New and revised materials and properties in MPDB v9.75 as compared to v9.73

Key to property symbols (number of datasets):

D = Density	DLL = Linear thermal expansion (ΔL/L)
MTE = Mean coefficient of thermal expansion	CTE = Coefficient of thermal expansion (CTE)
E = Elastic/Young's modulus	G = Shear modulus
v = Poisson's ratio	K = Bulk modulus
TC = Thermal conductivity	TD = Thermal diffusivity
SH = Specific heat	HC = Heat capacity
SSC = True stress-strain curve (tension)	SSCC = True stress-strain curve (compression)
UTS = Tensile strength	YS = Yield strength (tension)
UCS = Compressive strength	YSC = Yield strength (compression)
%El = Elongation	SR = Stress rupture
FEN = Fatigue ε-N curve	FSN = Fatigue S-N curve
CRS = Creep strength	IC = Isochronous creep
HE = Hemispherical total emissivity	NE = Normal total emissivity
VP = Vapor pressure	Vis = Viscosity
ST = Surface tension	RHO = Electrical resistivity
SIGMA = Electrical conductivity	SV = Specific volume
AV = Apparent viscosity	FM = Flexural modulus
FS = Flexural strength	ESSC = Engineering stress-strain curve (tension)
ESSCC = Engineering stress-strain curve (compression)	CRM = Creep modulus
RPB = Relative permeability	AP = Absolute permeability
BH = B-H curve	HB = H-B curve
CL = Core loss	EP = Exciting Power
DCRPT = Relative permittivity	DF = Dissipation factor
RIW = Refractive index vs λ	RIT = Refractive index vs T
S = Seebeck coefficient

"(N)" indicates the data is new, "(R)" indicates the data has been revised, * indicates the data is the RT value only

120 new materials, 2097 new property sets, 116 revised properties, and 496 new RT values

1075	301	347	405	410
430	2090	5754	6005	6061
8090	A383	A283C (S235)	Acktar Diffusive White coating (New)	Acktar Fractal Black coating (New)
ACuZinc 5	AE44	AgCl	Air	Al - 5.9 Si - 1.6 Fe (wt %) (New)
Al - 90 Si (wt %) (New)	AlBeMet 162	Alloy 7	Alloy 2	Alloy 3
Alloy 5	AlN	Al₂O₃ (alpha)	ALON	AM-350
Argon	As₂Se₃	BaF₂	BaFe₁₂O₁₉ (Co doped)	Betamate 4601
Bi₀_.₉₈₅Na₀_.₀₁₅CuSeO (Pb doped) (New)	Biodiesel	Bismuth (Revised)	Bi₂Te₂_.₇Se₀_.₃ (various dopants)	B₂O₃ (Revised)
B500SP (steel reinforcing bar) (New)	CaCO₃ (calcite)	CaC₂O₄-H₂O (New)	CaC₂O₄ (New)	Ca₃Co₄O₉ (Sr doped)
Cadmium (Revised)	CaF₂	Canola/rapeseed oil	Capric acid (New)	Carpenter Stainless Type 430F solenoid quality
Carpenter Stainless Type 430FR solenoid quality	CaS	CdP₂ (New)	CdS	CE30
Cellulose acetate butyrate (CAB)	CF8	CF20	CF3	CFC-113 (C₂Cl₃F₃) (New)
CFC-114 (C₂Cl₂F₄) (New)	CFC-11 (CCl₃F) (New)	CFC-12 (CCl₂F₂) (New)	CFC-13 (CClF₃) (New)	CF8C
CF16F	CF12M	CF3M	CF8M	CH₄ (methane)
CH20	CHEMGLAZE Z306 black coating (New)	Chrome Core 18-FM Solenoid Quality Stainless	Chrome core 12-FM	Chrome core 8-FM
Chrome core 8	Chrome core 12	Chromel R (New)	CK20	CN7M
CO	Coconut oil (New)	Consumet electrical iron	Corn oil	Crambe oil (New)
CsBr	CsI	Cu - 16 Ag (wt %)	Cu - 24 Ag (wt %)	Cu - 7 Ag (wt %)
Cu - 40 Ag (wt %) (New)	Cu - 2 Ag (wt %) (New)	Cu - 8 Ag (wt %) (New)	Cu - 10 Ag (wt %) (New)	Cu - 4 Ag (wt %) (New)
Cu - 20 Ag (wt %) (New)	Cu - 6 Ag (wt %) (New)	Cu - 30 Ag (wt %) (New)	98.4 Cu - 1.6 Bi (at %) (New)	98.7 Cu - 1.3 Bi (at %) (New)
99 Cu - 1 Bi (at %) (New)	99.4 Cu - 0.6 Bi (at %) (New)	99.7 Cu - 0.3 Bi (at %) (New)	76.7 Cu - 23.3 Bi (at %) (New)	83.1 Cu - 16.9 Bi (at %) (New)
88.5 Cu - 11.5 Bi (at %) (New)	92.9 Cu - 7.1 Bi (at %) (New)	96.7 Cu - 3.3 Bi (at %) (New)	90 Cu - 8 Pb - 2 Fe (at %) (New)	90 Cu - 6 Pb - 4 Fe (at %) (New)
90 Cu - 4 Pb - 6 Fe (at %) (New)	90 Cu - 2 Pb - 8 Fe (at %) (New)	90 Cu - 0 Pb - 10 Fe (at %) (New)	80 Cu - 20 Pb - 0 Fe (at %) (New)	80 Cu - 18 Pb - 2 Fe (at %) (New)
80 Cu - 16 Pb - 4 Fe (at %) (New)	80 Cu - 14 Pb - 6 Fe (at %) (New)	80 Cu - 12 Pb - 8 Fe (at %) (New)	80 Cu - 10 Pb - 10 Fe (at %) (New)	70 Cu - 30 Pb - 0 Fe (at %) (New)
70 Cu - 27 Pb - 3 Fe (at %) (New)	70 Cu - 24 Pb - 6 Fe (at %) (New)	70 Cu - 21 Pb - 9 Fe (at %) (New)	90 Cu - 10 Pb - 0 Fe (at %) (New)	Cu₁₂_-_mCo_mSb₄S₁₃_-_nSe_n (New)
Cu₁_-_xFeS₂ (Pd doped) (New)	CuFeS₂	Cu₆Fe₂SnS₈/Cu₂FeSnS₄ composite (New)	Cu₁₂Sb₄S₁₃ (New)	Cu₂Se (Cl doped)
Diesel fuel	DP 690	DP 600	Ductile Ni-Resist D-5S	Dy₃TaO₇ (Revised)
Er₃TaO₇ (Revised)	Erucic acid (New)	EuPd₂As₂ (New)	Eu₃TaO₇ (Revised)	Fe - 3.9 Si (wt %) (Revised)
Fe - 4.4 Si (wt %) (Revised)	Fe - 8 Si (wt %) (Revised)	Fe - 10 Si (wt %) (Revised)	Fe - 12 Si (wt %) (Revised)	Fe - 1 Si (wt %) (Revised)
Fe - 1.8 Si (wt %) (Revised)	Fe - 2.8 Si (wt %) (Revised)	Fluorine	GaAs	GaSb
Gd₃TaO₇ (Revised)	GdVO₄	Ge₀_.₉₅_-_xMg₀_.₀₅Sb_xTe (New)	GeTe	Grapeseed oil
Graphite AXF-5Q (Revised)	Graphite AXM-5Q	Graphite ZXF-5Q (Revised)	Haynes R-41 (Rene 41) (Revised)	H₃BO₃ (Revised)
HCFC-22 (CHClF) (New)	HCFC-123 (C₂HCl₂F₃) (Revised)	HCFC-142b (CH₃CClF₂) (New)	HF Alloy	HFC-23 (CHF₃)
HFC-152a (C₂H₄F₂)	HFC-134a (C₂HF₅) (Revised)	HfSi₂	High Permeability 49	High Permeability 55 (New)
Hiperco 50 alloy	Hiperco 50 HS alloy	Hiperco 50A alloy	Hipernom alloy	HoCa₄O(BO₃)₃
Ho₃TaO₇ (Revised)	Hy-Ra 80 alloy	Hydrogen	HyMu 80 alloy (Permalloy 80)	Hytrel 4068
Hytrel 4069	Hytrel 4556	Hytrel 5526	Hytrel 5556	Hytrel 6356
Hytrel 7246	Hytrel 8238	Hytrel 3078	Hytrel 4056	Hytrel G4078
Hytrel G4774	Hytrel G5544	Hytrel G3548	Hytrel G4074	Hytrel G4078LS
Hytrel 5555HS	IN-100	Inconel 600	Inconel X-750 (Revised)	InSb
KBr	KI	KURARITY KL-LK9333 (New)	KURARITY LA4285	KURARITY LA2250
KURARITY LA2270	KURARITY LA2114 (New)	KURARITY LA2330 (New)	KURARITY LA3320 (New)	KURARITY LK9243 (New)
304L	La₃TaO₇ (Revised)	Lauric acid (New)	Lesquerella oil (New)	LiAl (New)
LiF	Li₁₃Si₄ (Revised)	Lu₃TaO₇ (Revised)	Manganese (Revised)	MgF₂
MgO	Milkweed oil (New)	Monel K-500 (Revised)	Myristic acid (New)	NaCl
NaF	NaNO₃	Nd:GdVO₄ (Revised)	Nd:YVO₄ (Revised)	Neon
9 Ni steel	Nickel 270 (New)	Nickel (Revised)	Niobium	Nitrogen
Nonanoic acid (New)	Oleic acid (New)	Palm oil	Palmitic acid (New)	PbSe (Revised)
PbTe (Revised)	Platinum (Revised)	Pt - 10 Ir (wt %) (New)	Pt - 20 Ir (wt %) (New)	Pt - 30 Ir (wt %) (New)
Pt - 20 Rh (wt %) (PtRh20)	Pt - 15 Rh (wt %) (PtRh15) (New)	Pt - 7 Rh (wt %) (PtRh7) (New)	Pt - 30 Rh (wt %) (PtRh30) (New)	Pt - 10 Rh (wt %) (PtRh10) (Revised)
Pt - 12 Rh (wt %)	PWA 1484	Pyrolytic graphite	R-449A (New)	RE-170 (CH₃OCH₃) (Revised)
Rene 95	Rubitherm RT70HC PCM (New)	65 Se - 35 As (at %) (New)	60 Se - 40 As (at %) (New)	91.6 Se - 8.4 As (at %) (New)
90 Se - 10 As (at %) (New)	85 Se - 15 As (at %) (New)	80 Se - 20 As (at %) (New)	75 Se - 25 As (at %) (New)	70 Se - 30 As (at %) (New)
SEN6 (New)	Silicon core iron A-FM	Silicon core iron A	Silicon core iron B-FM	Silicon core iron B
Silicon core iron C	Sm₃TaO₇ (Revised)	Sn - 3.5 Ag (wt %)	Soybean oil	SrTiO₃ (Cr doped)
Stearic acid (New)	Sunflower oil	Superloy GDSL	Tata NO30-1500H electrical steel (New)	Tata NO35-1750H electrical steel (New)
Tata NO18-1160H electrical steel (New)	Tata NO20-1200H electrical steel (New)	Tata NO20-1300H electrical steel (New)	Tata NO25-1350H electrical steel (New)	Tata NO27-1400H electrical steel (New)
Tata NO27-1450H electrical steel (New)	Tata NO12-1180N electrical steel (New)	Tata NO15-1230N electrical steel (New)	Tata NO20-1350N electrical steel (New)	Tata NO10-1270N electrical steel (New)
Tata NO18-1280N electrical steel (New)	Tellurium	Temperature compensator 32 (type 1)	Temperature compensator 30 (types 2, 3, 4)	Ti - 5 Al - 2.5 Sn (Grade 6) (Revised)
Ti - 3 Al - 2.5 V - 0.05 Pd (Grade 18)	Ti - 3 Al - 2.5 V (Grade 9)	Ti - 6 Al - 4 V	Ti - 16 V - 2.5 Al (wt %) (New)	Ti - 13 V - 11 Cr - 3 Al (wt %) (Revised)
Ti - 32.4 V (wt %) (New)	Ti - 13.2 V (wt %) (New)	Ti - 26.2 V (wt %) (New)	TiO₂ (rutile)	TiSi₂
TiSi	40 TlBr - 60 TlCl (mol %)	42 TlBr - 58 TlI (mol %) (New)	Tritan TX1001	UNS C96970
UNS C17200	UNS C27400	UNS C70500 (New)	UNS C71100 (New)	UNS C72150 (New)
V - 4.7 Ti (wt %)	V - 48.4 Ti (wt %) (New)	V - 11.8 Ti (wt %) (New)	V - 23.9 Ti (wt %) (New)	V - 36.1 Ti (wt %) (New)
Vanadium	Vespel SP-21	WE43	Wear Resistant HyMu 800A alloy	Y₃Al₅O₁₂ (YAG) (Revised)
YVO₄	Zinc (Revised)	80 ZrO₂ - 20 Al₂O₃ (wt %)	55 ZrO₂ - 45 Al₂O₃ (wt %)	ZrSi₂

1075

    FEN    (N):    hardened & tempered || tested at 21 °C (70 °F), R = -1, flexure, maximum strain || 988|14|0|0
    FEN    (N):    hardened & tempered || tested at -79 °C (-110 °F), R = -1, flexure, maximum strain || 988|14|0|1
    FEN    (N):    hardened & tempered || tested at -195.6 °C (-320 °F), R = -1, flexure, maximum strain || 988|14|0|2
    FEN    (N):    hardened & tempered || tested at -252.8 °C (-423 °F), R = -1, flexure, maximum strain || 988|14|0|3

return to listing

301

    UTS    (N):    60% cold-rolled || unnotched, longitudinal || 1244|5|4|0
    UTS    (N):    60% cold-rolled || unnotched, transverse || 1244|5|4|1
    UTS    (N):    60% cold-rolled || notched, K_t = 3.2, longitudinal || 1244|5|4|2
    UTS    (N):    60% cold-rolled || notched, K_t = 3.2, transverse || 1244|5|4|3
    UTS    (N):    60% cold-rolled || notched, K_t = 6.3, longitudinal || 1244|5|4|4
    UTS    (N):    60% cold-rolled || notched, K_t = 6.3, transverse || 1244|5|4|5
    UTS    (N):    60% cold-rolled || notched, K_t = 19, longitudinal || 1244|5|4|6
    UTS    (N):    60% cold-rolled || notched, K_t = 19, transverse || 1244|5|4|7
    UTS    (N):    60% cold-rolled || weld joint, longitudinal || 1244|5|4|8
    UTS    (N):    60% cold-rolled || weld joint, transverse || 1244|5|4|9
    YS     (N):    60% cold-rolled || unnotched, longitudinal || 1244|13|4|0
    YS     (N):    60% cold-rolled || unnotched, transverse || 1244|13|4|1
    %El    (N):    60% cold-rolled || unnotched, longitudinal || 1244|29|4|0
    %El    (N):    60% cold-rolled || unnotched, transverse || 1244|29|4|1
    %El    (N):    60% cold-rolled || weld joint, longitudinal || 1244|29|4|2
    %El    (N):    60% cold-rolled || weld joint, transverse || 1244|29|4|3

return to listing

347

    FEN    (N):    annealed sheet || tested at 21 °C (70 °F), R = -1, flexure, maximum strain || 1271|14|1|0
    FEN    (N):    annealed sheet || tested at -79 °C (-110 °F), R = -1, flexure, maximum strain || 1271|14|1|1
    FEN    (N):    annealed sheet || tested at -195.6 °C (-320 °F), R = -1, flexure, maximum strain || 1271|14|1|2
    FEN    (N):    annealed sheet || tested at -252.8 °C (-423 °F), R = -1, flexure, maximum strain || 1271|14|1|3

return to listing

405

    SR     (N):    annealed || tested at 482 °C (900 °F) || 997|22|0|0
    SR     (N):    annealed || tested at 538 °C (1000 °F) || 997|22|0|1
    SR     (N):    annealed || tested at 593 °C (1100 °F) || 997|22|0|2
    SR     (N):    annealed || tested at 649 °C (1200 °F) || 997|22|0|3
    SR     (N):    annealed || tested at 704 °C (1300 °F) || 997|22|0|4
    SR     (N):    annealed || tested at 760 °C (1400 °F) || 997|22|0|5
    SR     (N):    annealed || tested at 816 °C (1500 °F) || 997|22|0|6
    SR     (N):    annealed || Master curve (LMP) || 997|22|0|7
    CRS    (N):    0.1% strain || tested at 538 °C (1000 °F) || 997|30|0|0
    CRS    (N):    0.1% strain || tested at 593 °C (1100 °F) || 997|30|0|1
    CRS    (N):    0.1% strain || Master curve (LMP) || 997|30|0|2
    CRS    (N):    0.2% strain || tested at 538 °C (1000 °F) || 997|30|1|0
    CRS    (N):    0.2% strain || tested at 593 °C (1100 °F) || 997|30|1|1
    CRS    (N):    0.2% strain || Master curve (LMP) || 997|30|1|2
    CRS    (N):    0.5% strain || tested at 538 °C (1000 °F) || 997|30|2|0
    CRS    (N):    0.5% strain || tested at 593 °C (1100 °F) || 997|30|2|1
    CRS    (N):    0.5% strain || Master curve (LMP) || 997|30|2|2
    CRS    (N):    1% strain || tested at 538 °C (1000 °F) || 997|30|3|0
    CRS    (N):    1% strain || tested at 593 °C (1100 °F) || 997|30|3|1
    CRS    (N):    1% strain || Master curve (LMP) || 997|30|3|2
    IC     (N):    tested at 538 °C (1000 °F) || 5,000 h || 997|39|0|0
    IC     (N):    tested at 538 °C (1000 °F) || 7,000 h || 997|39|0|1
    IC     (N):    tested at 538 °C (1000 °F) || 10,000 h || 997|39|0|2
    IC     (N):    tested at 593 °C (1100 °F) || 5,000 h || 997|39|1|0
    IC     (N):    tested at 593 °C (1100 °F) || 7,000 h || 997|39|1|1
    IC     (N):    tested at 593 °C (1100 °F) || 10,000 h || 997|39|1|2

return to listing

410

    SR     (N):    annealed || tested at 427 °C (800 °F) || 1000|22|1|0
    SR     (N):    annealed || tested at 482 °C (900 °F) || 1000|22|1|1
    SR     (N):    annealed || tested at 538 °C (1000 °F) || 1000|22|1|2
    SR     (N):    annealed || tested at 593 °C (1100 °F) || 1000|22|1|3
    SR     (N):    annealed || tested at 649 °C (1200 °F) || 1000|22|1|4
    SR     (N):    annealed || tested at 704 °C (1300 °F) || 1000|22|1|5
    SR     (N):    annealed || tested at 760 °C (1400 °F) || 1000|22|1|6
    SR     (N):    annealed || Master curve (LMP) || 1000|22|1|7
    CRS    (N):    0.1% strain || tested at 427 °C (800 °F) || 1000|30|0|0
    CRS    (N):    0.1% strain || tested at 482 °C (900 °F) || 1000|30|0|1
    CRS    (N):    0.1% strain || tested at 538 °C (1000 °F) || 1000|30|0|2
    CRS    (N):    0.1% strain || tested at 593 °C (1100 °F) || 1000|30|0|3
    CRS    (N):    0.1% strain || tested at 649 °C (1200 °F) || 1000|30|0|4
    CRS    (N):    0.1% strain || tested at 704 °C (1300 °F) || 1000|30|0|5
    CRS    (N):    0.1% strain || tested at 760 °C (1400 °F) || 1000|30|0|6
    CRS    (N):    0.2% strain || tested at 427 °C (800 °F) || 1000|30|1|0
    CRS    (N):    0.2% strain || tested at 482 °C (900 °F) || 1000|30|1|1
    CRS    (N):    0.2% strain || tested at 538 °C (1000 °F) || 1000|30|1|2
    CRS    (N):    0.2% strain || tested at 593 °C (1100 °F) || 1000|30|1|3
    CRS    (N):    0.2% strain || tested at 649 °C (1200 °F) || 1000|30|1|4
    CRS    (N):    0.2% strain || tested at 704 °C (1300 °F) || 1000|30|1|5
    CRS    (N):    0.2% strain || tested at 760 °C (1400 °F) || 1000|30|1|6
    CRS    (N):    0.5% strain || tested at 427 °C (800 °F) || 1000|30|2|0
    CRS    (N):    0.5% strain || tested at 482 °C (900 °F) || 1000|30|2|1
    CRS    (N):    0.5% strain || tested at 538 °C (1000 °F) || 1000|30|2|2
    CRS    (N):    0.5% strain || tested at 593 °C (1100 °F) || 1000|30|2|3
    CRS    (N):    0.5% strain || tested at 649 °C (1200 °F) || 1000|30|2|4
    CRS    (N):    0.5% strain || tested at 704 °C (1300 °F) || 1000|30|2|5
    CRS    (N):    0.5% strain || tested at 760 °C (1400 °F) || 1000|30|2|6
    CRS    (N):    1% strain || tested at 427 °C (800 °F) || 1000|30|3|0
    CRS    (N):    1% strain || tested at 482 °C (900 °F) || 1000|30|3|1
    CRS    (N):    1% strain || tested at 538 °C (1000 °F) || 1000|30|3|2
    CRS    (N):    1% strain || tested at 593 °C (1100 °F) || 1000|30|3|3
    CRS    (N):    1% strain || tested at 649 °C (1200 °F) || 1000|30|3|4
    CRS    (N):    1% strain || tested at 704 °C (1300 °F) || 1000|30|3|5
    CRS    (N):    1% strain || tested at 760 °C (1400 °F) || 1000|30|3|6
    IC     (N):    tested at 427 °C (800 °F) || 5,000 h || 1000|39|0|0
    IC     (N):    tested at 427 °C (800 °F) || 6,000 h || 1000|39|0|1
    IC     (N):    tested at 427 °C (800 °F) || 7,000 h || 1000|39|0|2
    IC     (N):    tested at 427 °C (800 °F) || 8,000 h || 1000|39|0|3
    IC     (N):    tested at 427 °C (800 °F) || 9,000 h || 1000|39|0|4
    IC     (N):    tested at 427 °C (800 °F) || 10,000 h || 1000|39|0|5
    IC     (N):    tested at 427 °C (800 °F) || 20,000 h || 1000|39|0|6
    IC     (N):    tested at 482 °C (900 °F) || 5,000 h || 1000|39|1|0
    IC     (N):    tested at 482 °C (900 °F) || 6,000 h || 1000|39|1|1
    IC     (N):    tested at 482 °C (900 °F) || 7,000 h || 1000|39|1|2
    IC     (N):    tested at 482 °C (900 °F) || 8,000 h || 1000|39|1|3
    IC     (N):    tested at 482 °C (900 °F) || 9,000 h || 1000|39|1|4
    IC     (N):    tested at 482 °C (900 °F) || 10,000 h || 1000|39|1|5
    IC     (N):    tested at 482 °C (900 °F) || 20,000 h || 1000|39|1|6
    IC     (N):    tested at 538 °C (1000 °F) || 5,000 h || 1000|39|2|0
    IC     (N):    tested at 538 °C (1000 °F) || 6,000 h || 1000|39|2|1
    IC     (N):    tested at 538 °C (1000 °F) || 7,000 h || 1000|39|2|2
    IC     (N):    tested at 538 °C (1000 °F) || 8,000 h || 1000|39|2|3
    IC     (N):    tested at 538 °C (1000 °F) || 9,000 h || 1000|39|2|4
    IC     (N):    tested at 538 °C (1000 °F) || 10,000 h || 1000|39|2|5
    IC     (N):    tested at 538 °C (1000 °F) || 20,000 h || 1000|39|2|6
    IC     (N):    tested at 593 °C (1100 °F) || 5,000 h || 1000|39|3|0
    IC     (N):    tested at 593 °C (1100 °F) || 6,000 h || 1000|39|3|1
    IC     (N):    tested at 593 °C (1100 °F) || 7,000 h || 1000|39|3|2
    IC     (N):    tested at 593 °C (1100 °F) || 8,000 h || 1000|39|3|3
    IC     (N):    tested at 593 °C (1100 °F) || 9,000 h || 1000|39|3|4
    IC     (N):    tested at 593 °C (1100 °F) || 10,000 h || 1000|39|3|5
    IC     (N):    tested at 593 °C (1100 °F) || 20,000 h || 1000|39|3|6
    IC     (N):    tested at 649 °C (1200 °F) || 5,000 h || 1000|39|4|0
    IC     (N):    tested at 649 °C (1200 °F) || 6,000 h || 1000|39|4|1
    IC     (N):    tested at 649 °C (1200 °F) || 7,000 h || 1000|39|4|2
    IC     (N):    tested at 649 °C (1200 °F) || 8,000 h || 1000|39|4|3
    IC     (N):    tested at 649 °C (1200 °F) || 9,000 h || 1000|39|4|4
    IC     (N):    tested at 649 °C (1200 °F) || 10,000 h || 1000|39|4|5
    IC     (N):    tested at 649 °C (1200 °F) || 20,000 h || 1000|39|4|6
    IC     (N):    tested at 704 °C (1300 °F) || 5,000 h || 1000|39|5|0
    IC     (N):    tested at 704 °C (1300 °F) || 6,000 h || 1000|39|5|1
    IC     (N):    tested at 704 °C (1300 °F) || 7,000 h || 1000|39|5|2
    IC     (N):    tested at 704 °C (1300 °F) || 8,000 h || 1000|39|5|3
    IC     (N):    tested at 704 °C (1300 °F) || 9,000 h || 1000|39|5|4
    IC     (N):    tested at 704 °C (1300 °F) || 10,000 h || 1000|39|5|5
    IC     (N):    tested at 704 °C (1300 °F) || 20,000 h || 1000|39|5|6
    IC     (N):    tested at 760 °C (1400 °F) || 5,000 h || 1000|39|6|0
    IC     (N):    tested at 760 °C (1400 °F) || 6,000 h || 1000|39|6|1
    IC     (N):    tested at 760 °C (1400 °F) || 7,000 h || 1000|39|6|2
    IC     (N):    tested at 760 °C (1400 °F) || 8,000 h || 1000|39|6|3
    IC     (N):    tested at 760 °C (1400 °F) || 9,000 h || 1000|39|6|4
    IC     (N):    tested at 760 °C (1400 °F) || 10,000 h || 1000|39|6|5
    IC     (N):    tested at 760 °C (1400 °F) || 20,000 h || 1000|39|6|6

return to listing

430

    CRS    (N):    0.1% strain || tested at 427 °C (800 °F) || 1005|30|0|0
    CRS    (N):    0.1% strain || tested at 482 °C (900 °F) || 1005|30|0|1
    CRS    (N):    0.1% strain || tested at 538 °C (1000 °F) || 1005|30|0|2
    CRS    (N):    0.1% strain || tested at 593 °C (1100 °F) || 1005|30|0|3
    CRS    (N):    0.1% strain || tested at 649 °C (1200 °F) || 1005|30|0|4
    CRS    (N):    0.1% strain || tested at 704 °C (1300 °F) || 1005|30|0|5
    CRS    (N):    0.1% strain || tested at 760 °C (1400 °F) || 1005|30|0|6
    CRS    (N):    0.1% strain || tested at 816 °C (1500 °F) || 1005|30|0|7
    CRS    (N):    0.1% strain || Master curve (LMP) || 1005|30|0|8
    CRS    (N):    0.2% strain || tested at 427 °C (800 °F) || 1005|30|1|0
    CRS    (N):    0.2% strain || tested at 482 °C (900 °F) || 1005|30|1|1
    CRS    (N):    0.2% strain || tested at 538 °C (1000 °F) || 1005|30|1|2
    CRS    (N):    0.2% strain || tested at 593 °C (1100 °F) || 1005|30|1|3
    CRS    (N):    0.2% strain || tested at 649 °C (1200 °F) || 1005|30|1|4
    CRS    (N):    0.2% strain || tested at 704 °C (1300 °F) || 1005|30|1|5
    CRS    (N):    0.2% strain || tested at 760 °C (1400 °F) || 1005|30|1|6
    CRS    (N):    0.2% strain || tested at 816 °C (1500 °F) || 1005|30|1|7
    CRS    (N):    0.2% strain || Master curve (LMP) || 1005|30|1|8
    CRS    (N):    0.5% strain || tested at 427 °C (800 °F) || 1005|30|2|0
    CRS    (N):    0.5% strain || tested at 482 °C (900 °F) || 1005|30|2|1
    CRS    (N):    0.5% strain || tested at 538 °C (1000 °F) || 1005|30|2|2
    CRS    (N):    0.5% strain || tested at 593 °C (1100 °F) || 1005|30|2|3
    CRS    (N):    0.5% strain || tested at 649 °C (1200 °F) || 1005|30|2|4
    CRS    (N):    0.5% strain || tested at 704 °C (1300 °F) || 1005|30|2|5
    CRS    (N):    0.5% strain || tested at 760 °C (1400 °F) || 1005|30|2|6
    CRS    (N):    0.5% strain || tested at 816 °C (1500 °F) || 1005|30|2|7
    CRS    (N):    0.5% strain || Master curve (LMP) || 1005|30|2|8
    CRS    (N):    1% strain || tested at 427 °C (800 °F) || 1005|30|3|0
    CRS    (N):    1% strain || tested at 482 °C (900 °F) || 1005|30|3|1
    CRS    (N):    1% strain || tested at 538 °C (1000 °F) || 1005|30|3|2
    CRS    (N):    1% strain || tested at 593 °C (1100 °F) || 1005|30|3|3
    CRS    (N):    1% strain || tested at 649 °C (1200 °F) || 1005|30|3|4
    CRS    (N):    1% strain || tested at 704 °C (1300 °F) || 1005|30|3|5
    CRS    (N):    1% strain || tested at 760 °C (1400 °F) || 1005|30|3|6
    CRS    (N):    1% strain || tested at 816 °C (1500 °F) || 1005|30|3|7
    CRS    (N):    1% strain || Master curve (LMP) || 1005|30|3|8
    IC     (N):    tested at 427 °C (800 °F) || 5,000 h || 1005|39|0|0
    IC     (N):    tested at 427 °C (800 °F) || 6,000 h || 1005|39|0|1
    IC     (N):    tested at 427 °C (800 °F) || 7,000 h || 1005|39|0|2
    IC     (N):    tested at 427 °C (800 °F) || 8,000 h || 1005|39|0|3
    IC     (N):    tested at 427 °C (800 °F) || 9,000 h || 1005|39|0|4
    IC     (N):    tested at 427 °C (800 °F) || 10,000 h || 1005|39|0|5
    IC     (N):    tested at 427 °C (800 °F) || 20,000 h || 1005|39|0|6
    IC     (N):    tested at 482 °C (900 °F) || 5,000 h || 1005|39|1|0
    IC     (N):    tested at 482 °C (900 °F) || 6,000 h || 1005|39|1|1
    IC     (N):    tested at 482 °C (900 °F) || 7,000 h || 1005|39|1|2
    IC     (N):    tested at 482 °C (900 °F) || 8,000 h || 1005|39|1|3
    IC     (N):    tested at 482 °C (900 °F) || 9,000 h || 1005|39|1|4
    IC     (N):    tested at 482 °C (900 °F) || 10,000 h || 1005|39|1|5
    IC     (N):    tested at 482 °C (900 °F) || 20,000 h || 1005|39|1|6
    IC     (N):    tested at 538 °C (1000 °F) || 5,000 h || 1005|39|2|0
    IC     (N):    tested at 538 °C (1000 °F) || 6,000 h || 1005|39|2|1
    IC     (N):    tested at 538 °C (1000 °F) || 7,000 h || 1005|39|2|2
    IC     (N):    tested at 538 °C (1000 °F) || 8,000 h || 1005|39|2|3
    IC     (N):    tested at 538 °C (1000 °F) || 9,000 h || 1005|39|2|4
    IC     (N):    tested at 538 °C (1000 °F) || 10,000 h || 1005|39|2|5
    IC     (N):    tested at 538 °C (1000 °F) || 20,000 h || 1005|39|2|6
    IC     (N):    tested at 593 °C (1100 °F) || 5,000 h || 1005|39|3|0
    IC     (N):    tested at 593 °C (1100 °F) || 6,000 h || 1005|39|3|1
    IC     (N):    tested at 593 °C (1100 °F) || 7,000 h || 1005|39|3|2
    IC     (N):    tested at 593 °C (1100 °F) || 8,000 h || 1005|39|3|3
    IC     (N):    tested at 593 °C (1100 °F) || 9,000 h || 1005|39|3|4
    IC     (N):    tested at 593 °C (1100 °F) || 10,000 h || 1005|39|3|5
    IC     (N):    tested at 593 °C (1100 °F) || 20,000 h || 1005|39|3|6
    IC     (N):    tested at 649 °C (1200 °F) || 5,000 h || 1005|39|4|0
    IC     (N):    tested at 649 °C (1200 °F) || 6,000 h || 1005|39|4|1
    IC     (N):    tested at 649 °C (1200 °F) || 7,000 h || 1005|39|4|2
    IC     (N):    tested at 649 °C (1200 °F) || 8,000 h || 1005|39|4|3
    IC     (N):    tested at 649 °C (1200 °F) || 9,000 h || 1005|39|4|4
    IC     (N):    tested at 649 °C (1200 °F) || 10,000 h || 1005|39|4|5
    IC     (N):    tested at 649 °C (1200 °F) || 20,000 h || 1005|39|4|6
    IC     (N):    tested at 704 °C (1300 °F) || 5,000 h || 1005|39|5|0
    IC     (N):    tested at 704 °C (1300 °F) || 6,000 h || 1005|39|5|1
    IC     (N):    tested at 704 °C (1300 °F) || 7,000 h || 1005|39|5|2
    IC     (N):    tested at 704 °C (1300 °F) || 8,000 h || 1005|39|5|3
    IC     (N):    tested at 704 °C (1300 °F) || 9,000 h || 1005|39|5|4
    IC     (N):    tested at 704 °C (1300 °F) || 10,000 h || 1005|39|5|5
    IC     (N):    tested at 704 °C (1300 °F) || 20,000 h || 1005|39|5|6
    IC     (N):    tested at 760 °C (1400 °F) || 5,000 h || 1005|39|6|0
    IC     (N):    tested at 760 °C (1400 °F) || 6,000 h || 1005|39|6|1
    IC     (N):    tested at 760 °C (1400 °F) || 7,000 h || 1005|39|6|2
    IC     (N):    tested at 760 °C (1400 °F) || 8,000 h || 1005|39|6|3
    IC     (N):    tested at 760 °C (1400 °F) || 9,000 h || 1005|39|6|4
    IC     (N):    tested at 760 °C (1400 °F) || 10,000 h || 1005|39|6|5
    IC     (N):    tested at 760 °C (1400 °F) || 20,000 h || 1005|39|6|6
    IC     (N):    tested at 816 °C (1500 °F) || 5,000 h || 1005|39|7|0
    IC     (N):    tested at 816 °C (1500 °F) || 6,000 h || 1005|39|7|1
    IC     (N):    tested at 816 °C (1500 °F) || 7,000 h || 1005|39|7|2
    IC     (N):    tested at 816 °C (1500 °F) || 8,000 h || 1005|39|7|3
    IC     (N):    tested at 816 °C (1500 °F) || 9,000 h || 1005|39|7|4
    IC     (N):    tested at 816 °C (1500 °F) || 10,000 h || 1005|39|7|5
    IC     (N):    tested at 816 °C (1500 °F) || 20,000 h || 1005|39|7|6

return to listing

2090

    TC     (N):    solid || T81 temper || 36|1|0|0
    TC     (N):    solid || unknown condition || 36|1|0|1
    UTS    (N):    plate, T8xxx tempers || longitudinal || 36|5|1|0
    UTS    (N):    plate, T8xxx tempers || transverse || 36|5|1|1
    UTS    (N):    plate, T8xxx tempers || 45 degrees || 36|5|1|2
    SH     (N):    solid || 36|9|0|-1
    YS     (N):    plate, T8xxx tempers || longitudinal || 36|13|1|0
    YS     (N):    plate, T8xxx tempers || transverse || 36|13|1|1
    YS     (N):    plate, T8xxx tempers || 45 degrees || 36|13|1|2
    TD     (N):    solid || T81 temper || 36|25|0|0
    TD     (N):    solid || unknown condition || 36|25|0|1
    %El    (N):    plate, T8xxx tempers || longitudinal || 36|29|1|0
    %El    (N):    plate, T8xxx tempers || transverse || 36|29|1|1
    %El    (N):    plate, T8xxx tempers || 45 degrees || 36|29|1|2

return to listing

5754

    FSN    (N):    shear fatigue of adhesively bonded lap-joint || tested at 20 °C (68 °F), R = -1, maximum stress || 63|6|0|0

return to listing

6005

    SSCC   (N):    1 x 10^-⁴/s || tested at 100 °C (212 °F) || 64|12|0|0
    SSCC   (N):    1 x 10^-⁴/s || tested at 150 °C (302 °F) || 64|12|0|1
    SSCC   (N):    1 x 10^-⁴/s || tested at 175 °C (347 °F) || 64|12|0|2
    SSCC   (N):    1 x 10^-⁴/s || tested at 200 °C (392 °F) || 64|12|0|3
    SSCC   (N):    1 x 10^-⁴/s || tested at 250 °C (482 °F) || 64|12|0|4
    SSCC   (N):    1 x 10^-⁴/s || tested at 300 °C (572 °F) || 64|12|0|5
    SSCC   (N):    1 x 10^-⁴/s || tested at 350 °C (662 °F) || 64|12|0|6
    SSCC   (N):    4 x 10^-⁴/s || tested at 100 °C (212 °F) || 64|12|1|0
    SSCC   (N):    4 x 10^-⁴/s || tested at 150 °C (302 °F) || 64|12|1|1
    SSCC   (N):    4 x 10^-⁴/s || tested at 175 °C (347 °F) || 64|12|1|2
    SSCC   (N):    4 x 10^-⁴/s || tested at 200 °C (392 °F) || 64|12|1|3
    SSCC   (N):    4 x 10^-⁴/s || tested at 250 °C (482 °F) || 64|12|1|4
    SSCC   (N):    4 x 10^-⁴/s || tested at 300 °C (572 °F) || 64|12|1|5
    SSCC   (N):    4 x 10^-⁴/s || tested at 350 °C (662 °F) || 64|12|1|6

return to listing

6061

    SSCC   (N):    1 x 10^-⁴/s || tested at 100 °C (212 °F) || 70|12|0|0
    SSCC   (N):    1 x 10^-⁴/s || tested at 150 °C (302 °F) || 70|12|0|1
    SSCC   (N):    1 x 10^-⁴/s || tested at 175 °C (347 °F) || 70|12|0|2
    SSCC   (N):    1 x 10^-⁴/s || tested at 200 °C (392 °F) || 70|12|0|3
    SSCC   (N):    1 x 10^-⁴/s || tested at 250 °C (482 °F) || 70|12|0|4
    SSCC   (N):    1 x 10^-⁴/s || tested at 300 °C (572 °F) || 70|12|0|5
    SSCC   (N):    1 x 10^-⁴/s || tested at 350 °C (662 °F) || 70|12|0|6
    SSCC   (N):    1 x 10^-⁴/s || tested at 375 °C (707 °F) || 70|12|0|7
    SSCC   (N):    4 x 10^-⁴/s || tested at 100 °C (212 °F) || 70|12|1|0
    SSCC   (N):    4 x 10^-⁴/s || tested at 150 °C (302 °F) || 70|12|1|1
    SSCC   (N):    4 x 10^-⁴/s || tested at 200 °C (392 °F) || 70|12|1|3
    SSCC   (N):    4 x 10^-⁴/s || tested at 250 °C (482 °F) || 70|12|1|4
    SSCC   (N):    4 x 10^-⁴/s || tested at 300 °C (572 °F) || 70|12|1|5
    SSCC   (N):    4 x 10^-⁴/s || tested at 350 °C (662 °F) || 70|12|1|6
    SSCC   (N):    4 x 10^-⁴/s || tested at 375 °C (707 °F) || 70|12|1|7

return to listing

8090

    TC     (N):    solid || T352 temper, forging || 92|1|0|0
    TC     (N):    solid || T8771 temper, rolled plate || 92|1|0|1
    UTS    (N):    plate, T3 temper || longitudinal || 92|5|1|0
    UTS    (N):    plate, T3 temper || transverse || 92|5|1|1
    UTS    (N):    plate, T8xxx tempers || longitudinal || 92|5|2|0
    UTS    (N):    plate, T8xxx tempers || transverse || 92|5|2|1
    UTS    (N):    plate, T8xxx tempers || 45 degrees || 92|5|2|2
    UTS    (N):    plate, T8xxx tempers || through thickness || 92|5|2|3
    FSN    (N):    T6 temper || tested at -196.1 °C (-321.1 °F), R = 0, axial, stress amplitude || 92|6|0|0
    FSN    (N):    T6 temper || tested at 27 °C (80 °F), R = 0, axial, stress amplitude || 92|6|0|1
    SH     (N):    solid || 92|9|0|-1
    YS     (N):    plate, T3 temper || longitudinal || 92|13|1|0
    YS     (N):    plate, T3 temper || transverse || 92|13|1|1
    YS     (N):    plate, T8xxx tempers || longitudinal || 92|13|2|0
    YS     (N):    plate, T8xxx tempers || transverse || 92|13|2|1
    YS     (N):    plate, T8xxx tempers || 45 degrees || 92|13|2|2
    YS     (N):    plate, T8xxx tempers || through thickness || 92|13|2|3
    TD     (N):    solid || T352 temper forging || 92|25|0|0
    TD     (N):    solid || T8771 temper, rolled plate || 92|25|0|1
    %El    (N):    plate, T3 temper || longitudinal || 92|29|1|0
    %El    (N):    plate, T3 temper || transverse || 92|29|1|1
    %El    (N):    plate, T8xxx tempers || longitudinal || 92|29|2|0
    %El    (N):    plate, T8xxx tempers || transverse || 92|29|2|1
    %El    (N):    plate, T8xxx tempers || 45 degrees || 92|29|2|2
    %El    (N):    plate, T8xxx tempers || through thickness || 92|29|2|3

return to listing

A383

    DLL    (N):    liquid || 15104|0|1|-1
    MTE    (N):    liquid || 15104|8|1|-1
    CTE    (N):    liquid || 15104|16|1|-1
    D      (N):    liquid || 15104|24|1|-1
    ST     (N):    liquid || 15104|38|1|-1

return to listing

A283C (S235)

    Vis    (N):    semi-solid state || 16258|26|1|-1
    AV     (N):    semi-solid state || tested at 1485 °C (2705 °F) || 16258|34|1|0

return to listing

Acktar Diffusive White coating (New)

    HE        :    15 microns thick || 16265|20|0|-1

return to listing

Acktar Fractal Black coating (New)

    HE        :    20 microns thick || 16264|20|0|-1
    HE        :    30 microns thick || 16264|20|1|-1
    HE        :    45 microns thick || 16264|20|2|-1

return to listing

ACuZinc 5

    TC    (N*):    solid || 16136|1|0|-1
    MTE   (N*):    solid || 16136|8|0|-1

return to listing

AE44

    UTS    (N):    sand cast, as-cast || 10215|5|0|-1
    UTS    (N):    die cast, as-cast || 10215|5|1|-1
    YS     (N):    sand cast, as-cast || 10215|13|0|-1
    YS     (N):    die cast, as-cast || 10215|13|1|-1
    %El    (N):    sand cast, as-cast || 10215|29|0|-1
    %El    (N):    die cast, as-cast || 10215|29|1|-1

return to listing

AgCl

    RIW    (N):    measured in unknown ambient || tested at 24 °C (75 °F) || 2445|45|0|0

return to listing

Air

    SH     (N):    saturated liquid || 2151|9|1|-1
    VP     (N):    saturated liquid || 2151|18|1|-1
    VP     (N):    saturated vapor || 2151|18|2|-1

return to listing

Al - 5.9 Si - 1.6 Fe (wt %) (New)

    DLL       :    liquid || 16202|0|1|-1
    MTE       :    liquid || 16202|8|1|-1
    CTE       :    liquid || 16202|16|1|-1
    D         :    liquid || 16202|24|1|-1
    ST        :    liquid || 16202|38|1|-1

return to listing

Al - 90 Si (wt %) (New)

    DLL       :    liquid || 16201|0|1|-1
    MTE       :    liquid || 16201|8|1|-1
    CTE       :    liquid || 16201|16|1|-1
    D         :    liquid || 16201|24|1|-1

return to listing

AlBeMet 162

    RHO   (N*):    solid || 1659|2|0|-1
    SH    (N*):    solid || 1659|9|0|-1
    SIGMA (N*):    solid || 1659|10|0|-1
    G     (N*):    solid || 1659|11|0|-1
    v     (N*):    solid || 1659|19|0|-1
    TD    (N*):    solid || 1659|25|0|-1
    K     (N*):    solid || 1659|27|0|-1

return to listing

Alloy 7

    E     (N*):    solid || 9004|3|0|-1
    SH     (N):    solid || 9004|9|0|-1
    TD    (N*):    solid || 9004|25|0|-1

return to listing

Alloy 2

    SH     (N):    solid || 9001|9|0|-1
    TD    (N*):    solid || 9001|25|0|-1

return to listing

Alloy 3

    SH     (N):    solid || 9002|9|0|-1
    TD    (N*):    solid || 9002|25|0|-1

return to listing

Alloy 5

    SH     (N):    solid || 9003|9|0|-1
    TD    (N*):    solid || 9003|25|0|-1

return to listing

AlN

    G     (N*):    solid || 1965|11|0|-1
    v     (N*):    solid || 1965|19|0|-1
    K     (N*):    solid || 1965|27|0|-1

return to listing

Al₂O₃ (alpha)

    RIW    (N):    measured in unknown ambient || tested at 24 °C (75 °F) || 2648|45|0|0

return to listing

ALON

    TC    (N*):    solid || 1966|1|0|-1

return to listing

AM-350

    RHO    (N):    solid || sub-zero cooled, tempered at 454 °C (850 °F) || 1021|2|0|2
    SIGMA (N):    solid || sub-zero cooled, tempered at 454 °C (850 °F) || 1021|10|0|2
    SR     (N):    sub-zero cooled, tempered at 454 °C (850 °F) || tested at 427 °C (800 °F) || 1021|22|1|0
    SR     (N):    sub-zero cooled, tempered at 454 °C (850 °F) || tested at 482 °C (900 °F) || 1021|22|1|1
    SR     (N):    sub-zero cooled, tempered at 538 °C (1000 °F) || tested at 427 °C (800 °F) || 1021|22|2|0
    SR     (N):    sub-zero cooled, tempered at 538 °C (1000 °F) || tested at 482 °C (900 °F) || 1021|22|2|1

return to listing

Argon

    Vis    (N):    saturated liquid || 849|26|1|-1

return to listing

As₂Se₃

    RIW    (N):    glass, measured in unknown ambient || tested at 25 °C (77 °F) || 15824|45|0|0

return to listing

BaF₂

    RIW    (N):    measured in unknown ambient || tested at 25 °C (77 °F) || 2452|45|0|0

return to listing

BaFe₁₂O₁₉ (Co doped)

    SIGMA (N):    Co doped || x = 0.05, BaFe₁₂_-_xCo_xO₁₉, AC at 100 Hz || 14640|10|1|0
    SIGMA (N):    Co doped || x = 0.1, BaFe₁₂_-_xCo_xO₁₉, AC at 100 Hz || 14640|10|1|1

return to listing

Betamate 4601

    FSN    (N):    shear fatigue of adhesively bonded lap-joint || tested at 20 °C (68 °F), R = -1, maximum stress || 957|6|0|0
    D     (N*):    solid || 957|24|0|-1
    %El   (N*):    solid || at break || 957|29|0|0

return to listing

Bi₀_.₉₈₅Na₀_.₀₁₅CuSeO (Pb doped) (New)

    TC        :    undoped || Bi₀_.₉₈₅Na₀_.₀₁₅CuSeO || 16211|1|0|0
    TC        :    Pb doped || 0.04 Pb, Bi₀_.₉₄₅Na₀_.₀₁₅Pb₀_.₀₄CuSeO || 16211|1|1|0
    TC        :    Pb doped || 0.06 Pb, Bi₀_.₉₂₅Na₀_.₀₁₅Pb₀_.₀₆CuSeO || 16211|1|1|1
    TC        :    Pb doped || 0.08 Pb, Bi₀_.₉₀₅Na₀_.₀₁₅Pb₀_.₀₈CuSeO || 16211|1|1|2
    RHO       :    undoped || Bi₀_.₉₈₅Na₀_.₀₁₅CuSeO || 16211|2|0|0
    RHO       :    Pb doped || 0.04 Pb, Bi₀_.₉₄₅Na₀_.₀₁₅Pb₀_.₀₄CuSeO || 16211|2|1|0
    RHO       :    Pb doped || 0.06 Pb, Bi₀_.₉₂₅Na₀_.₀₁₅Pb₀_.₀₆CuSeO || 16211|2|1|1
    RHO       :    Pb doped || 0.08 Pb, Bi₀_.₉₀₅Na₀_.₀₁₅Pb₀_.₀₈CuSeO || 16211|2|1|2
    SIGMA    :    undoped || Bi₀_.₉₈₅Na₀_.₀₁₅CuSeO || 16211|10|0|0
    SIGMA    :    Pb doped || 0.04 Pb, Bi₀_.₉₄₅Na₀_.₀₁₅Pb₀_.₀₄CuSeO || 16211|10|1|0
    SIGMA    :    Pb doped || 0.06 Pb, Bi₀_.₉₂₅Na₀_.₀₁₅Pb₀_.₀₆CuSeO || 16211|10|1|1
    SIGMA    :    Pb doped || 0.08 Pb, Bi₀_.₉₀₅Na₀_.₀₁₅Pb₀_.₀₈CuSeO || 16211|10|1|2
    D     (*):    undoped || 16211|24|0|-1
    S         :    undoped || Bi₀_.₉₈₅Na₀_.₀₁₅CuSeO || 16211|48|0|0
    S         :    Pb doped || 0.04 Pb, Bi₀_.₉₄₅Na₀_.₀₁₅Pb₀_.₀₄CuSeO || 16211|48|1|0
    S         :    Pb doped || 0.06 Pb, Bi₀_.₉₂₅Na₀_.₀₁₅Pb₀_.₀₆CuSeO || 16211|48|1|1
    S         :    Pb doped || 0.08 Pb, Bi₀_.₉₀₅Na₀_.₀₁₅Pb₀_.₀₈CuSeO || 16211|48|1|2

return to listing

Biodiesel

    Vis    (N):    liquid || 3414|26|1|-1

return to listing

Bismuth

    SH     (R):    solid || 917|9|0|-1
    HC     (R):    solid || 917|17|0|-1
    TD     (N):    solid || perpendicular to the trigonal axis || 917|25|0|1
    TD     (N):    solid || parallel to the trigonal axis || 917|25|0|2

return to listing

Bi₂Te₂_.₇Se₀_.₃ (various dopants)

    TC     (N):    Cu doped || 0.008 Cu, carrier concentration = 3.96 x 10¹⁹/cm³, mobility = 141 cm²/(V-s) || 14642|1|4|0
    TC     (N):    Cu & In doped || 0.008 Cu + 0.005 In, carrier concentration = 3.91 x 10¹⁹/cm³, mobility = 139 cm²/(V-s) || 14642|1|7|0
    TC     (N):    Cu & In doped || 0.008 Cu + 0.01 In, carrier concentration = 3.86 x 10¹⁹/cm³, mobility = 132 cm²/(V-s) || 14642|1|7|1
    TC     (N):    Cu & In doped || 0.008 Cu + 0.015 In, carrier concentration = 3.79 x 10¹⁹/cm³, mobility = 129 cm²/(V-s) || 14642|1|7|2
    RHO    (N):    Cu doped || 0.008 Cu, carrier concentration = 3.96 x 10¹⁹/cm³, mobility = 141 cm²/(V-s) || 14642|2|4|0
    RHO    (N):    Cu & In doped || 0.008 Cu + 0.005 In, carrier concentration = 3.91 x 10¹⁹/cm³, mobility = 139 cm²/(V-s) || 14642|2|7|0
    RHO    (N):    Cu & In doped || 0.008 Cu + 0.01 In, carrier concentration = 3.86 x 10¹⁹/cm³, mobility = 132 cm²/(V-s) || 14642|2|7|1
    RHO    (N):    Cu & In doped || 0.008 Cu + 0.015 In, carrier concentration = 3.79 x 10¹⁹/cm³, mobility = 129 cm²/(V-s) || 14642|2|7|2
    SIGMA (N):    Cu doped || 0.008 Cu, carrier concentration = 3.96 x 10¹⁹/cm³, mobility = 141 cm²/(V-s) || 14642|10|4|0
    SIGMA (N):    Cu & In doped || 0.008 Cu + 0.005 In, carrier concentration = 3.91 x 10¹⁹/cm³, mobility = 139 cm²/(V-s) || 14642|10|7|0
    SIGMA (N):    Cu & In doped || 0.008 Cu + 0.01 In, carrier concentration = 3.86 x 10¹⁹/cm³, mobility = 132 cm²/(V-s) || 14642|10|7|1
    SIGMA (N):    Cu & In doped || 0.008 Cu + 0.015 In, carrier concentration = 3.79 x 10¹⁹/cm³, mobility = 129 cm²/(V-s) || 14642|10|7|2
    S      (N):    Cu doped || 0.008 Cu, carrier concentration = 3.96 x 10¹⁹/cm³, mobility = 141 cm²/(V-s) || 14642|48|4|0
    S      (N):    Cu & In doped || 0.008 Cu + 0.005 In, carrier concentration = 3.91 x 10¹⁹/cm³, mobility = 139 cm²/(V-s) || 14642|48|7|0
    S      (N):    Cu & In doped || 0.008 Cu + 0.01 In, carrier concentration = 3.86 x 10¹⁹/cm³, mobility = 132 cm²/(V-s) || 14642|48|7|1
    S      (N):    Cu & In doped || 0.008 Cu + 0.015 In, carrier concentration = 3.79 x 10¹⁹/cm³, mobility = 129 cm²/(V-s) || 14642|48|7|2

return to listing

B₂O₃

    SH     (R):    solid || 6198|9|0|-1
    HC     (R):    solid || 6198|17|0|-1

return to listing

B500SP (steel reinforcing bar) (New)

    DLL       :    solid || 16257|0|0|-1
    E         :    solid || 16257|3|0|-1
    MTE       :    solid || 16257|8|0|-1
    SH        :    solid || 16257|9|0|-1
    G         :    solid || 16257|11|0|-1
    CTE       :    solid || 16257|16|0|-1
    v         :    solid || 16257|19|0|-1
    D         :    solid || 16257|24|0|-1
    Vis       :    semi-solid state || 16257|26|1|-1
    K         :    solid || 16257|27|0|-1
    AV        :    semi-solid state || tested at 1456 °C (2653 °F) || 16257|34|1|0
    AV        :    semi-solid state || tested at 1460 °C (2660 °F) || 16257|34|1|1
    AV        :    semi-solid state || tested at 1462 °C (2664 °F) || 16257|34|1|2
    AV        :    semi-solid state || tested at 1466 °C (2671 °F) || 16257|34|1|3
    AV        :    semi-solid state || tested at 1468 °C (2674 °F) || 16257|34|1|4

return to listing

CaCO₃ (calcite)

    RIW    (N):    measured in unknown ambient || tested at 19 °C (66 °F), ordinary ray || 2465|45|0|0
    RIW    (N):    measured in unknown ambient || tested at 19 °C (66 °F), extraordinary ray || 2465|45|0|1

return to listing

CaC₂O₄-H₂O (New)

    SH        :    solid || without peak do to phase change || 16199|9|0|0
    SH        :    solid || with peak do to phase change || 16199|9|0|1

return to listing

CaC₂O₄ (New)

    SH        :    solid || 16200|9|0|-1

return to listing

Ca₃Co₄O₉ (Sr doped)

    RHO    (N):    as hot-pressed, not aged || 16288|2|0|-1
    RHO    (N):    aged 24 h at 850 °C (1562 °F) || 16288|2|1|-1
    RHO    (N):    aged 96 h at 850 °C (1562 °F) || 16288|2|2|-1
    RHO    (N):    aged 384 h at 850 °C (1562 °F) || 16288|2|3|-1
    RHO    (N):    aged 1536 h at 850 °C (1562 °F) || 16288|2|4|-1
    SIGMA (N):    as hot-pressed, not aged || 16288|10|0|-1
    SIGMA (N):    aged 24 h at 850 °C (1562 °F) || 16288|10|1|-1
    SIGMA (N):    aged 96 h at 850 °C (1562 °F) || 16288|10|2|-1
    SIGMA (N):    aged 384 h at 850 °C (1562 °F) || 16288|10|3|-1
    SIGMA (N):    aged 1536 h at 850 °C (1562 °F) || 16288|10|4|-1
    S      (N):    as hot-pressed, not aged || 16288|48|0|-1
    S      (N):    aged 24 h at 850 °C (1562 °F) || 16288|48|1|-1
    S      (N):    aged 96 h at 850 °C (1562 °F) || 16288|48|2|-1
    S      (N):    aged 386 h at 850 °C (1562 °F) || 16288|48|3|-1
    S      (N):    aged 1536 h at 850 °C (1562 °F) || 16288|48|4|-1

return to listing

Cadmium

    SH     (R):    solid || 882|9|0|-1
    HC     (R):    solid || 882|17|0|-1
    TD     (R):    solid || 882|25|0|-1

return to listing

CaF₂

    RIW    (N):    measured in unknown ambient || tested at 20 °C (68 °F) || 2453|45|2|0

return to listing

Canola/rapeseed oil

    Vis    (N):    liquid || 3411|26|1|-1

return to listing

Capric acid (New)

    Vis       :    liquid || 16187|26|1|-1

return to listing

Carpenter Stainless Type 430F solenoid quality

    UTS   (N*):    25.4 mm (1 inch) diameter bar || mill annealed || 1652|5|0|0
    UTS   (N*):    25.4 mm (1 inch) diameter bar || H₂ annealed || 1652|5|0|1
    YS    (N*):    25.4 mm (1 inch) diameter bar || mill annealed || 1652|13|0|0
    YS    (N*):    25.4 mm (1 inch) diameter bar || H₂ annealed || 1652|13|0|1
    %El   (N*):    25.4 mm (1 inch) diameter bar || mill annealed || 1652|29|0|0
    %El   (N*):    25.4 mm (1 inch) diameter bar || H₂ annealed || 1652|29|0|1

return to listing

Carpenter Stainless Type 430FR solenoid quality

    UTS   (N*):    25.4 mm (1 inch) diameter bar || mill annealed || 1653|5|0|0
    YS    (N*):    25.4 mm (1 inch) diameter bar || mill annealed || 1653|13|0|0
    %El   (N*):    25.4 mm (1 inch) diameter bar || mill annealed || 1653|29|0|0

return to listing

CaS

    RHO    (N):    solid || 15685|2|0|-1
    SIGMA (N):    solid || 15685|10|0|-1

return to listing

CdP₂ (New)

    TC        :    beta phase || perpendicular to c-axis || 16286|1|0|0
    TC        :    beta phase || parallel to c-axis || 16286|1|0|1
    SIGMA    :    [001] || AC at 100 Hz || 16286|10|0|0
    SIGMA    :    [001] || AC at 1 kHz || 16286|10|0|1
    SIGMA    :    [001] || AC at 10 kHz || 16286|10|0|2
    SIGMA    :    [001] || AC at 1 MHz || 16286|10|0|3
    SIGMA    :    [100] || AC at 100 Hz || 16286|10|1|0
    SIGMA    :    [100] || AC at 1 kHz || 16286|10|1|1
    SIGMA    :    [100] || AC at 10 kHz || 16286|10|1|2
    SIGMA    :    [100] || AC at 1 MHz || 16286|10|1|3
    D     (*):    solid || 16286|24|0|-1
    RIW       :    measured in air || tested at 23 °C (73 °F), ordinary ray || 16286|45|0|0
    RIW       :    measured in air || tested at 23 °C (73 °F), extraordinary ray || 16286|45|0|1

return to listing

CdS

    TC    (N*):    solid || 2471|1|0|-1
    TD    (N*):    solid || 2471|25|0|-1
    RIW    (N):    measured in unknown ambient || tested at 23 °C (73 °F) || 2471|45|0|0

return to listing

CE30

    RHO   (N*):    solid || 9640|2|0|-1
    SH    (N*):    solid || 9640|9|0|-1
    SIGMA (N*):    solid || 9640|10|0|-1
    TD    (N*):    solid || 9640|25|0|-1

return to listing

Cellulose acetate butyrate (CAB)

    RIW    (N):    measured in air || tested at 23 °C (73 °F) || 9801|45|0|0

return to listing

CF8

    RHO   (N*):    solid || 9643|2|0|-1
    SIGMA (N*):    solid || 9643|10|0|-1

return to listing

CF20

    RHO   (N*):    solid || 9648|2|0|-1
    SIGMA (N*):    solid || 9648|10|0|-1

return to listing

CF3

    RHO   (N*):    solid || 9641|2|0|-1
    SIGMA (N*):    solid || 9641|10|0|-1

return to listing

CFC-113 (C₂Cl₃F₃) (New)

    ST        :    saturated liquid || 16281|38|1|-1

return to listing

CFC-114 (C₂Cl₂F₄) (New)

    ST        :    saturated liquid || 16282|38|1|-1

return to listing

CFC-11 (CCl₃F) (New)

    TC        :    liquid || 16279|1|1|-1
    TC        :    vapor || 16279|1|2|-1
    SH        :    saturated liquid || 16279|9|1|-1
    HC        :    saturated liquid || 16279|17|1|-1
    Vis       :    liquid || 16279|26|1|-1
    Vis       :    gas || 16279|26|2|-1
    ST        :    saturated liquid || 16279|38|1|-1

return to listing

CFC-12 (CCl₂F₂) (New)

    TC        :    liquid || 16280|1|1|-1
    TC        :    gas || at 1 bar || 16280|1|2|0
    TC        :    gas || at 10 bar || 16280|1|2|1
    TC        :    gas || at 15 bar || 16280|1|2|2
    TC        :    gas || at 18 bar || 16280|1|2|3
    TC        :    gas || at 20 bar || 16280|1|2|4
    TC        :    gas || at 23 bar || 16280|1|2|5
    TC        :    gas || at 25 bar || 16280|1|2|6
    TC        :    gas || at 28 bar || 16280|1|2|7
    TC        :    gas || at 30 bar || 16280|1|2|8
    TC        :    gas || at 32 bar || 16280|1|2|9
    TC        :    gas || at 34 bar || 16280|1|2|10
    TC        :    gas || at 36 bar || 16280|1|2|11
    TC        :    gas || at 38 bar || 16280|1|2|12
    TC        :    gas || at 40 bar || 16280|1|2|13
    TC        :    gas || at 42 bar || 16280|1|2|14
    TC        :    gas || at 42.8 bar || 16280|1|2|15
    SH        :    saturated liquid || 16280|9|1|-1
    HC        :    saturated liquid || 16280|17|1|-1
    Vis       :    liquid || 16280|26|1|-1
    Vis       :    gas || 16280|26|2|-1
    ST        :    saturated liquid || 16280|38|1|-1

return to listing

CFC-13 (CClF₃) (New)

    TC        :    gas || at 1 bar || 16283|1|2|0
    TC        :    gas || at 10 bar || 16283|1|2|1
    TC        :    gas || at 15 bar || 16283|1|2|2
    TC        :    gas || at 18 bar || 16283|1|2|3
    TC        :    gas || at 20 bar || 16283|1|2|4
    TC        :    gas || at 23 bar || 16283|1|2|5
    TC        :    gas || at 25 bar || 16283|1|2|6
    TC        :    gas || at 28 bar || 16283|1|2|7
    TC        :    gas || at 30 bar || 16283|1|2|8
    TC        :    gas || at 32 bar || 16283|1|2|9
    TC        :    gas || at 34 bar || 16283|1|2|10
    TC        :    gas || at 36 bar || 16283|1|2|11
    TC        :    gas || at 38 bar || 16283|1|2|12
    TC        :    gas || at 40 bar || 16283|1|2|13
    TC        :    gas || at 42 bar || 16283|1|2|14
    TC        :    gas || at 44 bar || 16283|1|2|15
    TC        :    gas || at 46 bar || 16283|1|2|16
    TC        :    gas || at 48 bar || 16283|1|2|17
    TC        :    gas || at 50 bar || 16283|1|2|18
    TC        :    gas || at 52 bar || 16283|1|2|19
    TC        :    gas || at 54 bar || 16283|1|2|20
    TC        :    gas || at 56 bar || 16283|1|2|21
    TC        :    gas || at 58 bar || 16283|1|2|22
    TC        :    gas || at 60 bar || 16283|1|2|23
    TC        :    gas || at 62 bar || 16283|1|2|24
    TC        :    gas || at 64 bar || 16283|1|2|25
    TC        :    gas || at 66 bar || 16283|1|2|26
    TC        :    gas || at 68 bar || 16283|1|2|27
    TC        :    gas || at 69.6 bar || 16283|1|2|28

return to listing

CF8C

    RHO   (N*):    solid || 9644|2|0|-1
    SIGMA (N*):    solid || 9644|10|0|-1

return to listing

CF16F

    RHO   (N*):    solid || 9647|2|0|-1
    SH    (N*):    solid || 9647|9|0|-1
    SIGMA (N*):    solid || 9647|10|0|-1
    TD    (N*):    solid || 9647|25|0|-1

return to listing

CF12M

    RHO   (N*):    solid || 9646|2|0|-1
    SIGMA (N*):    solid || 9646|10|0|-1

return to listing

CF3M

    RHO   (N*):    solid || 9642|2|0|-1
    SH    (N*):    solid || 9642|9|0|-1
    SIGMA (N*):    solid || 9642|10|0|-1
    TD    (N*):    solid || 9642|25|0|-1

return to listing

CF8M

    RHO   (N*):    solid || 9645|2|0|-1
    SIGMA (N*):    solid || 9645|10|0|-1

return to listing

CH₄ (methane)

    TC     (N):    solid || 2102|1|0|-1
    SH     (N):    solid || 2102|9|0|-1
    HC     (N):    solid || 2102|17|0|-1
    TD     (N):    liquid || 2102|25|1|-1

return to listing

CH20

    RHO   (N*):    solid || 9650|2|0|-1
    SH    (N*):    solid || 9650|9|0|-1
    SIGMA (N*):    solid || 9650|10|0|-1
    TD    (N*):    solid || 9650|25|0|-1

return to listing

CHEMGLAZE Z306 black coating (New)

    HE        :    55 microns thick || 16266|20|0|-1

return to listing

Chrome Core 18-FM Solenoid Quality Stainless

    UTS   (N*):    annealed || 3109|5|0|-1
    UTS   (N*):    stress relieved || 3109|5|1|-1
    YS    (N*):    annealed || 3109|13|0|-1
    YS    (N*):    stress relieved || 3109|13|1|-1
    %El   (N*):    annealed || 3109|29|0|-1
    %El   (N*):    stress relieved || 3109|29|1|-1

return to listing

Chrome core 12-FM

    UTS   (N*):    annealed for optimum magnetic properties || 1657|5|0|-1
    YS    (N*):    annealed for optimum magnetic properties || 1657|13|0|-1
    %El   (N*):    annealed for optimum magnetic properties || 1657|29|0|-1

return to listing

Chrome core 8-FM

    UTS   (N*):    annealed for optimum magnetic properties || 1655|5|0|-1
    SH    (N*):    solid || 1655|9|0|-1
    YS    (N*):    annealed for optimum magnetic properties || 1655|13|0|-1
    %El   (N*):    annealed for optimum magnetic properties || 1655|29|0|-1

return to listing

Chrome core 8

    RHO   (N*):    solid || 1654|2|0|-1
    E     (N*):    solid || 1654|3|0|-1
    UTS   (N*):    annealed for optimum magnetic properties || 1654|5|0|-1
    SH    (N*):    solid || 1654|9|0|-1
    SIGMA (N*):    solid || 1654|10|0|-1
    YS    (N*):    annealed for optimum magnetic properties || 1654|13|0|-1
    %El   (N*):    annealed for optimum magnetic properties || 1654|29|0|-1

return to listing

Chrome core 12

    RHO   (N*):    solid || 1656|2|0|-1
    E     (N*):    solid || 1656|3|0|-1
    UTS   (N*):    annealed for optimum magnetic properties || 1656|5|0|-1
    SH    (N*):    solid || 1656|9|0|-1
    SIGMA (N*):    solid || 1656|10|0|-1
    YS    (N*):    annealed for optimum magnetic properties || 1656|13|0|-1
    %El   (N*):    annealed for optimum magnetic properties || 1656|29|0|-1

return to listing

Chromel R (New)

    E     (*):    0.0127 mm (0.0005 inch) wire || as-received condition || 16267|3|0|0
    SSC       :    0.0127 mm (0.0005 inch) wire, as-received condition || tested at 20 °C (68 °F), 8.33 x 10^-⁴/s || 16267|4|0|0
    UTS   (*):    0.0127 mm (0.0005 inch) wire || as-received condition || 16267|5|0|0
    YS    (*):    0.0127 mm (0.0005 inch) wire || as-received condition || 16267|13|0|0
    %El   (*):    0.0127 mm (0.0005 inch) wire || as-received condition || 16267|29|0|0

return to listing

CK20

    RHO   (N*):    solid || 9651|2|0|-1
    SIGMA (N*):    solid || 9651|10|0|-1

return to listing

CN7M

    TC    (N*):    solid || 9652|1|0|-1
    RHO   (N*):    solid || 9652|2|0|-1
    SH    (N*):    solid || 9652|9|0|-1
    SIGMA (N*):    solid || 9652|10|0|-1
    TD    (N*):    solid || 9652|25|0|-1

return to listing

CO

    Vis    (N):    liquid || 2657|26|1|-1

return to listing

Coconut oil (New)

    Vis       :    liquid || 16182|26|1|-1

return to listing

Consumet electrical iron

    RHO   (N*):    solid || 1634|2|0|-1
    UTS   (N*):    bar || annealed || 1634|5|0|0
    SIGMA (N*):    solid || 1634|10|0|-1
    YS    (N*):    bar || annealed || 1634|13|0|0
    %El   (N*):    bar || annealed || 1634|29|0|0

return to listing

Corn oil

    Vis    (N):    liquid || 3410|26|1|-1

return to listing

Crambe oil (New)

    Vis       :    liquid || 16183|26|1|-1

return to listing

CsBr

    RIW    (N):    measured in unknown ambient || tested at 27 °C (81 °F) || 2439|45|0|0

return to listing

CsI

    RIW    (N):    measured in unknown ambient || tested at 24 °C (75 °F) || 2461|45|0|0

return to listing

Cu - 16 Ag (wt %)

    DLL    (N):    liquid || 9088|0|1|-1
    MTE    (N):    liquid || 9088|8|1|-1
    D      (N):    liquid || 9088|24|1|-1

return to listing

Cu - 24 Ag (wt %)

    ST     (N):    liquid || 853|38|1|-1

return to listing

Cu - 7 Ag (wt %)

    ST     (N):    liquid || 854|38|1|-1

return to listing

Cu - 40 Ag (wt %) (New)

    DLL       :    liquid || 16256|0|1|-1
    MTE       :    liquid || 16256|8|1|-1
    D         :    liquid || 16256|24|1|-1
    ST        :    liquid || 16256|38|1|-1

return to listing

Cu - 2 Ag (wt %) (New)

    DLL       :    liquid || 16249|0|1|-1
    MTE       :    liquid || 16249|8|1|-1
    D         :    liquid || 16249|24|1|-1
    ST        :    liquid || 16249|38|1|-1

return to listing

Cu - 8 Ag (wt %) (New)

    DLL       :    liquid || 16252|0|1|-1
    MTE       :    liquid || 16252|8|1|-1
    D         :    liquid || 16252|24|1|-1
    ST        :    liquid || 16252|38|1|-1

return to listing

Cu - 10 Ag (wt %) (New)

    DLL       :    liquid || 16253|0|1|-1
    MTE       :    liquid || 16253|8|1|-1
    D         :    liquid || 16253|24|1|-1
    ST        :    liquid || 16253|38|1|-1

return to listing

Cu - 4 Ag (wt %) (New)

    DLL       :    liquid || 16250|0|1|-1
    MTE       :    liquid || 16250|8|1|-1
    D         :    liquid || 16250|24|1|-1
    ST        :    liquid || 16250|38|1|-1

return to listing

Cu - 20 Ag (wt %) (New)

    DLL       :    liquid || 16254|0|1|-1
    MTE       :    liquid || 16254|8|1|-1
    D         :    liquid || 16254|24|1|-1
    ST        :    liquid || 16254|38|1|-1

return to listing

Cu - 6 Ag (wt %) (New)

    DLL       :    liquid || 16251|0|1|-1
    MTE       :    liquid || 16251|8|1|-1
    D         :    liquid || 16251|24|1|-1
    ST        :    liquid || 16251|38|1|-1

return to listing

Cu - 30 Ag (wt %) (New)

    DLL       :    liquid || 16255|0|1|-1
    MTE       :    liquid || 16255|8|1|-1
    D         :    liquid || 16255|24|1|-1
    ST        :    liquid || 16255|38|1|-1

return to listing

98.4 Cu - 1.6 Bi (at %) (New)

    DLL       :    liquid || 16243|0|1|-1
    MTE       :    liquid || 16243|8|1|-1
    D         :    liquid || 16243|24|1|-1
    ST        :    liquid || 16243|38|1|-1

return to listing

98.7 Cu - 1.3 Bi (at %) (New)

    DLL       :    liquid || 16242|0|1|-1
    MTE       :    liquid || 16242|8|1|-1
    D         :    liquid || 16242|24|1|-1
    ST        :    liquid || 16242|38|1|-1

return to listing

99 Cu - 1 Bi (at %) (New)

    DLL       :    liquid || 16241|0|1|-1
    MTE       :    liquid || 16241|8|1|-1
    D         :    liquid || 16241|24|1|-1
    ST        :    liquid || 16241|38|1|-1

return to listing

99.4 Cu - 0.6 Bi (at %) (New)

    DLL       :    liquid || 16240|0|1|-1
    MTE       :    liquid || 16240|8|1|-1
    D         :    liquid || 16240|24|1|-1
    ST        :    liquid || 16240|38|1|-1

return to listing

99.7 Cu - 0.3 Bi (at %) (New)

    DLL       :    liquid || 16239|0|1|-1
    MTE       :    liquid || 16239|8|1|-1
    D         :    liquid || 16239|24|1|-1
    ST        :    liquid || 16239|38|1|-1

return to listing

76.7 Cu - 23.3 Bi (at %) (New)

    DLL       :    liquid || 16248|0|1|-1
    MTE       :    liquid || 16248|8|1|-1
    D         :    liquid || 16248|24|1|-1
    ST        :    liquid || 16248|38|1|-1

return to listing

83.1 Cu - 16.9 Bi (at %) (New)

    DLL       :    liquid || 16247|0|1|-1
    MTE       :    liquid || 16247|8|1|-1
    D         :    liquid || 16247|24|1|-1
    ST        :    liquid || 16247|38|1|-1

return to listing

88.5 Cu - 11.5 Bi (at %) (New)

    DLL       :    liquid || 16246|0|1|-1
    MTE       :    liquid || 16246|8|1|-1
    D         :    liquid || 16246|24|1|-1
    ST        :    liquid || 16246|38|1|-1

return to listing

92.9 Cu - 7.1 Bi (at %) (New)

    DLL       :    liquid || 16245|0|1|-1
    MTE       :    liquid || 16245|8|1|-1
    D         :    liquid || 16245|24|1|-1
    ST        :    liquid || 16245|38|1|-1

return to listing

96.7 Cu - 3.3 Bi (at %) (New)

    DLL       :    liquid || 16244|0|1|-1
    MTE       :    liquid || 16244|8|1|-1
    D         :    liquid || 16244|24|1|-1
    ST        :    liquid || 16244|38|1|-1

return to listing

90 Cu - 8 Pb - 2 Fe (at %) (New)

    DLL       :    liquid || 16218|0|1|-1
    MTE       :    liquid || 16218|8|1|-1
    D         :    liquid || 16218|24|1|-1

return to listing

90 Cu - 6 Pb - 4 Fe (at %) (New)

    DLL       :    liquid || 16219|0|1|-1
    MTE       :    liquid || 16219|8|1|-1
    D         :    liquid || 16219|24|1|-1

return to listing

90 Cu - 4 Pb - 6 Fe (at %) (New)

    DLL       :    liquid || 16220|0|1|-1
    MTE       :    liquid || 16220|8|1|-1
    D         :    liquid || 16220|24|1|-1

return to listing

90 Cu - 2 Pb - 8 Fe (at %) (New)

    DLL       :    liquid || 16221|0|1|-1
    MTE       :    liquid || 16221|8|1|-1
    D         :    liquid || 16221|24|1|-1

return to listing

90 Cu - 0 Pb - 10 Fe (at %) (New)

    DLL       :    liquid || 16222|0|1|-1
    MTE       :    liquid || 16222|8|1|-1
    D         :    liquid || 16222|24|1|-1

return to listing

80 Cu - 20 Pb - 0 Fe (at %) (New)

    DLL       :    liquid || 16223|0|1|-1
    MTE       :    liquid || 16223|8|1|-1
    D         :    liquid || 16223|24|1|-1

return to listing

80 Cu - 18 Pb - 2 Fe (at %) (New)

    DLL       :    liquid || 16224|0|1|-1
    MTE       :    liquid || 16224|8|1|-1
    D         :    liquid || 16224|24|1|-1

return to listing

80 Cu - 16 Pb - 4 Fe (at %) (New)

    DLL       :    liquid || 16225|0|1|-1
    MTE       :    liquid || 16225|8|1|-1
    D         :    liquid || 16225|24|1|-1

return to listing

80 Cu - 14 Pb - 6 Fe (at %) (New)

    DLL       :    liquid || 16226|0|1|-1
    MTE       :    liquid || 16226|8|1|-1
    D         :    liquid || 16226|24|1|-1

return to listing

80 Cu - 12 Pb - 8 Fe (at %) (New)

    DLL       :    liquid || 16227|0|1|-1
    MTE       :    liquid || 16227|8|1|-1
    D         :    liquid || 16227|24|1|-1

return to listing

80 Cu - 10 Pb - 10 Fe (at %) (New)

    DLL       :    liquid || 16228|0|1|-1
    MTE       :    liquid || 16228|8|1|-1
    D         :    liquid || 16228|24|1|-1

return to listing

70 Cu - 30 Pb - 0 Fe (at %) (New)

    DLL       :    liquid || 16229|0|1|-1
    MTE       :    liquid || 16229|8|1|-1
    D         :    liquid || 16229|24|1|-1

return to listing

70 Cu - 27 Pb - 3 Fe (at %) (New)

    DLL       :    liquid || 16230|0|1|-1
    MTE       :    liquid || 16230|8|1|-1
    D         :    liquid || 16230|24|1|-1

return to listing

70 Cu - 24 Pb - 6 Fe (at %) (New)

    DLL       :    liquid || 16231|0|1|-1
    MTE       :    liquid || 16231|8|1|-1
    D         :    liquid || 16231|24|1|-1

return to listing

70 Cu - 21 Pb - 9 Fe (at %) (New)

    DLL       :    liquid || 16232|0|1|-1
    MTE       :    liquid || 16232|8|1|-1
    D         :    liquid || 16232|24|1|-1

return to listing

90 Cu - 10 Pb - 0 Fe (at %) (New)

    DLL       :    liquid || 16217|0|1|-1
    MTE       :    liquid || 16217|8|1|-1
    D         :    liquid || 16217|24|1|-1

return to listing

Cu₁₂_-_mCo_mSb₄S₁₃_-_nSe_n (New)

    RHO       :    m = 0.5, n = 0 || Cu₁₁_.₅Co₀_.₅Sb₄S₁₃ || 16290|2|0|0
    RHO       :    m = 0.5, n = 0.5 || Cu₁₁_.₅Co₀_.₅Sb₄S₁₂_.₅Se₀_.₅ || 16290|2|1|0
    RHO       :    m = 0.5, n = 1 || Cu₁₁_.₅Co₀_.₅Sb₄S₁₂Se || 16290|2|2|0
    RHO       :    m = 1, n = 1 || Cu₁₁CoSb₄S₁₂Se || 16290|2|3|0
    RHO       :    m = 1.5, n = 1 || Cu₁₀_.₅Co₁_.₅Sb₄S₁₂Se || 16290|2|4|0
    SIGMA    :    m = 0.5, n = 0 || Cu₁₁_.₅Co₀_.₅Sb₄S₁₃ || 16290|10|0|0
    SIGMA    :    m = 0.5, n = 0.5 || Cu₁₁_.₅Co₀_.₅Sb₄S₁₂_.₅Se₀_.₅ || 16290|10|1|0
    SIGMA    :    m = 0.5, n = 1 || Cu₁₁_.₅Co₀_.₅Sb₄S₁₂Se || 16290|10|2|0
    SIGMA    :    m = 1, n = 1 || Cu₁₁CoSb₄S₁₂Se || 16290|10|3|0
    SIGMA    :    m = 1.5, n = 1 || Cu₁₀_.₅Co₁_.₅Sb₄S₁₂Se || 16290|10|4|0
    D     (*):    solid || 16290|24|0|-1
    S         :    m = 0.5, n = 0 || Cu₁₁_.₅Co₀_.₅Sb₄S₁₃ || 16290|48|0|0
    S         :    m = 0.5, n = 0.5 || Cu₁₁_.₅Co₀_.₅Sb₄S₁₂_.₅Se₀_.₅ || 16290|48|1|0
    S         :    m = 0.5, n = 1 || Cu₁₁_.₅Co₀_.₅Sb₄S₁₂Se || 16290|48|2|0
    S         :    m = 1, n = 1 || Cu₁₁CoSb₄S₁₂Se || 16290|48|3|0
    S         :    m = 1.5, n = 1 || Cu₁₀_.₅Co₁_.₅Sb₄S₁₂Se || 16290|48|4|0

return to listing

Cu₁_-_xFeS₂ (Pd doped) (New)

    TC        :    CuFeS₂ || 16289|1|0|-1
    TC        :    Pd doped || x = 0.01, Cu₀_.₉₉Pd₀_.₀₁FeS₂ || 16289|1|1|0
    TC        :    Pd doped || x = 0.02, Cu₀_.₉₈Pd₀_.₀₂FeS₂ || 16289|1|1|1
    TC        :    Pd doped || x = 0.03, Cu₀_.₉₇Pd₀_.₀₃FeS₂ || 16289|1|1|2
    TC        :    Pd doped || x = 0.05, Cu₀_.₉₅Pd₀_.₀₅FeS₂ || 16289|1|1|3
    TC        :    Pd doped || x = 0.07, Cu₀_.₉₃Pd₀_.₀₇FeS₂ || 16289|1|1|4
    TC        :    Pd doped || x = 0.1, Cu₀_.₉Pd₀_.₁FeS₂ || 16289|1|1|5
    RHO       :    CuFeS₂ || 16289|2|0|-1
    RHO       :    Pd doped || x = 0.01, Cu₀_.₉₉Pd₀_.₀₁FeS₂ || 16289|2|1|0
    RHO       :    Pd doped || x = 0.02, Cu₀_.₉₈Pd₀_.₀₂FeS₂ || 16289|2|1|1
    RHO       :    Pd doped || x = 0.03, Cu₀_.₉₇Pd₀_.₀₃FeS₂ || 16289|2|1|2
    RHO       :    Pd doped || x = 0.05, Cu₀_.₉₅Pd₀_.₀₅FeS₂ || 16289|2|1|3
    RHO       :    Pd doped || x = 0.07, Cu₀_.₉₃Pd₀_.₀₇FeS₂ || 16289|2|1|4
    RHO       :    Pd doped || x = 0.1, Cu₀_.₉Pd₀_.₁FeS₂ || 16289|2|1|5
    SIGMA    :    CuFeS₂ || 16289|10|0|-1
    SIGMA    :    Pd doped || x = 0.01, Cu₀_.₉₉Pd₀_.₀₁FeS₂ || 16289|10|1|0
    SIGMA    :    Pd doped || x = 0.02, Cu₀_.₉₈Pd₀_.₀₂FeS₂ || 16289|10|1|1
    SIGMA    :    Pd doped || x = 0.03, Cu₀_.₉₇Pd₀_.₀₃FeS₂ || 16289|10|1|2
    SIGMA    :    Pd doped || x = 0.05, Cu₀_.₉₅Pd₀_.₀₅FeS₂ || 16289|10|1|3
    SIGMA    :    Pd doped || x = 0.07, Cu₀_.₉₃Pd₀_.₀₇FeS₂ || 16289|10|1|4
    SIGMA    :    Pd doped || x = 0.1, Cu₀_.₉Pd₀_.₁FeS₂ || 16289|10|1|5
    S         :    CuFeS₂ || 16289|48|0|-1
    S         :    Pd doped || x = 0.01, Cu₀_.₉₉Pd₀_.₀₁FeS₂ || 16289|48|1|0
    S         :    Pd doped || x = 0.02, Cu₀_.₉₈Pd₀_.₀₂FeS₂ || 16289|48|1|1
    S         :    Pd doped || x = 0.03, Cu₀_.₉₇Pd₀_.₀₃FeS₂ || 16289|48|1|2
    S         :    Pd doped || x = 0.05, Cu₀_.₉₅Pd₀_.₀₅FeS₂ || 16289|48|1|3
    S         :    Pd doped || x = 0.07, Cu₀_.₉₃Pd₀_.₀₇FeS₂ || 16289|48|1|4
    S         :    Pd doped || x = 0.1, Cu₀_.₉Pd₀_.₁FeS₂ || 16289|48|1|5

return to listing

CuFeS₂

    TC     (N):    CuFeS₂ || Navratil et. al., hot-pressed || 15780|1|0|2
    RHO    (N):    CuFeS₂ || Navratil et. al., hot-pressed || 15780|2|0|2
    SIGMA (N):    CuFeS₂ || Navratil et. al., hot-pressed || 15780|10|0|2
    S      (N):    CuFeS₂ || Navratil et. al., hot-pressed || 15780|48|0|2

return to listing

Cu₆Fe₂SnS₈/Cu₂FeSnS₄ composite (New)

    TC        :    solid || 16291|1|0|-1
    RHO       :    solid || 16291|2|0|-1
    SH    (*):    solid || 16291|9|0|-1
    SIGMA    :    solid || 16291|10|0|-1
    D     (*):    solid || 16291|24|0|-1
    TD        :    solid || 16291|25|0|-1
    S         :    solid || 16291|48|0|-1

return to listing

Cu₁₂Sb₄S₁₃ (New)

    TC        :    hot-pressed || 400 °C (752 °F) || 16287|1|0|0
    TC        :    hot-pressed || 450 °C (842 °F) || 16287|1|0|1
    TC        :    hot-pressed || 500 °C (932 °F) || 16287|1|0|2
    RHO       :    hot-pressed || 400 °C (752 °F) || 16287|2|0|0
    RHO       :    hot-pressed || 450 °C (842 °F) || 16287|2|0|1
    RHO       :    hot-pressed || 500 °C (932 °F) || 16287|2|0|2
    SIGMA    :    hot-pressed || 400 °C (752 °F) || 16287|10|0|0
    SIGMA    :    hot-pressed || 450 °C (842 °F) || 16287|10|0|1
    SIGMA    :    hot-pressed || 500 °C (932 °F) || 16287|10|0|2
    D     (*):    solid || 16287|24|0|-1
    S         :    hot-pressed || 400 °C (752 °F) || 16287|48|0|0
    S         :    hot-pressed || 450 °C (842 °F) || 16287|48|0|1
    S         :    hot-pressed || 500 °C (932 °F) || 16287|48|0|2

return to listing

Cu₂Se (Cl doped)

    TC     (N):    undoped || monoclinic structure, space group C2/c, Kim et. al. || 15411|1|0|2
    TC     (N):    Cl doped || 0.02, Cu₂Se₀_.₉₈Cl₀_.₀₂ || 15411|1|1|0
    TC     (N):    Cl doped || 0.04, Cu₂Se₀_.₉₆Cl₀_.₀₄ || 15411|1|1|1
    TC     (N):    Cl doped || 0.08, Cu₂Se₀_.₉₂Cl₀_.₀₈ || 15411|1|1|2
    RHO    (N):    undoped || monoclinic structure, space group C2/c, Kim et. al. || 15411|2|0|2
    RHO    (N):    Cl doped || 0.02, Cu₂Se₀_.₉₈Cl₀_.₀₂ || 15411|2|1|0
    RHO    (N):    Cl doped || 0.04, Cu₂Se₀_.₉₆Cl₀_.₀₄ || 15411|2|1|1
    RHO    (N):    Cl doped || 0.08, Cu₂Se₀_.₉₂Cl₀_.₀₈ || 15411|2|1|2
    SIGMA (N):    undoped || monoclinic structure, space group C2/c, Kim et. al. || 15411|10|0|2
    SIGMA (N):    Cl doped || 0.02, Cu₂Se₀_.₉₈Cl₀_.₀₂ || 15411|10|1|0
    SIGMA (N):    Cl doped || 0.04, Cu₂Se₀_.₉₆Cl₀_.₀₄ || 15411|10|1|1
    SIGMA (N):    Cl doped || 0.08, Cu₂Se₀_.₉₂Cl₀_.₀₈ || 15411|10|1|2
    TD     (N):    undoped || monoclinic structure, space group C2/c, Kim et. al. || 15411|25|0|2
    TD     (N):    Cl doped || 0.02, Cu₂Se₀_.₉₈Cl₀_.₀₂ || 15411|25|1|0
    TD     (N):    Cl doped || 0.04, Cu₂Se₀_.₉₆Cl₀_.₀₄ || 15411|25|1|1
    TD     (N):    Cl doped || 0.08, Cu₂Se₀_.₉₂Cl₀_.₀₈ || 15411|25|1|2
    S      (N):    undoped || monoclinic structure, space group C2/c || 15411|48|0|0
    S      (N):    Cl doped || 0.02, Cu₂Se₀_.₉₈Cl₀_.₀₂ || 15411|48|1|0
    S      (N):    Cl doped || 0.04, Cu₂Se₀_.₉₆Cl₀_.₀₄ || 15411|48|1|1
    S      (N):    Cl doped || 0.08, Cu₂Se₀_.₉₂Cl₀_.₀₈ || 15411|48|1|2

return to listing

Diesel fuel

    Vis    (N):    liquid || 2134|26|1|-1

return to listing

DP 690

    RHO    (N):    solid || 10327|2|0|-1
    SIGMA (N):    solid || 10327|10|0|-1

return to listing

DP 600

    RHO    (N):    solid || 1145|2|0|-1
    RPB    (N):    1.6 mm (0.063 inch) thick sheet, tested at 20 °C (68 °F) || 1145|7|0|-1
    RPB    (N):    1.6 mm (0.063 inch) thick sheet, tested at 250 °C (482 °F) || 1145|7|1|-1
    RPB    (N):    1.6 mm (0.063 inch) thick sheet, tested at 500 °C (932 °F) || 1145|7|2|-1
    RPB    (N):    1.6 mm (0.063 inch) thick sheet, tested at 750 °C (1382 °F) || 1145|7|3|-1
    SIGMA (N):    solid || 1145|10|0|-1
    AP     (N):    1.6 mm (0.063 inch) thick sheet, tested at 20 °C (68 °F) || 1145|15|0|-1
    AP     (N):    1.6 mm (0.063 inch) thick sheet, tested at 250 °C (482 °F) || 1145|15|1|-1
    AP     (N):    1.6 mm (0.063 inch) thick sheet, tested at 500 °C (932 °F) || 1145|15|2|-1
    AP     (N):    1.6 mm (0.063 inch) thick sheet, tested at 750 °C (1382 °F) || 1145|15|3|-1
    BH     (N):    1.6 mm (0.063 inch) thick sheet, tested at 20 °C (68 °F) || 1145|23|0|-1
    BH     (N):    1.6 mm (0.063 inch) thick sheet, tested at 250 °C (482 °F) || 1145|23|1|-1
    BH     (N):    1.6 mm (0.063 inch) thick sheet, tested at 500 °C (932 °F) || 1145|23|2|-1
    BH     (N):    1.6 mm (0.063 inch) thick sheet, tested at 750 °C (1382 °F) || 1145|23|3|-1
    HB     (N):    1.6 mm (0.063 inch) thick sheet, tested at 20 °C (68 °F) || 1145|31|0|-1
    HB     (N):    1.6 mm (0.063 inch) thick sheet, tested at 250 °C (482 °F) || 1145|31|1|-1
    HB     (N):    1.6 mm (0.063 inch) thick sheet, tested at 500 °C (932 °F) || 1145|31|2|-1
    HB     (N):    1.6 mm (0.063 inch) thick sheet, tested at 750 °C (1382 °F) || 1145|31|3|-1
    CL     (N):    1.6 mm (0.063 inch) thick sheet || tested at 20 °C (68 °F), 280 kHz || 1145|43|0|0

return to listing

Ductile Ni-Resist D-5S

    FEN    (N):    condition not specified || tested at 300 °C (572 °F), R = -1, axial, total strain amplitude || 10308|14|1|0
    FEN    (N):    condition not specified || tested at 500 °C (932 °F), R = -1, axial, total strain amplitude || 10308|14|1|1
    FEN    (N):    condition not specified || tested at 600 °C (1112 °F), R = -1, axial, total strain amplitude || 10308|14|1|2
    FEN    (N):    condition not specified || tested at 700 °C (1292 °F), R = -1, axial, total strain amplitude || 10308|14|1|3
    FEN    (N):    condition not specified || tested at 800 °C (1472 °F), R = -1, axial, total strain amplitude || 10308|14|1|4

return to listing

Dy₃TaO₇

    SH     (R):    solid || 530|9|0|-1

return to listing

Er₃TaO₇

    SH     (R):    solid || 534|9|0|-1

return to listing

Erucic acid (New)

    Vis       :    liquid || 16193|26|1|-1

return to listing

EuPd₂As₂ (New)

    RHO       :    solid || 16210|2|0|-1
    SH        :    solid || 16210|9|0|-1
    SIGMA    :    solid || 16210|10|0|-1
    HC        :    solid || 16210|17|0|-1

return to listing

Eu₃TaO₇

    SH     (R):    solid || 536|9|0|-1

return to listing

Fe - 3.9 Si (wt %)

    DLL    (R):    solid || 1128|0|0|-1
    TC     (R):    solid || 1128|1|0|-1
    MTE    (R):    solid || 1128|8|0|-1
    CTE    (R):    solid || 1128|16|0|-1
    D      (R):    solid || 1128|24|0|-1
    TD     (R):    solid || 1128|25|0|-1

return to listing

Fe - 4.4 Si (wt %)

    DLL    (R):    solid || 9011|0|0|-1
    MTE    (R):    solid || 9011|8|0|-1
    CTE    (R):    solid || 9011|16|0|-1
    D      (R):    solid || 9011|24|0|-1
    TD     (R):    solid || 9011|25|0|-1

return to listing

Fe - 8 Si (wt %)

    DLL    (R):    solid || 9013|0|0|-1
    MTE    (R):    solid || 9013|8|0|-1
    CTE    (R):    solid || 9013|16|0|-1
    D      (R):    solid || 9013|24|0|-1

return to listing

Fe - 10 Si (wt %)

    DLL    (R):    solid || 9012|0|0|-1
    MTE    (R):    solid || 9012|8|0|-1
    CTE    (R):    solid || 9012|16|0|-1
    D      (R):    solid || 9012|24|0|-1

return to listing

Fe - 12 Si (wt %)

    DLL    (R):    solid || 9015|0|0|-1
    MTE    (R):    solid || 9015|8|0|-1
    D      (R):    solid || 9015|24|0|-1

return to listing

Fe - 1 Si (wt %)

    DLL    (R):    solid || 1125|0|0|-1
    TC     (R):    solid || 1125|1|0|-1
    MTE    (R):    solid || 1125|8|0|-1
    CTE    (R):    solid || 1125|16|0|-1
    D      (R):    solid || 1125|24|0|-1
    TD     (R):    solid || 1125|25|0|-1

return to listing

Fe - 1.8 Si (wt %)

    DLL    (R):    solid || 1126|0|0|-1
    TC     (R):    solid || 1126|1|0|-1
    MTE    (R):    solid || 1126|8|0|-1
    CTE    (R):    solid || 1126|16|0|-1
    D      (R):    solid || 1126|24|0|-1
    TD     (R):    solid || 1126|25|0|-1

return to listing

Fe - 2.8 Si (wt %)

    DLL    (R):    solid || 1127|0|0|-1
    TC     (R):    solid || 1127|1|0|-1
    MTE    (R):    solid || 1127|8|0|-1
    CTE    (R):    solid || 1127|16|0|-1
    D      (R):    solid || 1127|24|0|-1
    TD     (R):    solid || 1127|25|0|-1

return to listing

Fluorine

    Vis    (N):    liquid || 840|26|1|-1

return to listing

GaAs

    RIW    (N):    measured in unknown ambient || tested at 23 °C (73 °F) || 2475|45|0|0

return to listing

GaSb

    RIW    (N):    measured in unknown ambient || tested at 23 °C (73 °F) || 2498|45|0|0

return to listing

Gd₃TaO₇

    SH     (R):    solid || 548|9|0|-1

return to listing

GdVO₄

    TC     (N):    solid || polycrystal || 2538|1|0|0
    TC     (N):    solid || a-axis || 2538|1|0|1
    TC     (N):    solid || c-axis || 2538|1|0|2
    SH     (N):    solid || 2538|9|0|-1
    HC     (N):    solid || 2538|17|0|-1
    TD     (N):    solid || polycrystal || 2538|25|0|0
    TD     (N):    solid || a-axis || 2538|25|0|1
    TD     (N):    solid || c-axis || 2538|25|0|2

return to listing

Ge₀_.₉₅_-_xMg₀_.₀₅Sb_xTe (New)

    DLL       :    x = 0.1 || Ge₀_.₈₅Mg₀_.₀₅Sb₀_.₁Te || 16196|0|3|0
    TC        :    x = 0 || Ge₀_.₉₅Mg₀_.₀₅Te || 16196|1|0|0
    TC        :    x = 0.05 || Ge₀_.₉Mg₀_.₀₅Sb₀_.₀₅Te || 16196|1|1|0
    TC        :    x = 0.075 || Ge₀_.₈₇₅Mg₀_.₀₅Sb₀_.₀₇₅Te || 16196|1|2|0
    TC        :    x = 0.1 || Ge₀_.₈₅Mg₀_.₀₅Sb₀_.₁Te || 16196|1|3|0
    RHO       :    x = 0 || Ge₀_.₉₅Mg₀_.₀₅Te || 16196|2|0|0
    RHO       :    x = 0.05 || Ge₀_.₉Mg₀_.₀₅Sb₀_.₀₅Te || 16196|2|1|0
    RHO       :    x = 0.075 || Ge₀_.₈₇₅Mg₀_.₀₅Sb₀_.₀₇₅Te || 16196|2|2|0
    RHO       :    x = 0.1 || Ge₀_.₈₅Mg₀_.₀₅Sb₀_.₁Te || 16196|2|3|0
    MTE   (*):    x = 0 || Ge₀_.₉₅Mg₀_.₀₅Te || 16196|8|0|0
    MTE   (*):    x = 0.05 || Ge₀_.₉Mg₀_.₀₅Sb₀_.₀₅Te || 16196|8|1|0
    MTE   (*):    x = 0.075 || Ge₀_.₈₇₅Mg₀_.₀₅Sb₀_.₀₇₅Te || 16196|8|2|0
    MTE       :    x = 0.1 || Ge₀_.₈₅Mg₀_.₀₅Sb₀_.₁Te || 16196|8|3|0
    SIGMA    :    x = 0 || Ge₀_.₉₅Mg₀_.₀₅Te || 16196|10|0|0
    SIGMA    :    x = 0.05 || Ge₀_.₉Mg₀_.₀₅Sb₀_.₀₅Te || 16196|10|1|0
    SIGMA    :    x = 0.075 || Ge₀_.₈₇₅Mg₀_.₀₅Sb₀_.₀₇₅Te || 16196|10|2|0
    SIGMA    :    x = 0.1 || Ge₀_.₈₅Mg₀_.₀₅Sb₀_.₁Te || 16196|10|3|0
    D     (*):    x = 0 || Ge₀_.₉₅Mg₀_.₀₅Te || 16196|24|0|0
    D     (*):    x = 0.05 || Ge₀_.₉Mg₀_.₀₅Sb₀_.₀₅Te || 16196|24|1|0
    D     (*):    x = 0.075 || Ge₀_.₈₇₅Mg₀_.₀₅Sb₀_.₀₇₅Te || 16196|24|2|0
    D         :    x = 0.1 || Ge₀_.₈₅Mg₀_.₀₅Sb₀_.₁Te || 16196|24|3|0
    S         :    x = 0 || Ge₀_.₉₅Mg₀_.₀₅Te || 16196|48|0|0
    S         :    x = 0.05 || Ge₀_.₉Mg₀_.₀₅Sb₀_.₀₅Te || 16196|48|1|0
    S         :    x = 0.075 || Ge₀_.₈₇₅Mg₀_.₀₅Sb₀_.₀₇₅Te || 16196|48|2|0
    S         :    x = 0.1 || Ge₀_.₈₅Mg₀_.₀₅Sb₀_.₁Te || 16196|48|3|0

return to listing

GeTe

    MTE   (N*):    solid || 15416|8|0|-1

return to listing

Grapeseed oil

    Vis    (N):    liquid || 3417|26|1|-1

return to listing

Graphite AXF-5Q

    TC     (R):    solid || 233|1|0|-1
    SH     (N):    solid || 233|9|0|-1
    TD     (N):    solid || 233|25|0|-1
    NE     (N):    solid || 233|28|0|-1

return to listing

Graphite AXM-5Q

    NE     (N):    solid || 234|28|0|-1

return to listing

Graphite ZXF-5Q

    TC     (N):    solid || 245|1|0|-1
    TD     (R):    solid || 245|25|0|-1

return to listing

Haynes R-41 (Rene 41)

    UTS    (N):    sheet || solution treated at 1079 °C (1975 °F) & aged || 1939|5|0|2
    YS     (N):    sheet || solution treated at 1079 °C (1975 °F) & aged || 1939|13|0|2
    SR     (R):    age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) || tested at 649 °C (1200 °F) || 1939|22|0|0
    SR     (R):    age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) || tested at 704 °C (1300 °F) || 1939|22|0|1
    SR     (R):    age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) || tested at 760 °C (1400 °F) || 1939|22|0|2
    SR     (R):    age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) || tested at 816 °C (1500 °F) || 1939|22|0|3
    SR     (R):    age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) || tested at 871 °C (1600 °F) || 1939|22|0|4
    SR     (R):    age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) || tested at 927 °C (1700 °F) || 1939|22|0|5
    SR     (R):    age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) || tested at 982 °C (1800 °F) || 1939|22|0|6
    SR     (R):    age hardened sheet (1121 °C (2050 °F)/899 °C (1650 °F)) || Master curve (LMP) || 1939|22|0|7
    SR     (N):    age hardened sheet (1066 °C (1950 °F)/760 °C (1400 °F)) || tested at 649 °C (1200 °F) || 1939|22|1|0
    SR     (N):    age hardened sheet (1066 °C (1950 °F)/760 °C (1400 °F)) || tested at 704 °C (1300 °F) || 1939|22|1|1
    SR     (N):    age hardened sheet (1066 °C (1950 °F)/760 °C (1400 °F)) || tested at 760 °C (1400 °F) || 1939|22|1|2
    SR     (N):    age hardened sheet (1066 °C (1950 °F)/760 °C (1400 °F)) || tested at 871 °C (1600 °F) || 1939|22|1|3
    SR     (N):    age hardened sheet (1066 °C (1950 °F)/760 °C (1400 °F)) || tested at 982 °C (1800 °F) || 1939|22|1|4
    SR     (N):    age hardened sheet (1066 °C (1950 °F)/760 °C (1400 °F)) || Master curve (LMP) || 1939|22|1|5
    CRS    (N):    0.5% strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) || tested at 760 °C (1400 °F) || 1939|30|0|0
    CRS    (N):    0.5% strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) || tested at 843 °C (1550 °F) || 1939|30|0|1
    CRS    (N):    0.5% strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) || tested at 927 °C (1700 °F) || 1939|30|0|2
    CRS    (N):    0.5% strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) || tested at 1010 °C (1850 °F) || 1939|30|0|3
    CRS    (N):    0.5% strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) || tested at 1093 °C (2000 °F) || 1939|30|0|4
    CRS    (N):    1% strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) || tested at 843 °C (1550 °F) || 1939|30|1|1
    CRS    (N):    1% strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) || tested at 927 °C (1700 °F) || 1939|30|1|2
    CRS    (N):    1% strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) || tested at 1010 °C (1850 °F) || 1939|30|1|3
    CRS    (N):    1% strain, age hardened sheet (1079 °C (1975 °F)/760 °C (1400 °F)) || tested at 1093 °C (2000 °F) || 1939|30|1|4
    IC     (N):    tested at 843 °C (1550 °F) || 150 h || 1939|39|0|2
    IC     (N):    tested at 843 °C (1550 °F) || 200 h || 1939|39|0|3
    IC     (N):    tested at 843 °C (1550 °F) || 250 h || 1939|39|0|4
    IC     (N):    tested at 843 °C (1550 °F) || 300 h || 1939|39|0|5
    IC     (N):    tested at 927 °C (1700 °F) || 100 h || 1939|39|1|1
    IC     (N):    tested at 927 °C (1700 °F) || 150 h || 1939|39|1|2
    IC     (N):    tested at 1010 °C (1850 °F) || 75 h || 1939|39|2|0
    IC     (N):    tested at 1010 °C (1850 °F) || 100 h || 1939|39|2|1
    IC     (N):    tested at 1010 °C (1850 °F) || 150 h || 1939|39|2|2
    IC     (N):    tested at 1010 °C (1850 °F) || 200 h || 1939|39|2|3
    IC     (N):    tested at 1093 °C (2000 °F) || 75 h || 1939|39|3|0

return to listing

H₃BO₃

    SH     (R):    solid || 15902|9|0|-1
    HC     (R):    solid || 15902|17|0|-1

return to listing

HCFC-22 (CHClF) (New)

    TC        :    gas || at 1 bar || 16284|1|2|0
    TC        :    gas || at 10 bar || 16284|1|2|1
    TC        :    gas || at 15 bar || 16284|1|2|2
    TC        :    gas || at 18 bar || 16284|1|2|3
    TC        :    gas || at 20 bar || 16284|1|2|4
    TC        :    gas || at 23 bar || 16284|1|2|5
    TC        :    gas || at 25 bar || 16284|1|2|6
    TC        :    gas || at 28 bar || 16284|1|2|7
    TC        :    gas || at 30 bar || 16284|1|2|8
    TC        :    gas || at 32 bar || 16284|1|2|9
    TC        :    gas || at 34 bar || 16284|1|2|10
    TC        :    gas || at 36 bar || 16284|1|2|11
    TC        :    gas || at 38 bar || 16284|1|2|12
    TC        :    gas || at 40 bar || 16284|1|2|13
    TC        :    gas || at 42 bar || 16284|1|2|14
    TC        :    gas || at 44 bar || 16284|1|2|15
    TC        :    gas || at 46 bar || 16284|1|2|16
    TC        :    gas || at 48 bar || 16284|1|2|17
    TC        :    gas || at 50 bar || 16284|1|2|18
    TC        :    gas || at 52 bar || 16284|1|2|19
    TC        :    gas || at 54 bar || 16284|1|2|20
    TC        :    gas || at 56 bar || 16284|1|2|21
    TC        :    gas || at 57.6 bar || 16284|1|2|22

return to listing

HCFC-123 (C₂HCl₂F₃)

    TC     (N):    liquid || 3419|1|1|-1
    TC     (N):    vapor || 3419|1|2|-1
    SH     (N):    saturated liquid || 3419|9|1|-1
    HC     (N):    saturated liquid || 3419|17|1|-1
    TD     (N):    liquid || 3419|25|1|-1
    Vis    (N):    liquid || 3419|26|1|-1
    Vis    (R):    gas || 3419|26|2|-1

return to listing

HCFC-142b (CH₃CClF₂) (New)

    TC        :    gas || 16278|1|2|-1
    Vis       :    gas || 16278|26|2|-1

return to listing

HF Alloy

    TC    (N*):    solid || 16195|1|0|-1
    E     (N*):    Effect of wall thickness || 1 mm (0.0394 inch), as-cast || 16195|3|0|0
    E     (N*):    Effect of wall thickness || 1.5 mm (0.0591 inch), after 8 weeks || 16195|3|0|1
    UTS   (N*):    Effect of wall thickness || 1 mm (0.0394 inch), as-cast || 16195|5|0|0
    UTS   (N*):    Effect of wall thickness || 1 mm (0.0394 inch), aged 10 days at 95 °C (203 °F) || 16195|5|0|1
    UTS   (N*):    Effect of wall thickness || 1.5 mm (0.0591 inch), after 8 weeks || 16195|5|0|2
    MTE   (N*):    solid || 16195|8|0|-1
    SH     (N):    solid || 16195|9|0|-1
    YS    (N*):    Effect of wall thickness || 1 mm (0.0394 inch), as-cast || 16195|13|0|0
    YS    (N*):    Effect of wall thickness || 1 mm (0.0394 inch), aged 10 days at 95 °C (203 °F) || 16195|13|0|1
    YS    (N*):    Effect of wall thickness || 1.5 mm (0.0591 inch), after 8 weeks || 16195|13|0|2
    D     (N*):    solid || 16195|24|0|-1
    TD    (N*):    solid || 16195|25|0|-1
    %El   (N*):    Effect of wall thickness || 1 mm (0.0394 inch), as-cast || 16195|29|0|0
    %El   (N*):    Effect of wall thickness || 1 mm (0.0394 inch), aged 10 days at 95 °C (203 °F) || 16195|29|0|1
    %El   (N*):    Effect of wall thickness || 1.5 mm (0.0591 inch), after 8 weeks || 16195|29|0|2

return to listing

HFC-23 (CHF₃)

    TC     (N):    gas || at 1 bar || 3418|1|2|0
    TC     (N):    gas || at 10 bar || 3418|1|2|1
    TC     (N):    gas || at 15 bar || 3418|1|2|2
    TC     (N):    gas || at 18 bar || 3418|1|2|3
    TC     (N):    gas || at 20 bar || 3418|1|2|4
    TC     (N):    gas || at 23 bar || 3418|1|2|5
    TC     (N):    gas || at 25 bar || 3418|1|2|6
    TC     (N):    gas || at 28 bar || 3418|1|2|7
    TC     (N):    gas || at 30 bar || 3418|1|2|8
    TC     (N):    gas || at 32 bar || 3418|1|2|9
    TC     (N):    gas || at 34 bar || 3418|1|2|10
    TC     (N):    gas || at 36 bar || 3418|1|2|11
    TC     (N):    gas || at 38 bar || 3418|1|2|12
    TC     (N):    gas || at 40 bar || 3418|1|2|13
    TC     (N):    gas || at 42 bar || 3418|1|2|14
    TC     (N):    gas || at 44 bar || 3418|1|2|15
    TC     (N):    gas || at 46 bar || 3418|1|2|16
    TC     (N):    gas || at 48 bar || 3418|1|2|17
    TC     (N):    gas || at 50 bar || 3418|1|2|18
    TC     (N):    gas || at 52 bar || 3418|1|2|19
    TC     (N):    gas || at 54 bar || 3418|1|2|20
    TC     (N):    gas || at 56 bar || 3418|1|2|21
    TC     (N):    gas || at 58 bar || 3418|1|2|22
    TC     (N):    gas || at 60 bar || 3418|1|2|23
    TC     (N):    gas || at 62 bar || 3418|1|2|24
    TC     (N):    gas || at 64 bar || 3418|1|2|25
    TC     (N):    gas || at 66 bar || 3418|1|2|26
    TC     (N):    gas || at 68 bar || 3418|1|2|27
    TC     (N):    gas || at 69.6 bar || 3418|1|2|28

return to listing

HFC-152a (C₂H₄F₂)

    TC     (N):    gas || 3421|1|2|-1
    VP     (N):    saturated liquid || 3421|18|1|-1

return to listing

HFC-134a (C₂HF₅)

    TC     (R):    liquid || 3008|1|1|-1
    TC     (N):    vapor || 3008|1|2|-1
    SH     (N):    saturated liquid || 3008|9|1|-1
    HC     (N):    saturated liquid || 3008|17|1|-1
    TD     (N):    liquid || 3008|25|1|-1
    Vis    (N):    liquid || 3008|26|1|-1
    Vis    (R):    gas || 3008|26|2|-1

return to listing

HfSi₂

    RHO    (N):    solid || 2601|2|0|-1
    SIGMA (N):    solid || 2601|10|0|-1

return to listing

High Permeability 49

    DLL    (N):    solid || 1635|0|0|-1
    E     (N*):    bar || as cold-drawn || 1635|3|0|0
    E     (N*):    bar || H₂ annealed at 1177 °C (2150 °F) || 1635|3|0|1
    E     (N*):    bar || after process anneal at 871 °C (1600 °F) || 1635|3|0|2
    E     (N*):    strip || cold-rolled || 1635|3|1|0
    E     (N*):    strip || forming and deep draw quality || 1635|3|1|1
    UTS   (N*):    bar || as cold-drawn || 1635|5|0|0
    UTS   (N*):    bar || H₂ annealed at 1177 °C (2150 °F) || 1635|5|0|1
    UTS   (N*):    bar || after process anneal at 871 °C (1600 °F) || 1635|5|0|2
    UTS   (N*):    strip || cold-rolled || 1635|5|1|0
    UTS   (N*):    strip || forming and deep draw quality || 1635|5|1|1
    UTS   (N*):    effect of tempering temperature on RT value || 1.52 mm (0.06 inch) strip tempered at 788 °C (1450 °F) for 2 h || 1635|5|2|0
    UTS   (N*):    effect of tempering temperature on RT value || 1.52 mm (0.06 inch) strip tempered at 871 °C (1600 °F) for 2 h || 1635|5|2|1
    UTS   (N*):    effect of tempering temperature on RT value || 1.52 mm (0.06 inch) strip tempered at 954 °C (1750 °F) for 2 h || 1635|5|2|2
    MTE    (N):    solid || 1635|8|0|-1
    SH    (N*):    solid || 1635|9|0|-1
    YS    (N*):    bar || as cold-drawn || 1635|13|0|0
    YS    (N*):    bar || H₂ annealed at 1177 °C (2150 °F) || 1635|13|0|1
    YS    (N*):    bar || after process anneal at 871 °C (1600 °F) || 1635|13|0|2
    YS    (N*):    effect of tempering temperature on RT value || 1.52 mm (0.06 inch) strip tempered at 788 °C (1450 °F) for 2 h || 1635|13|2|0
    YS    (N*):    effect of tempering temperature on RT value || 1.52 mm (0.06 inch) strip tempered at 871 °C (1600 °F) for 2 h || 1635|13|2|1
    YS    (N*):    effect of tempering temperature on RT value || 1.52 mm (0.06 inch) strip tempered at 954 °C (1750 °F) for 2 h || 1635|13|2|2
    CTE    (N):    solid || 1635|16|0|-1
    D      (N):    solid || 1635|24|0|-1
    TD    (N*):    solid || 1635|25|0|-1
    %El   (N*):    bar || as cold-drawn || 1635|29|0|0
    %El   (N*):    bar || H₂ annealed at 1177 °C (2150 °F) || 1635|29|0|1
    %El   (N*):    bar || after process anneal at 871 °C (1600 °F) || 1635|29|0|2
    %El   (N*):    strip || cold-rolled || 1635|29|1|0
    %El   (N*):    strip || forming and deep draw quality || 1635|29|1|1
    %El   (N*):    effect of tempering temperature on RT value || 1.52 mm (0.06 inch) strip tempered at 788 °C (1450 °F) for 2 h || 1635|29|2|0
    %El   (N*):    effect of tempering temperature on RT value || 1.52 mm (0.06 inch) strip tempered at 871 °C (1600 °F) for 2 h || 1635|29|2|1
    %El   (N*):    effect of tempering temperature on RT value || 1.52 mm (0.06 inch) strip tempered at 954 °C (1750 °F) for 2 h || 1635|29|2|2
    CL     (N):    transformer grade, 0.152 mm (0.006 inch) thick || tested at 20 °C (68 °F), 60 Hz, annealed at 1177 °C (2150 °F) || 1635|43|0|0
    CL     (N):    transformer grade, 0.152 mm (0.006 inch) thick || tested at 20 °C (68 °F), 400 Hz, annealed at 1177 °C (2150 °F) || 1635|43|0|1
    CL     (N):    transformer grade, 0.356 mm (0.014 inch) thick || tested at 20 °C (68 °F), 60 Hz, annealed at 1177 °C (2150 °F) || 1635|43|1|0
    CL     (N):    transformer grade, 0.356 mm (0.014 inch) thick || tested at 20 °C (68 °F), 400 Hz, annealed at 1177 °C (2150 °F) || 1635|43|1|1
    CL     (N):    rotor grade, 0.178 mm (0.007 inch) thick || tested at 20 °C (68 °F), 60 Hz, annealed at 1177 °C (2150 °F) || 1635|43|2|0
    CL     (N):    rotor grade, 0.178 mm (0.007 inch) thick || tested at 20 °C (68 °F), 400 Hz, annealed at 1177 °C (2150 °F) || 1635|43|2|1
    CL     (N):    rotor grade, 0.356 mm (0.014 inch) thick || tested at 20 °C (68 °F), 60 Hz, annealed at 1177 °C (2150 °F) || 1635|43|3|0
    CL     (N):    rotor grade, 0.356 mm (0.014 inch) thick || tested at 20 °C (68 °F), 400 Hz, annealed at 1177 °C (2150 °F) || 1635|43|3|1

return to listing

High Permeability 55 (New)

    RPB       :    tape core || tested at 20 °C (68 °F), annealed at 1180 °C (2156 °F), 60 Hz || 16213|7|0|0
    AP        :    tape core || tested at 20 °C (68 °F), annealed at 1180 °C (2156 °F), 60 Hz || 16213|15|0|0
    BH        :    tape core || tested at 20 °C (68 °F), annealed at 1180 °C (2156 °F), 60 Hz || 16213|23|0|0
    HB        :    tape core || tested at 20 °C (68 °F), annealed at 1180 °C (2156 °F), 60 Hz || 16213|31|0|0

return to listing

Hiperco 50 alloy

    UTS   (N*):    strip, as cold-drawn || 1646|5|0|-1
    UTS   (N*):    strip, annealed 760 °C (1400 °F) for 2 h || 0.152 mm (0.006 inch) || 1646|5|1|0
    UTS   (N*):    strip, annealed 760 °C (1400 °F) for 2 h || 0.356 mm (0.014 inch) || 1646|5|1|1
    UTS   (N*):    strip, annealed 843 °C (1550 °F) for 2 h || 0.152 mm (0.006 inch) || 1646|5|2|0
    UTS   (N*):    strip, annealed 843 °C (1550 °F) for 2 h || 0.356 mm (0.014 inch) || 1646|5|2|1
    YS    (N*):    strip, as cold-drawn || 1646|13|0|-1
    YS    (N*):    strip, annealed 760 °C (1400 °F) for 2 h || 0.152 mm (0.006 inch) || 1646|13|1|0
    YS    (N*):    strip, annealed 760 °C (1400 °F) for 2 h || 0.356 mm (0.014 inch) || 1646|13|1|1
    YS    (N*):    strip, annealed 843 °C (1550 °F) for 2 h || 0.152 mm (0.006 inch) || 1646|13|2|0
    YS    (N*):    strip, annealed 843 °C (1550 °F) for 2 h || 0.356 mm (0.014 inch) || 1646|13|2|1
    %El   (N*):    strip, as cold-drawn || 1646|29|0|-1
    %El   (N*):    strip, annealed 760 °C (1400 °F) for 2 h || 0.152 mm (0.006 inch) || 1646|29|1|0
    %El   (N*):    strip, annealed 760 °C (1400 °F) for 2 h || 0.356 mm (0.014 inch) || 1646|29|1|1
    %El   (N*):    strip, annealed 843 °C (1550 °F) for 2 h || 0.152 mm (0.006 inch) || 1646|29|2|0
    %El   (N*):    strip, annealed 843 °C (1550 °F) for 2 h || 0.356 mm (0.014 inch) || 1646|29|2|1

return to listing

Hiperco 50 HS alloy

    TC    (N*):    solid || 1648|1|0|-1
    RHO   (N*):    solid || 1648|2|0|-1
    E     (N*):    solid || 1648|3|0|-1
    UTS   (N*):    effect of tempering temperature on RT value || 720 °C (1328 °F) for 1 h || 1648|5|0|0
    UTS   (N*):    effect of tempering temperature on RT value || 720 °C (1328 °F) for 2 h || 1648|5|0|1
    UTS   (N*):    effect of tempering temperature on RT value || 720 °C (1328 °F) for 4 h || 1648|5|0|2
    UTS   (N*):    effect of tempering temperature on RT value || 740 °C (1364 °F) for 1 h || 1648|5|0|3
    UTS   (N*):    effect of tempering temperature on RT value || 740 °C (1364 °F) for 2 h || 1648|5|0|4
    UTS   (N*):    effect of tempering temperature on RT value || 740 °C (1364 °F) for 4 h || 1648|5|0|5
    UTS   (N*):    effect of tempering temperature on RT value || 760 °C (1400 °F) for 1 h || 1648|5|0|6
    UTS   (N*):    effect of tempering temperature on RT value || 760 °C (1400 °F) for 2 h || 1648|5|0|7
    UTS   (N*):    effect of tempering temperature on RT value || 760 °C (1400 °F) for 4 h || 1648|5|0|8
    UTS   (N*):    effect of tempering temperature on RT value || 800 °C (1472 °F) for 4 h || 1648|5|0|9
    SIGMA (N*):    solid || 1648|10|0|-1
    YS    (N*):    effect of tempering temperature on RT value || 720 °C (1328 °F) for 1 h || 1648|13|0|0
    YS    (N*):    effect of tempering temperature on RT value || 720 °C (1328 °F) for 2 h || 1648|13|0|1
    YS    (N*):    effect of tempering temperature on RT value || 720 °C (1328 °F) for 4 h || 1648|13|0|2
    YS    (N*):    effect of tempering temperature on RT value || 740 °C (1364 °F) for 1 h || 1648|13|0|3
    YS    (N*):    effect of tempering temperature on RT value || 740 °C (1364 °F) for 2 h || 1648|13|0|4
    YS    (N*):    effect of tempering temperature on RT value || 740 °C (1364 °F) for 4 h || 1648|13|0|5
    YS    (N*):    effect of tempering temperature on RT value || 760 °C (1400 °F) for 1 h || 1648|13|0|6
    YS    (N*):    effect of tempering temperature on RT value || 760 °C (1400 °F) for 2 h || 1648|13|0|7
    YS    (N*):    effect of tempering temperature on RT value || 760 °C (1400 °F) for 4 h || 1648|13|0|8
    YS    (N*):    effect of tempering temperature on RT value || 800 °C (1472 °F) for 4 h || 1648|13|0|9
    %El   (N*):    effect of tempering temperature on RT value || 720 °C (1328 °F) for 1 h || 1648|29|0|0
    %El   (N*):    effect of tempering temperature on RT value || 720 °C (1328 °F) for 2 h || 1648|29|0|1
    %El   (N*):    effect of tempering temperature on RT value || 720 °C (1328 °F) for 4 h || 1648|29|0|2
    %El   (N*):    effect of tempering temperature on RT value || 740 °C (1364 °F) for 1 h || 1648|29|0|3
    %El   (N*):    effect of tempering temperature on RT value || 740 °C (1364 °F) for 2 h || 1648|29|0|4
    %El   (N*):    effect of tempering temperature on RT value || 740 °C (1364 °F) for 4 h || 1648|29|0|5
    %El   (N*):    effect of tempering temperature on RT value || 760 °C (1400 °F) for 1 h || 1648|29|0|6
    %El   (N*):    effect of tempering temperature on RT value || 760 °C (1400 °F) for 2 h || 1648|29|0|7
    %El   (N*):    effect of tempering temperature on RT value || 760 °C (1400 °F) for 4 h || 1648|29|0|8
    %El   (N*):    effect of tempering temperature on RT value || 800 °C (1472 °F) for 4 h || 1648|29|0|9

return to listing

Hiperco 50A alloy

    UTS   (N*):    strip || as cold-drawn || 1647|5|0|0
    UTS   (N*):    strip || H₂ annealed at 843 °C (1550 °F) || 1647|5|0|1
    YS    (N*):    strip || as cold-drawn || 1647|13|0|0
    YS    (N*):    strip || H₂ annealed at 843 °C (1550 °F) || 1647|13|0|1
    %El   (N*):    strip || as cold-drawn || 1647|29|0|0
    %El   (N*):    strip || H₂ annealed at 843 °C (1550 °F) || 1647|29|0|1

return to listing

Hipernom alloy

    UTS   (N*):    effect of cold work on RT value || 0% cold worked || 1643|5|0|0
    UTS   (N*):    effect of cold work on RT value || 10% cold worked || 1643|5|0|1
    UTS   (N*):    effect of cold work on RT value || 20% cold worked || 1643|5|0|2
    UTS   (N*):    effect of cold work on RT value || 30% cold worked || 1643|5|0|3
    UTS   (N*):    effect of cold work on RT value || 50% cold worked || 1643|5|0|4
    YS    (N*):    effect of cold work on RT value || 0% cold worked || 1643|13|0|0
    YS    (N*):    effect of cold work on RT value || 10% cold worked || 1643|13|0|1
    YS    (N*):    effect of cold work on RT value || 20% cold worked || 1643|13|0|2
    YS    (N*):    effect of cold work on RT value || 30% cold worked || 1643|13|0|3
    YS    (N*):    effect of cold work on RT value || 50% cold worked || 1643|13|0|4
    %El   (N*):    effect of cold work on RT value || 0% cold worked || 1643|29|0|0
    %El   (N*):    effect of cold work on RT value || 10% cold worked || 1643|29|0|1
    %El   (N*):    effect of cold work on RT value || 20% cold worked || 1643|29|0|2
    %El   (N*):    effect of cold work on RT value || 30% cold worked || 1643|29|0|3
    %El   (N*):    effect of cold work on RT value || 50% cold worked || 1643|29|0|4

return to listing

HoCa₄O(BO₃)₃

    DLL    (N):    solid || 11 direction || 16197|0|0|0
    DLL    (N):    solid || 22 direction || 16197|0|0|1
    DLL    (N):    solid || 33 direction || 16197|0|0|2
    DLL    (N):    solid || polycrystal || 16197|0|0|3
    MTE    (N):    solid || 11 direction || 16197|8|0|0
    MTE    (N):    solid || 22 direction || 16197|8|0|1
    MTE    (N):    solid || 33 direction || 16197|8|0|2
    MTE    (N):    solid || polycrystal || 16197|8|0|3
    CTE    (N):    solid || 11 direction || 16197|16|0|0
    CTE    (N):    solid || 22 direction || 16197|16|0|1
    CTE    (N):    solid || 33 direction || 16197|16|0|2
    CTE    (N):    solid || polycrystal || 16197|16|0|3
    TD     (N):    solid || 11 direction || 16197|25|0|0
    TD     (N):    solid || 22 direction || 16197|25|0|1
    TD     (N):    solid || 33 direction || 16197|25|0|2
    TD     (N):    solid || polycrystal || 16197|25|0|3

return to listing

Ho₃TaO₇

    SH     (R):    solid || 560|9|0|-1

return to listing

Hy-Ra 80 alloy

    TC    (N*):    solid || 1640|1|0|-1
    RPB    (N):    0.0508 mm (0.002 inch) thick tape toroid || tested at 20 °C (68 °F), DC || 1640|7|0|0
    SH    (N*):    solid || 1640|9|0|-1
    AP     (N):    0.0508 mm (0.002 inch) thick tape toroid || tested at 20 °C (68 °F), DC || 1640|15|0|0
    BH     (N):    0.0508 mm (0.002 inch) thick tape toroid || tested at 20 °C (68 °F), DC || 1640|23|0|0
    TD    (N*):    solid || 1640|25|0|-1
    HB     (N):    0.0508 mm (0.002 inch) thick tape toroid || tested at 20 °C (68 °F), DC || 1640|31|0|0

return to listing

Hydrogen

    Vis    (N):    liquid || 832|26|1|-1

return to listing

HyMu 80 alloy (Permalloy 80)

    E     (N*):    bar || as cold-drawn || 1636|3|0|0
    E     (N*):    bar || H₂ annealed at 1121 °C (2050 °F) || 1636|3|0|1
    E     (N*):    bar || after process anneal at 871 °C (1600 °F) || 1636|3|0|2
    UTS   (N*):    bar || as cold-drawn || 1636|5|0|0
    UTS   (N*):    bar || H₂ annealed at 1121 °C (2050 °F) || 1636|5|0|1
    UTS   (N*):    bar || after process anneal at 871 °C (1600 °F) || 1636|5|0|2
    UTS   (N*):    strip || as cold-drawn || 1636|5|1|0
    UTS   (N*):    strip || H₂ annealed at 1121 °C (2050 °F) || 1636|5|1|1
    UTS   (N*):    strip || after process anneal at 871 °C (1600 °F) || 1636|5|1|2
    YS    (N*):    bar || as cold-drawn || 1636|13|0|0
    YS    (N*):    bar || H₂ annealed at 1121 °C (2050 °F) || 1636|13|0|1
    YS    (N*):    bar || after process anneal at 871 °C (1600 °F) || 1636|13|0|2
    YS    (N*):    strip || H₂ annealed at 1121 °C (2050 °F) || 1636|13|1|1
    YS    (N*):    strip || after process anneal at 871 °C (1600 °F) || 1636|13|1|2
    %El   (N*):    bar || as cold-drawn || 1636|29|0|0
    %El   (N*):    bar || H₂ annealed at 1121 °C (2050 °F) || 1636|29|0|1
    %El   (N*):    bar || after process anneal at 871 °C (1600 °F) || 1636|29|0|2
    %El   (N*):    strip || as cold-drawn || 1636|29|1|0
    %El   (N*):    strip || H₂ annealed at 1121 °C (2050 °F) || 1636|29|1|1
    %El   (N*):    strip || after process anneal at 871 °C (1600 °F) || 1636|29|1|2

return to listing

Hytrel 4068

    UTS   (N*):    ISO 527 || 3302|5|0|-1
    %El   (N*):    ISO 527 || at break || 3302|29|0|0

return to listing

Hytrel 4069

    UTS   (N*):    ISO 527 || 2232|5|0|-1
    %El   (N*):    ISO 527 || at break || 2232|29|0|0

return to listing

Hytrel 4556

    UTS   (N*):    ISO 527 || 2233|5|0|-1
    %El   (N*):    ISO 527 || at break || 2233|29|0|0

return to listing

Hytrel 5526

    UTS   (N*):    ISO 527 || 2234|5|0|-1
    YS    (N*):    ISO 527 || 2234|13|0|-1
    %El   (N*):    ISO 527 || at break || 2234|29|0|0
    %El   (N*):    ISO 527 || at yield || 2234|29|0|1

return to listing

Hytrel 5556

    UTS   (N*):    ISO 527 || 2235|5|0|-1
    YS    (N*):    ISO 527 || 2235|13|0|-1
    %El   (N*):    ISO 527 || at break || 2235|29|0|0
    %El   (N*):    ISO 527 || at yield || 2235|29|0|1

return to listing

Hytrel 6356

    UTS   (N*):    ISO 527 || 2236|5|0|-1
    %El   (N*):    ISO 527 || at yield || 2236|29|0|1

return to listing

Hytrel 7246

    UTS   (N*):    ISO 527 || 2237|5|0|-1
    YS    (N*):    ISO 527 || 2237|13|0|-1
    %El   (N*):    ISO 527 || at break || 2237|29|0|0
    %El   (N*):    ISO 527 || at yield || 2237|29|0|1

return to listing

Hytrel 8238

    UTS   (N*):    ISO 527 || 2238|5|0|-1
    %El   (N*):    ISO 527 || at yield || 2238|29|0|1

return to listing

Hytrel 3078

    UTS   (N*):    ISO 527 || 2230|5|0|-1
    %El   (N*):    ISO 527 || at break || 2230|29|0|0

return to listing

Hytrel 4056

    UTS   (N*):    ISO 527 || 2231|5|0|-1
    %El   (N*):    ISO 527 || at break || 2231|29|0|0

return to listing

Hytrel G4078

    UTS   (N*):    ISO 527 || 2241|5|0|-1
    %El   (N*):    ISO 527 || at break || 2241|29|0|0

return to listing

Hytrel G4774

    UTS   (N*):    ISO 527 || 2243|5|0|-1
    %El   (N*):    ISO 527 || at break || 2243|29|0|0

return to listing

Hytrel G5544

    UTS   (N*):    ISO 527 || 2244|5|0|-1
    %El   (N*):    ISO 527 || at break || 2244|29|0|0

return to listing

Hytrel G3548

    E      (N):    solid || 2239|3|0|-1
    UTS   (N*):    ISO 527 || 2239|5|0|-1
    %El   (N*):    ISO 527 || at break || 2239|29|0|0
    AV     (N):    liquid || tested at 170 °C (338 °F) || 2239|34|1|0
    AV     (N):    liquid || tested at 190 °C (374 °F) || 2239|34|1|1
    AV     (N):    liquid || tested at 210 °C (410 °F) || 2239|34|1|2
    AV     (N):    liquid || tested at 230 °C (446 °F) || 2239|34|1|3

return to listing

Hytrel G4074

    UTS   (N*):    ISO 527 || 2240|5|0|-1
    %El   (N*):    ISO 527 || at break || 2240|29|0|0

return to listing

Hytrel G4078LS

    UTS   (N*):    ISO 527 || 2242|5|0|-1

return to listing

Hytrel 5555HS

    UTS   (N*):    ISO 527 || 3303|5|0|-1
    YS    (N*):    ISO 527 || 3303|13|0|-1
    %El   (N*):    ISO 527 || at break || 3303|29|0|0
    %El   (N*):    ISO 527 || at yield || 3303|29|0|1

return to listing

IN-100

    RHO   (N*):    solid || 1951|2|0|-1
    SIGMA (N*):    solid || 1951|10|0|-1

return to listing

Inconel 600

    FSN    (N):    sheet || tested at 21 °C (70 °F), R = -1, K_t = 3.2, flexure, maximum stress || 1856|6|5|0
    FSN    (N):    sheet || tested at -79 °C (-110 °F), R = -1, K_t = 3.2, flexure, maximum stress || 1856|6|5|1
    FSN    (N):    sheet || tested at -195.6 °C (-320 °F), R = -1, K_t = 3.2, flexure, maximum stress || 1856|6|5|2
    FSN    (N):    sheet || tested at -252.8 °C (-423 °F), R = -1, K_t = 3.2, flexure, maximum stress || 1856|6|5|3
    FEN    (N):    sheet || tested at 21 °C (70 °F), R = -1, flexure, maximum strain || 1856|14|2|0
    FEN    (N):    sheet || tested at -79 °C (-110 °F), R = -1, flexure, maximum strain || 1856|14|2|1
    FEN    (N):    sheet || tested at -195.6 °C (-320 °F), R = -1, flexure, maximum strain || 1856|14|2|2
    FEN    (N):    sheet || tested at -252.8 °C (-423 °F), R = -1, flexure, maximum strain || 1856|14|2|3

return to listing

Inconel X-750

    FSN    (R):    cold-rolled sheet || tested at 21 °C (70 °F), R = -1, bending, flexure, aged at 704 °C (1300 °F) for 20 h, maximum stress || 1871|6|1|1
    FSN    (N):    cold-rolled sheet || tested at 21 °C (70 °F), R = -1, K_t = 3.2, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress || 1871|6|1|2
    FSN    (N):    cold-rolled sheet || tested at -79 °C (-110 °F), R = -1, K_t = 3.2, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress || 1871|6|1|3
    FSN    (N):    cold-rolled sheet || tested at -195.6 °C (-320 °F), R = -1, K_t = 3.2, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress || 1871|6|1|4
    FSN    (N):    cold-rolled sheet || tested at -252.8 °C (-423 °F), R = -1, K_t = 3.2, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress || 1871|6|1|5
    FSN    (R):    cold-rolled sheet || tested at 21 °C (70 °F), R = -1, K_t = 6.4, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress || 1871|6|1|6
    FSN    (N):    cold-rolled sheet || tested at -79 °C (-110 °F), R = -1, K_t = 6.4, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress || 1871|6|1|7
    FSN    (N):    cold-rolled sheet || tested at -195.6 °C (-320 °F), R = -1, K_t = 6.4, flexure, aged 704 °C (1300 °F) for 20 h, maximum stress || 1871|6|1|8
    FEN    (R):    cold-rolled sheet || tested at 21 °C (70 °F), R = -1, flexure, aged 704 °C (1300 °F) for 20 h, maximum strain || 1871|14|0|0
    FEN    (N):    cold-rolled sheet || tested at -79 °C (-110 °F), R = -1, flexure, aged 704 °C (1300 °F) for 20 h, maximum strain || 1871|14|0|1
    FEN    (N):    cold-rolled sheet || tested at -195.6 °C (-320 °F), R = -1, flexure, aged 704 °C (1300 °F) for 20 h, maximum strain || 1871|14|0|2
    FEN    (N):    cold-rolled sheet || tested at -252.8 °C (-423 °F), R = -1, flexure, aged 704 °C (1300 °F) for 20 h, maximum strain || 1871|14|0|3

return to listing

InSb

    RIW    (N):    measured in unknown ambient || tested at 23 °C (73 °F) || 2510|45|0|0

return to listing

KBr

    RIW    (N):    measured in unknown ambient || tested at 22 °C (72 °F) || 2440|45|0|0

return to listing

KI

    RIW    (N):    measured in unknown ambient || tested at 20 °C (68 °F) || 2462|45|0|0
    RIW    (N):    measured in unknown ambient || tested at 38 °C (100 °F) || 2462|45|0|1
    RIW    (N):    measured in unknown ambient || tested at 29 °C (84 °F) || 2462|45|0|2

return to listing

KURARITY KL-LK9333 (New)

    TC    (*):    solid || 16262|1|0|-1
    D     (*):    solid || 16262|24|0|-1
    DCRPT    :    1 mm (0.0394 inch) thick || tested at 23 °C (73 °F) || 16262|41|0|0
    DF        :    1 mm (0.0394 inch) thick || tested at 23 °C (73 °F) || 16262|42|0|0

return to listing

KURARITY LA4285

    DLL    (N):    solid || 14900|0|0|-1
    TC    (N*):    solid || 14900|1|0|-1
    RHO   (N*):    solid || IEC 60093 || 14900|2|0|0
    MTE    (N):    solid || 14900|8|0|-1
    SIGMA (N*):    solid || IEC 60093 || 14900|10|0|0
    D      (N):    solid || 14900|24|0|-1
    FM    (N*):    ISO 178 || 14900|32|0|-1
    AV     (N):    liquid || tested at 180 °C (356 °F) || 14900|34|1|0
    AV     (N):    liquid || tested at 200 °C (392 °F) || 14900|34|1|1
    AV     (N):    liquid || tested at 220 °C (428 °F) || 14900|34|1|2
    AV     (N):    liquid || tested at 240 °C (464 °F) || 14900|34|1|3
    DCRPT (N):    1 mm (0.0394 inch) thick || tested at 23 °C (73 °F) || 14900|41|0|0
    DF     (N):    1 mm (0.0394 inch) thick || tested at 23 °C (73 °F) || 14900|42|0|0

return to listing

KURARITY LA2250

    TC    (N*):    solid || 14898|1|0|-1
    AV     (N):    liquid || tested at 160 °C (320 °F) || 14898|34|1|0
    AV     (N):    liquid || tested at 180 °C (356 °F) || 14898|34|1|1
    AV     (N):    liquid || tested at 200 °C (392 °F) || 14898|34|1|2

return to listing

KURARITY LA2270

    TC    (N*):    solid || 14899|1|0|-1
    AV     (N):    liquid || tested at 160 °C (320 °F) || 14899|34|1|0
    AV     (N):    liquid || tested at 180 °C (356 °F) || 14899|34|1|1
    AV     (N):    liquid || tested at 200 °C (392 °F) || 14899|34|1|2
    DCRPT (N):    1 mm (0.0394 inch) thick || tested at 23 °C (73 °F) || 14899|41|0|0
    DF     (N):    1 mm (0.0394 inch) thick || tested at 23 °C (73 °F) || 14899|42|0|0

return to listing

KURARITY LA2114 (New)

    D     (*):    solid || 16263|24|0|-1
    Vis       :    liquid || 16263|26|1|-1

return to listing

KURARITY LA2330 (New)

    TC    (*):    solid || 16259|1|0|-1
    D     (*):    solid || 16259|24|0|-1
    DCRPT    :    1 mm (0.0394 inch) thick || tested at 23 °C (73 °F) || 16259|41|0|0
    DF        :    1 mm (0.0394 inch) thick || tested at 23 °C (73 °F) || 16259|42|0|0

return to listing

KURARITY LA3320 (New)

    TC    (*):    solid || 16260|1|0|-1
    D     (*):    solid || 16260|24|0|-1
    DCRPT    :    1 mm (0.0394 inch) thick || tested at 23 °C (73 °F) || 16260|41|0|0
    DF        :    1 mm (0.0394 inch) thick || tested at 23 °C (73 °F) || 16260|42|0|0

return to listing

KURARITY LK9243 (New)

    TC    (*):    solid || 16261|1|0|-1
    D     (*):    solid || 16261|24|0|-1
    DCRPT    :    1 mm (0.0394 inch) thick || tested at 23 °C (73 °F) || 16261|41|0|0
    DF        :    1 mm (0.0394 inch) thick || tested at 23 °C (73 °F) || 16261|42|0|0

return to listing

304L

    UTS    (N):    50% cold-rolled || unnotched, longitudinal || 1251|5|2|0
    UTS    (N):    50% cold-rolled || unnotched, transverse || 1251|5|2|1
    UTS    (N):    50% cold-rolled || notched, K_t = 3.2, longitudinal || 1251|5|2|2
    UTS    (N):    50% cold-rolled || notched, K_t = 3.2, transverse || 1251|5|2|3
    UTS    (N):    50% cold-rolled || notched, K_t = 6.3, longitudinal || 1251|5|2|4
    UTS    (N):    50% cold-rolled || notched, K_t = 6.3, transverse || 1251|5|2|5
    UTS    (N):    50% cold-rolled || notched, K_t = 19, longitudinal || 1251|5|2|6
    UTS    (N):    50% cold-rolled || notched, K_t = 19, transverse || 1251|5|2|7
    UTS    (N):    50% cold-rolled || weld joint, longitudinal || 1251|5|2|8
    UTS    (N):    50% cold-rolled || weld joint, transverse || 1251|5|2|9
    YS     (N):    50% cold-rolled || unnotched, longitudinal || 1251|13|2|0
    YS     (N):    50% cold-rolled || unnotched, transverse || 1251|13|2|1
    %El    (N):    60% cold-rolled || unnotched, longitudinal || 1251|29|2|0
    %El    (N):    60% cold-rolled || unnotched, transverse || 1251|29|2|1
    %El    (N):    60% cold-rolled || weld joint, longitudinal || 1251|29|2|2
    %El    (N):    60% cold-rolled || weld joint, transverse || 1251|29|2|3

return to listing

La₃TaO₇

    SH     (R):    solid || 565|9|0|-1

return to listing

Lauric acid (New)

    Vis       :    liquid || 16188|26|1|-1

return to listing

Lesquerella oil (New)

    Vis       :    liquid || 16184|26|1|-1

return to listing

LiAl (New)

    TC        :    cold-pressed powder (71% dense) || 16277|1|0|-1
    SH        :    cold-pressed powder (71% dense) || 16277|9|0|-1
    D     (*):    solid || orthorhombic Pbam || 16277|24|0|0
    TD        :    cold-pressed powder (71% dense) || 16277|25|0|-1

return to listing

LiF

    RIW    (N):    measured in unknown ambient || tested at 24 °C (74 °F) || 2455|45|0|0

return to listing

Li₁₃Si₄

    TC     (N):    cold-pressed powder (68% dense) || 12453|1|1|-1
    SH     (N):    cold-pressed powder (68% dense) || 12453|9|1|-1
    D     (R*):    solid || 12453|24|0|-1
    TD     (N):    cold-pressed powder (68% dense) || 12453|25|1|-1

return to listing

Lu₃TaO₇

    SH     (R):    solid || 584|9|0|-1

return to listing

Manganese

    SH     (R):    solid || 859|9|0|-1
    HC     (R):    solid || 859|17|0|-1
    TD     (R):    solid || 859|25|0|-1

return to listing

MgF₂

    RIW    (N):    measured in air || tested at 21 °C (70 °F), ordinary ray || 2456|45|0|0
    RIW    (N):    measured in air || tested at 21 °C (70 °F), extraordinary ray || 2456|45|0|1

return to listing

MgO

    RIW    (N):    measured in unknown ambient || tested at 23 °C (74 °F) || 2687|45|0|0

return to listing

Milkweed oil (New)

    Vis       :    liquid || 16185|26|1|-1

return to listing

Monel K-500

    FSN    (R):    sheet || tested at 21 °C (70 °F), R = -1, flexure, maximum stress || 1846|6|0|0
    FSN    (R):    sheet || tested at -79 °C (-110 °F), R = -1, flexure, maximum stress || 1846|6|0|1
    FSN    (R):    sheet || tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress || 1846|6|0|2
    FSN    (R):    sheet || tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress || 1846|6|0|3
    FSN    (N):    sheet || tested at 21 °C (70 °F), R = -1, K_t = 3.2, flexure, maximum stress || 1846|6|0|4
    FSN    (N):    sheet || tested at -79 °C (-110 °F), R = -1, K_t = 3.2, flexure, maximum stress || 1846|6|0|5
    FSN    (N):    sheet || tested at -195.6 °C (-320 °F), R = -1, K_t = 3.2, flexure, maximum stress || 1846|6|0|6
    FSN    (N):    sheet || tested at -252.8 °C (-423 °F), R = -1, K_t = 3.2, flexure, maximum stress || 1846|6|0|7

return to listing

Myristic acid (New)

    Vis       :    liquid || 16189|26|1|-1

return to listing

NaCl

    RIW    (N):    measured in unknown ambient || tested at 20 °C (68 °F) || 2449|45|0|0

return to listing

NaF

    RIW    (N):    measured in unknown ambient || tested at 19 °C (66 °F) || 2457|45|0|0

return to listing

NaNO₃

    RIW    (N):    measured in unknown ambient || tested at 23 °C (73 °F), ordinary ray || 3513|45|0|0
    RIW    (N):    measured in unknown ambient || tested at 23 °C (73 °F), extraordinary ray || 3513|45|0|1

return to listing

Nd:GdVO₄

    TC     (N):    solid || polycrystal || 2539|1|0|0
    TC     (N):    solid || a-axis || 2539|1|0|1
    TC     (N):    solid || c-axis || 2539|1|0|2
    SH     (R):    solid || 2539|9|0|-1
    TD     (N):    solid || polycrystal || 2539|25|0|0
    TD     (N):    solid || a-axis || 2539|25|0|1
    TD     (N):    solid || c-axis || 2539|25|0|2

return to listing

Nd:YVO₄

    TC     (N):    solid || polycrystal || 2540|1|0|0
    TC     (N):    solid || a-axis || 2540|1|0|1
    TC     (N):    solid || c-axis || 2540|1|0|2
    SH     (R):    solid || 2540|9|0|-1
    TD     (N):    solid || polycrystal || 2540|25|0|0
    TD     (N):    solid || a-axis || 2540|25|0|1
    TD     (N):    solid || c-axis || 2540|25|0|2

return to listing

Neon

    SH     (N):    solid || 841|9|0|-1
    HC     (N):    solid || 841|17|0|-1
    TD     (N):    liquid || 841|25|1|-1

return to listing

9 Ni steel

    FEN    (N):    normalized & aged || tested at 21 °C (70 °F), R = -1, flexure, maximum strain || 1211|14|0|0
    FEN    (N):    normalized & aged || tested at -79 °C (-110 °F), R = -1, flexure, maximum strain || 1211|14|0|1
    FEN    (N):    normalized & aged || tested at -195.6 °C (-320 °F), R = -1, flexure, maximum strain || 1211|14|0|2
    FEN    (N):    normalized & aged || tested at -252.8 °C (-423 °F), R = -1, flexure, maximum strain || 1211|14|0|3

return to listing

Nickel 270 (New)

    DLL       :    solid || 16168|0|0|-1
    TC    (*):    solid || 16168|1|0|-1
    RHO   (*):    solid || 16168|2|0|-1
    UTS   (*):    solid || annealed || 16168|5|0|0
    MTE       :    solid || 16168|8|0|-1
    SH    (*):    solid || 16168|9|0|-1
    SIGMA (*):    solid || 16168|10|0|-1
    YS    (*):    solid || annealed || 16168|13|0|0
    CTE       :    solid || 16168|16|0|-1
    D         :    solid || 16168|24|0|-1
    TD    (*):    solid || 16168|25|0|-1
    %El   (*):    solid || annealed || 16168|29|0|0

return to listing

Nickel

    SH     (R):    solid || 862|9|0|-1
    HC     (R):    solid || 862|17|0|-1
    TD     (R):    solid || 862|25|0|-1

return to listing

Niobium

    UTS    (N):    effect of H and strain rate || 1 ppm H, as-received, 8.33 x 10^-⁵/s || 875|5|1|0
    UTS    (N):    effect of H and strain rate || 1 ppm H, as-received, 0.00167/s || 875|5|1|1
    UTS    (N):    effect of H and strain rate || 1 ppm H, as-received, 0.1/s || 875|5|1|2
    UTS    (N):    effect of H and strain rate || 9 ppm H, annealed for 3 h at 400 °C (752 °F), 8.33 x 10^-⁵/s || 875|5|1|3
    UTS    (N):    effect of H and strain rate || 30 ppm H, annealed for 6 h at 400 °C (752 °F), 8.33 x 10^-⁵/s || 875|5|1|4
    YS     (N):    effect of H and strain rate || 1 ppm H, as-received, 8.33 x 10^-⁵/s || 875|13|1|0
    YS     (N):    effect of H and strain rate || 1 ppm H, as-received, 0.1/s || 875|13|1|2
    YS     (N):    effect of H and strain rate || 9 ppm H, annealed for 3 h at 400 °C (752 °F), 8.33 x 10^-⁵/s || 875|13|1|3
    YS     (N):    effect of H and strain rate || 30 ppm H, annealed for 6 h at 400 °C (752 °F), 8.33 x 10^-⁵/s || 875|13|1|4
    %El    (N):    effect of H and strain rate || 1 ppm H, as-received, 8.33 x 10^-⁵/s || 875|29|1|0
    %El    (N):    effect of H and strain rate || 1 ppm H, as-received, 0.00167/s || 875|29|1|1
    %El    (N):    effect of H and strain rate || 1 ppm H, as-received, 0.1/s || 875|29|1|2
    %El    (N):    effect of H and strain rate || 9 ppm H, annealed for 3 h at 400 °C (752 °F), 8.33 x 10^-⁵/s || 875|29|1|3
    %El    (N):    effect of H and strain rate || 30 ppm H, annealed for 6 h at 400 °C (752 °F), 8.33 x 10^-⁵/s || 875|29|1|4

return to listing

Nitrogen

    DCRPT (N):    solid || 838|41|0|-1

return to listing

Nonanoic acid (New)

    Vis       :    liquid || 16186|26|1|-1

return to listing

Oleic acid (New)

    Vis       :    liquid || 16192|26|1|-1

return to listing

Palm oil

    Vis    (N):    liquid || 3416|26|1|-1

return to listing

Palmitic acid (New)

    Vis       :    liquid || 16190|26|1|-1

return to listing

PbSe

    SH     (R):    solid || 2513|9|0|-1
    HC     (R):    solid || 2513|17|0|-1
    TD     (R):    solid || 2513|25|0|-1

return to listing

PbTe

    SH     (R):    solid || 15564|9|0|-1
    HC     (R):    solid || 15564|17|0|-1

return to listing

Platinum

    UTS    (R):    wires and sheets || annealed at 1100 °C (2012 °F) for 5 minutes || 912|5|0|0
    %El    (R):    wires and sheets || annealed at 1100 °C (2012 °F) for 5 minutes || 912|29|0|0

return to listing

Pt - 10 Ir (wt %) (New)

    E         :    solid || 16236|3|0|-1
    G         :    solid || 16236|11|0|-1
    v         :    solid || 16236|19|0|-1
    K         :    solid || 16236|27|0|-1

return to listing

Pt - 20 Ir (wt %) (New)

    E         :    solid || 16237|3|0|-1
    G         :    solid || 16237|11|0|-1
    v         :    solid || 16237|19|0|-1
    K         :    solid || 16237|27|0|-1

return to listing

Pt - 30 Ir (wt %) (New)

    E         :    solid || 16238|3|0|-1
    G         :    solid || 16238|11|0|-1
    v         :    solid || 16238|19|0|-1
    K         :    solid || 16238|27|0|-1

return to listing

Pt - 20 Rh (wt %) (PtRh20)

    E      (N):    solid || 3382|3|0|-1
    UTS    (N):    wires and sheets || 3382|5|0|-1
    G      (N):    solid || 3382|11|0|-1
    v      (N):    solid || 3382|19|0|-1
    K      (N):    solid || 3382|27|0|-1
    %El    (N):    wires and sheets || 3382|29|0|-1

return to listing

Pt - 15 Rh (wt %) (PtRh15) (New)

    UTS       :    wires and sheets || 16234|5|0|-1
    %El       :    wires and sheets || 16234|29|0|-1

return to listing

Pt - 7 Rh (wt %) (PtRh7) (New)

    UTS       :    wires and sheets || 16233|5|0|-1
    D     (*):    solid || 16233|24|0|-1
    %El       :    wires and sheets || 16233|29|0|-1

return to listing

Pt - 30 Rh (wt %) (PtRh30) (New)

    E         :    solid || 16235|3|0|-1
    G         :    solid || 16235|11|0|-1
    v         :    solid || 16235|19|0|-1
    K         :    solid || 16235|27|0|-1

return to listing

Pt - 10 Rh (wt %) (PtRh10)

    E      (N):    solid || 3378|3|0|-1
    UTS    (R):    wires and sheets || annealed at 1100 °C (2012 °F) for 5 minutes || 3378|5|0|0
    G      (N):    solid || 3378|11|0|-1
    v      (N):    solid || 3378|19|0|-1
    K      (N):    solid || 3378|27|0|-1
    %El    (R):    wires and sheets || annealed at 1100 °C (2012 °F) for 5 minutes || 3378|29|0|0

return to listing

Pt - 12 Rh (wt %)

    UTS    (N):    wires and sheets || 9344|5|0|-1
    %El    (N):    wires and sheets || 9344|29|0|-1

return to listing

PWA 1484

    CRS    (N):    1% strain || tested at 871 °C (1600 °F) || 1888|30|0|0
    CRS    (N):    1% strain || tested at 982 °C (1800 °F) || 1888|30|0|1
    CRS    (N):    1% strain || tested at 1038 °C (1900 °F) || 1888|30|0|2
    CRS    (N):    1% strain || Master curve (LMP) || 1888|30|0|3
    CRS    (N):    2.5% strain || tested at 871 °C (1600 °F) || 1888|30|1|0
    CRS    (N):    2.5% strain || tested at 982 °C (1800 °F) || 1888|30|1|1
    CRS    (N):    2.5% strain || tested at 1038 °C (1900 °F) || 1888|30|1|2
    CRS    (N):    2.5% strain || Master curve (LMP) || 1888|30|1|3
    CRS    (N):    5% strain || tested at 871 °C (1600 °F) || 1888|30|2|0
    CRS    (N):    5% strain || tested at 982 °C (1800 °F) || 1888|30|2|1
    CRS    (N):    5% strain || tested at 1038 °C (1900 °F) || 1888|30|2|2
    CRS    (N):    5% strain || Master curve (LMP) || 1888|30|2|3
    CRS    (N):    7.5% strain || tested at 871 °C (1600 °F) || 1888|30|3|0
    CRS    (N):    7.5% strain || tested at 982 °C (1800 °F) || 1888|30|3|1
    CRS    (N):    7.5% strain || tested at 1038 °C (1900 °F) || 1888|30|3|2
    CRS    (N):    7.5% strain || Master curve (LMP) || 1888|30|3|3
    CRS    (N):    10% strain || tested at 871 °C (1600 °F) || 1888|30|4|0
    CRS    (N):    10% strain || tested at 982 °C (1800 °F) || 1888|30|4|1
    CRS    (N):    10% strain || tested at 1038 °C (1900 °F) || 1888|30|4|2
    CRS    (N):    10% strain || Master curve (LMP) || 1888|30|4|3
    CRS    (N):    15% strain || tested at 871 °C (1600 °F) || 1888|30|5|0
    CRS    (N):    15% strain || tested at 1038 °C (1900 °F) || 1888|30|5|2
    CRS    (N):    15% strain || Master curve (LMP) || 1888|30|5|3
    CRS    (N):    20% strain || tested at 871 °C (1600 °F) || 1888|30|6|0
    IC     (N):    tested at 871 °C (1600 °F), (001) direction || 300 h || 1888|39|0|6
    IC     (N):    tested at 871 °C (1600 °F), (001) direction || 1,000 h || 1888|39|0|7
    IC     (N):    tested at 871 °C (1600 °F), (001) direction || 3,000 h || 1888|39|0|8
    IC     (N):    tested at 871 °C (1600 °F), (001) direction || 10,000 h || 1888|39|0|9
    IC     (N):    tested at 871 °C (1600 °F), (001) direction || 30,000 h || 1888|39|0|10
    IC     (N):    tested at 871 °C (1600 °F), (001) direction || 100,000 h || 1888|39|0|11
    IC     (N):    tested at 871 °C (1600 °F), (001) direction || 300,000 h || 1888|39|0|12
    IC     (N):    tested at 982 °C (1800 °F), (001) direction || 3 h || 1888|39|1|2
    IC     (N):    tested at 982 °C (1800 °F), (001) direction || 10 h || 1888|39|1|3
    IC     (N):    tested at 982 °C (1800 °F), (001) direction || 30 h || 1888|39|1|4
    IC     (N):    tested at 982 °C (1800 °F), (001) direction || 100 h || 1888|39|1|5
    IC     (N):    tested at 982 °C (1800 °F), (001) direction || 300 h || 1888|39|1|6
    IC     (N):    tested at 982 °C (1800 °F), (001) direction || 1,000 h || 1888|39|1|7
    IC     (N):    tested at 982 °C (1800 °F), (001) direction || 3,000 h || 1888|39|1|8
    IC     (N):    tested at 1038 °C (1900 °F), (001) direction || 0.3 h || 1888|39|2|0
    IC     (N):    tested at 1038 °C (1900 °F), (001) direction || 1 h || 1888|39|2|1
    IC     (N):    tested at 1038 °C (1900 °F), (001) direction || 3 h || 1888|39|2|2
    IC     (N):    tested at 1038 °C (1900 °F), (001) direction || 10 h || 1888|39|2|3
    IC     (N):    tested at 1038 °C (1900 °F), (001) direction || 30 h || 1888|39|2|4
    IC     (N):    tested at 1038 °C (1900 °F), (001) direction || 100 h || 1888|39|2|5
    IC     (N):    tested at 1038 °C (1900 °F), (001) direction || 300 h || 1888|39|2|6

return to listing

Pyrolytic graphite

    NE     (N):    solid || 228|28|0|-1

return to listing

R-449A (New)

    TC        :    saturated liquid || 16285|1|1|-1
    TC        :    saturated vapor || 16285|1|2|-1
    TC        :    superheated vapor || at 10 kPa (1.45 psi) || 16285|1|3|0
    TC        :    superheated vapor || at 101 kPa (14.7 psi) || 16285|1|3|1
    TC        :    superheated vapor || at 200 kPa (29.0 psi) || 16285|1|3|2
    TC        :    superheated vapor || at 300 kPa (43.5 psi) || 16285|1|3|3
    TC        :    superheated vapor || at 400 kPa (58.0 psi) || 16285|1|3|4
    TC        :    superheated vapor || at 500 kPa (72.5 psi) || 16285|1|3|5
    TC        :    superheated vapor || at 600 kPa (87.0 psi) || 16285|1|3|6
    TC        :    superheated vapor || at 800 kPa (116 psi) || 16285|1|3|7
    TC        :    superheated vapor || at 1 MPa (145 psi) || 16285|1|3|8
    TC        :    superheated vapor || at 1.50 MPa (218 psi) || 16285|1|3|9
    TC        :    superheated vapor || at 2 MPa (290 psi) || 16285|1|3|10
    TC        :    superheated vapor || at 2.50 MPa (363 psi) || 16285|1|3|11
    TC        :    superheated vapor || at 3 MPa (435 psi) || 16285|1|3|12
    SH        :    saturated liquid || 16285|9|1|-1
    SH        :    saturated vapor || 16285|9|2|-1
    SH        :    superheated vapor || at 10 kPa (1.45 psi) || 16285|9|3|0
    SH        :    superheated vapor || at 101 kPa (14.7 psi) || 16285|9|3|1
    SH        :    superheated vapor || at 200 kPa (29.0 psi) || 16285|9|3|2
    SH        :    superheated vapor || at 300 kPa (43.5 psi) || 16285|9|3|3
    SH        :    superheated vapor || at 400 kPa (58.0 psi) || 16285|9|3|4
    SH        :    superheated vapor || at 500 kPa (72.5 psi) || 16285|9|3|5
    SH        :    superheated vapor || at 600 kPa (87.0 psi) || 16285|9|3|6
    SH        :    superheated vapor || at 800 kPa (116 psi) || 16285|9|3|7
    SH        :    superheated vapor || at 1 MPa (145 psi) || 16285|9|3|8
    SH        :    superheated vapor || at 1.50 MPa (218 psi) || 16285|9|3|9
    SH        :    superheated vapor || at 2 MPa (290 psi) || 16285|9|3|10
    SH        :    superheated vapor || at 2.50 MPa (363 psi) || 16285|9|3|11
    SH        :    superheated vapor || at 3 MPa (435 psi) || 16285|9|3|12
    Vis       :    saturated liquid || 16285|26|1|-1
    Vis       :    saturated vapor || 16285|26|2|-1
    Vis       :    superheated vapor || at 10 kPa (1.45 psi) || 16285|26|3|0
    Vis       :    superheated vapor || at 101 kPa (14.7 psi) || 16285|26|3|1
    Vis       :    superheated vapor || at 200 kPa (29.0 psi) || 16285|26|3|2
    Vis       :    superheated vapor || at 300 kPa (43.5 psi) || 16285|26|3|3
    Vis       :    superheated vapor || at 400 kPa (58.0 psi) || 16285|26|3|4
    Vis       :    superheated vapor || at 500 kPa (72.5 psi) || 16285|26|3|5
    Vis       :    superheated vapor || at 600 kPa (87.0 psi) || 16285|26|3|6
    Vis       :    superheated vapor || at 800 kPa (116 psi) || 16285|26|3|7
    Vis       :    superheated vapor || at 1 MPa (145 psi) || 16285|26|3|8
    Vis       :    superheated vapor || at 1.50 MPa (218 psi) || 16285|26|3|9
    Vis       :    superheated vapor || at 2 MPa (290 psi) || 16285|26|3|10
    Vis       :    superheated vapor || at 2.50 MPa (363 psi) || 16285|26|3|11
    Vis       :    superheated vapor || at 3 MPa (435 psi) || 16285|26|3|12
    ST        :    saturated liquid || 16285|38|1|-1

return to listing

RE-170 (CH₃OCH₃)

    DLL    (R):    liquid || 3422|0|1|-1
    MTE    (R):    liquid || 3422|8|1|-1
    VP     (N):    saturated liquid || 3422|18|1|-1
    D      (R):    liquid || 3422|24|1|-1

return to listing

Rene 95

    CRS    (N):    0.75% strain || tested at 650 °C (1202 °F) || 1910|30|0|0
    CRS    (N):    1% strain || tested at 650 °C (1202 °F) || 1910|30|1|0
    CRS    (N):    1.5% strain || tested at 650 °C (1202 °F) || 1910|30|2|0
    CRS    (N):    2% strain || tested at 650 °C (1202 °F) || 1910|30|3|0
    IC     (N):    tested at 650 °C (1202 °F) || 0.1 h || 1910|39|0|0
    IC     (N):    tested at 650 °C (1202 °F) || 0.3 h || 1910|39|0|1
    IC     (N):    tested at 650 °C (1202 °F) || 1 h || 1910|39|0|2
    IC     (N):    tested at 650 °C (1202 °F) || 3 h || 1910|39|0|3

return to listing

Rubitherm RT70HC PCM (New)

    TC        :    solid || 16198|1|0|-1
    TC        :    liquid || 16198|1|1|-1
    SH        :    solid || 16198|9|0|-1
    SH        :    liquid || 16198|9|1|-1
    D     (*):    solid || 16198|24|0|-1
    D         :    liquid || 16198|24|1|-1
    TD        :    solid || 16198|25|0|-1
    TD        :    liquid || 16198|25|1|-1

return to listing

65 Se - 35 As (at %) (New)

    DLL       :    glass || 16275|0|0|-1
    MTE       :    glass || 16275|8|0|-1
    CTE       :    glass || 16275|16|0|-1
    D         :    glass || 16275|24|0|-1
    Vis       :    liquid || 16275|26|1|-1

return to listing

60 Se - 40 As (at %) (New)

    DLL       :    glass || 16276|0|0|-1
    MTE       :    glass || 16276|8|0|-1
    CTE       :    glass || 16276|16|0|-1
    D         :    glass || 16276|24|0|-1
    Vis       :    liquid || 16276|26|1|-1

return to listing

91.6 Se - 8.4 As (at %) (New)

    DLL       :    glass || 16269|0|0|-1
    TC    (*):    glass || 16269|1|0|-1
    MTE       :    glass || 16269|8|0|-1
    CTE       :    glass || 16269|16|0|-1
    D         :    glass || 16269|24|0|-1
    RIW       :    glass, measured in unknown ambient || tested at 27 °C (81 °F) || 16269|45|0|0

return to listing

90 Se - 10 As (at %) (New)

    DLL       :    glass || 16270|0|0|-1
    MTE       :    glass || 16270|8|0|-1
    CTE       :    glass || 16270|16|0|-1
    D         :    glass || 16270|24|0|-1
    Vis       :    liquid || 16270|26|1|-1

return to listing

85 Se - 15 As (at %) (New)

    DLL       :    glass || 16271|0|0|-1
    MTE       :    glass || 16271|8|0|-1
    CTE       :    glass || 16271|16|0|-1
    D         :    glass || 16271|24|0|-1
    Vis       :    liquid || 16271|26|1|-1

return to listing

80 Se - 20 As (at %) (New)

    DLL       :    glass || 16272|0|0|-1
    MTE       :    glass || 16272|8|0|-1
    CTE       :    glass || 16272|16|0|-1
    D         :    glass || 16272|24|0|-1
    Vis       :    liquid || 16272|26|1|-1

return to listing

75 Se - 25 As (at %) (New)

    DLL       :    glass || 16273|0|0|-1
    MTE       :    glass || 16273|8|0|-1
    CTE       :    glass || 16273|16|0|-1
    D         :    glass || 16273|24|0|-1
    Vis       :    liquid || 16273|26|1|-1

return to listing

70 Se - 30 As (at %) (New)

    DLL       :    glass || 16274|0|0|-1
    MTE       :    glass || 16274|8|0|-1
    CTE       :    glass || 16274|16|0|-1
    D         :    glass || 16274|24|0|-1
    Vis       :    liquid || 16274|26|1|-1

return to listing

SEN6 (New)

    SSC       :    die cast || tested at 25 °C (77 °F), 0.001/s || 16292|4|0|0
    UTS   (*):    die cast || 16292|5|0|-1
    FSN       :    die cast || tested at 23 °C (73 °F), R = -1, axial, stress amplitude || 16292|6|0|0
    YS    (*):    die cast || 16292|13|0|-1
    %El   (*):    die cast || 16292|29|0|-1

return to listing

Silicon core iron A-FM

    DLL    (N):    solid || 3112|0|0|-1
    UTS   (N*):    9.52 mm (0.375 inch) diameter bar || mill annealed || 3112|5|0|0
    UTS   (N*):    9.52 mm (0.375 inch) diameter bar || annealed for magnetic properties || 3112|5|0|1
    MTE    (N):    solid || 3112|8|0|-1
    YS    (N*):    9.52 mm (0.375 inch) diameter bar || mill annealed || 3112|13|0|0
    YS    (N*):    9.52 mm (0.375 inch) diameter bar || annealed for magnetic properties || 3112|13|0|1
    CTE    (N):    solid || 3112|16|0|-1
    D      (N):    solid || 3112|24|0|-1
    %El   (N*):    9.52 mm (0.375 inch) diameter bar || annealed for magnetic properties || 3112|29|0|1

return to listing

Silicon core iron A

    DLL    (N):    solid || 1649|0|0|-1
    UTS   (N*):    cold-rolled 7.62 mm (0.3 inch) thick strip || mill annealed || 1649|5|0|0
    UTS   (N*):    annealed for magnetic properties || 816 °C (1500 °F) || 1649|5|1|0
    MTE    (N):    solid || 1649|8|0|-1
    YS    (N*):    cold-rolled 7.62 mm (0.3 inch) thick strip || mill annealed || 1649|13|0|0
    YS    (N*):    annealed for magnetic properties || 816 °C (1500 °F) || 1649|13|1|0
    CTE    (N):    solid || 1649|16|0|-1
    D      (N):    solid || 1649|24|0|-1
    %El   (N*):    cold-rolled 7.62 mm (0.3 inch) thick strip || mill annealed || 1649|29|0|0
    %El   (N*):    annealed for magnetic properties || 816 °C (1500 °F) || 1649|29|1|0

return to listing

Silicon core iron B-FM

    DLL    (N):    solid || 3114|0|0|-1
    UTS   (N*):    9.52 mm (0.375 inch) diameter bar || mill annealed || 3114|5|0|0
    UTS   (N*):    9.52 mm (0.375 inch) diameter bar || annealed for magnetic properties || 3114|5|0|1
    MTE    (N):    solid || 3114|8|0|-1
    YS    (N*):    9.52 mm (0.375 inch) diameter bar || mill annealed || 3114|13|0|0
    YS    (N*):    9.52 mm (0.375 inch) diameter bar || annealed for magnetic properties || 3114|13|0|1
    CTE    (N):    solid || 3114|16|0|-1
    D      (N):    solid || 3114|24|0|-1
    %El   (N*):    9.52 mm (0.375 inch) diameter bar || annealed for magnetic properties || 3114|29|0|1

return to listing

Silicon core iron B

    DLL    (N):    solid || 3113|0|0|-1
    UTS   (N*):    9.52 mm (0.375 inch) diameter bar || mill annealed || 3113|5|0|0
    UTS   (N*):    9.52 mm (0.375 inch) diameter bar || annealed for magnetic properties || 3113|5|0|1
    MTE    (N):    solid || 3113|8|0|-1
    YS    (N*):    9.52 mm (0.375 inch) diameter bar || mill annealed || 3113|13|0|0
    YS    (N*):    9.52 mm (0.375 inch) diameter bar || annealed for magnetic properties || 3113|13|0|1
    CTE    (N):    solid || 3113|16|0|-1
    D      (N):    solid || 3113|24|0|-1
    %El   (N*):    9.52 mm (0.375 inch) diameter bar || annealed for magnetic properties || 3113|29|0|1

return to listing

Silicon core iron C

    UTS   (N*):    9.52 mm (0.375 inch) diameter bar || unannealed || 1651|5|0|0
    UTS   (N*):    9.52 mm (0.375 inch) diameter bar || annealed for magnetic properties || 1651|5|0|1
    YS    (N*):    9.52 mm (0.375 inch) diameter bar || unannealed || 1651|13|0|0
    YS    (N*):    9.52 mm (0.375 inch) diameter bar || annealed for magnetic properties || 1651|13|0|1
    %El   (N*):    9.52 mm (0.375 inch) diameter bar || annealed for magnetic properties || 1651|29|0|1

return to listing

Sm₃TaO₇

    DLL    (N):    solid || polycrystal || 628|0|0|0
    DLL    (N):    solid || a-axis || 628|0|0|1
    DLL    (N):    solid || b-axis || 628|0|0|2
    DLL    (N):    solid || c-axis || 628|0|0|3
    MTE    (N):    solid || polycrystal || 628|8|0|0
    MTE    (N):    solid || a-axis || 628|8|0|1
    MTE    (N):    solid || b-axis || 628|8|0|2
    MTE    (N):    solid || c-axis || 628|8|0|3
    SH     (R):    solid || 628|9|0|-1
    CTE    (N):    solid || polycrystal || 628|16|0|0
    CTE    (N):    solid || a-axis || 628|16|0|1
    CTE    (N):    solid || b-axis || 628|16|0|2
    CTE    (N):    solid || c-axis || 628|16|0|3
    HC     (R):    solid || 628|17|0|-1
    D      (R):    solid || orthorhombic || 628|24|0|0

return to listing

Sn - 3.5 Ag (wt %)

    ST     (N):    liquid || 2745|38|1|-1

return to listing

Soybean oil

    Vis    (N):    liquid || 3413|26|1|-1

return to listing

SrTiO₃ (Cr doped)

    TC     (N):    Cr doped || 0.001 || 1311|1|1|0
    TC     (N):    Cr doped || 0.002 || 1311|1|1|1
    TC     (N):    Cr doped || 0.003 || 1311|1|1|2
    TC     (N):    Cr doped || 0.004 || 1311|1|1|3
    RHO    (N):    Cr doped || 0.001 || 1311|2|1|0
    RHO    (N):    Cr doped || 0.002 || 1311|2|1|1
    RHO    (N):    Cr doped || 0.003 || 1311|2|1|2
    RHO    (N):    Cr doped || 0.004 || 1311|2|1|3
    SIGMA (N):    Cr doped || 0.001 || 1311|10|1|0
    SIGMA (N):    Cr doped || 0.002 || 1311|10|1|1
    SIGMA (N):    Cr doped || 0.003 || 1311|10|1|2
    SIGMA (N):    Cr doped || 0.004 || 1311|10|1|3
    RIW    (N):    measured in unknown ambient || tested at 23 °C (73 °F) || 1311|45|0|0
    S      (N):    Cr doped || 0.001 || 1311|48|1|0
    S      (N):    Cr doped || 0.002 || 1311|48|1|1
    S      (N):    Cr doped || 0.003 || 1311|48|1|2
    S      (N):    Cr doped || 0.004 || 1311|48|1|3

return to listing

Stearic acid (New)

    Vis       :    liquid || 16191|26|1|-1

return to listing

Sunflower oil

    Vis    (N):    liquid || 3415|26|1|-1

return to listing

Superloy GDSL

    TC    (N*):    solid || 16194|1|0|-1
    E     (N*):    Effect of wall thickness || 1 mm (0.0394 inch), as-cast || 16194|3|0|0
    E     (N*):    Effect of wall thickness || 1.5 mm (0.0591 inch), after 8 weeks || 16194|3|0|1
    UTS   (N*):    Effect of wall thickness || 1 mm (0.0394 inch), as-cast || 16194|5|0|0
    UTS   (N*):    Effect of wall thickness || 1.5 mm (0.0591 inch), after 8 weeks || 16194|5|0|1
    MTE   (N*):    solid || 16194|8|0|-1
    SH     (N):    solid || 16194|9|0|-1
    YS    (N*):    Effect of wall thickness || 1 mm (0.0394 inch), as-cast || 16194|13|0|0
    YS    (N*):    Effect of wall thickness || 1 mm (0.0394 inch), after 8 weeks || 16194|13|0|1
    D     (N*):    solid || 16194|24|0|-1
    TD    (N*):    solid || 16194|25|0|-1
    %El   (N*):    Effect of wall thickness || 1 mm (0.0394 inch), as-cast || 16194|29|0|0
    %El   (N*):    Effect of wall thickness || 1 mm (0.0394 inch), aged 10 days at 95 °C (203 °F) || 16194|29|0|1
    %El   (N*):    Effect of wall thickness || 1 mm (0.0394 inch), after 8 weeks || 16194|29|0|2

return to listing

Tata NO30-1500H electrical steel (New)

    DLL       :    0.3 mm (0.0118 inch) non-oriented sheet || 16180|0|0|-1
    TC    (*):    0.3 mm (0.0118 inch) non-oriented sheet || 16180|1|0|-1
    RHO   (*):    0.3 mm (0.0118 inch) non-oriented sheet || 16180|2|0|-1
    E     (*):    0.3 mm (0.0118 inch) non-oriented sheet || in rolling direction || 16180|3|0|0
    UTS   (*):    0.3 mm (0.0118 inch) non-oriented sheet || in rolling direction || 16180|5|0|0
    RPB       :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16180|7|0|0
    RPB       :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16180|7|0|1
    RPB       :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16180|7|0|2
    RPB       :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16180|7|0|3
    RPB       :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16180|7|0|4
    RPB       :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16180|7|0|5
    RPB       :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16180|7|0|6
    RPB       :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16180|7|0|7
    RPB       :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16180|7|0|8
    MTE       :    0.3 mm (0.0118 inch) non-oriented sheet || 16180|8|0|-1
    SIGMA (*):    0.3 mm (0.0118 inch) non-oriented sheet || 16180|10|0|-1
    YS    (*):    0.3 mm (0.0118 inch) non-oriented sheet || in rolling direction || 16180|13|0|0
    AP        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16180|15|0|0
    AP        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16180|15|0|1
    AP        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16180|15|0|2
    AP        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16180|15|0|3
    AP        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16180|15|0|4
    AP        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16180|15|0|5
    AP        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16180|15|0|6
    AP        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16180|15|0|7
    AP        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16180|15|0|8
    BH        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16180|23|0|0
    BH        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16180|23|0|1
    BH        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16180|23|0|2
    BH        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16180|23|0|3
    BH        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16180|23|0|4
    BH        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16180|23|0|5
    BH        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16180|23|0|6
    BH        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16180|23|0|7
    BH        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16180|23|0|8
    D         :    0.3 mm (0.0118 inch) non-oriented sheet || 16180|24|0|-1
    %El   (*):    0.3 mm (0.0118 inch) non-oriented sheet || in rolling direction || 16180|29|0|0
    HB        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16180|31|0|0
    HB        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16180|31|0|1
    HB        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16180|31|0|2
    HB        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16180|31|0|3
    HB        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16180|31|0|4
    HB        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16180|31|0|5
    HB        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16180|31|0|6
    HB        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16180|31|0|7
    HB        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16180|31|0|8
    CL        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16180|43|0|0
    CL        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16180|43|0|1
    CL        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16180|43|0|2
    CL        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16180|43|0|3
    CL        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16180|43|0|4
    CL        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16180|43|0|5
    CL        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16180|43|0|6
    CL        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16180|43|0|7
    CL        :    0.3 mm (0.0118 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16180|43|0|8

return to listing

Tata NO35-1750H electrical steel (New)

    DLL       :    0.35 mm (0.0138 inch) non-oriented sheet || 16181|0|0|-1
    TC    (*):    0.35 mm (0.0138 inch) non-oriented sheet || 16181|1|0|-1
    RHO   (*):    0.35 mm (0.0138 inch) non-oriented sheet || 16181|2|0|-1
    E     (*):    0.35 mm (0.0138 inch) non-oriented sheet || in rolling direction || 16181|3|0|0
    UTS   (*):    0.35 mm (0.0138 inch) non-oriented sheet || in rolling direction || 16181|5|0|0
    RPB       :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16181|7|0|0
    RPB       :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16181|7|0|1
    RPB       :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16181|7|0|2
    RPB       :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16181|7|0|3
    RPB       :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16181|7|0|4
    RPB       :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16181|7|0|5
    RPB       :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16181|7|0|6
    RPB       :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16181|7|0|7
    RPB       :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16181|7|0|8
    MTE       :    0.35 mm (0.0138 inch) non-oriented sheet || 16181|8|0|-1
    SIGMA (*):    0.35 mm (0.0138 inch) non-oriented sheet || 16181|10|0|-1
    YS    (*):    0.35 mm (0.0138 inch) non-oriented sheet || in rolling direction || 16181|13|0|0
    AP        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16181|15|0|0
    AP        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16181|15|0|1
    AP        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16181|15|0|2
    AP        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16181|15|0|3
    AP        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16181|15|0|4
    AP        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16181|15|0|5
    AP        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16181|15|0|6
    AP        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16181|15|0|7
    AP        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16181|15|0|8
    BH        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16181|23|0|0
    BH        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16181|23|0|1
    BH        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16181|23|0|2
    BH        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16181|23|0|3
    BH        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16181|23|0|4
    BH        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16181|23|0|5
    BH        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16181|23|0|6
    BH        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16181|23|0|7
    BH        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16181|23|0|8
    D         :    0.35 mm (0.0138 inch) non-oriented sheet || 16181|24|0|-1
    %El   (*):    0.35 mm (0.0138 inch) non-oriented sheet || in rolling direction || 16181|29|0|0
    HB        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16181|31|0|0
    HB        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16181|31|0|1
    HB        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16181|31|0|2
    HB        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16181|31|0|3
    HB        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16181|31|0|4
    HB        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16181|31|0|5
    HB        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16181|31|0|6
    HB        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16181|31|0|7
    HB        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16181|31|0|8
    CL        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16181|43|0|0
    CL        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16181|43|0|1
    CL        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16181|43|0|2
    CL        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16181|43|0|3
    CL        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16181|43|0|4
    CL        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16181|43|0|5
    CL        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16181|43|0|6
    CL        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16181|43|0|7
    CL        :    0.35 mm (0.0138 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16181|43|0|8

return to listing

Tata NO18-1160H electrical steel (New)

    DLL       :    0.18 mm (0.00709 inch) non-oriented sheet || 16172|0|0|-1
    TC    (*):    0.18 mm (0.00709 inch) non-oriented sheet || 16172|1|0|-1
    RHO   (*):    0.18 mm (0.00709 inch) non-oriented sheet || 16172|2|0|-1
    E     (*):    0.18 mm (0.00709 inch) non-oriented sheet || in rolling direction || 16172|3|0|0
    UTS   (*):    0.18 mm (0.00709 inch) non-oriented sheet || in rolling direction || 16172|5|0|0
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16172|7|0|0
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16172|7|0|1
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16172|7|0|2
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16172|7|0|3
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16172|7|0|4
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16172|7|0|5
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16172|7|0|6
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16172|7|0|7
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16172|7|0|8
    MTE       :    0.18 mm (0.00709 inch) non-oriented sheet || 16172|8|0|-1
    SIGMA (*):    0.18 mm (0.00709 inch) non-oriented sheet || 16172|10|0|-1
    YS    (*):    0.18 mm (0.00709 inch) non-oriented sheet || in rolling direction || 16172|13|0|0
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16172|15|0|0
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16172|15|0|1
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16172|15|0|2
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16172|15|0|3
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16172|15|0|4
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16172|15|0|5
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16172|15|0|6
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16172|15|0|7
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16172|15|0|8
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16172|23|0|0
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16172|23|0|1
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16172|23|0|2
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16172|23|0|3
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16172|23|0|4
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16172|23|0|5
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16172|23|0|6
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16172|23|0|7
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16172|23|0|8
    D         :    0.18 mm (0.00709 inch) non-oriented sheet || 16172|24|0|-1
    %El   (*):    0.18 mm (0.00709 inch) non-oriented sheet || in rolling direction || 16172|29|0|0
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16172|31|0|0
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16172|31|0|1
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16172|31|0|2
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16172|31|0|3
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16172|31|0|4
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16172|31|0|5
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16172|31|0|6
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16172|31|0|7
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16172|31|0|8
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16172|43|0|0
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16172|43|0|1
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16172|43|0|2
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16172|43|0|3
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16172|43|0|4
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16172|43|0|5
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16172|43|0|6
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16172|43|0|7
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16172|43|0|8

return to listing

Tata NO20-1200H electrical steel (New)

    DLL       :    0.2 mm (0.00787 inch) non-oriented sheet || 16174|0|0|-1
    TC    (*):    0.2 mm (0.00787 inch) non-oriented sheet || 16174|1|0|-1
    RHO   (*):    0.2 mm (0.00787 inch) non-oriented sheet || 16174|2|0|-1
    E     (*):    0.2 mm (0.00787 inch) non-oriented sheet || in rolling direction || 16174|3|0|0
    UTS   (*):    0.2 mm (0.00787 inch) non-oriented sheet || in rolling direction || 16174|5|0|0
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16174|7|0|0
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16174|7|0|1
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16174|7|0|2
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16174|7|0|3
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16174|7|0|4
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16174|7|0|5
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16174|7|0|6
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16174|7|0|7
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16174|7|0|8
    MTE       :    0.2 mm (0.00787 inch) non-oriented sheet || 16174|8|0|-1
    SIGMA (*):    0.2 mm (0.00787 inch) non-oriented sheet || 16174|10|0|-1
    YS    (*):    0.2 mm (0.00787 inch) non-oriented sheet || in rolling direction || 16174|13|0|0
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16174|15|0|0
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16174|15|0|1
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16174|15|0|2
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16174|15|0|3
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16174|15|0|4
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16174|15|0|5
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16174|15|0|6
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16174|15|0|7
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16174|15|0|8
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16174|23|0|0
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16174|23|0|1
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16174|23|0|2
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16174|23|0|3
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16174|23|0|4
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16174|23|0|5
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16174|23|0|6
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16174|23|0|7
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16174|23|0|8
    D         :    0.2 mm (0.00787 inch) non-oriented sheet || 16174|24|0|-1
    %El   (*):    0.2 mm (0.00787 inch) non-oriented sheet || in rolling direction || 16174|29|0|0
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16174|31|0|0
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16174|31|0|1
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16174|31|0|2
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16174|31|0|3
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16174|31|0|4
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16174|31|0|5
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16174|31|0|6
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16174|31|0|7
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16174|31|0|8
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16174|43|0|0
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16174|43|0|1
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16174|43|0|2
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16174|43|0|3
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16174|43|0|4
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16174|43|0|5
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16174|43|0|6
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16174|43|0|7
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16174|43|0|8

return to listing

Tata NO20-1300H electrical steel (New)

    DLL       :    0.2 mm (0.00787 inch) non-oriented sheet || 16175|0|0|-1
    TC    (*):    0.2 mm (0.00787 inch) non-oriented sheet || 16175|1|0|-1
    RHO   (*):    0.2 mm (0.00787 inch) non-oriented sheet || 16175|2|0|-1
    E     (*):    0.2 mm (0.00787 inch) non-oriented sheet || in rolling direction || 16175|3|0|0
    UTS   (*):    0.2 mm (0.00787 inch) non-oriented sheet || in rolling direction || 16175|5|0|0
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16175|7|0|0
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16175|7|0|1
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16175|7|0|2
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16175|7|0|3
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16175|7|0|4
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16175|7|0|5
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16175|7|0|6
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16175|7|0|7
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16175|7|0|8
    MTE       :    0.2 mm (0.00787 inch) non-oriented sheet || 16175|8|0|-1
    SIGMA (*):    0.2 mm (0.00787 inch) non-oriented sheet || 16175|10|0|-1
    YS    (*):    0.2 mm (0.00787 inch) non-oriented sheet || in rolling direction || 16175|13|0|0
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16175|15|0|0
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16175|15|0|1
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16175|15|0|2
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16175|15|0|3
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16175|15|0|4
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16175|15|0|5
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16175|15|0|6
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16175|15|0|7
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16175|15|0|8
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16175|23|0|0
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16175|23|0|1
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16175|23|0|2
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16175|23|0|3
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16175|23|0|4
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16175|23|0|5
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16175|23|0|6
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16175|23|0|7
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16175|23|0|8
    D         :    0.2 mm (0.00787 inch) non-oriented sheet || 16175|24|0|-1
    %El   (*):    0.2 mm (0.00787 inch) non-oriented sheet || in rolling direction || 16175|29|0|0
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16175|31|0|0
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16175|31|0|1
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16175|31|0|2
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16175|31|0|3
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16175|31|0|4
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16175|31|0|5
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16175|31|0|6
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16175|31|0|7
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16175|31|0|8
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16175|43|0|0
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16175|43|0|1
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16175|43|0|2
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16175|43|0|3
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16175|43|0|4
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16175|43|0|5
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16175|43|0|6
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16175|43|0|7
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16175|43|0|8

return to listing

Tata NO25-1350H electrical steel (New)

    DLL       :    0.25 mm (0.00984 inch) non-oriented sheet || 16177|0|0|-1
    TC    (*):    0.25 mm (0.00984 inch) non-oriented sheet || 16177|1|0|-1
    RHO   (*):    0.25 mm (0.00984 inch) non-oriented sheet || 16177|2|0|-1
    E     (*):    0.25 mm (0.00984 inch) non-oriented sheet || in rolling direction || 16177|3|0|0
    UTS   (*):    0.25 mm (0.00984 inch) non-oriented sheet || in rolling direction || 16177|5|0|0
    RPB       :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16177|7|0|0
    RPB       :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16177|7|0|1
    RPB       :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16177|7|0|2
    RPB       :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16177|7|0|3
    RPB       :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16177|7|0|4
    RPB       :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16177|7|0|5
    RPB       :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16177|7|0|6
    RPB       :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16177|7|0|7
    RPB       :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16177|7|0|8
    MTE       :    0.25 mm (0.00984 inch) non-oriented sheet || 16177|8|0|-1
    SIGMA (*):    0.25 mm (0.00984 inch) non-oriented sheet || 16177|10|0|-1
    YS    (*):    0.25 mm (0.00984 inch) non-oriented sheet || in rolling direction || 16177|13|0|0
    AP        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16177|15|0|0
    AP        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16177|15|0|1
    AP        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16177|15|0|2
    AP        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16177|15|0|3
    AP        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16177|15|0|4
    AP        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16177|15|0|5
    AP        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16177|15|0|6
    AP        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16177|15|0|7
    AP        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16177|15|0|8
    BH        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16177|23|0|0
    BH        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16177|23|0|1
    BH        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16177|23|0|2
    BH        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16177|23|0|3
    BH        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16177|23|0|4
    BH        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16177|23|0|5
    BH        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16177|23|0|6
    BH        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16177|23|0|7
    BH        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16177|23|0|8
    D         :    0.25 mm (0.00984 inch) non-oriented sheet || 16177|24|0|-1
    %El   (*):    0.25 mm (0.00984 inch) non-oriented sheet || in rolling direction || 16177|29|0|0
    HB        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16177|31|0|0
    HB        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16177|31|0|1
    HB        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16177|31|0|2
    HB        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16177|31|0|3
    HB        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16177|31|0|4
    HB        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16177|31|0|5
    HB        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16177|31|0|6
    HB        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16177|31|0|7
    HB        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16177|31|0|8
    CL        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16177|43|0|0
    CL        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16177|43|0|1
    CL        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16177|43|0|2
    CL        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16177|43|0|3
    CL        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16177|43|0|4
    CL        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16177|43|0|5
    CL        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16177|43|0|6
    CL        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16177|43|0|7
    CL        :    0.25 mm (0.00984 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16177|43|0|8

return to listing

Tata NO27-1400H electrical steel (New)

    DLL       :    0.27 mm (0.0106 inch) non-oriented sheet || 16178|0|0|-1
    TC    (*):    0.27 mm (0.0106 inch) non-oriented sheet || 16178|1|0|-1
    RHO   (*):    0.27 mm (0.0106 inch) non-oriented sheet || 16178|2|0|-1
    E     (*):    0.27 mm (0.0106 inch) non-oriented sheet || in rolling direction || 16178|3|0|0
    UTS   (*):    0.27 mm (0.0106 inch) non-oriented sheet || in rolling direction || 16178|5|0|0
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16178|7|0|0
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16178|7|0|1
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16178|7|0|2
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16178|7|0|3
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16178|7|0|4
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16178|7|0|5
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16178|7|0|6
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16178|7|0|7
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16178|7|0|8
    MTE       :    0.27 mm (0.0106 inch) non-oriented sheet || 16178|8|0|-1
    SIGMA (*):    0.27 mm (0.0106 inch) non-oriented sheet || 16178|10|0|-1
    YS    (*):    0.27 mm (0.0106 inch) non-oriented sheet || in rolling direction || 16178|13|0|0
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16178|15|0|0
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16178|15|0|1
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16178|15|0|2
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16178|15|0|3
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16178|15|0|4
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16178|15|0|5
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16178|15|0|6
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16178|15|0|7
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16178|15|0|8
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16178|23|0|0
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16178|23|0|1
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16178|23|0|2
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16178|23|0|3
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16178|23|0|4
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16178|23|0|5
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16178|23|0|6
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16178|23|0|7
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16178|23|0|8
    D         :    0.27 mm (0.0106 inch) non-oriented sheet || 16178|24|0|-1
    %El   (*):    0.27 mm (0.0106 inch) non-oriented sheet || in rolling direction || 16178|29|0|0
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16178|31|0|0
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16178|31|0|1
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16178|31|0|2
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16178|31|0|3
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16178|31|0|4
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16178|31|0|5
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16178|31|0|6
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16178|31|0|7
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16178|31|0|8
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16178|43|0|0
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16178|43|0|1
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16178|43|0|2
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16178|43|0|3
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16178|43|0|4
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16178|43|0|5
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16178|43|0|6
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16178|43|0|7
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16178|43|0|8

return to listing

Tata NO27-1450H electrical steel (New)

    DLL       :    0.27 mm (0.0106 inch) non-oriented sheet || 16179|0|0|-1
    TC    (*):    0.27 mm (0.0106 inch) non-oriented sheet || 16179|1|0|-1
    RHO   (*):    0.27 mm (0.0106 inch) non-oriented sheet || 16179|2|0|-1
    E     (*):    0.27 mm (0.0106 inch) non-oriented sheet || in rolling direction || 16179|3|0|0
    UTS   (*):    0.27 mm (0.0106 inch) non-oriented sheet || in rolling direction || 16179|5|0|0
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16179|7|0|0
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16179|7|0|1
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16179|7|0|2
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16179|7|0|3
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16179|7|0|4
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16179|7|0|5
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16179|7|0|6
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16179|7|0|7
    RPB       :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16179|7|0|8
    MTE       :    0.27 mm (0.0106 inch) non-oriented sheet || 16179|8|0|-1
    SIGMA (*):    0.27 mm (0.0106 inch) non-oriented sheet || 16179|10|0|-1
    YS    (*):    0.27 mm (0.0106 inch) non-oriented sheet || in rolling direction || 16179|13|0|0
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16179|15|0|0
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16179|15|0|1
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16179|15|0|2
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16179|15|0|3
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16179|15|0|4
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16179|15|0|5
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16179|15|0|6
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16179|15|0|7
    AP        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16179|15|0|8
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16179|23|0|0
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16179|23|0|1
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16179|23|0|2
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16179|23|0|3
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16179|23|0|4
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16179|23|0|5
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16179|23|0|6
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16179|23|0|7
    BH        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16179|23|0|8
    D         :    0.27 mm (0.0106 inch) non-oriented sheet || 16179|24|0|-1
    %El   (*):    0.27 mm (0.0106 inch) non-oriented sheet || in rolling direction || 16179|29|0|0
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16179|31|0|0
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16179|31|0|1
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16179|31|0|2
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16179|31|0|3
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16179|31|0|4
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16179|31|0|5
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16179|31|0|6
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16179|31|0|7
    HB        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16179|31|0|8
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16179|43|0|0
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16179|43|0|1
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16179|43|0|2
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16179|43|0|3
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16179|43|0|4
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16179|43|0|5
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16179|43|0|6
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16179|43|0|7
    CL        :    0.27 mm (0.0106 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16179|43|0|8

return to listing

Tata NO12-1180N electrical steel (New)

    DLL       :    0.12 mm (0.00472 inch) non-oriented sheet || 16170|0|0|-1
    TC    (*):    0.12 mm (0.00472 inch) non-oriented sheet || 16170|1|0|-1
    RHO   (*):    0.12 mm (0.00472 inch) non-oriented sheet || 16170|2|0|-1
    E     (*):    0.12 mm (0.00472 inch) non-oriented sheet || in rolling direction || 16170|3|0|0
    UTS   (*):    0.12 mm (0.00472 inch) non-oriented sheet || in rolling direction || 16170|5|0|0
    RPB       :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16170|7|0|0
    RPB       :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16170|7|0|1
    RPB       :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16170|7|0|2
    RPB       :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16170|7|0|3
    RPB       :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16170|7|0|4
    RPB       :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16170|7|0|5
    RPB       :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16170|7|0|6
    RPB       :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16170|7|0|7
    RPB       :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16170|7|0|8
    MTE       :    0.12 mm (0.00472 inch) non-oriented sheet || 16170|8|0|-1
    SIGMA (*):    0.12 mm (0.00472 inch) non-oriented sheet || 16170|10|0|-1
    YS    (*):    0.12 mm (0.00472 inch) non-oriented sheet || in rolling direction || 16170|13|0|0
    AP        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16170|15|0|0
    AP        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16170|15|0|1
    AP        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16170|15|0|2
    AP        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16170|15|0|3
    AP        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16170|15|0|4
    AP        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16170|15|0|5
    AP        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16170|15|0|6
    AP        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16170|15|0|7
    AP        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16170|15|0|8
    BH        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16170|23|0|0
    BH        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16170|23|0|1
    BH        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16170|23|0|2
    BH        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16170|23|0|3
    BH        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16170|23|0|4
    BH        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16170|23|0|5
    BH        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16170|23|0|6
    BH        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16170|23|0|7
    BH        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16170|23|0|8
    D         :    0.12 mm (0.00472 inch) non-oriented sheet || 16170|24|0|-1
    %El   (*):    0.12 mm (0.00472 inch) non-oriented sheet || in rolling direction || 16170|29|0|0
    HB        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16170|31|0|0
    HB        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16170|31|0|1
    HB        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16170|31|0|2
    HB        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16170|31|0|3
    HB        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16170|31|0|4
    HB        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16170|31|0|5
    HB        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16170|31|0|6
    HB        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16170|31|0|7
    HB        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16170|31|0|8
    CL        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16170|43|0|0
    CL        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16170|43|0|1
    CL        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16170|43|0|2
    CL        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16170|43|0|3
    CL        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16170|43|0|4
    CL        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16170|43|0|5
    CL        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16170|43|0|6
    CL        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16170|43|0|7
    CL        :    0.12 mm (0.00472 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16170|43|0|8

return to listing

Tata NO15-1230N electrical steel (New)

    DLL       :    0.15 mm (0.00591 inch) non-oriented sheet || 16171|0|0|-1
    TC    (*):    0.15 mm (0.00591 inch) non-oriented sheet || 16171|1|0|-1
    RHO   (*):    0.15 mm (0.00591 inch) non-oriented sheet || 16171|2|0|-1
    E     (*):    0.15 mm (0.00591 inch) non-oriented sheet || in rolling direction || 16171|3|0|0
    UTS   (*):    0.15 mm (0.00591 inch) non-oriented sheet || in rolling direction || 16171|5|0|0
    RPB       :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16171|7|0|0
    RPB       :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16171|7|0|1
    RPB       :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16171|7|0|2
    RPB       :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16171|7|0|3
    RPB       :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16171|7|0|4
    RPB       :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16171|7|0|5
    RPB       :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16171|7|0|6
    RPB       :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16171|7|0|7
    RPB       :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16171|7|0|8
    MTE       :    0.15 mm (0.00591 inch) non-oriented sheet || 16171|8|0|-1
    SIGMA (*):    0.15 mm (0.00591 inch) non-oriented sheet || 16171|10|0|-1
    YS    (*):    0.15 mm (0.00591 inch) non-oriented sheet || in rolling direction || 16171|13|0|0
    AP        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16171|15|0|0
    AP        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16171|15|0|1
    AP        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16171|15|0|2
    AP        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16171|15|0|3
    AP        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16171|15|0|4
    AP        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16171|15|0|5
    AP        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16171|15|0|6
    AP        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16171|15|0|7
    AP        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16171|15|0|8
    BH        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16171|23|0|0
    BH        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16171|23|0|1
    BH        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16171|23|0|2
    BH        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16171|23|0|3
    BH        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16171|23|0|4
    BH        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16171|23|0|5
    BH        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16171|23|0|6
    BH        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16171|23|0|7
    BH        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16171|23|0|8
    D         :    0.15 mm (0.00591 inch) non-oriented sheet || 16171|24|0|-1
    %El   (*):    0.15 mm (0.00591 inch) non-oriented sheet || in rolling direction || 16171|29|0|0
    HB        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16171|31|0|0
    HB        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16171|31|0|1
    HB        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16171|31|0|2
    HB        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16171|31|0|3
    HB        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16171|31|0|4
    HB        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16171|31|0|5
    HB        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16171|31|0|6
    HB        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16171|31|0|7
    HB        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16171|31|0|8
    CL        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16171|43|0|0
    CL        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16171|43|0|1
    CL        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16171|43|0|2
    CL        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16171|43|0|3
    CL        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16171|43|0|4
    CL        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16171|43|0|5
    CL        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16171|43|0|6
    CL        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16171|43|0|7
    CL        :    0.15 mm (0.00591 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16171|43|0|8

return to listing

Tata NO20-1350N electrical steel (New)

    DLL       :    0.2 mm (0.00787 inch) non-oriented sheet || 16176|0|0|-1
    TC    (*):    0.2 mm (0.00787 inch) non-oriented sheet || 16176|1|0|-1
    RHO   (*):    0.2 mm (0.00787 inch) non-oriented sheet || 16176|2|0|-1
    E     (*):    0.2 mm (0.00787 inch) non-oriented sheet || in rolling direction || 16176|3|0|0
    UTS   (*):    0.2 mm (0.00787 inch) non-oriented sheet || in rolling direction || 16176|5|0|0
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16176|7|0|0
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16176|7|0|1
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16176|7|0|2
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16176|7|0|3
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16176|7|0|4
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16176|7|0|5
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16176|7|0|6
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16176|7|0|7
    RPB       :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16176|7|0|8
    MTE       :    0.2 mm (0.00787 inch) non-oriented sheet || 16176|8|0|-1
    SIGMA (*):    0.2 mm (0.00787 inch) non-oriented sheet || 16176|10|0|-1
    YS    (*):    0.2 mm (0.00787 inch) non-oriented sheet || in rolling direction || 16176|13|0|0
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16176|15|0|0
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16176|15|0|1
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16176|15|0|2
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16176|15|0|3
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16176|15|0|4
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16176|15|0|5
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16176|15|0|6
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16176|15|0|7
    AP        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16176|15|0|8
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16176|23|0|0
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16176|23|0|1
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16176|23|0|2
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16176|23|0|3
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16176|23|0|4
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16176|23|0|5
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16176|23|0|6
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16176|23|0|7
    BH        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16176|23|0|8
    D         :    0.2 mm (0.00787 inch) non-oriented sheet || 16176|24|0|-1
    %El   (*):    0.2 mm (0.00787 inch) non-oriented sheet || in rolling direction || 16176|29|0|0
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16176|31|0|0
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16176|31|0|1
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16176|31|0|2
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16176|31|0|3
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16176|31|0|4
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16176|31|0|5
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16176|31|0|6
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16176|31|0|7
    HB        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16176|31|0|8
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16176|43|0|0
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16176|43|0|1
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16176|43|0|2
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16176|43|0|3
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16176|43|0|4
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16176|43|0|5
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16176|43|0|6
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16176|43|0|7
    CL        :    0.2 mm (0.00787 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16176|43|0|8

return to listing

Tata NO10-1270N electrical steel (New)

    DLL       :    0.1 mm (0.00394 inch) non-oriented sheet || 16169|0|0|-1
    TC    (*):    0.1 mm (0.00394 inch) non-oriented sheet || 16169|1|0|-1
    RHO   (*):    0.1 mm (0.00394 inch) non-oriented sheet || 16169|2|0|-1
    E     (*):    0.1 mm (0.00394 inch) non-oriented sheet || in rolling direction || 16169|3|0|0
    UTS   (*):    0.1 mm (0.00394 inch) non-oriented sheet || in rolling direction || 16169|5|0|0
    RPB       :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16169|7|0|0
    RPB       :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16169|7|0|1
    RPB       :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16169|7|0|2
    RPB       :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16169|7|0|3
    RPB       :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16169|7|0|4
    RPB       :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16169|7|0|5
    RPB       :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16169|7|0|6
    RPB       :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16169|7|0|7
    RPB       :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16169|7|0|8
    MTE       :    0.1 mm (0.00394 inch) non-oriented sheet || 16169|8|0|-1
    SIGMA (*):    0.1 mm (0.00394 inch) non-oriented sheet || 16169|10|0|-1
    YS    (*):    0.1 mm (0.00394 inch) non-oriented sheet || in rolling direction || 16169|13|0|0
    AP        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16169|15|0|0
    AP        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16169|15|0|1
    AP        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16169|15|0|2
    AP        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16169|15|0|3
    AP        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16169|15|0|4
    AP        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16169|15|0|5
    AP        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16169|15|0|6
    AP        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16169|15|0|7
    AP        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16169|15|0|8
    BH        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16169|23|0|0
    BH        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16169|23|0|1
    BH        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16169|23|0|2
    BH        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16169|23|0|3
    BH        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16169|23|0|4
    BH        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16169|23|0|5
    BH        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16169|23|0|6
    BH        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16169|23|0|7
    BH        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16169|23|0|8
    D         :    0.1 mm (0.00394 inch) non-oriented sheet || 16169|24|0|-1
    %El   (*):    0.1 mm (0.00394 inch) non-oriented sheet || in rolling direction || 16169|29|0|0
    HB        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16169|31|0|0
    HB        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16169|31|0|1
    HB        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16169|31|0|2
    HB        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16169|31|0|3
    HB        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16169|31|0|4
    HB        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16169|31|0|5
    HB        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16169|31|0|6
    HB        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16169|31|0|7
    HB        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16169|31|0|8
    CL        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16169|43|0|0
    CL        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16169|43|0|1
    CL        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16169|43|0|2
    CL        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16169|43|0|3
    CL        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16169|43|0|4
    CL        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16169|43|0|5
    CL        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16169|43|0|6
    CL        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16169|43|0|7
    CL        :    0.1 mm (0.00394 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16169|43|0|8

return to listing

Tata NO18-1280N electrical steel (New)

    DLL       :    0.18 mm (0.00709 inch) non-oriented sheet || 16173|0|0|-1
    TC    (*):    0.18 mm (0.00709 inch) non-oriented sheet || 16173|1|0|-1
    RHO   (*):    0.18 mm (0.00709 inch) non-oriented sheet || 16173|2|0|-1
    E     (*):    0.18 mm (0.00709 inch) non-oriented sheet || in rolling direction || 16173|3|0|0
    UTS   (*):    0.18 mm (0.00709 inch) non-oriented sheet || in rolling direction || 16173|5|0|0
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16173|7|0|0
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16173|7|0|1
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16173|7|0|2
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16173|7|0|3
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16173|7|0|4
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16173|7|0|5
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16173|7|0|6
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16173|7|0|7
    RPB       :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16173|7|0|8
    MTE       :    0.18 mm (0.00709 inch) non-oriented sheet || 16173|8|0|-1
    SIGMA (*):    0.18 mm (0.00709 inch) non-oriented sheet || 16173|10|0|-1
    YS    (*):    0.18 mm (0.00709 inch) non-oriented sheet || in rolling direction || 16173|13|0|0
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16173|15|0|0
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16173|15|0|1
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16173|15|0|2
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16173|15|0|3
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16173|15|0|4
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16173|15|0|5
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16173|15|0|6
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16173|15|0|7
    AP        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16173|15|0|8
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16173|23|0|0
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16173|23|0|1
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16173|23|0|2
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16173|23|0|3
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16173|23|0|4
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16173|23|0|5
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16173|23|0|6
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16173|23|0|7
    BH        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16173|23|0|8
    D         :    0.18 mm (0.00709 inch) non-oriented sheet || 16173|24|0|-1
    %El   (*):    0.18 mm (0.00709 inch) non-oriented sheet || in rolling direction || 16173|29|0|0
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16173|31|0|0
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16173|31|0|1
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16173|31|0|2
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16173|31|0|3
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16173|31|0|4
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16173|31|0|5
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16173|31|0|6
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16173|31|0|7
    HB        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16173|31|0|8
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 50 Hz || 16173|43|0|0
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 100 Hz || 16173|43|0|1
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 200 Hz || 16173|43|0|2
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 400 Hz || 16173|43|0|3
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 700 Hz || 16173|43|0|4
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 1 kHz || 16173|43|0|5
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 2.5 kHz || 16173|43|0|6
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 5 kHz || 16173|43|0|7
    CL        :    0.18 mm (0.00709 inch) non-oriented sheet || tested at 20 °C (68 °F), 10 kHz || 16173|43|0|8

return to listing

Tellurium

    RIW    (N):    measured in unknown ambient || tested at 23 °C (73 °F), parallel to c-axis || 886|45|0|0
    RIW    (N):    measured in unknown ambient || tested at 23 °C (73 °F), perpendicular to c-axis || 886|45|0|1

return to listing

Temperature compensator 32 (type 1)

    UTS   (N*):    annealed || 1641|5|0|-1
    YS    (N*):    annealed || 1641|13|0|-1
    %El   (N*):    annealed || 1641|29|0|-1

return to listing

Temperature compensator 30 (types 2, 3, 4)

    UTS   (N*):    annealed || 1642|5|0|-1
    YS    (N*):    annealed || 1642|13|0|-1
    %El   (N*):    annealed || 1642|29|0|-1

return to listing

Ti - 5 Al - 2.5 Sn (Grade 6)

    UTS    (R):    mill annealed || 9355|5|0|-1
    YS     (R):    mill annealed || 9355|13|0|-1
    %El    (R):    mill annealed || 9355|29|0|-1

return to listing

Ti - 3 Al - 2.5 V - 0.05 Pd (Grade 18)

    RHO   (N*):    solid || 9353|2|0|-1
    SIGMA (N*):    solid || 9353|10|0|-1

return to listing

Ti - 3 Al - 2.5 V (Grade 9)

    RHO   (N*):    solid || 9352|2|0|-1
    SIGMA (N*):    solid || 9352|10|0|-1

return to listing

Ti - 6 Al - 4 V

    RHO    (N):    solid || 1177 °C (2150 °F) and above || 2836|2|0|1
    SIGMA (N):    solid || 1177 °C (2150 °F) and above || 2836|10|0|1

return to listing

Ti - 16 V - 2.5 Al (wt %) (New)

    DLL       :    solution treated & aged sheet || 16212|0|0|-1
    TC        :    solution treated & aged sheet || 16212|1|0|-1
    E         :    solution treated & aged sheet || 16212|3|0|-1
    SSC       :    sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 20 °C (68 °F), 8.3 x 10^-⁴/s || 16212|4|0|0
    UTS       :    solution treated & aged sheet || 16212|5|0|-1
    FSN       :    sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 21 °C (70 °F), R = 0, axial, maximum stress || 16212|6|0|0
    FSN       :    sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 204 °C (400 °F), R = 0, axial, maximum stress || 16212|6|0|1
    FSN       :    sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 316 °C (600 °F), R = 0, axial, maximum stress || 16212|6|0|2
    FSN       :    sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 427 °C (800 °F), R = 0, axial, maximum stress || 16212|6|0|3
    FSN       :    sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 482 °C (900 °F), R = 0, axial, maximum stress || 16212|6|0|4
    MTE       :    solution treated & aged sheet || 16212|8|0|-1
    SH        :    solution treated & aged sheet || 16212|9|0|-1
    G         :    solution treated & aged sheet || 16212|11|0|-1
    YS        :    solution treated & aged sheet || 16212|13|0|-1
    CTE       :    solution treated & aged sheet || 16212|16|0|-1
    v         :    solution treated & aged sheet || 16212|19|0|-1
    SR        :    sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 371 °C (700 °F) || 16212|22|0|0
    SR        :    sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 427 °C (800 °F) || 16212|22|0|1
    SR        :    sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 482 °C (900 °F) || 16212|22|0|2
    SR        :    sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || Master curve (LMP) || 16212|22|0|3
    D         :    solution treated & aged sheet || 16212|24|0|-1
    TD        :    solution treated & aged sheet || 16212|25|0|-1
    K         :    solution treated & aged sheet || 16212|27|0|-1
    %El       :    solution treated & aged sheet || 16212|29|0|-1
    CRS       :    0.05% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 316 °C (600 °F) || 16212|30|0|0
    CRS       :    0.05% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 371 °C (700 °F) || 16212|30|0|1
    CRS       :    0.05% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 427 °C (800 °F) || 16212|30|0|2
    CRS       :    0.05% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || Master curve (LMP) || 16212|30|0|3
    CRS       :    0.1% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 316 °C (600 °F) || 16212|30|1|0
    CRS       :    0.1% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 371 °C (700 °F) || 16212|30|1|1
    CRS       :    0.1% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 427 °C (800 °F) || 16212|30|1|2
    CRS       :    0.1% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || Master curve (LMP) || 16212|30|1|3
    CRS       :    0.2% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 316 °C (600 °F) || 16212|30|2|0
    CRS       :    0.2% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 371 °C (700 °F) || 16212|30|2|1
    CRS       :    0.2% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 427 °C (800 °F) || 16212|30|2|2
    CRS       :    0.2% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || Master curve (LMP) || 16212|30|2|3
    CRS       :    0.5% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 316 °C (600 °F) || 16212|30|3|0
    CRS       :    0.5% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 371 °C (700 °F) || 16212|30|3|1
    CRS       :    0.5% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 427 °C (800 °F) || 16212|30|3|2
    CRS       :    0.5% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || Master curve (LMP) || 16212|30|3|3
    CRS       :    1% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 316 °C (600 °F) || 16212|30|4|0
    CRS       :    1% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 371 °C (700 °F) || 16212|30|4|1
    CRS       :    1% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || tested at 427 °C (800 °F) || 16212|30|4|2
    CRS       :    1% strain, sheet, 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || Master curve (LMP) || 16212|30|4|3
    IC        :    tested at 316 °C (600 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 0.1 h || 16212|39|0|0
    IC        :    tested at 316 °C (600 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 0.3 h || 16212|39|0|1
    IC        :    tested at 316 °C (600 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 1 h || 16212|39|0|2
    IC        :    tested at 316 °C (600 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 3 h || 16212|39|0|3
    IC        :    tested at 316 °C (600 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 10 h || 16212|39|0|4
    IC        :    tested at 316 °C (600 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 30 h || 16212|39|0|5
    IC        :    tested at 316 °C (600 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 100 h || 16212|39|0|6
    IC        :    tested at 316 °C (600 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 300 h || 16212|39|0|7
    IC        :    tested at 371 °C (700 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 0.1 h || 16212|39|1|0
    IC        :    tested at 371 °C (700 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 0.3 h || 16212|39|1|1
    IC        :    tested at 371 °C (700 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 1 h || 16212|39|1|2
    IC        :    tested at 371 °C (700 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 3 h || 16212|39|1|3
    IC        :    tested at 371 °C (700 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 10 h || 16212|39|1|4
    IC        :    tested at 371 °C (700 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 30 h || 16212|39|1|5
    IC        :    tested at 371 °C (700 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 100 h || 16212|39|1|6
    IC        :    tested at 371 °C (700 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 300 h || 16212|39|1|7
    IC        :    tested at 427 °C (800 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 0.3 h || 16212|39|2|1
    IC        :    tested at 427 °C (800 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 1 h || 16212|39|2|2
    IC        :    tested at 427 °C (800 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 3 h || 16212|39|2|3
    IC        :    tested at 427 °C (800 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 10 h || 16212|39|2|4
    IC        :    tested at 427 °C (800 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 30 h || 16212|39|2|5
    IC        :    tested at 427 °C (800 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 100 h || 16212|39|2|6
    IC        :    tested at 427 °C (800 °F), 1.6 mm (0.063 inch), tempered at 482 °C (900 °F) to 510 °C (950 °F) || 300 h || 16212|39|2|7

return to listing

Ti - 13 V - 11 Cr - 3 Al (wt %)

    DLL    (R):    solid || 2848|0|0|-1
    TC     (R):    solid || 2848|1|0|-1
    MTE    (R):    solid || 2848|8|0|-1
    SH     (R):    solid || 2848|9|0|-1
    CTE    (R):    solid || 2848|16|0|-1
    D      (R):    solid || 2848|24|0|-1
    TD     (R):    solid || 2848|25|0|-1

return to listing

Ti - 32.4 V (wt %) (New)

    ST        :    liquid || 16205|38|1|-1

return to listing

Ti - 13.2 V (wt %) (New)

    ST        :    liquid || 16203|38|1|-1

return to listing

Ti - 26.2 V (wt %) (New)

    ST        :    liquid || 16204|38|1|-1

return to listing

TiO₂ (rutile)

    RIW    (N):    measured in unknown ambient || tested at 23 °C (73 °F) || 2725|45|0|0

return to listing

TiSi₂

    RHO    (N):    solid || 2633|2|0|-1
    SIGMA (N):    solid || 2633|10|0|-1

return to listing

TiSi

    RHO    (N):    solid || 2632|2|0|-1
    SIGMA (N):    solid || 2632|10|0|-1

return to listing

40 TlBr - 60 TlCl (mol %)

    DLL    (N):    solid || 5972|0|0|-1
    TC    (N*):    solid || 5972|1|0|-1
    MTE    (N):    solid || 5972|8|0|-1
    CTE    (N):    solid || 5972|16|0|-1
    D      (N):    solid || 5972|24|0|-1
    RIW    (N):    measured in unknown ambient || tested at 23 °C (73 °F) || 5972|45|0|0

return to listing

42 TlBr - 58 TlI (mol %) (New)

    DLL       :    solid || 16268|0|0|-1
    TC    (*):    solid || 16268|1|0|-1
    MTE       :    solid || 16268|8|0|-1
    CTE       :    solid || 16268|16|0|-1
    D         :    solid || 16268|24|0|-1
    RIW       :    measured in unknown ambient || tested at 25 °C (77 °F) || 16268|45|0|0

return to listing

Tritan TX1001

    UTS   (N*):    ISO 527 || 3348|5|0|-1
    UTS   (N*):    ASTM D638 || 3348|5|1|-1
    YS    (N*):    ISO 527 || 3348|13|0|-1
    YS    (N*):    ASTM D638 || 3348|13|1|-1
    %El   (N*):    ISO 527 || at break || 3348|29|0|0
    %El   (N*):    ISO 527 || at yield || 3348|29|0|1
    %El   (N*):    ASTM D638 || at break || 3348|29|1|0
    %El   (N*):    ASTM D638 || at yield || 3348|29|1|1
    FS    (N*):    ISO 178 || at yield || 3348|33|0|0
    FS    (N*):    ASTM D790 || at yield || 3348|33|1|0

return to listing

UNS C96970

    TC    (N*):    solid || 3122|1|0|-1
    TD    (N*):    solid || 3122|25|0|-1

return to listing

UNS C17200

    FSN    (N):    AT || tested at 21 °C (70 °F), R = -1, flexure, maximum stress || 765|6|9|0
    FSN    (N):    AT || tested at -79 °C (-110 °F), R = -1, flexure, maximum stress || 765|6|9|1
    FSN    (N):    AT || tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress || 765|6|9|2
    FSN    (N):    AT || tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress || 765|6|9|3
    FSN    (N):    AT || tested at 21 °C (70 °F), R = -1, K_t = 3.2, flexure, maximum stress || 765|6|9|4
    FSN    (N):    AT || tested at -79 °C (-110 °F), R = -1, K_t = 3.2, flexure, maximum stress || 765|6|9|5
    FSN    (N):    AT || tested at -195.6 °C (-320 °F), R = -1, K_t = 3.2, flexure, maximum stress || 765|6|9|6
    FSN    (N):    AT || tested at -252.8 °C (-423 °F), R = -1, K_t = 3.2, flexure, maximum stress || 765|6|9|7
    FSN    (N):    1/2 HT || tested at 21 °C (70 °F), R = -1, flexure, maximum stress || 765|6|10|0
    FSN    (N):    1/2 HT || tested at -79 °C (-110 °F), R = -1, flexure, maximum stress || 765|6|10|1
    FSN    (N):    1/2 HT || tested at -195.6 °C (-320 °F), R = -1, flexure, maximum stress || 765|6|10|2
    FSN    (N):    1/2 HT || tested at -252.8 °C (-423 °F), R = -1, flexure, maximum stress || 765|6|10|3
    FSN    (N):    1/2 HT || tested at 21 °C (70 °F), R = -1, K_t = 3.1, flexure, maximum stress || 765|6|10|4
    FSN    (N):    1/2 HT || tested at -79 °C (-110 °F), R = -1, K_t = 3.1, flexure, maximum stress || 765|6|10|5
    FSN    (N):    1/2 HT || tested at -195.6 °C (-320 °F), R = -1, K_t = 3.1, flexure, maximum stress || 765|6|10|6
    FSN    (N):    1/2 HT || tested at -252.8 °C (-423 °F), R = -1, K_t = 3.1, flexure, maximum stress || 765|6|10|7
    FSN    (N):    1/2 HT || tested at 21 °C (70 °F), R = -1, K_t = 6.6, flexure, maximum stress || 765|6|10|8
    FSN    (N):    1/2 HT || tested at -79 °C (-110 °F), R = -1, K_t = 6.6, flexure, maximum stress || 765|6|10|9
    FSN    (N):    1/2 HT || tested at -195.6 °C (-320 °F), R = -1, K_t = 6.6, flexure, maximum stress || 765|6|10|10
    FSN    (N):    1/2 HT || tested at -252.8 °C (-423 °F), R = -1, K_t = 6.6, flexure, maximum stress || 765|6|10|11

return to listing

UNS C27400

    SSC    (N):    OS025 temper, 3 mm (0.118 inch) sheet || tested at 20 °C (68 °F), 0.013/s || 9684|4|0|0
    UTS   (N*):    3 mm (0.118 inch) sheet || OS025 temper || 9684|5|0|0
    YS    (N*):    3 mm (0.118 inch) sheet || OS025 temper || 9684|13|0|0
    %El   (N*):    3 mm (0.118 inch) sheet || OS025 temper || 9684|29|0|0

return to listing

UNS C70500 (New)

    DLL       :    solid || annealed || 16214|0|0|0
    TC    (*):    solid || 16214|1|0|-1
    RHO       :    solid || 16214|2|0|-1
    MTE       :    solid || annealed || 16214|8|0|0
    SH    (*):    solid || 16214|9|0|-1
    SIGMA    :    solid || 16214|10|0|-1
    CTE       :    solid || annealed || 16214|16|0|0
    D         :    solid || annealed || 16214|24|0|0
    TD    (*):    solid || 16214|25|0|-1

return to listing

UNS C71100 (New)

    DLL       :    solid || annealed || 16215|0|0|0
    TC    (*):    solid || 16215|1|0|-1
    RHO       :    solid || 16215|2|0|-1
    MTE       :    solid || annealed || 16215|8|0|0
    SH    (*):    solid || 16215|9|0|-1
    SIGMA    :    solid || 16215|10|0|-1
    CTE       :    solid || annealed || 16215|16|0|0
    D         :    solid || annealed || 16215|24|0|0
    TD    (*):    solid || 16215|25|0|-1

return to listing

UNS C72150 (New)

    DLL       :    solid || annealed || 16216|0|0|0
    TC    (*):    solid || 16216|1|0|-1
    RHO       :    solid || 16216|2|0|-1
    MTE       :    solid || annealed || 16216|8|0|0
    SH    (*):    solid || 16216|9|0|-1
    SIGMA    :    solid || 16216|10|0|-1
    CTE       :    solid || annealed || 16216|16|0|0
    D         :    solid || annealed || 16216|24|0|0
    TD    (*):    solid || 16216|25|0|-1

return to listing

V - 4.7 Ti (wt %)

    ST     (N):    liquid || 2346|38|1|-1

return to listing

V - 48.4 Ti (wt %) (New)

    ST        :    liquid || 16206|38|1|-1

return to listing

V - 11.8 Ti (wt %) (New)

    ST        :    liquid || 16209|38|1|-1

return to listing

V - 23.9 Ti (wt %) (New)

    ST        :    liquid || 16208|38|1|-1

return to listing

V - 36.1 Ti (wt %) (New)

    ST        :    liquid || 16207|38|1|-1

return to listing

Vanadium

    ST     (N):    liquid || 857|38|1|-1

return to listing

Vespel SP-21

    RHO   (N*):    solid || 2099|2|0|-1
    SIGMA (N*):    solid || 2099|10|0|-1

return to listing

WE43

    SSC    (N):    welded cast plates, T6 temper || tested at 20 °C (68 °F), 0.00159/s || 1712|4|0|0
    SSC    (N):    welded cast plates, T6 temper || tested at 100 °C (212 °F), 0.00159/s || 1712|4|0|1
    SSC    (N):    welded cast plates, T6 temper || tested at 150 °C (302 °F), 0.00159/s || 1712|4|0|2
    SSC    (N):    welded cast plates, T6 temper || tested at 200 °C (392 °F), 0.00159/s || 1712|4|0|3
    SSC    (N):    welded cast plates, T6 temper || tested at 250 °C (482 °F), 0.00159/s || 1712|4|0|4
    SSC    (N):    welded cast plates, T6 temper || tested at 300 °C (572 °F), 0.00159/s || 1712|4|0|5

return to listing

Wear Resistant HyMu 800A alloy

    TC    (N*):    solid || 1639|1|0|-1
    RPB    (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 60 Hz || 1639|7|0|0
    RPB    (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 1 kHz || 1639|7|0|1
    RPB    (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 10 kHz || 1639|7|0|2
    RPB    (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 100 kHz || 1639|7|0|3
    RPB    (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 1 MHz || 1639|7|0|4
    RPB    (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 60 Hz || 1639|7|1|0
    RPB    (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 1 kHz || 1639|7|1|1
    RPB    (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 10 kHz || 1639|7|1|2
    RPB    (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 100 kHz || 1639|7|1|3
    RPB    (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 1 MHz || 1639|7|1|4
    SH    (N*):    solid || 1639|9|0|-1
    AP     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 60 Hz || 1639|15|0|0
    AP     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 1 kHz || 1639|15|0|1
    AP     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 10 kHz || 1639|15|0|2
    AP     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 100 kHz || 1639|15|0|3
    AP     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 1 MHz || 1639|15|0|4
    AP     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 60 Hz || 1639|15|1|0
    AP     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 1 kHz || 1639|15|1|1
    AP     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 10 kHz || 1639|15|1|2
    AP     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 100 kHz || 1639|15|1|3
    AP     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 1 MHz || 1639|15|1|4
    BH     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 60 Hz || 1639|23|0|0
    BH     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 1 kHz || 1639|23|0|1
    BH     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 10 kHz || 1639|23|0|2
    BH     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 100 kHz || 1639|23|0|3
    BH     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 1 MHz || 1639|23|0|4
    BH     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 60 Hz || 1639|23|1|0
    BH     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 1 kHz || 1639|23|1|1
    BH     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 10 kHz || 1639|23|1|2
    BH     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 100 kHz || 1639|23|1|3
    BH     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 1 MHz || 1639|23|1|4
    TD    (N*):    solid || 1639|25|0|-1
    HB     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 60 Hz || 1639|31|0|0
    HB     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 1 kHz || 1639|31|0|1
    HB     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 10 kHz || 1639|31|0|2
    HB     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 100 kHz || 1639|31|0|3
    HB     (N):    as-supplied photoetch 0.0254 mm (0.001 inch) sheets || tested at 20 °C (68 °F), 1 MHz || 1639|31|0|4
    HB     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 60 Hz || 1639|31|1|0
    HB     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 1 kHz || 1639|31|1|1
    HB     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 10 kHz || 1639|31|1|2
    HB     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 100 kHz || 1639|31|1|3
    HB     (N):    as-supplied photoetch 0.0508 mm (0.002 inch) sheets || tested at 20 °C (68 °F), 1 MHz || 1639|31|1|4

return to listing

Y₃Al₅O₁₂ (YAG)

    SH     (R):    solid || 639|9|0|-1
    HC     (R):    solid || 639|17|0|-1
    TD     (R):    solid || 639|25|0|-1

return to listing

YVO₄

    TC     (N):    solid || polycrystal || 2166|1|0|0
    TC     (N):    solid || a-axis || 2166|1|0|1
    TC     (N):    solid || c-axis || 2166|1|0|2
    SH     (N):    solid || 2166|9|0|-1
    HC     (N):    solid || 2166|17|0|-1
    TD     (N):    solid || polycrystal || 2166|25|0|0
    TD     (N):    solid || a-axis || 2166|25|0|1
    TD     (N):    solid || c-axis || 2166|25|0|2

return to listing

Zinc

    SH     (R):    solid || 864|9|0|-1
    HC     (R):    solid || 864|17|0|-1
    TD     (R):    solid || annealed || 864|25|0|0

return to listing

80 ZrO₂ - 20 Al₂O₃ (wt %)

    ST     (N):    liquid || 15143|38|1|-1

return to listing

55 ZrO₂ - 45 Al₂O₃ (wt %)

    ST     (N):    liquid || 15141|38|1|-1

return to listing

ZrSi₂

    RHO    (N):    solid || 2644|2|0|-1
    SIGMA (N):    solid || 2644|10|0|-1

return to listing

Changes