Changes

New and revised materials and properties in MPDB v9.51 as compared to v9.49

Key to property symbols (number of datasets):

DLL = Density	TC = Linear thermal expansion (dL/L)
RHO = Mean coefficient of thermal expansion	E = Coefficient of thermal expansion (CTE)
SSC = Elastic/Young's modulus	UTS = Shear modulus
FSN = Poisson's ratio	RPB = Bulk modulus
MTE = Thermal conductivity	SH = Thermal diffusivity
SIGMA = Specific heat	G = Heat capacity
SSCC = True stress-strain curve (tension)	YS = True stress-strain curve (compression)
FEN = Tensile strength	AP = Yield strength (tension)
CTE = Compressive strength	HC = Yield strength (compression)
VP = Elongation	v = Stress rupture
HE = Fatigue e-N curve	YSC = Fatigue S-N curve
SR = Creep strength	BH = Isochronous creep
D = Hemispherical total emissivity	TD = Normal total emissivity
Vis = Vapor pressure	K = Viscosity
NE = Surface tension	%El = Electrical resistivity
CRS = Electrical conductivity	HB = Specific volume
FM = Apparent viscosity	FS = Flexural modulus
AV = Flexural strength	ESSC = Engineering stress-strain curve (tension)
ESSCC = Engineering stress-strain curve (compression)	CRM = Creep modulus
ST = Relative permeability	IC = Absolute permeability
SV = B-H curve	DCRPT = H-B curve
DF = Core loss	CL = Exciting Power
EP = Relative permittivity	RIW = Dissipation factor
RIT = Refractive index vs WL	UCS = Refractive index vs T

+ indicates the material or data is new, ^ indicates the data has been revised, * indicates the data is the RT value only

39 new materials, 877 new property sets, 23 revised properties, and 240 new RT values

718 Plus	A360.0	A380.0	Alloy 22-3	Alloy 27
Alloy 2	Alloy 42-6 (426)	Alloy 52	Alloy 7	Beralcast 363
CM 186 LC	CMSX-6	DD6	DS CM 247 LC	EP741NP
FB 780	Fe - 30 Mn - 1 C	GH413	GH742	Haynes HR-224
Haynes R-41 (Rene 41)	Haynes Ultimet	HCR	Hiperco 50 alloy	Hiperco 50A alloy
Hostaform C 9021 AW	HS 50	IN-100	IN-738	IN-792 5A
IN-792	Incoloy 864	Inconel 625LCF	Inconel 706	Inconel 718
Inconel 718SPF	Inconel HX / Hastelloy X / Nimonic PE13	MERL 76	Mumetal Plus	Mumetal
Permendur 24	Permendur 49	PM 1000	PWA 1480	PWA 1489
PWA 275	PWA 276	Radiometal 36	Radiometal 4550	Rene 88 DT
Rene 95	Rotelloy 3	Rotelloy 5	SC 16	SRR99
Super Mumetal 150	Super Mumetal 200	Super Mumetal 300	Super Mumetal	Super Radiometal
Telcalloy A	Telcalloy B	Temperature compensator R2799	Temperature compensator R2799A	Temperature compensator R2800
Temperature compensator R2800A	Temperature compensator R3100	Temperature compensator R3100A	TMW-4M3	TRAN-COR H-0 CARLITE DR electrical steel
Udimet 720	Udimet 720LI	Udimet D-979	Waspaloy

718 Plus

    FEN    (+):    standard heat treatment (968 °C (1775 °F) / 788 °C (1450 °F) / 704 °C (1300 °F)) : tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range : 2962|14|0|0
    FEN    (+):    standard heat treatment (968 °C (1775 °F) / 788 °C (1450 °F) / 704 °C (1300 °F)) : tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range : 2962|14|0|1
    FEN    (+):    standard heat treatment (968 °C (1775 °F) / 788 °C (1450 °F) / 704 °C (1300 °F)) : tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 2962|14|0|2
    FEN    (+):    standard heat treatment (968 °C (1775 °F) / 788 °C (1450 °F) / 704 °C (1300 °F)) : tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 2962|14|0|3
    FEN    (+):    standard heat treatment plus 732 °C (1350 °F) for 1000 h : tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range : 2962|14|1|0
    FEN    (+):    standard heat treatment plus 732 °C (1350 °F) for 1000 h : tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range : 2962|14|1|1
    FEN    (+):    standard heat treatment plus 732 °C (1350 °F) for 1000 h : tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 2962|14|1|2
    FEN    (+):    standard heat treatment plus 732 °C (1350 °F) for 1000 h : tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 2962|14|1|3
    FEN    (+):    866 °C (1590 °F) for 8 h plus standard heat treatment : tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range : 2962|14|2|0
    FEN    (+):    866 °C (1590 °F) for 8 h plus standard heat treatment : tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range : 2962|14|2|1
    FEN    (+):    866 °C (1590 °F) for 8 h plus standard heat treatment : tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 2962|14|2|2
    FEN    (+):    866 °C (1590 °F) for 8 h plus standard heat treatment : tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 2962|14|2|3
    FEN    (+):    overaged : tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range : 2962|14|3|0
    FEN    (+):    overaged : tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range : 2962|14|3|1
    FEN    (+):    overaged : tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 2962|14|3|2
    FEN    (+):    overaged : tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 2962|14|3|3
    FEN    (+):    combination of all 4 heat treatments : tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range : 2962|14|4|0
    FEN    (+):    combination of all 4 heat treatments : tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range : 2962|14|4|1
    FEN    (+):    combination of all 4 heat treatments : tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 2962|14|4|2
    FEN    (+):    combination of all 4 heat treatments : tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 2962|14|4|3

return to listing

A360.0

    TC    (+*):    solid : 121|1|0|-1
    RHO   (+*):    solid : 121|2|0|-1
    SIGMA (+*):    solid : 121|10|0|-1

return to listing

A380.0

    RHO   (+*):    solid : 122|2|0|-1
    SIGMA (+*):    solid : 122|10|0|-1

return to listing

Alloy 22-3

    UTS   (+*):    annealed : 705|5|0|-1
    YS    (+*):    annealed : 705|13|0|-1
    %El   (+*):    annealed : 705|29|0|-1

return to listing

Alloy 27

    UTS   (+*):    annealed : 706|5|0|-1
    SH    (+*):    solid : 706|9|0|-1
    YS    (+*):    annealed : 706|13|0|-1
    TD    (+*):    solid : 706|25|0|-1
    %El   (+*):    annealed : 706|29|0|-1

return to listing

Alloy 2

    TC    (+*):    solid : 9001|1|0|-1
    RHO   (+*):    solid : 9001|2|0|-1
    SIGMA (+*):    solid : 9001|10|0|-1
    %El   (+*):    solid : typical value : 9001|29|0|0

return to listing

Alloy 42-6 (426)

    TC    (+*):    solid : 709|1|0|-1
    UTS   (+*):    annealed : 709|5|0|-1
    SH    (+*):    solid : 709|9|0|-1
    YS    (+*):    annealed : 709|13|0|-1
    TD    (+*):    solid : 709|25|0|-1
    %El   (+*):    annealed : 709|29|0|-1

return to listing

Alloy 52

    RHO    (+):    solid : 714|2|0|-1
    UTS   (+*):    annealed : 714|5|0|-1
    SIGMA (+):    solid : 714|10|0|-1
    YS    (+*):    annealed : 714|13|0|-1
    %El   (+*):    annealed : 714|29|0|-1

return to listing

Alloy 7

    TC    (+*):    solid : 9004|1|0|-1
    RHO   (+*):    solid : 9004|2|0|-1
    SIGMA (+*):    solid : 9004|10|0|-1
    YS    (+*):    solid : 9004|13|0|-1

return to listing

Beralcast 363

    E     (+*):    solid : 3018|3|0|-1
    SSC    (+):    investment cast & HIPed : tested at 21 °C (70 °F), unknown strain rate : 3018|4|0|0
    SSC    (+):    investment cast & HIPed : tested at -73 °C (-100 °F), unknown strain rate : 3018|4|0|1
    SSC    (+):    investment cast & HIPed : tested at -195.6 °C (-320 °F), unknown strain rate : 3018|4|0|2
    SSC    (+):    investment cast & HIPed : tested at -252.8 °C (-423 °F), unknown strain rate : 3018|4|0|3
    UTS    (+):    investment cast & HIPed : 3018|5|0|-1
    FSN    (+):    investment cast & HIPed : tested at 20 °C (68 °F), R = -1, axial, maximum stress values : 3018|6|0|0
    FSN    (+):    investment cast & HIPed : tested at 20 °C (68 °F), R = 0.1, axial, maximum stress values : 3018|6|0|1
    FSN    (+):    investment cast & HIPed : tested at 232 °C (450 °F), R = -1, axial, maximum stress values : 3018|6|0|2
    SH    (+*):    solid : 3018|9|0|-1
    G     (+*):    solid : 3018|11|0|-1
    YS     (+):    investment cast & HIPed : 3018|13|0|-1
    v     (+*):    solid : 3018|19|0|-1
    D     (+*):    solid : 3018|24|0|-1
    TD    (+*):    solid : 3018|25|0|-1
    K     (+*):    solid : 3018|27|0|-1
    %El    (+):    investment cast & HIPed : 3018|29|0|-1

return to listing

CM 186 LC (*)

    UTS    (+):    as-cast : 1080 °C (1976 °F) for 4 h, 870 °C (1598 °F) for 16 h : 14926|5|0|0
    UTS    (+):    as-cast : 1190 °C (2174 °F) for 3 h, 1080 °C (1976 °F) for 4 h, 870 °C (1598 °F) for 16 h : 14926|5|0|1
    UTS    (+):    as-cast : 1150 °C (2102 °F) for 2 h, 870 °C (1598 °F) for 16 h : 14926|5|0|2
    YS     (+):    as-cast : 1080 °C (1976 °F) for 4 h, 870 °C (1598 °F) for 16 h : 14926|13|0|0
    YS     (+):    as-cast : 1190 °C (2174 °F) for 3 h, 1080 °C (1976 °F) for 4 h, 870 °C (1598 °F) for 16 h : 14926|13|0|1
    YS     (+):    as-cast : 1150 °C (2102 °F) for 2 h, 870 °C (1598 °F) for 16 h : 14926|13|0|2
    SR     (+):    as-cast, double aged : tested at 871 °C (1600 °F) : 14926|22|0|0
    SR     (+):    as-cast, double aged : tested at 899 °C (1650 °F) : 14926|22|0|1
    SR     (+):    as-cast, double aged : tested at 927 °C (1700 °F) : 14926|22|0|2
    SR     (+):    as-cast, double aged : tested at 954 °C (1750 °F) : 14926|22|0|3
    SR     (+):    as-cast, double aged : tested at 982 °C (1800 °F) : 14926|22|0|4
    SR     (+):    as-cast, double aged : Master curve (LMP) : 14926|22|0|5
    D     (+*):    solid : 14926|24|0|-1
    %El    (+):    as-cast : 1080 °C (1976 °F) for 4 h, 870 °C (1598 °F) for 16 h : 14926|29|0|0
    %El    (+):    as-cast : 1190 °C (2174 °F) for 3 h, 1080 °C (1976 °F) for 4 h, 870 °C (1598 °F) for 16 h : 14926|29|0|1
    %El    (+):    as-cast : 1150 °C (2102 °F) for 2 h, 870 °C (1598 °F) for 16 h : 14926|29|0|2
    CRS    (+):    3% strain, solution annealed & aged <001> orientated bars : tested at 750 °C (1382 °F) : 14926|30|0|0
    CRS    (+):    4% strain, solution annealed & aged <001> orientated bars : tested at 750 °C (1382 °F) : 14926|30|1|0
    CRS    (+):    5% strain, solution annealed & aged <001> orientated bars : tested at 750 °C (1382 °F) : 14926|30|2|0
    CRS    (+):    6% strain, solution annealed & aged <001> orientated bars : tested at 750 °C (1382 °F) : 14926|30|3|0
    CRS    (+):    7% strain, solution annealed & aged <001> orientated bars : tested at 750 °C (1382 °F) : 14926|30|4|0
    CRS    (+):    8% strain, solution annealed & aged <001> orientated bars : tested at 750 °C (1382 °F) : 14926|30|5|0
    IC     (+):    tested at 750 °C (1382 °F), solution annealed & aged <001> orientated bars : 200 h : 14926|39|0|0
    IC     (+):    tested at 750 °C (1382 °F), solution annealed & aged <001> orientated bars : 300 h : 14926|39|0|1
    IC     (+):    tested at 750 °C (1382 °F), solution annealed & aged <001> orientated bars : 700 h : 14926|39|0|2
    IC     (+):    tested at 750 °C (1382 °F), solution annealed & aged <001> orientated bars : 1,000 h : 14926|39|0|3

return to listing

CMSX-6 (*)

    DLL    (+):    solid : 14920|0|0|-1
    MTE    (+):    solid : 14920|8|0|-1
    FEN    (+):    no hold : tested at 980 °C (1796 °F), R = -1, axial, total strain range : 14920|14|0|0
    FEN    (+):    held for 300 s at the maximum tensile strain : tested at 980 °C (1796 °F), R = -1, axial, total strain range : 14920|14|1|0
    FEN    (+):    held for 300 s at the maximum compressive strain : tested at 980 °C (1796 °F), R = -1, axial, total strain range : 14920|14|2|0
    D      (+):    solid : 14920|24|0|-1

return to listing

DD6 (*)

    UTS    (+):    fully heat-treated : [001], no low angle boundaries : 14928|5|0|0
    UTS    (+):    fully heat-treated : [001], 0 degree to 3 degree misorientation : 14928|5|0|1
    UTS    (+):    fully heat-treated : [001], 3 degree to 6 degree misorientation : 14928|5|0|2
    UTS    (+):    fully heat-treated : [001], 6 degree to 9 degree misorientation : 14928|5|0|3
    UTS    (+):    fully heat-treated : [001], 9 degree to 12 degree misorientation : 14928|5|0|4
    D     (+*):    solid : 14928|24|0|-1
    %El    (+):    fully heat-treated : [001], no low angle boundaries : 14928|29|0|0
    %El    (+):    fully heat-treated : [001], 0 degree to 3 degree misorientation : 14928|29|0|1
    %El    (+):    fully heat-treated : [001], 3 degree to 6 degree misorientation : 14928|29|0|2
    %El    (+):    fully heat-treated : [001], 6 degree to 9 degree misorientation : 14928|29|0|3
    %El    (+):    fully heat-treated : [001], 9 degree to 12 degree misorientation : 14928|29|0|4

return to listing

DS CM 247 LC (*)

    UTS    (+):    2-step solutioning, aged : longitudinal : 14922|5|0|0
    UTS    (+):    2-step solutioning, aged : transverse : 14922|5|0|1
    FSN    (+):    longitudinal : tested at 871 °C (1600 °F), R = 0.1, axial, maximum stress values : 14922|6|0|0
    YS     (+):    2-step solutioning, aged : longitudinal : 14922|13|0|0
    YS     (+):    2-step solutioning, aged : transverse : 14922|13|0|1
    FEN    (+):    0.003/s strain rate : tested at 850 °C (1562 °F), R = -1, axial, longitudinal, total strain range : 14922|14|0|0
    FEN    (+):    0.003/s strain rate : tested at 950 °C (1742 °F), R = -1, axial, longitudinal, total strain range : 14922|14|0|1
    FEN    (+):    0.003/s strain rate : tested at 950 °C (1742 °F), R = -1, axial, long transverse, total strain range : 14922|14|0|2
    FEN    (+):    0.003/s strain rate : tested at 850 °C (1562 °F), R = -1, axial, longitudinal, plastic strain range : 14922|14|0|3
    FEN    (+):    0.003/s strain rate : tested at 950 °C (1742 °F), R = -1, axial, longitudinal, plastic strain range : 14922|14|0|4
    FEN    (+):    0.003/s strain rate : tested at 950 °C (1742 °F), R = -1, axial, long transverse, plastic strain range : 14922|14|0|5
    FEN    (+):    0.003/s strain rate : tested at 850 °C (1562 °F), R = -1, axial, longitudinal, elastic strain range : 14922|14|0|6
    FEN    (+):    0.003/s strain rate : tested at 950 °C (1742 °F), R = -1, axial, longitudinal, elastic strain range : 14922|14|0|7
    FEN    (+):    0.003/s strain rate : tested at 950 °C (1742 °F), R = -1, axial, long transverse, elastic strain range : 14922|14|0|8
    SR     (+):    equiaxed : tested at 871 °C (1600 °F) : 14922|22|0|0
    SR     (+):    equiaxed : tested at 899 °C (1650 °F) : 14922|22|0|1
    SR     (+):    equiaxed : tested at 927 °C (1700 °F) : 14922|22|0|2
    SR     (+):    equiaxed : tested at 954 °C (1750 °F) : 14922|22|0|3
    SR     (+):    equiaxed : tested at 982 °C (1800 °F) : 14922|22|0|4
    SR     (+):    equiaxed : Master curve (LMP) : 14922|22|0|5
    SR     (+):    transverse : tested at 871 °C (1600 °F) : 14922|22|1|0
    SR     (+):    transverse : tested at 899 °C (1650 °F) : 14922|22|1|1
    SR     (+):    transverse : tested at 927 °C (1700 °F) : 14922|22|1|2
    SR     (+):    transverse : tested at 954 °C (1750 °F) : 14922|22|1|3
    SR     (+):    transverse : tested at 982 °C (1800 °F) : 14922|22|1|4
    SR     (+):    transverse : Master curve (LMP) : 14922|22|1|5
    SR     (+):    longitudinal, heat treatment A : tested at 871 °C (1600 °F) : 14922|22|2|0
    SR     (+):    longitudinal, heat treatment A : tested at 899 °C (1650 °F) : 14922|22|2|1
    SR     (+):    longitudinal, heat treatment A : tested at 927 °C (1700 °F) : 14922|22|2|2
    SR     (+):    longitudinal, heat treatment A : tested at 954 °C (1750 °F) : 14922|22|2|3
    SR     (+):    longitudinal, heat treatment A : tested at 982 °C (1800 °F) : 14922|22|2|4
    SR     (+):    longitudinal, heat treatment A : Master curve (LMP) : 14922|22|2|5
    SR     (+):    longitudinal, heat treatment B : tested at 871 °C (1600 °F) : 14922|22|3|0
    SR     (+):    longitudinal, heat treatment B : tested at 899 °C (1650 °F) : 14922|22|3|1
    SR     (+):    longitudinal, heat treatment B : tested at 927 °C (1700 °F) : 14922|22|3|2
    SR     (+):    longitudinal, heat treatment B : tested at 954 °C (1750 °F) : 14922|22|3|3
    SR     (+):    longitudinal, heat treatment B : tested at 982 °C (1800 °F) : 14922|22|3|4
    SR     (+):    longitudinal, heat treatment B : Master curve (LMP) : 14922|22|3|5
    SR     (+):    longitudinal, heat treatment C : tested at 871 °C (1600 °F) : 14922|22|4|0
    SR     (+):    longitudinal, heat treatment C : tested at 899 °C (1650 °F) : 14922|22|4|1
    SR     (+):    longitudinal, heat treatment C : tested at 927 °C (1700 °F) : 14922|22|4|2
    SR     (+):    longitudinal, heat treatment C : tested at 954 °C (1750 °F) : 14922|22|4|3
    SR     (+):    longitudinal, heat treatment C : tested at 982 °C (1800 °F) : 14922|22|4|4
    SR     (+):    longitudinal, heat treatment C : Master curve (LMP) : 14922|22|4|5
    SR     (+):    longitudinal, heat treatment D : tested at 871 °C (1600 °F) : 14922|22|5|0
    SR     (+):    longitudinal, heat treatment D : tested at 899 °C (1650 °F) : 14922|22|5|1
    SR     (+):    longitudinal, heat treatment D : tested at 927 °C (1700 °F) : 14922|22|5|2
    SR     (+):    longitudinal, heat treatment D : tested at 954 °C (1750 °F) : 14922|22|5|3
    SR     (+):    longitudinal, heat treatment D : tested at 982 °C (1800 °F) : 14922|22|5|4
    SR     (+):    longitudinal, heat treatment D : Master curve (LMP) : 14922|22|5|5
    D     (+*):    solid : 14922|24|0|-1
    %El    (+):    2-step solutioning, aged : longitudinal : 14922|29|0|0
    %El    (+):    2-step solutioning, aged : transverse : 14922|29|0|1

return to listing

EP741NP (*)

    DLL    (+):    solid : discs, HIPed, aged & hardened : 14918|0|0|0
    TC     (+):    solid : discs, HIPed, aged & hardened : 14918|1|0|0
    E     (+*):    discs, HIPed, aged & hardened : 14918|3|0|-1
    UTS   (+*):    discs, HIPed, aged & hardened : 14918|5|0|-1
    MTE    (+):    solid : discs, HIPed, aged & hardened : 14918|8|0|0
    SH     (+):    solid : discs, HIPed, aged & hardened : 14918|9|0|0
    YS    (+*):    discs, HIPed, aged & hardened : 14918|13|0|-1
    CTE    (+):    solid : discs, HIPed, aged & hardened : 14918|16|0|0
    SR     (+):    discs, HIPed, aged & hardened : tested at 343 °C (650 °F) : 14918|22|0|0
    D      (+):    solid : discs, HIPed, aged & hardened : 14918|24|0|0
    TD     (+):    solid : discs, HIPed, aged & hardened : 14918|25|0|0
    %El   (+*):    discs, HIPed, aged & hardened : 14918|29|0|-1

return to listing

FB 780

    E     (+*):    solid : 10207|3|0|-1

return to listing

Fe - 30 Mn - 1 C (*)

    DLL    (+):    solid : 14919|0|0|-1
    TC     (+):    solid : 14919|1|0|-1
    MTE    (+):    solid : 14919|8|0|-1
    SH     (+):    solid : 14919|9|0|-1
    CTE    (+):    solid : 14919|16|0|-1
    D      (+):    solid : 14919|24|0|-1
    TD     (+):    solid : 14919|25|0|-1

return to listing

GH413

    UTS   (+*):    solution treated & aged : 10259|5|0|-1
    YS    (+*):    solution treated & aged : 10259|13|0|-1
    %El   (+*):    solution treated & aged : 10259|29|0|-1

return to listing

GH742 (*)

    YSC    (+):    solution treated at 1150 °C (2102 °F) : 0.001/s : 14927|21|0|0
    YSC    (+):    solution treated at 1150 °C (2102 °F) : 0.01/s : 14927|21|0|1
    YSC    (+):    solution treated at 1150 °C (2102 °F) : 0.1/s : 14927|21|0|2
    YSC    (+):    solution treated at 1150 °C (2102 °F) : 1/s : 14927|21|0|3
    D     (+*):    solid : 14927|24|0|-1

return to listing

Haynes HR-224

    IC     (+):    tested at 649 °C (1200 °F), solution heat-treated : 10 h : 14915|39|0|0
    IC     (+):    tested at 649 °C (1200 °F), solution heat-treated : 30 h : 14915|39|0|1
    IC     (+):    tested at 649 °C (1200 °F), solution heat-treated : 100 h : 14915|39|0|2
    IC     (+):    tested at 649 °C (1200 °F), solution heat-treated : 300 h : 14915|39|0|3
    IC     (+):    tested at 649 °C (1200 °F), solution heat-treated : 1,000 h : 14915|39|0|4
    IC     (+):    tested at 649 °C (1200 °F), solution heat-treated : 3,000 h : 14915|39|0|5
    IC     (+):    tested at 649 °C (1200 °F), solution heat-treated : 10,000 h : 14915|39|0|6
    IC     (+):    tested at 704 °C (1300 °F), solution heat-treated : 10 h : 14915|39|1|0
    IC     (+):    tested at 704 °C (1300 °F), solution heat-treated : 30 h : 14915|39|1|1
    IC     (+):    tested at 704 °C (1300 °F), solution heat-treated : 100 h : 14915|39|1|2
    IC     (+):    tested at 704 °C (1300 °F), solution heat-treated : 300 h : 14915|39|1|3
    IC     (+):    tested at 704 °C (1300 °F), solution heat-treated : 1,000 h : 14915|39|1|4
    IC     (+):    tested at 704 °C (1300 °F), solution heat-treated : 3,000 h : 14915|39|1|5
    IC     (+):    tested at 704 °C (1300 °F), solution heat-treated : 10,000 h : 14915|39|1|6
    IC     (+):    tested at 760 °C (1400 °F), solution heat-treated : 10 h : 14915|39|2|0
    IC     (+):    tested at 760 °C (1400 °F), solution heat-treated : 30 h : 14915|39|2|1
    IC     (+):    tested at 760 °C (1400 °F), solution heat-treated : 100 h : 14915|39|2|2
    IC     (+):    tested at 760 °C (1400 °F), solution heat-treated : 300 h : 14915|39|2|3
    IC     (+):    tested at 760 °C (1400 °F), solution heat-treated : 1,000 h : 14915|39|2|4
    IC     (+):    tested at 760 °C (1400 °F), solution heat-treated : 3,000 h : 14915|39|2|5
    IC     (+):    tested at 760 °C (1400 °F), solution heat-treated : 10,000 h : 14915|39|2|6
    IC     (+):    tested at 816 °C (1500 °F), solution heat-treated : 10 h : 14915|39|3|0
    IC     (+):    tested at 816 °C (1500 °F), solution heat-treated : 30 h : 14915|39|3|1
    IC     (+):    tested at 816 °C (1500 °F), solution heat-treated : 100 h : 14915|39|3|2
    IC     (+):    tested at 816 °C (1500 °F), solution heat-treated : 300 h : 14915|39|3|3
    IC     (+):    tested at 816 °C (1500 °F), solution heat-treated : 1,000 h : 14915|39|3|4
    IC     (+):    tested at 816 °C (1500 °F), solution heat-treated : 3,000 h : 14915|39|3|5
    IC     (+):    tested at 816 °C (1500 °F), solution heat-treated : 10,000 h : 14915|39|3|6
    IC     (+):    tested at 871 °C (1600 °F), solution heat-treated : 10 h : 14915|39|4|0
    IC     (+):    tested at 871 °C (1600 °F), solution heat-treated : 30 h : 14915|39|4|1
    IC     (+):    tested at 871 °C (1600 °F), solution heat-treated : 100 h : 14915|39|4|2
    IC     (+):    tested at 871 °C (1600 °F), solution heat-treated : 300 h : 14915|39|4|3
    IC     (+):    tested at 871 °C (1600 °F), solution heat-treated : 1,000 h : 14915|39|4|4
    IC     (+):    tested at 871 °C (1600 °F), solution heat-treated : 3,000 h : 14915|39|4|5
    IC     (+):    tested at 871 °C (1600 °F), solution heat-treated : 10,000 h : 14915|39|4|6
    IC     (+):    tested at 927 °C (1700 °F), solution heat-treated : 10 h : 14915|39|5|0
    IC     (+):    tested at 927 °C (1700 °F), solution heat-treated : 30 h : 14915|39|5|1
    IC     (+):    tested at 927 °C (1700 °F), solution heat-treated : 100 h : 14915|39|5|2
    IC     (+):    tested at 927 °C (1700 °F), solution heat-treated : 300 h : 14915|39|5|3
    IC     (+):    tested at 927 °C (1700 °F), solution heat-treated : 1,000 h : 14915|39|5|4
    IC     (+):    tested at 927 °C (1700 °F), solution heat-treated : 3,000 h : 14915|39|5|5
    IC     (+):    tested at 927 °C (1700 °F), solution heat-treated : 10,000 h : 14915|39|5|6
    IC     (+):    tested at 982 °C (1800 °F), solution heat-treated : 10 h : 14915|39|6|0
    IC     (+):    tested at 982 °C (1800 °F), solution heat-treated : 30 h : 14915|39|6|1
    IC     (+):    tested at 982 °C (1800 °F), solution heat-treated : 100 h : 14915|39|6|2
    IC     (+):    tested at 982 °C (1800 °F), solution heat-treated : 300 h : 14915|39|6|3
    IC     (+):    tested at 982 °C (1800 °F), solution heat-treated : 1,000 h : 14915|39|6|4
    IC     (+):    tested at 982 °C (1800 °F), solution heat-treated : 3,000 h : 14915|39|6|5
    IC     (+):    tested at 982 °C (1800 °F), solution heat-treated : 10,000 h : 14915|39|6|6
    IC     (+):    tested at 1038 °C (1900 °F), solution heat-treated : 10 h : 14915|39|7|0
    IC     (+):    tested at 1038 °C (1900 °F), solution heat-treated : 30 h : 14915|39|7|1
    IC     (+):    tested at 1038 °C (1900 °F), solution heat-treated : 100 h : 14915|39|7|2
    IC     (+):    tested at 1038 °C (1900 °F), solution heat-treated : 300 h : 14915|39|7|3
    IC     (+):    tested at 1038 °C (1900 °F), solution heat-treated : 1,000 h : 14915|39|7|4
    IC     (+):    tested at 1038 °C (1900 °F), solution heat-treated : 3,000 h : 14915|39|7|5
    IC     (+):    tested at 1038 °C (1900 °F), solution heat-treated : 10,000 h : 14915|39|7|6
    IC     (+):    tested at 1093 °C (2000 °F), solution heat-treated : 10 h : 14915|39|8|0
    IC     (+):    tested at 1093 °C (2000 °F), solution heat-treated : 30 h : 14915|39|8|1
    IC     (+):    tested at 1093 °C (2000 °F), solution heat-treated : 100 h : 14915|39|8|2
    IC     (+):    tested at 1093 °C (2000 °F), solution heat-treated : 300 h : 14915|39|8|3
    IC     (+):    tested at 1093 °C (2000 °F), solution heat-treated : 1,000 h : 14915|39|8|4
    IC     (+):    tested at 1093 °C (2000 °F), solution heat-treated : 3,000 h : 14915|39|8|5
    IC     (+):    tested at 1093 °C (2000 °F), solution heat-treated : 10,000 h : 14915|39|8|6

return to listing

Haynes R-41 (Rene 41)

    CRS    (+):    1% strain, age hardened sheet : Master curve (LMP) : 1939|30|0|6

return to listing

Haynes Ultimet

    FSN    (+):    solution annealed : tested at 20 °C (68 °F), R = 0.05, axial, dry air at 20 Hz, maximum stress values : 475|6|0|0
    FSN    (+):    solution annealed : tested at 20 °C (68 °F), R = 0.05, axial, regular air at 20 Hz, maximum stress values : 475|6|0|1
    FSN    (+):    solution annealed : tested at 20 °C (68 °F), R = 0.05, axial, vacuum at 20 Hz, maximum stress values : 475|6|0|2
    FSN    (+):    solution annealed : tested at 20 °C (68 °F), R = 0.05, axial, regular air at 1000 Hz, maximum stress values : 475|6|0|3

return to listing

HCR (*)

    TC    (+*):    solid : 14945|1|0|-1
    RHO   (+*):    solid : 14945|2|0|-1
    E     (+*):    solid : 14945|3|0|-1
    UTS   (+*):    hard rolled : 14945|5|1|-1
    RPB    (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|7|0|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|7|0|1
    RPB    (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|7|0|2
    RPB    (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 3200 Hz : 14945|7|0|3
    RPB    (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|7|1|0
    RPB    (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|7|1|1
    RPB    (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|7|1|2
    RPB    (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 3200 Hz : 14945|7|1|3
    RPB    (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|7|2|0
    RPB    (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|7|2|1
    RPB    (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|7|2|2
    RPB    (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 3200 Hz : 14945|7|2|3
    SH    (+*):    solid : 14945|9|0|-1
    SIGMA (+*):    solid : 14945|10|0|-1
    AP     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|15|0|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|15|0|1
    AP     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|15|0|2
    AP     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 3200 Hz : 14945|15|0|3
    AP     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|15|1|0
    AP     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|15|1|1
    AP     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|15|1|2
    AP     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 3200 Hz : 14945|15|1|3
    AP     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|15|2|0
    AP     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|15|2|1
    AP     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|15|2|2
    AP     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 3200 Hz : 14945|15|2|3
    BH     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|23|0|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|23|0|1
    BH     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|23|0|2
    BH     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 3200 Hz : 14945|23|0|3
    BH     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|23|1|0
    BH     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|23|1|1
    BH     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|23|1|2
    BH     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 3200 Hz : 14945|23|1|3
    BH     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|23|2|0
    BH     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|23|2|1
    BH     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|23|2|2
    BH     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 3200 Hz : 14945|23|2|3
    D     (+*):    solid : 14945|24|0|-1
    TD    (+*):    solid : 14945|25|0|-1
    HB     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|31|0|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|31|0|1
    HB     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|31|0|2
    HB     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 3200 Hz : 14945|31|0|3
    HB     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|31|1|0
    HB     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|31|1|1
    HB     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|31|1|2
    HB     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 3200 Hz : 14945|31|1|3
    HB     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|31|2|0
    HB     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|31|2|1
    HB     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|31|2|2
    HB     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 3200 Hz : 14945|31|2|3
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|43|0|0
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|43|0|1
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|43|0|2
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 2400 Hz : 14945|43|0|3
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|43|1|0
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|43|1|1
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|43|1|2
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 2400 Hz : 14945|43|1|3
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14945|43|2|0
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14945|43|2|1
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 1600 Hz : 14945|43|2|2
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 2400 Hz : 14945|43|2|3

return to listing

Hiperco 50 alloy

    HB     (^):    0.356 mm (0.014 inch) thick strip, standard magnetic anneal : tested at 20 °C (68 °F) : 1646|31|0|0

return to listing

Hiperco 50A alloy

    HB     (^):    bar & other shapes : tested at 20 °C (68 °F), standard heat-treated : 1647|31|1|0

return to listing

Hostaform C 9021 AW

    CRS    (+):    1% strain : tested at 80 °C (176 °F) : 13471|30|0|0
    CRS    (+):    1.5% strain : tested at 80 °C (176 °F) : 13471|30|1|0
    CRS    (+):    2% strain : tested at 80 °C (176 °F) : 13471|30|2|0
    CRS    (+):    2.5% strain : tested at 80 °C (176 °F) : 13471|30|3|0
    CRS    (+):    3% strain : tested at 80 °C (176 °F) : 13471|30|4|0

return to listing

HS 50 (*)

    TC    (+*):    solid : 14955|1|0|-1
    RHO   (+*):    solid : 14955|2|0|-1
    E     (+*):    solid : 14955|3|0|-1
    UTS   (+*):    treated at 760 °C (1400 °F) : 14955|5|0|-1
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14955|7|0|0
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 850 °C (1562 °F) : 14955|7|0|1
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 920 °C (1688 °F) : 14955|7|0|2
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 970 °C (1778 °F) : 14955|7|0|3
    SH    (+*):    solid : 14955|9|0|-1
    SIGMA (+*):    solid : 14955|10|0|-1
    YS    (+*):    treated at 760 °C (1400 °F) : 14955|13|0|-1
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14955|15|0|0
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 850 °C (1562 °F) : 14955|15|0|1
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 920 °C (1688 °F) : 14955|15|0|2
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 970 °C (1778 °F) : 14955|15|0|3
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14955|23|0|0
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 850 °C (1562 °F) : 14955|23|0|1
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 920 °C (1688 °F) : 14955|23|0|2
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 970 °C (1778 °F) : 14955|23|0|3
    D     (+*):    solid : 14955|24|0|-1
    TD    (+*):    solid : 14955|25|0|-1
    %El   (+*):    treated at 760 °C (1400 °F) : 14955|29|0|-1
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14955|31|0|0
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 850 °C (1562 °F) : 14955|31|0|1
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 920 °C (1688 °F) : 14955|31|0|2
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 970 °C (1778 °F) : 14955|31|0|3

return to listing

IN-100

    FSN    (+):    subsolvus powder processed pancake forging : tested at 650 °C (1202 °F), R = 0.05, axial, maximum stress values : 1951|6|0|0
    FSN    (+):    subsolvus powder processed pancake forging : tested at 650 °C (1202 °F), R = 0.05, axial, 6 s at peak load, maximum stress values : 1951|6|0|1
    FEN    (+):    GATORIZED, forged, solution annealed & aged : tested at 649 °C (1200 °F), R = -1, axial, no hold, total strain range : 1951|14|1|0
    FEN    (+):    GATORIZED, forged, solution annealed & aged : tested at 649 °C (1200 °F), R = -1, axial, 900 s hold at max tensile strain, total strain range : 1951|14|1|1
    CRS    (^):    0.1% strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : tested at 1038 °C (1900 °F) : 1951|30|0|4
    CRS    (^):    0.1% strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : Master curve (LMP) : 1951|30|0|5
    CRS    (^):    0.2% strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : tested at 816 °C (1500 °F) : 1951|30|1|1
    CRS    (^):    0.2% strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : tested at 1038 °C (1900 °F) : 1951|30|1|4
    CRS    (^):    0.2% strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : Master curve (LMP) : 1951|30|1|5
    CRS    (^):    0.5% strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : tested at 816 °C (1500 °F) : 1951|30|2|1
    CRS    (^):    0.5% strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : Master curve (LMP) : 1951|30|2|5
    CRS    (^):    1% strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : tested at 816 °C (1500 °F) : 1951|30|3|1
    CRS    (^):    1% strain, as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : Master curve (LMP) : 1951|30|3|5
    CRS    (^):    0.1% strain, as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material : tested at 816 °C (1500 °F) : 1951|30|4|0
    IC     (+):    tested at 732 °C (1350 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 3 h : 1951|39|0|0
    IC     (+):    tested at 732 °C (1350 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 10 h : 1951|39|0|1
    IC     (+):    tested at 732 °C (1350 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 30 h : 1951|39|0|2
    IC     (+):    tested at 732 °C (1350 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 100 h : 1951|39|0|3
    IC     (+):    tested at 732 °C (1350 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 300 h : 1951|39|0|4
    IC     (+):    tested at 816 °C (1500 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 3 h : 1951|39|1|0
    IC     (+):    tested at 816 °C (1500 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 10 h : 1951|39|1|1
    IC     (+):    tested at 816 °C (1500 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 30 h : 1951|39|1|2
    IC     (+):    tested at 816 °C (1500 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 100 h : 1951|39|1|3
    IC     (+):    tested at 816 °C (1500 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 300 h : 1951|39|1|4
    IC     (+):    tested at 927 °C (1700 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 3 h : 1951|39|2|0
    IC     (+):    tested at 927 °C (1700 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 10 h : 1951|39|2|1
    IC     (+):    tested at 927 °C (1700 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 30 h : 1951|39|2|2
    IC     (+):    tested at 927 °C (1700 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 100 h : 1951|39|2|3
    IC     (+):    tested at 927 °C (1700 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 300 h : 1951|39|2|4
    IC     (+):    tested at 927 °C (1700 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 1,000 h : 1951|39|2|5
    IC     (+):    tested at 982 °C (1800 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 10 h : 1951|39|3|1
    IC     (+):    tested at 982 °C (1800 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 30 h : 1951|39|3|2
    IC     (+):    tested at 982 °C (1800 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 100 h : 1951|39|3|3
    IC     (+):    tested at 982 °C (1800 °F), as-cast, coarse grain (≥ 3.17 mm (0.125 inch)) material : 300 h : 1951|39|3|4
    IC     (+):    tested at 816 °C (1500 °F), as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material : 3 h : 1951|39|4|0
    IC     (+):    tested at 816 °C (1500 °F), as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material : 10 h : 1951|39|4|1
    IC     (+):    tested at 816 °C (1500 °F), as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material : 30 h : 1951|39|4|2
    IC     (+):    tested at 816 °C (1500 °F), as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material : 100 h : 1951|39|4|3
    IC     (+):    tested at 927 °C (1700 °F), as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material : 30 h : 1951|39|5|2
    IC     (+):    tested at 927 °C (1700 °F), as-cast, fine grain (≤ 1.59 mm (0.0625 inch)) material : 100 h : 1951|39|5|3

return to listing

IN-738

    FEN    (+):    cast : tested at 850 °C (1562 °F), R = -1, axial, total strain range : 1953|14|0|0
    FEN    (+):    cast : tested at 850 °C (1562 °F), R = -1, axial, plastic strain range : 1953|14|0|1

return to listing

IN-792 5A

    DLL    (+):    solid : 10258|0|0|-1
    MTE    (+):    solid : 10258|8|0|-1
    D      (+):    solid : 10258|24|0|-1

return to listing

IN-792 (*)

    DLL    (+):    solid : 14925|0|0|-1
    MTE    (+):    solid : 14925|8|0|-1
    D      (+):    solid : 14925|24|0|-1

return to listing

Incoloy 864

    SR     (^):    annealed : tested at 760 °C (1400 °F) : 1079|22|0|0
    SR     (^):    annealed : tested at 871 °C (1600 °F) : 1079|22|0|1
    SR     (^):    annealed : tested at 982 °C (1800 °F) : 1079|22|0|2
    SR     (^):    annealed : Master curve (LMP) : 1079|22|0|3

return to listing

Inconel 625LCF

    FSN    (+):    bending fatigue, sheet : tested at 20 °C (68 °F), R = -1, annealed, maximum stress values : 10299|6|0|0

return to listing

Inconel 706

    SSCC   (+):    0.0005/s, cast : tested at 1050 °C (1922 °F) : 1866|12|0|0
    SSCC   (+):    0.001/s, cast : tested at 1050 °C (1922 °F) : 1866|12|1|0
    SSCC   (+):    0.01/s, cast : tested at 900 °C (1652 °F) : 1866|12|2|0
    SSCC   (+):    0.01/s, cast : tested at 950 °C (1742 °F) : 1866|12|2|1
    SSCC   (+):    0.01/s, cast : tested at 1000 °C (1832 °F) : 1866|12|2|2
    SSCC   (+):    0.01/s, cast : tested at 1050 °C (1922 °F) : 1866|12|2|3
    SSCC   (+):    0.01/s, cast : tested at 1100 °C (2012 °F) : 1866|12|2|4
    SSCC   (+):    0.1/s, cast : tested at 1050 °C (1922 °F) : 1866|12|3|0
    SSCC   (+):    1/s, cast : tested at 1050 °C (1922 °F) : 1866|12|4|0

return to listing

Inconel 718

    UTS    (+):    other conditions : VIM/VAR forging, aged : 1868|5|0|4
    FSN    (+):    solution treated & aged, grain size ASTM 10 : tested at 20 °C (68 °F), R = -1, ultrasonic at 19.5 kHz, UTS = 1.46 GPa (212 ksi), YS = 1.32 GPa (191 ksi), stress amplitude values : 1868|6|5|0
    FSN    (+):    solution treated & aged, grain size ASTM 10 : tested at 20 °C (68 °F), R = -1, rotary bending, 55 Hz, UTS = 1.46 GPa (212 ksi), YS = 1.32 GPa (191 ksi), stress amplitude values : 1868|6|5|1
    FSN    (+):    solution treated & aged, grain size ASTM 10 : tested at 20 °C (68 °F), R = -1, axial, UTS = 1.46 GPa (212 ksi), YS = 1.32 GPa (191 ksi), stress amplitude values : 1868|6|5|2
    FSN    (+):    solution treated & aged, grain size ASTM 10 : tested at 20 °C (68 °F), R = -1, ultrasonic at 20 kHz, UTS = 1.39 GPa (202 ksi), YS = 1.22 GPa (177 ksi), stress amplitude values : 1868|6|5|3
    FSN    (+):    forgings, double aged : tested at 350 °C (662 °F), R = 0.05, axial, ASTM 6/7, maximum stress values : 1868|6|6|0
    FSN    (+):    forgings, double aged : tested at 550 °C (1022 °F), R = 0.05, axial, ASTM 6/7, maximum stress values : 1868|6|6|1
    FSN    (+):    forgings, double aged : tested at 25 °C (77 °F), R = 0.05, axial, ASTM 8/10, stress range values : 1868|6|6|2
    FSN    (+):    forgings, double aged : tested at 550 °C (1022 °F), R = 0.05, axial, ASTM 8/10, stress range values : 1868|6|6|3
    FSN    (+):    forgings, double aged : tested at 650 °C (1202 °F), R = 0.05, axial, ASTM 8/10, stress range values : 1868|6|6|4
    FSN    (+):    forgings, double aged : tested at 350 °C (662 °F), R = 0.05, axial, ASTM 10/11, maximum stress values : 1868|6|6|5
    FSN    (+):    forgings, double aged : tested at 550 °C (1022 °F), R = 0.05, axial, ASTM 10/11, maximum stress values : 1868|6|6|6
    YS     (+):    other conditions : VIM/VAR forging, aged : 1868|13|0|4
    FEN    (+):    solution annealed at 954 °C (1750 °F), aged at 720 °C (1328 °F) & 620 °C (1148 °F) : tested at 25 °C (77 °F), R = 0, axial, K_t = 3, total strain range : 1868|14|3|1
    FEN    (+):    solution annealed at 954 °C (1750 °F), aged at 720 °C (1328 °F) & 620 °C (1148 °F) : tested at 650 °C (1202 °F), R = 0, axial, K_t = 3, total strain range : 1868|14|3|2
    FEN    (+):    solution annealed at 954 °C (1750 °F), aged at 720 °C (1328 °F) & 620 °C (1148 °F) : tested at 25 °C (77 °F), R = 0, axial, K_t = 3, plastic strain amplitude : 1868|14|3|3
    FEN    (+):    solution annealed at 954 °C (1750 °F), aged at 720 °C (1328 °F) & 620 °C (1148 °F) : tested at 650 °C (1202 °F), R = 0, axial, K_t = 3, plastic strain amplitude : 1868|14|3|4
    FEN    (+):    forgings, double aged : tested at 25 °C (77 °F), R = 0.05, axial, ASTM 8/10, total strain range : 1868|14|5|0
    FEN    (+):    forgings, double aged : tested at 550 °C (1022 °F), R = 0.05, axial, ASTM 8/10, total strain range : 1868|14|5|1
    FEN    (+):    forgings, double aged : tested at 650 °C (1202 °F), R = 0.05, axial, ASTM 8/10, total strain range : 1868|14|5|2
    FEN    (+):    forgings, double aged : tested at 25 °C (77 °F), R = 0.05, axial, ASTM 8/10, plastic strain range : 1868|14|5|3
    FEN    (+):    forgings, double aged : tested at 550 °C (1022 °F), R = 0.05, axial, ASTM 8/10, plastic strain range : 1868|14|5|4
    FEN    (+):    forgings, double aged : tested at 650 °C (1202 °F), R = 0.05, axial, ASTM 8/10, plastic strain range : 1868|14|5|5

return to listing

Inconel 718SPF

    UTS   (+*):    mill annealed at 927 °C (1700 °F), 0.508 mm (0.02 inch) thick sheet : 9266|5|0|-1
    UTS   (+*):    aged, 0.508 mm (0.02 inch) thick sheet : 9266|5|1|-1
    UTS   (+*):    effect of cold work on RT properties : 0% cold worked : 9266|5|2|0
    UTS   (+*):    effect of cold work on RT properties : 13% cold worked : 9266|5|2|1
    UTS   (+*):    effect of cold work on RT properties : 19% cold worked : 9266|5|2|2
    UTS   (+*):    effect of cold work on RT properties : 33% cold worked : 9266|5|2|3
    YS    (+*):    mill annealed at 927 °C (1700 °F), 0.508 mm (0.02 inch) thick sheet : 9266|13|0|-1
    YS    (+*):    aged, 0.508 mm (0.02 inch) thick sheet : 9266|13|1|-1
    YS    (+*):    effect of cold work on RT properties : 0% cold worked : 9266|13|2|0
    YS    (+*):    effect of cold work on RT properties : 13% cold worked : 9266|13|2|1
    YS    (+*):    effect of cold work on RT properties : 19% cold worked : 9266|13|2|2
    YS    (+*):    effect of cold work on RT properties : 33% cold worked : 9266|13|2|3
    SR     (+):    aged sheet : tested at 649 °C (1200 °F) : 9266|22|0|0
    %El   (+*):    mill annealed at 927 °C (1700 °F), 0.508 mm (0.02 inch) thick sheet : 9266|29|0|-1
    %El   (+*):    aged, 0.508 mm (0.02 inch) thick sheet : 9266|29|1|-1
    %El   (+*):    effect of cold work on RT properties : 0% cold worked : 9266|29|2|0
    %El   (+*):    effect of cold work on RT properties : 13% cold worked : 9266|29|2|1
    %El   (+*):    effect of cold work on RT properties : 19% cold worked : 9266|29|2|2
    %El   (+*):    effect of cold work on RT properties : 33% cold worked : 9266|29|2|3

return to listing

Inconel HX / Hastelloy X / Nimonic PE13

    FEN    (+):    solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled : tested at 816 °C (1500 °F), R = -1, axial, total strain amplitude : 1873|14|0|0
    FEN    (+):    solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled : tested at 816 °C (1500 °F), R = -1, axial, plastic strain amplitude : 1873|14|0|1
    FEN    (+):    solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled : tested at 816 °C (1500 °F), R = -1, axial, elastic strain amplitude : 1873|14|0|2
    FEN    (+):    solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled : tested at 871 °C (1600 °F), R = -1, axial, total strain range : 1873|14|0|3
    FEN    (+):    solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled : tested at 927 °C (1700 °F), R = -1, axial, total strain amplitude : 1873|14|0|4
    FEN    (+):    solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled : tested at 927 °C (1700 °F), R = -1, axial, plastic strain amplitude : 1873|14|0|5
    FEN    (+):    solution-annealed, annealed at 954 °C (1750 °F), rapid air cooled : tested at 927 °C (1700 °F), R = -1, axial, elastic strain amplitude : 1873|14|0|6

return to listing

MERL 76 (*)

    DLL    (+):    solid : 14932|0|0|-1
    TC     (+):    solid : 14932|1|0|-1
    E      (+):    solid : 14932|3|0|-1
    UTS    (+):    HIPed, solution annealed & aged : 14932|5|0|-1
    FSN    (+):    K_t = 1.0 : tested at 427 °C (800 °F), R = -1, axial, maximum stress values : 14932|6|0|0
    FSN    (+):    K_t = 1.0 : tested at 538 °C (1000 °F), R = -1, axial, maximum stress values : 14932|6|0|1
    FSN    (+):    K_t = 1.0 : tested at 635 °C (1175 °F), R = -1, axial, maximum stress values : 14932|6|0|2
    FSN    (+):    K_t = 2.0 : tested at 427 °C (800 °F), R = -1, axial, maximum stress values : 14932|6|1|0
    FSN    (+):    K_t = 2.0 : tested at 538 °C (1000 °F), R = -1, axial, maximum stress values : 14932|6|1|1
    FSN    (+):    K_t = 2.0 : tested at 635 °C (1175 °F), R = -1, axial, maximum stress values : 14932|6|1|2
    FSN    (+):    K_t = 3.0 : tested at 427 °C (800 °F), R = -1, axial, maximum stress values : 14932|6|2|0
    FSN    (+):    K_t = 3.0 : tested at 538 °C (1000 °F), R = -1, axial, maximum stress values : 14932|6|2|1
    FSN    (+):    K_t = 3.0 : tested at 635 °C (1175 °F), R = -1, axial, maximum stress values : 14932|6|2|2
    MTE    (+):    solid : 14932|8|0|-1
    SH     (+):    solid : 14932|9|0|-1
    YS     (+):    HIPed, solution annealed & aged : 14932|13|0|-1
    FEN    (+):    HIPed, solution annealed & aged : tested at 649 °C (1200 °F), R = -1, axial, no hold, total strain range : 14932|14|0|0
    FEN    (+):    HIPed, solution annealed & aged : tested at 649 °C (1200 °F), R = -1, axial, 900 s hold at max tensile strain, total strain range : 14932|14|0|1
    SR     (+):    HIPed, solution treated & aged : tested at 649 °C (1200 °F) : 14932|22|0|0
    SR     (+):    HIPed, solution treated & aged : tested at 704 °C (1300 °F) : 14932|22|0|1
    SR     (+):    HIPed, solution treated & aged : tested at 732 °C (1350 °F) : 14932|22|0|2
    SR     (+):    HIPed, solution treated & aged : tested at 760 °C (1400 °F) : 14932|22|0|3
    SR     (+):    HIPed, solution treated & aged : Master curve (LMP) : 14932|22|0|4
    D      (+):    solid : 14932|24|0|-1
    TD     (+):    solid : 14932|25|0|-1
    %El    (+):    HIPed, solution annealed & aged : 14932|29|0|-1
    CRS    (+):    0.1% strain, HIPed, solution treated & aged : tested at 649 °C (1200 °F) : 14932|30|0|0
    CRS    (+):    0.1% strain, HIPed, solution treated & aged : tested at 732 °C (1350 °F) : 14932|30|0|1
    CRS    (+):    0.1% strain, HIPed, solution treated & aged : tested at 760 °C (1400 °F) : 14932|30|0|2
    CRS    (+):    0.2% strain, HIPed, solution treated & aged : tested at 649 °C (1200 °F) : 14932|30|1|0
    CRS    (+):    0.2% strain, HIPed, solution treated & aged : tested at 732 °C (1350 °F) : 14932|30|1|1
    CRS    (+):    0.2% strain, HIPed, solution treated & aged : tested at 760 °C (1400 °F) : 14932|30|1|2
    IC     (+):    tested at 649 °C (1200 °F), HIPed, solution treated & aged : 100 h : 14932|39|0|1
    IC     (+):    tested at 732 °C (1350 °F), HIPed, solution treated & aged : 30 h : 14932|39|1|0
    IC     (+):    tested at 732 °C (1350 °F), HIPed, solution treated & aged : 100 h : 14932|39|1|1
    IC     (+):    tested at 732 °C (1350 °F), HIPed, solution treated & aged : 300 h : 14932|39|1|2
    IC     (+):    tested at 760 °C (1400 °F), HIPed, solution treated & aged : 100 h : 14932|39|2|1
    IC     (+):    tested at 760 °C (1400 °F), HIPed, solution treated & aged : 300 h : 14932|39|2|2

return to listing

Mumetal Plus (*)

    TC    (+*):    solid : 14936|1|0|-1
    RHO   (+*):    solid : 14936|2|0|-1
    E     (+*):    solid : 14936|3|0|-1
    UTS   (+*):    annealed : 14936|5|0|-1
    UTS   (+*):    hard rolled : 14936|5|1|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14936|7|0|0
    RPB    (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14936|7|1|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14936|7|2|0
    SH    (+*):    solid : 14936|9|0|-1
    SIGMA (+*):    solid : 14936|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14936|15|0|0
    AP     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14936|15|1|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14936|15|2|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14936|23|0|0
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14936|23|1|0
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14936|23|1|1
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14936|23|1|2
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14936|23|2|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14936|23|2|1
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14936|23|2|2
    D     (+*):    solid : 14936|24|0|-1
    TD    (+*):    solid : 14936|25|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14936|31|0|0
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14936|31|1|0
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14936|31|1|1
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14936|31|1|2
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14936|31|2|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14936|31|2|1
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14936|31|2|2

return to listing

Mumetal (*)

    TC    (+*):    solid : 14934|1|0|-1
    RHO   (+*):    solid : 14934|2|0|-1
    E     (+*):    solid : 14934|3|0|-1
    UTS   (+*):    annealed : 14934|5|0|-1
    UTS   (+*):    hard rolled : 14934|5|1|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14934|7|0|0
    RPB    (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14934|7|1|0
    RPB    (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14934|7|2|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14934|7|3|0
    SH    (+*):    solid : 14934|9|0|-1
    SIGMA (+*):    solid : 14934|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14934|15|0|0
    AP     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14934|15|1|0
    AP     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14934|15|2|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14934|15|3|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14934|23|0|0
    BH     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14934|23|1|0
    BH     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14934|23|1|1
    BH     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14934|23|1|2
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14934|23|2|0
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14934|23|2|1
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14934|23|2|2
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14934|23|3|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14934|23|3|1
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14934|23|3|2
    D     (+*):    solid : 14934|24|0|-1
    TD    (+*):    solid : 14934|25|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14934|31|0|0
    HB     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14934|31|1|0
    HB     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14934|31|1|1
    HB     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14934|31|1|2
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14934|31|2|0
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14934|31|2|1
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14934|31|2|2
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14934|31|3|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14934|31|3|1
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14934|31|3|2
    CL     (+):    0.3 mm (0.0118 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14934|43|0|0
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14934|43|1|0
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14934|43|1|1
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 1.6 kHz : 14934|43|1|2
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 3.2 kHz : 14934|43|1|3
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14934|43|2|0
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14934|43|2|1
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 1.6 kHz : 14934|43|2|2
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 3.2 kHz : 14934|43|2|3
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 1.6 kHz : 14934|43|3|0
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 3.2 kHz : 14934|43|3|1
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 10 kHz : 14934|43|3|2
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 25 kHz : 14934|43|3|3
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 50 kHz : 14934|43|3|4
    CL     (+):    0.013 mm (0.000512 inch) thick strip : tested at 20 °C (68 °F), 10 kHz : 14934|43|4|0
    CL     (+):    0.013 mm (0.000512 inch) thick strip : tested at 20 °C (68 °F), 25 kHz : 14934|43|4|1
    CL     (+):    0.013 mm (0.000512 inch) thick strip : tested at 20 °C (68 °F), 50 kHz : 14934|43|4|2

return to listing

Permendur 24 (*)

    TC    (+*):    solid : 14953|1|0|-1
    RHO   (+*):    solid : 14953|2|0|-1
    E     (+*):    solid : 14953|3|0|-1
    UTS   (+*):    treated at 760 °C (1400 °F) : 14953|5|0|-1
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14953|7|0|0
    RPB    (+):    solid section, heat treated 2 h at 850 °C (1562 °F) : tested at 20 °C (68 °F) : 14953|7|1|0
    SH    (+*):    solid : 14953|9|0|-1
    SIGMA (+*):    solid : 14953|10|0|-1
    YS    (+*):    treated at 760 °C (1400 °F) : 14953|13|0|-1
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14953|15|0|0
    AP     (+):    solid section, heat treated 2 h at 850 °C (1562 °F) : tested at 20 °C (68 °F) : 14953|15|1|0
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14953|23|0|0
    BH     (+):    solid section, heat treated 2 h at 850 °C (1562 °F) : tested at 20 °C (68 °F) : 14953|23|1|0
    D     (+*):    solid : 14953|24|0|-1
    TD    (+*):    solid : 14953|25|0|-1
    %El   (+*):    treated at 760 °C (1400 °F) : 14953|29|0|-1
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14953|31|0|0
    HB     (+):    solid section, heat treated 2 h at 850 °C (1562 °F) : tested at 20 °C (68 °F), heat treated at 720 °C (1328 °F) : 14953|31|1|0
    CL     (+):    0.35 mm (0.0138 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 50 Hz : 14953|43|0|0
    CL     (+):    0.35 mm (0.0138 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 400 Hz : 14953|43|0|1
    CL     (+):    0.2 mm (0.00787 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 50 Hz : 14953|43|1|0
    CL     (+):    0.2 mm (0.00787 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 400 Hz : 14953|43|1|1

return to listing

Permendur 49 (*)

    TC    (+*):    solid : 14956|1|0|-1
    RHO   (+*):    solid : 14956|2|0|-1
    E     (+*):    solid : 14956|3|0|-1
    UTS   (+*):    treated at 760 °C (1400 °F) : 14956|5|0|-1
    RPB    (+):    solid section, heat treated 2 h at 850 °C (1562 °F) : tested at 20 °C (68 °F) : 14956|7|0|0
    SH    (+*):    solid : 14956|9|0|-1
    SIGMA (+*):    solid : 14956|10|0|-1
    YS    (+*):    treated at 760 °C (1400 °F) : 14956|13|0|-1
    AP     (+):    solid section, heat treated 2 h at 850 °C (1562 °F) : tested at 20 °C (68 °F) : 14956|15|0|0
    BH     (+):    solid section, heat treated 2 h at 850 °C (1562 °F) : tested at 20 °C (68 °F) : 14956|23|0|0
    D     (+*):    solid : 14956|24|0|-1
    TD    (+*):    solid : 14956|25|0|-1
    %El   (+*):    treated at 760 °C (1400 °F) : 14956|29|0|-1
    HB     (+):    solid section, heat treated 2 h at 850 °C (1562 °F) : tested at 20 °C (68 °F), heat treated at 720 °C (1328 °F) : 14956|31|0|0

return to listing

PM 1000 (*)

    FEN    (+):    fully recrystallized, 0.001/s : tested at 850 °C (1562 °F), R = -1, axial, total strain amplitude : 14923|14|0|0
    FEN    (+):    fully recrystallized, 0.001/s : tested at 1000 °C (1832 °F), R = -1, axial, total strain amplitude : 14923|14|0|1
    FEN    (+):    fully recrystallized, 1x10^-5/s : tested at 850 °C (1562 °F), R = -1, axial, total strain amplitude : 14923|14|1|0
    FEN    (+):    fully recrystallized, 1x10^-5/s : tested at 1000 °C (1832 °F), R = -1, axial, total strain amplitude : 14923|14|1|1
    D     (+*):    solid : 14923|24|0|-1

return to listing

PWA 1480

    SR     (+):    condition not specified : tested at 927 °C (1700 °F) : 1887|22|0|0
    SR     (+):    condition not specified : tested at 954 °C (1750 °F) : 1887|22|0|1
    SR     (+):    condition not specified : tested at 982 °C (1800 °F) : 1887|22|0|2
    SR     (+):    condition not specified : tested at 1010 °C (1850 °F) : 1887|22|0|3
    SR     (+):    condition not specified : tested at 1038 °C (1900 °F) : 1887|22|0|4
    SR     (+):    condition not specified : tested at 1066 °C (1950 °F) : 1887|22|0|5
    SR     (+):    condition not specified : tested at 1093 °C (2000 °F) : 1887|22|0|6
    SR     (+):    condition not specified : Master curve (LMP) : 1887|22|0|7

return to listing

PWA 1489 (*)

    FEN    (+):    in air : tested at 20 °C (68 °F), R = -1, axial, total strain amplitude : 14933|14|0|0
    FEN    (+):    in H2 : tested at 20 °C (68 °F), R = -1, axial, total strain amplitude : 14933|14|1|0

return to listing

PWA 275 (*)

    E      (+):    solid : 14931|3|0|-1
    YS     (+):    solid : 14931|13|0|-1

return to listing

PWA 276 (*)

    DLL    (+):    solid : 14930|0|0|-1
    E      (+):    solid : 14930|3|0|-1
    UTS    (+):    solid : 14930|5|0|-1
    MTE    (+):    solid : 14930|8|0|-1
    YS     (+):    solid : 14930|13|0|-1
    %El    (+):    solid : 14930|29|0|-1

return to listing

Radiometal 36 (*)

    TC    (+*):    solid : 14942|1|0|-1
    RHO   (+*):    solid : 14942|2|0|-1
    E     (+*):    solid : 14942|3|0|-1
    UTS   (+*):    annealed : 14942|5|0|-1
    UTS   (+*):    hard rolled : 14942|5|1|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14942|7|0|0
    SH    (+*):    solid : 14942|9|0|-1
    SIGMA (+*):    solid : 14942|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14942|15|0|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14942|23|0|0
    D     (+*):    solid : 14942|24|0|-1
    TD    (+*):    solid : 14942|25|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14942|31|0|0
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 800 Hz : 14942|43|0|0
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 5 kHz : 14942|43|0|1

return to listing

Radiometal 4550 (*)

    TC    (+*):    solid : 14944|1|0|-1
    RHO   (+*):    solid : 14944|2|0|-1
    E     (+*):    solid : 14944|3|0|-1
    UTS   (+*):    annealed : 14944|5|0|-1
    UTS   (+*):    hard rolled : 14944|5|1|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14944|7|0|0
    RPB    (+):    0.35 mm (0.0138 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14944|7|1|0
    RPB    (+):    0.35 mm (0.0138 inch) thick strip at 60 Hz : tested at 20 °C (68 °F) : 14944|7|2|0
    RPB    (+):    0.35 mm (0.0138 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14944|7|3|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14944|7|4|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14944|7|5|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 1600 Hz : tested at 20 °C (68 °F) : 14944|7|6|0
    SH    (+*):    solid : 14944|9|0|-1
    SIGMA (+*):    solid : 14944|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14944|15|0|0
    AP     (+):    0.35 mm (0.0138 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14944|15|1|0
    AP     (+):    0.35 mm (0.0138 inch) thick strip at 60 Hz : tested at 20 °C (68 °F) : 14944|15|2|0
    AP     (+):    0.35 mm (0.0138 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14944|15|3|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14944|15|4|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14944|15|5|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 1600 Hz : tested at 20 °C (68 °F) : 14944|15|6|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14944|23|0|0
    BH     (+):    0.35 mm (0.0138 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14944|23|1|0
    BH     (+):    0.35 mm (0.0138 inch) thick strip at 60 Hz : tested at 20 °C (68 °F) : 14944|23|2|0
    BH     (+):    0.35 mm (0.0138 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14944|23|3|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14944|23|4|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14944|23|5|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 1600 Hz : tested at 20 °C (68 °F) : 14944|23|6|0
    D     (+*):    solid : 14944|24|0|-1
    TD    (+*):    solid : 14944|25|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14944|31|0|0
    HB     (+):    0.35 mm (0.0138 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14944|31|1|0
    HB     (+):    0.35 mm (0.0138 inch) thick strip at 60 Hz : tested at 20 °C (68 °F) : 14944|31|2|0
    HB     (+):    0.35 mm (0.0138 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14944|31|3|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14944|31|4|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14944|31|5|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 1600 Hz : tested at 20 °C (68 °F) : 14944|31|6|0
    CL     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14944|43|0|0
    CL     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), 60 Hz : 14944|43|0|1
    CL     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14944|43|0|2
    CL     (+):    0.2 mm (0.00787 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14944|43|1|0
    CL     (+):    0.2 mm (0.00787 inch) thick strip : tested at 20 °C (68 °F), 60 Hz : 14944|43|1|1
    CL     (+):    0.2 mm (0.00787 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14944|43|1|2

return to listing

Rene 88 DT (*)

    UTS    (+):    annealed : 14924|5|0|-1
    FSN    (+):    forging, supersolvus heat treatment, aged : tested at 593 °C (1100 °F), R = 0.05, axial, 10 Hz, maximum stress values : 14924|6|0|0
    FSN    (+):    forging, supersolvus heat treatment, aged : tested at 593 °C (1100 °F), R = 0.05, axial, ultrasonic, 19.2 kHz, maximum stress values : 14924|6|0|1
    SSCC   (+):    0.00032/s : tested at 1052 °C (1925 °F) : 14924|12|0|0
    SSCC   (+):    0.0032/s : tested at 1052 °C (1925 °F) : 14924|12|1|0
    SSCC   (+):    0.032/s : tested at 1052 °C (1925 °F) : 14924|12|2|0
    SSCC   (+):    0.1/s : tested at 1052 °C (1925 °F) : 14924|12|3|0
    YS     (+):    annealed : 14924|13|0|-1
    D     (+*):    solid : 14924|24|0|-1

return to listing

Rene 95

    FEN    (+):    HIPed, forged, solution annealed & aged : tested at 649 °C (1200 °F), R = -1, axial, no hold, total strain range : 1910|14|1|0
    FEN    (+):    HIPed, forged, solution annealed & aged : tested at 649 °C (1200 °F), R = -1, axial, 900 s hold at max tensile strain, total strain range : 1910|14|1|1

return to listing

Rotelloy 3 (*)

    TC    (+*):    solid : 14952|1|0|-1
    RHO   (+*):    solid : 14952|2|0|-1
    E     (+*):    solid : 14952|3|0|-1
    UTS   (+*):    treated at 760 °C (1400 °F) : 14952|5|0|-1
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 720 °C (1328 °F) : 14952|7|0|0
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14952|7|0|1
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 800 °C (1472 °F) : 14952|7|0|2
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 850 °C (1562 °F) : 14952|7|0|3
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 950 °C (1742 °F) : 14952|7|0|4
    SH    (+*):    solid : 14952|9|0|-1
    SIGMA (+*):    solid : 14952|10|0|-1
    YS    (+*):    treated at 760 °C (1400 °F) : 14952|13|0|-1
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 720 °C (1328 °F) : 14952|15|0|0
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14952|15|0|1
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 800 °C (1472 °F) : 14952|15|0|2
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 850 °C (1562 °F) : 14952|15|0|3
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 950 °C (1742 °F) : 14952|15|0|4
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 720 °C (1328 °F) : 14952|23|0|0
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14952|23|0|1
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 800 °C (1472 °F) : 14952|23|0|2
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 850 °C (1562 °F) : 14952|23|0|3
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 950 °C (1742 °F) : 14952|23|0|4
    D     (+*):    solid : 14952|24|0|-1
    TD    (+*):    solid : 14952|25|0|-1
    %El   (+*):    treated at 760 °C (1400 °F) : 14952|29|0|-1
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 720 °C (1328 °F) : 14952|31|0|0
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14952|31|0|1
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 800 °C (1472 °F) : 14952|31|0|2
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 850 °C (1562 °F) : 14952|31|0|3
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 950 °C (1742 °F) : 14952|31|0|4
    CL     (+):    0.35 mm (0.0138 inch) thick strip, heat treated at 720 °C (1328 °F) : tested at 20 °C (68 °F), 400 Hz : 14952|43|0|0
    CL     (+):    0.35 mm (0.0138 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 50 Hz : 14952|43|1|0
    CL     (+):    0.35 mm (0.0138 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 60 Hz : 14952|43|1|1
    CL     (+):    0.35 mm (0.0138 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 400 Hz : 14952|43|1|2
    CL     (+):    0.35 mm (0.0138 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 800 Hz : 14952|43|1|3
    CL     (+):    0.35 mm (0.0138 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 1200 Hz : 14952|43|1|4
    CL     (+):    0.35 mm (0.0138 inch) thick strip, heat treated at 850 °C (1562 °F) : tested at 20 °C (68 °F), 400 Hz : 14952|43|2|0
    CL     (+):    0.2 mm (0.00787 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 400 Hz : 14952|43|3|0
    CL     (+):    0.2 mm (0.00787 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 800 Hz : 14952|43|3|1
    CL     (+):    0.2 mm (0.00787 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 1200 Hz : 14952|43|3|2
    CL     (+):    0.1 mm (0.00394 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 400 Hz : 14952|43|4|0
    CL     (+):    0.1 mm (0.00394 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 800 Hz : 14952|43|4|1
    CL     (+):    0.1 mm (0.00394 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 1200 Hz : 14952|43|4|2

return to listing

Rotelloy 5 (*)

    TC    (+*):    solid : 14954|1|0|-1
    RHO   (+*):    solid : 14954|2|0|-1
    E     (+*):    solid : 14954|3|0|-1
    UTS   (+*):    treated at 760 °C (1400 °F) : 14954|5|0|-1
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 680 °C (1256 °F) : 14954|7|0|0
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 700 °C (1292 °F) : 14954|7|0|1
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 720 °C (1328 °F) : 14954|7|0|2
    RPB    (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14954|7|0|3
    RPB    (+):    0.2 mm (0.00787 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14954|7|1|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14954|7|2|0
    SH    (+*):    solid : 14954|9|0|-1
    SIGMA (+*):    solid : 14954|10|0|-1
    YS    (+*):    treated at 760 °C (1400 °F) : 14954|13|0|-1
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 680 °C (1256 °F) : 14954|15|0|0
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 700 °C (1292 °F) : 14954|15|0|1
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 720 °C (1328 °F) : 14954|15|0|2
    AP     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14954|15|0|3
    AP     (+):    0.2 mm (0.00787 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14954|15|1|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14954|15|2|0
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 680 °C (1256 °F) : 14954|23|0|0
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 700 °C (1292 °F) : 14954|23|0|1
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 720 °C (1328 °F) : 14954|23|0|2
    BH     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14954|23|0|3
    BH     (+):    0.2 mm (0.00787 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14954|23|1|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14954|23|2|0
    D     (+*):    solid : 14954|24|0|-1
    TD    (+*):    solid : 14954|25|0|-1
    %El   (+*):    treated at 760 °C (1400 °F) : 14954|29|0|-1
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 680 °C (1256 °F) : 14954|31|0|0
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 700 °C (1292 °F) : 14954|31|0|1
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 720 °C (1328 °F) : 14954|31|0|2
    HB     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14954|31|0|3
    HB     (+):    0.2 mm (0.00787 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14954|31|1|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), heat treated at 760 °C (1400 °F) : 14954|31|2|0
    CL     (+):    0.35 mm (0.0138 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 50 Hz : 14954|43|0|0
    CL     (+):    0.35 mm (0.0138 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 400 Hz : 14954|43|0|1
    CL     (+):    0.35 mm (0.0138 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 1600 Hz : 14954|43|0|2
    CL     (+):    0.2 mm (0.00787 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 50 Hz : 14954|43|1|0
    CL     (+):    0.2 mm (0.00787 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 400 Hz : 14954|43|1|1
    CL     (+):    0.2 mm (0.00787 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 1600 Hz : 14954|43|1|2
    CL     (+):    0.1 mm (0.00394 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 50 Hz : 14954|43|2|0
    CL     (+):    0.1 mm (0.00394 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 400 Hz : 14954|43|2|1
    CL     (+):    0.1 mm (0.00394 inch) thick strip, heat treated at 760 °C (1400 °F) : tested at 20 °C (68 °F), 1600 Hz : 14954|43|2|2

return to listing

SC 16 (*)

    FEN    (+):    0.001/s strain rate : tested at 950 °C (1742 °F), R = -1, axial, total strain range : 14921|14|0|0
    FEN    (+):    0.00001/s strain rate : tested at 950 °C (1742 °F), R = -1, axial, total strain range : 14921|14|1|0

return to listing

SRR99

    E      (+):    solution treated & aged : <001> : 3365|3|0|0
    E      (+):    solution treated & aged : <011> : 3365|3|0|1
    E      (+):    solution treated & aged : <111> : 3365|3|0|2
    SSC    (+):    solution treated & aged, <001> : tested at 20 °C (68 °F), 0.00033/s : 3365|4|0|0
    SSC    (+):    solution treated & aged, <001> : tested at 600 °C (1112 °F), 0.00033/s : 3365|4|0|1
    SSC    (+):    solution treated & aged, <001> : tested at 800 °C (1472 °F), 0.00033/s : 3365|4|0|2
    SSC    (+):    solution treated & aged, <011> : tested at 20 °C (68 °F), 0.00033/s : 3365|4|1|0
    SSC    (+):    solution treated & aged, <011> : tested at 600 °C (1112 °F), 0.00033/s : 3365|4|1|1
    SSC    (+):    solution treated & aged, <011> : tested at 800 °C (1472 °F), 0.00033/s : 3365|4|1|2
    SSC    (+):    solution treated & aged, <111> : tested at 20 °C (68 °F), 0.00033/s : 3365|4|2|0
    SSC    (+):    solution treated & aged, <111> : tested at 600 °C (1112 °F), 0.00033/s : 3365|4|2|1
    SSC    (+):    solution treated & aged, <111> : tested at 800 °C (1472 °F), 0.00033/s : 3365|4|2|2
    YS     (+):    solution treated & aged : <001> : 3365|13|0|0
    YS     (+):    solution treated & aged : <011> : 3365|13|0|1
    YS     (+):    solution treated & aged : <111> : 3365|13|0|2
    FEN    (+):    no hold : tested at 980 °C (1796 °F), R = -1, axial, total strain range : 3365|14|0|0
    FEN    (+):    held for 300 s at the maximum tensile strain : tested at 980 °C (1796 °F), R = -1, axial, total strain range : 3365|14|1|0
    FEN    (+):    held for 300 s at the maximum compressive strain : tested at 980 °C (1796 °F), R = -1, axial, total strain range : 3365|14|2|0

return to listing

Super Mumetal 150 (*)

    TC    (+*):    solid : 14939|1|0|-1
    RHO   (+*):    solid : 14939|2|0|-1
    E     (+*):    solid : 14939|3|0|-1
    UTS   (+*):    hard rolled : 14939|5|0|-1
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14939|7|0|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14939|7|0|1
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14939|7|0|2
    SH    (+*):    solid : 14939|9|0|-1
    SIGMA (+*):    solid : 14939|10|0|-1
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14939|15|0|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14939|15|0|1
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14939|15|0|2
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14939|23|0|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14939|23|0|1
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14939|23|0|2
    D     (+*):    solid : 14939|24|0|-1
    TD    (+*):    solid : 14939|25|0|-1
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14939|31|0|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14939|31|0|1
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14939|31|0|2

return to listing

Super Mumetal 200 (*)

    TC    (+*):    solid : 14940|1|0|-1
    RHO   (+*):    solid : 14940|2|0|-1
    E     (+*):    solid : 14940|3|0|-1
    UTS   (+*):    hard rolled : 14940|5|0|-1
    RPB    (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14940|7|0|0
    SH    (+*):    solid : 14940|9|0|-1
    SIGMA (+*):    solid : 14940|10|0|-1
    AP     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14940|15|0|0
    BH     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14940|23|0|0
    BH     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14940|23|0|1
    BH     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14940|23|0|2
    D     (+*):    solid : 14940|24|0|-1
    TD    (+*):    solid : 14940|25|0|-1
    HB     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14940|31|0|0
    HB     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14940|31|0|1
    HB     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14940|31|0|2

return to listing

Super Mumetal 300 (*)

    TC    (+*):    solid : 14941|1|0|-1
    RHO   (+*):    solid : 14941|2|0|-1
    E     (+*):    solid : 14941|3|0|-1
    UTS   (+*):    hard rolled : 14941|5|0|-1
    RPB    (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14941|7|0|0
    SH    (+*):    solid : 14941|9|0|-1
    SIGMA (+*):    solid : 14941|10|0|-1
    AP     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14941|15|0|0
    BH     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14941|23|0|0
    BH     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14941|23|0|1
    BH     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14941|23|0|2
    D     (+*):    solid : 14941|24|0|-1
    TD    (+*):    solid : 14941|25|0|-1
    HB     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14941|31|0|0
    HB     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14941|31|0|1
    HB     (+):    0.065 mm (0.00256 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14941|31|0|2

return to listing

Super Mumetal (*)

    TC    (+*):    solid : 14937|1|0|-1
    RHO   (+*):    solid : 14937|2|0|-1
    E     (+*):    solid : 14937|3|0|-1
    UTS   (+*):    annealed : 14937|5|0|-1
    UTS   (+*):    hard rolled : 14937|5|1|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14937|7|0|0
    RPB    (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14937|7|1|0
    SH    (+*):    solid : 14937|9|0|-1
    SIGMA (+*):    solid : 14937|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14937|15|0|0
    AP     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14937|15|1|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14937|23|0|0
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14937|23|1|0
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14937|23|1|1
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14937|23|1|2
    D     (+*):    solid : 14937|24|0|-1
    TD    (+*):    solid : 14937|25|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14937|31|0|0
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14937|31|1|0
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14937|31|1|1
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14937|31|1|2

return to listing

Super Radiometal (*)

    TC    (+*):    solid : 14943|1|0|-1
    RHO   (+*):    solid : 14943|2|0|-1
    E     (+*):    solid : 14943|3|0|-1
    UTS   (+*):    hard rolled : 14943|5|0|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14943|7|0|0
    RPB    (+):    0.35 mm (0.0138 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14943|7|1|0
    RPB    (+):    0.35 mm (0.0138 inch) thick strip at 60 Hz : tested at 20 °C (68 °F) : 14943|7|2|0
    RPB    (+):    0.35 mm (0.0138 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14943|7|3|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14943|7|4|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14943|7|5|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 1600 Hz : tested at 20 °C (68 °F) : 14943|7|6|0
    SH    (+*):    solid : 14943|9|0|-1
    SIGMA (+*):    solid : 14943|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14943|15|0|0
    AP     (+):    0.35 mm (0.0138 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14943|15|1|0
    AP     (+):    0.35 mm (0.0138 inch) thick strip at 60 Hz : tested at 20 °C (68 °F) : 14943|15|2|0
    AP     (+):    0.35 mm (0.0138 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14943|15|3|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14943|15|4|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14943|15|5|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 1600 Hz : tested at 20 °C (68 °F) : 14943|15|6|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14943|23|0|0
    BH     (+):    0.35 mm (0.0138 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14943|23|1|0
    BH     (+):    0.35 mm (0.0138 inch) thick strip at 60 Hz : tested at 20 °C (68 °F) : 14943|23|2|0
    BH     (+):    0.35 mm (0.0138 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14943|23|3|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14943|23|4|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14943|23|5|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 1600 Hz : tested at 20 °C (68 °F) : 14943|23|6|0
    D     (+*):    solid : 14943|24|0|-1
    TD    (+*):    solid : 14943|25|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14943|31|0|0
    HB     (+):    0.35 mm (0.0138 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14943|31|1|0
    HB     (+):    0.35 mm (0.0138 inch) thick strip at 60 Hz : tested at 20 °C (68 °F) : 14943|31|2|0
    HB     (+):    0.35 mm (0.0138 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14943|31|3|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F) : 14943|31|4|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 400 Hz : tested at 20 °C (68 °F) : 14943|31|5|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 1.6 kHz : tested at 20 °C (68 °F) : 14943|31|6|0
    CL     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14943|43|0|0
    CL     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), 60 Hz : 14943|43|0|1
    CL     (+):    0.35 mm (0.0138 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14943|43|0|2

return to listing

Telcalloy A (*)

    TC    (+*):    solid : 14935|1|0|-1
    RHO   (+*):    solid : 14935|2|0|-1
    E     (+*):    solid : 14935|3|0|-1
    UTS   (+*):    annealed : 14935|5|0|-1
    UTS   (+*):    hard rolled : 14935|5|1|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14935|7|0|0
    RPB    (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14935|7|1|0
    RPB    (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14935|7|2|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14935|7|3|0
    SH    (+*):    solid : 14935|9|0|-1
    SIGMA (+*):    solid : 14935|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14935|15|0|0
    AP     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14935|15|1|0
    AP     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14935|15|2|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14935|15|3|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14935|23|0|0
    BH     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14935|23|1|0
    BH     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14935|23|1|1
    BH     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14935|23|1|2
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14935|23|2|0
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14935|23|2|1
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14935|23|2|2
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14935|23|3|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14935|23|3|1
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14935|23|3|2
    D     (+*):    solid : 14935|24|0|-1
    TD    (+*):    solid : 14935|25|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14935|31|0|0
    HB     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14935|31|1|0
    HB     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14935|31|1|1
    HB     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14935|31|1|2
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14935|31|2|0
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14935|31|2|1
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14935|31|2|2
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14935|31|3|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14935|31|3|1
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14935|31|3|2
    CL     (+):    0.3 mm (0.0118 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14935|43|0|0
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14935|43|1|0
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14935|43|1|1
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 1.6 kHz : 14935|43|1|2
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 3.2 kHz : 14935|43|1|3
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14935|43|2|0
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14935|43|2|1
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 1.6 kHz : 14935|43|2|2
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 3.2 kHz : 14935|43|2|3
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 1.6 kHz : 14935|43|3|0
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 3.2 kHz : 14935|43|3|1
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 10 kHz : 14935|43|3|2
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 25 kHz : 14935|43|3|3
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 50 kHz : 14935|43|3|4
    CL     (+):    0.013 mm (0.000512 inch) thick strip : tested at 20 °C (68 °F), 10 kHz : 14935|43|4|0
    CL     (+):    0.013 mm (0.000512 inch) thick strip : tested at 20 °C (68 °F), 25 kHz : 14935|43|4|1
    CL     (+):    0.013 mm (0.000512 inch) thick strip : tested at 20 °C (68 °F), 50 kHz : 14935|43|4|2

return to listing

Telcalloy B (*)

    TC    (+*):    solid : 14938|1|0|-1
    RHO   (+*):    solid : 14938|2|0|-1
    E     (+*):    solid : 14938|3|0|-1
    UTS   (+*):    annealed : 14938|5|0|-1
    UTS   (+*):    hard rolled : 14938|5|1|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14938|7|0|0
    RPB    (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14938|7|1|0
    RPB    (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14938|7|2|0
    RPB    (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14938|7|3|0
    SH    (+*):    solid : 14938|9|0|-1
    SIGMA (+*):    solid : 14938|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14938|15|0|0
    AP     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14938|15|1|0
    AP     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14938|15|2|0
    AP     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14938|15|3|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14938|23|0|0
    BH     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14938|23|1|0
    BH     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14938|23|1|1
    BH     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14938|23|1|2
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14938|23|2|0
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14938|23|2|1
    BH     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14938|23|2|2
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14938|23|3|0
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14938|23|3|1
    BH     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14938|23|3|2
    D     (+*):    solid : 14938|24|0|-1
    TD    (+*):    solid : 14938|25|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14938|31|0|0
    HB     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14938|31|1|0
    HB     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14938|31|1|1
    HB     (+):    0.3 mm (0.0118 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14938|31|1|2
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14938|31|2|0
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14938|31|2|1
    HB     (+):    0.2 mm (0.00787 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14938|31|2|2
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), total RMS field : 14938|31|3|0
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), reactive component : 14938|31|3|1
    HB     (+):    0.1 mm (0.00394 inch) thick strip at 50 Hz : tested at 20 °C (68 °F), loss component : 14938|31|3|2
    CL     (+):    0.3 mm (0.0118 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14938|43|0|0
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14938|43|1|0
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14938|43|1|1
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 1.6 kHz : 14938|43|1|2
    CL     (+):    0.1 mm (0.00394 inch) thick strip : tested at 20 °C (68 °F), 3.2 kHz : 14938|43|1|3
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 50 Hz : 14938|43|2|0
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 400 Hz : 14938|43|2|1
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 1.6 kHz : 14938|43|2|2
    CL     (+):    0.05 mm (0.00197 inch) thick strip : tested at 20 °C (68 °F), 3.2 kHz : 14938|43|2|3
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 1.6 kHz : 14938|43|3|0
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 3.2 kHz : 14938|43|3|1
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 10 kHz : 14938|43|3|2
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 25 kHz : 14938|43|3|3
    CL     (+):    0.025 mm (0.000984 inch) thick strip : tested at 20 °C (68 °F), 50 kHz : 14938|43|3|4
    CL     (+):    0.013 mm (0.000512 inch) thick strip : tested at 20 °C (68 °F), 10 kHz : 14938|43|4|0
    CL     (+):    0.013 mm (0.000512 inch) thick strip : tested at 20 °C (68 °F), 25 kHz : 14938|43|4|1
    CL     (+):    0.013 mm (0.000512 inch) thick strip : tested at 20 °C (68 °F), 50 kHz : 14938|43|4|2

return to listing

Temperature compensator R2799 (*)

    RHO   (+*):    solid : 14946|2|0|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14946|7|0|0
    SIGMA (+*):    solid : 14946|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14946|15|0|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14946|23|0|0
    D     (+*):    solid : 14946|24|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14946|31|0|0

return to listing

Temperature compensator R2799A (*)

    RHO   (+*):    solid : 14947|2|0|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14947|7|0|0
    SIGMA (+*):    solid : 14947|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14947|15|0|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14947|23|0|0
    D     (+*):    solid : 14947|24|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14947|31|0|0

return to listing

Temperature compensator R2800 (*)

    RHO   (+*):    solid : 14948|2|0|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14948|7|0|0
    SIGMA (+*):    solid : 14948|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14948|15|0|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14948|23|0|0
    D     (+*):    solid : 14948|24|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14948|31|0|0

return to listing

Temperature compensator R2800A (*)

    RHO   (+*):    solid : 14949|2|0|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14949|7|0|0
    SIGMA (+*):    solid : 14949|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14949|15|0|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14949|23|0|0
    D     (+*):    solid : 14949|24|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14949|31|0|0

return to listing

Temperature compensator R3100 (*)

    RHO   (+*):    solid : 14950|2|0|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14950|7|0|0
    SIGMA (+*):    solid : 14950|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14950|15|0|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14950|23|0|0
    D     (+*):    solid : 14950|24|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14950|31|0|0

return to listing

Temperature compensator R3100A (*)

    RHO   (+*):    solid : 14951|2|0|-1
    RPB    (+):    measured with a DC field : tested at 20 °C (68 °F) : 14951|7|0|0
    SIGMA (+*):    solid : 14951|10|0|-1
    AP     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14951|15|0|0
    BH     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14951|23|0|0
    D     (+*):    solid : 14951|24|0|-1
    HB     (+):    measured with a DC field : tested at 20 °C (68 °F) : 14951|31|0|0

return to listing

TMW-4M3 (*)

    UTS    (+):    solution annealed & aged : 14929|5|0|-1
    SSCC   (+):    0.0005/s : tested at 950 °C (1742 °F) : 14929|12|0|0
    SSCC   (+):    0.005/s : tested at 950 °C (1742 °F) : 14929|12|1|0
    SSCC   (+):    0.05/s : tested at 950 °C (1742 °F) : 14929|12|2|0
    YS     (+):    solution annealed & aged : 14929|13|0|-1
    FEN    (+):    solution annealed & aged : tested at 400 °C (752 °F), R = 0, axial, total strain range : 14929|14|0|0
    FEN    (+):    solution annealed & aged : tested at 650 °C (1202 °F), R = 0, axial, total strain range : 14929|14|0|1
    FEN    (+):    solution annealed & aged : tested at 725 °C (1337 °F), R = 0, axial, total strain range : 14929|14|0|2
    FEN    (+):    solution annealed & aged : tested at 400 °C (752 °F), R = 0, axial, plastic strain range : 14929|14|0|3
    FEN    (+):    solution annealed & aged : tested at 650 °C (1202 °F), R = 0, axial, plastic strain range : 14929|14|0|4
    FEN    (+):    solution annealed & aged : tested at 725 °C (1337 °F), R = 0, axial, plastic strain range : 14929|14|0|5
    SR     (+):    solution annealed & aged : tested at 725 °C (1337 °F) : 14929|22|0|0
    %El    (+):    solution annealed & aged : 14929|29|0|-1

return to listing

TRAN-COR H-0 CARLITE DR electrical steel

    HB     (^):    stress relief annealed, GOES, 50/50 : tested at 20 °C (68 °F) : 10280|31|0|0

return to listing

Udimet 720

    SSCC   (+):    0.0001/s : tested at 1100 °C (2012 °F) : 1946|12|0|0
    SSCC   (+):    0.001/s : tested at 1100 °C (2012 °F) : 1946|12|1|0
    SSCC   (+):    0.01/s : tested at 1100 °C (2012 °F) : 1946|12|2|0
    SSCC   (+):    0.1/s : tested at 1100 °C (2012 °F) : 1946|12|3|0
    FEN    (+):    conventionally atomized : tested at 538 °C (1000 °F), R = 0, K_t = 1.0, axial, total strain range : 1946|14|0|0
    FEN    (+):    HYN atomized : tested at 538 °C (1000 °F), R = 0, K_t = 1.0, axial, total strain range : 1946|14|1|0

return to listing

Udimet 720LI

    UTS    (^):    solution annealed & aged : 1947|5|0|-1
    YS     (^):    solution annealed & aged : 1947|13|0|-1
    FEN    (+):    disc sized forging : tested at 700 °C (1292 °F), R = 0, axial, in air, total strain range : 1947|14|0|0
    FEN    (+):    disc sized forging : tested at 700 °C (1292 °F), R = 0, axial, in vacuum, total strain range : 1947|14|0|1
    FEN    (+):    disc sized forging : tested at 700 °C (1292 °F), R = 0, axial, in air, plastic strain range : 1947|14|0|2
    FEN    (+):    disc sized forging : tested at 700 °C (1292 °F), R = 0, axial, in vacuum, plastic strain range : 1947|14|0|3
    FEN    (+):    disc sized forging : tested at 700 °C (1292 °F), R = 0, axial, in air, elastic strain range : 1947|14|0|4
    FEN    (+):    disc sized forging : tested at 700 °C (1292 °F), R = 0, axial, in vacuum, elastic strain range : 1947|14|0|5

return to listing

Udimet D-979

    CRS    (+):    1% strain, solution treated & aged : tested at 593 °C (1100 °F) : 1948|30|0|0
    CRS    (+):    1% strain, solution treated & aged : tested at 649 °C (1200 °F) : 1948|30|0|1
    CRS    (+):    1% strain, solution treated & aged : tested at 704 °C (1300 °F) : 1948|30|0|2
    CRS    (+):    1% strain, solution treated & aged : tested at 760 °C (1400 °F) : 1948|30|0|3
    CRS    (+):    1% strain, solution treated & aged : tested at 816 °C (1500 °F) : 1948|30|0|4
    CRS    (+):    1% strain, solution treated & aged : Master curve (LMP) : 1948|30|0|5

return to listing

Waspaloy

    FEN    (+):    standard heat treatment (1018 °C (1865 °F) / 843 °C (1550 °F) / 760 °C (1400 °F)) : tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range : 1964|14|3|0
    FEN    (+):    standard heat treatment (1018 °C (1865 °F) / 843 °C (1550 °F) / 760 °C (1400 °F)) : tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range : 1964|14|3|1
    FEN    (+):    standard heat treatment (1018 °C (1865 °F) / 843 °C (1550 °F) / 760 °C (1400 °F)) : tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 1964|14|3|2
    FEN    (+):    standard heat treatment (1018 °C (1865 °F) / 843 °C (1550 °F) / 760 °C (1400 °F)) : tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 1964|14|3|3
    FEN    (+):    standard heat treatment plus 732 °C (1350 °F) for 1000 h : tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range : 1964|14|4|0
    FEN    (+):    standard heat treatment plus 732 °C (1350 °F) for 1000 h : tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range : 1964|14|4|1
    FEN    (+):    standard heat treatment plus 732 °C (1350 °F) for 1000 h : tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 1964|14|4|2
    FEN    (+):    standard heat treatment plus 732 °C (1350 °F) for 1000 h : tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 1964|14|4|3
    FEN    (+):    combination of both heat treatments from Kearsey et. al. : tested at 649 °C (1200 °F), R = 0, axial, to initiation, total strain range : 1964|14|5|0
    FEN    (+):    combination of both heat treatments from Kearsey et. al. : tested at 704 °C (1300 °F), R = 0, axial, to initiation, total strain range : 1964|14|5|1
    FEN    (+):    combination of both heat treatments from Kearsey et. al. : tested at 649 °C (1200 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 1964|14|5|2
    FEN    (+):    combination of both heat treatments from Kearsey et. al. : tested at 704 °C (1300 °F), R = 0, axial, to initiation, 100 s dwell, total strain range : 1964|14|5|3
    SR     (^):    age hardened bar : tested at 649 °C (1200 °F) : 1964|22|2|0
    SR     (^):    age hardened bar : tested at 732 °C (1350 °F) : 1964|22|2|1
    SR     (^):    age hardened bar : tested at 816 °C (1500 °F) : 1964|22|2|2
    SR     (^):    age hardened bar : Master curve (LMP) : 1964|22|2|3

return to listing