Changes

New and revised materials and properties in MPDB v9.61 as compared to v9.59

Key to property symbols (number of datasets):

D = Density	DLL = Linear thermal expansion (dL/L)
MTE = Mean coefficient of thermal expansion	CTE = Coefficient of thermal expansion (CTE)
E = Elastic/Young's modulus	G = Shear modulus
v = Poisson's ratio	K = Bulk modulus
TC = Thermal conductivity	TD = Thermal diffusivity
SH = Specific heat	HC = Heat capacity
SSC = True stress-strain curve (tension)	SSCC = True stress-strain curve (compression)
UTS = Tensile strength	YS = Yield strength (tension)
UCS = Compressive strength	YSC = Yield strength (compression)
%El = Elongation	SR = Stress rupture
FEN = Fatigue e-N curve	FSN = Fatigue S-N curve
CRS = Creep strength	IC = Isochronous creep
HE = Hemispherical total emissivity	NE = Normal total emissivity
VP = Vapor pressure	Vis = Viscosity
ST = Surface tension	RHO = Electrical resistivity
SIGMA = Electrical conductivity	SV = Specific volume
AV = Apparent viscosity	FM = Flexural modulus
FS = Flexural strength	ESSC = Engineering stress-strain curve (tension)
ESSCC = Engineering stress-strain curve (compression)	CRM = Creep modulus
RPB = Relative permeability	AP = Absolute permeability
BH = B-H curve	HB = H-B curve
CL = Core loss	EP = Exciting Power
DCRPT = Relative permittivity	DF = Dissipation factor
RIW = Refractive index vs WL	RIT = Refractive index vs T

N indicates the data is new, R indicates the data has been revised, * indicates the data is the RT value only

43 new materials, 786 new property sets, 63 revised properties, and 61 new RT values

15 Sn - 85 Pb (wt%) (New)	20 Sn - 80 Pb (wt%) (New)	30 Sn - 70 Pb (wt%) (New)	5 Sn - 95 Pb (wt%) (Revised)	50 Al, 50 Ni (wt%) Raney nickel
55 Sn - 45 Pb (wt%) (New)	6061	63 Sn - 37 Pb (wt%) (Revised)	65 Sn - 35 Pb (wt%) (New)	70 Sn - 30 Pb (wt%) (New)
80 Sn - 20 Pb (wt%) (New)	97.5 Sn - 2.5 Pb (wt%) (New)	Al - 13 Si (wt%) (Revised)	Al - 17 Si (wt%) (Revised)	Al - 20 Si (wt%) (Revised)
Al - 22 Si (wt%) (Revised)	Al - 30 Si (wt%) (Revised)	Al - 35 Si (wt%) (Revised)	Al - 41 Si (wt%) (Revised)	Al - 51 Si (wt%) (Revised)
Al₃Ni	AlCr₀.₂₅FeNi₂.₇₅ (New)	AlCr₀.₅FeNi₂.₅ (New)	AlCr₀.₇₅FeNi₂.₂₅ (New)	AlCr₁.₂₅FeNi₁.₇₅ (New)
AlCr₁.₅FeNi₁.₅ (New)	AlCrFeNi (New)	ALON	AZ31 (Revised)	AZ61
AZ63 (Revised)	AZ92	Bi₂Te₂.₇Se₀.₃ (n-type) (Revised)	Cd - 10.4 Sb (wt%) (New)	Cd - 24 Sb (wt%) (New)
Cd - 48.6 Sb (wt%) (New)	Cd - 5 Sb (wt%) (New)	Cd - 52 Sb (wt%) (New)	Cd - 55 Sb (wt%) (New)	Cd - 58.5 Sb (wt%) (New)
Cd - 65 Sb (wt%) (New)	Cd - 7.7 Sb (wt%) (New)	Cd - 88 Sb (wt%) (New)	Ce₄RuMg (New)	CeRuAl (New)
CoCrFe₀.₂MnNi (New)	CoCrFe₁₆MnNi (New)	CoCrFe₄MnNi (New)	CoCrFe₈MnNi (New)	CoMnP₂O₇ (New)
Corning 1724 (Revised)	Cu₂Se (New)	CuAlO₂	CuGe₂P₃ (New)	CuGe₄P₃ (New)
CuSi₂P₃ (New)	CuSi₄P₃	EK30	EK41	EZ33
Fe - 27 Mn - 10 Al - 1 C (wt%) (New)	Graphite CZR (Revised)	Graphite DFP-1 (Revised)	Graphite HPD (Revised)	Graphite PLS-1 (Revised)
Graphite SCF (Revised)	Graphite SFG-1 (Revised)	HK31	HZ32	In₂Se₃
Lead (Revised)	Li₂Na₂P₂O₇ (New)	NbTiVZr₀.₅ (New)	Pb - 55 Bi (at%) (eutectic) (Revised)	Ti - 15 Mo (wt%) (New)
Ti - 15 Mo - 0.5 Si (wt%) (New)	Ti - 15 Mo - 1 Si (wt%) (New)	Ti - 15 Mo - 1.5 Si (wt%) (New)	Ti - 15 Mo - 2 Si (wt%) (New)	Ti - 6 Al - 4 V
Tin (Revised)	ZH62	ZK51	ZK60 (Revised)

15 Sn - 85 Pb (wt%) (New)

    DLL       :    liquid : 15379|0|1|-1
    MTE       :    liquid : 15379|8|1|-1
    CTE       :    liquid : 15379|16|1|-1
    D         :    liquid : 15379|24|1|-1
    Vis       :    liquid : 15379|26|1|-1

return to listing

20 Sn - 80 Pb (wt%) (New)

    DLL       :    liquid : 15380|0|1|-1
    MTE       :    liquid : 15380|8|1|-1
    CTE       :    liquid : 15380|16|1|-1
    D         :    liquid : 15380|24|1|-1
    Vis       :    liquid : 15380|26|1|-1

return to listing

30 Sn - 70 Pb (wt%) (New)

    DLL       :    liquid : 15395|0|1|-1
    MTE       :    liquid : 15395|8|1|-1
    CTE       :    liquid : 15395|16|1|-1
    D         :    liquid : 15395|24|1|-1

return to listing

5 Sn - 95 Pb (wt%)

    DLL    (R):    liquid : 2736|0|1|-1
    MTE    (R):    liquid : 2736|8|1|-1
    CTE    (N):    liquid : 2736|16|1|-1
    D      (R):    liquid : 2736|24|1|-1
    Vis    (R):    liquid : 2736|26|1|-1

return to listing

50 Al, 50 Ni (wt%) Raney nickel

    ST     (N):    liquid : 1560|38|1|-1

return to listing

55 Sn - 45 Pb (wt%) (New)

    DLL       :    liquid : 15381|0|1|-1
    MTE       :    liquid : 15381|8|1|-1
    CTE       :    liquid : 15381|16|1|-1
    D         :    liquid : 15381|24|1|-1
    Vis       :    liquid : 15381|26|1|-1

return to listing

6061

    SSC    (N):    pre-heated to 410 °C (770 °F), hot-rolled, cold-rolled & aged : tested at 20 °C (68 °F), unknown strain rate, as-rolled : 70|4|5|0
    SSC    (N):    pre-heated to 410 °C (770 °F), hot-rolled, cold-rolled & aged : tested at 20 °C (68 °F), unknown strain rate, temper T4 : 70|4|5|1
    SSC    (N):    pre-heated to 410 °C (770 °F), hot-rolled, cold-rolled & aged : tested at 20 °C (68 °F), unknown strain rate, temper T4P : 70|4|5|2
    SSC    (N):    pre-heated to 560 °C (1040 °F), hot-rolled, cold-rolled & aged : tested at 20 °C (68 °F), unknown strain rate, as-rolled : 70|4|6|0
    SSC    (N):    pre-heated to 560 °C (1040 °F), hot-rolled, cold-rolled & aged : tested at 20 °C (68 °F), unknown strain rate, temper T4 : 70|4|6|1
    SSC    (N):    pre-heated to 560 °C (1040 °F), hot-rolled, cold-rolled & aged : tested at 20 °C (68 °F), unknown strain rate, temper T4P : 70|4|6|2

return to listing

63 Sn - 37 Pb (wt%)

    DLL    (R):    liquid : 2739|0|1|-1
    MTE    (R):    liquid : 2739|8|1|-1
    CTE    (R):    liquid : 2739|16|1|-1
    D      (R):    liquid : 2739|24|1|-1

return to listing

65 Sn - 35 Pb (wt%) (New)

    Vis       :    liquid : 15382|26|1|-1

return to listing

70 Sn - 30 Pb (wt%) (New)

    DLL       :    liquid : 15383|0|1|-1
    MTE       :    liquid : 15383|8|1|-1
    CTE       :    liquid : 15383|16|1|-1
    D         :    liquid : 15383|24|1|-1
    Vis       :    liquid : 15383|26|1|-1

return to listing

80 Sn - 20 Pb (wt%) (New)

    DLL       :    liquid : 15396|0|1|-1
    MTE       :    liquid : 15396|8|1|-1
    CTE       :    liquid : 15396|16|1|-1
    D         :    liquid : 15396|24|1|-1

return to listing

97.5 Sn - 2.5 Pb (wt%) (New)

    DLL       :    liquid : 15384|0|1|-1
    MTE       :    liquid : 15384|8|1|-1
    CTE       :    liquid : 15384|16|1|-1
    D         :    liquid : 15384|24|1|-1
    Vis       :    liquid : 15384|26|1|-1

return to listing

Al - 13 Si (wt%)

    DLL    (R):    liquid : 9044|0|1|-1
    MTE    (R):    liquid : 9044|8|1|-1
    CTE    (N):    solid : 9044|16|0|-1
    CTE    (R):    liquid : 9044|16|1|-1
    D      (R):    liquid : 9044|24|1|-1

return to listing

Al - 17 Si (wt%)

    DLL    (R):    liquid : 9045|0|1|-1
    MTE    (R):    liquid : 9045|8|1|-1
    CTE    (R):    liquid : 9045|16|1|-1

return to listing

Al - 20 Si (wt%)

    DLL    (R):    liquid : 9434|0|1|-1
    MTE    (R):    liquid : 9434|8|1|-1
    CTE    (R):    liquid : 9434|16|1|-1

return to listing

Al - 22 Si (wt%)

    DLL    (R):    liquid : 136|0|1|-1
    MTE    (R):    liquid : 136|8|1|-1
    CTE    (R):    liquid : 136|16|1|-1

return to listing

Al - 30 Si (wt%)

    DLL    (R):    liquid : 137|0|1|-1
    MTE    (R):    liquid : 137|8|1|-1
    CTE    (R):    liquid : 137|16|1|-1

return to listing

Al - 35 Si (wt%)

    DLL    (R):    liquid : 9435|0|1|-1
    MTE    (R):    liquid : 9435|8|1|-1
    CTE    (R):    liquid : 9435|16|1|-1

return to listing

Al - 41 Si (wt%)

    DLL    (R):    liquid : 9436|0|1|-1
    MTE    (R):    liquid : 9436|8|1|-1
    CTE    (R):    liquid : 9436|16|1|-1

return to listing

Al - 51 Si (wt%)

    DLL    (R):    liquid : 9437|0|1|-1
    MTE    (R):    liquid : 9437|8|1|-1
    CTE    (R):    liquid : 9437|16|1|-1

return to listing

Al₃Ni

    ST     (N):    liquid : 1549|38|1|-1

return to listing

AlCr₀.₂₅FeNi₂.₇₅ (New)

    SSCC      :    as-cast, 5 x 10⁻⁴/s : tested at 20 °C (68 °F) : 15401|12|0|0
    YSC   (*):    as-cast : 15401|21|0|-1
    %El   (*):    as-cast : in compression : 15401|29|0|0
    UCS   (*):    as-cast : 15401|47|0|-1

return to listing

AlCr₀.₅FeNi₂.₅ (New)

    SSCC      :    as-cast, 5 x 10⁻⁴/s : tested at 20 °C (68 °F) : 15402|12|0|0
    YSC   (*):    as-cast : 15402|21|0|-1
    %El   (*):    as-cast : in compression : 15402|29|0|0
    UCS   (*):    as-cast : 15402|47|0|-1

return to listing

AlCr₀.₇₅FeNi₂.₂₅ (New)

    SSCC      :    as-cast, 5 x 10⁻⁴/s : tested at 20 °C (68 °F) : 15403|12|0|0
    YSC   (*):    as-cast : 15403|21|0|-1
    %El   (*):    as-cast : in compression : 15403|29|0|0
    UCS   (*):    as-cast : 15403|47|0|-1

return to listing

AlCr₁.₂₅FeNi₁.₇₅ (New)

    SSCC      :    as-cast, 5 x 10⁻⁴/s : tested at 20 °C (68 °F) : 15405|12|0|0
    YSC   (*):    as-cast : 15405|21|0|-1
    %El   (*):    as-cast : in compression : 15405|29|0|0
    UCS   (*):    as-cast : 15405|47|0|-1

return to listing

AlCr₁.₅FeNi₁.₅ (New)

    SSCC      :    as-cast, 5 x 10⁻⁴/s : tested at 20 °C (68 °F) : 15406|12|0|0
    YSC   (*):    as-cast : 15406|21|0|-1
    %El   (*):    as-cast : in compression : 15406|29|0|0
    UCS   (*):    as-cast : 15406|47|0|-1

return to listing

AlCrFeNi (New)

    SSCC      :    as-cast, 5 x 10⁻⁴/s : tested at 20 °C (68 °F) : 15404|12|0|0
    YSC   (*):    as-cast : 15404|21|0|-1
    %El   (*):    as-cast : in compression : 15404|29|0|0
    UCS   (*):    as-cast : 15404|47|0|-1

return to listing

ALON

    E     (N*):    solid : 1966|3|0|-1
    G     (N*):    solid : 1966|11|0|-1
    v     (N*):    solid : 1966|19|0|-1
    K     (N*):    solid : 1966|27|0|-1

return to listing

AZ31

    DLL    (R):    F temper : casting : 1684|0|0|0
    DLL    (N):    T4 temper : casting : 1684|0|1|0
    DLL    (N):    average of F and T4 tempers : casting : 1684|0|2|0
    MTE    (R):    F temper : casting : 1684|8|0|0
    MTE    (N):    T4 temper : casting : 1684|8|1|0
    MTE    (N):    average of F and T4 tempers : casting : 1684|8|2|0
    SH     (R):    solid : 1684|9|0|-1
    CTE    (R):    F temper : casting : 1684|16|0|0
    CTE    (N):    T4 temper : casting : 1684|16|1|0
    CTE    (N):    average of F and T4 tempers : casting : 1684|16|2|0
    SR     (N):    F temper, 12.7 mm (0.5 inch) diameter extrusions : tested at 35 °C (95 °F) : 1684|22|0|0
    SR     (N):    F temper, 12.7 mm (0.5 inch) diameter extrusions : tested at 149 °C (300 °F) : 1684|22|0|1
    SR     (N):    F temper, 12.7 mm (0.5 inch) diameter extrusions : Master curve (LMP) : 1684|22|0|2
    SR     (N):    H24 temper, 0 mm (0. 64 inch) thick sheet : tested at 149 °C (300 °F) : 1684|22|1|0
    SR     (N):    H24 temper, 0 mm (0. 64 inch) thick sheet : tested at 232 °C (450 °F) : 1684|22|1|1
    SR     (N):    H24 temper, 0 mm (0. 64 inch) thick sheet : Master curve (LMP) : 1684|22|1|2
    D      (R):    solid : 1684|24|0|-1
    CRS    (N):    0.1% strain, O temper, sheet : tested at 93 °C (200 °F) : 1684|30|0|0
    CRS    (N):    0.1% strain, O temper, sheet : tested at 121 °C (250 °F) : 1684|30|0|1
    CRS    (N):    0.1% strain, O temper, sheet : tested at 149 °C (300 °F) : 1684|30|0|2
    CRS    (N):    0.1% strain, O temper, sheet : tested at 177 °C (350 °F) : 1684|30|0|3
    CRS    (N):    0.1% strain, O temper, sheet : Master curve (LMP) : 1684|30|0|4
    CRS    (N):    0.2% strain, O temper, sheet : tested at 93 °C (200 °F) : 1684|30|1|0
    CRS    (N):    0.2% strain, O temper, sheet : tested at 121 °C (250 °F) : 1684|30|1|1
    CRS    (N):    0.2% strain, O temper, sheet : tested at 149 °C (300 °F) : 1684|30|1|2
    CRS    (N):    0.2% strain, O temper, sheet : tested at 177 °C (350 °F) : 1684|30|1|3
    CRS    (N):    0.2% strain, O temper, sheet : Master curve (LMP) : 1684|30|1|4
    CRS    (N):    0.5% strain, O temper, sheet : tested at 93 °C (200 °F) : 1684|30|2|0
    CRS    (N):    0.5% strain, O temper, sheet : tested at 121 °C (250 °F) : 1684|30|2|1
    CRS    (N):    0.5% strain, O temper, sheet : tested at 149 °C (300 °F) : 1684|30|2|2
    CRS    (N):    0.5% strain, O temper, sheet : tested at 177 °C (350 °F) : 1684|30|2|3
    CRS    (N):    0.5% strain, O temper, sheet : Master curve (LMP) : 1684|30|2|4
    CRS    (N):    1% strain, O temper, sheet : tested at 93 °C (200 °F) : 1684|30|3|0
    CRS    (N):    1% strain, O temper, sheet : tested at 121 °C (250 °F) : 1684|30|3|1
    CRS    (N):    1% strain, O temper, sheet : tested at 149 °C (300 °F) : 1684|30|3|2
    CRS    (N):    1% strain, O temper, sheet : tested at 177 °C (350 °F) : 1684|30|3|3
    CRS    (N):    1% strain, O temper, sheet : Master curve (LMP) : 1684|30|3|4
    CRS    (N):    0.1% strain, F temper, extrusions : tested at 93 °C (200 °F) : 1684|30|4|0
    CRS    (N):    0.1% strain, F temper, extrusions : tested at 121 °C (250 °F) : 1684|30|4|1
    CRS    (N):    0.1% strain, F temper, extrusions : tested at 149 °C (300 °F) : 1684|30|4|2
    CRS    (N):    0.1% strain, F temper, extrusions : tested at 177 °C (350 °F) : 1684|30|4|3
    CRS    (N):    0.1% strain, F temper, extrusions : Master curve (LMP) : 1684|30|4|4
    CRS    (N):    0.2% strain, F temper, extrusions : tested at 93 °C (200 °F) : 1684|30|5|0
    CRS    (N):    0.2% strain, F temper, extrusions : tested at 121 °C (250 °F) : 1684|30|5|1
    CRS    (N):    0.2% strain, F temper, extrusions : tested at 149 °C (300 °F) : 1684|30|5|2
    CRS    (N):    0.2% strain, F temper, extrusions : tested at 177 °C (350 °F) : 1684|30|5|3
    CRS    (N):    0.2% strain, F temper, extrusions : Master curve (LMP) : 1684|30|5|4
    CRS    (N):    0.5% strain, F temper, extrusions : tested at 93 °C (200 °F) : 1684|30|6|0
    CRS    (N):    0.5% strain, F temper, extrusions : tested at 121 °C (250 °F) : 1684|30|6|1
    CRS    (N):    0.5% strain, F temper, extrusions : tested at 149 °C (300 °F) : 1684|30|6|2
    CRS    (N):    0.5% strain, F temper, extrusions : tested at 177 °C (350 °F) : 1684|30|6|3
    CRS    (N):    0.5% strain, F temper, extrusions : Master curve (LMP) : 1684|30|6|4
    CRS    (N):    1% strain, F temper, extrusions : tested at 93 °C (200 °F) : 1684|30|7|0
    CRS    (N):    1% strain, F temper, extrusions : tested at 121 °C (250 °F) : 1684|30|7|1
    CRS    (N):    1% strain, F temper, extrusions : tested at 149 °C (300 °F) : 1684|30|7|2
    CRS    (N):    1% strain, F temper, extrusions : tested at 177 °C (350 °F) : 1684|30|7|3
    CRS    (N):    1% strain, F temper, extrusions : Master curve (LMP) : 1684|30|7|4
    CRS    (N):    0.1% strain, H24 temper, sheet : tested at 93 °C (200 °F) : 1684|30|8|0
    CRS    (N):    0.1% strain, H24 temper, sheet : tested at 121 °C (250 °F) : 1684|30|8|1
    CRS    (N):    0.1% strain, H24 temper, sheet : tested at 149 °C (300 °F) : 1684|30|8|2
    CRS    (N):    0.1% strain, H24 temper, sheet : tested at 177 °C (350 °F) : 1684|30|8|3
    CRS    (N):    0.1% strain, H24 temper, sheet : Master curve (LMP) : 1684|30|8|4
    CRS    (N):    0.2% strain, H24 temper, sheet : tested at 93 °C (200 °F) : 1684|30|9|0
    CRS    (N):    0.2% strain, H24 temper, sheet : tested at 121 °C (250 °F) : 1684|30|9|1
    CRS    (N):    0.2% strain, H24 temper, sheet : tested at 149 °C (300 °F) : 1684|30|9|2
    CRS    (N):    0.2% strain, H24 temper, sheet : tested at 177 °C (350 °F) : 1684|30|9|3
    CRS    (N):    0.2% strain, H24 temper, sheet : Master curve (LMP) : 1684|30|9|4
    CRS    (N):    0.5% strain, H24 temper, sheet : tested at 93 °C (200 °F) : 1684|30|10|0
    CRS    (N):    0.5% strain, H24 temper, sheet : tested at 121 °C (250 °F) : 1684|30|10|1
    CRS    (N):    0.5% strain, H24 temper, sheet : tested at 149 °C (300 °F) : 1684|30|10|2
    CRS    (N):    0.5% strain, H24 temper, sheet : tested at 177 °C (350 °F) : 1684|30|10|3
    CRS    (N):    0.5% strain, H24 temper, sheet : Master curve (LMP) : 1684|30|10|4
    CRS    (N):    1% strain, H24 temper, sheet : tested at 93 °C (200 °F) : 1684|30|11|0
    CRS    (N):    1% strain, H24 temper, sheet : tested at 121 °C (250 °F) : 1684|30|11|1
    CRS    (N):    1% strain, H24 temper, sheet : tested at 149 °C (300 °F) : 1684|30|11|2
    CRS    (N):    1% strain, H24 temper, sheet : tested at 177 °C (350 °F) : 1684|30|11|3
    CRS    (N):    1% strain, H24 temper, sheet : Master curve (LMP) : 1684|30|11|4
    IC     (N):    tested at 93 °C (200 °F), O temper, sheet : 1 h : 1684|39|0|0
    IC     (N):    tested at 93 °C (200 °F), O temper, sheet : 3 h : 1684|39|0|1
    IC     (N):    tested at 93 °C (200 °F), O temper, sheet : 10 h : 1684|39|0|2
    IC     (N):    tested at 93 °C (200 °F), O temper, sheet : 30 h : 1684|39|0|3
    IC     (N):    tested at 93 °C (200 °F), O temper, sheet : 100 h : 1684|39|0|4
    IC     (N):    tested at 93 °C (200 °F), O temper, sheet : 300 h : 1684|39|0|5
    IC     (N):    tested at 93 °C (200 °F), O temper, sheet : 500 h : 1684|39|0|6
    IC     (N):    tested at 121 °C (250 °F), O temper, sheet : 1 h : 1684|39|1|0
    IC     (N):    tested at 121 °C (250 °F), O temper, sheet : 3 h : 1684|39|1|1
    IC     (N):    tested at 121 °C (250 °F), O temper, sheet : 10 h : 1684|39|1|2
    IC     (N):    tested at 121 °C (250 °F), O temper, sheet : 30 h : 1684|39|1|3
    IC     (N):    tested at 121 °C (250 °F), O temper, sheet : 100 h : 1684|39|1|4
    IC     (N):    tested at 121 °C (250 °F), O temper, sheet : 300 h : 1684|39|1|5
    IC     (N):    tested at 121 °C (250 °F), O temper, sheet : 500 h : 1684|39|1|6
    IC     (N):    tested at 149 °C (300 °F), O temper, sheet : 1 h : 1684|39|2|0
    IC     (N):    tested at 149 °C (300 °F), O temper, sheet : 3 h : 1684|39|2|1
    IC     (N):    tested at 149 °C (300 °F), O temper, sheet : 10 h : 1684|39|2|2
    IC     (N):    tested at 149 °C (300 °F), O temper, sheet : 30 h : 1684|39|2|3
    IC     (N):    tested at 149 °C (300 °F), O temper, sheet : 100 h : 1684|39|2|4
    IC     (N):    tested at 149 °C (300 °F), O temper, sheet : 300 h : 1684|39|2|5
    IC     (N):    tested at 149 °C (300 °F), O temper, sheet : 500 h : 1684|39|2|6
    IC     (N):    tested at 177 °C (350 °F), O temper, sheet : 1 h : 1684|39|3|0
    IC     (N):    tested at 177 °C (350 °F), O temper, sheet : 3 h : 1684|39|3|1
    IC     (N):    tested at 177 °C (350 °F), O temper, sheet : 10 h : 1684|39|3|2
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 1 h : 1684|39|4|0
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 3 h : 1684|39|4|1
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 10 h : 1684|39|4|2
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 30 h : 1684|39|4|3
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 100 h : 1684|39|4|4
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 300 h : 1684|39|4|5
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 500 h : 1684|39|4|6
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 1 h : 1684|39|5|0
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 3 h : 1684|39|5|1
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 10 h : 1684|39|5|2
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 30 h : 1684|39|5|3
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 100 h : 1684|39|5|4
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 300 h : 1684|39|5|5
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 500 h : 1684|39|5|6
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 1 h : 1684|39|6|0
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 3 h : 1684|39|6|1
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 10 h : 1684|39|6|2
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 30 h : 1684|39|6|3
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 100 h : 1684|39|6|4
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 300 h : 1684|39|6|5
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 500 h : 1684|39|6|6
    IC     (N):    tested at 177 °C (350 °F), F temper, extrusions : 1 h : 1684|39|7|0
    IC     (N):    tested at 177 °C (350 °F), F temper, extrusions : 3 h : 1684|39|7|1
    IC     (N):    tested at 177 °C (350 °F), F temper, extrusions : 10 h : 1684|39|7|2
    IC     (N):    tested at 93 °C (200 °F), H24 temper, sheet : 1 h : 1684|39|8|0
    IC     (N):    tested at 93 °C (200 °F), H24 temper, sheet : 3 h : 1684|39|8|1
    IC     (N):    tested at 93 °C (200 °F), H24 temper, sheet : 10 h : 1684|39|8|2
    IC     (N):    tested at 93 °C (200 °F), H24 temper, sheet : 30 h : 1684|39|8|3
    IC     (N):    tested at 93 °C (200 °F), H24 temper, sheet : 100 h : 1684|39|8|4
    IC     (N):    tested at 93 °C (200 °F), H24 temper, sheet : 300 h : 1684|39|8|5
    IC     (N):    tested at 93 °C (200 °F), H24 temper, sheet : 500 h : 1684|39|8|6
    IC     (N):    tested at 121 °C (250 °F), H24 temper, sheet : 1 h : 1684|39|9|0
    IC     (N):    tested at 121 °C (250 °F), H24 temper, sheet : 3 h : 1684|39|9|1
    IC     (N):    tested at 121 °C (250 °F), H24 temper, sheet : 10 h : 1684|39|9|2
    IC     (N):    tested at 121 °C (250 °F), H24 temper, sheet : 30 h : 1684|39|9|3
    IC     (N):    tested at 121 °C (250 °F), H24 temper, sheet : 100 h : 1684|39|9|4
    IC     (N):    tested at 121 °C (250 °F), H24 temper, sheet : 300 h : 1684|39|9|5
    IC     (N):    tested at 121 °C (250 °F), H24 temper, sheet : 500 h : 1684|39|9|6
    IC     (N):    tested at 149 °C (300 °F), H24 temper, sheet : 1 h : 1684|39|10|0
    IC     (N):    tested at 149 °C (300 °F), H24 temper, sheet : 3 h : 1684|39|10|1
    IC     (N):    tested at 149 °C (300 °F), H24 temper, sheet : 10 h : 1684|39|10|2
    IC     (N):    tested at 149 °C (300 °F), H24 temper, sheet : 30 h : 1684|39|10|3
    IC     (N):    tested at 149 °C (300 °F), H24 temper, sheet : 100 h : 1684|39|10|4
    IC     (N):    tested at 149 °C (300 °F), H24 temper, sheet : 300 h : 1684|39|10|5
    IC     (N):    tested at 149 °C (300 °F), H24 temper, sheet : 500 h : 1684|39|10|6
    IC     (N):    tested at 177 °C (350 °F), H24 temper, sheet : 1 h : 1684|39|11|0
    IC     (N):    tested at 177 °C (350 °F), H24 temper, sheet : 3 h : 1684|39|11|1
    IC     (N):    tested at 177 °C (350 °F), H24 temper, sheet : 10 h : 1684|39|11|2

return to listing

AZ61

    SR     (N):    F temper, 19 mm (0.75 inch) diameter extrusions : tested at 35 °C (95 °F) : 1685|22|0|0
    SR     (N):    F temper, 19 mm (0.75 inch) diameter extrusions : tested at 149 °C (300 °F) : 1685|22|0|1
    CRS    (N):    0.1% strain, F temper, extrusions : tested at 93 °C (200 °F) : 1685|30|4|0
    CRS    (N):    0.1% strain, F temper, extrusions : tested at 121 °C (250 °F) : 1685|30|4|1
    CRS    (N):    0.1% strain, F temper, extrusions : tested at 149 °C (300 °F) : 1685|30|4|2
    CRS    (N):    0.1% strain, F temper, extrusions : Master curve (LMP) : 1685|30|4|4
    CRS    (N):    0.2% strain, F temper, extrusions : tested at 93 °C (200 °F) : 1685|30|5|0
    CRS    (N):    0.2% strain, F temper, extrusions : tested at 121 °C (250 °F) : 1685|30|5|1
    CRS    (N):    0.2% strain, F temper, extrusions : tested at 149 °C (300 °F) : 1685|30|5|2
    CRS    (N):    0.2% strain, F temper, extrusions : tested at 177 °C (350 °F) : 1685|30|5|3
    CRS    (N):    0.5% strain, F temper, extrusions : tested at 93 °C (200 °F) : 1685|30|6|0
    CRS    (N):    0.5% strain, F temper, extrusions : tested at 121 °C (250 °F) : 1685|30|6|1
    CRS    (N):    0.5% strain, F temper, extrusions : tested at 149 °C (300 °F) : 1685|30|6|2
    CRS    (N):    0.5% strain, F temper, extrusions : tested at 177 °C (350 °F) : 1685|30|6|3
    CRS    (N):    0.5% strain, F temper, extrusions : Master curve (LMP) : 1685|30|6|4
    CRS    (N):    1% strain, F temper, extrusions : tested at 93 °C (200 °F) : 1685|30|7|0
    CRS    (N):    1% strain, F temper, extrusions : tested at 121 °C (250 °F) : 1685|30|7|1
    CRS    (N):    1% strain, F temper, extrusions : tested at 149 °C (300 °F) : 1685|30|7|2
    CRS    (N):    1% strain, F temper, extrusions : tested at 177 °C (350 °F) : 1685|30|7|3
    CRS    (N):    1% strain, F temper, extrusions : Master curve (LMP) : 1685|30|7|4
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 1 h : 1685|39|1|0
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 3 h : 1685|39|1|1
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 10 h : 1685|39|1|2
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 30 h : 1685|39|1|3
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 100 h : 1685|39|1|4
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 300 h : 1685|39|1|5
    IC     (N):    tested at 93 °C (200 °F), F temper, extrusions : 500 h : 1685|39|1|6
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 1 h : 1685|39|2|0
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 3 h : 1685|39|2|1
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 10 h : 1685|39|2|2
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 30 h : 1685|39|2|3
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 100 h : 1685|39|2|4
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 300 h : 1685|39|2|5
    IC     (N):    tested at 121 °C (250 °F), F temper, extrusions : 500 h : 1685|39|2|6
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 1 h : 1685|39|3|0
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 3 h : 1685|39|3|1
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 10 h : 1685|39|3|2
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 30 h : 1685|39|3|3
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 100 h : 1685|39|3|4
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 300 h : 1685|39|3|5
    IC     (N):    tested at 149 °C (300 °F), F temper, extrusions : 500 h : 1685|39|3|6
    IC     (N):    tested at 177 °C (350 °F), F temper, extrusions : 1 h : 1685|39|4|0
    IC     (N):    tested at 177 °C (350 °F), F temper, extrusions : 3 h : 1685|39|4|1
    IC     (N):    tested at 177 °C (350 °F), F temper, extrusions : 10 h : 1685|39|4|2

return to listing

AZ63

    DLL    (N):    solid : F temper : 1686|0|0|0
    DLL    (N):    solid : T4 temper : 1686|0|0|1
    DLL    (N):    solid : T5 temper : 1686|0|0|2
    DLL    (N):    solid : T6 temper : 1686|0|0|3
    DLL    (N):    solid : average of all tempers : 1686|0|0|4
    UTS    (N):    T6 temper : sand castings : 1686|5|0|0
    MTE    (N):    solid : F temper : 1686|8|0|0
    MTE    (N):    solid : T4 temper : 1686|8|0|1
    MTE    (N):    solid : T5 temper : 1686|8|0|2
    MTE    (N):    solid : T6 temper : 1686|8|0|3
    MTE    (N):    solid : average of all tempers : 1686|8|0|4
    YS     (N):    T6 temper : sand castings : 1686|13|0|0
    CTE    (N):    solid : F temper : 1686|16|0|0
    CTE    (N):    solid : T4 temper : 1686|16|0|1
    CTE    (N):    solid : T5 temper : 1686|16|0|2
    CTE    (N):    solid : T6 temper : 1686|16|0|3
    CTE    (N):    solid : average of all tempers : 1686|16|0|4
    SR     (N):    T6 temper, sand castings : tested at 35 °C (95 °F) : 1686|22|0|0
    SR     (N):    T6 temper, sand castings : tested at 149 °C (300 °F) : 1686|22|0|1
    SR     (N):    T6 temper, sand castings : Master curve (LMP) : 1686|22|0|2
    D      (R):    solid : 1686|24|0|-1
    TD     (N):    solid : F temper, sand cast : 1686|25|0|0
    %El    (N):    T6 temper : sand castings : 1686|29|0|0
    CRS    (N):    0.1% strain, T6 temper, sand castings : tested at 93 °C (200 °F) : 1686|30|0|0
    CRS    (N):    0.1% strain, T6 temper, sand castings : tested at 149 °C (300 °F) : 1686|30|0|1
    CRS    (N):    0.1% strain, T6 temper, sand castings : tested at 204 °C (400 °F) : 1686|30|0|2
    CRS    (N):    0.1% strain, T6 temper, sand castings : Master curve (LMP) : 1686|30|0|4
    CRS    (N):    0.2% strain, T6 temper, sand castings : tested at 93 °C (200 °F) : 1686|30|1|0
    CRS    (N):    0.2% strain, T6 temper, sand castings : tested at 149 °C (300 °F) : 1686|30|1|1
    CRS    (N):    0.2% strain, T6 temper, sand castings : tested at 204 °C (400 °F) : 1686|30|1|2
    CRS    (N):    0.2% strain, T6 temper, sand castings : tested at 260 °C (500 °F) : 1686|30|1|3
    CRS    (N):    0.2% strain, T6 temper, sand castings : Master curve (LMP) : 1686|30|1|4
    CRS    (N):    0.5% strain, T6 temper, sand castings : tested at 93 °C (200 °F) : 1686|30|2|0
    CRS    (N):    0.5% strain, T6 temper, sand castings : tested at 149 °C (300 °F) : 1686|30|2|1
    CRS    (N):    0.5% strain, T6 temper, sand castings : tested at 204 °C (400 °F) : 1686|30|2|2
    CRS    (N):    0.5% strain, T6 temper, sand castings : tested at 260 °C (500 °F) : 1686|30|2|3
    CRS    (N):    0.5% strain, T6 temper, sand castings : Master curve (LMP) : 1686|30|2|4
    CRS    (N):    1% strain, T6 temper, sand castings : tested at 93 °C (200 °F) : 1686|30|3|0
    CRS    (N):    1% strain, T6 temper, sand castings : tested at 149 °C (300 °F) : 1686|30|3|1
    CRS    (N):    1% strain, T6 temper, sand castings : tested at 204 °C (400 °F) : 1686|30|3|2
    CRS    (N):    1% strain, T6 temper, sand castings : tested at 260 °C (500 °F) : 1686|30|3|3
    CRS    (N):    1% strain, T6 temper, sand castings : Master curve (LMP) : 1686|30|3|4
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand castings : 1 h : 1686|39|0|0
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand castings : 3 h : 1686|39|0|1
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand castings : 10 h : 1686|39|0|2
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand castings : 30 h : 1686|39|0|3
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand castings : 100 h : 1686|39|0|4
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand castings : 300 h : 1686|39|0|5
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand castings : 1,000 h : 1686|39|0|6
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand castings : 1 h : 1686|39|1|0
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand castings : 3 h : 1686|39|1|1
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand castings : 10 h : 1686|39|1|2
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand castings : 30 h : 1686|39|1|3
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand castings : 100 h : 1686|39|1|4
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand castings : 300 h : 1686|39|1|5
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand castings : 1,000 h : 1686|39|1|6
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 1 h : 1686|39|2|0
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 3 h : 1686|39|2|1
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 10 h : 1686|39|2|2
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 1 h : 1686|39|3|0
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 3 h : 1686|39|3|1
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 10 h : 1686|39|3|2

return to listing

AZ92

    SR     (N):    T6 temper, sand castings : tested at 35 °C (95 °F) : 1690|22|0|0
    SR     (N):    T6 temper, sand castings : tested at 121 °C (250 °F) : 1690|22|0|1
    SR     (N):    T6 temper, sand castings : tested at 149 °C (300 °F) : 1690|22|0|2
    SR     (N):    T6 temper, sand castings : Master curve (LMP) : 1690|22|0|3
    CRS    (N):    0.1% strain, T6 temper, sand cast bars : tested at 93 °C (200 °F) : 1690|30|0|0
    CRS    (N):    0.1% strain, T6 temper, sand cast bars : tested at 149 °C (300 °F) : 1690|30|0|1
    CRS    (N):    0.1% strain, T6 temper, sand cast bars : tested at 204 °C (400 °F) : 1690|30|0|2
    CRS    (N):    0.1% strain, T6 temper, sand cast bars : Master curve (LMP) : 1690|30|0|4
    CRS    (N):    0.2% strain, T6 temper, sand cast bars : tested at 93 °C (200 °F) : 1690|30|1|0
    CRS    (N):    0.2% strain, T6 temper, sand cast bars : tested at 149 °C (300 °F) : 1690|30|1|1
    CRS    (N):    0.2% strain, T6 temper, sand cast bars : tested at 204 °C (400 °F) : 1690|30|1|2
    CRS    (N):    0.2% strain, T6 temper, sand cast bars : tested at 260 °C (500 °F) : 1690|30|1|3
    CRS    (N):    0.2% strain, T6 temper, sand cast bars : Master curve (LMP) : 1690|30|1|4
    CRS    (N):    0.5% strain, T6 temper, sand cast bars : tested at 93 °C (200 °F) : 1690|30|2|0
    CRS    (N):    0.5% strain, T6 temper, sand cast bars : tested at 149 °C (300 °F) : 1690|30|2|1
    CRS    (N):    0.5% strain, T6 temper, sand cast bars : tested at 204 °C (400 °F) : 1690|30|2|2
    CRS    (N):    0.5% strain, T6 temper, sand cast bars : tested at 260 °C (500 °F) : 1690|30|2|3
    CRS    (N):    0.5% strain, T6 temper, sand cast bars : Master curve (LMP) : 1690|30|2|4
    CRS    (N):    1% strain, T6 temper, sand cast bars : tested at 93 °C (200 °F) : 1690|30|3|0
    CRS    (N):    1% strain, T6 temper, sand cast bars : tested at 149 °C (300 °F) : 1690|30|3|1
    CRS    (N):    1% strain, T6 temper, sand cast bars : tested at 204 °C (400 °F) : 1690|30|3|2
    CRS    (N):    1% strain, T6 temper, sand cast bars : tested at 260 °C (500 °F) : 1690|30|3|3
    CRS    (N):    1% strain, T6 temper, sand cast bars : Master curve (LMP) : 1690|30|3|4
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand cast bars : 1 h : 1690|39|0|0
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand cast bars : 3 h : 1690|39|0|1
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand cast bars : 10 h : 1690|39|0|2
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand cast bars : 30 h : 1690|39|0|3
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand cast bars : 100 h : 1690|39|0|4
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand cast bars : 300 h : 1690|39|0|5
    IC     (N):    tested at 93 °C (200 °F), T6 temper, sand cast bars : 1,000 h : 1690|39|0|6
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand cast bars : 1 h : 1690|39|1|0
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand cast bars : 3 h : 1690|39|1|1
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand cast bars : 10 h : 1690|39|1|2
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand cast bars : 30 h : 1690|39|1|3
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand cast bars : 100 h : 1690|39|1|4
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand cast bars : 300 h : 1690|39|1|5
    IC     (N):    tested at 149 °C (300 °F), T6 temper, sand cast bars : 1,000 h : 1690|39|1|6
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand cast bars : 1 h : 1690|39|2|0
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand cast bars : 3 h : 1690|39|2|1
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand cast bars : 10 h : 1690|39|2|2
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand cast bars : 30 h : 1690|39|2|3
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand cast bars : 100 h : 1690|39|2|4
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand cast bars : 300 h : 1690|39|2|5
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand cast bars : 1,000 h : 1690|39|2|6
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand cast bars : 1 h : 1690|39|3|0
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand cast bars : 3 h : 1690|39|3|1
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand cast bars : 10 h : 1690|39|3|2

return to listing

Bi₂Te₂.₇Se₀.₃ (n-type)

    TC     (R):    solid : undoped : 14642|1|0|0
    TC     (N):    solid : 0.5 wt% La2O3 : 14642|1|0|1
    TC     (N):    solid : 1 wt% La2O3 : 14642|1|0|2
    TC     (N):    solid : 1.5 wt% La2O3 : 14642|1|0|3
    RHO    (R):    solid : undoped : 14642|2|0|0
    RHO    (N):    solid : 0.5 wt% La2O3 : 14642|2|0|1
    RHO    (N):    solid : 1 wt% La2O3 : 14642|2|0|2
    RHO    (N):    solid : 1.5 wt% La2O3 : 14642|2|0|3
    SIGMA (R):    solid : undoped : 14642|10|0|0
    SIGMA (N):    solid : 0.5 wt% La2O3 : 14642|10|0|1
    SIGMA (N):    solid : 1 wt% La2O3 : 14642|10|0|2
    SIGMA (N):    solid : 1.5 wt% La2O3 : 14642|10|0|3

return to listing

Cd - 10.4 Sb (wt%) (New)

    Vis       :    liquid : 15388|26|1|-1

return to listing

Cd - 24 Sb (wt%) (New)

    Vis       :    liquid : 15385|26|1|-1

return to listing

Cd - 48.6 Sb (wt%) (New)

    Vis       :    liquid : 15390|26|1|-1

return to listing

Cd - 5 Sb (wt%) (New)

    Vis       :    liquid : 15386|26|1|-1

return to listing

Cd - 52 Sb (wt%) (New)

    Vis       :    liquid : 15392|26|1|-1

return to listing

Cd - 55 Sb (wt%) (New)

    Vis       :    liquid : 15393|26|1|-1

return to listing

Cd - 58.5 Sb (wt%) (New)

    Vis       :    liquid : 15391|26|1|-1

return to listing

Cd - 65 Sb (wt%) (New)

    Vis       :    liquid : 15394|26|1|-1

return to listing

Cd - 7.7 Sb (wt%) (New)

    Vis       :    liquid : 15387|26|1|-1

return to listing

Cd - 88 Sb (wt%) (New)

    Vis       :    liquid : 15389|26|1|-1

return to listing

Ce₄RuMg (New)

    SH        :    solid : 15409|9|0|-1
    HC        :    solid : 15409|17|0|-1

return to listing

CeRuAl (New)

    SH        :    solid : 15412|9|0|-1
    HC        :    solid : 15412|17|0|-1
    D     (*):    solid : 15412|24|0|-1

return to listing

CoCrFe₀.₂MnNi (New)

    SSC       :    as-cast, 0.001/s : tested at 20 °C (68 °F) : 15375|4|0|0
    UTS   (*):    as-cast : 15375|5|0|-1
    YS    (*):    as-cast : 15375|13|0|-1
    %El   (*):    as-cast : 15375|29|0|-1

return to listing

CoCrFe₁₆MnNi (New)

    SSC       :    as-cast, 0.001/s : tested at 20 °C (68 °F) : 15378|4|0|0
    UTS   (*):    as-cast : 15378|5|0|-1
    YS    (*):    as-cast : 15378|13|0|-1
    %El   (*):    as-cast : 15378|29|0|-1

return to listing

CoCrFe₄MnNi (New)

    SSC       :    as-cast, 0.001/s : tested at 20 °C (68 °F) : 15376|4|0|0
    UTS   (*):    as-cast : 15376|5|0|-1
    YS    (*):    as-cast : 15376|13|0|-1
    %El   (*):    as-cast : 15376|29|0|-1

return to listing

CoCrFe₈MnNi (New)

    SSC       :    as-cast, 0.001/s : tested at 20 °C (68 °F) : 15377|4|0|0
    UTS   (*):    as-cast : 15377|5|0|-1
    YS    (*):    as-cast : 15377|13|0|-1
    %El   (*):    as-cast : 15377|29|0|-1

return to listing

CoMnP₂O₇ (New)

    RHO       :    AC value : 10 kHz : 15407|2|0|0
    RHO       :    AC value : 100 kHz : 15407|2|0|1
    RHO       :    AC value : 1 MHz : 15407|2|0|2
    SIGMA    :    AC value : 10 kHz : 15407|10|0|0
    SIGMA    :    AC value : 100 kHz : 15407|10|0|1
    SIGMA    :    AC value : 1 MHz : 15407|10|0|2
    D     (*):    solid : 15407|24|0|-1

return to listing

Corning 1724

    DLL    (R):    solid : 1411|0|0|-1
    MTE    (R):    solid : 1411|8|0|-1
    CTE    (R):    solid : 1411|16|0|-1
    D      (R):    solid : 1411|24|0|-1

return to listing

Cu₂Se (New)

    TC        :    solid : monoclinic structure, space group C2/c : 15411|1|0|0
    TC        :    solid : cubic structure, space group Fm-3m : 15411|1|0|1
    RHO       :    solid : monoclinic structure, space group C2/c : 15411|2|0|0
    RHO       :    solid : cubic structure, space group Fm-3m : 15411|2|0|1
    SIGMA    :    solid : monoclinic structure, space group C2/c : 15411|10|0|0
    SIGMA    :    solid : cubic structure, space group Fm-3m : 15411|10|0|1
    D     (*):    solid : monoclinic structure, space group C2/c : 15411|24|0|0

return to listing

CuAlO₂

    TC     (N):    solid : 91.7% dense : 9782|1|0|0

return to listing

CuGe₂P₃ (New)

    TC        :    solid : non-stoichiometric, Cu0.89Si2.72P2.39 : 15398|1|0|0
    RHO       :    solid : non-stoichiometric, Cu0.89Si2.72P2.39 : 15398|2|0|0
    SIGMA    :    solid : non-stoichiometric, Cu0.89Si2.72P2.39 : 15398|10|0|0
    D     (*):    solid : 15398|24|0|-1

return to listing

CuGe₄P₃ (New)

    TC        :    solid : non-stoichiometric, Cu0.95Si4.48P2.57 : 15399|1|0|0
    RHO       :    solid : non-stoichiometric, Cu0.95Si4.48P2.57 : 15399|2|0|0
    SIGMA    :    solid : non-stoichiometric, Cu0.95Si4.48P2.57 : 15399|10|0|0
    D     (*):    solid : 15399|24|0|-1

return to listing

CuSi₂P₃ (New)

    TC        :    solid : non-stoichiometric, Cu0.84Si2.16P3 : 15397|1|0|0
    RHO       :    solid : non-stoichiometric, Cu0.84Si2.16P3 : 15397|2|0|0
    SIGMA    :    solid : non-stoichiometric, Cu0.84Si2.16P3 : 15397|10|0|0
    D     (*):    solid : 15397|24|0|-1

return to listing

CuSi₄P₃

    D      (N):    solid : 2536|24|0|-1

return to listing

EK30

    UTS    (N):    T6 temper : sand castings : 1707|5|0|0
    YS     (N):    T6 temper : sand castings : 1707|13|0|0
    CRS    (N):    0.1% strain, T6 temper, sand castings : tested at 204 °C (400 °F) : 1707|30|0|0
    CRS    (N):    0.1% strain, T6 temper, sand castings : tested at 260 °C (500 °F) : 1707|30|0|1
    CRS    (N):    0.1% strain, T6 temper, sand castings : tested at 316 °C (600 °F) : 1707|30|0|2
    CRS    (N):    0.1% strain, T6 temper, sand castings : Master curve (LMP) : 1707|30|0|3
    CRS    (N):    0.2% strain, T6 temper, sand castings : tested at 204 °C (400 °F) : 1707|30|1|0
    CRS    (N):    0.2% strain, T6 temper, sand castings : tested at 260 °C (500 °F) : 1707|30|1|1
    CRS    (N):    0.2% strain, T6 temper, sand castings : tested at 316 °C (600 °F) : 1707|30|1|2
    CRS    (N):    0.2% strain, T6 temper, sand castings : Master curve (LMP) : 1707|30|1|3
    CRS    (N):    0.5% strain, T6 temper, sand castings : tested at 204 °C (400 °F) : 1707|30|2|0
    CRS    (N):    0.5% strain, T6 temper, sand castings : tested at 260 °C (500 °F) : 1707|30|2|1
    CRS    (N):    0.5% strain, T6 temper, sand castings : tested at 316 °C (600 °F) : 1707|30|2|2
    CRS    (N):    0.5% strain, T6 temper, sand castings : Master curve (LMP) : 1707|30|2|3
    CRS    (N):    1% strain, T6 temper, sand castings : tested at 204 °C (400 °F) : 1707|30|3|0
    CRS    (N):    1% strain, T6 temper, sand castings : tested at 260 °C (500 °F) : 1707|30|3|1
    CRS    (N):    1% strain, T6 temper, sand castings : tested at 316 °C (600 °F) : 1707|30|3|2
    CRS    (N):    1% strain, T6 temper, sand castings : Master curve (LMP) : 1707|30|3|3
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 1 h : 1707|39|0|0
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 3 h : 1707|39|0|1
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 10 h : 1707|39|0|2
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 30 h : 1707|39|0|3
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 100 h : 1707|39|0|4
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 300 h : 1707|39|0|5
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 1,000 h : 1707|39|0|6
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 1 h : 1707|39|1|0
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 3 h : 1707|39|1|1
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 10 h : 1707|39|1|2
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 30 h : 1707|39|1|3
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 100 h : 1707|39|1|4
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 300 h : 1707|39|1|5
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 1,000 h : 1707|39|1|6
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 1 h : 1707|39|2|0
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 3 h : 1707|39|2|1
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 10 h : 1707|39|2|2
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 30 h : 1707|39|2|3
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 100 h : 1707|39|2|4
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 300 h : 1707|39|2|5
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 1,000 h : 1707|39|2|6

return to listing

EK41

    UTS    (N):    T5 temper : sand castings : 1708|5|0|0
    UTS    (N):    T6 temper : sand castings : 1708|5|1|0
    YS     (N):    T5 temper : sand castings : 1708|13|0|0
    YS     (N):    T6 temper : sand castings : 1708|13|1|0
    %El    (N):    T5 temper : sand castings : 1708|29|0|0
    %El    (N):    T6 temper : sand castings : 1708|29|1|0
    CRS    (N):    0.1% strain, T6 temper, sand castings : tested at 204 °C (400 °F) : 1708|30|0|0
    CRS    (N):    0.1% strain, T6 temper, sand castings : tested at 316 °C (600 °F) : 1708|30|0|1
    CRS    (N):    0.1% strain, T6 temper, sand castings : Master curve (LMP) : 1708|30|0|2
    CRS    (N):    0.2% strain, T6 temper, sand castings : tested at 204 °C (400 °F) : 1708|30|1|0
    CRS    (N):    0.2% strain, T6 temper, sand castings : tested at 316 °C (600 °F) : 1708|30|1|1
    CRS    (N):    0.2% strain, T6 temper, sand castings : Master curve (LMP) : 1708|30|1|2
    CRS    (N):    0.5% strain, T6 temper, sand castings : tested at 204 °C (400 °F) : 1708|30|2|0
    CRS    (N):    0.5% strain, T6 temper, sand castings : tested at 316 °C (600 °F) : 1708|30|2|1
    CRS    (N):    0.5% strain, T6 temper, sand castings : Master curve (LMP) : 1708|30|2|2
    CRS    (N):    1% strain, T6 temper, sand castings : tested at 204 °C (400 °F) : 1708|30|3|0
    CRS    (N):    1% strain, T6 temper, sand castings : tested at 316 °C (600 °F) : 1708|30|3|1
    CRS    (N):    1% strain, T6 temper, sand castings : Master curve (LMP) : 1708|30|3|2
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 1 h : 1708|39|0|0
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 3 h : 1708|39|0|1
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 10 h : 1708|39|0|2
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 30 h : 1708|39|0|3
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 100 h : 1708|39|0|4
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 300 h : 1708|39|0|5
    IC     (N):    tested at 204 °C (400 °F), T6 temper, sand castings : 1,000 h : 1708|39|0|6
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 1 h : 1708|39|1|0
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 3 h : 1708|39|1|1
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 10 h : 1708|39|1|2
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 30 h : 1708|39|1|3
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 100 h : 1708|39|1|4
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 300 h : 1708|39|1|5
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 1,000 h : 1708|39|1|6

return to listing

EZ33

    SR     (N):    T5 temper, sand castings : tested at 204 °C (400 °F) : 1697|22|0|0
    SR     (N):    T5 temper, sand castings : tested at 316 °C (600 °F) : 1697|22|0|1
    SR     (N):    T5 temper, sand castings : Master curve (LMP) : 1697|22|0|2
    CRS    (N):    0.1% strain (total), T5 temper, sand castings : tested at 204 °C (400 °F) : 1697|30|4|0
    CRS    (N):    0.1% strain (total), T5 temper, sand castings : tested at 260 °C (500 °F) : 1697|30|4|1
    CRS    (N):    0.1% strain (total), T5 temper, sand castings : tested at 316 °C (600 °F) : 1697|30|4|2
    CRS    (N):    0.1% strain (total), T5 temper, sand castings : Master curve (LMP) : 1697|30|4|3
    CRS    (N):    0.2% strain (total), T5 temper, sand castings : tested at 204 °C (400 °F) : 1697|30|5|0
    CRS    (N):    0.2% strain (total), T5 temper, sand castings : tested at 260 °C (500 °F) : 1697|30|5|1
    CRS    (N):    0.2% strain (total), T5 temper, sand castings : tested at 316 °C (600 °F) : 1697|30|5|2
    CRS    (N):    0.2% strain (total), T5 temper, sand castings : Master curve (LMP) : 1697|30|5|3
    CRS    (N):    0.5% strain (total), T5 temper, sand castings : tested at 204 °C (400 °F) : 1697|30|6|0
    CRS    (N):    0.5% strain (total), T5 temper, sand castings : tested at 260 °C (500 °F) : 1697|30|6|1
    CRS    (N):    0.5% strain (total), T5 temper, sand castings : tested at 316 °C (600 °F) : 1697|30|6|2
    CRS    (N):    0.5% strain (total), T5 temper, sand castings : Master curve (LMP) : 1697|30|6|3
    CRS    (N):    1% strain (total), T5 temper, sand castings : tested at 204 °C (400 °F) : 1697|30|7|0
    CRS    (N):    1% strain (total), T5 temper, sand castings : tested at 260 °C (500 °F) : 1697|30|7|1
    CRS    (N):    1% strain (total), T5 temper, sand castings : tested at 316 °C (600 °F) : 1697|30|7|2
    CRS    (N):    1% strain (total), T5 temper, sand castings : Master curve (LMP) : 1697|30|7|3
    IC     (N):    tested at 204 °C (400 °F), (total), T5 temper, sand castings : 1 h : 1697|39|6|0
    IC     (N):    tested at 204 °C (400 °F), (total), T5 temper, sand castings : 3 h : 1697|39|6|1
    IC     (N):    tested at 204 °C (400 °F), (total), T5 temper, sand castings : 10 h : 1697|39|6|2
    IC     (N):    tested at 204 °C (400 °F), (total), T5 temper, sand castings : 30 h : 1697|39|6|3
    IC     (N):    tested at 204 °C (400 °F), (total), T5 temper, sand castings : 100 h : 1697|39|6|4
    IC     (N):    tested at 204 °C (400 °F), (total), T5 temper, sand castings : 300 h : 1697|39|6|5
    IC     (N):    tested at 204 °C (400 °F), (total), T5 temper, sand castings : 1,000 h : 1697|39|6|6
    IC     (N):    tested at 260 °C (500 °F), (total), T5 temper, sand castings : 1 h : 1697|39|7|0
    IC     (N):    tested at 260 °C (500 °F), (total), T5 temper, sand castings : 3 h : 1697|39|7|1
    IC     (N):    tested at 260 °C (500 °F), (total), T5 temper, sand castings : 10 h : 1697|39|7|2
    IC     (N):    tested at 260 °C (500 °F), (total), T5 temper, sand castings : 30 h : 1697|39|7|3
    IC     (N):    tested at 260 °C (500 °F), (total), T5 temper, sand castings : 100 h : 1697|39|7|4
    IC     (N):    tested at 260 °C (500 °F), (total), T5 temper, sand castings : 300 h : 1697|39|7|5
    IC     (N):    tested at 260 °C (500 °F), (total), T5 temper, sand castings : 1,000 h : 1697|39|7|6
    IC     (N):    tested at 316 °C (600 °F), (total), T5 temper, sand castings : 1 h : 1697|39|8|0
    IC     (N):    tested at 316 °C (600 °F), (total), T5 temper, sand castings : 3 h : 1697|39|8|1
    IC     (N):    tested at 316 °C (600 °F), (total), T5 temper, sand castings : 10 h : 1697|39|8|2
    IC     (N):    tested at 316 °C (600 °F), (total), T5 temper, sand castings : 30 h : 1697|39|8|3
    IC     (N):    tested at 316 °C (600 °F), (total), T5 temper, sand castings : 100 h : 1697|39|8|4
    IC     (N):    tested at 316 °C (600 °F), (total), T5 temper, sand castings : 300 h : 1697|39|8|5
    IC     (N):    tested at 316 °C (600 °F), (total), T5 temper, sand castings : 1,000 h : 1697|39|8|6

return to listing

Fe - 27 Mn - 10 Al - 1 C (wt%) (New)

    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.01/s : tested at 850 °C (1562 °F) : 15408|12|0|0
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.01/s : tested at 900 °C (1652 °F) : 15408|12|0|1
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.01/s : tested at 950 °C (1742 °F) : 15408|12|0|2
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.01/s : tested at 1000 °C (1832 °F) : 15408|12|0|3
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.01/s : tested at 1050 °C (1922 °F) : 15408|12|0|4
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.1/s : tested at 850 °C (1562 °F) : 15408|12|1|0
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.1/s : tested at 900 °C (1652 °F) : 15408|12|1|1
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.1/s : tested at 950 °C (1742 °F) : 15408|12|1|2
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.1/s : tested at 1000 °C (1832 °F) : 15408|12|1|3
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 0.1/s : tested at 1050 °C (1922 °F) : 15408|12|1|4
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 1/s : tested at 850 °C (1562 °F) : 15408|12|2|0
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 1/s : tested at 900 °C (1652 °F) : 15408|12|2|1
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 1/s : tested at 950 °C (1742 °F) : 15408|12|2|2
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 1/s : tested at 1000 °C (1832 °F) : 15408|12|2|3
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 1/s : tested at 1050 °C (1922 °F) : 15408|12|2|4
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 5/s : tested at 850 °C (1562 °F) : 15408|12|3|0
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 5/s : tested at 900 °C (1652 °F) : 15408|12|3|1
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 5/s : tested at 950 °C (1742 °F) : 15408|12|3|2
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 5/s : tested at 1000 °C (1832 °F) : 15408|12|3|3
    SSCC      :    forged at 850 °C (1562 °F) to 1050 °C (1922 °F), 5/s : tested at 1050 °C (1922 °F) : 15408|12|3|4

return to listing

Graphite CZR

    D      (R):    solid : 14584|24|0|-1

return to listing

Graphite DFP-1

    D      (R):    solid : 236|24|0|-1

return to listing

Graphite HPD

    D      (R):    solid : 14583|24|0|-1

return to listing

Graphite PLS-1

    D      (R):    solid : 242|24|0|-1

return to listing

Graphite SCF

    D      (R):    solid : 14585|24|0|-1

return to listing

Graphite SFG-1

    D      (R):    solid : 243|24|0|-1

return to listing

HK31

    SR     (N):    T6 temper, sand castings : tested at 204 °C (400 °F) : 1695|22|1|0
    SR     (N):    T6 temper, sand castings : tested at 316 °C (600 °F) : 1695|22|1|1
    SR     (N):    T6 temper, sand castings : Master curve (LMP) : 1695|22|1|2
    CRS    (N):    0.1% strain, T6 temper, sand castings : tested at 260 °C (500 °F) : 1695|30|9|0
    CRS    (N):    0.1% strain, T6 temper, sand castings : tested at 316 °C (600 °F) : 1695|30|9|1
    CRS    (N):    0.1% strain, T6 temper, sand castings : Master curve (LMP) : 1695|30|9|2
    CRS    (N):    0.2% strain, T6 temper, sand castings : tested at 260 °C (500 °F) : 1695|30|10|0
    CRS    (N):    0.2% strain, T6 temper, sand castings : tested at 316 °C (600 °F) : 1695|30|10|1
    CRS    (N):    0.2% strain, T6 temper, sand castings : Master curve (LMP) : 1695|30|10|2
    CRS    (N):    0.5% strain, T6 temper, sand castings : tested at 260 °C (500 °F) : 1695|30|11|0
    CRS    (N):    0.5% strain, T6 temper, sand castings : tested at 316 °C (600 °F) : 1695|30|11|1
    CRS    (N):    0.5% strain, T6 temper, sand castings : Master curve (LMP) : 1695|30|11|2
    CRS    (N):    1% strain, T6 temper, sand castings : tested at 260 °C (500 °F) : 1695|30|12|0
    CRS    (N):    1% strain, T6 temper, sand castings : tested at 316 °C (600 °F) : 1695|30|12|1
    CRS    (N):    1% strain, T6 temper, sand castings : Master curve (LMP) : 1695|30|12|2
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 10 h : 1695|39|3|2
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 30 h : 1695|39|3|3
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 100 h : 1695|39|3|4
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 300 h : 1695|39|3|5
    IC     (N):    tested at 260 °C (500 °F), T6 temper, sand castings : 1,000 h : 1695|39|3|6
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 10 h : 1695|39|4|2
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 30 h : 1695|39|4|3
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 100 h : 1695|39|4|4
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 300 h : 1695|39|4|5
    IC     (N):    tested at 316 °C (600 °F), T6 temper, sand castings : 1,000 h : 1695|39|4|6

return to listing

HZ32

    CRS    (N):    0.1% strain, T5 temper, sand castings : tested at 204 °C (400 °F) : 1696|30|0|0
    CRS    (N):    0.1% strain, T5 temper, sand castings : tested at 260 °C (500 °F) : 1696|30|0|1
    CRS    (N):    0.1% strain, T5 temper, sand castings : tested at 316 °C (600 °F) : 1696|30|0|2
    CRS    (N):    0.1% strain, T5 temper, sand castings : Master curve (LMP) : 1696|30|0|3
    CRS    (N):    0.2% strain, T5 temper, sand castings : tested at 204 °C (400 °F) : 1696|30|1|0
    CRS    (N):    0.2% strain, T5 temper, sand castings : tested at 260 °C (500 °F) : 1696|30|1|1
    CRS    (N):    0.2% strain, T5 temper, sand castings : tested at 316 °C (600 °F) : 1696|30|1|2
    CRS    (N):    0.2% strain, T5 temper, sand castings : Master curve (LMP) : 1696|30|1|3
    CRS    (N):    0.5% strain, T5 temper, sand castings : tested at 204 °C (400 °F) : 1696|30|2|0
    CRS    (N):    0.5% strain, T5 temper, sand castings : tested at 260 °C (500 °F) : 1696|30|2|1
    CRS    (N):    0.5% strain, T5 temper, sand castings : tested at 316 °C (600 °F) : 1696|30|2|2
    CRS    (N):    0.5% strain, T5 temper, sand castings : Master curve (LMP) : 1696|30|2|3
    CRS    (N):    1% strain, T5 temper, sand castings : tested at 204 °C (400 °F) : 1696|30|3|0
    CRS    (N):    1% strain, T5 temper, sand castings : tested at 260 °C (500 °F) : 1696|30|3|1
    CRS    (N):    1% strain, T5 temper, sand castings : tested at 316 °C (600 °F) : 1696|30|3|2
    CRS    (N):    1% strain, T5 temper, sand castings : Master curve (LMP) : 1696|30|3|3
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 1 h : 1696|39|0|0
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 3 h : 1696|39|0|1
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 10 h : 1696|39|0|2
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 30 h : 1696|39|0|3
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 100 h : 1696|39|0|4
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 300 h : 1696|39|0|5
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 1,000 h : 1696|39|0|6
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 1 h : 1696|39|1|0
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 3 h : 1696|39|1|1
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 10 h : 1696|39|1|2
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 30 h : 1696|39|1|3
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 100 h : 1696|39|1|4
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 300 h : 1696|39|1|5
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 1,000 h : 1696|39|1|6
    IC     (N):    tested at 316 °C (600 °F), T5 temper, sand castings : 1 h : 1696|39|2|0
    IC     (N):    tested at 316 °C (600 °F), T5 temper, sand castings : 3 h : 1696|39|2|1
    IC     (N):    tested at 316 °C (600 °F), T5 temper, sand castings : 10 h : 1696|39|2|2
    IC     (N):    tested at 316 °C (600 °F), T5 temper, sand castings : 30 h : 1696|39|2|3
    IC     (N):    tested at 316 °C (600 °F), T5 temper, sand castings : 100 h : 1696|39|2|4
    IC     (N):    tested at 316 °C (600 °F), T5 temper, sand castings : 300 h : 1696|39|2|5
    IC     (N):    tested at 316 °C (600 °F), T5 temper, sand castings : 1,000 h : 1696|39|2|6

return to listing

In₂Se₃

    RHO    (N):    amorphous thin film : In2Se2.84 : 2511|2|0|0
    RHO    (N):    amorphous thin film : Cu doped In2Se3.15 : 2511|2|0|1
    RHO    (N):    amorphous thin film : Cu doped In2Se3.18 : 2511|2|0|2
    SIGMA (N):    amorphous thin film : In2Se2.84 : 2511|10|0|0
    SIGMA (N):    amorphous thin film : Cu doped In2Se3.15 : 2511|10|0|1
    SIGMA (N):    amorphous thin film : Cu doped In2Se3.18 : 2511|10|0|2

return to listing

Lead

    Vis    (R):    liquid : 916|26|1|-1

return to listing

Li₂Na₂P₂O₇ (New)

    RHO       :    solid : 15410|2|0|-1
    SIGMA    :    solid : 15410|10|0|-1

return to listing

NbTiVZr₀.₅ (New)

    SSCC      :    as-cast : tested at 800 °C (1472 °F), 0.001/s : 15400|12|0|0
    SSCC      :    as-cast : tested at 900 °C (1652 °F), 0.001/s : 15400|12|0|1
    SSCC      :    as-cast : tested at 1000 °C (1832 °F), 0.001/s : 15400|12|0|2
    SSCC      :    as-cast : tested at 1000 °C (1832 °F), 0.01/s : 15400|12|0|3
    SSCC      :    as-cast : tested at 1000 °C (1832 °F), 0.1/s : 15400|12|0|4

return to listing

Pb - 55 Bi (at%) (eutectic)

    DLL    (R):    liquid : 9341|0|1|-1
    MTE    (R):    liquid : 9341|8|1|-1
    CTE    (R):    liquid : 9341|16|1|-1
    D      (R):    liquid : 9341|24|1|-1

return to listing

Ti - 15 Mo (wt%) (New)

    DLL       :    solid : measured at a heating rate of 5°C/min : 15370|0|0|0
    DLL       :    solid : measured at a heating rate of 10°C/min : 15370|0|0|1
    DLL       :    solid : average : 15370|0|0|2
    MTE       :    solid : measured at a heating rate of 5°C/min : 15370|8|0|0
    MTE       :    solid : measured at a heating rate of 10°C/min : 15370|8|0|1
    MTE       :    solid : average : 15370|8|0|2

return to listing

Ti - 15 Mo - 0.5 Si (wt%) (New)

    DLL       :    solid : measured at a heating rate of 5°C/min : 15371|0|0|0
    DLL       :    solid : measured at a heating rate of 10°C/min : 15371|0|0|1
    DLL       :    solid : average : 15371|0|0|2
    MTE       :    solid : measured at a heating rate of 5°C/min : 15371|8|0|0
    MTE       :    solid : measured at a heating rate of 10°C/min : 15371|8|0|1
    MTE       :    solid : average : 15371|8|0|2

return to listing

Ti - 15 Mo - 1 Si (wt%) (New)

    DLL       :    solid : measured at a heating rate of 5°C/min : 15372|0|0|0
    DLL       :    solid : measured at a heating rate of 10°C/min : 15372|0|0|1
    DLL       :    solid : average : 15372|0|0|2
    MTE       :    solid : measured at a heating rate of 5°C/min : 15372|8|0|0
    MTE       :    solid : measured at a heating rate of 10°C/min : 15372|8|0|1
    MTE       :    solid : average : 15372|8|0|2

return to listing

Ti - 15 Mo - 1.5 Si (wt%) (New)

    DLL       :    solid : measured at a heating rate of 5°C/min : 15373|0|0|0
    DLL       :    solid : measured at a heating rate of 10°C/min : 15373|0|0|1
    DLL       :    solid : average : 15373|0|0|2
    MTE       :    solid : measured at a heating rate of 5°C/min : 15373|8|0|0
    MTE       :    solid : measured at a heating rate of 10°C/min : 15373|8|0|1
    MTE       :    solid : average : 15373|8|0|2

return to listing

Ti - 15 Mo - 2 Si (wt%) (New)

    DLL       :    solid : measured at a heating rate of 5°C/min : 15374|0|0|0
    DLL       :    solid : measured at a heating rate of 10°C/min : 15374|0|0|1
    DLL       :    solid : average : 15374|0|0|2
    MTE       :    solid : measured at a heating rate of 5°C/min : 15374|8|0|0
    MTE       :    solid : measured at a heating rate of 10°C/min : 15374|8|0|1
    MTE       :    solid : average : 15374|8|0|2

return to listing

Ti - 6 Al - 4 V

    SSC    (N):    effect of pre-strain : tested at 20 °C (68 °F), 0% pre-strain, 0.001/s : 2836|4|6|0
    SSC    (N):    effect of pre-strain : tested at 20 °C (68 °F), 0.5% pre-strain, 0.001/s : 2836|4|6|1
    SSC    (N):    effect of pre-strain : tested at 20 °C (68 °F), 1% pre-strain, 0.001/s : 2836|4|6|2
    SSC    (N):    effect of pre-strain : tested at 20 °C (68 °F), 2% pre-strain, 0.001/s : 2836|4|6|3
    SSC    (N):    effect of pre-strain : tested at 20 °C (68 °F), 3% pre-strain, 0.001/s : 2836|4|6|4
    SSC    (N):    effect of pre-strain : tested at 20 °C (68 °F), 4% pre-strain, 0.001/s : 2836|4|6|5
    SSC    (N):    effect of pre-strain : tested at 20 °C (68 °F), 5% pre-strain, 0.001/s : 2836|4|6|6
    UTS   (N*):    effect of pre-strain on RT value : 0% pre-strain : 2836|5|6|0
    UTS   (N*):    effect of pre-strain on RT value : 0.5% pre-strain : 2836|5|6|1
    UTS   (N*):    effect of pre-strain on RT value : 1% pre-strain : 2836|5|6|2
    UTS   (N*):    effect of pre-strain on RT value : 2% pre-strain : 2836|5|6|3
    UTS   (N*):    effect of pre-strain on RT value : 3% pre-strain : 2836|5|6|4
    UTS   (N*):    effect of pre-strain on RT value : 4% pre-strain : 2836|5|6|5
    UTS   (N*):    effect of pre-strain on RT value : 5% pre-strain : 2836|5|6|6
    YS    (N*):    effect of pre-strain on RT value : 0% pre-strain : 2836|13|6|0
    YS    (N*):    effect of pre-strain on RT value : 0.5% pre-strain : 2836|13|6|1
    YS    (N*):    effect of pre-strain on RT value : 1% pre-strain : 2836|13|6|2
    YS    (N*):    effect of pre-strain on RT value : 2 pre-strain : 2836|13|6|3
    YS    (N*):    effect of pre-strain on RT value : 3% pre-strain : 2836|13|6|4
    YS    (N*):    effect of pre-strain on RT value : 4% pre-strain : 2836|13|6|5
    YS    (N*):    effect of pre-strain on RT value : 5% pre-strain : 2836|13|6|6
    %El   (N*):    effect of pre-strain on RT value : 0% pre-strain : 2836|29|3|0
    %El   (N*):    effect of pre-strain on RT value : 0.5% pre-strain : 2836|29|3|1
    %El   (N*):    effect of pre-strain on RT value : 1% pre-strain : 2836|29|3|2
    %El   (N*):    effect of pre-strain on RT value : 2% pre-strain : 2836|29|3|3
    %El   (N*):    effect of pre-strain on RT value : 3% pre-strain : 2836|29|3|4
    %El   (N*):    effect of pre-strain on RT value : 4% pre-strain : 2836|29|3|5
    %El   (N*):    effect of pre-strain on RT value : 5% pre-strain : 2836|29|3|6

return to listing

Tin

    Vis    (R):    liquid : 884|26|1|-1

return to listing

ZH62

    CRS    (N):    0.1% strain, T5 temper, sand castings : tested at 93 °C (200 °F) : 1701|30|0|0
    CRS    (N):    0.1% strain, T5 temper, sand castings : tested at 149 °C (300 °F) : 1701|30|0|1
    CRS    (N):    0.1% strain, T5 temper, sand castings : tested at 204 °C (400 °F) : 1701|30|0|2
    CRS    (N):    0.1% strain, T5 temper, sand castings : tested at 260 °C (500 °F) : 1701|30|0|3
    CRS    (N):    0.1% strain, T5 temper, sand castings : Master curve (LMP) : 1701|30|0|4
    CRS    (N):    0.2% strain, T5 temper, sand castings : tested at 93 °C (200 °F) : 1701|30|1|0
    CRS    (N):    0.2% strain, T5 temper, sand castings : tested at 149 °C (300 °F) : 1701|30|1|1
    CRS    (N):    0.2% strain, T5 temper, sand castings : tested at 204 °C (400 °F) : 1701|30|1|2
    CRS    (N):    0.2% strain, T5 temper, sand castings : tested at 260 °C (500 °F) : 1701|30|1|3
    CRS    (N):    0.2% strain, T5 temper, sand castings : Master curve (LMP) : 1701|30|1|4
    CRS    (N):    0.5% strain, T5 temper, sand castings : tested at 93 °C (200 °F) : 1701|30|2|0
    CRS    (N):    0.5% strain, T5 temper, sand castings : tested at 149 °C (300 °F) : 1701|30|2|1
    CRS    (N):    0.5% strain, T5 temper, sand castings : tested at 204 °C (400 °F) : 1701|30|2|2
    CRS    (N):    0.5% strain, T5 temper, sand castings : tested at 260 °C (500 °F) : 1701|30|2|3
    CRS    (N):    0.5% strain, T5 temper, sand castings : Master curve (LMP) : 1701|30|2|4
    CRS    (N):    1% strain, T5 temper, sand castings : tested at 93 °C (200 °F) : 1701|30|3|0
    CRS    (N):    1% strain, T5 temper, sand castings : tested at 149 °C (300 °F) : 1701|30|3|1
    CRS    (N):    1% strain, T5 temper, sand castings : tested at 204 °C (400 °F) : 1701|30|3|2
    CRS    (N):    1% strain, T5 temper, sand castings : tested at 260 °C (500 °F) : 1701|30|3|3
    CRS    (N):    1% strain, T5 temper, sand castings : Master curve (LMP) : 1701|30|3|4
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 1 h : 1701|39|0|0
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 3 h : 1701|39|0|1
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 10 h : 1701|39|0|2
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 30 h : 1701|39|0|3
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 100 h : 1701|39|0|4
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 300 h : 1701|39|0|5
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 1,000 h : 1701|39|0|6
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 1 h : 1701|39|1|0
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 3 h : 1701|39|1|1
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 10 h : 1701|39|1|2
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 30 h : 1701|39|1|3
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 100 h : 1701|39|1|4
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 300 h : 1701|39|1|5
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 1,000 h : 1701|39|1|6
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 1 h : 1701|39|2|0
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 3 h : 1701|39|2|1
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 10 h : 1701|39|2|2
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 30 h : 1701|39|2|3
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 100 h : 1701|39|2|4
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 300 h : 1701|39|2|5
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 1,000 h : 1701|39|2|6
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 1 h : 1701|39|3|0
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 3 h : 1701|39|3|1
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 10 h : 1701|39|3|2
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 30 h : 1701|39|3|3
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 100 h : 1701|39|3|4
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 300 h : 1701|39|3|5
    IC     (N):    tested at 260 °C (500 °F), T5 temper, sand castings : 1,000 h : 1701|39|3|6

return to listing

ZK51

    UTS    (N):    T5 temper : sand castings : 1704|5|0|0
    YS     (N):    T5 temper : sand castings : 1704|13|0|0
    %El    (N):    T5 temper : sand castings : 1704|29|0|0
    CRS    (N):    0.1% strain, T5 temper, sand castings : tested at 93 °C (200 °F) : 1704|30|0|0
    CRS    (N):    0.1% strain, T5 temper, sand castings : tested at 149 °C (300 °F) : 1704|30|0|1
    CRS    (N):    0.1% strain, T5 temper, sand castings : tested at 204 °C (400 °F) : 1704|30|0|2
    CRS    (N):    0.1% strain, T5 temper, sand castings : Master curve (LMP) : 1704|30|0|3
    CRS    (N):    0.2% strain, T5 temper, sand castings : tested at 93 °C (200 °F) : 1704|30|1|0
    CRS    (N):    0.2% strain, T5 temper, sand castings : tested at 149 °C (300 °F) : 1704|30|1|1
    CRS    (N):    0.2% strain, T5 temper, sand castings : tested at 204 °C (400 °F) : 1704|30|1|2
    CRS    (N):    0.2% strain, T5 temper, sand castings : Master curve (LMP) : 1704|30|1|3
    CRS    (N):    0.5% strain, T5 temper, sand castings : tested at 93 °C (200 °F) : 1704|30|2|0
    CRS    (N):    0.5% strain, T5 temper, sand castings : tested at 149 °C (300 °F) : 1704|30|2|1
    CRS    (N):    0.5% strain, T5 temper, sand castings : tested at 204 °C (400 °F) : 1704|30|2|2
    CRS    (N):    0.5% strain, T5 temper, sand castings : Master curve (LMP) : 1704|30|2|3
    CRS    (N):    1% strain, T5 temper, sand castings : tested at 93 °C (200 °F) : 1704|30|3|0
    CRS    (N):    1% strain, T5 temper, sand castings : tested at 149 °C (300 °F) : 1704|30|3|1
    CRS    (N):    1% strain, T5 temper, sand castings : tested at 204 °C (400 °F) : 1704|30|3|2
    CRS    (N):    1% strain, T5 temper, sand castings : Master curve (LMP) : 1704|30|3|3
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 1 h : 1704|39|0|0
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 3 h : 1704|39|0|1
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 10 h : 1704|39|0|2
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 30 h : 1704|39|0|3
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 100 h : 1704|39|0|4
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 300 h : 1704|39|0|5
    IC     (N):    tested at 93 °C (200 °F), T5 temper, sand castings : 1,000 h : 1704|39|0|6
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 1 h : 1704|39|1|0
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 3 h : 1704|39|1|1
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 10 h : 1704|39|1|2
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 30 h : 1704|39|1|3
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 100 h : 1704|39|1|4
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 300 h : 1704|39|1|5
    IC     (N):    tested at 149 °C (300 °F), T5 temper, sand castings : 1,000 h : 1704|39|1|6
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 1 h : 1704|39|2|0
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 3 h : 1704|39|2|1
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 10 h : 1704|39|2|2
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 30 h : 1704|39|2|3
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 100 h : 1704|39|2|4
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 300 h : 1704|39|2|5
    IC     (N):    tested at 204 °C (400 °F), T5 temper, sand castings : 1,000 h : 1704|39|2|6

return to listing

ZK60

    DLL    (R):    F temper : extrusion, longitudinal : 1705|0|0|0
    DLL    (N):    F temper : extrusion, transverse : 1705|0|0|1
    DLL    (N):    F temper : extrusion, average : 1705|0|0|2
    DLL    (N):    T5 temper : extrusion, longitudinal : 1705|0|1|0
    DLL    (N):    T5 temper : extrusion, transverse : 1705|0|1|1
    DLL    (N):    T5 temper : extrusion, average : 1705|0|1|2
    DLL    (N):    average of F and T5 tempers : extrusion : 1705|0|2|0
    MTE    (R):    F temper : extrusion, longitudinal : 1705|8|0|0
    MTE    (N):    F temper : extrusion, transverse : 1705|8|0|1
    MTE    (N):    F temper : extrusion, average : 1705|8|0|2
    MTE    (N):    T5 temper : extrusion, longitudinal : 1705|8|1|0
    MTE    (N):    T5 temper : extrusion, transverse : 1705|8|1|1
    MTE    (N):    T5 temper : extrusion, average : 1705|8|1|2
    MTE    (N):    average of F and T5 tempers : extrusion : 1705|8|2|0
    CTE    (R):    F temper : extrusion, longitudinal : 1705|16|0|0
    CTE    (N):    F temper : extrusion, transverse : 1705|16|0|1
    CTE    (N):    F temper : extrusion, average : 1705|16|0|2
    CTE    (N):    T5 temper : extrusion, longitudinal : 1705|16|1|0
    CTE    (N):    T5 temper : extrusion, transverse : 1705|16|1|1
    CTE    (N):    T5 temper : extrusion, average : 1705|16|1|2
    CTE    (N):    average of F and T5 tempers : extrusion : 1705|16|2|0
    D      (R):    solid : 1705|24|0|-1
    TD     (R):    solid : T5 temper, extruded : 1705|25|0|0
    CRS    (N):    0.2% strain, T5 temper, extrusions : tested at 35 °C (95 °F) : 1705|30|0|0
    CRS    (N):    0.2% strain, T5 temper, extrusions : tested at 93 °C (200 °F) : 1705|30|0|1
    CRS    (N):    0.2% strain, T5 temper, extrusions : tested at 121 °C (250 °F) : 1705|30|0|2
    CRS    (N):    0.2% strain, T5 temper, extrusions : tested at 149 °C (300 °F) : 1705|30|0|3
    CRS    (N):    0.2% strain, T5 temper, extrusions : Master curve (LMP) : 1705|30|0|4
    CRS    (N):    0.5% strain, T5 temper, extrusions : tested at 35 °C (95 °F) : 1705|30|1|0
    CRS    (N):    0.5% strain, T5 temper, extrusions : tested at 93 °C (200 °F) : 1705|30|1|1
    CRS    (N):    0.5% strain, T5 temper, extrusions : tested at 121 °C (250 °F) : 1705|30|1|2
    CRS    (N):    0.5% strain, T5 temper, extrusions : tested at 149 °C (300 °F) : 1705|30|1|3
    CRS    (N):    0.5% strain, T5 temper, extrusions : Master curve (LMP) : 1705|30|1|4
    CRS    (N):    1% strain, T5 temper, extrusions : tested at 35 °C (95 °F) : 1705|30|2|0
    CRS    (N):    1% strain, T5 temper, extrusions : tested at 93 °C (200 °F) : 1705|30|2|1
    CRS    (N):    1% strain, T5 temper, extrusions : tested at 121 °C (250 °F) : 1705|30|2|2
    CRS    (N):    1% strain, T5 temper, extrusions : tested at 149 °C (300 °F) : 1705|30|2|3
    CRS    (N):    1% strain, T5 temper, extrusions : Master curve (LMP) : 1705|30|2|4
    IC     (N):    tested at 35 °C (95 °F), T5 temper, extrusions : 1 h : 1705|39|0|0
    IC     (N):    tested at 35 °C (95 °F), T5 temper, extrusions : 3 h : 1705|39|0|1
    IC     (N):    tested at 35 °C (95 °F), T5 temper, extrusions : 10 h : 1705|39|0|2
    IC     (N):    tested at 35 °C (95 °F), T5 temper, extrusions : 30 h : 1705|39|0|3
    IC     (N):    tested at 35 °C (95 °F), T5 temper, extrusions : 100 h : 1705|39|0|4
    IC     (N):    tested at 35 °C (95 °F), T5 temper, extrusions : 300 h : 1705|39|0|5
    IC     (N):    tested at 35 °C (95 °F), T5 temper, extrusions : 500 h : 1705|39|0|6
    IC     (N):    tested at 93 °C (200 °F), T5 temper, extrusions : 1 h : 1705|39|1|0
    IC     (N):    tested at 93 °C (200 °F), T5 temper, extrusions : 3 h : 1705|39|1|1
    IC     (N):    tested at 93 °C (200 °F), T5 temper, extrusions : 10 h : 1705|39|1|2
    IC     (N):    tested at 93 °C (200 °F), T5 temper, extrusions : 30 h : 1705|39|1|3
    IC     (N):    tested at 93 °C (200 °F), T5 temper, extrusions : 100 h : 1705|39|1|4
    IC     (N):    tested at 93 °C (200 °F), T5 temper, extrusions : 300 h : 1705|39|1|5
    IC     (N):    tested at 93 °C (200 °F), T5 temper, extrusions : 500 h : 1705|39|1|6
    IC     (N):    tested at 121 °C (250 °F), T5 temper, extrusions : 1 h : 1705|39|2|0
    IC     (N):    tested at 121 °C (250 °F), T5 temper, extrusions : 3 h : 1705|39|2|1
    IC     (N):    tested at 121 °C (250 °F), T5 temper, extrusions : 10 h : 1705|39|2|2
    IC     (N):    tested at 121 °C (250 °F), T5 temper, extrusions : 30 h : 1705|39|2|3
    IC     (N):    tested at 121 °C (250 °F), T5 temper, extrusions : 100 h : 1705|39|2|4
    IC     (N):    tested at 121 °C (250 °F), T5 temper, extrusions : 300 h : 1705|39|2|5
    IC     (N):    tested at 121 °C (250 °F), T5 temper, extrusions : 500 h : 1705|39|2|6
    IC     (N):    tested at 149 °C (300 °F), T5 temper, extrusions : 1 h : 1705|39|3|0
    IC     (N):    tested at 149 °C (300 °F), T5 temper, extrusions : 3 h : 1705|39|3|1
    IC     (N):    tested at 149 °C (300 °F), T5 temper, extrusions : 10 h : 1705|39|3|2
    IC     (N):    tested at 149 °C (300 °F), T5 temper, extrusions : 30 h : 1705|39|3|3
    IC     (N):    tested at 149 °C (300 °F), T5 temper, extrusions : 100 h : 1705|39|3|4

return to listing