgO - 4 CaS - 4 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New)

    Vis       :    liquid  ||  16539|26|1|-1

return to listing



24 SiO2 - 28 FeO - 11 ZnO - 20 CaO - 5 MgO - 4 CaS - 4 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New)

    Vis       :    liquid  ||  16540|26|1|-1

return to listing



37 SiO2 - 28 FeO - 11 ZnO - 7 CaO - 5 MgO - 4 CaS - 4 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New)

    Vis       :    liquid  ||  16541|26|1|-1

return to listing



31 SiO2 - 28 FeO - 11 ZnO - 7 CaO - 5 MgO - 4 CaS - 10 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New)

    Vis       :    liquid  ||  16542|26|1|-1

return to listing



25 SiO2 - 29 FeO - 12 ZnO - 8 CaO - 5 MgO - 5 CaS - 12 Al2O3 - 2 Fe2O3 - 2 PbO (wt %) (New)

    Vis       :    liquid  ||  16543|26|1|-1

return to listing



27 SiO2 - 32 FeO - 13 ZnO - 8 CaO - 6 MgO - 5 CaS - 4 Al2O3 - 3 Fe2O3 - 2 PbO (wt %) (New)

    Vis       :    liquid  ||  16535|26|1|-1

return to listing



73 SiO2 - 12 K2O - 6 Na2O - 5 CaO - 4 MgO (wt %) (New)

    DLL       :    solid  ||  17005|0|0|-1
    MTE       :    solid  ||  17005|8|0|-1
    D         :    solid  ||  17005|24|0|-1
    Vis       :    liquid  ||  17005|26|1|-1

return to listing



67 SiO2 - 12 K2O - 8 ZrO2 - 6 Na2O - 4 TiO2 - 1 CaO - 1 Al2O3 - 1 MgO (wt %) (New)

    DLL       :    solid  ||  17006|0|0|-1
    MTE       :    solid  ||  17006|8|0|-1
    D         :    solid  ||  17006|24|0|-1
    Vis       :    liquid  ||  17006|26|1|-1

return to listing



67 SiO2 - 12 K2O - 8 ZrO2 - 6 Na2O - 4 ZnO - 1 CaO - 1 Al2O3 - 1 MgO (wt %) (New)

    DLL       :    solid  ||  17007|0|0|-1
    MTE       :    solid  ||  17007|8|0|-1
    D         :    solid  ||  17007|24|0|-1
    Vis       :    liquid  ||  17007|26|1|-1

return to listing



47 SiO2 - 8 MgO - 17 CaO - 14 Al2O3 - 4 K2O - 1.1 Na2O - 4.5 Fe - 1.4 Cr2O3 (wt %) (New)

    Vis       :    liquid  ||  16476|26|1|-1

return to listing



47 SiO2 - 8 MgO - 18 CaO - 14 Al2O3 - 4 K2O - 1.1 Na2O - 5 Fe - 0.9 Cr2O3 (wt %) (New)

    Vis       :    liquid  ||  16475|26|1|-1

return to listing



40 SiO2 - 8 MgO - 14 CaO - 11 Al2O3 - 3.2 K2O - 1.3 Na2O - 4 Fe - 15 Cu (wt %) (New)

    Vis       :    liquid  ||  16463|26|1|-1

return to listing



46 SiO2 - 9 MgO - 15 CaO - 12 Al2O3 - 4 K2O - 1.5 Na2O - 5 Fe - 3.6 Cu (wt %) (New)

    Vis       :    liquid  ||  16471|26|1|-1

return to listing



45 SiO2 - 9 MgO - 15 CaO - 11 Al2O3 - 3.6 K2O - 1.4 Na2O - 5 Fe - 6 Cu (wt %) (New)

    Vis       :    liquid  ||  16472|26|1|-1

return to listing



43 SiO2 - 8 MgO - 15 CaO - 11 Al2O3 - 3.5 K2O - 1.4 Na2O - 5 Fe - 9 Cu (wt %) (New)

    Vis       :    liquid  ||  16473|26|1|-1

return to listing



49 SiO2 - 8 MgO - 16 CaO - 14 Al2O3 - 4 K2O - 1 Na2O - 4.5 Fe (wt %) (New)

    Vis       :    liquid  ||  16461|26|1|-1

return to listing



52 SiO2 - 8 MgO - 16 CaO - 13 Al2O3 - 3 K2O - 1 Na2O - 3.8 Fe (wt %) (New)

    Vis       :    liquid  ||  16462|26|1|-1

return to listing



55 SiO2 - 7 MgO - 14 CaO - 13 Al2O3 - 3.3 K2O - 0.8 Na2O - 4 Fe (wt %) (New)

    Vis       :    liquid  ||  16477|26|1|-1

return to listing



30 SiO2 - 8 MgO - 42 CaO - 9 Al2O3 - 2.3 K2O - 1 Na2O - 3.8 Fe (wt %) (New)

    Vis       :    liquid  ||  16467|26|1|-1

return to listing



41 SiO2 - 19 MgO - 16 CaO - 11 Al2O3 - 3.2 K2O - 1.2 Na2O - 5 Fe (wt %) (New)

    Vis       :    liquid  ||  16474|26|1|-1

return to listing



48 SiO2 - 8 MgO - 16 CaO - 12 Al2O3 - 4 K2O - 1.5 Na2O - 5.6 Fe (wt %) (New)

    Vis       :    liquid  ||  16460|26|1|-1

return to listing



43 SiO2 - 12 MgO - 21 CaO - 12 Al2O3 - 3 K2O - 1.3 Na2O - 5 Fe (wt %) (New)

    Vis       :    liquid  ||  16464|26|1|-1

return to listing



40 SiO2 - 10 MgO - 25 CaO - 13 Al2O3 - 3 K2O - 1.2 Na2O - 4.7 Fe (wt %) (New)

    Vis       :    liquid  ||  16465|26|1|-1

return to listing



36 SiO2 - 9 MgO - 32 CaO - 12 Al2O3 - 3 K2O - 1 Na2O - 4.5 Fe (wt %) (New)

    Vis       :    liquid  ||  16466|26|1|-1

return to listing



44 SiO2 - 7.6 MgO - 15 CaO - 10 Al2O3 - 3.5 K2O - 1.4 Na2O - 12 Fe2O3 - 12 Fe (wt %) (New)

    Vis       :    liquid  ||  16469|26|1|-1

return to listing



41 SiO2 - 7.2 MgO - 14 CaO - 9 Al2O3 - 3 K2O - 1.3 Na2O - 20 Fe2O3 - 16 Fe (wt %) (New)

    Vis       :    liquid  ||  16470|26|1|-1

return to listing



46 SiO2 - 8 MgO - 16 CaO - 11 Al2O3 - 4 K2O - 1.1 Na2O - 6 Fe2O3 - 9 Fe (wt %) (New)

    Vis       :    liquid  ||  16468|26|1|-1

return to listing



59 SiO2 - 35 Na2O - 6 Al2O3 (mol %)

    D     (N*):    solid  ||  glassy  ||  15132|24|0|0
    RIT    (N):    solid, measured in vacuum  ||  measured at 632.8 nm  ||  15132|46|0|0
    RIT    (N):    liquid, measured in vacuum  ||  measured at 632.8 nm  ||  15132|46|1|0

return to listing



60 SiO2 - 20 Na2O - 20 Al2O3 (mol %) (New)

    DLL       :    glass  ||  16607|0|0|-1
    MTE       :    glass  ||  16607|8|0|-1
    D         :    glass  ||  16607|24|0|-1
    RIT       :    solid, measured in vacuum  ||  measured at 632.8 nm  ||  16607|46|0|0
    RIT       :    liquid, measured in vacuum  ||  measured at 632.8 nm  ||  16607|46|1|0

return to listing



50 SiO2 - 25 Na2O - 25 Al2O3 (mol %) (New)

    D     (*):    solid  ||  glassy  ||  16609|24|0|0
    RIT       :    solid, measured in vacuum  ||  measured at 632.8 nm  ||  16609|46|0|0
    RIT       :    liquid, measured in vacuum  ||  measured at 632.8 nm  ||  16609|46|1|0

return to listing



75 SiO2 - 12.5 Na2O - 12.5 Al2O3 (mol %) (New)

    D     (*):    solid  ||  glassy  ||  16610|24|0|0
    RIT       :    solid, measured in vacuum  ||  measured at 632.8 nm  ||  16610|46|0|0
    RIT       :    liquid, measured in vacuum  ||  measured at 632.8 nm  ||  16610|46|1|0

return to listing



60 SiO2 - 28 Na2O - 12 Al2O3 (mol %) (New)

    D     (*):    solid  ||  glassy  ||  16606|24|0|0
    RIT       :    solid, measured in vacuum  ||  measured at 632.8 nm  ||  16606|46|0|0
    RIT       :    liquid, measured in vacuum  ||  measured at 632.8 nm  ||  16606|46|1|0

return to listing



60 SiO2 - 26.7 Na2O - 13.3 Al2O3 (mol %) (New)

    DLL       :    glass  ||  16968|0|0|-1
    MTE       :    glass  ||  16968|8|0|-1
    D         :    glass  ||  16968|24|0|-1

return to listing



70 SiO2 - 25 Na2O - 3 CaO - 1 Al2O3 - 1 TiO2 (wt %) (New)

    RHO       :    solid  ||  16976|2|0|-1
    SIGMA     :    solid  ||  16976|10|0|-1
    RIW       :    measured in air  ||  tested at 20 °C (68 °F)  ||  16976|45|0|0

return to listing



65 SiO2 - 25 Na2O - 5 ZnO - 3 CaO - 1 Al2O3 - 1 TiO2 (wt %) (New)

    RHO       :    solid  ||  16977|2|0|-1
    SIGMA     :    solid  ||  16977|10|0|-1
    RIW       :    measured in air  ||  tested at 20 °C (68 °F)  ||  16977|45|0|0

return to listing



60 SiO2 - 25 Na2O - 10 ZnO - 3 CaO - 1 Al2O3 - 1 TiO2 (wt %) (New)

    RHO       :    solid  ||  16978|2|0|-1
    SIGMA     :    solid  ||  16978|10|0|-1
    RIW       :    measured in air  ||  tested at 20 °C (68 °F)  ||  16978|45|0|0

return to listing



55 SiO2 - 25 Na2O - 15 ZnO - 3 CaO - 1 Al2O3 - 1 TiO2 (wt %) (New)

    RHO       :    solid  ||  16979|2|0|-1
    SIGMA     :    solid  ||  16979|10|0|-1
    RIW       :    measured in air  ||  tested at 20 °C (68 °F)  ||  16979|45|0|0

return to listing



55 SiO2 - 45 Na2O (mol %) slag (New)

    TC        :    liquid  ||  16719|1|1|-1
    SH    (*):    solid  ||  16719|9|0|-1
    D     (*):    solid  ||  16719|24|0|-1

return to listing



70 SiO2 - 30 Na2O (mol %) slag (New)

    TC        :    liquid  ||  16720|1|1|-1
    SH    (*):    solid  ||  16720|9|0|-1
    D     (*):    solid  ||  16720|24|0|-1

return to listing



60 SiO2 - 40 Na2O (mol %) (New)

    RIT       :    solid, measured in vacuum  ||  measured at 632.8 nm  ||  16608|46|0|0
    RIT       :    liquid, measured in vacuum  ||  measured at 632.8 nm  ||  16608|46|1|0

return to listing



Sn - 30.6 Bi (wt %) (New)

    DLL       :    liquid  ||  16359|0|1|-1
    MTE       :    liquid  ||  16359|8|1|-1
    CTE       :    liquid  ||  16359|16|1|-1
    D         :    liquid  ||  16359|24|1|-1
    ST        :    liquid  ||  16359|38|1|-1

return to listing



63 Sn - 37 Pb (wt %)

    TC     (N):    liquid  ||  2739|1|1|-1
    SSC    (N):    casting  ||  tested at -150 °C (-238 °F), 6.67 x 10-4/s  ||  2739|4|0|0
    SSC    (N):    casting  ||  tested at -100 °C (-148 °F), 6.67 x 10-4/s  ||  2739|4|0|1
    SSC    (N):    casting  ||  tested at -50 °C (-58 °F), 6.67 x 10-4/s  ||  2739|4|0|2
    SSC    (N):    casting  ||  tested at 0 °C (32 °F), 6.67 x 10-4/s  ||  2739|4|0|6
    UTS    (N):    solid  ||  6.67 x 10-4/s strain rate  ||  2739|5|0|4
    YS     (N):    solid  ||  6.67 x 10-4/s strain rate  ||  2739|13|0|4
    %El    (N):    solid  ||  6.67 x 10-4/s strain rate  ||  2739|29|0|4
    ST     (N):    liquid  ||  2739|38|1|-1

return to listing



70 Sn - 30 Pb (wt %)

    ST     (N):    liquid  ||  15383|38|1|-1

return to listing



10 Sn - 90 Pb (wt %)

    ST     (N):    liquid  ||  2737|38|1|-1

return to listing



20 Sn - 80 Pb (wt %)

    ST     (N):    liquid  ||  15380|38|1|-1

return to listing



25 Sn - 75 Pb (wt %)

    ST     (N):    liquid  ||  12310|38|1|-1

return to listing



60 Sn - 40 Pb (wt %)

    ST     (N):    liquid  ||  2738|38|1|-1

return to listing



36 Sn - 64 Pb (wt %) (New)

    ST        :    liquid  ||  16554|38|1|-1

return to listing



48 Sn - 52 Pb (wt %) (New)

    ST        :    liquid  ||  16558|38|1|-1

return to listing



52 Sn - 48 Pb (wt %) (New)

    ST        :    liquid  ||  16555|38|1|-1

return to listing



74 Sn - 26 Pb (wt %) (New)

    ST        :    liquid  ||  16557|38|1|-1

return to listing



88 Sn - 12 Pb (wt %) (New)

    ST        :    liquid  ||  16556|38|1|-1

return to listing



5 Sn - 95 Pb (wt %)

    ST     (R):    liquid  ||  2736|38|1|-1

return to listing



Sn - 62 Zn (wt %) (New)

    DLL       :    liquid  ||  16438|0|1|-1
    MTE       :    liquid  ||  16438|8|1|-1
    CTE       :    liquid  ||  16438|16|1|-1
    D         :    liquid  ||  16438|24|1|-1
    Vis       :    liquid  ||  16438|26|1|-1

return to listing



Sn - 83 Zn (wt %) (New)

    DLL       :    liquid  ||  16437|0|1|-1
    MTE       :    liquid  ||  16437|8|1|-1
    CTE       :    liquid  ||  16437|16|1|-1
    D         :    liquid  ||  16437|24|1|-1
    Vis       :    liquid  ||  16437|26|1|-1

return to listing



Sn - 5 Zn (wt %) (New)

    DLL       :    liquid  ||  16440|0|1|-1
    MTE       :    liquid  ||  16440|8|1|-1
    CTE       :    liquid  ||  16440|16|1|-1
    D         :    liquid  ||  16440|24|1|-1
    Vis       :    liquid  ||  16440|26|1|-1

return to listing



Sn - 8 Zn (wt %) (New)

    DLL       :    liquid  ||  16381|0|1|-1
    TC        :    liquid  ||  16381|1|1|-1
    MTE       :    liquid  ||  16381|8|1|-1
    CTE       :    liquid  ||  16381|16|1|-1
    D         :    liquid  ||  16381|24|1|-1
    Vis       :    liquid  ||  16381|26|1|-1

return to listing



Sn - 35 Zn (wt %) (New)

    DLL       :    liquid  ||  16439|0|1|-1
    MTE       :    liquid  ||  16439|8|1|-1
    CTE       :    liquid  ||  16439|16|1|-1
    D         :    liquid  ||  16439|24|1|-1
    Vis       :    liquid  ||  16439|26|1|-1

return to listing



Sn - 9 Zn (wt %)

    DLL    (R):    liquid  ||  2760|0|1|-1
    MTE    (R):    liquid  ||  2760|8|1|-1
    CTE    (R):    liquid  ||  2760|16|1|-1
    D      (R):    liquid  ||  2760|24|1|-1
    Vis    (R):    liquid  ||  2760|26|1|-1

return to listing



Soderberg electrode paste (New)

    TC        :    65 °C (149 °F) softening point binder  ||  16890|1|0|-1
    TC        :    90 °C (194 °F) softening point binder  ||  16890|1|1|-1
    TC        :    90 °C (194 °F) softening point binder, baked to 1200 °C (2192 °F)  ||  16890|1|2|-1
    TD        :    65 °C (149 °F) softening point binder  ||  16890|25|0|-1
    TD        :    90 °C (194 °F) softening point binder  ||  16890|25|1|-1
    TD        :    90 °C (194 °F) softening point binder, baked to 1200 °C (2192 °F)  ||  16890|25|2|-1

return to listing



Soybean oil

    SH     (N):    liquid  ||  3413|9|1|-1

return to listing



Sunflower oil

    SH     (N):    liquid  ||  3415|9|1|-1

return to listing



Ta - 8 W - 2 Hf (wt %) (T-111)

    SR     (N):    cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  2326|22|0|0
    SR     (N):    cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  2326|22|0|1
    SR     (N):    cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  2326|22|0|2
    SR     (N):    cold worked sheet  ||  Master curve (LMP)  ||  2326|22|0|3
    CRS    (N):    1% plastic strain, cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  2326|30|0|0
    CRS    (N):    1% plastic strain, cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  2326|30|0|1
    CRS    (N):    1% plastic strain, cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  2326|30|0|2
    CRS    (N):    2% plastic strain, cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  2326|30|1|0
    CRS    (N):    2% plastic strain, cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  2326|30|1|1
    CRS    (N):    2% plastic strain, cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  2326|30|1|2
    CRS    (N):    2% plastic strain, cold worked sheet  ||  Master curve (LMP)  ||  2326|30|1|3
    CRS    (N):    5% plastic strain, cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  2326|30|2|0
    CRS    (N):    5% plastic strain, cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  2326|30|2|1
    CRS    (N):    5% plastic strain, cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  2326|30|2|2
    CRS    (N):    5% plastic strain, cold worked sheet  ||  Master curve (LMP)  ||  2326|30|2|3
    CRS    (N):    10% plastic strain, cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  2326|30|3|0
    CRS    (N):    10% plastic strain, cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  2326|30|3|1
    CRS    (N):    10% plastic strain, cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  2326|30|3|2
    CRS    (N):    10% plastic strain, cold worked sheet  ||  Master curve (LMP)  ||  2326|30|3|3
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  1 h  ||  2326|39|0|0
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  2 h  ||  2326|39|0|1
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  3 h  ||  2326|39|0|2
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  5 h  ||  2326|39|0|3
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  10 h  ||  2326|39|0|4
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  30 h  ||  2326|39|0|5
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  100 h  ||  2326|39|0|6
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  150 h  ||  2326|39|0|7
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  200 h  ||  2326|39|0|8
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  300 h  ||  2326|39|0|9
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  400 h  ||  2326|39|0|10
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  500 h  ||  2326|39|0|11
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  1 h  ||  2326|39|1|0
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  2 h  ||  2326|39|1|1
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  3 h  ||  2326|39|1|2
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  5 h  ||  2326|39|1|3
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  10 h  ||  2326|39|1|4
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  30 h  ||  2326|39|1|5
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  100 h  ||  2326|39|1|6
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  150 h  ||  2326|39|1|7
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  200 h  ||  2326|39|1|8
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  300 h  ||  2326|39|1|9
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  400 h  ||  2326|39|1|10
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  1 h  ||  2326|39|2|0
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  2 h  ||  2326|39|2|1
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  3 h  ||  2326|39|2|2
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  5 h  ||  2326|39|2|3
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  10 h  ||  2326|39|2|4
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  30 h  ||  2326|39|2|5
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  100 h  ||  2326|39|2|6
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  150 h  ||  2326|39|2|7
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  200 h  ||  2326|39|2|8

return to listing



Ta - 10 W (wt %)

    SR     (N):    cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  2324|22|0|1
    SR     (N):    cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  2324|22|0|3
    SR     (N):    cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  2324|22|0|4
    SR     (R):    cold worked sheet  ||  Master curve (LMP)  ||  2324|22|0|5
    CRS    (N):    1% plastic strain, cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  2324|30|1|0
    CRS    (N):    1% plastic strain, cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  2324|30|1|1
    CRS    (N):    1% plastic strain, cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  2324|30|1|2
    CRS    (N):    2% plastic strain, cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  2324|30|2|0
    CRS    (N):    2% plastic strain, cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  2324|30|2|1
    CRS    (N):    2% plastic strain, cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  2324|30|2|2
    CRS    (N):    5% plastic strain, cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  2324|30|3|0
    CRS    (N):    5% plastic strain, cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  2324|30|3|1
    CRS    (N):    5% plastic strain, cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  2324|30|3|2
    CRS    (N):    10% plastic strain, cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  2324|30|4|0
    CRS    (N):    10% plastic strain, cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  2324|30|4|1
    CRS    (N):    10% plastic strain, cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  2324|30|4|2
    CRS    (N):    10% plastic strain, cold worked sheet  ||  Master curve (LMP)  ||  2324|30|4|3
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  1 h  ||  2324|39|0|0
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  2 h  ||  2324|39|0|1
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  4 h  ||  2324|39|0|2
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  10 h  ||  2324|39|0|3
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  30 h  ||  2324|39|0|4
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  50 h  ||  2324|39|0|5
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  100 h  ||  2324|39|0|6
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  150 h  ||  2324|39|0|7
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  200 h  ||  2324|39|0|8
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  250 h  ||  2324|39|0|9
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  300 h  ||  2324|39|0|10
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  1 h  ||  2324|39|1|0
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  2 h  ||  2324|39|1|1
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  4 h  ||  2324|39|1|2
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  10 h  ||  2324|39|1|3
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  30 h  ||  2324|39|1|4
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  50 h  ||  2324|39|1|5
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  100 h  ||  2324|39|1|6
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  150 h  ||  2324|39|1|7
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  200 h  ||  2324|39|1|8
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  250 h  ||  2324|39|1|9
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  300 h  ||  2324|39|1|10
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  1 h  ||  2324|39|2|0
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  2 h  ||  2324|39|2|1
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  4 h  ||  2324|39|2|2
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  10 h  ||  2324|39|2|3
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  30 h  ||  2324|39|2|4
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  50 h  ||  2324|39|2|5
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  100 h  ||  2324|39|2|6

return to listing



Tantalum

    SR     (N):    cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  907|22|1|0
    SR     (N):    cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  907|22|1|1
    SR     (N):    cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  907|22|1|2
    SR     (N):    cold worked sheet  ||  Master curve (LMP)  ||  907|22|1|3
    CRS    (N):    1% plastic strain, cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  907|30|4|0
    CRS    (N):    1% plastic strain, cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  907|30|4|1
    CRS    (N):    1% plastic strain, cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  907|30|4|2
    CRS    (N):    1% plastic strain, cold worked sheet  ||  Master curve (LMP)  ||  907|30|4|3
    CRS    (N):    2% plastic strain, cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  907|30|5|0
    CRS    (N):    2% plastic strain, cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  907|30|5|1
    CRS    (N):    2% plastic strain, cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  907|30|5|2
    CRS    (N):    2% plastic strain, cold worked sheet  ||  Master curve (LMP)  ||  907|30|5|3
    CRS    (N):    5% plastic strain, cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  907|30|6|0
    CRS    (N):    5% plastic strain, cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  907|30|6|1
    CRS    (N):    5% plastic strain, cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  907|30|6|2
    CRS    (N):    5% plastic strain, cold worked sheet  ||  Master curve (LMP)  ||  907|30|6|3
    CRS    (N):    10% plastic strain, cold worked sheet  ||  tested at 1204 °C (2200 °F)  ||  907|30|7|0
    CRS    (N):    10% plastic strain, cold worked sheet  ||  tested at 1427 °C (2600 °F)  ||  907|30|7|1
    CRS    (N):    10% plastic strain, cold worked sheet  ||  tested at 1649 °C (3000 °F)  ||  907|30|7|2
    CRS    (N):    10% plastic strain, cold worked sheet  ||  Master curve (LMP)  ||  907|30|7|3
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  0.3 h  ||  907|39|4|0
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  1 h  ||  907|39|4|1
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  2 h  ||  907|39|4|2
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  3 h  ||  907|39|4|3
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  5 h  ||  907|39|4|4
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  10 h  ||  907|39|4|5
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  30 h  ||  907|39|4|6
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  100 h  ||  907|39|4|7
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  150 h  ||  907|39|4|8
    IC     (N):    tested at 1204 °C (2200 °F), plastic strain, cold worked sheet  ||  200 h  ||  907|39|4|9
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  0.3 h  ||  907|39|5|0
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  1 h  ||  907|39|5|1
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  2 h  ||  907|39|5|2
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  3 h  ||  907|39|5|3
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  5 h  ||  907|39|5|4
    IC     (N):    tested at 1427 °C (2600 °F), plastic strain, cold worked sheet  ||  10 h  ||  907|39|5|5
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  0.3 h  ||  907|39|6|0
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  1 h  ||  907|39|6|1
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  2 h  ||  907|39|6|2
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  3 h  ||  907|39|6|3
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  5 h  ||  907|39|6|4
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  10 h  ||  907|39|6|5
    IC     (N):    tested at 1649 °C (3000 °F), plastic strain, cold worked sheet  ||  30 h  ||  907|39|6|6

return to listing



Tellurium

    DLL    (R):    liquid  ||  886|0|1|-1
    MTE    (R):    liquid  ||  886|8|1|-1
    CTE    (R):    liquid  ||  886|16|1|-1
    D      (R):    liquid  ||  886|24|1|-1

return to listing



Thallium

    TC     (R):    solid  ||  annealed  ||  915|1|0|0
    TD     (R):    solid  ||  annealed  ||  915|25|0|0

return to listing



Ti - 6 Al - 2 Sn - 4 Zr - 2 Mo (wt %)

    SR     (N):    duplex annealed  ||  tested at 482 °C (900 °F)  ||  2846|22|1|0
    SR     (N):    duplex annealed  ||  tested at 593 °C (1100 °F)  ||  2846|22|1|1
    SR     (N):    duplex annealed  ||  Master curve (LMP)  ||  2846|22|1|2

return to listing



Ti - 6 Al - 4 V (Grade 5)

    SSC    (N):    metal injection molded  ||  tested at 20 °C (68 °F), 0.00278/s, sintered at 1100 °C (2012 °F)  ||  8958|4|0|0
    SSC    (N):    metal injection molded  ||  tested at 20 °C (68 °F), 0.00278/s, sintered at 1150 °C (2102 °F)  ||  8958|4|0|1

return to listing



Ti - 6 Al - 4 V

    FSN    (N):    annealed  ||  tested at 25 °C (77 °F), R = -1, Kt = 2, axial, maximum stress  ||  2836|6|0|16
    FSN    (N):    annealed  ||  tested at 316 °C (600 °F), R = -1, Kt = 2, axial, maximum stress  ||  2836|6|0|17

return to listing



Ti - 6 Al - 4 Zr - 4 Nb (wt %) (New)

    YSC       :    spark plasma sintered  ||  as-built  ||  16377|21|0|0
    YSC       :    laser powder bed fusion  ||  energy density = 50 J/mm3, as-built  ||  16377|21|1|0
    YSC       :    laser powder bed fusion  ||  energy density = 42 J/mm3, as-built  ||  16377|21|1|1
    YSC       :    laser powder bed fusion  ||  energy density = 36 J/mm3, as-built  ||  16377|21|1|2
    YSC       :    laser powder bed fusion  ||  energy density = 160 J/mm3, as-built  ||  16377|21|1|3
    YSC       :    laser powder bed fusion  ||  energy density = 42 J/mm3, stress-relieved  ||  16377|21|1|4
    YSC       :    laser powder bed fusion  ||  energy density = 160 J/mm3, stress-relieved  ||  16377|21|1|5
    YSC       :    laser powder bed fusion  ||  energy density = 42 J/mm3, aged  ||  16377|21|1|6
    YSC       :    laser powder bed fusion  ||  energy density = 160 J/mm3, aged  ||  16377|21|1|7
    YSC       :    laser powder bed fusion  ||  energy density = 42 J/mm3, HIPed  ||  16377|21|1|8
    YSC       :    laser powder bed fusion  ||  energy density = 160 J/mm3, HIPed  ||  16377|21|1|9
    YSC       :    forged  ||  bimodal structure  ||  16377|21|2|0
    YSC       :    forged  ||  lamellar structure  ||  16377|21|2|1

return to listing



Ti3Al

    DLL    (R):    solid  ||  polycrystal  ||  1567|0|0|0
    DLL    (N):    solid  ||  a-axis  ||  1567|0|0|1
    DLL    (N):    solid  ||  c-axis  ||  1567|0|0|2
    MTE    (R):    solid  ||  polycrystal  ||  1567|8|0|0
    MTE    (N):    solid  ||  a-axis  ||  1567|8|0|1
    MTE    (N):    solid  ||  c-axis  ||  1567|8|0|2
    D      (R):    solid  ||  1567|24|0|-1

return to listing



TiC

    TC     (N):    solid  ||  spark plasma sintered, 94.3% dense, Ozer et. al.  ||  203|1|0|1
    RHO    (N):    solid  ||  spark plasma sintered, 94.3% dense, Ozer et. al.  ||  203|2|0|2
    SIGMA  (N):    solid  ||  spark plasma sintered, 94.3% dense, Ozer et. al.  ||  203|10|0|2
    TD     (N):    solid  ||  spark plasma sintered, 94.3% dense, Ozer et. al.  ||  203|25|0|1
    NE     (N):    solid  ||  Fisenko and Lemberg  ||  203|28|0|1
    S      (N):    Ozer et. al.  ||  spark plasma sintered  ||  203|48|0|0

return to listing



86 TiO2 - 6 FeO - 0.0 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)

    RHO       :    solid  ||  16867|2|0|-1
    SIGMA     :    solid  ||  16867|10|0|-1

return to listing



72.1 TiO2 - 6 FeO - 13.9 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)

    RHO       :    solid  ||  16856|2|0|-1
    SIGMA     :    solid  ||  16856|10|0|-1

return to listing



69.6 TiO2 - 9 FeO - 13.4 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)

    RHO       :    solid  ||  16857|2|0|-1
    SIGMA     :    solid  ||  16857|10|0|-1

return to listing



67.1 TiO2 - 12 FeO - 12.9 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)

    RHO       :    solid  ||  16858|2|0|-1
    SIGMA     :    solid  ||  16858|10|0|-1

return to listing



64.6 TiO2 - 15 FeO - 12.4 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)

    RHO       :    solid  ||  16859|2|0|-1
    SIGMA     :    solid  ||  16859|10|0|-1

return to listing



75.0 TiO2 - 9.5 FeO - 7.5 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)

    RHO       :    solid  ||  16860|2|0|-1
    SIGMA     :    solid  ||  16860|10|0|-1

return to listing



67.3 TiO2 - 9.6 FeO - 15.1 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)

    RHO       :    solid  ||  16861|2|0|-1
    SIGMA     :    solid  ||  16861|10|0|-1

return to listing



59.4 TiO2 - 9.7 FeO - 22.9 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)

    RHO       :    solid  ||  16862|2|0|-1
    SIGMA     :    solid  ||  16862|10|0|-1

return to listing



51.4 TiO2 - 9.8 FeO - 30.8 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)

    RHO       :    solid  ||  16863|2|0|-1
    SIGMA     :    solid  ||  16863|10|0|-1

return to listing



77 TiO2 - 15 FeO - 0.0 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)

    RHO       :    solid  ||  16864|2|0|-1
    SIGMA     :    solid  ||  16864|10|0|-1

return to listing



80 TiO2 - 12 FeO - 0.0 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)

    RHO       :    solid  ||  16865|2|0|-1
    SIGMA     :    solid  ||  16865|10|0|-1

return to listing



83 TiO2 - 9 FeO - 0.0 Ti2O3 - 1 CaO - 3 SiO2 - 2 MgO - 2 Al2O3 (wt %) slag (New)

    RHO       :    solid  ||  16866|2|0|-1
    SIGMA     :    solid  ||  16866|10|0|-1

return to listing



81 Tl - 17 Cd - 2 Bi (wt %) (New)

    DLL       :    liquid  ||  16578|0|1|-1
    MTE       :    liquid  ||  16578|8|1|-1
    CTE       :    liquid  ||  16578|16|1|-1
    D         :    liquid  ||  16578|24|1|-1

return to listing



13 Tl - 26 Cd - 61 Bi (wt %) (New)

    DLL       :    liquid  ||  16579|0|1|-1
    MTE       :    liquid  ||  16579|8|1|-1
    CTE       :    liquid  ||  16579|16|1|-1
    D         :    liquid  ||  16579|24|1|-1

return to listing



44 Tl - 11 Cd - 45 Bi (wt %) (New)

    DLL       :    liquid  ||  16577|0|1|-1
    MTE       :    liquid  ||  16577|8|1|-1
    CTE       :    liquid  ||  16577|16|1|-1
    D         :    liquid  ||  16577|24|1|-1

return to listing



TRIP 9 Cr - 8 Ni - 4 Mo - 3 Mn - 3 Si (wt %) (New)

    SSC       :    processed at 450 °C (842 °F)  ||  tested at 25 °C (77 °F), deformed 20%, unknown strain rate  ||  16384|4|0|0
    SSC       :    processed at 450 °C (842 °F)  ||  tested at 200 °C (392 °F), deformed 20%, unknown strain rate  ||  16384|4|0|1
    SSC       :    processed at 450 °C (842 °F)  ||  tested at 25 °C (77 °F), deformed 80%, unknown strain rate  ||  16384|4|0|2
    SSC       :    processed at 450 °C (842 °F)  ||  tested at 200 °C (392 °F), deformed 80%, unknown strain rate  ||  16384|4|0|3
    SSC       :    processed at 250 °C (482 °F)  ||  tested at 25 °C (77 °F), deformed 20%, unknown strain rate  ||  16384|4|1|0
    SSC       :    processed at 250 °C (482 °F)  ||  tested at 200 °C (392 °F), deformed 20%, unknown strain rate  ||  16384|4|1|1
    SSC       :    processed at 250 °C (482 °F)  ||  tested at 25 °C (77 °F), deformed 80%, unknown strain rate  ||  16384|4|1|2
    SSC       :    processed at 250 °C (482 °F)  ||  tested at 200 °C (392 °F), deformed 80%, unknown strain rate  ||  16384|4|1|3
    FSN       :    processed at 450 °C (842 °F)  ||  tested at 25 °C (77 °F), R = -1, axial, deformed 20%, stress range  ||  16384|6|0|0
    FSN       :    processed at 450 °C (842 °F)  ||  tested at 200 °C (392 °F), R = -1, axial, deformed 20%, stress range  ||  16384|6|0|1
    FSN       :    processed at 450 °C (842 °F)  ||  tested at 25 °C (77 °F), R = -1, axial, deformed 80%, stress range  ||  16384|6|0|2
    FSN       :    processed at 450 °C (842 °F)  ||  tested at 200 °C (392 °F), R = -1, axial, deformed 80%, stress range  ||  16384|6|0|3
    FSN       :    processed at 250 °C (482 °F)  ||  tested at 25 °C (77 °F), R = -1, axial, deformed 20%, stress range  ||  16384|6|1|0
    FSN       :    processed at 250 °C (482 °F)  ||  tested at 200 °C (392 °F), R = -1, axial, deformed 20%, stress range  ||  16384|6|1|1
    FSN       :    processed at 250 °C (482 °F)  ||  tested at 25 °C (77 °F), R = -1, axial, deformed 80%, stress range  ||  16384|6|1|2
    FSN       :    processed at 250 °C (482 °F)  ||  tested at 200 °C (392 °F), R = -1, axial, deformed 80%, stress range  ||  16384|6|1|3
    FEN       :    processed at 450 °C (842 °F)  ||  tested at 25 °C (77 °F), R = -1, axial, deformed 20%, plastic strain range  ||  16384|14|0|0
    FEN       :    processed at 450 °C (842 °F)  ||  tested at 200 °C (392 °F), R = -1, axial, deformed 20%, plastic strain range  ||  16384|14|0|1
    FEN       :    processed at 450 °C (842 °F)  ||  tested at 25 °C (77 °F), R = -1, axial, deformed 80%, plastic strain range  ||  16384|14|0|2
    FEN       :    processed at 450 °C (842 °F)  ||  tested at 200 °C (392 °F), R = -1, axial, deformed 80%, plastic strain range  ||  16384|14|0|3
    FEN       :    processed at 450 °C (842 °F)  ||  tested at 25 °C (77 °F), R = -1, axial, deformed 20%, total strain range  ||  16384|14|0|4
    FEN       :    processed at 450 °C (842 °F)  ||  tested at 200 °C (392 °F), R = -1, axial, deformed 20%, total strain range  ||  16384|14|0|5
    FEN       :    processed at 450 °C (842 °F)  ||  tested at 25 °C (77 °F), R = -1, axial, deformed 80%, total strain range  ||  16384|14|0|6
    FEN       :    processed at 450 °C (842 °F)  ||  tested at 200 °C (392 °F), R = -1, axial, deformed 80%, total strain range  ||  16384|14|0|7
    FEN       :    processed at 250 °C (482 °F)  ||  tested at 25 °C (77 °F), R = -1, axial, deformed 20%, plastic strain range  ||  16384|14|1|0
    FEN       :    processed at 250 °C (482 °F)  ||  tested at 200 °C (392 °F), R = -1, axial, deformed 20%, plastic strain range  ||  16384|14|1|1
    FEN       :    processed at 250 °C (482 °F)  ||  tested at 25 °C (77 °F), R = -1, axial, deformed 80%, plastic strain range  ||  16384|14|1|2
    FEN       :    processed at 250 °C (482 °F)  ||  tested at 200 °C (392 °F), R = -1, axial, deformed 80%, plastic strain range  ||  16384|14|1|3
    FEN       :    processed at 250 °C (482 °F)  ||  tested at 25 °C (77 °F), R = -1, axial, deformed 20%, total strain range  ||  16384|14|1|4
    FEN       :    processed at 250 °C (482 °F)  ||  tested at 200 °C (392 °F), R = -1, axial, deformed 20%, total strain range  ||  16384|14|1|5
    FEN       :    processed at 250 °C (482 °F)  ||  tested at 25 °C (77 °F), R = -1, axial, deformed 80%, total strain range  ||  16384|14|1|6
    FEN       :    processed at 250 °C (482 °F)  ||  tested at 200 °C (392 °F), R = -1, axial, deformed 80%, total strain range  ||  16384|14|1|7

return to listing



Tritan FX200 (New)

    DLL       :    solid  ||  16369|0|0|-1
    E     (*):    254 mm/min  ||  machine direction  ||  16369|3|0|0
    E     (*):    254 mm/min  ||  cross-machine direction  ||  16369|3|0|1
    UTS   (*):    254 mm/min  ||  machine direction  ||  16369|5|0|0
    UTS   (*):    254 mm/min  ||  cross-machine direction  ||  16369|5|0|1
    MTE       :    solid  ||  16369|8|0|-1
    SH        :    solid  ||  16369|9|0|-1
    YS    (*):    254 mm/min  ||  machine direction  ||  16369|13|0|0
    YS    (*):    254 mm/min  ||  cross-machine direction  ||  16369|13|0|1
    CTE       :    solid  ||  16369|16|0|-1
    D         :    solid  ||  16369|24|0|-1
    %El   (*):    254 mm/min, at break  ||  machine direction  ||  16369|29|0|0
    %El   (*):    254 mm/min, at break  ||  cross-machine direction  ||  16369|29|0|1
    %El   (*):    254 mm/min, at yield  ||  machine direction  ||  16369|29|1|0
    %El   (*):    254 mm/min, at yield  ||  cross-machine direction  ||  16369|29|1|1
    RIT   (*):    measured in air  ||  measured at 589.3 nm  ||  16369|46|0|0

return to listing



Tritan HX100 (New)

    DLL       :    solid  ||  16370|0|0|-1
    E     (*):    254 mm/min  ||  machine direction  ||  16370|3|0|0
    E     (*):    254 mm/min  ||  cross-machine direction  ||  16370|3|0|1
    UTS   (*):    254 mm/min  ||  machine direction  ||  16370|5|0|0
    UTS   (*):    254 mm/min  ||  cross-machine direction  ||  16370|5|0|1
    MTE       :    solid  ||  16370|8|0|-1
    SH        :    solid  ||  16370|9|0|-1
    YS    (*):    254 mm/min  ||  machine direction  ||  16370|13|0|0
    YS    (*):    254 mm/min  ||  cross-machine direction  ||  16370|13|0|1
    CTE       :    solid  ||  16370|16|0|-1
    D         :    solid  ||  16370|24|0|-1
    %El   (*):    254 mm/min, at break  ||  machine direction  ||  16370|29|0|0
    %El   (*):    254 mm/min, at break  ||  cross-machine direction  ||  16370|29|0|1
    %El   (*):    254 mm/min, at yield  ||  machine direction  ||  16370|29|1|0
    %El   (*):    254 mm/min, at yield  ||  cross-machine direction  ||  16370|29|1|1
    RIT   (*):    measured in air  ||  measured at 589.3 nm  ||  16370|46|0|0

return to listing



Tritan MP100 (New)

    DLL       :    solid  ||  16371|0|0|-1
    E     (*):    254 mm/min  ||  machine direction  ||  16371|3|0|0
    E     (*):    254 mm/min  ||  cross-machine direction  ||  16371|3|0|1
    UTS   (*):    254 mm/min  ||  machine direction  ||  16371|5|0|0
    UTS   (*):    254 mm/min  ||  cross-machine direction  ||  16371|5|0|1
    MTE       :    solid  ||  16371|8|0|-1
    SH        :    solid  ||  16371|9|0|-1
    YS    (*):    254 mm/min  ||  machine direction  ||  16371|13|0|0
    YS    (*):    254 mm/min  ||  cross-machine direction  ||  16371|13|0|1
    CTE       :    solid  ||  16371|16|0|-1
    D         :    solid  ||  16371|24|0|-1
    %El   (*):    254 mm/min, at break  ||  machine direction  ||  16371|29|0|0
    %El   (*):    254 mm/min, at break  ||  cross-machine direction  ||  16371|29|0|1
    %El   (*):    254 mm/min, at yield  ||  machine direction  ||  16371|29|1|0
    %El   (*):    254 mm/min, at yield  ||  cross-machine direction  ||  16371|29|1|1
    RIT   (*):    measured in air  ||  measured at 589.3 nm  ||  16371|46|0|0

return to listing



Tritan MX711

    AV     (N):    liquid  ||  tested at 271 °C (520 °F)  ||  16358|34|1|0
    AV     (N):    liquid  ||  tested at 282 °C (540 °F)  ||  16358|34|1|1
    AV     (N):    liquid  ||  tested at 293 °C (560 °F)  ||  16358|34|1|2

return to listing



Udimet 500

    FSN    (N):    cast bars  ||  tested at 816 °C (1500 °F), R = -1, axial, 0.0016 cpm, stress amplitude  ||  1941|6|0|0
    FSN    (N):    cast bars  ||  tested at 816 °C (1500 °F), R = -1, axial, 0.04 cpm, stress amplitude  ||  1941|6|0|1
    FSN    (N):    cast bars  ||  tested at 816 °C (1500 °F), R = -1, axial, 1 cpm, stress amplitude  ||  1941|6|0|2
    FSN    (N):    cast bars  ||  tested at 816 °C (1500 °F), R = -1, axial, 25 cpm, stress amplitude  ||  1941|6|0|3
    FSN    (N):    cast bars  ||  tested at 816 °C (1500 °F), R = -1, axial, 625 cpm, stress amplitude  ||  1941|6|0|4
    FEN    (N):    cast bars  ||  tested at 816 °C (1500 °F), R = -1, axial, 0.0016 cpm, total strain range  ||  1941|14|0|0
    FEN    (N):    cast bars  ||  tested at 816 °C (1500 °F), R = -1, axial, 0.04 cpm, total strain range  ||  1941|14|0|1
    FEN    (N):    cast bars  ||  tested at 816 °C (1500 °F), R = -1, axial, 1 cpm, total strain range  ||  1941|14|0|2
    FEN    (N):    cast bars  ||  tested at 816 °C (1500 °F), R = -1, axial, 25 cpm, total strain range  ||  1941|14|0|3
    FEN    (N):    cast bars  ||  tested at 816 °C (1500 °F), R = -1, axial, 625 cpm, total strain range  ||  1941|14|0|4

return to listing



UNS C11000 (ETP)

    TC     (R):    solid  ||  741|1|0|-1

return to listing



UNS C43000

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9708|5|0|0
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|5|2|0
    UTS   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|5|3|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|5|4|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|5|5|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9708|5|6|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9708|5|7|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9708|13|0|0
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|13|2|0
    YS    (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|13|3|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|13|4|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|13|5|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9708|13|6|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9708|13|7|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9708|29|0|0
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|29|2|0
    %El   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|29|3|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|29|4|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9708|29|5|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9708|29|6|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9708|29|7|0

return to listing



UNS C43400

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9709|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9709|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9709|5|0|2
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|5|2|0
    UTS   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|5|3|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|5|4|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|5|5|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9709|5|6|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9709|5|7|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9709|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9709|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9709|13|0|2
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|13|2|0
    YS    (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|13|3|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|13|4|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|13|5|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9709|13|6|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9709|13|7|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9709|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9709|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9709|29|0|2
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|29|2|0
    %El   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|29|3|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|29|4|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9709|29|5|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9709|29|6|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9709|29|7|0

return to listing



UNS C43500

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9710|5|0|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9710|5|1|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9710|5|2|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9710|13|0|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9710|13|1|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9710|13|2|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9710|29|0|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9710|29|1|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9710|29|2|0

return to listing



UNS C44300

    RHO    (N):    solid  ||  annealed  ||  778|2|0|0
    RHO    (N):    solid  ||  fully cold worked  ||  778|2|0|1
    SIGMA  (N):    solid  ||  annealed  ||  778|10|0|0
    SIGMA  (N):    solid  ||  fully cold worked  ||  778|10|0|1

return to listing



UNS C46500

    UTS   (N*):    soft anneal  ||  6.35 mm (0.25 inch) rod  ||  9713|5|0|0
    UTS   (N*):    light anneal  ||  6.35 mm (0.25 inch) rod  ||  9713|5|1|0
    UTS   (N*):    quarter hard  ||  6.35 mm (0.25 inch) rod  ||  9713|5|2|0
    UTS   (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  9713|5|3|0
    YS    (N*):    soft anneal  ||  6.35 mm (0.25 inch) rod  ||  9713|13|0|0
    YS    (N*):    light anneal  ||  6.35 mm (0.25 inch) rod  ||  9713|13|1|0
    YS    (N*):    quarter hard  ||  6.35 mm (0.25 inch) rod  ||  9713|13|2|0
    YS    (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  9713|13|3|0
    %El   (N*):    soft anneal  ||  6.35 mm (0.25 inch) rod  ||  9713|29|0|0
    %El   (N*):    light anneal  ||  6.35 mm (0.25 inch) rod  ||  9713|29|1|0
    %El   (N*):    quarter hard  ||  6.35 mm (0.25 inch) rod  ||  9713|29|2|0
    %El   (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  9713|29|3|0

return to listing



UNS C46600

    UTS   (N*):    soft anneal  ||  6.35 mm (0.25 inch) rod  ||  9714|5|0|0
    UTS   (N*):    light anneal  ||  6.35 mm (0.25 inch) rod  ||  9714|5|1|0
    UTS   (N*):    quarter hard  ||  6.35 mm (0.25 inch) rod  ||  9714|5|2|0
    UTS   (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  9714|5|3|0
    YS    (N*):    soft anneal  ||  6.35 mm (0.25 inch) rod  ||  9714|13|0|0
    YS    (N*):    light anneal  ||  6.35 mm (0.25 inch) rod  ||  9714|13|1|0
    YS    (N*):    quarter hard  ||  6.35 mm (0.25 inch) rod  ||  9714|13|2|0
    YS    (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  9714|13|3|0
    %El   (N*):    soft anneal  ||  6.35 mm (0.25 inch) rod  ||  9714|29|0|0
    %El   (N*):    light anneal  ||  6.35 mm (0.25 inch) rod  ||  9714|29|1|0
    %El   (N*):    quarter hard  ||  6.35 mm (0.25 inch) rod  ||  9714|29|2|0
    %El   (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  9714|29|3|0

return to listing



UNS C46700

    UTS   (N*):    soft anneal  ||  6.35 mm (0.25 inch) rod  ||  9715|5|0|0
    UTS   (N*):    light anneal  ||  6.35 mm (0.25 inch) rod  ||  9715|5|1|0
    UTS   (N*):    quarter hard  ||  6.35 mm (0.25 inch) rod  ||  9715|5|2|0
    UTS   (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  9715|5|3|0
    YS    (N*):    soft anneal  ||  6.35 mm (0.25 inch) rod  ||  9715|13|0|0
    YS    (N*):    light anneal  ||  6.35 mm (0.25 inch) rod  ||  9715|13|1|0
    YS    (N*):    quarter hard  ||  6.35 mm (0.25 inch) rod  ||  9715|13|2|0
    YS    (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  9715|13|3|0
    %El   (N*):    soft anneal  ||  6.35 mm (0.25 inch) rod  ||  9715|29|0|0
    %El   (N*):    light anneal  ||  6.35 mm (0.25 inch) rod  ||  9715|29|1|0
    %El   (N*):    quarter hard  ||  6.35 mm (0.25 inch) rod  ||  9715|29|2|0
    %El   (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  9715|29|3|0

return to listing



UNS C48200

    UTS   (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9716|5|0|0
    UTS   (N*):    light anneal  ||  25.4 mm (1 inch) rod  ||  9716|5|1|0
    UTS   (N*):    quarter hard  ||  25.4 mm (1 inch) rod  ||  9716|5|2|0
    UTS   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9716|5|3|0
    YS    (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9716|13|0|0
    YS    (N*):    light anneal  ||  25.4 mm (1 inch) rod  ||  9716|13|1|0
    YS    (N*):    quarter hard  ||  25.4 mm (1 inch) rod  ||  9716|13|2|0
    YS    (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9716|13|3|0
    %El   (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9716|29|0|0
    %El   (N*):    light anneal  ||  25.4 mm (1 inch) rod  ||  9716|29|1|0
    %El   (N*):    quarter hard  ||  25.4 mm (1 inch) rod  ||  9716|29|2|0
    %El   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9716|29|3|0

return to listing



UNS C48500

    UTS   (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9717|5|0|0
    UTS   (N*):    quarter hard  ||  25.4 mm (1 inch) rod  ||  9717|5|1|0
    UTS   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9717|5|2|0
    YS    (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9717|13|0|0
    YS    (N*):    quarter hard  ||  25.4 mm (1 inch) rod  ||  9717|13|1|0
    YS    (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9717|13|2|0
    %El   (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9717|29|0|0
    %El   (N*):    quarter hard  ||  25.4 mm (1 inch) rod  ||  9717|29|1|0
    %El   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9717|29|2|0

return to listing



UNS C50500

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet  ||  780|5|0|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  780|5|1|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  780|5|2|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  780|5|3|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet  ||  780|13|0|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  780|13|2|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet  ||  780|29|0|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  780|29|1|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  780|29|2|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  780|29|3|0

return to listing



UNS C52100

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  783|5|1|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  783|5|1|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  783|5|1|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  783|5|1|3
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  783|5|2|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  783|5|3|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  783|5|4|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  783|5|5|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  783|5|6|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  783|13|1|2
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  783|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  783|13|3|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  783|13|4|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  783|29|1|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  783|29|1|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  783|29|1|2
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  783|29|1|3
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  783|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  783|29|3|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  783|29|4|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  783|29|5|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  783|29|6|0

return to listing



UNS C52400

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet  ||  784|5|0|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  784|5|1|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  784|5|2|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  784|5|3|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  784|5|4|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  784|5|5|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet  ||  784|13|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet  ||  784|29|0|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  784|29|1|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  784|29|2|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  784|29|3|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  784|29|4|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  784|29|5|0

return to listing



UNS C60600

    DLL    (N):    solid  ||  12434|0|0|-1
    TC     (N):    solid  ||  12434|1|0|-1
    RHO   (N*):    solid  ||  12434|2|0|-1
    E     (N*):    annealed  ||  12434|3|0|-1
    E     (N*):    lightly cold worked  ||  12434|3|1|-1
    MTE    (N):    solid  ||  12434|8|0|-1
    SH    (N*):    solid  ||  12434|9|0|-1
    SIGMA (N*):    solid  ||  12434|10|0|-1
    G     (N*):    annealed  ||  12434|11|0|-1
    G     (N*):    lightly cold worked  ||  12434|11|1|-1
    CTE    (N):    solid  ||  12434|16|0|-1
    v     (N*):    annealed  ||  12434|19|0|-1
    v     (N*):    lightly cold worked  ||  12434|19|1|-1
    D      (N):    solid  ||  12434|24|0|-1
    TD    (N*):    solid  ||  12434|25|0|-1
    K     (N*):    annealed  ||  12434|27|0|-1
    K     (N*):    lightly cold worked  ||  12434|27|1|-1

return to listing



UNS C60800

    UTS   (N*):    annealed  ||  25.4 mm (1 inch) tube, 25 micron grain size  ||  9718|5|0|0
    YS    (N*):    annealed  ||  25.4 mm (1 inch) tube, 25 micron grain size  ||  9718|13|0|0
    %El   (N*):    annealed  ||  25.4 mm (1 inch) tube, 25 micron grain size  ||  9718|29|0|0

return to listing



UNS C61000

    UTS    (N):    annealed  ||  3 mm (0.118 inch) rod  ||  9719|5|0|0
    UTS   (N*):    soft anneal  ||  25.4 mm (1 inch) thick plate  ||  9719|5|1|0
    UTS   (N*):    hard  ||  sheet 12.7 mm (0.5 inch) and under  ||  9719|5|2|0
    UTS   (N*):    hard  ||  plate over 12.7 mm (0.5 inch)  ||  9719|5|2|1
    YS     (N):    annealed  ||  3 mm (0.118 inch) rod  ||  9719|13|0|0
    YS    (N*):    soft anneal  ||  25.4 mm (1 inch) thick plate  ||  9719|13|1|0
    YS    (N*):    hard  ||  sheet 12.7 mm (0.5 inch) and under  ||  9719|13|2|0
    YS    (N*):    hard  ||  plate over 12.7 mm (0.5 inch)  ||  9719|13|2|1
    %El   (N*):    soft anneal  ||  25.4 mm (1 inch) thick plate  ||  9719|29|1|0
    %El   (N*):    hard  ||  sheet 12.7 mm (0.5 inch) and under  ||  9719|29|2|0
    %El   (N*):    hard  ||  plate over 12.7 mm (0.5 inch)  ||  9719|29|2|1

return to listing



UNS C61300

    UTS   (N*):    soft anneal  ||  3.17 mm (0.125 inch) plate  ||  786|5|0|0
    UTS   (N*):    soft anneal  ||  12.7 mm (0.5 inch) plate  ||  786|5|0|1
    UTS   (N*):    soft anneal  ||  25.4 mm (1 inch) plate  ||  786|5|0|2
    UTS   (N*):    soft anneal  ||  76.2 mm (3 inch) plate  ||  786|5|0|3
    UTS   (N*):    hard  ||  12.7 mm (0.5 inch) plate  ||  786|5|1|0
    UTS   (N*):    hard  ||  25.4 mm (1 inch) plate  ||  786|5|1|1
    UTS   (N*):    hard  ||  50.8 mm (2 inch) plate  ||  786|5|1|2
    YS    (N*):    soft anneal  ||  3.17 mm (0.125 inch) plate  ||  786|13|0|0
    YS    (N*):    soft anneal  ||  12.7 mm (0.5 inch) plate  ||  786|13|0|1
    YS    (N*):    soft anneal  ||  25.4 mm (1 inch) plate  ||  786|13|0|2
    YS    (N*):    soft anneal  ||  76.2 mm (3 inch) plate  ||  786|13|0|3
    YS    (N*):    hard  ||  12.7 mm (0.5 inch) plate  ||  786|13|1|0
    YS    (N*):    hard  ||  25.4 mm (1 inch) plate  ||  786|13|1|1
    YS    (N*):    hard  ||  50.8 mm (2 inch) plate  ||  786|13|1|2
    %El   (N*):    soft anneal  ||  3.17 mm (0.125 inch) plate  ||  786|29|0|0
    %El   (N*):    soft anneal  ||  12.7 mm (0.5 inch) plate  ||  786|29|0|1
    %El   (N*):    soft anneal  ||  25.4 mm (1 inch) plate  ||  786|29|0|2
    %El   (N*):    soft anneal  ||  76.2 mm (3 inch) plate  ||  786|29|0|3
    %El   (N*):    hard  ||  12.7 mm (0.5 inch) plate  ||  786|29|1|0
    %El   (N*):    hard  ||  25.4 mm (1 inch) plate  ||  786|29|1|1
    %El   (N*):    hard  ||  50.8 mm (2 inch) plate  ||  786|29|1|2

return to listing



UNS C61800

    UTS   (N*):    half hard  ||  25.4 mm (1 inch) plate  ||  9720|5|0|0
    UTS   (N*):    half hard  ||  50.8 mm (2 inch) plate  ||  9720|5|0|1
    UTS   (N*):    half hard  ||  76.2 mm (3 inch) plate  ||  9720|5|0|2
    YS    (N*):    half hard  ||  25.4 mm (1 inch) plate  ||  9720|13|0|0
    YS    (N*):    half hard  ||  50.8 mm (2 inch) plate  ||  9720|13|0|1
    YS    (N*):    half hard  ||  76.2 mm (3 inch) plate  ||  9720|13|0|2
    %El   (N*):    half hard  ||  25.4 mm (1 inch) plate  ||  9720|29|0|0
    %El   (N*):    half hard  ||  50.8 mm (2 inch) plate  ||  9720|29|0|1
    %El   (N*):    half hard  ||  76.2 mm (3 inch) plate  ||  9720|29|0|2

return to listing



UNS C61900

    UTS   (N*):    1.02 mm (0.04 inch) thick sheet  ||  annealed  ||  9721|5|0|0
    UTS   (N*):    1.02 mm (0.04 inch) thick sheet  ||  half hard  ||  9721|5|0|1
    UTS   (N*):    1.02 mm (0.04 inch) thick sheet  ||  hard  ||  9721|5|0|2
    UTS   (N*):    1.02 mm (0.04 inch) thick sheet  ||  hard, 1 h at 232 °C (450 °F)  ||  9721|5|0|3
    UTS   (N*):    1.02 mm (0.04 inch) thick sheet  ||  spring  ||  9721|5|0|4
    UTS   (N*):    1.02 mm (0.04 inch) thick sheet  ||  spring, 1 h at 232 °C (450 °F)  ||  9721|5|0|5
    UTS   (N*):    1.02 mm (0.04 inch) thick sheet  ||  extra spring  ||  9721|5|0|6
    UTS   (N*):    1.02 mm (0.04 inch) thick sheet  ||  extra spring, 1 h at 232 °C (450 °F)  ||  9721|5|0|7
    YS    (N*):    1.02 mm (0.04 inch) thick sheet  ||  annealed  ||  9721|13|0|0
    YS    (N*):    1.02 mm (0.04 inch) thick sheet  ||  half hard  ||  9721|13|0|1
    YS    (N*):    1.02 mm (0.04 inch) thick sheet  ||  hard  ||  9721|13|0|2
    YS    (N*):    1.02 mm (0.04 inch) thick sheet  ||  hard, 1 h at 232 °C (450 °F)  ||  9721|13|0|3
    YS    (N*):    1.02 mm (0.04 inch) thick sheet  ||  spring  ||  9721|13|0|4
    YS    (N*):    1.02 mm (0.04 inch) thick sheet  ||  spring, 1 h at 232 °C (450 °F)  ||  9721|13|0|5
    YS    (N*):    1.02 mm (0.04 inch) thick sheet  ||  extra spring  ||  9721|13|0|6
    YS    (N*):    1.02 mm (0.04 inch) thick sheet  ||  extra spring, 1 h at 232 °C (450 °F)  ||  9721|13|0|7
    %El   (N*):    1.02 mm (0.04 inch) thick sheet  ||  annealed  ||  9721|29|0|0
    %El   (N*):    1.02 mm (0.04 inch) thick sheet  ||  half hard  ||  9721|29|0|1
    %El   (N*):    1.02 mm (0.04 inch) thick sheet  ||  hard  ||  9721|29|0|2
    %El   (N*):    1.02 mm (0.04 inch) thick sheet  ||  hard, 1 h at 232 °C (450 °F)  ||  9721|29|0|3
    %El   (N*):    1.02 mm (0.04 inch) thick sheet  ||  spring  ||  9721|29|0|4
    %El   (N*):    1.02 mm (0.04 inch) thick sheet  ||  spring, 1 h at 232 °C (450 °F)  ||  9721|29|0|5
    %El   (N*):    1.02 mm (0.04 inch) thick sheet  ||  extra spring  ||  9721|29|0|6
    %El   (N*):    1.02 mm (0.04 inch) thick sheet  ||  extra spring, 1 h at 232 °C (450 °F)  ||  9721|29|0|7

return to listing



UNS C62300

    UTS    (N):    annealed  ||  49 mm (1.93 inch) bar  ||  788|5|0|0
    UTS    (N):    0.4% cold worked  ||  49 mm (1.93 inch) bar  ||  788|5|1|0
    YS     (N):    annealed  ||  49 mm (1.93 inch) bar  ||  788|13|0|0
    YS     (N):    0.4% cold worked  ||  49 mm (1.93 inch) bar  ||  788|13|1|0
    %El    (N):    annealed  ||  49 mm (1.93 inch) bar  ||  788|29|0|0
    %El    (N):    0.4% cold worked  ||  49 mm (1.93 inch) bar  ||  788|29|1|0

return to listing



UNS C62400

    UTS   (N*):    light anneal  ||  25.4 mm (1 inch) bar  ||  9722|5|0|0
    UTS   (N*):    light anneal  ||  50.8 mm (2 inch) bar  ||  9722|5|0|1
    UTS   (N*):    as-extruded  ||  76.2 mm (3 inch) bar  ||  9722|5|1|0
    UTS   (N*):    as-extruded  ||  102 mm (4 inch) rod  ||  9722|5|1|1
    UTS   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9722|5|2|0
    UTS   (N*):    half hard  ||  50.8 mm (2 inch) rod  ||  9722|5|2|1
    UTS   (N*):    half hard  ||  76.2 mm (3 inch) rod  ||  9722|5|2|2
    YS    (N*):    light anneal  ||  25.4 mm (1 inch) bar  ||  9722|13|0|0
    YS    (N*):    light anneal  ||  50.8 mm (2 inch) bar  ||  9722|13|0|1
    YS    (N*):    as-extruded  ||  76.2 mm (3 inch) bar  ||  9722|13|1|0
    YS    (N*):    as-extruded  ||  102 mm (4 inch) rod  ||  9722|13|1|1
    YS    (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9722|13|2|0
    YS    (N*):    half hard  ||  50.8 mm (2 inch) rod  ||  9722|13|2|1
    YS    (N*):    half hard  ||  76.2 mm (3 inch) rod  ||  9722|13|2|2
    %El   (N*):    light anneal  ||  25.4 mm (1 inch) bar  ||  9722|29|0|0
    %El   (N*):    light anneal  ||  50.8 mm (2 inch) bar  ||  9722|29|0|1
    %El   (N*):    as-extruded  ||  76.2 mm (3 inch) bar  ||  9722|29|1|0
    %El   (N*):    as-extruded  ||  102 mm (4 inch) rod  ||  9722|29|1|1
    %El   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9722|29|2|0
    %El   (N*):    half hard  ||  50.8 mm (2 inch) rod  ||  9722|29|2|1
    %El   (N*):    half hard  ||  76.2 mm (3 inch) rod  ||  9722|29|2|2

return to listing



UNS C62500

    UTS   (N*):    as-extruded  ||  rod and bar  ||  9723|5|0|0
    YS    (N*):    as-extruded  ||  rod and bar  ||  9723|13|0|0
    %El   (N*):    as-extruded  ||  rod and bar  ||  9723|29|0|0

return to listing



UNS C63000

    UTS    (N):    annealed at 620 °C (1148 °F)  ||  50 mm (1.97 inch) rod  ||  789|5|4|0
    YS     (N):    annealed at 620 °C (1148 °F)  ||  50 mm (1.97 inch) rod  ||  789|13|4|0
    %El    (N):    annealed at 620 °C (1148 °F)  ||  50 mm (1.97 inch) rod  ||  789|29|4|0

return to listing



UNS C63600

    UTS   (N*):    annealed  ||  15.9 mm (0.625 inch) rod  ||  9724|5|0|0
    UTS   (N*):    annealed  ||  9.96 mm (0.392 inch) wire  ||  9724|5|0|1
    UTS   (N*):    eighth hard  ||  10.7 mm (0.422 inch) wire  ||  9724|5|1|0
    UTS   (N*):    quarter hard  ||  14.3 mm (0.5625 inch) rod  ||  9724|5|2|0
    UTS   (N*):    quarter hard  ||  12.4 mm (0.488 inch) wire  ||  9724|5|2|1
    %El   (N*):    annealed  ||  15.9 mm (0.625 inch) rod  ||  9724|29|0|0
    %El   (N*):    annealed  ||  9.96 mm (0.392 inch) wire  ||  9724|29|0|1
    %El   (N*):    eighth hard  ||  10.7 mm (0.422 inch) wire  ||  9724|29|1|0
    %El   (N*):    quarter hard  ||  14.3 mm (0.5625 inch) rod  ||  9724|29|2|0
    %El   (N*):    quarter hard  ||  12.4 mm (0.488 inch) wire  ||  9724|29|2|1

return to listing



UNS C63800

    UTS   (N*):    soft  ||  1.02 mm (0.04 inch) sheet  ||  791|5|0|0
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  791|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  791|5|2|0
    UTS   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  791|5|3|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  791|5|4|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  791|5|5|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  791|5|7|0
    YS    (N*):    soft  ||  1.02 mm (0.04 inch) sheet  ||  791|13|0|0
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  791|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  791|13|2|0
    YS    (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  791|13|3|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  791|13|4|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  791|13|5|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  791|13|7|0
    %El   (N*):    soft  ||  1.02 mm (0.04 inch) sheet  ||  791|29|0|0
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  791|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  791|29|2|0
    %El   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  791|29|3|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  791|29|4|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  791|29|5|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  791|29|7|0

return to listing



UNS C64200

    UTS    (N):    cold drawn  ||  9725|5|0|-1
    UTS    (N):    extruded, drawn, relief anneal  ||  9725|5|1|-1
    UTS    (N):    hard  ||  9725|5|2|-1
    UTS    (N):    annealed  ||  9725|5|3|-1
    YS     (N):    cold drawn  ||  9725|13|0|-1
    YS     (N):    extruded, drawn, relief anneal  ||  9725|13|1|-1
    YS     (N):    hard  ||  9725|13|2|-1
    YS     (N):    annealed  ||  9725|13|3|-1
    SR     (N):    annealed 1 h at 700 °C (1292 °F)  ||  tested at 550 °C (1022 °F)  ||  9725|22|0|0
    SR     (N):    annealed 1 h at 700 °C (1292 °F)  ||  tested at 600 °C (1112 °F)  ||  9725|22|0|1
    SR     (N):    annealed 1 h at 700 °C (1292 °F)  ||  Master curve (LMP)  ||  9725|22|0|2
    %El    (N):    cold drawn  ||  9725|29|0|-1
    %El    (N):    extruded, drawn, relief anneal  ||  9725|29|1|-1
    %El    (N):    hard  ||  9725|29|2|-1
    %El    (N):    annealed  ||  9725|29|3|-1

return to listing



UNS C64400

    UTS   (N*):    soft  ||  1.02 mm (0.04 inch) sheet  ||  9726|5|0|0
    UTS   (N*):    soft  ||  1.02 mm (0.04 inch) sheet, precipitation hardened  ||  9726|5|0|1
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet, as-rolled  ||  9726|5|1|0
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet, precipitation hardened  ||  9726|5|1|1
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet, as-rolled  ||  9726|5|2|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet, precipitation hardened  ||  9726|5|2|1
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet, as-rolled  ||  9726|5|3|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet, precipitation hardened  ||  9726|5|3|1
    YS    (N*):    soft  ||  1.02 mm (0.04 inch) sheet  ||  9726|13|0|0
    YS    (N*):    soft  ||  1.02 mm (0.04 inch) sheet, precipitation hardened  ||  9726|13|0|1
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet, as-rolled  ||  9726|13|1|0
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet, precipitation hardened  ||  9726|13|1|1
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet, as-rolled  ||  9726|13|2|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet, precipitation hardened  ||  9726|13|2|1
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet, as-rolled  ||  9726|13|3|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet, precipitation hardened  ||  9726|13|3|1
    %El   (N*):    soft  ||  1.02 mm (0.04 inch) sheet  ||  9726|29|0|0
    %El   (N*):    soft  ||  1.02 mm (0.04 inch) sheet, precipitation hardened  ||  9726|29|0|1
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet, as-rolled  ||  9726|29|1|0
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet, precipitation hardened  ||  9726|29|1|1
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet, as-rolled  ||  9726|29|2|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet, precipitation hardened  ||  9726|29|2|1
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet, as-rolled  ||  9726|29|3|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet, precipitation hardened  ||  9726|29|3|1

return to listing



UNS C64700

    DLL    (N):    solid  ||  792|0|0|-1
    TC    (N*):    solid  ||  solution heat treated  ||  792|1|0|0
    TC    (N*):    solid  ||  precipitation hardened  ||  792|1|0|1
    E     (N*):    solid  ||  solution heat treated  ||  792|3|0|0
    UTS    (N):    solution treated  ||  792|5|0|-1
    UTS    (N):    aged after cold working 75%  ||  792|5|2|-1
    MTE    (N):    solid  ||  792|8|0|-1
    SH    (N*):    solid  ||  792|9|0|-1
    G     (N*):    solid  ||  solution heat treated  ||  792|11|0|0
    G     (N*):    solid  ||  precipitation hardened  ||  792|11|0|1
    YS     (N):    aged after cold working 75%  ||  792|13|2|-1
    CTE    (N):    solid  ||  792|16|0|-1
    v     (N*):    solid  ||  solution heat treated  ||  792|19|0|0
    v     (N*):    solid  ||  precipitation hardened  ||  792|19|0|1
    SR     (N):    solution treated  ||  tested at 300 °C (572 °F)  ||  792|22|0|0
    SR     (N):    solution treated  ||  tested at 450 °C (842 °F)  ||  792|22|0|1
    SR     (N):    solution treated  ||  Master curve (LMP)  ||  792|22|0|2
    SR     (N):    precipitation hardened  ||  tested at 200 °C (392 °F)  ||  792|22|1|0
    SR     (N):    precipitation hardened  ||  tested at 300 °C (572 °F)  ||  792|22|1|1
    SR     (N):    precipitation hardened  ||  tested at 450 °C (842 °F)  ||  792|22|1|2
    SR     (N):    precipitation hardened  ||  Master curve (LMP)  ||  792|22|1|3
    SR     (N):    precipitation hardened after 75% cold work  ||  tested at 300 °C (572 °F)  ||  792|22|2|0
    SR     (N):    precipitation hardened after 75% cold work  ||  tested at 400 °C (752 °F)  ||  792|22|2|1
    SR     (N):    precipitation hardened after 75% cold work  ||  Master curve (LMP)  ||  792|22|2|2
    SR     (N):    precipitation hardened after 88% cold work  ||  tested at 204 °C (400 °F)  ||  792|22|3|0
    SR     (N):    precipitation hardened after 88% cold work  ||  tested at 260 °C (500 °F)  ||  792|22|3|1
    SR     (N):    precipitation hardened after 88% cold work  ||  Master curve (LMP)  ||  792|22|3|2
    D      (N):    solid  ||  792|24|0|-1
    TD    (N*):    solid  ||  solution heat treated  ||  792|25|0|0
    TD    (N*):    solid  ||  precipitation hardened  ||  792|25|0|1
    K     (N*):    solid  ||  solution heat treated  ||  792|27|0|0
    K     (N*):    solid  ||  precipitation hardened  ||  792|27|0|1
    %El    (N):    aged after cold working 75%  ||  792|29|2|-1

return to listing



UNS C65100

    UTS   (N*):    annealed  ||  35 micron grain size  ||  9727|5|0|0
    UTS   (N*):    annealed  ||  15 micron grain size  ||  9727|5|0|1
    UTS   (N*):    eighth hard  ||  2.03 mm (0.08 inch) wire  ||  9727|5|1|0
    UTS   (N*):    quarter hard  ||  2.03 mm (0.08 inch) wire  ||  9727|5|2|0
    UTS   (N*):    quarter hard  ||  11.2 mm (0.44 inch) wire  ||  9727|5|2|1
    UTS   (N*):    half hard  ||  2.03 mm (0.08 inch) wire  ||  9727|5|3|0
    UTS   (N*):    half hard  ||  11.2 mm (0.44 inch) wire  ||  9727|5|3|1
    UTS   (N*):    hard  ||  2.03 mm (0.08 inch) wire  ||  9727|5|4|0
    UTS   (N*):    hard  ||  11.2 mm (0.44 inch) wire  ||  9727|5|4|1
    UTS   (N*):    hard  ||  25.4 mm (1 inch) rod  ||  9727|5|4|2
    UTS   (N*):    extra hard  ||  2.03 mm (0.08 inch) wire  ||  9727|5|5|0
    UTS   (N*):    extra hard  ||  25.4 mm (1 inch) rod  ||  9727|5|5|2
    YS    (N*):    annealed  ||  35 micron grain size  ||  9727|13|0|0
    YS    (N*):    annealed  ||  15 micron grain size  ||  9727|13|0|1
    YS    (N*):    eighth hard  ||  2.03 mm (0.08 inch) wire  ||  9727|13|1|0
    YS    (N*):    quarter hard  ||  2.03 mm (0.08 inch) wire  ||  9727|13|2|0
    YS    (N*):    half hard  ||  2.03 mm (0.08 inch) wire  ||  9727|13|3|0
    YS    (N*):    hard  ||  2.03 mm (0.08 inch) wire  ||  9727|13|4|0
    YS    (N*):    hard  ||  25.4 mm (1 inch) rod  ||  9727|13|4|2
    YS    (N*):    extra hard  ||  2.03 mm (0.08 inch) wire  ||  9727|13|5|0
    YS    (N*):    extra hard  ||  25.4 mm (1 inch) rod  ||  9727|13|5|2
    %El   (N*):    annealed  ||  35 micron grain size  ||  9727|29|0|0
    %El   (N*):    annealed  ||  15 micron grain size  ||  9727|29|0|1
    %El   (N*):    eighth hard  ||  2.03 mm (0.08 inch) wire  ||  9727|29|1|0
    %El   (N*):    quarter hard  ||  2.03 mm (0.08 inch) wire  ||  9727|29|2|0
    %El   (N*):    quarter hard  ||  11.2 mm (0.44 inch) wire  ||  9727|29|2|1
    %El   (N*):    half hard  ||  2.03 mm (0.08 inch) wire  ||  9727|29|3|0
    %El   (N*):    half hard  ||  11.2 mm (0.44 inch) wire  ||  9727|29|3|1
    %El   (N*):    hard  ||  2.03 mm (0.08 inch) wire  ||  9727|29|4|0
    %El   (N*):    hard  ||  11.2 mm (0.44 inch) wire  ||  9727|29|4|1
    %El   (N*):    hard  ||  25.4 mm (1 inch) rod  ||  9727|29|4|2
    %El   (N*):    extra hard  ||  2.03 mm (0.08 inch) wire  ||  9727|29|5|0
    %El   (N*):    extra hard  ||  25.4 mm (1 inch) rod  ||  9727|29|5|2

return to listing



UNS C66700

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9728|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9728|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9728|5|0|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9728|5|0|3
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9728|5|0|4
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9728|5|0|5
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|5|2|0
    UTS   (N*):    half hard  ||  2.03 mm (0.08 inch) wire  ||  9728|5|2|1
    UTS   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|5|3|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|5|4|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|5|5|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9728|5|6|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9728|5|7|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9728|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9728|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9728|13|0|2
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9728|13|0|3
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9728|13|0|4
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9728|13|0|5
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|13|2|0
    YS    (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|13|3|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|13|4|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|13|5|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9728|13|6|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9728|13|7|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9728|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9728|29|0|2
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9728|29|0|3
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9728|29|0|4
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9728|29|0|5
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|29|2|0
    %El   (N*):    half hard  ||  2.03 mm (0.08 inch) wire  ||  9728|29|2|1
    %El   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|29|3|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|29|4|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9728|29|5|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9728|29|6|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9728|29|7|0

return to listing



UNS C67400

    UTS   (N*):    soft anneal  ||  19 mm (0.75 inch) rod  ||  9729|5|0|0
    UTS   (N*):    as-extruded  ||  50.8 mm to 76.2 mm (2 inch to 3 inch) bar  ||  9729|5|1|0
    UTS   (N*):    half hard, stress relieved  ||  19 mm (0.75 inch) rod  ||  9729|5|2|0
    UTS   (N*):    half hard, stress relieved  ||  50.8 mm to 76.2 mm (2 inch to 3 inch) bar  ||  9729|5|2|1
    YS    (N*):    soft anneal  ||  19 mm (0.75 inch) rod  ||  9729|13|0|0
    YS    (N*):    as-extruded  ||  50.8 mm to 76.2 mm (2 inch to 3 inch) bar  ||  9729|13|1|0
    YS    (N*):    half hard, stress relieved  ||  19 mm (0.75 inch) rod  ||  9729|13|2|0
    YS    (N*):    half hard, stress relieved  ||  50.8 mm to 76.2 mm (2 inch to 3 inch) bar  ||  9729|13|2|1
    %El   (N*):    soft anneal  ||  19 mm (0.75 inch) rod  ||  9729|29|0|0
    %El   (N*):    as-extruded  ||  50.8 mm to 76.2 mm (2 inch to 3 inch) bar  ||  9729|29|1|0
    %El   (N*):    half hard, stress relieved  ||  19 mm (0.75 inch) rod  ||  9729|29|2|0
    %El   (N*):    half hard, stress relieved  ||  50.8 mm to 76.2 mm (2 inch to 3 inch) bar  ||  9729|29|2|1

return to listing



UNS C67500

    UTS   (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9730|5|0|0
    UTS   (N*):    quarter hard  ||  25.4 mm (1 inch) rod  ||  9730|5|1|0
    UTS   (N*):    quarter hard  ||  50.8 mm (2 inch) rod  ||  9730|5|1|1
    UTS   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9730|5|2|0
    YS    (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9730|13|0|0
    YS    (N*):    quarter hard  ||  25.4 mm (1 inch) rod  ||  9730|13|1|0
    YS    (N*):    quarter hard  ||  50.8 mm (2 inch) rod  ||  9730|13|1|1
    YS    (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9730|13|2|0
    %El   (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9730|29|0|0
    %El   (N*):    quarter hard  ||  25.4 mm (1 inch) rod  ||  9730|29|1|0
    %El   (N*):    quarter hard  ||  50.8 mm (2 inch) rod  ||  9730|29|1|1
    %El   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9730|29|2|0

return to listing



UNS C69000

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet  ||  9732|5|0|0
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9732|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9732|5|2|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9732|5|3|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9732|5|4|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9732|5|5|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9732|5|6|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet  ||  9732|13|0|0
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9732|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9732|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9732|13|3|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9732|13|4|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9732|13|5|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9732|13|6|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet  ||  9732|29|0|0
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9732|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9732|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9732|29|3|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9732|29|4|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9732|29|5|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9732|29|6|0

return to listing



UNS C69400

    UTS   (N*):    soft anneal  ||  12.7 mm (0.5 inch) rod  ||  9733|5|0|0
    UTS   (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9733|5|0|1
    UTS   (N*):    soft anneal  ||  50.8 mm (2 inch) rod  ||  9733|5|0|2
    UTS   (N*):    eighth hard  ||  19 mm (0.75 inch) rod  ||  9733|5|1|0
    YS    (N*):    soft anneal  ||  12.7 mm (0.5 inch) rod  ||  9733|13|0|0
    YS    (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9733|13|0|1
    YS    (N*):    soft anneal  ||  50.8 mm (2 inch) rod  ||  9733|13|0|2
    YS    (N*):    eighth hard  ||  19 mm (0.75 inch) rod  ||  9733|13|1|0
    %El   (N*):    soft anneal  ||  12.7 mm (0.5 inch) rod  ||  9733|29|0|0
    %El   (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9733|29|0|1
    %El   (N*):    soft anneal  ||  50.8 mm (2 inch) rod  ||  9733|29|0|2
    %El   (N*):    eighth hard  ||  19 mm (0.75 inch) rod  ||  9733|29|1|0

return to listing



UNS C70400

    UTS   (N*):    annealed  ||  strip  ||  9734|5|0|0
    UTS   (N*):    quarter hard  ||  strip  ||  9734|5|1|0
    UTS   (N*):    half hard  ||  strip  ||  9734|5|2|0
    UTS   (N*):    hard  ||  strip  ||  9734|5|3|0
    UTS   (N*):    extra hard  ||  strip  ||  9734|5|4|0
    UTS   (N*):    spring  ||  strip  ||  9734|5|5|0
    YS    (N*):    annealed  ||  strip  ||  9734|13|0|0
    YS    (N*):    quarter hard  ||  strip  ||  9734|13|1|0
    YS    (N*):    half hard  ||  strip  ||  9734|13|2|0
    YS    (N*):    hard  ||  strip  ||  9734|13|3|0
    YS    (N*):    extra hard  ||  strip  ||  9734|13|4|0
    YS    (N*):    spring  ||  strip  ||  9734|13|5|0
    %El   (N*):    annealed  ||  strip  ||  9734|29|0|0
    %El   (N*):    quarter hard  ||  strip  ||  9734|29|1|0
    %El   (N*):    half hard  ||  strip  ||  9734|29|2|0
    %El   (N*):    hard  ||  strip  ||  9734|29|3|0
    %El   (N*):    extra hard  ||  strip  ||  9734|29|4|0
    %El   (N*):    spring  ||  strip  ||  9734|29|5|0

return to listing



UNS C72200

    UTS   (N*):    annealed  ||  strip  ||  9736|5|0|0
    UTS   (N*):    hard  ||  strip  ||  9736|5|1|0
    YS    (N*):    annealed  ||  strip  ||  9736|13|0|0
    YS    (N*):    hard  ||  strip  ||  9736|13|1|0
    %El   (N*):    annealed  ||  strip  ||  9736|29|0|0
    %El   (N*):    hard  ||  strip  ||  9736|29|1|0

return to listing



UNS C72800

    UTS   (N*):    quarter hard  ||  2.26 mm (0.089 inch) strip  ||  798|5|0|0
    UTS   (N*):    quarter hard & aged  ||  2.26 mm (0.089 inch) strip  ||  798|5|1|0
    UTS   (N*):    hard  ||  1.6 mm (0.063 inch) strip  ||  798|5|2|0
    UTS   (N*):    hard & aged  ||  0.063 strip  ||  798|5|3|0
    UTS   (N*):    spring  ||  1.6 mm (0.063 inch) strip  ||  798|5|4|0
    UTS   (N*):    spring & aged  ||  0.063 strip  ||  798|5|5|0
    UTS   (N*):    as-extruded & aged  ||  22.9 mm (0.9 inch) rod  ||  798|5|6|0
    UTS   (N*):    solution annealed  ||  6.35 mm (0.25 inch) rod  ||  798|5|7|0
    UTS   (N*):    solution annealed, cold worked, and aged  ||  2.87 mm (0.113 inch) rod  ||  798|5|8|0
    UTS   (N*):    solution annealed & aged  ||  19.3 mm (0.76 inch) rod  ||  798|5|9|0
    YS    (N*):    quarter hard  ||  2.26 mm (0.089 inch) strip  ||  798|13|0|0
    YS    (N*):    quarter hard & aged  ||  2.26 mm (0.089 inch) strip  ||  798|13|1|0
    YS    (N*):    hard  ||  1.6 mm (0.063 inch) strip  ||  798|13|2|0
    YS    (N*):    hard & aged  ||  1.6 mm (0.063 inch) strip  ||  798|13|3|0
    YS    (N*):    spring  ||  1.6 mm (0.063 inch) strip  ||  798|13|4|0
    YS    (N*):    spring & aged  ||  1.6 mm (0.063 inch) strip  ||  798|13|5|0
    YS    (N*):    as-extruded & aged  ||  22.9 mm (0.9 inch) rod  ||  798|13|6|0
    YS    (N*):    solution annealed  ||  6.35 mm (0.25 inch) rod  ||  798|13|7|0
    YS    (N*):    solution annealed, cold worked, and aged  ||  2.87 mm (0.113 inch) rod  ||  798|13|8|0
    YS    (N*):    solution annealed & aged  ||  19.3 mm (0.76 inch) rod  ||  798|13|9|0
    %El   (N*):    quarter hard  ||  2.26 mm (0.089 inch) strip  ||  798|29|0|0
    %El   (N*):    quarter hard & aged  ||  2.26 mm (0.089 inch) strip  ||  798|29|1|0
    %El   (N*):    hard  ||  1.6 mm (0.063 inch) strip  ||  798|29|2|0
    %El   (N*):    hard & aged  ||  1.6 mm (0.063 inch) strip  ||  798|29|3|0
    %El   (N*):    spring  ||  1.6 mm (0.063 inch) strip  ||  798|29|4|0
    %El   (N*):    spring & aged  ||  1.6 mm (0.063 inch) strip  ||  798|29|5|0
    %El   (N*):    as-extruded & aged  ||  22.9 mm (0.9 inch) rod  ||  798|29|6|0
    %El   (N*):    solution annealed  ||  6.35 mm (0.25 inch) rod  ||  798|29|7|0
    %El   (N*):    solution annealed, cold worked, and aged  ||  2.87 mm (0.113 inch) rod  ||  798|29|8|0
    %El   (N*):    solution annealed & aged  ||  19.3 mm (0.76 inch) rod  ||  798|29|9|0

return to listing



UNS C72900

    UTS   (N*):    solution annealed, cold worked, and aged  ||  0.381 mm (0.015 inch) sheet  ||  3123|5|0|0
    UTS   (N*):    solution annealed, cold worked, and aged  ||  0.686 mm (0.027 inch) sheet  ||  3123|5|0|1
    UTS   (N*):    solution annealed and aged  ||  extruded tube  ||  3123|5|1|0
    UTS   (N*):    solution annealed and aged  ||  0.762 mm (0.03 inch) wire  ||  3123|5|1|1
    YS    (N*):    solution annealed, cold worked, and aged  ||  0.381 mm (0.015 inch) sheet  ||  3123|13|0|0
    %El   (N*):    solution annealed, cold worked, and aged  ||  0.381 mm (0.015 inch) sheet  ||  3123|29|0|0
    %El   (N*):    solution annealed and aged  ||  extruded tube  ||  3123|29|1|0
    %El   (N*):    solution annealed and aged  ||  0.762 mm (0.03 inch) wire  ||  3123|29|1|1

return to listing



UNS C74500

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9738|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9738|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9738|5|0|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9738|5|0|3
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9738|5|0|4
    UTS   (N*):    annealed  ||  2.03 mm (0.08 inch) wire, 70 micron grain size  ||  9738|5|0|5
    UTS   (N*):    annealed  ||  2.03 mm (0.08 inch) wire, 50 micron grain size  ||  9738|5|0|6
    UTS   (N*):    annealed  ||  2.03 mm (0.08 inch) wire, 35 micron grain size  ||  9738|5|0|7
    UTS   (N*):    annealed  ||  2.03 mm (0.08 inch) wire, 25 micron grain size  ||  9738|5|0|8
    UTS   (N*):    annealed  ||  2.03 mm (0.08 inch) wire, 15 micron grain size  ||  9738|5|0|9
    UTS   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|5|1|0
    UTS   (N*):    eighth hard  ||  2.03 mm (0.08 inch) wire  ||  9738|5|1|1
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|5|2|0
    UTS   (N*):    quarter hard  ||  2.03 mm (0.08 inch) wire  ||  9738|5|2|1
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|5|3|0
    UTS   (N*):    half hard  ||  2.03 mm (0.08 inch) wire  ||  9738|5|3|1
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|5|4|0
    UTS   (N*):    hard  ||  2.03 mm (0.08 inch) wire  ||  9738|5|4|1
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|5|5|0
    UTS   (N*):    extra hard  ||  2.03 mm (0.08 inch) wire  ||  9738|5|5|1
    UTS   (N*):    spring  ||  2.03 mm (0.08 inch) wire  ||  9738|5|6|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9738|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9738|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9738|13|0|2
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9738|13|0|3
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9738|13|0|4
    YS    (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|13|1|0
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|13|2|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|13|3|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|13|4|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|13|5|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9738|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9738|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9738|29|0|2
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9738|29|0|3
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9738|29|0|4
    %El   (N*):    annealed  ||  2.03 mm (0.08 inch) wire, 70 micron grain size  ||  9738|29|0|5
    %El   (N*):    annealed  ||  2.03 mm (0.08 inch) wire, 50 micron grain size  ||  9738|29|0|6
    %El   (N*):    annealed  ||  2.03 mm (0.08 inch) wire, 35 micron grain size  ||  9738|29|0|7
    %El   (N*):    annealed  ||  2.03 mm (0.08 inch) wire, 25 micron grain size  ||  9738|29|0|8
    %El   (N*):    annealed  ||  2.03 mm (0.08 inch) wire, 15 micron grain size  ||  9738|29|0|9
    %El   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|29|1|0
    %El   (N*):    eighth hard  ||  2.03 mm (0.08 inch) wire  ||  9738|29|1|1
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|29|2|0
    %El   (N*):    quarter hard  ||  2.03 mm (0.08 inch) wire  ||  9738|29|2|1
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|29|3|0
    %El   (N*):    half hard  ||  2.03 mm (0.08 inch) wire  ||  9738|29|3|1
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|29|4|0
    %El   (N*):    hard  ||  2.03 mm (0.08 inch) wire  ||  9738|29|4|1
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9738|29|5|0
    %El   (N*):    extra hard  ||  2.03 mm (0.08 inch) wire  ||  9738|29|5|1
    %El   (N*):    spring  ||  2.03 mm (0.08 inch) wire  ||  9738|29|6|0

return to listing



UNS C75700

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9741|5|5|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9741|5|5|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9741|5|5|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9741|5|5|3
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9741|5|5|4
    UTS   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|5|6|0
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|5|7|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|5|8|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|5|9|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|5|10|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9741|13|5|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9741|13|5|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9741|13|5|2
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9741|13|5|3
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9741|13|5|4
    YS    (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|13|6|0
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|13|7|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|13|8|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|13|9|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|13|10|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9741|29|5|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9741|29|5|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9741|29|5|2
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9741|29|5|3
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9741|29|5|4
    %El   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|29|6|0
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|29|7|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|29|8|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|29|9|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9741|29|10|0

return to listing



UNS C76390

    UTS   (N*):    hard  ||  6.35 mm (0.25 inch) rod  ||  9742|5|0|0
    YS    (N*):    hard  ||  6.35 mm (0.25 inch) rod  ||  9742|13|0|0
    %El   (N*):    hard  ||  6.35 mm (0.25 inch) rod  ||  9742|29|0|0

return to listing



UNS C78200

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9744|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9744|5|0|1
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|5|2|0
    UTS   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|5|3|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|5|4|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|5|5|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9744|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9744|13|0|1
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|13|2|0
    YS    (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|13|3|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|13|4|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|13|5|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9744|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9744|29|0|1
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|29|2|0
    %El   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|29|3|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|29|4|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9744|29|5|0

return to listing



UNS C95200

    CRS    (N):    0.1% plastic strain, as-cast  ||  tested at 204 °C (400 °F)  ||  807|30|0|0
    CRS    (N):    0.1% plastic strain, as-cast  ||  tested at 316 °C (600 °F)  ||  807|30|0|1
    CRS    (N):    0.1% plastic strain, as-cast  ||  Master curve (LMP)  ||  807|30|0|2

return to listing



UNS C95300

    UTS    (N):    chill cast  ||  12420|5|2|-1
    G     (N*):    solid  ||  12420|11|0|-1
    YS     (N):    chill cast  ||  12420|13|2|-1
    v     (N*):    solid  ||  12420|19|0|-1
    K     (N*):    solid  ||  12420|27|0|-1
    %El    (N):    chill cast  ||  12420|29|2|-1

return to listing



UNS C95500

    CRS    (N):    0.1% plastic strain, as-cast  ||  tested at 204 °C (400 °F)  ||  808|30|0|0
    CRS    (N):    0.1% plastic strain, as-cast  ||  tested at 316 °C (600 °F)  ||  808|30|0|1
    CRS    (N):    0.1% plastic strain, as-cast  ||  Master curve (LMP)  ||  808|30|0|2

return to listing



UNS C10800

    UTS   (N*):    annealed  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|5|0|0
    UTS   (N*):    eighth hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|5|1|0
    UTS   (N*):    quarter hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|5|2|0
    UTS   (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|5|3|0
    UTS   (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|5|4|0
    UTS   (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|5|5|0
    UTS   (N*):    hot-rolled  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|5|6|0
    YS    (N*):    annealed  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|13|0|0
    YS    (N*):    eighth hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|13|1|0
    YS    (N*):    quarter hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|13|2|0
    YS    (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|13|3|0
    YS    (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|13|4|0
    YS    (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|13|5|0
    YS    (N*):    hot-rolled  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|13|6|0
    %El   (N*):    annealed  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|29|0|0
    %El   (N*):    eighth hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|29|1|0
    %El   (N*):    quarter hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|29|2|0
    %El   (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|29|3|0
    %El   (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|29|4|0
    %El   (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|29|5|0
    %El   (N*):    hot-rolled  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  740|29|6|0

return to listing



UNS C11100

    UTS   (N*):    hard  ||  2.03 mm (0.08 inch) wire  ||  742|5|0|0
    %El   (N*):    hard  ||  2.03 mm (0.08 inch) wire  ||  742|29|0|0

return to listing



UNS C12000

    UTS    (N):    annealed  ||  744|5|0|-1
    UTS    (N):    hot worked  ||  744|5|1|-1
    UTS    (N):    cold worked 5% to 7%  ||  744|5|2|-1
    YS     (N):    annealed  ||  744|13|0|-1
    YS     (N):    cold worked 5% to 7%  ||  744|13|2|-1
    %El    (N):    annealed  ||  744|29|0|-1
    %El    (N):    hot worked  ||  744|29|1|-1
    %El    (N):    cold worked 5% to 7%  ||  744|29|2|-1

return to listing



UNS C12100

    UTS   (N*):    annealed  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|5|0|0
    UTS   (N*):    eighth hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|5|1|0
    UTS   (N*):    quarter hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|5|2|0
    UTS   (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|5|3|0
    UTS   (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|5|4|0
    UTS   (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|5|5|0
    UTS   (N*):    extra spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|5|6|0
    UTS   (N*):    hot-rolled  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|5|7|0
    YS    (N*):    annealed  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|13|0|0
    YS    (N*):    eighth hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|13|1|0
    YS    (N*):    quarter hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|13|2|0
    YS    (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|13|3|0
    YS    (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|13|4|0
    YS    (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|13|5|0
    YS    (N*):    extra spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|13|6|0
    YS    (N*):    hot-rolled  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|13|7|0
    %El   (N*):    annealed  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|29|0|0
    %El   (N*):    eighth hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|29|1|0
    %El   (N*):    quarter hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|29|2|0
    %El   (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|29|3|0
    %El   (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|29|4|0
    %El   (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|29|5|0
    %El   (N*):    extra spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|29|6|0
    %El   (N*):    hot-rolled  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  745|29|7|0

return to listing



UNS C12500

    UTS   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  748|5|0|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  748|5|1|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  748|5|2|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  748|5|3|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  748|5|4|0
    UTS   (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  748|5|5|0
    UTS   (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  748|5|5|1
    UTS   (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  748|5|5|2
    YS    (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  748|13|0|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  748|13|1|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  748|13|2|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  748|13|3|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  748|13|4|0
    YS    (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  748|13|5|0
    YS    (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  748|13|5|1
    YS    (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  748|13|5|2
    %El   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  748|29|0|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  748|29|1|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  748|29|2|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  748|29|3|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  748|29|4|0
    %El   (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  748|29|5|0
    %El   (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  748|29|5|1
    %El   (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  748|29|5|2

return to listing



UNS C12700

    UTS   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  749|5|0|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  749|5|1|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  749|5|2|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  749|5|3|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  749|5|4|0
    UTS   (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  749|5|5|0
    UTS   (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  749|5|5|1
    UTS   (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  749|5|5|2
    YS    (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  749|13|0|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  749|13|1|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  749|13|2|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  749|13|3|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  749|13|4|0
    YS    (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  749|13|5|0
    YS    (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  749|13|5|1
    YS    (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  749|13|5|2
    %El   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  749|29|0|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  749|29|1|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  749|29|2|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  749|29|3|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  749|29|4|0
    %El   (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  749|29|5|0
    %El   (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  749|29|5|1
    %El   (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  749|29|5|2

return to listing



UNS C12800

    UTS   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  750|5|0|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  750|5|1|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  750|5|2|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  750|5|3|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  750|5|4|0
    UTS   (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  750|5|5|0
    UTS   (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  750|5|5|1
    UTS   (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  750|5|5|2
    YS    (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  750|13|0|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  750|13|1|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  750|13|2|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  750|13|3|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  750|13|4|0
    YS    (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  750|13|5|0
    YS    (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  750|13|5|1
    YS    (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  750|13|5|2
    %El   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  750|29|0|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  750|29|1|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  750|29|2|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  750|29|3|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  750|29|4|0
    %El   (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  750|29|5|0
    %El   (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  750|29|5|1
    %El   (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  750|29|5|2

return to listing



UNS C12900

    UTS   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  751|5|0|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  751|5|1|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  751|5|2|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  751|5|3|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  751|5|4|0
    UTS   (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  751|5|5|0
    UTS   (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  751|5|5|1
    UTS   (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  751|5|5|2
    YS    (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  751|13|0|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  751|13|1|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  751|13|2|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  751|13|3|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  751|13|4|0
    YS    (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  751|13|5|0
    YS    (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  751|13|5|1
    YS    (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  751|13|5|2
    %El   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  751|29|0|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  751|29|1|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  751|29|2|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  751|29|3|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  751|29|4|0
    %El   (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  751|29|5|0
    %El   (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  751|29|5|1
    %El   (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  751|29|5|2

return to listing



UNS C13000

    UTS   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  752|5|0|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  752|5|1|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  752|5|2|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  752|5|3|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  752|5|4|0
    UTS   (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  752|5|5|0
    UTS   (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  752|5|5|1
    UTS   (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  752|5|5|2
    YS    (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  752|13|0|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  752|13|1|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  752|13|2|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  752|13|3|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  752|13|4|0
    YS    (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  752|13|5|0
    YS    (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  752|13|5|1
    YS    (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  752|13|5|2
    %El   (N*):    eighth hard  ||  1.02 mm (0.04 inch) sheet  ||  752|29|0|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  752|29|1|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  752|29|2|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  752|29|3|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  752|29|4|0
    %El   (N*):    hot-rolled  ||  1.02 mm (0.04 inch) sheet  ||  752|29|5|0
    %El   (N*):    hot-rolled  ||  12.7 mm (0.5 inch)  ||  752|29|5|1
    %El   (N*):    hot-rolled  ||  25.4 mm (1 inch) rod  ||  752|29|5|2

return to listing



UNS C14300

    UTS   (N*):    annealed  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  753|5|0|0
    UTS   (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  753|5|1|0
    UTS   (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  753|5|2|0
    UTS   (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  753|5|3|0
    YS    (N*):    annealed  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  753|13|0|0
    YS    (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  753|13|1|0
    YS    (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  753|13|2|0
    YS    (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  753|13|3|0
    %El   (N*):    annealed  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  753|29|0|0
    %El   (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  753|29|1|0
    %El   (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  753|29|2|0
    %El   (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  753|29|3|0

return to listing



UNS C14310

    UTS   (N*):    annealed  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  754|5|0|0
    UTS   (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  754|5|1|0
    UTS   (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  754|5|2|0
    UTS   (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  754|5|3|0
    YS    (N*):    annealed  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  754|13|0|0
    YS    (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  754|13|1|0
    YS    (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  754|13|2|0
    YS    (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  754|13|3|0
    %El   (N*):    annealed  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  754|29|0|0
    %El   (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  754|29|1|0
    %El   (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  754|29|2|0
    %El   (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) strip  ||  754|29|3|0

return to listing



UNS C14700

    UTS   (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  758|5|0|0
    UTS   (N*):    eighth hard  ||  12.7 mm (0.5 inch) rod  ||  758|5|1|0
    UTS   (N*):    half hard  ||  12.7 mm (0.5 inch) rod  ||  758|5|2|0
    UTS   (N*):    hard  ||  12.7 mm (0.5 inch) rod  ||  758|5|3|0
    YS    (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  758|13|0|0
    YS    (N*):    eighth hard  ||  12.7 mm (0.5 inch) rod  ||  758|13|1|0
    YS    (N*):    half hard  ||  12.7 mm (0.5 inch) rod  ||  758|13|2|0
    YS    (N*):    hard  ||  12.7 mm (0.5 inch) rod  ||  758|13|3|0
    %El   (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  758|29|0|0
    %El   (N*):    eighth hard  ||  12.7 mm (0.5 inch) rod  ||  758|29|1|0
    %El   (N*):    half hard  ||  12.7 mm (0.5 inch) rod  ||  758|29|2|0
    %El   (N*):    hard  ||  12.7 mm (0.5 inch) rod  ||  758|29|3|0

return to listing



UNS C14710

    UTS   (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  759|5|0|0
    UTS   (N*):    eighth hard  ||  12.7 mm (0.5 inch) rod  ||  759|5|1|0
    UTS   (N*):    half hard  ||  12.7 mm (0.5 inch) rod  ||  759|5|2|0
    UTS   (N*):    hard  ||  12.7 mm (0.5 inch) rod  ||  759|5|3|0
    YS    (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  759|13|0|0
    YS    (N*):    eighth hard  ||  12.7 mm (0.5 inch) rod  ||  759|13|1|0
    YS    (N*):    half hard  ||  12.7 mm (0.5 inch) rod  ||  759|13|2|0
    YS    (N*):    hard  ||  12.7 mm (0.5 inch) rod  ||  759|13|3|0
    %El   (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  759|29|0|0
    %El   (N*):    eighth hard  ||  12.7 mm (0.5 inch) rod  ||  759|29|1|0
    %El   (N*):    half hard  ||  12.7 mm (0.5 inch) rod  ||  759|29|2|0
    %El   (N*):    hard  ||  12.7 mm (0.5 inch) rod  ||  759|29|3|0

return to listing



UNS C14720

    UTS   (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  760|5|0|0
    UTS   (N*):    eighth hard  ||  12.7 mm (0.5 inch) rod  ||  760|5|1|0
    UTS   (N*):    half hard  ||  12.7 mm (0.5 inch) rod  ||  760|5|2|0
    UTS   (N*):    hard  ||  12.7 mm (0.5 inch) rod  ||  760|5|3|0
    YS    (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  760|13|0|0
    YS    (N*):    eighth hard  ||  12.7 mm (0.5 inch) rod  ||  760|13|1|0
    YS    (N*):    half hard  ||  12.7 mm (0.5 inch) rod  ||  760|13|2|0
    YS    (N*):    hard  ||  12.7 mm (0.5 inch) rod  ||  760|13|3|0
    %El   (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  760|29|0|0
    %El   (N*):    eighth hard  ||  12.7 mm (0.5 inch) rod  ||  760|29|1|0
    %El   (N*):    half hard  ||  12.7 mm (0.5 inch) rod  ||  760|29|2|0
    %El   (N*):    hard  ||  12.7 mm (0.5 inch) rod  ||  760|29|3|0

return to listing



UNS C15000

    E      (N):    cold-drawn 50% & aged (half hard)  ||  761|3|1|-1
    UTS    (N):    bar  ||  half hard, 19 mm (0.748 inch)  ||  761|5|1|0
    YS     (N):    bar  ||  half hard, 19 mm (0.748 inch)  ||  761|13|1|0
    FEN    (N):    half hard  ||  tested at 482 °C (900 °F), R = -1, axial, total strain range  ||  761|14|0|0
    FEN    (N):    half hard  ||  tested at 538 °C (1000 °F), R = -1, axial, total strain range  ||  761|14|0|1
    FEN    (N):    half hard  ||  tested at 593 °C (1100 °F), R = -1, axial, total strain range  ||  761|14|0|2

return to listing



UNS C15500

    UTS   (N*):    light anneal  ||  1.02 mm (0.04 inch) sheet  ||  9745|5|0|0
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9745|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9745|5|2|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9745|5|3|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9745|5|4|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9745|5|5|0
    UTS   (N*):    super spring  ||  1.02 mm (0.04 inch) sheet  ||  9745|5|6|0
    YS    (N*):    light anneal  ||  1.02 mm (0.04 inch) sheet  ||  9745|13|0|0
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9745|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9745|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9745|13|3|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9745|13|4|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9745|13|5|0
    YS    (N*):    super spring  ||  1.02 mm (0.04 inch) sheet  ||  9745|13|6|0
    %El   (N*):    light anneal  ||  1.02 mm (0.04 inch) sheet  ||  9745|29|0|0
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9745|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9745|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9745|29|3|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9745|29|4|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9745|29|5|0
    %El   (N*):    super spring  ||  1.02 mm (0.04 inch) sheet  ||  9745|29|6|0

return to listing



UNS C15715

    UTS   (N*):    annealed at 316 °C (600 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9665|5|0|0
    UTS   (N*):    annealed at 316 °C (600 °F)  ||  6.99 mm (0.275 inch) rod  ||  9665|5|0|1
    UTS   (N*):    annealed at 316 °C (600 °F)  ||  1.27 mm (0.05 inch) wire  ||  9665|5|0|2
    UTS   (N*):    annealed at 649 °C (1200 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9665|5|1|0
    UTS   (N*):    annealed at 649 °C (1200 °F)  ||  6.99 mm (0.275 inch) rod  ||  9665|5|1|1
    UTS   (N*):    annealed at 649 °C (1200 °F)  ||  1.27 mm (0.05 inch) wire  ||  9665|5|1|2
    UTS   (N*):    annealed at 982 °C (1800 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9665|5|2|0
    UTS   (N*):    annealed at 982 °C (1800 °F)  ||  6.99 mm (0.275 inch) rod  ||  9665|5|2|1
    UTS   (N*):    annealed at 982 °C (1800 °F)  ||  1.27 mm (0.05 inch) wire  ||  9665|5|2|2
    UTS   (N*):    as-extruded  ||  6.35 mm (0.25 inch) plate  ||  9665|5|3|0
    UTS   (N*):    as-extruded  ||  28.6 mm (1.125 inch) rod  ||  9665|5|3|1
    UTS   (N*):    cold worked  ||  2.29 mm (0.09 inch) sheet, cold worked 64%  ||  9665|5|4|0
    UTS   (N*):    cold worked  ||  1.27 mm (0.05 inch) sheet, cold worked 80%  ||  9665|5|4|1
    UTS   (N*):    cold worked  ||  0.762 mm (0.03 inch) sheet, cold worked 88%  ||  9665|5|4|2
    UTS   (N*):    cold worked  ||  0.254 mm (0.01 inch) sheet, cold worked 96%  ||  9665|5|4|3
    UTS   (N*):    cold worked  ||  19 mm (0.75 inch) rod, cold worked 55%  ||  9665|5|4|4
    UTS   (N*):    cold worked  ||  12.7 mm (0.5 inch) rod, cold worked 80%  ||  9665|5|4|5
    UTS   (N*):    cold worked  ||  6.99 mm (0.275 inch) rod, cold worked 94%  ||  9665|5|4|6
    UTS   (N*):    cold worked  ||  2.54 mm (0.1 inch) wire, cold worked 99.2%  ||  9665|5|4|7
    UTS   (N*):    cold worked  ||  1.27 mm (0.05 inch) wire, cold worked 99.8%  ||  9665|5|4|8
    UTS   (N*):    cold worked  ||  0.508 mm (0.02 inch) wire, cold worked 99.9%  ||  9665|5|4|9
    UTS   (N*):    cold worked  ||  0.356 mm (0.014 inch) wire, cold worked 99.9%  ||  9665|5|4|10
    YS    (N*):    annealed at 316 °C (600 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9665|13|0|0
    YS    (N*):    annealed at 316 °C (600 °F)  ||  6.99 mm (0.275 inch) rod  ||  9665|13|0|1
    YS    (N*):    annealed at 316 °C (600 °F)  ||  1.27 mm (0.05 inch) wire  ||  9665|13|0|2
    YS    (N*):    annealed at 649 °C (1200 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9665|13|1|0
    YS    (N*):    annealed at 649 °C (1200 °F)  ||  6.99 mm (0.275 inch) rod  ||  9665|13|1|1
    YS    (N*):    annealed at 649 °C (1200 °F)  ||  1.27 mm (0.05 inch) wire  ||  9665|13|1|2
    YS    (N*):    annealed at 982 °C (1800 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9665|13|2|0
    YS    (N*):    annealed at 982 °C (1800 °F)  ||  6.99 mm (0.275 inch) rod  ||  9665|13|2|1
    YS    (N*):    annealed at 982 °C (1800 °F)  ||  1.27 mm (0.05 inch) wire  ||  9665|13|2|2
    YS    (N*):    as-extruded  ||  6.35 mm (0.25 inch) plate  ||  9665|13|3|0
    YS    (N*):    as-extruded  ||  28.6 mm (1.125 inch) rod  ||  9665|13|3|1
    YS    (N*):    cold worked  ||  2.29 mm (0.09 inch) sheet, cold worked 64%  ||  9665|13|4|0
    YS    (N*):    cold worked  ||  1.27 mm (0.05 inch) sheet, cold worked 80%  ||  9665|13|4|1
    YS    (N*):    cold worked  ||  0.762 mm (0.03 inch) sheet, cold worked 88%  ||  9665|13|4|2
    YS    (N*):    cold worked  ||  0.254 mm (0.01 inch) sheet, cold worked 96%  ||  9665|13|4|3
    YS    (N*):    cold worked  ||  19 mm (0.75 inch) rod, cold worked 55%  ||  9665|13|4|4
    YS    (N*):    cold worked  ||  12.7 mm (0.5 inch) rod, cold worked 80%  ||  9665|13|4|5
    YS    (N*):    cold worked  ||  6.99 mm (0.275 inch) rod, cold worked 94%  ||  9665|13|4|6
    YS    (N*):    cold worked  ||  2.54 mm (0.1 inch) wire, cold worked 99.2%  ||  9665|13|4|7
    YS    (N*):    cold worked  ||  1.27 mm (0.05 inch) wire, cold worked 99.8%  ||  9665|13|4|8
    YS    (N*):    cold worked  ||  0.508 mm (0.02 inch) wire, cold worked 99.9%  ||  9665|13|4|9
    YS    (N*):    cold worked  ||  0.356 mm (0.014 inch) wire, cold worked 99.9%  ||  9665|13|4|10
    %El   (N*):    annealed at 316 °C (600 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9665|29|0|0
    %El   (N*):    annealed at 316 °C (600 °F)  ||  6.99 mm (0.275 inch) rod  ||  9665|29|0|1
    %El   (N*):    annealed at 316 °C (600 °F)  ||  1.27 mm (0.05 inch) wire  ||  9665|29|0|2
    %El   (N*):    annealed at 649 °C (1200 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9665|29|1|0
    %El   (N*):    annealed at 649 °C (1200 °F)  ||  6.99 mm (0.275 inch) rod  ||  9665|29|1|1
    %El   (N*):    annealed at 649 °C (1200 °F)  ||  1.27 mm (0.05 inch) wire  ||  9665|29|1|2
    %El   (N*):    annealed at 982 °C (1800 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9665|29|2|0
    %El   (N*):    annealed at 982 °C (1800 °F)  ||  6.99 mm (0.275 inch) rod  ||  9665|29|2|1
    %El   (N*):    annealed at 982 °C (1800 °F)  ||  1.27 mm (0.05 inch) wire  ||  9665|29|2|2
    %El   (N*):    as-extruded  ||  6.35 mm (0.25 inch) plate  ||  9665|29|3|0
    %El   (N*):    as-extruded  ||  28.6 mm (1.125 inch) rod  ||  9665|29|3|1
    %El   (N*):    cold worked  ||  2.29 mm (0.09 inch) sheet, cold worked 64%  ||  9665|29|4|0
    %El   (N*):    cold worked  ||  1.27 mm (0.05 inch) sheet, cold worked 80%  ||  9665|29|4|1
    %El   (N*):    cold worked  ||  0.762 mm (0.03 inch) sheet, cold worked 88%  ||  9665|29|4|2
    %El   (N*):    cold worked  ||  0.254 mm (0.01 inch) sheet, cold worked 96%  ||  9665|29|4|3
    %El   (N*):    cold worked  ||  19 mm (0.75 inch) rod, cold worked 55%  ||  9665|29|4|4
    %El   (N*):    cold worked  ||  12.7 mm (0.5 inch) rod, cold worked 80%  ||  9665|29|4|5
    %El   (N*):    cold worked  ||  6.99 mm (0.275 inch) rod, cold worked 94%  ||  9665|29|4|6
    %El   (N*):    cold worked  ||  2.54 mm (0.1 inch) wire, cold worked 99.2%  ||  9665|29|4|7
    %El   (N*):    cold worked  ||  1.27 mm (0.05 inch) wire, cold worked 99.8%  ||  9665|29|4|8
    %El   (N*):    cold worked  ||  0.508 mm (0.02 inch) wire, cold worked 99.9%  ||  9665|29|4|9
    %El   (N*):    cold worked  ||  0.356 mm (0.014 inch) wire, cold worked 99.9%  ||  9665|29|4|10

return to listing



UNS C15720

    UTS   (N*):    annealed at 316 °C (600 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9666|5|0|0
    UTS   (N*):    annealed at 316 °C (600 °F)  ||  6.99 mm (0.275 inch) rod  ||  9666|5|0|1
    UTS   (N*):    annealed at 316 °C (600 °F)  ||  1.27 mm (0.05 inch) wire  ||  9666|5|0|2
    UTS   (N*):    annealed at 649 °C (1200 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9666|5|1|0
    UTS   (N*):    annealed at 649 °C (1200 °F)  ||  6.99 mm (0.275 inch) rod  ||  9666|5|1|1
    UTS   (N*):    annealed at 649 °C (1200 °F)  ||  1.27 mm (0.05 inch) wire  ||  9666|5|1|2
    UTS   (N*):    annealed at 982 °C (1800 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9666|5|2|0
    UTS   (N*):    annealed at 982 °C (1800 °F)  ||  6.99 mm (0.275 inch) rod  ||  9666|5|2|1
    UTS   (N*):    annealed at 982 °C (1800 °F)  ||  1.27 mm (0.05 inch) wire  ||  9666|5|2|2
    UTS   (N*):    as-extruded  ||  6.35 mm (0.25 inch) plate  ||  9666|5|3|0
    UTS   (N*):    as-extruded  ||  28.6 mm (1.125 inch) rod  ||  9666|5|3|1
    UTS   (N*):    cold worked  ||  2.29 mm (0.09 inch) sheet, cold worked 64%  ||  9666|5|4|0
    UTS   (N*):    cold worked  ||  1.27 mm (0.05 inch) sheet, cold worked 80%  ||  9666|5|4|1
    UTS   (N*):    cold worked  ||  0.762 mm (0.03 inch) sheet, cold worked 88%  ||  9666|5|4|2
    UTS   (N*):    cold worked  ||  0.254 mm (0.01 inch) sheet, cold worked 96%  ||  9666|5|4|3
    UTS   (N*):    cold worked  ||  19 mm (0.75 inch) rod, cold worked 55%  ||  9666|5|4|4
    UTS   (N*):    cold worked  ||  12.7 mm (0.5 inch) rod, cold worked 80%  ||  9666|5|4|5
    UTS   (N*):    cold worked  ||  6.99 mm (0.275 inch) rod, cold worked 94%  ||  9666|5|4|6
    UTS   (N*):    cold worked  ||  2.54 mm (0.1 inch) wire, cold worked 99.2%  ||  9666|5|4|7
    UTS   (N*):    cold worked  ||  1.27 mm (0.05 inch) wire, cold worked 99.8%  ||  9666|5|4|8
    UTS   (N*):    cold worked  ||  0.508 mm (0.02 inch) wire, cold worked 99.9%  ||  9666|5|4|9
    UTS   (N*):    cold worked  ||  0.356 mm (0.014 inch) wire, cold worked 99.9%  ||  9666|5|4|10
    YS    (N*):    annealed at 316 °C (600 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9666|13|0|0
    YS    (N*):    annealed at 316 °C (600 °F)  ||  6.99 mm (0.275 inch) rod  ||  9666|13|0|1
    YS    (N*):    annealed at 316 °C (600 °F)  ||  1.27 mm (0.05 inch) wire  ||  9666|13|0|2
    YS    (N*):    annealed at 649 °C (1200 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9666|13|1|0
    YS    (N*):    annealed at 649 °C (1200 °F)  ||  6.99 mm (0.275 inch) rod  ||  9666|13|1|1
    YS    (N*):    annealed at 649 °C (1200 °F)  ||  1.27 mm (0.05 inch) wire  ||  9666|13|1|2
    YS    (N*):    annealed at 982 °C (1800 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9666|13|2|0
    YS    (N*):    annealed at 982 °C (1800 °F)  ||  6.99 mm (0.275 inch) rod  ||  9666|13|2|1
    YS    (N*):    annealed at 982 °C (1800 °F)  ||  1.27 mm (0.05 inch) wire  ||  9666|13|2|2
    YS    (N*):    as-extruded  ||  6.35 mm (0.25 inch) plate  ||  9666|13|3|0
    YS    (N*):    as-extruded  ||  28.6 mm (1.125 inch) rod  ||  9666|13|3|1
    YS    (N*):    cold worked  ||  2.29 mm (0.09 inch) sheet, cold worked 64%  ||  9666|13|4|0
    YS    (N*):    cold worked  ||  1.27 mm (0.05 inch) sheet, cold worked 80%  ||  9666|13|4|1
    YS    (N*):    cold worked  ||  0.762 mm (0.03 inch) sheet, cold worked 88%  ||  9666|13|4|2
    YS    (N*):    cold worked  ||  0.254 mm (0.01 inch) sheet, cold worked 96%  ||  9666|13|4|3
    YS    (N*):    cold worked  ||  19 mm (0.75 inch) rod, cold worked 55%  ||  9666|13|4|4
    YS    (N*):    cold worked  ||  12.7 mm (0.5 inch) rod, cold worked 80%  ||  9666|13|4|5
    YS    (N*):    cold worked  ||  6.99 mm (0.275 inch) rod, cold worked 94%  ||  9666|13|4|6
    YS    (N*):    cold worked  ||  2.54 mm (0.1 inch) wire, cold worked 99.2%  ||  9666|13|4|7
    YS    (N*):    cold worked  ||  1.27 mm (0.05 inch) wire, cold worked 99.8%  ||  9666|13|4|8
    YS    (N*):    cold worked  ||  0.508 mm (0.02 inch) wire, cold worked 99.9%  ||  9666|13|4|9
    YS    (N*):    cold worked  ||  0.356 mm (0.014 inch) wire, cold worked 99.9%  ||  9666|13|4|10
    %El   (N*):    annealed at 316 °C (600 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9666|29|0|0
    %El   (N*):    annealed at 316 °C (600 °F)  ||  6.99 mm (0.275 inch) rod  ||  9666|29|0|1
    %El   (N*):    annealed at 316 °C (600 °F)  ||  1.27 mm (0.05 inch) wire  ||  9666|29|0|2
    %El   (N*):    annealed at 649 °C (1200 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9666|29|1|0
    %El   (N*):    annealed at 649 °C (1200 °F)  ||  6.99 mm (0.275 inch) rod  ||  9666|29|1|1
    %El   (N*):    annealed at 649 °C (1200 °F)  ||  1.27 mm (0.05 inch) wire  ||  9666|29|1|2
    %El   (N*):    annealed at 982 °C (1800 °F)  ||  1.27 mm (0.05 inch) sheet  ||  9666|29|2|0
    %El   (N*):    annealed at 982 °C (1800 °F)  ||  6.99 mm (0.275 inch) rod  ||  9666|29|2|1
    %El   (N*):    annealed at 982 °C (1800 °F)  ||  1.27 mm (0.05 inch) wire  ||  9666|29|2|2
    %El   (N*):    as-extruded  ||  6.35 mm (0.25 inch) plate  ||  9666|29|3|0
    %El   (N*):    as-extruded  ||  28.6 mm (1.125 inch) rod  ||  9666|29|3|1
    %El   (N*):    cold worked  ||  2.29 mm (0.09 inch) sheet, cold worked 64%  ||  9666|29|4|0
    %El   (N*):    cold worked  ||  1.27 mm (0.05 inch) sheet, cold worked 80%  ||  9666|29|4|1
    %El   (N*):    cold worked  ||  0.762 mm (0.03 inch) sheet, cold worked 88%  ||  9666|29|4|2
    %El   (N*):    cold worked  ||  0.254 mm (0.01 inch) sheet, cold worked 96%  ||  9666|29|4|3
    %El   (N*):    cold worked  ||  19 mm (0.75 inch) rod, cold worked 55%  ||  9666|29|4|4
    %El   (N*):    cold worked  ||  12.7 mm (0.5 inch) rod, cold worked 80%  ||  9666|29|4|5
    %El   (N*):    cold worked  ||  6.99 mm (0.275 inch) rod, cold worked 94%  ||  9666|29|4|6
    %El   (N*):    cold worked  ||  2.54 mm (0.1 inch) wire, cold worked 99.2%  ||  9666|29|4|7
    %El   (N*):    cold worked  ||  1.27 mm (0.05 inch) wire, cold worked 99.8%  ||  9666|29|4|8
    %El   (N*):    cold worked  ||  0.508 mm (0.02 inch) wire, cold worked 99.9%  ||  9666|29|4|9
    %El   (N*):    cold worked  ||  0.356 mm (0.014 inch) wire, cold worked 99.9%  ||  9666|29|4|10

return to listing



UNS C15760

    UTS   (N*):    annealed at 316 °C (600 °F)  ||  6.99 mm (0.275 inch) rod  ||  9667|5|0|0
    UTS   (N*):    annealed at 649 °C (1200 °F)  ||  6.99 mm (0.275 inch) rod  ||  9667|5|1|0
    UTS   (N*):    annealed at 982 °C (1800 °F)  ||  6.99 mm (0.275 inch) rod  ||  9667|5|2|0
    UTS   (N*):    as-extruded  ||  13.7 mm (0.54 inch) rod  ||  9667|5|3|0
    UTS   (N*):    as-extruded  ||  63.5 mm (2.5 inch) bar  ||  9667|5|3|1
    UTS   (N*):    as-extruded  ||  12.7 mm (0.5 inch) bar  ||  9667|5|3|2
    UTS   (N*):    cold worked  ||  12.7 mm (0.5 inch) rod, cold worked 14%  ||  9667|5|4|0
    UTS   (N*):    cold worked  ||  6.99 mm (0.275 inch) rod, cold worked 74%  ||  9667|5|4|1
    YS    (N*):    annealed at 316 °C (600 °F)  ||  6.99 mm (0.275 inch) rod  ||  9667|13|0|0
    YS    (N*):    annealed at 649 °C (1200 °F)  ||  6.99 mm (0.275 inch) rod  ||  9667|13|1|0
    YS    (N*):    annealed at 982 °C (1800 °F)  ||  6.99 mm (0.275 inch) rod  ||  9667|13|2|0
    YS    (N*):    as-extruded  ||  13.7 mm (0.54 inch) rod  ||  9667|13|3|0
    YS    (N*):    as-extruded  ||  63.5 mm (2.5 inch) bar  ||  9667|13|3|1
    YS    (N*):    as-extruded  ||  12.7 mm (0.5 inch) bar  ||  9667|13|3|2
    YS    (N*):    cold worked  ||  12.7 mm (0.5 inch) rod, cold worked 14%  ||  9667|13|4|0
    YS    (N*):    cold worked  ||  6.99 mm (0.275 inch) rod, cold worked 74%  ||  9667|13|4|1
    %El   (N*):    annealed at 316 °C (600 °F)  ||  6.99 mm (0.275 inch) rod  ||  9667|29|0|0
    %El   (N*):    annealed at 649 °C (1200 °F)  ||  6.99 mm (0.275 inch) rod  ||  9667|29|1|0
    %El   (N*):    annealed at 982 °C (1800 °F)  ||  6.99 mm (0.275 inch) rod  ||  9667|29|2|0
    %El   (N*):    as-extruded  ||  13.7 mm (0.54 inch) rod  ||  9667|29|3|0
    %El   (N*):    as-extruded  ||  63.5 mm (2.5 inch) bar  ||  9667|29|3|1
    %El   (N*):    as-extruded  ||  12.7 mm (0.5 inch) bar  ||  9667|29|3|2
    %El   (N*):    cold worked  ||  12.7 mm (0.5 inch) rod, cold worked 14%  ||  9667|29|4|0
    %El   (N*):    cold worked  ||  6.99 mm (0.275 inch) rod, cold worked 74%  ||  9667|29|4|1

return to listing



UNS C16500

    CRS    (N):    0.1% plastic strain, annealed  ||  tested at 200 °C (392 °F)  ||  9668|30|0|0
    CRS    (N):    0.2% plastic strain, annealed  ||  tested at 200 °C (392 °F)  ||  9668|30|1|0
    CRS    (N):    0.1% plastic strain, hard  ||  tested at 200 °C (392 °F)  ||  9668|30|2|0
    CRS    (N):    0.2% plastic strain, hard  ||  tested at 200 °C (392 °F)  ||  9668|30|3|0
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed  ||  1,000 h  ||  9668|39|0|0
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed  ||  1,300 h  ||  9668|39|0|1
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed  ||  1,500 h  ||  9668|39|0|2
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed  ||  2,000 h  ||  9668|39|0|3
    IC     (N):    tested at 200 °C (392 °F), plastic strain, hard  ||  1,000 h  ||  9668|39|1|0
    IC     (N):    tested at 200 °C (392 °F), plastic strain, hard  ||  1,300 h  ||  9668|39|1|1
    IC     (N):    tested at 200 °C (392 °F), plastic strain, hard  ||  1,500 h  ||  9668|39|1|2
    IC     (N):    tested at 200 °C (392 °F), plastic strain, hard  ||  2,000 h  ||  9668|39|1|3

return to listing



UNS C17200

    SR     (N):    precipitation hardened  ||  tested at 149 °C (300 °F)  ||  765|22|0|0
    SR     (N):    precipitation hardened  ||  tested at 204 °C (400 °F)  ||  765|22|0|1
    SR     (N):    precipitation hardened  ||  tested at 260 °C (500 °F)  ||  765|22|0|2
    SR     (N):    precipitation hardened  ||  tested at 316 °C (600 °F)  ||  765|22|0|3
    SR     (N):    precipitation hardened  ||  tested at 427 °C (800 °F)  ||  765|22|0|4
    SR     (N):    precipitation hardened  ||  Master curve (LMP)  ||  765|22|0|5

return to listing



UNS C18090

    UTS   (N*):    soft anneal  ||  flat products  ||  9669|5|0|0
    UTS   (N*):    half hard  ||  flat products  ||  9669|5|1|0
    UTS   (N*):    hard  ||  flat products  ||  9669|5|2|0
    UTS   (N*):    spring  ||  flat products  ||  9669|5|3|0
    YS    (N*):    soft anneal  ||  flat products  ||  9669|13|0|0
    YS    (N*):    half hard  ||  flat products  ||  9669|13|1|0
    YS    (N*):    hard  ||  flat products  ||  9669|13|2|0
    YS    (N*):    spring  ||  flat products  ||  9669|13|3|0
    %El   (N*):    soft anneal  ||  flat products  ||  9669|29|0|0
    %El   (N*):    half hard  ||  flat products  ||  9669|29|1|0
    %El   (N*):    hard  ||  flat products  ||  9669|29|2|0
    %El   (N*):    spring  ||  flat products  ||  9669|29|3|0

return to listing



UNS C18150

    RHO   (N*):    laser powder bed fusion  ||  as-built  ||  769|2|1|0
    RHO   (N*):    laser powder bed fusion  ||  solution treated & aged  ||  769|2|1|1
    RHO   (N*):    laser powder bed fusion  ||  aged  ||  769|2|1|2
    SSC    (N):    laser powder bed fusion  ||  tested at 20 °C (68 °F), as-built, unknown strain rate  ||  769|4|2|0
    SSC    (N):    laser powder bed fusion  ||  tested at 20 °C (68 °F), solution treated & aged, unknown strain rate  ||  769|4|2|1
    SSC    (N):    laser powder bed fusion  ||  tested at 20 °C (68 °F), aged, unknown strain rate  ||  769|4|2|2
    SIGMA (N*):    laser powder bed fusion  ||  as-built  ||  769|10|1|0
    SIGMA (N*):    laser powder bed fusion  ||  solution treated & aged  ||  769|10|1|1
    SIGMA (N*):    laser powder bed fusion  ||  aged  ||  769|10|1|2

return to listing



UNS C18700

    UTS   (N*):    annealed  ||  25.4 mm (1 inch) rod  ||  9671|5|0|0
    UTS   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9671|5|1|0
    UTS   (N*):    hard  ||  25.4 mm (1 inch) rod  ||  9671|5|2|0
    YS    (N*):    annealed  ||  25.4 mm (1 inch) rod  ||  9671|13|0|0
    YS    (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9671|13|1|0
    YS    (N*):    hard  ||  25.4 mm (1 inch) rod  ||  9671|13|2|0
    %El   (N*):    annealed  ||  25.4 mm (1 inch) rod  ||  9671|29|0|0
    %El   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9671|29|1|0
    %El   (N*):    hard  ||  25.4 mm (1 inch) rod  ||  9671|29|2|0

return to listing



UNS C19000

    UTS   (N*):    solution treated  ||  25.4 mm (1 inch) rod  ||  9672|5|0|0
    UTS   (N*):    age hardened  ||  25.4 mm (1 inch) rod  ||  9672|5|1|0
    YS    (N*):    solution treated  ||  25.4 mm (1 inch) rod  ||  9672|13|0|0
    YS    (N*):    age hardened  ||  25.4 mm (1 inch) rod  ||  9672|13|1|0
    %El   (N*):    solution treated  ||  25.4 mm (1 inch) rod  ||  9672|29|0|0
    %El   (N*):    age hardened  ||  25.4 mm (1 inch) rod  ||  9672|29|1|0

return to listing



UNS C19200

    UTS   (N*):    soft anneal  ||  1.02 mm (0.04 inch) sheet  ||  9749|5|0|0
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9749|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9749|5|2|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9749|5|3|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9749|5|4|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9749|5|5|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9749|5|6|0
    YS    (N*):    soft anneal  ||  1.02 mm (0.04 inch) sheet  ||  9749|13|0|0
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9749|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9749|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9749|13|3|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9749|13|4|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9749|13|5|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9749|13|6|0
    %El   (N*):    soft anneal  ||  1.02 mm (0.04 inch) sheet  ||  9749|29|0|0
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9749|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9749|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9749|29|3|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9749|29|4|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9749|29|5|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9749|29|6|0

return to listing



UNS C19220

    UTS   (N*):    soft anneal  ||  0.254 mm (0.01 inch) sheet  ||  9675|5|0|0
    UTS   (N*):    quarter hard  ||  0.254 mm (0.01 inch) sheet  ||  9675|5|1|0
    UTS   (N*):    half hard  ||  0.254 mm (0.01 inch) sheet  ||  9675|5|2|0
    UTS   (N*):    hard  ||  0.254 mm (0.01 inch) sheet  ||  9675|5|3|0
    UTS   (N*):    extra hard  ||  0.254 mm (0.01 inch) sheet  ||  9675|5|4|0
    %El   (N*):    soft anneal  ||  0.254 mm (0.01 inch) sheet  ||  9675|29|0|0
    %El   (N*):    quarter hard  ||  0.254 mm (0.01 inch) sheet  ||  9675|29|1|0
    %El   (N*):    half hard  ||  0.254 mm (0.01 inch) sheet  ||  9675|29|2|0
    %El   (N*):    hard  ||  0.254 mm (0.01 inch) sheet  ||  9675|29|3|0
    %El   (N*):    extra hard  ||  0.254 mm (0.01 inch) sheet  ||  9675|29|4|0

return to listing



UNS C19280

    UTS   (N*):    half hard  ||  0.254 mm (0.01 inch) sheet  ||  9676|5|0|0
    UTS   (N*):    hard  ||  0.254 mm (0.01 inch) sheet  ||  9676|5|1|0
    UTS   (N*):    extra hard  ||  0.254 mm (0.01 inch) sheet  ||  9676|5|2|0
    %El   (N*):    half hard  ||  0.254 mm (0.01 inch) sheet  ||  9676|29|0|0
    %El   (N*):    hard  ||  0.254 mm (0.01 inch) sheet  ||  9676|29|1|0
    %El   (N*):    extra hard  ||  0.254 mm (0.01 inch) sheet  ||  9676|29|2|0

return to listing



UNS C22000

    CRS    (N):    0.1% plastic strain, cold worked 44% and stress relieved  ||  tested at 200 °C (392 °F)  ||  770|30|0|0
    CRS    (N):    0.2% plastic strain, cold worked 44% and stress relieved  ||  tested at 200 °C (392 °F)  ||  770|30|1|0
    IC     (N):    tested at 200 °C (392 °F), plastic strain, cold worked 44% and stress relieved  ||  1,000 h  ||  770|39|0|0
    IC     (N):    tested at 200 °C (392 °F), plastic strain, cold worked 44% and stress relieved  ||  1,300 h  ||  770|39|0|1
    IC     (N):    tested at 200 °C (392 °F), plastic strain, cold worked 44% and stress relieved  ||  1,500 h  ||  770|39|0|2
    IC     (N):    tested at 200 °C (392 °F), plastic strain, cold worked 44% and stress relieved  ||  2,000 h  ||  770|39|0|3

return to listing



UNS C26000

    RHO    (N):    solid  ||  annealed  ||  772|2|0|0
    RHO    (N):    solid  ||  fully cold worked  ||  772|2|0|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  772|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  772|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  772|5|0|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  772|5|0|3
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  772|5|0|4
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  772|5|0|5
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  772|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  772|5|2|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  772|5|3|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  772|5|4|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  772|5|5|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  772|5|6|0
    SIGMA  (N):    solid  ||  annealed  ||  772|10|0|0
    SIGMA  (N):    solid  ||  fully cold worked  ||  772|10|0|2
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  772|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  772|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  772|13|0|2
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  772|13|0|3
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  772|13|0|4
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  772|13|0|5
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  772|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  772|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  772|13|3|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  772|13|4|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  772|13|5|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  772|13|6|0
    SR     (N):    annealed at 675 °C (1247 °F)  ||  tested at 324 °C (615 °F)  ||  772|22|0|0
    SR     (N):    annealed at 675 °C (1247 °F)  ||  tested at 413 °C (775 °F)  ||  772|22|0|1
    SR     (N):    annealed at 675 °C (1247 °F)  ||  tested at 503 °C (937 °F)  ||  772|22|0|2
    SR     (N):    annealed at 675 °C (1247 °F)  ||  tested at 550 °C (1022 °F)  ||  772|22|0|3
    SR     (N):    annealed at 675 °C (1247 °F)  ||  Master curve (LMP)  ||  772|22|0|4
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  772|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  772|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  772|29|0|2
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  772|29|0|3
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  772|29|0|4
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  772|29|0|5
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  772|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  772|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  772|29|3|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  772|29|4|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  772|29|5|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  772|29|6|0

return to listing



UNS C26100

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9754|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9754|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9754|5|0|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9754|5|0|3
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9754|5|0|4
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9754|5|0|5
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9754|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9754|5|2|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9754|5|3|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9754|5|4|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9754|5|5|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9754|5|6|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9754|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9754|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9754|13|0|2
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9754|13|0|3
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9754|13|0|4
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9754|13|0|5
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9754|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9754|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9754|13|3|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9754|13|4|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9754|13|5|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9754|13|6|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9754|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9754|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9754|29|0|2
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9754|29|0|3
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9754|29|0|4
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9754|29|0|5
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9754|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9754|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9754|29|3|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9754|29|4|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9754|29|5|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9754|29|6|0

return to listing



UNS C26130

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9755|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9755|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9755|5|0|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9755|5|0|3
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9755|5|0|4
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9755|5|0|5
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9755|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9755|5|2|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9755|5|3|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9755|5|4|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9755|5|5|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9755|5|6|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9755|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9755|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9755|13|0|2
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9755|13|0|3
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9755|13|0|4
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9755|13|0|5
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9755|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9755|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9755|13|3|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9755|13|4|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9755|13|5|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9755|13|6|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9755|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9755|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9755|29|0|2
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9755|29|0|3
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9755|29|0|4
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9755|29|0|5
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9755|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9755|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9755|29|3|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9755|29|4|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9755|29|5|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9755|29|6|0

return to listing



UNS C26200

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9756|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9756|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9756|5|0|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9756|5|0|3
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9756|5|0|4
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9756|5|0|5
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9756|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9756|5|2|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9756|5|3|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9756|5|4|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9756|5|5|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9756|5|6|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9756|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9756|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9756|13|0|2
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9756|13|0|3
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9756|13|0|4
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9756|13|0|5
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9756|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9756|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9756|13|3|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9756|13|4|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9756|13|5|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9756|13|6|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9756|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9756|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9756|29|0|2
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9756|29|0|3
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9756|29|0|4
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9756|29|0|5
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9756|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9756|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9756|29|3|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9756|29|4|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9756|29|5|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9756|29|6|0

return to listing



UNS C27200

    UTS    (N):    annealed  ||  12448|5|11|-1
    UTS    (N):    cold worked 20%  ||  12448|5|12|-1
    YS     (N):    annealed  ||  0.1% offset  ||  12448|13|11|0
    %El    (N):    annealed  ||  12448|29|11|-1
    %El    (N):    cold worked 20%  ||  12448|29|12|-1

return to listing



UNS C27400

    UTS    (N):    annealed  ||  9684|5|1|-1
    UTS    (N):    cold worked 20%  ||  9684|5|2|-1
    YS     (N):    annealed  ||  0.1% offset  ||  9684|13|1|0
    %El    (N):    annealed  ||  9684|29|1|-1
    %El    (N):    cold worked 20%  ||  9684|29|2|-1

return to listing



UNS C31600

    UTS   (N*):    annealed  ||  25.4 mm (1 inch) rod  ||  9685|5|0|0
    UTS   (N*):    hard  ||  25.4 mm (1 inch) rod  ||  9685|5|1|0
    YS    (N*):    annealed  ||  25.4 mm (1 inch) rod  ||  9685|13|0|0
    YS    (N*):    hard  ||  25.4 mm (1 inch) rod  ||  9685|13|1|0
    %El   (N*):    annealed  ||  25.4 mm (1 inch) rod  ||  9685|29|0|0
    %El   (N*):    hard  ||  25.4 mm (1 inch) rod  ||  9685|29|1|0

return to listing



UNS C32000

    UTS   (N*):    annealed  ||  25.4 mm (1 inch) rod  ||  9686|5|0|0
    UTS   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9686|5|1|0
    UTS   (N*):    hard  ||  25.4 mm (1 inch) rod  ||  9686|5|2|0
    YS    (N*):    annealed  ||  25.4 mm (1 inch) rod  ||  9686|13|0|0
    YS    (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9686|13|1|0
    YS    (N*):    hard  ||  25.4 mm (1 inch) rod  ||  9686|13|2|0
    %El   (N*):    annealed  ||  25.4 mm (1 inch) rod  ||  9686|29|0|0
    %El   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9686|29|1|0
    %El   (N*):    hard  ||  25.4 mm (1 inch) rod  ||  9686|29|2|0

return to listing



UNS C33000

    UTS   (N*):    annealed  ||  25.4 mm (1 inch) tube, 50 micron grain size  ||  9687|5|0|0
    UTS   (N*):    annealed  ||  25.4 mm (1 inch) tube, 25 micron grain size  ||  9687|5|0|1
    UTS   (N*):    hard drawn  ||  25.4 mm (1 inch) tube  ||  9687|5|1|0
    YS    (N*):    annealed  ||  25.4 mm (1 inch) tube, 50 micron grain size  ||  9687|13|0|0
    YS    (N*):    annealed  ||  25.4 mm (1 inch) tube, 25 micron grain size  ||  9687|13|0|1
    YS    (N*):    hard drawn  ||  25.4 mm (1 inch) tube  ||  9687|13|1|0
    %El   (N*):    annealed  ||  25.4 mm (1 inch) tube, 50 micron grain size  ||  9687|29|0|0
    %El   (N*):    annealed  ||  25.4 mm (1 inch) tube, 25 micron grain size  ||  9687|29|0|1
    %El   (N*):    hard drawn  ||  25.4 mm (1 inch) tube  ||  9687|29|1|0

return to listing



UNS C33100

    UTS   (N*):    annealed  ||  25.4 mm (1 inch) tube, 50 micron grain size  ||  9688|5|0|0
    UTS   (N*):    annealed  ||  25.4 mm (1 inch) tube, 25 micron grain size  ||  9688|5|0|1
    UTS   (N*):    hard drawn  ||  25.4 mm (1 inch) tube  ||  9688|5|1|0
    YS    (N*):    annealed  ||  25.4 mm (1 inch) tube, 50 micron grain size  ||  9688|13|0|0
    YS    (N*):    annealed  ||  25.4 mm (1 inch) tube, 25 micron grain size  ||  9688|13|0|1
    YS    (N*):    hard drawn  ||  25.4 mm (1 inch) tube  ||  9688|13|1|0
    %El   (N*):    annealed  ||  25.4 mm (1 inch) tube, 50 micron grain size  ||  9688|29|0|0
    %El   (N*):    annealed  ||  25.4 mm (1 inch) tube, 25 micron grain size  ||  9688|29|0|1
    %El   (N*):    hard drawn  ||  25.4 mm (1 inch) tube  ||  9688|29|1|0

return to listing



UNS C33200

    UTS   (N*):    annealed  ||  25.4 mm (1 inch) tube, 50 micron grain size  ||  9689|5|0|0
    UTS   (N*):    annealed  ||  25.4 mm (1 inch) tube, 25 micron grain size  ||  9689|5|0|1
    UTS   (N*):    hard drawn  ||  25.4 mm (1 inch) tube  ||  9689|5|1|0
    YS    (N*):    annealed  ||  25.4 mm (1 inch) tube, 50 micron grain size  ||  9689|13|0|0
    YS    (N*):    annealed  ||  25.4 mm (1 inch) tube, 25 micron grain size  ||  9689|13|0|1
    YS    (N*):    hard drawn  ||  25.4 mm (1 inch) tube  ||  9689|13|1|0
    %El   (N*):    annealed  ||  25.4 mm (1 inch) tube, 50 micron grain size  ||  9689|29|0|0
    %El   (N*):    annealed  ||  25.4 mm (1 inch) tube, 25 micron grain size  ||  9689|29|0|1
    %El   (N*):    hard drawn  ||  25.4 mm (1 inch) tube  ||  9689|29|1|0

return to listing



UNS C33500

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9690|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9690|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9690|5|0|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9690|5|0|3
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9690|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9690|5|2|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9690|5|3|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9690|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9690|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9690|13|0|2
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9690|13|0|3
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9690|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9690|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9690|13|3|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9690|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9690|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9690|29|0|2
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9690|29|0|3
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9690|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9690|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9690|29|3|0

return to listing



UNS C34000

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9691|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9691|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9691|5|0|2
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9691|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9691|5|2|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9691|5|3|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9691|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9691|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9691|13|0|2
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9691|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9691|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9691|13|3|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9691|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9691|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9691|29|0|2
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9691|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9691|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9691|29|3|0

return to listing



UNS C34200

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9692|5|0|0
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9692|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9692|5|2|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9692|5|3|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9692|5|4|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9692|13|0|0
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9692|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9692|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9692|13|3|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9692|13|4|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9692|29|0|0
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9692|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9692|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9692|29|3|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9692|29|4|0

return to listing



UNS C35000

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9694|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9694|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9694|5|0|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9694|5|0|3
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|5|2|0
    UTS   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|5|3|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|5|4|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|5|5|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9694|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9694|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9694|13|0|2
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9694|13|0|3
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|13|2|0
    YS    (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|13|3|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|13|4|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|13|5|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9694|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9694|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9694|29|0|2
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9694|29|0|3
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|29|2|0
    %El   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|29|3|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|29|4|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9694|29|5|0

return to listing



UNS C35600

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9695|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9695|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9695|5|0|2
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9695|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9695|5|2|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9695|5|3|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9695|5|4|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9695|5|5|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9695|5|6|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9695|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9695|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9695|13|0|2
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9695|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9695|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9695|13|3|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9695|13|4|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9695|13|5|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9695|13|6|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9695|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9695|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9695|29|0|2
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9695|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9695|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9695|29|3|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9695|29|4|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9695|29|5|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9695|29|6|0

return to listing



UNS C36200

    UTS   (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9696|5|0|0
    UTS   (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  9696|5|1|0
    UTS   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9696|5|1|1
    UTS   (N*):    half hard  ||  50.8 mm (2 inch) rod  ||  9696|5|1|2
    YS    (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9696|13|0|0
    YS    (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  9696|13|1|0
    YS    (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9696|13|1|1
    YS    (N*):    half hard  ||  50.8 mm (2 inch) rod  ||  9696|13|1|2
    %El   (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  9696|29|0|0
    %El   (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  9696|29|1|0
    %El   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  9696|29|1|1
    %El   (N*):    half hard  ||  50.8 mm (2 inch) rod  ||  9696|29|1|2

return to listing



UNS C36500

    UTS    (N):    annealed  ||  9697|5|0|-1
    UTS    (N):    cold worked 12%  ||  9697|5|1|-1
    UTS   (N*):    as hot-rolled  ||  25.4 mm (1 inch) plate  ||  9697|5|2|0
    YS    (N*):    as hot-rolled  ||  25.4 mm (1 inch) plate  ||  9697|13|2|0
    %El    (N):    annealed  ||  9697|29|0|-1
    %El    (N):    cold worked 12%  ||  9697|29|1|-1
    %El   (N*):    as hot-rolled  ||  25.4 mm (1 inch) plate  ||  9697|29|2|0

return to listing



UNS C36600

    UTS   (N*):    as hot-rolled  ||  25.4 mm (1 inch) plate  ||  9698|5|0|0
    YS    (N*):    as hot-rolled  ||  25.4 mm (1 inch) plate  ||  9698|13|0|0
    %El   (N*):    as hot-rolled  ||  25.4 mm (1 inch) plate  ||  9698|29|0|0

return to listing



UNS C36700

    UTS   (N*):    as hot-rolled  ||  25.4 mm (1 inch) plate  ||  9699|5|0|0
    YS    (N*):    as hot-rolled  ||  25.4 mm (1 inch) plate  ||  9699|13|0|0
    %El   (N*):    as hot-rolled  ||  25.4 mm (1 inch) plate  ||  9699|29|0|0

return to listing



UNS C36800

    UTS   (N*):    as hot-rolled  ||  25.4 mm (1 inch) plate  ||  9700|5|0|0
    YS    (N*):    as hot-rolled  ||  25.4 mm (1 inch) plate  ||  9700|13|0|0
    %El   (N*):    as hot-rolled  ||  25.4 mm (1 inch) plate  ||  9700|29|0|0

return to listing



UNS C37000

    UTS    (N):    annealed  ||  9701|5|0|-1
    UTS    (N):    cold worked 12%  ||  9701|5|1|-1
    UTS   (N*):    hard drawn  ||  38.1 mm (1.5 inch) OD tube  ||  9701|5|2|0
    UTS   (N*):    hard drawn  ||  50.8 mm (2 inch) OD tube  ||  9701|5|2|1
    YS    (N*):    hard drawn  ||  38.1 mm (1.5 inch) OD tube  ||  9701|13|2|0
    YS    (N*):    hard drawn  ||  50.8 mm (2 inch) OD tube  ||  9701|13|2|1
    %El    (N):    annealed  ||  9701|29|0|-1
    %El    (N):    cold worked 12%  ||  9701|29|1|-1
    %El   (N*):    hard drawn  ||  38.1 mm (1.5 inch) OD tube  ||  9701|29|2|0
    %El   (N*):    hard drawn  ||  50.8 mm (2 inch) OD tube  ||  9701|29|2|1

return to listing



UNS C37100

    UTS   (N*):    hard drawn  ||  38.1 mm (1.5 inch) OD tube  ||  9702|5|0|0
    UTS   (N*):    hard drawn  ||  50.8 mm (2 inch) OD tube  ||  9702|5|0|1
    YS    (N*):    hard drawn  ||  38.1 mm (1.5 inch) OD tube  ||  9702|13|0|0
    YS    (N*):    hard drawn  ||  50.8 mm (2 inch) OD tube  ||  9702|13|0|1
    %El   (N*):    hard drawn  ||  38.1 mm (1.5 inch) OD tube  ||  9702|29|0|0
    %El   (N*):    hard drawn  ||  50.8 mm (2 inch) OD tube  ||  9702|29|0|1

return to listing



UNS C38500

    UTS    (N):    annealed  ||  9703|5|0|-1
    UTS    (N):    extruded  ||  9703|5|1|-1
    UTS    (N):    cold worked, hard  ||  9703|5|2|-1
    YS     (N):    annealed  ||  9703|13|0|-1
    YS     (N):    extruded  ||  9703|13|1|-1
    %El    (N):    annealed  ||  9703|29|0|-1
    %El    (N):    extruded  ||  9703|29|1|-1
    %El    (N):    cold worked, hard  ||  9703|29|2|-1

return to listing



UNS C40800

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9704|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9704|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9704|5|0|2
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|5|2|0
    UTS   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|5|3|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|5|4|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|5|5|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9704|5|6|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9704|5|7|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9704|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9704|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9704|13|0|2
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|13|2|0
    YS    (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|13|3|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|13|4|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|13|5|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9704|13|6|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9704|13|7|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9704|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9704|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9704|29|0|2
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|29|2|0
    %El   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|29|3|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|29|4|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9704|29|5|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9704|29|6|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9704|29|7|0

return to listing



UNS C41100

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9750|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9750|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9750|5|0|2
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|5|2|0
    UTS   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|5|3|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|5|4|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|5|5|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9750|5|6|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9750|5|7|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9750|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9750|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9750|13|0|2
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|13|2|0
    YS    (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|13|3|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|13|4|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|13|5|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9750|13|6|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9750|13|7|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9750|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9750|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9750|29|0|2
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|29|2|0
    %El   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|29|3|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|29|4|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9750|29|5|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9750|29|6|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9750|29|7|0

return to listing



UNS C41300

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9705|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9705|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9705|5|0|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9705|5|0|3
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9705|5|0|4
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9705|5|0|5
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|5|2|0
    UTS   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|5|3|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|5|4|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|5|5|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9705|5|6|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9705|5|7|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9705|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9705|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9705|13|0|2
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9705|13|0|3
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9705|13|0|4
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9705|13|0|5
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|13|2|0
    YS    (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|13|3|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|13|4|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|13|5|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9705|13|6|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9705|13|7|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 100 micron grain size  ||  9705|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 70 micron grain size  ||  9705|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  9705|29|0|2
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9705|29|0|3
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  9705|29|0|4
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9705|29|0|5
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|29|2|0
    %El   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|29|3|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|29|4|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9705|29|5|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9705|29|6|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9705|29|7|0

return to listing



UNS C41500

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9706|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9706|5|0|1
    UTS   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|5|1|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|5|2|0
    UTS   (N*):    3/4 hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|5|3|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|5|4|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|5|5|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9706|5|6|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9706|5|7|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9706|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9706|13|0|1
    YS    (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|13|1|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|13|2|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|13|4|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|13|5|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9706|13|6|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9706|13|7|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  9706|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  9706|29|0|1
    %El   (N*):    quarter hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|29|1|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|29|2|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|29|4|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  9706|29|5|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  9706|29|6|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  9706|29|7|0

return to listing



UNS C63020 (New)

    DLL       :    solid  ||  16373|0|0|-1
    TC        :    solid  ||  16373|1|0|-1
    RHO   (*):    solid  ||  16373|2|0|-1
    E     (*):    solid  ||  16373|3|0|-1
    MTE       :    solid  ||  16373|8|0|-1
    SH    (*):    solid  ||  16373|9|0|-1
    SIGMA (*):    solid  ||  16373|10|0|-1
    G     (*):    solid  ||  16373|11|0|-1
    CTE       :    solid  ||  16373|16|0|-1
    v     (*):    solid  ||  16373|19|0|-1
    D         :    solid  ||  16373|24|0|-1
    TD    (*):    solid  ||  16373|25|0|-1
    K     (*):    solid  ||  16373|27|0|-1

return to listing



UNS C76300 (New)

    DLL       :    solid  ||  16368|0|0|-1
    TC    (*):    solid  ||  16368|1|0|-1
    RHO   (*):    annealed  ||  16368|2|0|-1
    E     (*):    solid  ||  annealed  ||  16368|3|0|0
    E     (*):    solid  ||  cold worked  ||  16368|3|0|1
    UTS       :    annealed  ||  16368|5|0|-1
    MTE       :    solid  ||  16368|8|0|-1
    SH    (*):    solid  ||  16368|9|0|-1
    SIGMA (*):    annealed  ||  16368|10|0|-1
    G     (*):    solid  ||  annealed  ||  16368|11|0|0
    G     (*):    solid  ||  cold worked  ||  16368|11|0|1
    CTE       :    solid  ||  16368|16|0|-1
    v     (*):    solid  ||  annealed  ||  16368|19|0|0
    v     (*):    solid  ||  cold worked  ||  16368|19|0|1
    D         :    solid  ||  16368|24|0|-1
    TD    (*):    solid  ||  16368|25|0|-1
    K     (*):    solid  ||  annealed  ||  16368|27|0|0
    K     (*):    solid  ||  cold worked  ||  16368|27|0|1
    %El       :    annealed  ||  16368|29|0|-1

return to listing



UNS C24000

    RHO    (R):    solid  ||  annealed  ||  9681|2|0|0
    RHO    (N):    solid  ||  fully cold worked  ||  9681|2|0|1
    SIGMA  (R):    solid  ||  annealed  ||  9681|10|0|0
    SIGMA  (N):    solid  ||  fully cold worked  ||  9681|10|0|1

return to listing



UNS C61400

    UTS    (R):    annealed  ||  36 micron grain size  ||  787|5|0|1
    UTS    (N):    annealed  ||  25 micron grain size  ||  787|5|0|2
    YS     (R):    annealed  ||  36 micron grain size  ||  787|13|0|1
    YS     (N):    annealed  ||  25 micron grain size  ||  787|13|0|2
    SR     (N):    0.8 Ni, annealed, 37 micron grain  ||  tested at 500 °C (932 °F)  ||  787|22|0|0
    SR     (N):    0.8 Ni, cold worked 25%  ||  tested at 500 °C (932 °F)  ||  787|22|1|0
    SR     (N):    2.2 Ni, annealed, 37 micron grain  ||  tested at 500 °C (932 °F)  ||  787|22|2|0
    SR     (N):    2.2 Ni, annealed, 82 micron grain size  ||  tested at 500 °C (932 °F)  ||  787|22|3|0
    SR     (N):    2.2 Ni, cold worked 25%  ||  tested at 500 °C (932 °F)  ||  787|22|4|0
    %El    (N):    annealed  ||  25 micron grain size  ||  787|29|0|2

return to listing



UNS C10400

    TC     (R):    solid  ||  737|1|0|-1
    TD     (R):    solid  ||  737|25|0|-1

return to listing



UNS C10500

    TC     (R):    solid  ||  738|1|0|-1
    UTS   (N*):    eighth hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|5|1|0
    UTS   (N*):    quarter hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|5|2|0
    UTS   (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|5|3|0
    UTS   (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|5|4|0
    UTS   (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|5|5|0
    UTS   (N*):    extra spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|5|6|0
    UTS   (N*):    hot-rolled  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|5|7|0
    YS    (N*):    eighth hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|13|1|0
    YS    (N*):    quarter hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|13|2|0
    YS    (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|13|3|0
    YS    (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|13|4|0
    YS    (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|13|5|0
    YS    (N*):    extra spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|13|6|0
    YS    (N*):    hot-rolled  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|13|7|0
    TD     (R):    solid  ||  738|25|0|-1
    %El   (N*):    eighth hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|29|1|0
    %El   (N*):    quarter hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|29|2|0
    %El   (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|29|3|0
    %El   (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|29|4|0
    %El   (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|29|5|0
    %El   (N*):    extra spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|29|6|0
    %El   (N*):    hot-rolled  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  738|29|7|0

return to listing



UNS C12200

    UTS    (R):    solid  ||  annealed  ||  746|5|0|0
    UTS    (N):    solid  ||  cold worked 5% to 7%  ||  746|5|0|5
    YS     (N):    solid  ||  cold worked 5% to 7%  ||  746|13|0|5
    %El    (R):    solid  ||  annealed  ||  746|29|0|0
    %El    (N):    solid  ||  cold worked 5% to 7%  ||  746|29|0|5

return to listing



UNS C14200

    UTS    (R):    plate  ||  annealed  ||  9751|5|0|0
    %El    (R):    plate  ||  annealed  ||  9751|29|0|0

return to listing



UNS C36000

    UTS   (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  776|5|0|0
    UTS   (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  776|5|1|0
    UTS   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  776|5|1|1
    UTS   (N*):    half hard  ||  50.8 mm (2 inch) rod  ||  776|5|1|2
    YS    (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  776|13|0|0
    YS    (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  776|13|1|0
    YS    (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  776|13|1|1
    YS    (N*):    half hard  ||  50.8 mm (2 inch) rod  ||  776|13|1|2
    Vis    (R):    liquid  ||  776|26|1|-1
    %El   (N*):    soft anneal  ||  25.4 mm (1 inch) rod  ||  776|29|0|0
    %El   (N*):    half hard  ||  6.35 mm (0.25 inch) rod  ||  776|29|1|0
    %El   (N*):    half hard  ||  25.4 mm (1 inch) rod  ||  776|29|1|1
    %El   (N*):    half hard  ||  50.8 mm (2 inch) rod  ||  776|29|1|2

return to listing



UNS C46400

    UTS    (N):    hot-rolled  ||  779|5|1|-1
    UTS    (N):    forged  ||  779|5|2|-1
    UTS    (N):    cold worked 28%  ||  779|5|3|-1
    YS     (N):    hot-rolled  ||  779|13|1|-1
    YS     (N):    forged  ||  779|13|2|-1
    Vis    (R):    liquid  ||  779|26|1|-1
    %El    (N):    hot-rolled  ||  779|29|1|-1
    %El    (N):    forged  ||  779|29|2|-1
    %El    (N):    cold worked 28%  ||  779|29|3|-1

return to listing



UNS C26800

    TC     (R):    solid  ||  9682|1|0|-1
    RHO    (R):    solid  ||  annealed  ||  9682|2|0|0
    UTS    (R):    annealed  ||  9682|5|0|-1
    UTS    (N):    cold worked 40%  ||  9682|5|11|-1
    UTS    (N):    cold worked 50%  ||  9682|5|12|-1
    SIGMA  (R):    solid  ||  annealed  ||  9682|10|0|0
    %El    (R):    annealed  ||  9682|29|0|-1
    %El    (N):    cold worked 40%  ||  9682|29|11|-1
    %El    (N):    cold worked 50%  ||  9682|29|12|-1

return to listing



UNS C63200

    UTS    (R):    annealed  ||  10 mm (0.394 inch) plate  ||  790|5|0|0
    YS     (R):    annealed  ||  10 mm (0.394 inch) plate  ||  790|13|0|0
    SR     (R):    annealed 2 h at 750 °C (1382 °F)  ||  tested at 250 °C (482 °F)  ||  790|22|0|0
    SR     (R):    annealed 2 h at 750 °C (1382 °F)  ||  tested at 350 °C (662 °F)  ||  790|22|0|1
    SR     (R):    annealed 2 h at 750 °C (1382 °F)  ||  tested at 450 °C (842 °F)  ||  790|22|0|2
    SR     (R):    annealed 2 h at 750 °C (1382 °F)  ||  tested at 550 °C (1022 °F)  ||  790|22|0|3
    SR     (R):    annealed 2 h at 750 °C (1382 °F)  ||  Master curve (LMP)  ||  790|22|0|4
    SR     (N):    annealed 0.5 h at 850 °C (1562 °F)  ||  tested at 200 °C (392 °F)  ||  790|22|1|0
    %El    (R):    annealed  ||  10 mm (0.394 inch) plate  ||  790|29|0|0
    CRS    (N):    0.05% plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  tested at 200 °C (392 °F)  ||  790|30|0|0
    CRS    (N):    0.1% plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  tested at 200 °C (392 °F)  ||  790|30|1|0
    CRS    (N):    0.1% plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  Master curve (LMP)  ||  790|30|1|1
    CRS    (N):    0.2% plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  tested at 200 °C (392 °F)  ||  790|30|2|0
    CRS    (N):    0.2% plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  Master curve (LMP)  ||  790|30|2|1
    CRS    (N):    0.5% plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  tested at 200 °C (392 °F)  ||  790|30|3|0
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  100 h  ||  790|39|0|0
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  170 h  ||  790|39|0|1
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  250 h  ||  790|39|0|2
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  330 h  ||  790|39|0|3
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  400 h  ||  790|39|0|4
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  475 h  ||  790|39|0|5
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  550 h  ||  790|39|0|6
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  620 h  ||  790|39|0|7
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  700 h  ||  790|39|0|8
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  770 h  ||  790|39|0|9
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  850 h  ||  790|39|0|10
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  920 h  ||  790|39|0|11
    IC     (N):    tested at 200 °C (392 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  1,000 h  ||  790|39|0|12
    IC     (N):    tested at 300 °C (572 °F), plastic strain, annealed 0.5 h at 850 °C (1562 °F)  ||  1,000 h  ||  790|39|1|12
    IC     (N):    tested at 300 °C (572 °F), plastic strain, hot-rolled  ||  2,000 h  ||  790|39|2|13
    IC     (N):    tested at 400 °C (752 °F), plastic strain, hot-rolled  ||  2,000 h  ||  790|39|3|13

return to listing



UNS C10700

    TC     (R):    solid  ||  739|1|0|-1
    UTS   (N*):    eighth hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|5|1|0
    UTS   (N*):    quarter hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|5|2|0
    UTS   (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|5|3|0
    UTS   (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|5|4|0
    UTS   (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|5|5|0
    UTS   (N*):    extra spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|5|6|0
    UTS   (N*):    hot-rolled  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|5|7|0
    YS    (N*):    eighth hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|13|1|0
    YS    (N*):    quarter hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|13|2|0
    YS    (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|13|3|0
    YS    (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|13|4|0
    YS    (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|13|5|0
    YS    (N*):    extra spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|13|6|0
    YS    (N*):    hot-rolled  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|13|7|0
    TD     (R):    solid  ||  739|25|0|-1
    %El   (N*):    eighth hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|29|1|0
    %El   (N*):    quarter hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|29|2|0
    %El   (N*):    half hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|29|3|0
    %El   (N*):    hard  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|29|4|0
    %El   (N*):    spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|29|5|0
    %El   (N*):    extra spring  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|29|6|0
    %El   (N*):    hot-rolled  ||  1.02 mm to 6.35 mm (0.04 inch to 0.25 inch) sheet  ||  739|29|7|0

return to listing



UNS C95800

    E     (R*):    solid  ||  809|3|0|-1
    G     (N*):    solid  ||  809|11|0|-1
    v     (N*):    solid  ||  809|19|0|-1
    K     (N*):    solid  ||  809|27|0|-1
    CRS    (N):    0.1% plastic strain, sand cast  ||  tested at 204 °C (400 °F), 25 mm (0.984 inch) diameter  ||  809|30|0|0
    CRS    (N):    0.1% plastic strain, sand cast  ||  tested at 316 °C (600 °F), 25 mm (0.984 inch) diameter  ||  809|30|0|1
    CRS    (N):    0.1% plastic strain, sand cast  ||  Master curve (LMP), 25 mm (0.984 inch) diameter  ||  809|30|0|2
    CRS    (N):    0.1% plastic strain, sand cast  ||  tested at 204 °C (400 °F), 75 mm (2.95 inch) diameter  ||  809|30|0|3
    CRS    (N):    0.1% plastic strain, sand cast  ||  tested at 316 °C (600 °F), 75 mm (2.95 inch) diameter  ||  809|30|0|4
    CRS    (N):    0.1% plastic strain, sand cast  ||  Master curve (LMP), 75 mm (2.95 inch) diameter  ||  809|30|0|5
    CRS    (N):    0.1% plastic strain, sand cast  ||  tested at 204 °C (400 °F), 75 mm (2.95 inch) diameter, heat-treated  ||  809|30|0|6
    CRS    (N):    0.1% plastic strain, sand cast  ||  tested at 316 °C (600 °F), 75 mm (2.95 inch) diameter, heat-treated  ||  809|30|0|7
    CRS    (N):    0.1% plastic strain, sand cast  ||  Master curve (LMP), 75 mm (2.95 inch) diameter, heat-treated  ||  809|30|0|8
    CRS    (N):    0.1% plastic strain, chill cast  ||  tested at 204 °C (400 °F), 25 mm (0.984 inch) diameter  ||  809|30|1|0
    CRS    (N):    0.1% plastic strain, chill cast  ||  tested at 316 °C (600 °F), 25 mm (0.984 inch) diameter  ||  809|30|1|1
    CRS    (N):    0.1% plastic strain, chill cast  ||  Master curve (LMP), 25 mm (0.984 inch) diameter  ||  809|30|1|2

return to listing



UNS C11400

    TC     (R):    solid  ||  743|1|0|-1

return to listing



UNS C28000

    TC     (R):    solid  ||  annealed  ||  773|1|0|0
    RHO    (R):    solid  ||  annealed  ||  773|2|0|0
    UTS    (N):    cold worked 25%  ||  773|5|1|-1
    SIGMA  (R):    solid  ||  annealed  ||  773|10|0|0
    %El    (N):    cold worked 25%  ||  773|29|1|-1

return to listing



UNS C31400

    UTS   (N*):    annealed  ||  typical value  ||  775|5|0|0
    YS    (N*):    annealed  ||  typical value  ||  775|13|0|0
    Vis    (R):    liquid  ||  775|26|1|-1
    %El   (N*):    annealed  ||  typical value  ||  775|29|0|0

return to listing



UNS C14500

    UTS   (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  755|5|0|0
    YS     (R):    annealed  ||  25 micron grain size  ||  755|13|0|0
    %El   (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  755|29|0|0

return to listing



UNS C51000

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  781|5|0|0
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  781|5|0|1
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  781|5|0|2
    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  781|5|0|3
    UTS    (N):    annealed  ||  1.6 mm (0.063 inch) sheet, unknown grain size  ||  781|5|0|4
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  781|5|1|0
    UTS   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  781|5|2|0
    UTS   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  781|5|3|0
    UTS   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  781|5|4|0
    UTS   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  781|5|5|0
    UTS    (N):    cold worked 61%  ||  1.6 mm (0.063 inch) sheet  ||  781|5|6|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  781|13|0|0
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  781|13|0|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  781|13|0|2
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  781|13|0|3
    YS     (N):    annealed  ||  1.6 mm (0.063 inch) sheet, unknown grain size  ||  781|13|0|4
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  781|13|1|0
    YS    (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  781|13|2|0
    YS    (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  781|13|3|0
    YS    (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  781|13|4|0
    YS    (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  781|13|5|0
    YS     (N):    cold worked 61%  ||  1.6 mm (0.063 inch) sheet  ||  781|13|6|0
    SR     (N):    spring  ||  tested at 200 °C (392 °F)  ||  781|22|0|0
    Vis    (R):    liquid  ||  781|26|1|-1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 50 micron grain size  ||  781|29|0|0
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 35 micron grain size  ||  781|29|0|1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 25 micron grain size  ||  781|29|0|2
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet, 15 micron grain size  ||  781|29|0|3
    %El    (N):    annealed  ||  1.6 mm (0.063 inch) sheet, unknown grain size  ||  781|29|0|4
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  781|29|1|0
    %El   (N*):    hard  ||  1.02 mm (0.04 inch) sheet  ||  781|29|2|0
    %El   (N*):    extra hard  ||  1.02 mm (0.04 inch) sheet  ||  781|29|3|0
    %El   (N*):    spring  ||  1.02 mm (0.04 inch) sheet  ||  781|29|4|0
    %El   (N*):    extra spring  ||  1.02 mm (0.04 inch) sheet  ||  781|29|5|0
    %El    (N):    cold worked 61%  ||  1.6 mm (0.063 inch) sheet  ||  781|29|6|0

return to listing



UNS C65500

    DLL    (R):    solid  ||  794|0|0|-1
    TC     (R):    solid  ||  above RT, unknown temper  ||  794|1|0|0
    RHO    (R):    solid  ||  soft annealed  ||  794|2|0|0
    UTS    (N):    solid  ||  cold worked 42%  ||  794|5|0|3
    MTE    (R):    solid  ||  794|8|0|-1
    SIGMA  (R):    solid  ||  soft annealed  ||  794|10|0|0
    CTE    (R):    solid  ||  794|16|0|-1
    D      (R):    solid  ||  794|24|0|-1
    %El    (N):    solid  ||  cold worked 42%  ||  794|29|0|3

return to listing



UNS C14510

    UTS   (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  756|5|0|0
    YS     (R):    annealed  ||  25 micron grain size  ||  756|13|0|0
    %El   (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  756|29|0|0

return to listing



UNS C37700

    UTS    (N):    annealed  ||  777|5|4|-1
    UTS    (N):    cold worked 12%  ||  777|5|5|-1
    Vis    (R):    liquid  ||  777|26|1|-1
    %El    (N):    annealed  ||  777|29|4|-1
    %El    (N):    cold worked 12%  ||  777|29|5|-1

return to listing



UNS C54400

    UTS   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet  ||  785|5|0|0
    UTS   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  785|5|1|0
    UTS   (N*):    hard  ||  12.7 mm (0.5 inch) plate  ||  785|5|2|0
    UTS   (N*):    hard  ||  25.4 mm (1 inch) plate  ||  785|5|2|1
    YS    (N*):    annealed  ||  1.02 mm (0.04 inch) sheet  ||  785|13|0|0
    YS    (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  785|13|1|0
    YS    (N*):    hard  ||  12.7 mm (0.5 inch) plate  ||  785|13|2|0
    YS    (N*):    hard  ||  25.4 mm (1 inch) plate  ||  785|13|2|1
    Vis    (R):    liquid  ||  785|26|1|-1
    %El   (N*):    annealed  ||  1.02 mm (0.04 inch) sheet  ||  785|29|0|0
    %El   (N*):    half hard  ||  1.02 mm (0.04 inch) sheet  ||  785|29|1|0
    %El   (N*):    hard  ||  12.7 mm (0.5 inch) plate  ||  785|29|2|0
    %El   (N*):    hard  ||  25.4 mm (1 inch) plate  ||  785|29|2|1

return to listing



UNS C68700

    RHO    (R):    solid  ||  annealed  ||  795|2|0|0
    SIGMA  (R):    solid  ||  annealed  ||  795|10|0|0
    %El    (R):    hard  ||  4.75 mm (0.187 inch) sheet  ||  795|29|1|0

return to listing



UNS C21000

    RHO    (R):    solid  ||  annealed  ||  9679|2|0|0
    RHO    (R):    solid  ||  fully cold worked  ||  9679|2|0|1
    UTS    (N):    cold worked 51%  ||  9679|5|10|-1
    SIGMA  (R):    solid  ||  annealed  ||  9679|10|0|0
    SIGMA  (R):    solid  ||  fully cold worked  ||  9679|10|0|1
    YS     (N):    cold worked 51%  ||  9679|13|10|-1
    %El    (N):    cold worked 51%  ||  9679|29|10|-1
    CRS    (N):    0.1% plastic strain, cold worked 51%  ||  tested at 200 °C (392 °F)  ||  9679|30|0|0
    CRS    (N):    0.2% plastic strain, cold worked 51%  ||  tested at 200 °C (392 °F)  ||  9679|30|1|0
    IC     (N):    tested at 200 °C (392 °F), plastic strain, cold worked 51%  ||  1,000 h  ||  9679|39|0|0
    IC     (N):    tested at 200 °C (392 °F), plastic strain, cold worked 51%  ||  1,300 h  ||  9679|39|0|1
    IC     (N):    tested at 200 °C (392 °F), plastic strain, cold worked 51%  ||  1,500 h  ||  9679|39|0|2
    IC     (N):    tested at 200 °C (392 °F), plastic strain, cold worked 51%  ||  2,000 h  ||  9679|39|0|3

return to listing



UNS C14520

    UTS   (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  757|5|0|0
    YS     (R):    annealed  ||  25 micron grain size  ||  757|13|0|0
    %El   (N*):    annealed  ||  12.7 mm (0.5 inch) rod  ||  757|29|0|0

return to listing



UNS C23000

    RHO    (R):    solid  ||  annealed  ||  771|2|0|0
    UTS    (R):    annealed  ||  771|5|0|-1
    UTS    (N):    cold worked 14%  ||  771|5|1|-1
    UTS    (N):    cold worked 37%  ||  771|5|2|-1
    SIGMA  (R):    solid  ||  annealed  ||  771|10|0|0
    YS     (R):    annealed  ||  771|13|0|-1
    YS     (N):    cold worked 14%  ||  771|13|1|-1
    %El    (R):    annealed  ||  771|29|0|-1
    %El    (N):    cold worked 14%  ||  771|29|1|-1
    %El    (N):    cold worked 37%  ||  771|29|2|-1

return to listing



V - H (beta) (New)

    RHO       :    solid  ||  33.8 H (at %)  ||  16559|2|0|0
    RHO       :    solid  ||  35.7 H (at %)  ||  16559|2|0|1
    RHO       :    solid  ||  38.3 H (at %)  ||  16559|2|0|2
    RHO       :    solid  ||  41.2 H (at %)  ||  16559|2|0|3
    RHO       :    solid  ||  42.1 H (at %)  ||  16559|2|0|4
    SIGMA     :    solid  ||  33.8 H (at %)  ||  16559|10|0|0
    SIGMA     :    solid  ||  35.7 H (at %)  ||  16559|10|0|1
    SIGMA     :    solid  ||  38.3 H (at %)  ||  16559|10|0|2
    SIGMA     :    solid  ||  41.2 H (at %)  ||  16559|10|0|3
    SIGMA     :    solid  ||  42.1 H (at %)  ||  16559|10|0|4

return to listing



Vespel TP-8395

    E      (R):    ISO 527  ||  9401|3|0|-1
    UTS    (R):    ISO 527  ||  9401|5|0|-1
    %El    (R):    ISO 527  ||  at break  ||  9401|29|0|0
    UCS    (N):    ISO 604  ||  9401|47|0|-1

return to listing



Vespel TP-8549

    E      (R):    ISO 527  ||  9405|3|0|-1
    UTS    (R):    ISO 527  ||  9405|5|0|-1
    %El    (R):    ISO 527  ||  at break  ||  9405|29|0|0
    UCS    (N):    ISO 604  ||  9405|47|0|-1

return to listing



Vespel TP-8792

    E      (R):    ISO 527  ||  9406|3|0|-1
    UTS    (R):    ISO 527  ||  9406|5|0|-1
    %El    (R):    ISO 527  ||  at break  ||  9406|29|0|0
    UCS    (N):    ISO 604  ||  9406|47|0|-1

return to listing



Vespel TP-8054

    E      (R):    ISO 527  ||  9400|3|0|-1
    UTS    (R):    ISO 527  ||  9400|5|0|-1
    %El    (R):    ISO 527  ||  at break  ||  9400|29|0|0
    UCS    (N):    ISO 604  ||  9400|47|0|-1

return to listing



Vespel TP-8130

    E      (R):    ISO 527  ||  9403|3|0|-1
    UTS    (R):    ISO 527  ||  9403|5|0|-1
    %El    (R):    ISO 527  ||  at break  ||  9403|29|0|0
    UCS    (N):    ISO 604  ||  9403|47|0|-1

return to listing



Vespel TP-8212

    E      (R):    ISO 527  ||  9402|3|0|-1
    UTS    (R):    ISO 527  ||  9402|5|0|-1
    %El    (R):    ISO 527  ||  at break  ||  9402|29|0|0
    UCS    (N):    ISO 604  ||  9402|47|0|-1

return to listing



Vespel TP-8311

    E      (R):    ISO 527  ||  9404|3|0|-1
    UTS    (R):    ISO 527  ||  9404|5|0|-1
    %El    (R):    ISO 527  ||  at break  ||  9404|29|0|0
    UCS    (N):    ISO 604  ||  9404|47|0|-1

return to listing



W - 20 Ta - 12 Mo (wt %)

    SR     (N):    cast and extruded  ||  tested at 1927 °C (3500 °F)  ||  9519|22|0|0
    SR     (N):    cast and extruded  ||  Master curve (LMP)  ||  9519|22|0|1

return to listing



WC - 13 Co (wt %)

    E      (N):    solid  ||  456|3|0|-1
    G      (N):    solid  ||  456|11|0|-1
    SSCC   (N):    5 x 10-3/s  ||  tested at 20 °C (68 °F)  ||  456|12|0|0
    SSCC   (N):    5 x 10-3/s  ||  tested at 200 °C (392 °F)  ||  456|12|0|1
    SSCC   (N):    5 x 10-3/s  ||  tested at 400 °C (752 °F)  ||  456|12|0|2
    SSCC   (N):    5 x 10-3/s  ||  tested at 600 °C (1112 °F)  ||  456|12|0|3
    SSCC   (N):    5 x 10-3/s  ||  tested at 800 °C (1472 °F)  ||  456|12|0|4
    SSCC   (N):    5 x 10-3/s  ||  tested at 900 °C (1652 °F)  ||  456|12|0|5
    v      (N):    solid  ||  456|19|0|-1
    YSC    (N):    solid  ||  456|21|0|-1
    K      (N):    solid  ||  456|27|0|-1

return to listing



WC - 15 Co (wt %)

    G      (N):    solid  ||  457|11|0|-1
    v      (N):    solid  ||  457|19|0|-1
    TD     (N):    solid  ||  0.5 micron WC grain size  ||  457|25|0|0
    TD     (N):    solid  ||  0.3 micron to 5.2 micron WC grain size, hardness 1530 HV10  ||  457|25|0|1
    TD     (N):    solid  ||  0.3 micron to 5.2 micron WC grain size, hardness 1175 HV10  ||  457|25|0|2
    K      (N):    solid  ||  457|27|0|-1

return to listing



WC - 8 Co (wt %) (New)

    DLL       :    solid  ||  16580|0|0|-1
    E         :    solid  ||  Dawihl and Mal  ||  16580|3|0|0
    MTE       :    solid  ||  16580|8|0|-1
    G         :    solid  ||  Dawihl and Mal  ||  16580|11|0|0
    CTE       :    solid  ||  16580|16|0|-1
    v         :    solid  ||  16580|19|0|-1
    D         :    solid  ||  16580|24|0|-1
    K         :    solid  ||  Dawihl and Mal  ||  16580|27|0|0

return to listing



WC - 10 Co (wt %) (New)

    DLL       :    solid  ||  16560|0|0|-1
    E         :    solid  ||  16560|3|0|-1
    MTE       :    solid  ||  16560|8|0|-1
    G         :    solid  ||  16560|11|0|-1
    SSCC      :    5 x 10-3/s  ||  tested at 20 °C (68 °F)  ||  16560|12|0|0
    SSCC      :    5 x 10-3/s  ||  tested at 200 °C (392 °F)  ||  16560|12|0|1
    SSCC      :    5 x 10-3/s  ||  tested at 400 °C (752 °F)  ||  16560|12|0|2
    SSCC      :    5 x 10-3/s  ||  tested at 600 °C (1112 °F)  ||  16560|12|0|3
    SSCC      :    5 x 10-3/s  ||  tested at 800 °C (1472 °F)  ||  16560|12|0|4
    SSCC      :    5 x 10-3/s  ||  tested at 900 °C (1652 °F)  ||  16560|12|0|5
    CTE       :    solid  ||  16560|16|0|-1
    v         :    solid  ||  16560|19|0|-1
    YSC       :    solid  ||  16560|21|0|-1
    D         :    solid  ||  16560|24|0|-1
    TD        :    solid  ||  1 micron WC grain size  ||  16560|25|0|0
    TD        :    solid  ||  0.5 micron WC grain size  ||  16560|25|0|1
    TD        :    solid  ||  0.3 micron WC grain size  ||  16560|25|0|2
    TD        :    solid  ||  0.2 micron WC grain size  ||  16560|25|0|3
    TD        :    solid  ||  0.3 micron to 5.2 micron WC grain size, hardness 1530 HV10  ||  16560|25|0|4
    TD        :    solid  ||  0.3 micron to 5.2 micron WC grain size, hardness 1175 HV10  ||  16560|25|0|5
    K         :    solid  ||  16560|27|0|-1

return to listing



WC - 20 Co (wt %) (New)

    E         :    solid  ||  16561|3|0|-1
    G         :    solid  ||  16561|11|0|-1
    v         :    solid  ||  16561|19|0|-1
    D     (*):    solid  ||  16561|24|0|-1
    TD        :    solid  ||  0.5 micron WC grain size  ||  16561|25|0|0
    TD        :    solid  ||  0.3 micron to 5.2 micron WC grain size, hardness 1530 HV10  ||  16561|25|0|1
    TD        :    solid  ||  0.3 micron to 5.2 micron WC grain size, hardness 1175 HV10  ||  16561|25|0|2
    K         :    solid  ||  16561|27|0|-1

return to listing



WC - 3 Co (wt %)

    E      (N):    solid  ||  449|3|0|-1
    SH     (R):    solid  ||  449|9|0|-1
    G      (N):    solid  ||  449|11|0|-1
    v      (N):    solid  ||  449|19|0|-1
    K      (N):    solid  ||  449|27|0|-1

return to listing



WC - 25 Co (wt %)

    G      (N):    solid  ||  458|11|0|-1
    v      (R):    solid  ||  458|19|0|-1
    K      (N):    solid  ||  458|27|0|-1

return to listing



WC - 9 Co (wt %)

    G      (N):    solid  ||  453|11|0|-1
    SSCC   (R):    1 x 10-4/s  ||  tested at 20 °C (68 °F)  ||  453|12|0|0
    v      (N):    solid  ||  453|19|0|-1
    K      (N):    solid  ||  453|27|0|-1

return to listing



WC - 5 Co (wt %)

    TC     (N):    solid  ||  0.5 micron WC grain size, hardness 1800 HV10  ||  450|1|0|0
    TC     (N):    solid  ||  0.3 micron to 5.2 micron WC grain size, hardness 1530 HV10  ||  450|1|0|1
    E      (N):    solid  ||  450|3|0|-1
    SH     (R):    solid  ||  450|9|0|-1
    G      (N):    solid  ||  450|11|0|-1
    v      (N):    solid  ||  450|19|0|-1
    TD     (N):    solid  ||  0.5 micron WC grain size, hardness 1800 HV10  ||  450|25|0|0
    TD     (N):    solid  ||  0.3 micron to 5.2 micron WC grain size, hardness 1530 HV10  ||  450|25|0|1
    K      (N):    solid  ||  450|27|0|-1

return to listing



WC - 11 Co (wt %)

    E      (N):    solid  ||  454|3|0|-1
    G      (N):    solid  ||  454|11|0|-1
    SSCC   (R):    1 x 10-4/s  ||  tested at 20 °C (68 °F)  ||  454|12|0|0
    SSCC   (N):    5 x 10-3/s  ||  tested at 20 °C (68 °F)  ||  454|12|1|0
    SSCC   (N):    5 x 10-3/s  ||  tested at 200 °C (392 °F)  ||  454|12|1|1
    SSCC   (N):    5 x 10-3/s  ||  tested at 400 °C (752 °F)  ||  454|12|1|2
    SSCC   (N):    5 x 10-3/s  ||  tested at 600 °C (1112 °F)  ||  454|12|1|3
    SSCC   (N):    5 x 10-3/s  ||  tested at 800 °C (1472 °F)  ||  454|12|1|4
    SSCC   (N):    5 x 10-3/s  ||  tested at 900 °C (1652 °F)  ||  454|12|1|5
    v      (N):    solid  ||  454|19|0|-1
    YSC    (N):    solid  ||  454|21|0|-1
    K      (N):    solid  ||  454|27|0|-1

return to listing



WC - 12 Co (wt %)

    E      (N):    solid  ||  455|3|0|-1
    SH     (R):    solid  ||  455|9|0|-1
    G      (N):    solid  ||  455|11|0|-1
    SSCC   (N):    5 x 10-3/s  ||  tested at 20 °C (68 °F)  ||  455|12|0|0
    SSCC   (N):    5 x 10-3/s  ||  tested at 200 °C (392 °F)  ||  455|12|0|1
    SSCC   (N):    5 x 10-3/s  ||  tested at 400 °C (752 °F)  ||  455|12|0|2
    SSCC   (N):    5 x 10-3/s  ||  tested at 600 °C (1112 °F)  ||  455|12|0|3
    SSCC   (N):    5 x 10-3/s  ||  tested at 800 °C (1472 °F)  ||  455|12|0|4
    SSCC   (N):    5 x 10-3/s  ||  tested at 900 °C (1652 °F)  ||  455|12|0|5
    v      (N):    solid  ||  455|19|0|-1
    YSC    (N):    solid  ||  455|21|0|-1
    K      (N):    solid  ||  455|27|0|-1

return to listing



WC - 6 Co (wt %)

    E      (N):    solid  ||  Teppernegg et. al.  ||  451|3|0|1
    E      (N):    solid  ||  average  ||  451|3|0|2
    G      (N):    solid  ||  Dawihl and Mal  ||  451|11|0|0
    G      (N):    solid  ||  Teppernegg et. al.  ||  451|11|0|1
    G      (N):    solid  ||  average  ||  451|11|0|2
    SSCC   (R):    1 x 10-4/s  ||  tested at 20 °C (68 °F)  ||  451|12|0|0
    SSCC   (N):    5 x 10-3/s  ||  tested at 20 °C (68 °F)  ||  451|12|1|0
    SSCC   (N):    5 x 10-3/s  ||  tested at 200 °C (392 °F)  ||  451|12|1|1
    SSCC   (N):    5 x 10-3/s  ||  tested at 400 °C (752 °F)  ||  451|12|1|2
    SSCC   (N):    5 x 10-3/s  ||  tested at 600 °C (1112 °F)  ||  451|12|1|3
    SSCC   (N):    5 x 10-3/s  ||  tested at 800 °C (1472 °F)  ||  451|12|1|4
    SSCC   (N):    5 x 10-3/s  ||  tested at 900 °C (1652 °F)  ||  451|12|1|5
    v      (N):    solid  ||  451|19|0|-1
    YSC    (N):    solid  ||  0.2% offset  ||  451|21|0|1
    K      (N):    solid  ||  Dawihl and Mal  ||  451|27|0|0
    K      (N):    solid  ||  Teppernegg et. al.  ||  451|27|0|1
    K      (N):    solid  ||  average  ||  451|27|0|2

return to listing



WC - 7 Co (wt %)

    E      (N):    solid  ||  452|3|0|-1
    SH     (R):    solid  ||  452|9|0|-1
    G      (N):    solid  ||  452|11|0|-1
    v      (N):    solid  ||  452|19|0|-1
    K      (N):    solid  ||  452|27|0|-1

return to listing



WSe2

    RIW    (N):    measured in unknown ambient  ||  tested at 23 °C (73 °F), 100 nm thick film  ||  2527|45|0|0
    RIW    (N):    measured in unknown ambient  ||  tested at 23 °C (73 °F), 175 nm thick film  ||  2527|45|0|1
    RIW    (N):    measured in unknown ambient  ||  tested at 23 °C (73 °F), 250 nm thick film  ||  2527|45|0|2
    RIW    (N):    measured in unknown ambient  ||  tested at 23 °C (73 °F), 325 nm thick film  ||  2527|45|0|3
    RIW    (N):    measured in unknown ambient  ||  tested at 23 °C (73 °F), 400 nm thick film  ||  2527|45|0|4

return to listing



Y3Fe5O12 (YIG)

    E      (N):    solid  ||  along the [100] direction  ||  641|3|0|0
    E      (N):    solid  ||  along the [110] direction  ||  641|3|0|1
    G      (N):    solid  ||  along the [100] direction  ||  641|11|0|0
    v      (N):    solid  ||  along the [100] direction  ||  641|19|0|0
    K      (N):    solid  ||  along the [100] direction  ||  641|27|0|0

return to listing



Zinc

    ST     (N):    liquid  ||  positive temperature dependence  ||  864|38|1|1

return to listing



Zircaloy-2

    SSC    (N):    11 micron grain size  ||  tested at 350 °C (662 °F), 6.3 x 10-5/s  ||  2379|4|0|0
    SSC    (N):    11 micron grain size  ||  tested at 350 °C (662 °F), 6.3 x 10-3/s  ||  2379|4|0|1
    SSC    (N):    11 micron grain size  ||  tested at 350 °C (662 °F), 0.63/s  ||  2379|4|0|2

return to listing



Zirconium

    SSC    (N):    annealed, 10 micron grains  ||  tested at -196.1 °C (-321.1 °F), 4.2 x 10-4/s  ||  874|4|0|0
    SSC    (N):    annealed, 10 micron grains  ||  tested at 23 °C (73 °F), 4.2 x 10-4/s  ||  874|4|0|1
    SSC    (N):    annealed, 10 micron grains  ||  tested at 180 °C (356 °F), 4.2 x 10-4/s  ||  874|4|0|2
    SSC    (N):    annealed, 47 micron grains  ||  tested at -196.1 °C (-321.1 °F), 4.2 x 10-4/s  ||  874|4|2|0
    SSC    (N):    annealed, 47 micron grains  ||  tested at 23 °C (73 °F), 4.2 x 10-4/s  ||  874|4|2|1
    SSC    (N):    annealed, 47 micron grains  ||  tested at 180 °C (356 °F), 4.2 x 10-4/s  ||  874|4|2|2
    FSN    (N):    0.003 O2 (wt %)  ||  tested at 20 °C (68 °F), R = -1, axial, 36 micron grain size, maximum stress  ||  874|6|0|0
    FSN    (N):    0.003 O2 (wt %)  ||  tested at 20 °C (68 °F), R = -1, axial, 110 micron grain size, maximum stress  ||  874|6|0|1
    FSN    (N):    0.0775 O2 (wt %)  ||  tested at 20 °C (68 °F), R = -1, axial, 30 micron grain size, maximum stress  ||  874|6|1|0
    FSN    (N):    0.0775 O2 (wt %)  ||  tested at 20 °C (68 °F), R = -1, axial, 93 micron grain size, maximum stress  ||  874|6|1|1
    HE     (N):    liquid  ||  874|20|1|-1
    ST     (N):    liquid  ||  874|38|1|-1

return to listing



Zn - 0.16 Pb (at %) (New)

    DLL       :    liquid  ||  16446|0|1|-1
    MTE       :    liquid  ||  16446|8|1|-1
    CTE       :    liquid  ||  16446|16|1|-1
    D         :    liquid  ||  16446|24|1|-1
    Vis       :    liquid  ||  16446|26|1|-1

return to listing



Zn - 0.52 Pb (at %) (New)

    DLL       :    liquid  ||  16447|0|1|-1
    MTE       :    liquid  ||  16447|8|1|-1
    CTE       :    liquid  ||  16447|16|1|-1
    D         :    liquid  ||  16447|24|1|-1
    Vis       :    liquid  ||  16447|26|1|-1

return to listing



ZnTe

    VP     (N):    solid  ||  partial pressure of Zn  ||  2524|18|0|0

return to listing



ZrC

    NE     (N):    solid  ||  Fisenko and Lemberg  ||  208|28|0|1

return to listing



Zr2Ni (New)

    ST        :    liquid  ||  16611|38|1|-1

return to listing



Zytel 101

    Vis    (N):    liquid  ||  measured at a shear rate of 1000/s  ||  1998|26|1|0
    AV     (N):    liquid  ||  tested at 290 °C (554 °F)  ||  1998|34|1|0
    AV     (N):    liquid  ||  tested at 295 °C (563 °F), 0.07% H2O  ||  1998|34|1|1
    AV     (N):    liquid  ||  tested at 295 °C (563 °F), 0.2% H2O  ||  1998|34|1|2
    SV     (N):    tested at pressure = 100 kPa (14.5 psi)  ||  1998|40|0|-1
    SV     (N):    tested at pressure = 30 MPa (4.35 ksi)  ||  1998|40|1|-1
    SV     (N):    tested at pressure = 60 MPa (8.70 ksi)  ||  1998|40|2|-1
    SV     (N):    tested at pressure = 80 MPa (11.6 ksi)  ||  1998|40|3|-1
    SV     (N):    tested at pressure = 100 MPa (14.5 ksi)  ||  1998|40|4|-1
    SV     (N):    tested at pressure = 120 MPa (17.4 ksi)  ||  1998|40|5|-1
    SV     (N):    tested at pressure = 150 MPa (21.8 ksi)  ||  1998|40|6|-1

return to listing



Zytel 70G30HSL

    Vis    (N):    liquid  ||  measured at a shear rate of 1000/s  ||  2013|26|1|0
    AV     (N):    liquid  ||  tested at 290 °C (554 °F)  ||  2013|34|1|0

return to listing



Zytel ST801

    Vis    (N):    liquid  ||  measured at a shear rate of 1000/s  ||  2010|26|1|0
    AV     (N):    liquid  ||  tested at 290 °C (554 °F)  ||  2010|34|1|0

return to listing



Data listing by property
Dataset listing by material
JAHM Software