Changes

New and revised materials and properties in MPDB v9.67 as compared to v9.65

Key to property symbols (number of datasets):

D = Density	DLL = Linear thermal expansion (dL/L)
MTE = Mean coefficient of thermal expansion	CTE = Coefficient of thermal expansion (CTE)
E = Elastic/Young's modulus	G = Shear modulus
v = Poisson's ratio	K = Bulk modulus
TC = Thermal conductivity	TD = Thermal diffusivity
SH = Specific heat	HC = Heat capacity
SSC = True stress-strain curve (tension)	SSCC = True stress-strain curve (compression)
UTS = Tensile strength	YS = Yield strength (tension)
UCS = Compressive strength	YSC = Yield strength (compression)
%El = Elongation	SR = Stress rupture
FEN = Fatigue e-N curve	FSN = Fatigue S-N curve
CRS = Creep strength	IC = Isochronous creep
HE = Hemispherical total emissivity	NE = Normal total emissivity
VP = Vapor pressure	Vis = Viscosity
ST = Surface tension	RHO = Electrical resistivity
SIGMA = Electrical conductivity	SV = Specific volume
AV = Apparent viscosity	FM = Flexural modulus
FS = Flexural strength	ESSC = Engineering stress-strain curve (tension)
ESSCC = Engineering stress-strain curve (compression)	CRM = Creep modulus
RPB = Relative permeability	AP = Absolute permeability
BH = B-H curve	HB = H-B curve
CL = Core loss	EP = Exciting Power
DCRPT = Relative permittivity	DF = Dissipation factor
RIW = Refractive index vs WL	RIT = Refractive index vs T
S = Seebeck coefficient

N indicates the data is new, R indicates the data has been revised, * indicates the data is the RT value only

24 new materials, 515 new property sets, 5 revised properties, and 46 new RT values

As₂S₃	Ba₈Ga₁₆Sn₃₀ (New)	BaFe₁₂O₁₉	BaSnO₃	Bi₀.₄₈Sb₁.₅₂Te₃ + x% PbTe (New)
Bi₂S₃	Bi₂Te₃ + NiTe composites (New)	Bi₂Te₃	Bi₂Te₃Cuₓ (Cu doped) (New)	Ca₀.₉Yb₀.₁MnO₃ (New)
CaCu₃Ti₄O₁₂ (New)	CeₓFe₃CoSb₁₂ (New)	CoSb₃ + PbTe composites	CoSb₃	Cu + carbon nanotubes (New)
Ingeo Grade 7000D (Revised)	Mg₂.₀₈Si₀.₄₋ₓSn₀.₆Sbₓ (New)	Mg₂Si₀.₂₅Sn₀.₇₅ (Na doped) (New)	PbTe (Bi and In doped) (New)	PbTe (Bi doped, nanostructured) (New)
PbTe (Ti doped) (New)	PbTe + x% CdSe (New)	PbTe + x% In₄SnSe₄ (New)	PbTe + x% InSe (New)	PbTe - 0.4% InSe + x% Sn (New)
PbTe	PLA Conductive (New)	PLA LAVA (New)	PLA Red (New)	PLA Super Blue (New)
PLA Tough White (New)	Sb₂S₃	Sn₁₇Zn₇P₂₂Br₈ (New)	Sn₂₄P₁₉.₃Br₈ (New)

As₂S₃

    Vis    (N):    liquid || 1538|26|1|-1

return to listing

Ba₈Ga₁₆Sn₃₀ (New)

    TC        :    crystals grown at 650 °C (1202 °F), Hong et. al. || 15581|1|0|-1
    TC        :    hot-pressed, Nolas et. al. || 15581|1|1|-1
    RHO       :    crystals grown at 650 °C (1202 °F), Hong et. al. || 15581|2|0|-1
    RHO       :    hot-pressed, Nolas et. al. || 15581|2|1|-1
    SIGMA    :    crystals grown at 650 °C (1202 °F), Hong et. al. || 15581|10|0|-1
    SIGMA    :    hot-pressed, Nolas et. al. || 15581|10|1|-1
    D     (*):    solid || 15581|24|0|-1
    S         :    crystals grown at 650 °C (1202 °F), Hong et. al. || 15581|48|0|-1
    S         :    hot-pressed, Nolas et. al. || 15581|48|1|-1

return to listing

BaFe₁₂O₁₉

    DLL    (N):    solid || polycrystal || 14640|0|0|0
    DLL    (N):    solid || a-axis || 14640|0|0|1
    DLL    (N):    solid || c-axis || 14640|0|0|2
    MTE    (N):    solid || polycrystal || 14640|8|0|0
    MTE    (N):    solid || a-axis || 14640|8|0|1
    MTE    (N):    solid || c-axis || 14640|8|0|2
    CTE    (N):    solid || polycrystal || 14640|16|0|0
    CTE    (N):    solid || a-axis || 14640|16|0|1
    CTE    (N):    solid || c-axis || 14640|16|0|2
    D      (N):    solid || 14640|24|0|-1
    DCRPT (N):    Polley et. al. || tested at 23 °C (73 °F), sintered 4 h at 1100 °C (2012 °F) || 14640|41|1|0
    DCRPT (N):    Polley et. al. || tested at 23 °C (73 °F), sintered 4 h at 1200 °C (2192 °F) || 14640|41|1|1
    DCRPT (N):    Polley et. al. || tested at 23 °C (73 °F), sintered 4 h at 1300 °C (2372 °F) || 14640|41|1|2
    DF     (N):    Polley et. al. || tested at 23 °C (73 °F), sintered 4 h at 1100 °C (2012 °F) || 14640|42|1|0
    DF     (N):    Polley et. al. || tested at 23 °C (73 °F), sintered 4 h at 1200 °C (2192 °F) || 14640|42|1|1
    DF     (N):    Polley et. al. || tested at 23 °C (73 °F), sintered 4 h at 1300 °C (2372 °F) || 14640|42|1|2

return to listing

BaSnO₃

    RHO    (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 1.02 x 10²¹/cm³, mobility = 63 cm²/(V-s) || 1279|2|0|0
    RHO    (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 9.24 x 10²⁰/cm³, mobility = 80 cm²/(V-s) || 1279|2|0|1
    RHO    (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 4.06 x 10²⁰/cm³, mobility = 120 cm²/(V-s) || 1279|2|0|2
    RHO    (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 2.53 x 10²⁰/cm³, mobility = 115 cm²/(V-s) || 1279|2|0|3
    RHO    (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 1.27 x 10²⁰/cm³, mobility = 118 cm²/(V-s) || 1279|2|0|4
    RHO    (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 6.64 x 10¹⁹/cm³, mobility = 112 cm²/(V-s) || 1279|2|0|5
    RHO    (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 4.2 x 10¹⁹/cm³, mobility = 100 cm²/(V-s) || 1279|2|0|6
    RHO    (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 1.51 x 10¹⁹/cm³, mobility = 27 cm²/(V-s) || 1279|2|0|7
    RHO    (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 5.48 x 10¹⁸/cm³, mobility = 1.90 cm²/(V-s) || 1279|2|0|8
    SIGMA (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 1.02 x 10²¹/cm³, mobility = 63 cm²/(V-s) || 1279|10|0|0
    SIGMA (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 9.24 x 10²⁰/cm³, mobility = 80 cm²/(V-s) || 1279|10|0|1
    SIGMA (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 4.06 x 10²⁰/cm³, mobility = 120 cm²/(V-s) || 1279|10|0|2
    SIGMA (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 2.53 x 10²⁰/cm³, mobility = 115 cm²/(V-s) || 1279|10|0|3
    SIGMA (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 1.27 x 10²⁰/cm³, mobility = 118 cm²/(V-s) || 1279|10|0|4
    SIGMA (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 6.64 x 10¹⁹/cm³, mobility = 112 cm²/(V-s) || 1279|10|0|5
    SIGMA (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 4.2 x 10¹⁹/cm³, mobility = 100 cm²/(V-s) || 1279|10|0|6
    SIGMA (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 1.51 x 10¹⁹/cm³, mobility = 27 cm²/(V-s) || 1279|10|0|7
    SIGMA (N):    Ba₁₋ₓLaₓSnO₃ / BaSnO₃ / SrTiO₃ heterostructures || carrier concentration = 5.48 x 10¹⁸/cm³, mobility = 1.90 cm²/(V-s) || 1279|10|0|8

return to listing

Bi₀.₄₈Sb₁.₅₂Te₃ + x% PbTe (New)

    TC        :    undoped || carrier concentration = 3.37 x 10¹⁹/cm³, mobility = 238 cm²/(V-s) || 15572|1|0|0
    TC        :    PbTe doped || 0.05 wt% PbTe, carrier concentration = 5.23 x 10¹⁹/cm³, mobility = 211 cm²/(V-s) || 15572|1|1|0
    TC        :    PbTe doped || 0.1 wt% PbTe, carrier concentration = 6.84 x 10¹⁹/cm³, mobility = 191 cm²/(V-s) || 15572|1|1|1
    TC        :    PbTe doped || 0.15 wt% PbTe, carrier concentration = 5.56 x 10¹⁹/cm³, mobility = 232 cm²/(V-s) || 15572|1|1|2
    RHO       :    undoped || carrier concentration = 3.37 x 10¹⁹/cm³, mobility = 238 cm²/(V-s) || 15572|2|0|0
    RHO       :    PbTe doped || 0.05 wt% PbTe, carrier concentration = 5.23 x 10¹⁹/cm³, mobility = 211 cm²/(V-s) || 15572|2|1|0
    RHO       :    PbTe doped || 0.1 wt% PbTe, carrier concentration = 6.84 x 10¹⁹/cm³, mobility = 191 cm²/(V-s) || 15572|2|1|1
    RHO       :    PbTe doped || 0.15 wt% PbTe, carrier concentration = 5.56 x 10¹⁹/cm³, mobility = 232 cm²/(V-s) || 15572|2|1|2
    SIGMA    :    undoped || carrier concentration = 3.37 x 10¹⁹/cm³, mobility = 238 cm²/(V-s) || 15572|10|0|0
    SIGMA    :    PbTe doped || 0.05 wt% PbTe, carrier concentration = 5.23 x 10¹⁹/cm³, mobility = 211 cm²/(V-s) || 15572|10|1|0
    SIGMA    :    PbTe doped || 0.1 wt% PbTe, carrier concentration = 6.84 x 10¹⁹/cm³, mobility = 191 cm²/(V-s) || 15572|10|1|1
    SIGMA    :    PbTe doped || 0.15 wt% PbTe, carrier concentration = 5.56 x 10¹⁹/cm³, mobility = 232 cm²/(V-s) || 15572|10|1|2
    S         :    undoped || carrier concentration = 3.37 x 10¹⁹/cm³, mobility = 238 cm²/(V-s) || 15572|48|0|0
    S         :    PbTe doped || 0.05 wt% PbTe, carrier concentration = 5.23 x 10¹⁹/cm³, mobility = 211 cm²/(V-s) || 15572|48|1|0
    S         :    PbTe doped || 0.1 wt% PbTe, carrier concentration = 6.84 x 10¹⁹/cm³, mobility = 191 cm²/(V-s) || 15572|48|1|1
    S         :    PbTe doped || 0.15 wt% PbTe, carrier concentration = 5.56 x 10¹⁹/cm³, mobility = 232 cm²/(V-s) || 15572|48|1|2

return to listing

Bi₂S₃

    TC     (N):    solid || hot-pressed || 3548|1|0|0
    RHO    (N):    solid || hot-pressed || 3548|2|0|0
    SIGMA (N):    solid || hot-pressed || 3548|10|0|0
    TD    (N*):    solid || 3548|25|0|-1
    S      (N):    solid || hot-pressed || 3548|48|0|0

return to listing

Bi₂Te₃ + NiTe composites (New)

    TC        :    NiTe composite || 1 vol% NiTe, parallel to pressing direction, carrier concentration = 5.52 x 10¹⁹/cm³, mobility = 239 cm²/(V-s) || 15567|1|0|0
    TC        :    NiTe composite || 2 vol% NiTe, parallel to pressing direction, carrier concentration = 5.8 x 10¹⁸/cm³, mobility = 150 cm²/(V-s) || 15567|1|0|1
    TC        :    NiTe composite || 3 vol% NiTe, parallel to pressing direction, carrier concentration = 1.6 x 10¹⁹/cm³, mobility = 188 cm²/(V-s) || 15567|1|0|2
    TC        :    NiTe composite || 5 vol% NiTe, parallel to pressing direction, carrier concentration = 1.19 x 10¹⁹/cm³, mobility = 142 cm²/(V-s) || 15567|1|0|3
    TC        :    NiTe composite || 1 vol% NiTe, perpendicular to pressing direction, carrier concentration = 5.52 x 10¹⁹/cm³, mobility = 239 cm²/(V-s) || 15567|1|0|4
    TC        :    NiTe composite || 2 vol% NiTe, perpendicular to pressing direction, carrier concentration = 5.8 x 10¹⁸/cm³, mobility = 150 cm²/(V-s) || 15567|1|0|5
    TC        :    NiTe composite || 3 vol% NiTe, perpendicular to pressing direction, carrier concentration = 1.6 x 10¹⁹/cm³, mobility = 188 cm²/(V-s) || 15567|1|0|6
    TC        :    NiTe composite || 5 vol% NiTe, perpendicular to pressing direction, carrier concentration = 1.19 x 10¹⁹/cm³, mobility = 142 cm²/(V-s) || 15567|1|0|7
    TC        :    NiTe composite || 1 vol% NiTe, average, carrier concentration = 5.52 x 10¹⁹/cm³, mobility = 239 cm²/(V-s) || 15567|1|0|8
    TC        :    NiTe composite || 2 vol% NiTe, average, carrier concentration = 5.8 x 10¹⁸/cm³, mobility = 150 cm²/(V-s) || 15567|1|0|9
    TC        :    NiTe composite || 3 vol% NiTe, average, carrier concentration = 1.6 x 10¹⁹/cm³, mobility = 188 cm²/(V-s) || 15567|1|0|10
    TC        :    NiTe composite || 5 vol% NiTe, average, carrier concentration = 1.19 x 10¹⁹/cm³, mobility = 142 cm²/(V-s) || 15567|1|0|11
    RHO       :    pure material || carrier concentration = 9.85 x 10¹⁹/cm³, mobility = 93 cm²/(V-s) || 15567|2|0|0
    RHO       :    NiTe composite || 1 vol% NiTe, carrier concentration = 5.52 x 10¹⁹/cm³, mobility = 239 cm²/(V-s) || 15567|2|1|0
    RHO       :    NiTe composite || 2 vol% NiTe, carrier concentration = 5.8 x 10¹⁸/cm³, mobility = 150 cm²/(V-s) || 15567|2|1|1
    RHO       :    NiTe composite || 3 vol% NiTe, carrier concentration = 1.6 x 10¹⁹/cm³, mobility = 188 cm²/(V-s) || 15567|2|1|2
    RHO       :    NiTe composite || 5 vol% NiTe, carrier concentration = 1.19 x 10¹⁹/cm³, mobility = 142 cm²/(V-s) || 15567|2|1|3
    RHO       :    NiTe composite || 5 vol% NiTe (solvothermal), carrier concentration = 9.85 x 10¹⁹/cm³, mobility = 93 cm²/(V-s) || 15567|2|1|4
    SIGMA    :    pure material || carrier concentration = 9.85 x 10¹⁹/cm³, mobility = 93 cm²/(V-s) || 15567|10|0|0
    SIGMA    :    NiTe composite || 1 vol% NiTe, carrier concentration = 5.52 x 10¹⁹/cm³, mobility = 239 cm²/(V-s) || 15567|10|1|0
    SIGMA    :    NiTe composite || 2 vol% NiTe, carrier concentration = 5.8 x 10¹⁸/cm³, mobility = 150 cm²/(V-s) || 15567|10|1|1
    SIGMA    :    NiTe composite || 3 vol% NiTe, carrier concentration = 1.6 x 10¹⁹/cm³, mobility = 188 cm²/(V-s) || 15567|10|1|2
    SIGMA    :    NiTe composite || 5 vol% NiTe, carrier concentration = 1.19 x 10¹⁹/cm³, mobility = 142 cm²/(V-s) || 15567|10|1|3
    SIGMA    :    NiTe composite || 5 vol% NiTe (solvothermal), carrier concentration = 9.85 x 10¹⁹/cm³, mobility = 93 cm²/(V-s) || 15567|10|1|4
    S         :    pure material || carrier concentration = 9.85 x 10¹⁹/cm³, mobility = 93 cm²/(V-s) || 15567|48|0|0
    S         :    NiTe composite || 1 vol% NiTe, carrier concentration = 5.52 x 10¹⁹/cm³, mobility = 239 cm²/(V-s) || 15567|48|1|0
    S         :    NiTe composite || 2 vol% NiTe, carrier concentration = 5.8 x 10¹⁸/cm³, mobility = 150 cm²/(V-s) || 15567|48|1|1
    S         :    NiTe composite || 3 vol% NiTe, carrier concentration = 1.6 x 10¹⁹/cm³, mobility = 188 cm²/(V-s) || 15567|48|1|2
    S         :    NiTe composite || 5 vol% NiTe, carrier concentration = 1.19 x 10¹⁹/cm³, mobility = 142 cm²/(V-s) || 15567|48|1|3
    S         :    NiTe composite || 5 vol% NiTe (solvothermal) || 15567|48|1|4

return to listing

Bi₂Te₃

    TC     (N):    polycrystal || Chen et. al., carrier concentration = 5.34 x 10¹⁹/cm³, mobility = 117 cm²/(V-s) || 3284|1|0|9
    RHO    (N):    bulk material || Sumithra et. al., carrier concentration = 9.85 x 10¹⁹/cm³, mobility = 93 cm²/(V-s) || 3284|2|0|8
    RHO    (N):    bulk material || Chen et. al., carrier concentration = 5.34 x 10¹⁹/cm³, mobility = 117 cm²/(V-s) || 3284|2|0|9
    SIGMA (N):    bulk material || Sumithra et. al., carrier concentration = 9.85 x 10¹⁹/cm³, mobility = 93 cm²/(V-s) || 3284|10|0|8
    SIGMA (N):    bulk material || Chen et. al., carrier concentration = 5.34 x 10¹⁹/cm³, mobility = 117 cm²/(V-s) || 3284|10|0|9
    S      (N):    bulk material || Sumithra et. al., carrier concentration = 9.85 x 10¹⁹/cm³, mobility = 93 cm²/(V-s) || 3284|48|0|8
    S      (N):    bulk material || Chen et. al., carrier concentration = 5.34 x 10¹⁹/cm³, mobility = 117 cm²/(V-s) || 3284|48|0|9

return to listing

Bi₂Te₃Cuₓ (Cu doped) (New)

    TC        :    undoped || carrier concentration = 5.34 x 10¹⁹/cm³, mobility = 117 cm²/(V-s) || 15574|1|0|0
    TC        :    Cu doped || x = 0.01, carrier concentration = 4.5 x 10¹⁸/cm³, mobility = 337 cm²/(V-s) || 15574|1|1|0
    TC        :    Cu doped || x = 0.025, carrier concentration = 6.7 x 10¹⁸/cm³, mobility = 147 cm²/(V-s) || 15574|1|1|1
    TC        :    Cu doped || x = 0.05, carrier concentration = 9.5 x 10¹⁸/cm³, mobility = 188 cm²/(V-s) || 15574|1|1|2
    RHO       :    undoped || carrier concentration = 5.34 x 10¹⁹/cm³, mobility = 117 cm²/(V-s) || 15574|2|0|0
    RHO       :    Cu doped || x = 0.01, carrier concentration = 4.5 x 10¹⁸/cm³, mobility = 337 cm²/(V-s) || 15574|2|1|0
    RHO       :    Cu doped || x = 0.025, carrier concentration = 6.7 x 10¹⁸/cm³, mobility = 147 cm²/(V-s) || 15574|2|1|1
    RHO       :    Cu doped || x = 0.05, carrier concentration = 9.5 x 10¹⁸/cm³, mobility = 188 cm²/(V-s) || 15574|2|1|2
    SIGMA    :    undoped || carrier concentration = 5.34 x 10¹⁹/cm³, mobility = 117 cm²/(V-s) || 15574|10|0|0
    SIGMA    :    Cu doped || x = 0.01, carrier concentration = 4.5 x 10¹⁸/cm³, mobility = 337 cm²/(V-s) || 15574|10|1|0
    SIGMA    :    Cu doped || x = 0.025, carrier concentration = 6.7 x 10¹⁸/cm³, mobility = 147 cm²/(V-s) || 15574|10|1|1
    SIGMA    :    Cu doped || x = 0.05, carrier concentration = 9.5 x 10¹⁸/cm³, mobility = 188 cm²/(V-s) || 15574|10|1|2
    S         :    undoped || carrier concentration = 5.34 x 10¹⁹/cm³, mobility = 117 cm²/(V-s) || 15574|48|0|0
    S         :    Cu doped || x = 0.01, carrier concentration = 4.5 x 10¹⁸/cm³, mobility = 337 cm²/(V-s) || 15574|48|1|0
    S         :    Cu doped || x = 0.025, carrier concentration = 6.7 x 10¹⁸/cm³, mobility = 147 cm²/(V-s) || 15574|48|1|1
    S         :    Cu doped || x = 0.05, carrier concentration = 9.5 x 10¹⁸/cm³, mobility = 188 cm²/(V-s) || 15574|48|1|2

return to listing

Ca₀.₉Yb₀.₁MnO₃ (New)

    TC        :    air sintered || 100 wt% nanoparticles || 15575|1|0|0
    TC        :    air sintered || 75 wt% nanoparticles / 25 wt% microparticles || 15575|1|0|1
    TC        :    air sintered || 50 wt% nanoparticles / 50 wt% microparticles || 15575|1|0|2
    TC        :    air sintered || 25 wt% nanoparticles / 75 wt% microparticles || 15575|1|0|3
    TC        :    air sintered || 100 wt% microparticles || 15575|1|0|4
    RHO       :    air sintered || 100 wt% nanoparticles || 15575|2|0|0
    RHO       :    air sintered || 75 wt% nanoparticles / 25 wt% microparticles || 15575|2|0|1
    RHO       :    air sintered || 50 wt% nanoparticles / 50 wt% microparticles || 15575|2|0|2
    RHO       :    air sintered || 25 wt% nanoparticles / 75 wt% microparticles || 15575|2|0|3
    RHO       :    air sintered || 100 wt% microparticles || 15575|2|0|4
    SIGMA    :    air sintered || 100 wt% nanoparticles || 15575|10|0|0
    SIGMA    :    air sintered || 75 wt% nanoparticles / 25 wt% microparticles || 15575|10|0|1
    SIGMA    :    air sintered || 50 wt% nanoparticles / 50 wt% microparticles || 15575|10|0|2
    SIGMA    :    air sintered || 25 wt% nanoparticles / 75 wt% microparticles || 15575|10|0|3
    SIGMA    :    air sintered || 100 wt% microparticles || 15575|10|0|4
    D     (*):    solid || 15575|24|0|-1
    S         :    air sintered || 100 wt% nanoparticles || 15575|48|0|0
    S         :    air sintered || 75 wt% nanoparticles / 25 wt% microparticles || 15575|48|0|1
    S         :    air sintered || 50 wt% nanoparticles / 50 wt% microparticles || 15575|48|0|2
    S         :    air sintered || 25 wt% nanoparticles / 75 wt% microparticles || 15575|48|0|3
    S         :    air sintered || 100 wt% microparticles || 15575|48|0|4

return to listing

CaCu₃Ti₄O₁₂ (New)

    TC        :    sintered at 1080 °C (1976 °F) || 15577|1|0|-1
    RHO       :    sintered at 1050 °C (1922 °F) || 15577|2|0|-1
    RHO       :    sintered at 1080 °C (1976 °F) || 15577|2|1|-1
    RHO       :    sintered at 1120 °C (2048 °F) || 15577|2|2|-1
    SIGMA    :    sintered at 1050 °C (1922 °F) || 15577|10|0|-1
    SIGMA    :    sintered at 1080 °C (1976 °F) || 15577|10|1|-1
    SIGMA    :    sintered at 1120 °C (2048 °F) || 15577|10|2|-1
    S         :    sintered at 1050 °C (1922 °F) || 15577|48|0|-1
    S         :    sintered at 1080 °C (1976 °F) || 15577|48|1|-1
    S         :    sintered at 1120 °C (2048 °F) || 15577|48|2|-1

return to listing

CeₓFe₃CoSb₁₂ (New)

    TC        :    x = 0.6 || 15579|1|0|-1
    TC        :    x = 0.7 || 15579|1|1|-1
    TC        :    x = 0.8 || 15579|1|2|-1
    TC        :    x = 0.9 || 15579|1|3|-1
    TC        :    x = 1.0 || 15579|1|4|-1
    RHO       :    x = 0.6 || 15579|2|0|-1
    RHO       :    x = 0.7 || 15579|2|1|-1
    RHO       :    x = 0.8 || 15579|2|2|-1
    RHO       :    x = 0.9 || 15579|2|3|-1
    RHO       :    x = 1.0 || 15579|2|4|-1
    SIGMA    :    x = 0.6 || 15579|10|0|-1
    SIGMA    :    x = 0.7 || 15579|10|1|-1
    SIGMA    :    x = 0.8 || 15579|10|2|-1
    SIGMA    :    x = 0.9 || 15579|10|3|-1
    SIGMA    :    x = 1.0 || 15579|10|4|-1
    S         :    x = 0.6 || 15579|48|0|-1
    S         :    x = 0.7 || 15579|48|1|-1
    S         :    x = 0.8 || 15579|48|2|-1
    S         :    x = 0.9 || 15579|48|3|-1
    S         :    x = 1.0 || 15579|48|4|-1

return to listing

CoSb₃ + PbTe composites

    S      (N):    PbTe composite || 0 wt% PbTe || 15421|48|0|0

return to listing

CoSb₃

    S      (N):    spark plasma sintered || > 98% dense || 1620|48|1|0

return to listing

Cu + carbon nanotubes (New)

    DLL       :    solid || 2.9 carbon nanotubes, 0.716 Ni (wt%) || 15584|0|0|0
    DLL       :    solid || 3 carbon nanotubes, 0.007 Ni (wt%) || 15584|0|0|1
    TC        :    solid || 2.9 carbon nanotubes, 0.716 Ni (wt%) || 15584|1|0|0
    TC        :    solid || 3 carbon nanotubes, 0.007 Ni (wt%) || 15584|1|0|1
    E     (*):    solid || 2.9 carbon nanotubes, 0.716 Ni (wt%) || 15584|3|0|0
    E     (*):    solid || 3 carbon nanotubes, 0.007 Ni (wt%) || 15584|3|0|1
    UTS   (*):    solid || 2.9 carbon nanotubes, 0.716 Ni (wt%) || 15584|5|0|0
    UTS   (*):    solid || 3 carbon nanotubes, 0.007 Ni (wt%) || 15584|5|0|1
    MTE       :    solid || 2.9 carbon nanotubes, 0.716 Ni (wt%) || 15584|8|0|0
    MTE       :    solid || 3 carbon nanotubes, 0.007 Ni (wt%) || 15584|8|0|1
    D         :    solid || 2.9 carbon nanotubes, 0.716 Ni (wt%) || 15584|24|0|0
    D         :    solid || 3 carbon nanotubes, 0.007 Ni (wt%) || 15584|24|0|1
    %El   (*):    solid || 2.9 carbon nanotubes, 0.716 Ni (wt%) || 15584|29|0|0
    %El   (*):    solid || 3 carbon nanotubes, 0.007 Ni (wt%) || 15584|29|0|1

return to listing

Ingeo Grade 7000D

    DLL    (R):    solid || 9781|0|0|-1
    TC     (R):    solid || 9781|1|0|-1
    MTE    (R):    solid || 9781|8|0|-1
    CTE    (R):    solid || 9781|16|0|-1
    D      (R):    solid || 9781|24|0|-1
    TD     (N):    solid || 9781|25|0|-1

return to listing

Mg₂.₀₈Si₀.₄₋ₓSn₀.₆Sbₓ (New)

    DLL       :    solid || 15580|0|0|-1
    TC        :    x = 0, carrier concentration = 4.9 x 10¹⁸/cm³, mobility = 60 cm²/(V-s) || 15580|1|0|-1
    TC        :    x = 0.012, carrier concentration = 4.1 x 10¹⁹/cm³, mobility = 45 cm²/(V-s) || 15580|1|1|-1
    TC        :    x = 0.024, carrier concentration = 2.1 x 10¹⁹/cm³, mobility = 18 cm²/(V-s) || 15580|1|2|-1
    TC        :    x = 0.036, carrier concentration = 2.5 x 10²⁰/cm³, mobility = 42 cm²/(V-s) || 15580|1|3|-1
    TC        :    x = 0.048 || 15580|1|4|-1
    TC        :    x = 0.06 || 15580|1|5|-1
    TC        :    x = 0.072 || 15580|1|6|-1
    RHO       :    x = 0, carrier concentration = 4.9 x 10¹⁸/cm³, mobility = 60 cm²/(V-s) || 15580|2|0|-1
    RHO       :    x = 0.012, carrier concentration = 4.1 x 10¹⁹/cm³, mobility = 45 cm²/(V-s) || 15580|2|1|-1
    RHO       :    x = 0.024, carrier concentration = 2.1 x 10¹⁹/cm³, mobility = 18 cm²/(V-s) || 15580|2|2|-1
    RHO       :    x = 0.036, carrier concentration = 2.5 x 10²⁰/cm³, mobility = 42 cm²/(V-s) || 15580|2|3|-1
    RHO       :    x = 0.048 || 15580|2|4|-1
    RHO       :    x = 0.06 || 15580|2|5|-1
    RHO       :    x = 0.072 || 15580|2|6|-1
    E         :    x = 0 || 15580|3|0|-1
    MTE       :    solid || 15580|8|0|-1
    SH        :    x = 0, carrier concentration = 4.9 x 10¹⁸/cm³, mobility = 60 cm²/(V-s) || 15580|9|0|-1
    SH        :    x = 0.012, carrier concentration = 4.1 x 10¹⁹/cm³, mobility = 45 cm²/(V-s) || 15580|9|1|-1
    SH        :    x = 0.024, carrier concentration = 2.1 x 10¹⁹/cm³, mobility = 18 cm²/(V-s) || 15580|9|2|-1
    SH        :    x = 0.036, carrier concentration = 2.5 x 10²⁰/cm³, mobility = 42 cm²/(V-s) || 15580|9|3|-1
    SH        :    x = 0.048 || 15580|9|4|-1
    SH        :    x = 0.06 || 15580|9|5|-1
    SH        :    x = 0.072 || 15580|9|6|-1
    SIGMA    :    x = 0, carrier concentration = 4.9 x 10¹⁸/cm³, mobility = 60 cm²/(V-s) || 15580|10|0|-1
    SIGMA    :    x = 0.012, carrier concentration = 4.1 x 10¹⁹/cm³, mobility = 45 cm²/(V-s) || 15580|10|1|-1
    SIGMA    :    x = 0.024, carrier concentration = 2.1 x 10¹⁹/cm³, mobility = 18 cm²/(V-s) || 15580|10|2|-1
    SIGMA    :    x = 0.036, carrier concentration = 2.5 x 10²⁰/cm³, mobility = 42 cm²/(V-s) || 15580|10|3|-1
    SIGMA    :    x = 0.048 || 15580|10|4|-1
    SIGMA    :    x = 0.06 || 15580|10|5|-1
    SIGMA    :    x = 0.072 || 15580|10|6|-1
    G         :    x = 0 || 15580|11|0|-1
    CTE       :    solid || 15580|16|0|-1
    v         :    x = 0 || 15580|19|0|-1
    D         :    solid || 15580|24|0|-1
    TD        :    x = 0, carrier concentration = 4.9 x 10¹⁸/cm³, mobility = 60 cm²/(V-s) || 15580|25|0|-1
    TD        :    x = 0.012, carrier concentration = 4.1 x 10¹⁹/cm³, mobility = 45 cm²/(V-s) || 15580|25|1|-1
    TD        :    x = 0.024, carrier concentration = 2.1 x 10¹⁹/cm³, mobility = 18 cm²/(V-s) || 15580|25|2|-1
    TD        :    x = 0.036, carrier concentration = 2.5 x 10²⁰/cm³, mobility = 42 cm²/(V-s) || 15580|25|3|-1
    TD        :    x = 0.048 || 15580|25|4|-1
    TD        :    x = 0.06 || 15580|25|5|-1
    TD        :    x = 0.072 || 15580|25|6|-1
    K         :    x = 0 || 15580|27|0|-1
    S         :    x = 0, carrier concentration = 4.9 x 10¹⁸/cm³, mobility = 60 cm²/(V-s) || 15580|48|0|-1
    S         :    x = 0.012, carrier concentration = 4.1 x 10¹⁹/cm³, mobility = 45 cm²/(V-s) || 15580|48|1|-1
    S         :    x = 0.024, carrier concentration = 2.1 x 10¹⁹/cm³, mobility = 18 cm²/(V-s) || 15580|48|2|-1
    S         :    x = 0.036, carrier concentration = 2.5 x 10²⁰/cm³, mobility = 42 cm²/(V-s) || 15580|48|3|-1
    S         :    x = 0.048 || 15580|48|4|-1
    S         :    x = 0.06 || 15580|48|5|-1
    S         :    x = 0.072 || 15580|48|6|-1

return to listing

Mg₂Si₀.₂₅Sn₀.₇₅ (Na doped) (New)

    TC        :    Na doped || 0.02 Na as acetate, carrier concentration = 8.01 x 10¹⁸/cm³, mobility = 133 cm²/(V-s) || 15576|1|0|0
    TC        :    Na doped || 0.025 Na as acetate, carrier concentration = 1.84 x 10¹⁹/cm³, mobility = 68.2 cm²/(V-s) || 15576|1|0|1
    TC        :    Na doped || 0.03 Na as acetate, carrier concentration = 2.1 x 10¹⁹/cm³, mobility = 67 cm²/(V-s) || 15576|1|0|2
    TC        :    Na doped || 0.02 metallic Na, carrier concentration = 1.22 x 10¹⁹/cm³, mobility = 46.8 cm²/(V-s) || 15576|1|0|3
    RHO       :    Na doped || 0.02 Na as acetate, carrier concentration = 8.01 x 10¹⁸/cm³, mobility = 133 cm²/(V-s) || 15576|2|0|0
    RHO       :    Na doped || 0.025 Na as acetate, carrier concentration = 1.84 x 10¹⁹/cm³, mobility = 68.2 cm²/(V-s) || 15576|2|0|1
    RHO       :    Na doped || 0.03 Na as acetate, carrier concentration = 2.1 x 10¹⁹/cm³, mobility = 67 cm²/(V-s) || 15576|2|0|2
    RHO       :    Na doped || 0.02 metallic Na, carrier concentration = 1.22 x 10¹⁹/cm³, mobility = 46.8 cm²/(V-s) || 15576|2|0|3
    SIGMA    :    Na doped || 0.02 Na as acetate, carrier concentration = 8.01 x 10¹⁸/cm³, mobility = 133 cm²/(V-s) || 15576|10|0|0
    SIGMA    :    Na doped || 0.025 Na as acetate, carrier concentration = 1.84 x 10¹⁹/cm³, mobility = 68.2 cm²/(V-s) || 15576|10|0|1
    SIGMA    :    Na doped || 0.03 Na as acetate, carrier concentration = 2.1 x 10¹⁹/cm³, mobility = 67 cm²/(V-s) || 15576|10|0|2
    SIGMA    :    Na doped || 0.02 metallic Na, carrier concentration = 1.22 x 10¹⁹/cm³, mobility = 46.8 cm²/(V-s) || 15576|10|0|3
    S         :    Na doped || 0.02 Na as acetate, carrier concentration = 8.01 x 10¹⁸/cm³, mobility = 133 cm²/(V-s) || 15576|48|0|0
    S         :    Na doped || 0.025 Na as acetate, carrier concentration = 1.84 x 10¹⁹/cm³, mobility = 68.2 cm²/(V-s) || 15576|48|0|1
    S         :    Na doped || 0.03 Na as acetate, carrier concentration = 2.1 x 10¹⁹/cm³, mobility = 67 cm²/(V-s) || 15576|48|0|2
    S         :    Na doped || 0.02 metallic Na, carrier concentration = 1.22 x 10¹⁹/cm³, mobility = 46.8 cm²/(V-s) || 15576|48|0|3

return to listing

PbTe (Bi and In doped) (New)

    TC        :    undoped || cast || 9326|1|0|0
    TC        :    In doped || 3 at% In || 9326|1|1|0
    TC        :    In doped || 5 at% In || 9326|1|1|1
    TC        :    In doped || 7 at% In || 9326|1|1|2
    TC        :    In doped || 9 at% In || 9326|1|1|3
    TC        :    Bi & In co-doped || 1 at% Bi + 1 at% In || 9326|1|2|0
    TC        :    Bi & In co-doped || 1.5 at% Bi + 3 at% In || 9326|1|2|1
    TC        :    Bi & In co-doped || 3 at% Bi + 5 at% In || 9326|1|2|2
    TC        :    Bi & In co-doped || 1 at% Bi + 5 at% In || 9326|1|2|3
    TC        :    Bi & In co-doped || 3 at% Bi + 1 at% In || 9326|1|2|4
    RHO       :    undoped || cast || 9326|2|0|0
    RHO       :    In doped || 3 at% In || 9326|2|1|0
    RHO       :    In doped || 5 at% In || 9326|2|1|1
    RHO       :    In doped || 7 at% In || 9326|2|1|2
    RHO       :    In doped || 9 at% In || 9326|2|1|3
    RHO       :    Bi & In co-doped || 1 at% Bi + 1 at% In || 9326|2|2|0
    RHO       :    Bi & In co-doped || 1.5 at% Bi + 3 at% In || 9326|2|2|1
    RHO       :    Bi & In co-doped || 3 at% Bi + 5 at% In || 9326|2|2|2
    RHO       :    Bi & In co-doped || 1 at% Bi + 5 at% In || 9326|2|2|3
    RHO       :    Bi & In co-doped || 3 at% Bi + 1 at% In || 9326|2|2|4
    SIGMA    :    undoped || cast || 9326|10|0|0
    SIGMA    :    In doped || 3 at% In || 9326|10|1|0
    SIGMA    :    In doped || 5 at% In || 9326|10|1|1
    SIGMA    :    In doped || 7 at% In || 9326|10|1|2
    SIGMA    :    In doped || 9 at% In || 9326|10|1|3
    SIGMA    :    Bi & In co-doped || 1 at% Bi + 1 at% In || 9326|10|2|0
    SIGMA    :    Bi & In co-doped || 1.5 at% Bi + 3 at% In || 9326|10|2|1
    SIGMA    :    Bi & In co-doped || 3 at% Bi + 5 at% In || 9326|10|2|2
    SIGMA    :    Bi & In co-doped || 1 at% Bi + 5 at% In || 9326|10|2|3
    SIGMA    :    Bi & In co-doped || 3 at% Bi + 1 at% In || 9326|10|2|4
    S         :    undoped || cast || 9326|48|0|0
    S         :    In doped || 3 at% In || 9326|48|1|0
    S         :    In doped || 5 at% In || 9326|48|1|1
    S         :    In doped || 7 at% In || 9326|48|1|2
    S         :    In doped || 9 at% In || 9326|48|1|3
    S         :    Bi & In co-doped || 1 at% Bi + 1 at% In || 9326|48|2|0
    S         :    Bi & In co-doped || 1.5 at% Bi + 3 at% In || 9326|48|2|1
    S         :    Bi & In co-doped || 3 at% Bi + 5 at% In || 9326|48|2|2
    S         :    Bi & In co-doped || 1 at% Bi + 5 at% In || 9326|48|2|3
    S         :    Bi & In co-doped || 3 at% Bi + 1 at% In || 9326|48|2|4

return to listing

PbTe (Bi doped, nanostructured) (New)

    TC        :    cold-pressed, Bi doped || 1 at% Bi || 15578|1|0|0
    TC        :    cold-pressed, Bi doped || 2 at% Bi || 15578|1|0|1
    TC        :    cold-pressed, Bi doped || 3 at% Bi || 15578|1|0|2
    TC        :    cold-pressed, Bi doped || 4 at% Bi || 15578|1|0|3
    TC        :    cold-pressed, Bi doped || 5 at% Bi || 15578|1|0|4
    TC        :    cold-pressed, Bi doped || 6 at% Bi || 15578|1|0|5
    TC        :    hot-pressed, Bi doped || 1 at% Bi || 15578|1|1|0
    TC        :    hot-pressed, Bi doped || 2 at% Bi || 15578|1|1|1
    TC        :    hot-pressed, Bi doped || 3 at% Bi || 15578|1|1|2
    TC        :    hot-pressed, Bi doped || 4 at% Bi || 15578|1|1|3
    TC        :    hot-pressed, Bi doped || 5 at% Bi || 15578|1|1|4
    TC        :    hot-pressed, Bi doped || 6 at% Bi || 15578|1|1|5
    RHO       :    cold-pressed, Bi doped || 1 at% Bi || 15578|2|0|0
    RHO       :    cold-pressed, Bi doped || 2 at% Bi || 15578|2|0|1
    RHO       :    cold-pressed, Bi doped || 3 at% Bi || 15578|2|0|2
    RHO       :    cold-pressed, Bi doped || 4 at% Bi || 15578|2|0|3
    RHO       :    cold-pressed, Bi doped || 5 at% Bi || 15578|2|0|4
    RHO       :    cold-pressed, Bi doped || 6 at% Bi || 15578|2|0|5
    RHO       :    hot-pressed, Bi doped || 1 at% Bi || 15578|2|1|0
    RHO       :    hot-pressed, Bi doped || 2 at% Bi || 15578|2|1|1
    RHO       :    hot-pressed, Bi doped || 3 at% Bi || 15578|2|1|2
    RHO       :    hot-pressed, Bi doped || 4 at% Bi || 15578|2|1|3
    RHO       :    hot-pressed, Bi doped || 5 at% Bi || 15578|2|1|4
    RHO       :    hot-pressed, Bi doped || 6 at% Bi || 15578|2|1|5
    SIGMA    :    cold-pressed, Bi doped || 1 at% Bi || 15578|10|0|0
    SIGMA    :    cold-pressed, Bi doped || 2 at% Bi || 15578|10|0|1
    SIGMA    :    cold-pressed, Bi doped || 3 at% Bi || 15578|10|0|2
    SIGMA    :    cold-pressed, Bi doped || 4 at% Bi || 15578|10|0|3
    SIGMA    :    cold-pressed, Bi doped || 5 at% Bi || 15578|10|0|4
    SIGMA    :    cold-pressed, Bi doped || 6 at% Bi || 15578|10|0|5
    SIGMA    :    hot-pressed, Bi doped || 1 at% Bi || 15578|10|1|0
    SIGMA    :    hot-pressed, Bi doped || 2 at% Bi || 15578|10|1|1
    SIGMA    :    hot-pressed, Bi doped || 3 at% Bi || 15578|10|1|2
    SIGMA    :    hot-pressed, Bi doped || 4 at% Bi || 15578|10|1|3
    SIGMA    :    hot-pressed, Bi doped || 5 at% Bi || 15578|10|1|4
    SIGMA    :    hot-pressed, Bi doped || 6 at% Bi || 15578|10|1|5
    S         :    cold-pressed, Bi doped || 1 at% Bi || 15578|48|0|0
    S         :    cold-pressed, Bi doped || 2 at% Bi || 15578|48|0|1
    S         :    cold-pressed, Bi doped || 3 at% Bi || 15578|48|0|2
    S         :    cold-pressed, Bi doped || 4 at% Bi || 15578|48|0|3
    S         :    cold-pressed, Bi doped || 5 at% Bi || 15578|48|0|4
    S         :    cold-pressed, Bi doped || 6 at% Bi || 15578|48|0|5
    S         :    hot-pressed, Bi doped || 1 at% Bi || 15578|48|1|0
    S         :    hot-pressed, Bi doped || 2 at% Bi || 15578|48|1|1
    S         :    hot-pressed, Bi doped || 3 at% Bi || 15578|48|1|2
    S         :    hot-pressed, Bi doped || 4 at% Bi || 15578|48|1|3
    S         :    hot-pressed, Bi doped || 5 at% Bi || 15578|48|1|4
    S         :    hot-pressed, Bi doped || 6 at% Bi || 15578|48|1|5

return to listing

PbTe (Ti doped) (New)

    TC        :    undoped || carrier concentration = 1.8 x 10¹⁸/cm³, mobility = 3988 cm²/(V-s) || 15568|1|0|0
    TC        :    Ti doped || 0.05 at% Ti, carrier concentration = 5.02 x 10¹⁸/cm³, mobility = 1871 cm²/(V-s) || 15568|1|1|0
    TC        :    Ti doped || 0.1 at% Ti, carrier concentration = 1.06 x 10¹⁹/cm³, mobility = 1028 cm²/(V-s) || 15568|1|1|1
    TC        :    Ti doped || 0.2 at% Ti, carrier concentration = 2.56 x 10¹⁹/cm³, mobility = 732 cm²/(V-s) || 15568|1|1|2
    TC        :    Ti doped || 0.4 at% Ti, carrier concentration = 2.61 x 10¹⁹/cm³, mobility = 668 cm²/(V-s) || 15568|1|1|3
    RHO       :    undoped || carrier concentration = 1.8 x 10¹⁸/cm³, mobility = 3988 cm²/(V-s) || 15568|2|0|0
    RHO       :    Ti doped || 0.05 at% Ti, carrier concentration = 5.02 x 10¹⁸/cm³, mobility = 1871 cm²/(V-s) || 15568|2|1|0
    RHO       :    Ti doped || 0.1 at% Ti, carrier concentration = 1.06 x 10¹⁹/cm³, mobility = 1028 cm²/(V-s) || 15568|2|1|1
    RHO       :    Ti doped || 0.2 at% Ti, carrier concentration = 2.56 x 10¹⁹/cm³, mobility = 732 cm²/(V-s) || 15568|2|1|2
    RHO       :    Ti doped || 0.4 at% Ti, carrier concentration = 2.61 x 10¹⁹/cm³, mobility = 668 cm²/(V-s) || 15568|2|1|3
    SIGMA    :    undoped || carrier concentration = 1.8 x 10¹⁸/cm³, mobility = 3988 cm²/(V-s) || 15568|10|0|0
    SIGMA    :    Ti doped || 0.05 at% Ti, carrier concentration = 5.02 x 10¹⁸/cm³, mobility = 1871 cm²/(V-s) || 15568|10|1|0
    SIGMA    :    Ti doped || 0.1 at% Ti, carrier concentration = 1.06 x 10¹⁹/cm³, mobility = 1028 cm²/(V-s) || 15568|10|1|1
    SIGMA    :    Ti doped || 0.2 at% Ti, carrier concentration = 2.56 x 10¹⁹/cm³, mobility = 732 cm²/(V-s) || 15568|10|1|2
    SIGMA    :    Ti doped || 0.4 at% Ti, carrier concentration = 2.61 x 10¹⁹/cm³, mobility = 668 cm²/(V-s) || 15568|10|1|3
    S         :    undoped || carrier concentration = 1.8 x 10¹⁸/cm³, mobility = 3988 cm²/(V-s) || 15568|48|0|0
    S         :    Ti doped || 0.05 at% Ti, carrier concentration = 5.02 x 10¹⁸/cm³, mobility = 1871 cm²/(V-s) || 15568|48|1|0
    S         :    Ti doped || 0.1 at% Ti, carrier concentration = 1.06 x 10¹⁹/cm³, mobility = 1028 cm²/(V-s) || 15568|48|1|1
    S         :    Ti doped || 0.2 at% Ti, carrier concentration = 2.56 x 10¹⁹/cm³, mobility = 732 cm²/(V-s) || 15568|48|1|2
    S         :    Ti doped || 0.4 at% Ti, carrier concentration = 2.61 x 10¹⁹/cm³, mobility = 668 cm²/(V-s) || 15568|48|1|3

return to listing

PbTe + x% CdSe (New)

    RHO       :    undoped || 15573|2|0|-1
    RHO       :    CdSe doped || 0.5 mol% CdSe || 15573|2|1|0
    RHO       :    CdSe doped || 1 mol% CdSe || 15573|2|1|1
    RHO       :    CdSe doped || 2 mol% CdSe || 15573|2|1|2
    RHO       :    CdSe doped || 3 mol% CdSe || 15573|2|1|3
    SIGMA    :    undoped || 15573|10|0|-1
    SIGMA    :    CdSe doped || 0.5 mol% CdSe || 15573|10|1|0
    SIGMA    :    CdSe doped || 1 mol% CdSe || 15573|10|1|1
    SIGMA    :    CdSe doped || 2 mol% CdSe || 15573|10|1|2
    SIGMA    :    CdSe doped || 3 mol% CdSe || 15573|10|1|3
    S         :    undoped || 15573|48|0|-1
    S         :    CdSe doped || 0.5 mol% CdSe || 15573|48|1|0
    S         :    CdSe doped || 1 mol% CdSe || 15573|48|1|1
    S         :    CdSe doped || 2 mol% CdSe || 15573|48|1|2
    S         :    CdSe doped || 3 mol% CdSe || 15573|48|1|3

return to listing

PbTe + x% In₄SnSe₄ (New)

    TC        :    undoped || carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15569|1|0|0
    TC        :    In₄SnSe₄ doped || 0.04 at% In₄SnSe₄, carrier concentration = 3.52 x 10¹⁹/cm³, mobility = 700 cm²/(V-s) || 15569|1|1|0
    TC        :    In₄SnSe₄ doped || 0.06 at% In₄SnSe₄, carrier concentration = 3.3 x 10¹⁹/cm³, mobility = 690 cm²/(V-s) || 15569|1|1|1
    TC        :    In₄SnSe₄ doped || 0.08 at% In₄SnSe₄, carrier concentration = 2 x 10¹⁹/cm³, mobility = 812 cm²/(V-s) || 15569|1|1|2
    TC        :    In₄SnSe₄ doped || 0.1 at% In₄SnSe₄, carrier concentration = 1 x 10¹⁹/cm³, mobility = 1211 cm²/(V-s) || 15569|1|1|3
    TC        :    In₄SnSe₄ doped || 0.12 at% In₄SnSe₄, carrier concentration = 7.83 x 10¹⁸/cm³, mobility = 1213 cm²/(V-s) || 15569|1|1|4
    TC        :    In₄SnSe₄ doped || 0.14 at% In₄SnSe₄, carrier concentration = 7.26 x 10¹⁸/cm³, mobility = 1035 cm²/(V-s) || 15569|1|1|5
    RHO       :    undoped || carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15569|2|0|0
    RHO       :    In₄SnSe₄ doped || 0.04 at% In₄SnSe₄, carrier concentration = 3.52 x 10¹⁹/cm³, mobility = 700 cm²/(V-s) || 15569|2|1|0
    RHO       :    In₄SnSe₄ doped || 0.06 at% In₄SnSe₄, carrier concentration = 3.3 x 10¹⁹/cm³, mobility = 690 cm²/(V-s) || 15569|2|1|1
    RHO       :    In₄SnSe₄ doped || 0.08 at% In₄SnSe₄, carrier concentration = 2 x 10¹⁹/cm³, mobility = 812 cm²/(V-s) || 15569|2|1|2
    RHO       :    In₄SnSe₄ doped || 0.1 at% In₄SnSe₄, carrier concentration = 1 x 10¹⁹/cm³, mobility = 1211 cm²/(V-s) || 15569|2|1|3
    RHO       :    In₄SnSe₄ doped || 0.12 at% In₄SnSe₄, carrier concentration = 7.83 x 10¹⁸/cm³, mobility = 1213 cm²/(V-s) || 15569|2|1|4
    RHO       :    In₄SnSe₄ doped || 0.14 at% In₄SnSe₄, carrier concentration = 7.26 x 10¹⁸/cm³, mobility = 1035 cm²/(V-s) || 15569|2|1|5
    SIGMA    :    undoped || carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15569|10|0|0
    SIGMA    :    In₄SnSe₄ doped || 0.04 at% In₄SnSe₄, carrier concentration = 3.52 x 10¹⁹/cm³, mobility = 700 cm²/(V-s) || 15569|10|1|0
    SIGMA    :    In₄SnSe₄ doped || 0.06 at% In₄SnSe₄, carrier concentration = 3.3 x 10¹⁹/cm³, mobility = 690 cm²/(V-s) || 15569|10|1|1
    SIGMA    :    In₄SnSe₄ doped || 0.08 at% In₄SnSe₄, carrier concentration = 2 x 10¹⁹/cm³, mobility = 812 cm²/(V-s) || 15569|10|1|2
    SIGMA    :    In₄SnSe₄ doped || 0.1 at% In₄SnSe₄, carrier concentration = 1 x 10¹⁹/cm³, mobility = 1211 cm²/(V-s) || 15569|10|1|3
    SIGMA    :    In₄SnSe₄ doped || 0.12 at% In₄SnSe₄, carrier concentration = 7.83 x 10¹⁸/cm³, mobility = 1213 cm²/(V-s) || 15569|10|1|4
    SIGMA    :    In₄SnSe₄ doped || 0.14 at% In₄SnSe₄, carrier concentration = 7.26 x 10¹⁸/cm³, mobility = 1035 cm²/(V-s) || 15569|10|1|5
    TD        :    undoped || carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15569|25|0|0
    TD        :    In₄SnSe₄ doped || 0.04 at% In₄SnSe₄, carrier concentration = 3.52 x 10¹⁹/cm³, mobility = 700 cm²/(V-s) || 15569|25|1|0
    TD        :    In₄SnSe₄ doped || 0.06 at% In₄SnSe₄, carrier concentration = 3.3 x 10¹⁹/cm³, mobility = 690 cm²/(V-s) || 15569|25|1|1
    TD        :    In₄SnSe₄ doped || 0.08 at% In₄SnSe₄, carrier concentration = 2 x 10¹⁹/cm³, mobility = 812 cm²/(V-s) || 15569|25|1|2
    TD        :    In₄SnSe₄ doped || 0.1 at% In₄SnSe₄, carrier concentration = 1 x 10¹⁹/cm³, mobility = 1211 cm²/(V-s) || 15569|25|1|3
    TD        :    In₄SnSe₄ doped || 0.12 at% In₄SnSe₄, carrier concentration = 7.83 x 10¹⁸/cm³, mobility = 1213 cm²/(V-s) || 15569|25|1|4
    TD        :    In₄SnSe₄ doped || 0.14 at% In₄SnSe₄, carrier concentration = 7.26 x 10¹⁸/cm³, mobility = 1035 cm²/(V-s) || 15569|25|1|5
    S         :    undoped || carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15569|48|0|0
    S         :    In₄SnSe₄ doped || 0.04 at% In₄SnSe₄, carrier concentration = 3.52 x 10¹⁹/cm³, mobility = 700 cm²/(V-s) || 15569|48|1|0
    S         :    In₄SnSe₄ doped || 0.06 at% In₄SnSe₄, carrier concentration = 3.3 x 10¹⁹/cm³, mobility = 690 cm²/(V-s) || 15569|48|1|1
    S         :    In₄SnSe₄ doped || 0.08 at% In₄SnSe₄, carrier concentration = 2 x 10¹⁹/cm³, mobility = 812 cm²/(V-s) || 15569|48|1|2
    S         :    In₄SnSe₄ doped || 0.1 at% In₄SnSe₄, carrier concentration = 1 x 10¹⁹/cm³, mobility = 1211 cm²/(V-s) || 15569|48|1|3
    S         :    In₄SnSe₄ doped || 0.12 at% In₄SnSe₄, carrier concentration = 7.83 x 10¹⁸/cm³, mobility = 1213 cm²/(V-s) || 15569|48|1|4
    S         :    In₄SnSe₄ doped || 0.14 at% In₄SnSe₄, carrier concentration = 7.26 x 10¹⁸/cm³, mobility = 1035 cm²/(V-s) || 15569|48|1|5

return to listing

PbTe + x% InSe (New)

    TC        :    undoped || carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15570|1|0|0
    TC        :    InSe doped || 0.2 at% InSe, carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 526 cm²/(V-s) || 15570|1|1|0
    TC        :    InSe doped || 0.3 at% InSe, carrier concentration = 1.03 x 10¹⁹/cm³, mobility = 659 cm²/(V-s) || 15570|1|1|1
    TC        :    InSe doped || 0.4 at% InSe, carrier concentration = 7.87 x 10¹⁸/cm³, mobility = 474 cm²/(V-s) || 15570|1|1|2
    TC        :    InSe doped || 0.5 at% InSe, carrier concentration = 6.1 x 10¹⁸/cm³, mobility = 485 cm²/(V-s) || 15570|1|1|3
    RHO       :    undoped || carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15570|2|0|0
    RHO       :    InSe doped || 0.2 at% InSe, carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 526 cm²/(V-s) || 15570|2|1|0
    RHO       :    InSe doped || 0.3 at% InSe, carrier concentration = 1.03 x 10¹⁹/cm³, mobility = 659 cm²/(V-s) || 15570|2|1|1
    RHO       :    InSe doped || 0.4 at% InSe, carrier concentration = 7.87 x 10¹⁸/cm³, mobility = 474 cm²/(V-s) || 15570|2|1|2
    RHO       :    InSe doped || 0.5 at% InSe, carrier concentration = 6.1 x 10¹⁸/cm³, mobility = 485 cm²/(V-s) || 15570|2|1|3
    SIGMA    :    undoped || carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15570|10|0|0
    SIGMA    :    InSe doped || 0.2 at% InSe, carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 526 cm²/(V-s) || 15570|10|1|0
    SIGMA    :    InSe doped || 0.3 at% InSe, carrier concentration = 1.03 x 10¹⁹/cm³, mobility = 659 cm²/(V-s) || 15570|10|1|1
    SIGMA    :    InSe doped || 0.4 at% InSe, carrier concentration = 7.87 x 10¹⁸/cm³, mobility = 474 cm²/(V-s) || 15570|10|1|2
    SIGMA    :    InSe doped || 0.5 at% InSe, carrier concentration = 6.1 x 10¹⁸/cm³, mobility = 485 cm²/(V-s) || 15570|10|1|3
    TD        :    undoped || carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15570|25|0|0
    TD        :    InSe doped || 0.2 at% InSe, carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 526 cm²/(V-s) || 15570|25|1|0
    TD        :    InSe doped || 0.3 at% InSe, carrier concentration = 1.03 x 10¹⁹/cm³, mobility = 659 cm²/(V-s) || 15570|25|1|1
    TD        :    InSe doped || 0.4 at% InSe, carrier concentration = 7.87 x 10¹⁸/cm³, mobility = 474 cm²/(V-s) || 15570|25|1|2
    TD        :    InSe doped || 0.5 at% InSe, carrier concentration = 6.1 x 10¹⁸/cm³, mobility = 485 cm²/(V-s) || 15570|25|1|3
    S         :    undoped || carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15570|48|0|0
    S         :    InSe doped || 0.2 at% InSe, carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 526 cm²/(V-s) || 15570|48|1|0
    S         :    InSe doped || 0.3 at% InSe, carrier concentration = 1.03 x 10¹⁹/cm³, mobility = 659 cm²/(V-s) || 15570|48|1|1
    S         :    InSe doped || 0.4 at% InSe, carrier concentration = 7.87 x 10¹⁸/cm³, mobility = 474 cm²/(V-s) || 15570|48|1|2
    S         :    InSe doped || 0.5 at% InSe, carrier concentration = 6.1 x 10¹⁸/cm³, mobility = 485 cm²/(V-s) || 15570|48|1|3

return to listing

PbTe - 0.4% InSe + x% Sn (New)

    TC        :    undoped || carrier concentration = 7.87 x 10¹⁸/cm³, mobility = 474 cm²/(V-s) || 15571|1|0|0
    TC        :    Sn doped || 0.05 at% Sn, carrier concentration = 8.2 x 10¹⁸/cm³, mobility = 575 cm²/(V-s) || 15571|1|1|0
    TC        :    Sn doped || 0.1 at% Sn, carrier concentration = 1.34 x 10¹⁹/cm³, mobility = 676 cm²/(V-s) || 15571|1|1|1
    TC        :    Sn doped || 0.2 at% Sn, carrier concentration = 1.29 x 10¹⁹/cm³, mobility = 1092 cm²/(V-s) || 15571|1|1|2
    TC        :    Sn doped || 0.3 at% Sn, carrier concentration = 1.16 x 10¹⁹/cm³, mobility = 1070 cm²/(V-s) || 15571|1|1|3
    RHO       :    undoped || carrier concentration = 7.87 x 10¹⁸/cm³, mobility = 474 cm²/(V-s) || 15571|2|0|0
    RHO       :    Sn doped || 0.05 at% Sn, carrier concentration = 8.2 x 10¹⁸/cm³, mobility = 575 cm²/(V-s) || 15571|2|1|0
    RHO       :    Sn doped || 0.1 at% Sn, carrier concentration = 1.34 x 10¹⁹/cm³, mobility = 676 cm²/(V-s) || 15571|2|1|1
    RHO       :    Sn doped || 0.2 at% Sn, carrier concentration = 1.29 x 10¹⁹/cm³, mobility = 1092 cm²/(V-s) || 15571|2|1|2
    RHO       :    Sn doped || 0.3 at% Sn, carrier concentration = 1.16 x 10¹⁹/cm³, mobility = 1070 cm²/(V-s) || 15571|2|1|3
    SIGMA    :    undoped || carrier concentration = 7.87 x 10¹⁸/cm³, mobility = 474 cm²/(V-s) || 15571|10|0|0
    SIGMA    :    Sn doped || 0.05 at% Sn, carrier concentration = 8.2 x 10¹⁸/cm³, mobility = 575 cm²/(V-s) || 15571|10|1|0
    SIGMA    :    Sn doped || 0.1 at% Sn, carrier concentration = 1.34 x 10¹⁹/cm³, mobility = 676 cm²/(V-s) || 15571|10|1|1
    SIGMA    :    Sn doped || 0.2 at% Sn, carrier concentration = 1.29 x 10¹⁹/cm³, mobility = 1092 cm²/(V-s) || 15571|10|1|2
    SIGMA    :    Sn doped || 0.3 at% Sn, carrier concentration = 1.16 x 10¹⁹/cm³, mobility = 1070 cm²/(V-s) || 15571|10|1|3
    TD        :    undoped || carrier concentration = 7.87 x 10¹⁸/cm³, mobility = 474 cm²/(V-s) || 15571|25|0|0
    TD        :    Sn doped || 0.05 at% Sn, carrier concentration = 8.2 x 10¹⁸/cm³, mobility = 575 cm²/(V-s) || 15571|25|1|0
    TD        :    Sn doped || 0.1 at% Sn, carrier concentration = 1.34 x 10¹⁹/cm³, mobility = 676 cm²/(V-s) || 15571|25|1|1
    TD        :    Sn doped || 0.2 at% Sn, carrier concentration = 1.29 x 10¹⁹/cm³, mobility = 1092 cm²/(V-s) || 15571|25|1|2
    TD        :    Sn doped || 0.3 at% Sn, carrier concentration = 1.16 x 10¹⁹/cm³, mobility = 1070 cm²/(V-s) || 15571|25|1|3
    S         :    undoped || carrier concentration = 7.87 x 10¹⁸/cm³, mobility = 474 cm²/(V-s) || 15571|48|0|0
    S         :    Sn doped || 0.05 at% Sn, carrier concentration = 8.2 x 10¹⁸/cm³, mobility = 575 cm²/(V-s) || 15571|48|1|0
    S         :    Sn doped || 0.1 at% Sn, carrier concentration = 1.34 x 10¹⁹/cm³, mobility = 676 cm²/(V-s) || 15571|48|1|1
    S         :    Sn doped || 0.2 at% Sn, carrier concentration = 1.29 x 10¹⁹/cm³, mobility = 1092 cm²/(V-s) || 15571|48|1|2
    S         :    Sn doped || 0.3 at% Sn, carrier concentration = 1.16 x 10¹⁹/cm³, mobility = 1070 cm²/(V-s) || 15571|48|1|3

return to listing

PbTe

    TC     (N):    cast || Bali et. al. || 15564|1|0|1
    TC     (N):    hot-pressed || carrier concentration = 1.8 x 10¹⁸/cm³, mobility = 3988 cm²/(V-s) || 15564|1|1|1
    TC     (N):    spark plasma sintered || sintered at 600 °C (1112 °F), carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15564|1|2|0
    RHO    (N):    cast || Bali et. al. || 15564|2|0|1
    RHO    (N):    cast || Kalmykov et. al. || 15564|2|0|2
    RHO    (N):    hot-pressed || carrier concentration = 1.8 x 10¹⁸/cm³, mobility = 3988 cm²/(V-s) || 15564|2|1|2
    RHO    (N):    spark plasma sintered || sintered at 600 °C (1112 °F), carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15564|2|2|3
    SIGMA (N):    cast || Bali et. al. || 15564|10|0|1
    SIGMA (N):    cast || Kalmykov et. al. || 15564|10|0|2
    SIGMA (N):    hot-pressed || carrier concentration = 1.8 x 10¹⁸/cm³, mobility = 3988 cm²/(V-s) || 15564|10|1|2
    SIGMA (N):    spark plasma sintered || sintered at 600 °C (1112 °F), carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15564|10|2|3
    TD     (N):    spark plasma sintered || sintered at 600 °C (1112 °F), carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15564|25|1|0
    S      (N):    cast || Bali et. al. || 15564|48|0|1
    S      (N):    cast || Kalmykov et. al. || 15564|48|0|2
    S      (N):    hot-pressed || carrier concentration = 1.8 x 10¹⁸/cm³, mobility = 3988 cm²/(V-s) || 15564|48|1|2
    S      (N):    spark plasma sintered || sintered at 600 °C (1112 °F), carrier concentration = 2.85 x 10¹⁹/cm³, mobility = 510 cm²/(V-s) || 15564|48|2|3

return to listing

PLA Conductive (New)

    DLL       :    solid || X : print direction || 15589|0|0|0
    DLL       :    solid || Y : in-plane normal to print direction || 15589|0|0|1
    DLL       :    solid || Z : build direction || 15589|0|0|2
    TC    (*):    solid || X : print direction || 15589|1|0|0
    TC    (*):    solid || Y : in-plane normal to print direction || 15589|1|0|1
    TC    (*):    solid || Z : build direction || 15589|1|0|2
    TC    (*):    solid || average of all directions || 15589|1|0|3
    MTE       :    solid || X : print direction || 15589|8|0|0
    MTE       :    solid || Y : in-plane normal to print direction || 15589|8|0|1
    MTE       :    solid || Z : build direction || 15589|8|0|2
    SH    (*):    solid || 15589|9|0|-1
    D         :    solid || 15589|24|0|-1
    TD    (*):    solid || X : print direction || 15589|25|0|0
    TD    (*):    solid || Y : in-plane normal to print direction || 15589|25|0|1
    TD    (*):    solid || Z : build direction || 15589|25|0|2
    TD    (*):    solid || average of all directions || 15589|25|0|3

return to listing

PLA LAVA (New)

    DLL       :    solid || X : print direction || 15588|0|0|0
    DLL       :    solid || Y : in-plane normal to print direction || 15588|0|0|1
    DLL       :    solid || Z : build direction || 15588|0|0|2
    TC    (*):    solid || X : print direction || 15588|1|0|0
    TC    (*):    solid || Y : in-plane normal to print direction || 15588|1|0|1
    TC    (*):    solid || Z : build direction || 15588|1|0|2
    TC    (*):    solid || average of all directions || 15588|1|0|3
    MTE       :    solid || X : print direction || 15588|8|0|0
    MTE       :    solid || Y : in-plane normal to print direction || 15588|8|0|1
    MTE       :    solid || Z : build direction || 15588|8|0|2
    SH    (*):    solid || 15588|9|0|-1
    D         :    solid || 15588|24|0|-1
    TD    (*):    solid || X : print direction || 15588|25|0|0
    TD    (*):    solid || Y : in-plane normal to print direction || 15588|25|0|1
    TD    (*):    solid || Z : build direction || 15588|25|0|2
    TD    (*):    solid || average of all directions || 15588|25|0|3

return to listing

PLA Red (New)

    DLL       :    solid || X : print direction || 15586|0|0|0
    DLL       :    solid || Y : in-plane normal to print direction || 15586|0|0|1
    DLL       :    solid || Z : build direction || 15586|0|0|2
    TC    (*):    solid || X : print direction || 15586|1|0|0
    TC    (*):    solid || Y : in-plane normal to print direction || 15586|1|0|1
    TC    (*):    solid || Z : build direction || 15586|1|0|2
    TC    (*):    solid || average of all directions || 15586|1|0|3
    MTE       :    solid || X : print direction || 15586|8|0|0
    MTE       :    solid || Y : in-plane normal to print direction || 15586|8|0|1
    MTE       :    solid || Z : build direction || 15586|8|0|2
    SH    (*):    solid || 15586|9|0|-1
    D         :    solid || 15586|24|0|-1
    TD    (*):    solid || X : print direction || 15586|25|0|0
    TD    (*):    solid || Y : in-plane normal to print direction || 15586|25|0|1
    TD    (*):    solid || Z : build direction || 15586|25|0|2
    TD    (*):    solid || average of all directions || 15586|25|0|3

return to listing

PLA Super Blue (New)

    DLL       :    solid || X : print direction || 15587|0|0|0
    DLL       :    solid || Y : in-plane normal to print direction || 15587|0|0|1
    DLL       :    solid || Z : build direction || 15587|0|0|2
    MTE       :    solid || X : print direction || 15587|8|0|0
    MTE       :    solid || Y : in-plane normal to print direction || 15587|8|0|1
    MTE       :    solid || Z : build direction || 15587|8|0|2

return to listing

PLA Tough White (New)

    DLL       :    solid || X : print direction || 15585|0|0|0
    DLL       :    solid || Y : in-plane normal to print direction || 15585|0|0|1
    DLL       :    solid || Z : build direction || 15585|0|0|2
    TC    (*):    solid || X : print direction || 15585|1|0|0
    TC    (*):    solid || Y : in-plane normal to print direction || 15585|1|0|1
    TC    (*):    solid || Z : build direction || 15585|1|0|2
    TC    (*):    solid || average of all directions || 15585|1|0|3
    MTE       :    solid || X : print direction || 15585|8|0|0
    MTE       :    solid || Y : in-plane normal to print direction || 15585|8|0|1
    MTE       :    solid || Z : build direction || 15585|8|0|2
    SH    (*):    solid || 15585|9|0|-1
    D         :    solid || 15585|24|0|-1
    TD    (*):    solid || X : print direction || 15585|25|0|0
    TD    (*):    solid || Y : in-plane normal to print direction || 15585|25|0|1
    TD    (*):    solid || Z : build direction || 15585|25|0|2
    TD    (*):    solid || average of all directions || 15585|25|0|3

return to listing

Sb₂S₃

    TC     (N):    solid || hot-pressed || 3552|1|0|0
    RHO    (N):    solid || nano-crystalline || 3552|2|0|0
    RHO    (N):    solid || glassy || 3552|2|0|1
    RHO    (N):    liquid || 3552|2|1|-1
    SIGMA (N):    solid || nano-crystalline || 3552|10|0|0
    SIGMA (N):    solid || glassy || 3552|10|0|1
    SIGMA (N):    liquid || 3552|10|1|-1
    D     (N*):    solid || 3552|24|0|-1
    Vis    (N):    liquid || 3552|26|1|-1

return to listing

Sn₁₇Zn₇P₂₂Br₈ (New)

    RHO       :    hot-pressed || 15583|2|0|-1
    SIGMA    :    hot-pressed || 15583|10|0|-1
    S         :    hot-pressed || 15583|48|0|-1

return to listing

Sn₂₄P₁₉.₃Br₈ (New)

    RHO       :    hot-pressed || 15582|2|0|-1
    SIGMA    :    hot-pressed || 15582|10|0|-1
    S         :    hot-pressed || 15582|48|0|-1

return to listing